JP7172701B2 - White paperboard and coated white paperboard - Google Patents
White paperboard and coated white paperboard Download PDFInfo
- Publication number
- JP7172701B2 JP7172701B2 JP2019024874A JP2019024874A JP7172701B2 JP 7172701 B2 JP7172701 B2 JP 7172701B2 JP 2019024874 A JP2019024874 A JP 2019024874A JP 2019024874 A JP2019024874 A JP 2019024874A JP 7172701 B2 JP7172701 B2 JP 7172701B2
- Authority
- JP
- Japan
- Prior art keywords
- surface layer
- layer
- white paperboard
- paper
- pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、古紙を含む白板紙及び塗工白板紙に関する。 The present invention relates to whiteboard and coated whiteboard including waste paper.
包装箱、本のカバー、絵本等に用いられる白板紙は、一般に、多層抄きされており、一方の面又は両面に、顔料塗工層が備えられて、塗工白板紙とされている場合もある。 White paperboard used for packaging boxes, book covers, picture books, etc. is generally multi-layered, and a coated white paperboard is provided with a pigment coating layer on one or both sides. There is also
白板紙には古紙資源の活用、製造時の経済性等の観点から、古紙パルプを原料として利用されることが多い。このため、特に表層の原料として古紙を使用すると、白板紙の品質を低下させる問題がある。この問題を解決するために、古紙に含まれる残留物質を除去する脱墨処理を強化することがあるが、コスト増等の問題が新たに生じる。 For white paperboard, waste paper pulp is often used as a raw material from the viewpoint of utilization of waste paper resources, economic efficiency at the time of production, and the like. For this reason, if used paper is used as the raw material for the surface layer, there is a problem of deteriorating the quality of the white paperboard. In order to solve this problem, the deinking process for removing the residual substances contained in the waste paper may be strengthened, but new problems such as an increase in cost arise.
そこで、特許文献１には、顔料塗工層に特定のタルクを含有させることにより、顔料塗工層の不透明度を高めて、白板紙のちり・くすみを覆い隠すことが提案されている。しかし、特許文献１の塗工白板紙には、顔料塗工層にタルクが必ず含有されるため、塗工白板紙の用途を狭める場合がある。 Therefore, Patent Document 1 proposes that the pigment coating layer contains a specific talc to increase the opacity of the pigment coating layer to cover up the dust and dullness of the white paperboard. However, the coated whiteboard paper of Patent Document 1 always contains talc in the pigment-coated layer, so the use of the coated whiteboard paper may be narrowed.
本発明は、白板紙の表層に古紙パルプを含みながらも、外観が良好な白板紙及び塗工白板紙を提供する。 The present invention provides a white paperboard and a coated white paperboard having a good appearance while containing waste paper pulp in the surface layer of the white paperboard.
［１］ 表層及び中層を有する多層抄きされた白板紙であって、前記表層は、古紙を原料とする脱インキパルプを含有し、前記表層のＥＲＩＣ値が１０～６０の範囲にあり、前記表層の平面視における、0.01mm2以上0.05mm2未満のちり個数が0～40000個/m2、0.05mm2以上2mm2未満のちり個数が0～4000個/m2の範囲にある、白板紙。
［２］ 前記表層の比吸収係数が５．０ｃｍ２／ｇ以上である、［１］に記載の白板紙。
［３］ 前記表層のISO白色度が６０～８５％の範囲にある、［１］又は［２］に記載の白板紙。
［４］ ［１］～［３］の何れか一項に記載の白板紙の少なくとも一方の表面に、顔料塗工層が設けられた塗工白板紙。
［５］ 前記顔料塗工層の塗工量は、乾燥固形分で１５～２５ｇ／ｍ２である、［４］に記載の塗工白板紙。
［６］ 前記顔料塗工層の不透明度が５０～１００％である、［４］又は［５］に記載の塗工白板紙。
[1] A multi-layered white paperboard having a surface layer and a middle layer, wherein the surface layer contains deinked pulp made from waste paper, the ERIC value of the surface layer is in the range of 10 to 60, and the A white board having a number of dust particles of 0.01 mm 2 or more and less than 0.05 mm 2 in a planar view of the surface layer in a range of 0 to 40000/m 2 and a number of dust particles of 0.05 mm 2 or more to less than 2 mm 2 in a range of 0 to 4000/m 2 . paper.
[2] The white paperboard according to [1], wherein the surface layer has a specific absorption coefficient of 5.0 cm 2 /g or more.
[3] The white paperboard according to [1] or [2], wherein the ISO whiteness of the surface layer is in the range of 60 to 85%.
[4] Coated whiteboard paper, wherein a pigment coating layer is provided on at least one surface of the whiteboard paperboard according to any one of [1] to [3].
[5] The coated white paperboard according to [4], wherein the coating amount of the pigment coating layer is 15 to 25 g/m 2 in dry solid content.
[6] The coated white paperboard according to [4] or [5], wherein the pigment coating layer has an opacity of 50 to 100%.
本発明の白板紙及び塗工白板紙は、表層に古紙パルプを含みながらも、外観が良好であるため、多様な用途に使用することができる。 INDUSTRIAL APPLICABILITY The white paperboard and coated white paperboard of the present invention can be used for various purposes because they have a good appearance while containing waste paper pulp in the surface layer.
≪白板紙≫
本発明の第一態様の白板紙は、多層抄きされており、少なくとも表層及び中層を有する。前記表層は、古紙を原料とする脱インキパルプを含有する。さらに、前記表層のERIC値が10～60の範囲にあり、前記表層の平面視における、0.01mm2以上0.05mm2未満のちり個数が0～40000個/m2、0.05mm2以上のちり個数が0～4000個/m2の範囲にある。
≪White paperboard≫
The white paperboard of the first aspect of the present invention is multi-layered and has at least a surface layer and an intermediate layer. The surface layer contains deinked pulp made from waste paper. Furthermore, the ERIC value of the surface layer is in the range of 10 to 60, the number of dust particles of 0.01 mm 2 or more and less than 0.05 mm 2 is 0 to 40000/m 2 , and the number of dust particles of 0.05 mm 2 or more is is in the range of 0 to 4000/ m2 .
表層は、多層抄き紙の最表面を構成する層である。表層は、古紙を原料とする脱インキパルプを含有する。
中層は、表層よりも白色度が低い層である。中層は、１層でもよいし、２～９層程度の多層構造であってもよい。中層は、古紙を含んでいてもよいし、含まなくてもよいが、古紙を含むことが望ましい。中層が多層構造である場合、中層の各層の原料組成は同じでもよいし、異なっていてもよい。
白板紙は、表層と中層の間に、表層に接する表下層を有してもよいし、有さなくてもよい。表下層の白色度は、中層よりも高く、表層よりも低いことが好ましい。
白板紙は、中層の表層とは反対側に、裏層を有していてもよいし、有さなくてもよい。裏層を形成する原料組成は、中層の原料組成と異なるので、互いの白色度も通常は異なる。
白板紙は、中層と裏層の間に、裏層に接する裏下層を有してもよいし、有さなくてもよい。裏下層の白色度は、中層よりも高く、裏層よりも低いことが好ましい。
The surface layer is a layer constituting the outermost surface of the multilayer paper. The surface layer contains deinked pulp made from waste paper.
The middle layer is a layer having a lower degree of whiteness than the surface layer. The middle layer may be a single layer, or may have a multi-layer structure of about 2 to 9 layers. The middle layer may or may not contain waste paper, but desirably contains waste paper. When the intermediate layer has a multi-layer structure, the raw material composition of each layer of the intermediate layer may be the same or different.
The white paperboard may or may not have a lower surface layer in contact with the surface layer between the surface layer and the middle layer. The whiteness of the lower surface layer is preferably higher than that of the middle layer and lower than that of the surface layer.
White paperboard may or may not have a back layer on the side opposite to the surface layer of the middle layer. Since the raw material composition forming the back layer is different from the raw material composition of the middle layer, the whiteness of each is also usually different.
The white paperboard may or may not have a lower back layer in contact with the back layer between the middle layer and the back layer. The whiteness of the lower back layer is preferably higher than that of the intermediate layer and lower than that of the back layer.
白板紙の坪量は特に制限されず、用途に応じて適宜設定され、例えば、１５０～７００ｇ／ｍ２とすることができ、２００～６００ｇ／ｍ２としてもよいし、３００～５００ｇ／ｍ２としてもよい。 The basis weight of the white paperboard is not particularly limited, and is appropriately set according to the application. may be
以下、各層について詳述する。表層以外の表下層、中層、裏下層、裏層については、公知の白板紙と同様としてよい。 Each layer will be described in detail below. The surface and bottom layers, middle layer, back layer and back layer other than the surface layer may be the same as those of known white paperboard.
［表層］
表層は古紙を原料とする脱インキパルプを含有するので、表層にはインキが残留している。この残留インキを定量する方法として、ＪＩＳ Ｐ ８２５４：２０１３「パルプ及び紙―赤外線反射率測定による有効残留インキ濃度（ＥＲＩＣ値）の試験方法」が知られている。
本態様においては上記ＪＩＳ規格のＥＲＩＣ値を表層の物性の一つとして特定する。具体的には、本態様の白板紙の表層のＥＲＩＣ値の範囲は、１０～６０であり、１５～５５であることが好ましく、２０～５０であることがより好ましい。
表層のＥＲＩＣ値が上記の下限値以上であると、表層の光の吸収量が増加して遮蔽性が高まり、中層のちり・くすみを充分に覆い隠すことができる。表層のＥＲＩＣ値が上記の上限値以下であると、表層の白色度がより向上し、くすみがなく、外観がより一層優れたものとなる。
[surface]
Since the surface layer contains deinked pulp made from waste paper, ink remains on the surface layer. As a method for quantifying this residual ink, JIS P 8254:2013 "Pulp and paper-Test method for effective residual ink concentration (ERIC value) by infrared reflectance measurement" is known.
In this embodiment, the ERIC value of the JIS standard is specified as one of the physical properties of the surface layer. Specifically, the range of the ERIC value of the surface layer of the white paperboard of the present embodiment is 10-60, preferably 15-55, and more preferably 20-50.
When the ERIC value of the surface layer is equal to or higher than the above lower limit, the amount of light absorbed by the surface layer increases to enhance shielding properties, and dust and dullness in the middle layer can be sufficiently covered. When the ERIC value of the surface layer is equal to or less than the above upper limit value, the whiteness of the surface layer is further improved, and the appearance is further improved without dullness.
表層のＥＲＩＣ値は、次の方法で測定される。
まず、白板紙（例えばＡ５サイズ）を５０±２０℃の水又は温水に１～３時間浸漬した後、乾かないうちにピンセットを用い、表層の端部をつまんで剥離させて、ロータリードライヤーにて乾燥して表層を得る。このようにして複数の表層を得た後、表層を複数枚重ね、目視で透けなくなることを確認して、中層側の面（剥離した面）とは反対側の面（表面）を上記ＪＩＳ規格に基づいて測定し、ＥＲＩＣ値を求める。複数の表層を重ねて測定する。
なお、表層に顔料塗工層を含むサンプルについては表面に透明テープを貼り付け、層間剥離させて顔料塗工層を取り除き、得られた塗工層を含まない紙層（表層）を上記測定法に準じて測定する。
ここでは白板紙から表層を剥離してＥＲＩＣ値を求める方法を示したが、本発明者らの検討によれば、白板紙から剥離した表層のＥＲＩＣ値は、抄き合わせる前の表層のみの表面を測定したＥＲＩＣ値と同等であった。よって、本発明のＥＲＩＣ値は、白板紙の製造時に得られる、抄き合わせる前の表層をサンプルとして測定した値であってもよい。
The ERIC value of the surface layer is measured by the following method.
First, white paperboard (for example, A5 size) is immersed in water or warm water at 50 ± 20 ° C. for 1 to 3 hours, and then, before it dries, use tweezers to pinch the edge of the surface layer and peel it off, and use a rotary dryer. Dry to obtain surface layer. After obtaining a plurality of surface layers in this way, a plurality of surface layers are superimposed, visually confirmed that they are not transparent, and the surface (surface) opposite to the surface on the middle layer side (peeled surface) is measured according to the above JIS standard. to determine the ERIC value. Multiple surface layers are overlapped and measured.
For samples containing a pigment coating layer on the surface layer, a transparent tape is attached to the surface, and the pigment coating layer is removed by delamination. Measure according to
Here, a method for obtaining the ERIC value by peeling the surface layer from the white paperboard is shown, but according to the study of the present inventors, the ERIC value of the surface layer peeled from the white paperboard is the surface of only the surface layer before papermaking. was equivalent to the measured ERIC value. Therefore, the ERIC value of the present invention may be a value obtained by measuring a sample of the surface layer before being combined, which is obtained when white paperboard is manufactured.
表層には、原料や製造工程に由来する、種々のサイズのちりが存在し得る。ちりの個数（ちり個数）は、表層を平面視して、ちりのサイズ毎に計測することができる。
表層のちり個数は、次の方法で測定される。
上述のＥＲＩＣ値を測定する場合と同様に、白板紙から表層を剥離して、表層の表面を測定する。また、同等の測定結果が得られる代替方法として、抄き合わせする前の表層の表面を測定する方法でもよい。
表層のちり個数の測定には、王子計測機器株式会社製の微細異物測定装置（型番：ＤＩＰ－２００）を用いる。装置が備えるスキャナの読み取り側に表層の表面をセットし、解像度１６００ｄｐｉで１０ｃｍ×１０ｃｍの画像を取り込み、付属のソフトウェアで解析して求める。
Dust of various sizes can be present on the surface layer due to raw materials and manufacturing processes. The number of dust particles (the number of dust particles) can be measured for each size of dust particles by viewing the surface layer from above.
The dust count on the surface layer is measured by the following method.
As in the case of measuring the ERIC value described above, the surface layer is peeled off from the white paperboard and the surface of the surface layer is measured. Also, as an alternative method for obtaining equivalent measurement results, a method of measuring the surface of the surface layer before the paper is combined may be used.
For measuring the number of dust particles on the surface layer, a micro foreign matter measuring device (model number: DIP-200) manufactured by Oji Scientific Instruments Co., Ltd. is used. The surface of the surface layer is set on the reading side of the scanner provided in the device, and an image of 10 cm x 10 cm is captured at a resolution of 1600 dpi and analyzed by attached software.
本態様の表層における、0.01mm2以上0.05mm2未満のちり個数は、0～40,000個/m2であり、5,000～37,000個/m2であることが好ましく、10,000～35,000個/m2であることがより好ましい。
上記サイズのちり個数が上記の上限値以下であると、外観がより一層優れたものとなる。
The number of dust particles of 0.01 mm 2 or more and less than 0.05 mm 2 in the surface layer of this embodiment is 0 to 40,000/m 2 , preferably 5,000 to 37,000/m 2 , and more preferably 10,000 to 35,000/m 2 . It is more preferable to have
When the number of dust particles having the above size is equal to or less than the above upper limit, the appearance becomes even more excellent.
本態様の表層における、0.05mm2以上2m m2未満のちり個数は、0～4,000個/ m2であり、50～2000個/ m2であることが好ましく、100～1500個/ m2であることがより好ましい。
上記サイズのちり個数が上記の上限値以下であると、外観がより一層優れたものとなる。
The number of dust particles of 0.05 mm 2 or more and less than 2 mm 2 in the surface layer of this embodiment is 0 to 4,000/m 2 , preferably 50 to 2,000 /m 2 , and 100 to 1,500/m 2 . It is more preferable to have
When the number of dust particles having the above size is equal to or less than the above upper limit, the appearance becomes even more excellent.
本態様の表層における、0.004mm m2以上0.01m m2未満のちり個数は、5,000～100,000個/ m2であることが好ましく、10,000～70,000個/ m2であることがより好ましく、30,000～50,000個/ m2であることがさらに好ましい。
上記サイズのちり個数が上記の下限値以上であると、製造工程のコストを低減できる。上記の上限値以下であると、外観がより一層優れたものとなる。
The number of dust particles of 0.004 mm 2 or more and less than 0.01 mm 2 in the surface layer of this embodiment is preferably 5,000 to 100,000/m 2 , more preferably 10,000 to 70,000/m 2 , and more preferably 30,000 to 50,000. more preferably pcs/ m2 .
When the number of dust particles having the above size is equal to or greater than the above lower limit, the cost of the manufacturing process can be reduced. When it is at most the above upper limit value, the appearance becomes much more excellent.
本態様の表層における比吸収係数は、５．０ｃｍ２／ｇ以上であることが好ましく、５．５ｃｍ２／ｇ以上であることがより好ましく、６．０ｃｍ２／ｇ以上であることがさらに好ましく、７．０ｃｍ２／ｇ以上であることが特に好ましい。
前記比吸収係数の上限値は特に制限されず、例えば、９．０ｃｍ２／ｇ以下を目安とすることができる。
比吸収係数が上記の下限値以上であると、表層の遮蔽性が高まり、中層のちり・くすみを充分に覆い隠すことができる。
The specific absorption coefficient of the surface layer of this embodiment is preferably 5.0 cm 2 /g or more, more preferably 5.5 cm 2 /g or more, and even more preferably 6.0 cm 2 /g or more. , 7.0 cm 2 /g or more.
The upper limit of the specific absorption coefficient is not particularly limited, and can be, for example, 9.0 cm 2 /g or less.
When the specific absorption coefficient is at least the above lower limit, the shielding property of the surface layer is enhanced, and the dust and dullness of the middle layer can be sufficiently covered.
表層の比吸収係数は、次の方法で測定される。
上述のＥＲＩＣ値を測定する場合と同様に、白板紙から表層を剥離して、表層の表面を測定する。また、同等の測定結果が得られる代替方法として、抄き合わせする前の表層の表面を測定する方法でもよい。
表層の比吸収係数K、比散乱係数Sは、ＪＩＳ Ｐ ８１４９：２０００の方法に準拠して、波長457nmの単一シート視感反射率R0、固有視感反射率R∞を測定し、このR0、R∞及び紙の坪量W(g/m2)を用いて下記の３つの式（１）により求めた。
The specific absorption coefficient of the surface layer is measured by the following method.
As in the case of measuring the ERIC value described above, the surface layer is peeled off from the white paperboard and the surface of the surface layer is measured. Also, as an alternative method for obtaining equivalent measurement results, a method of measuring the surface of the surface layer before the paper is combined may be used.
The specific absorption coefficient K and the specific scattering coefficient S of the surface layer are obtained by measuring the single sheet luminous reflectance R 0 and the intrinsic luminous reflectance R ∞ at a wavelength of 457 nm in accordance with the method of JIS P 8149:2000. Using R 0 , R ∞ and the basis weight W (g/m 2 ) of the paper, it was determined by the following three equations (1).
本態様の表層における比散乱係数は、３００ｃｍ２／ｇ以上であることが好ましく、３１０ｃｍ２／ｇ以上であることがより好ましく、３２０ｃｍ２／ｇ以上であることがさらに好ましい。
前記比散乱係数の上限値は特に制限されず、例えば、４００ｃｍ２／ｇ以下を目安とすることができる。
比散乱係数が上記の下限値以上であると、表層の遮蔽性が高まり、中層のちり・くすみを充分に覆い隠すことができる。
The specific scattering coefficient of the surface layer of this embodiment is preferably 300 cm 2 /g or more, more preferably 310 cm 2 /g or more, and even more preferably 320 cm 2 /g or more.
The upper limit of the specific scattering coefficient is not particularly limited, and can be, for example, 400 cm 2 /g or less.
When the specific scattering coefficient is equal to or higher than the above lower limit, the shielding property of the surface layer is enhanced, and the dust and dullness of the middle layer can be sufficiently covered.
本態様の表層におけるISO白色度は、６０～８５％であることが好ましく、７０～８５％であることがより好ましく、８０～８５％であることがさらに好ましい。
ISO白色度が上記の下限値以上であると、表層の外観が優れたものとなり、上記の上限値以下であると、表層の遮蔽性が高まり、中層のちり・くすみを充分に覆い隠すことができる。
The ISO whiteness of the surface layer of this embodiment is preferably 60 to 85%, more preferably 70 to 85%, even more preferably 80 to 85%.
If the ISO whiteness is above the lower limit or above, the appearance of the surface layer will be excellent, and if it is below the above upper limit, the shielding property of the surface layer will be enhanced, and the dust and dullness of the middle layer will be sufficiently covered. can.
表層のISO白色度は、次の方法で測定される。
上述のＥＲＩＣ値を測定する場合と同様に、白板紙から表層を剥離して、表層の表面を測定する。また、同等の測定結果が得られる代替方法として、抄き合わせする前の表層の表面を測定する方法法でもよい。
表層のISO白色度は、ＪＩＳ Ｐ ８１４８：２００１ 年に準拠して、紫外線を含む測定における白色度として求められる。
The ISO whiteness of the surface layer is measured by the following method.
As in the case of measuring the ERIC value described above, the surface layer is peeled off from the white paperboard and the surface of the surface layer is measured. Moreover, as an alternative method that can obtain equivalent measurement results, a method of measuring the surface of the surface layer before the sheets are combined may be used.
The ISO whiteness of the surface layer is determined as the whiteness in measurement including ultraviolet rays in accordance with JIS P 8148:2001.
表層の原料である脱インキパルプは、印刷古紙を分散処理した古紙パルプをさらに脱墨処理して得られたものである。印刷古紙としては、例えば、上質紙、中質紙、新聞紙、チラシ、雑誌、段ボール、紙パック等の印刷が施された古紙が挙げられる。これらのうち、段ボールや紙パックが予め除かれた選別古紙が好ましい。
前記脱墨処理は公知方法で行われる。
原料とする脱インキパルプのISO白色度は、コスト等を勘案して、５０～８０％程度であることが好ましい。
The deinked pulp, which is the raw material of the surface layer, is obtained by further deinking the waste paper pulp obtained by dispersing the printed waste paper. Printed waste paper includes, for example, printed waste paper such as high-quality paper, medium-quality paper, newspaper, fliers, magazines, corrugated cardboard, and paper packs. Among these, sorted waste paper from which corrugated cardboard and paper packs have been previously removed is preferable.
The deinking treatment is performed by a known method.
The ISO whiteness of the deinked pulp used as a raw material is preferably about 50 to 80% in consideration of cost and the like.
表層に含まれる脱インキパルプの含有量は、表層に含まれる全パルプの総質量に対して、例えば、６０～１００質量％が好ましく、７０～９５質量％がより好ましく、８０～９０質量％がさらに好ましい。
脱インキパルプの含有量が高いほど、古紙のリサイクルが促進される。フレッシュパルプを配合した場合には、表層の物性を上述した範囲にすることが容易になる。
The content of the deinked pulp contained in the surface layer is, for example, preferably 60 to 100% by mass, more preferably 70 to 95% by mass, and 80 to 90% by mass relative to the total mass of all pulp contained in the surface layer. More preferred.
A higher content of deinked pulp facilitates waste paper recycling. When fresh pulp is blended, it becomes easy to make the physical properties of the surface layer within the ranges described above.
フレッシュパルプとしては、例えば、クラフトパルプ、亜硫酸パルプなどの化学パルプ；サーモメカニカルパルプ、加圧砕木パルプなどの機械パルプ；ケミカルサーモメカニカルパルプなどの半化学パルプ等が挙げられる。 Examples of fresh pulp include chemical pulp such as kraft pulp and sulfite pulp; mechanical pulp such as thermomechanical pulp and pressure groundwood pulp; and semi-chemical pulp such as chemical thermomechanical pulp.
表層の坪量は、表下層や中層の白色ムラが表層の表面の外観に影響することを確実に防止する観点から、例えば、２０～１００ｇ／ｍ２が好ましく、２５～７０ｇ／ｍ２がより好ましく、３０～６０ｇ／ｍ２がさらに好ましく、３５～５０ｇ／ｍ２が特に好ましい。 The basis weight of the surface layer is preferably, for example, 20 to 100 g/m 2 , more preferably 25 to 70 g/m 2 , from the viewpoint of reliably preventing white unevenness in the lower surface layer and middle layer from affecting the appearance of the surface of the surface layer. Preferably, 30 to 60 g/m 2 is more preferable, and 35 to 50 g/m 2 is particularly preferable.
［裏層］
裏層には、表層程の白色度は求められないが、人の目に触れるため、通常、中層よりも白色度の高いパルプが使用される。オフィス用紙等のシュレッダー処理物由来のパルプを含ませてもよい。オフィス用紙等のシュレッダー処理物を離解処理したパルプは、脱墨、漂白処理を行わなくても白色度が比較的高いので、裏層に配合することが好ましい。オフィス用紙等のシュレッダー処理物を離解処理したパルプは、白色度を高めることができるが、その形状上、離解処理の際に水に馴染み難いため、多量に配合しにくい。そのため、裏層のパルプあたり、３～４０質量％、好ましくは３～３０質量％で使用することが好ましい。
[Back layer]
The back layer is not required to be as white as the surface layer, but since it is visible to the human eye, pulp with a higher whiteness than that of the middle layer is usually used. Pulp derived from shredded material such as office paper may also be included. Pulp obtained by defibrating shredded materials such as office paper has a relatively high degree of whiteness even without deinking and bleaching, so it is preferably blended in the backing layer. Pulp obtained by defibrating shredded materials such as office paper can increase the degree of whiteness. Therefore, it is preferably used in an amount of 3 to 40% by mass, preferably 3 to 30% by mass, based on the pulp of the backing layer.
［中層］
中層は通常複数の層から構成される。中層の各層を構成するパルプは、総て同じであってもよいし、異なっていてもよい。
中層は、表層と裏層の間に挟まれる層であるため、通常は、表層や裏層よりも低級なパルプが使用されるのが一般的である。例えば、新聞、雑誌、切符、中質反古、茶模造、段ボール、台紙、地券、ボール、等の離解パルプが挙げられる。
[middle class]
The middle layer is usually composed of multiple layers. Pulp constituting each layer of the middle layer may be the same or different.
Since the middle layer is a layer sandwiched between the surface layer and the back layer, pulp of a lower grade than that of the surface layer and the back layer is generally used. For example, disaggregated pulp from newspapers, magazines, tickets, medium-quality rolls, brown imitations, corrugated cardboard, mounts, coupons, balls, and the like.
表層と中層の間に表下層を設ける場合、表下層には、上記表層に使用されるパルプを使用してもよいが、通常は、表層と比較して低級な古紙、即ち中質繊維を多く含んだ古紙が使用される。例えば、新聞、雑誌、色上、ボール等の脱墨古紙パルプが使用されるのが一般的である。 When a lower surface layer is provided between the surface layer and the middle layer, the pulp used for the surface layer may be used for the lower surface layer, but usually low-grade waste paper compared to the surface layer, that is, a large amount of medium fiber Retained waste paper is used. For example, it is common to use deinked waste paper pulp from newspapers, magazines, colored paper, balls, and the like.
裏層と中層の間に裏下層を設ける場合、裏下層には、裏層に使用されるパルプを使用してもよいが、通常は、裏層と比較して低級な古紙、即ち中質繊維を多く含んだ古紙が使用される。
例えば、新聞、雑誌、色上、ボール等の脱墨古紙パルプが使用されるのが一般的である。
When a lower back layer is provided between the back layer and the middle layer, the pulp used in the back layer may be used for the lower back layer, but usually low-grade waste paper compared to the back layer, that is, medium-density fiber Waste paper containing a large amount of is used.
For example, it is common to use deinked waste paper pulp from newspapers, magazines, colored paper, balls, and the like.
＜作用効果＞
本発明の白板紙の表層は、ＥＲＩＣ値及びちり個数が特定の範囲にあるので、表層が表下層や中層の白色ムラやくすみを充分に遮蔽することができる。このため、本発明の白板紙の表層は、良好な外観を呈する。
<Effect>
Since the surface layer of the white paperboard of the present invention has the ERIC value and the number of dust particles within a specific range, the surface layer can sufficiently shield white unevenness and dullness of the surface lower layer and middle layer. Therefore, the surface layer of the white paperboard of the present invention exhibits a good appearance.
≪塗工白板紙≫
本発明の第二態様の塗工白板紙は、第一態様の白板紙の少なくとも一方の表面に、顔料塗工層が設けられたものである。
［顔料塗工層］
白板紙の表層の表面に形成された顔料塗工層は、顔料及び接着剤を含む層である。本態様が備える顔料塗工層は、１層でもよいし、２層以上でもよいが、白板紙の表層が優れた外観を呈するので、１層で充分である。
≪Coated white paperboard≫
The coated whiteboard paper of the second aspect of the present invention is obtained by providing a pigment coating layer on at least one surface of the whiteboard paper of the first aspect.
[Pigment coating layer]
The pigment coating layer formed on the surface of the white paperboard is a layer containing a pigment and an adhesive. The pigment-coated layer provided in this embodiment may be one layer or two or more layers, but since the surface layer of the white paperboard exhibits an excellent appearance, one layer is sufficient.
塗工白板紙の表層のＥＲＩＣ値は、次の方法で測定される。
まず、塗工白板紙（例えばＡ５サイズ）を５０±２０℃の水又は温水に１～３時間浸漬した後、乾かないうちにピンセットを用い、顔料塗工層の端部をつまんで剥離させて、顔料塗工層側の剥離体１と、中層側の剥離体２とに分割する。通常、剥離体１の顔料塗工層の塗工面（表層と接する面）側には、表層が剥離せずに残っている。この場合、剥離体２は、表層が除かれた白板紙からなる。
次に、剥離体１を乾燥した後、透明粘着テープを剥離体１に残る表層に貼付して、これを剥がし、透明粘着テープの粘着面に表層を移行させる。この粘着面に移行した表層を複数枚重ねて目視で透けなくなることを確認し、顔料塗工層側の表面を上記ＪＩＳ規格に基づいて測定し、ＥＲＩＣ値を求める。
ここでは塗工白板紙から表層を剥離してＥＲＩＣ値を求める方法を示したが、本発明者らの検討によれば、塗工白板紙から剥離した表層のＥＲＩＣ値は、白板紙を抄き合わせる前の表層のみの表面を測定したＥＲＩＣ値と同等であった。よって、本発明のＥＲＩＣ値は、塗工白板紙の製造時に得られる、白板紙を抄き合わせる前の表層をサンプルとして測定した値であってもよい。
The ERIC value of the surface layer of coated white paperboard is measured by the following method.
First, after immersing coated white paperboard (for example, A5 size) in water or hot water at 50 ± 20 ° C. for 1 to 3 hours, use tweezers before it dries, pinch the edge of the pigment coating layer and peel it off. , the separation body 1 on the pigment coating layer side and the separation body 2 on the middle layer side. Usually, the surface layer remains without being peeled off on the coating surface (surface in contact with the surface layer) side of the pigment coating layer of the release body 1 . In this case, the release body 2 is made of white paperboard from which the surface layer has been removed.
Next, after the release body 1 is dried, a transparent adhesive tape is attached to the surface layer remaining on the release body 1 and then peeled off to transfer the surface layer to the adhesive surface of the transparent adhesive tape. A plurality of surface layers transferred to the adhesive surface are superimposed and visually confirmed to be opaque, and the surface on the side of the pigment coating layer is measured according to the above JIS standard to determine the ERIC value.
Here, a method for obtaining the ERIC value by peeling off the surface layer from the coated whiteboard paper is shown, but according to the study of the present inventors, the ERIC value of the surface layer peeled off from the coated whiteboard paper is obtained by making white paperboard. It was equivalent to the ERIC value measured on the surface of only the surface layer before mating. Therefore, the ERIC value of the present invention may be a value obtained by measuring a sample of the surface layer of the white paperboard before the white paperboard is combined, which is obtained during the production of the coated white paperboard.
塗工白板紙の表層における、ちり個数、比吸収係数、比散乱係数、ISO白色度の各測定は、ＥＲＩＣ値を測定する場合と同様に、塗工白板紙から表層を剥離して測定する。また、同等の結果が得られる代替方法として、塗工白板紙の製造時に得られる、白板紙を抄き合わせる前の表層をサンプルとして測定してもよい。具体的な測定は、白板紙について上記の各測定を行う方法及び条件等に準拠して行う。 The dust count, specific absorption coefficient, specific scattering coefficient, and ISO whiteness in the surface layer of the coated whiteboard are measured by removing the surface layer from the coated whiteboard in the same manner as in measuring the ERIC value. In addition, as an alternative method for obtaining the same result, the surface layer of the white paperboard obtained during the manufacture of the coated white paperboard before being combined may be used as a sample for measurement. Specific measurements are performed in accordance with the method and conditions for each of the above measurements for white paperboard.
表層に設ける顔料塗工層の塗工量（坪量）は、乾燥固形分で、例えば、５～５０ｇ／ｍ２とすることができ、１０～３５ｇ／ｍ２が好ましく、１５～２５ｇ／ｍ２がより好ましい。
上記の下限値以上の塗工量であると、表層の表面を充分に被覆して、良好な外観を呈することができる。上記の上限値以下の塗工量であると、表層の優れた外観が顔料塗工層の外観に反映されやすくなり、コスト面でも有利である。
The coating weight (basis weight) of the pigment coating layer provided on the surface layer can be, for example, 5 to 50 g/m 2 in terms of dry solid content, preferably 10 to 35 g/m 2 , and 15 to 25 g/m 2 . 2 is more preferred.
When the coating amount is equal to or more than the above lower limit, the surface of the surface layer can be sufficiently covered and a good appearance can be exhibited. When the coating amount is equal to or less than the above upper limit, the excellent appearance of the surface layer is likely to be reflected in the appearance of the pigment coating layer, which is advantageous in terms of cost.
顔料塗工層の塗工量は、次の方法で求められる。
塗工白板紙（例えばＡ５サイズ）と、塗工白板紙より大きいサイズの透明ポリエチレンフィルム（重量既知）とを重ね合わせて熱圧着し、次いで当該圧着物を０．５モルの銅エチレンジアミン溶液に浸し、紙層を溶解後、水洗、風乾することでフィルムと顔料塗工層の一体化物を白板紙から分離する。フィルムと顔料塗工層の一体化物の質量からフィルム質量を引くことで、顔料塗工層の塗工量を求める。また、簡易的な測定方法として、顔料塗工層を形成する際に塗工した塗工液の塗工量（ｇ／ｍ２）に、塗工液の固形分の比率（不揮発成分の含有率）を積算して算出することもできる。また、塗工白板紙の坪量から白板紙の坪量を差し引いて算出してもよい。
The coating amount of the pigment coating layer is obtained by the following method.
A coated white paperboard (for example, A5 size) and a transparent polyethylene film (weight known) larger than the coated white paperboard are superimposed and thermocompressed, and then the pressed product is immersed in a 0.5 mol copper ethylenediamine solution. After dissolving the paper layer, the integrated product of the film and the pigment coating layer is separated from the white paperboard by washing with water and air-drying. The coating weight of the pigment coating layer is obtained by subtracting the film mass from the combined mass of the film and the pigment coating layer. In addition, as a simple measurement method, the coating amount (g/m 2 ) of the coating liquid applied when forming the pigment coating layer, the ratio of the solid content of the coating liquid (content of non-volatile components ) can also be calculated by accumulating. Alternatively, it may be calculated by subtracting the basis weight of the white paperboard from the basis weight of the coated white paperboard.
本態様の顔料塗工層の不透明度は、５０～１００％であることが好ましく、５５～８０％であることがより好ましく、５５～６５％であることがさらに好ましい。
上記の不透明度は、顔料塗工層の坪量に連動する。下限値以上の不透明度であると、塗工白板紙の外観が表層の影響を受け難くなる。上記の上限値以下の坪量であると、表層の優れた外観が顔料塗工層の外観に反映されやすくなり、コスト面でも有利である。
The opacity of the pigment coating layer of this embodiment is preferably 50 to 100%, more preferably 55 to 80%, even more preferably 55 to 65%.
The above opacity is linked to the basis weight of the pigment coating layer. When the opacity is equal to or higher than the lower limit, the appearance of the coated white paperboard is less likely to be affected by the surface layer. When the basis weight is equal to or less than the above upper limit, the excellent appearance of the surface layer is likely to be reflected in the appearance of the pigment coating layer, which is advantageous in terms of cost.
顔料塗工層の不透明度は、次の方法で測定される。
前述の方法で得られた透明ポリエチレンフィルムと顔料塗工層の一体化物の顔料塗工層の表層に接していた面とは反対側の表面から不透明度を測定する。
不透明度の測定は、ＪＩＳ Ｐ ８１４９:２０００の方法に準拠して行う。
The opacity of the pigment coating layer is measured by the following method.
The opacity is measured from the surface opposite to the surface of the pigment coating layer of the integrated product of the transparent polyethylene film and the pigment coating layer obtained by the above method.
The opacity is measured according to JIS P 8149:2000.
顔料塗工層に含まれる顔料は特に制限されず、例えば、ケイソウ土、タルク、カオリン、焼成カオリン、デラミネーティッドカオリン、重質炭酸カルシウム、軽質炭酸カルシウム、炭酸マグネシウム、炭酸バリウム、二酸化チタン、酸化亜鉛、酸化ケイ素、非晶質シリカ、亜硫酸カルシウム、石膏、ホワイトカーボン、水酸化アルミニウム、水酸化カルシウム、水酸化マグネシウム、水酸化亜鉛、製紙スラッジ、脱墨フロスからの再生無機粒子等の無機填料、尿素―ホルマリン樹脂、ポリスチレン樹脂、塩化ビニル樹脂、メラミン樹脂、フェノール樹脂、プラスチック微小中空粒子などの有機填料など、公知の顔料が挙げられる。
顔料塗工層に含まれる顔料は、１種でもよいし、２種類以上でもよい。
The pigment contained in the pigment coating layer is not particularly limited, and examples thereof include diatomaceous earth, talc, kaolin, calcined kaolin, delaminated kaolin, heavy calcium carbonate, light calcium carbonate, magnesium carbonate, barium carbonate, titanium dioxide, oxide Inorganic fillers such as zinc, silicon oxide, amorphous silica, calcium sulfite, gypsum, white carbon, aluminum hydroxide, calcium hydroxide, magnesium hydroxide, zinc hydroxide, paper sludge, recycled inorganic particles from deinking floss, Known pigments such as urea-formalin resin, polystyrene resin, vinyl chloride resin, melamine resin, phenol resin, and organic fillers such as plastic fine hollow particles can be used.
The pigment contained in the pigment coating layer may be one kind, or two or more kinds.
顔料塗工層に含まれる接着剤は特に制限されず、例えば、スチレン―ブタジエン系、スチレン―アクリル系、エチレン―酢酸ビニル系、ブタジエン―メチルメタクリレート系、酢酸ビニル―ブチルアクリレート系等の各種共重合体、ポリビニルアルコール、無水マレイン酸共重合体、およびアクリル酸―メチルメタクリレート系共重合体等の合成系接着剤；カゼイン、大豆蛋白、合成蛋白等の蛋白質類；酸化澱粉、陽性澱粉、尿素燐酸エステル化澱粉、ヒドロキシエチルエーテル化澱粉等のエーテル化澱粉、デキストリン等の澱粉類；カルボキシメチルセルロース、ヒドロキシエチルセルロース、ヒドロキシメチルセルロース等のセルロース誘導体等の顔料塗工層用の公知の接着剤が挙げられる。
顔料塗工層に含まれる接着剤は、１種でもよいし、２種類以上でもよい。
The adhesive contained in the pigment coating layer is not particularly limited. Synthetic adhesives such as coalescence, polyvinyl alcohol, maleic anhydride copolymer, and acrylic acid-methyl methacrylate copolymer; proteins such as casein, soybean protein, synthetic protein; oxidized starch, positive starch, urea phosphate Etherified starch such as modified starch and hydroxyethyl etherified starch; starches such as dextrin; and known adhesives for pigment coating layers such as cellulose derivatives such as carboxymethyl cellulose, hydroxyethyl cellulose and hydroxymethyl cellulose.
One type of adhesive may be contained in the pigment coating layer, or two or more types may be used.
顔料塗工層に含まれる顔料と接着剤の含有比率は特に制限されず、例えば、顔料１００質量部に対し、接着剤が５～３０質量部であることが好ましく、接着剤が８～２０質量部であることがより好ましい。上記の下限値以上であると、顔料塗工層の強度が充分に高まり、上記の上限値以下であると、コストを抑制することができる。 The content ratio of the pigment and the adhesive contained in the pigment coating layer is not particularly limited. Part is more preferred. When it is at least the above lower limit, the strength of the pigment coating layer is sufficiently increased, and when it is at most the above upper limit, the cost can be suppressed.
塗工白板紙の剛度を高めたり、カールを抑制したりする目的等で、白板紙の裏層側に顔料塗工層または顔料が少ないクリア塗工層（まとめて裏面塗工層という。）を形成してもよい。この場合、裏面塗工層を形成する塗工液には、必要に応じて、公知の、バインダー、分散剤、粘性改良剤、保水剤、消泡剤、耐水化剤、蛍光染料、着色染料、着色顔料、界面活性剤、ｐＨ調整剤、カチオン性樹脂、アニオン性樹脂、紫外線吸収剤、金属塩など、が配合されてもよい。 For the purpose of increasing the rigidity of coated white paperboard and suppressing curling, a pigment coating layer or a clear coating layer with less pigment (collectively referred to as a back coating layer) is applied to the back side of the white paperboard. may be formed. In this case, the coating liquid for forming the back coating layer may optionally contain known binders, dispersants, viscosity improvers, water retention agents, antifoaming agents, water resistance agents, fluorescent dyes, coloring dyes, Coloring pigments, surfactants, pH adjusters, cationic resins, anionic resins, UV absorbers, metal salts and the like may be blended.
前記裏面塗工層用の塗工液の塗工量は特に制限されず、例えば、乾燥固形分で０．１～５．０ｇ／ｍ２程度とすることができる。 The coating amount of the coating liquid for the back coating layer is not particularly limited, and can be, for example, about 0.1 to 5.0 g/m 2 in dry solid content.
＜作用効果＞
本発明の塗工白板紙を顔料塗工層側から観察した際の外観は、顔料塗工層に接する表層のチリ・くすみによる白色ムラの影響を大きく受ける。本発明における表層は、ＥＲＩＣ値及びちり個数が特定の範囲にあるので、表層が表下層や中層の白色ムラやくすみを充分に遮蔽することができる。このため、本発明の塗工白板紙にあっては、顔料塗工層の遮蔽性に依存することなく、良好な外観を呈する。
<Effect>
The appearance of the coated whiteboard of the present invention when observed from the pigment-coated layer side is greatly affected by white unevenness due to dust and dullness on the surface layer in contact with the pigment-coated layer. Since the surface layer in the present invention has the ERIC value and the number of dust particles within a specific range, the surface layer can sufficiently shield white unevenness and dullness of the lower surface layer and the middle layer. Therefore, the coated whiteboard of the present invention exhibits a good appearance without depending on the shielding properties of the pigment coating layer.
≪白板紙の製造方法≫
本発明の白板紙は、上述したＥＲＩＣ値及びちり個数等の物性値が特定の範囲になるように表層を形成すること以外は、従来の白板紙と同様に製造することができる。
≪Method for producing white paperboard≫
The white paperboard of the present invention can be produced in the same manner as conventional white paperboard, except that the surface layer is formed such that the physical property values such as the ERIC value and the number of dust particles fall within specific ranges.
白板紙を製造する際に、上述した物性を有する表層を形成する方法として、例えば、原料の古紙パルプに対する脱墨処理の強度やニーディング処理の回数を調整する方法が挙げられる。
古紙パルプの脱墨処理に用いる薬品の濃度を高めたり、脱墨処理時間を増やしたりして、脱墨処理の強度を上げると、脱インキパルプに残留するインキが低減するので、ＥＲＩＣ値を下げることができる。
古紙パルプのニーディング処理の回数を増やしたり、ニーディング処理に用いる装置の離解力を上げたりすると、脱インキパルプに付着する異物を微細化できるので、上述のちり個数の条件を満たすことができる。
Examples of methods for forming a surface layer having the above physical properties when white paperboard is produced include a method of adjusting the intensity of deinking treatment and the number of times of kneading treatment for the used paper pulp as a raw material.
Increasing the strength of the deinking process by increasing the concentration of the chemicals used in the deinking process of waste paper pulp or increasing the deinking process time will reduce the amount of ink remaining on the deinked pulp, so the ERIC value will be reduced. be able to.
By increasing the number of times of kneading treatment of waste paper pulp or increasing the defibering force of the device used for kneading treatment, the foreign matter adhering to the deinked pulp can be made finer, so the above-mentioned dust number condition can be satisfied. .
表層を抄紙する際に用いる原料スラリーに含まれる脱インキパルプの含有量は、該原料スラリーに含まれる全パルプの総質量に対して、例えば、６０～１００質量％が好ましく、７０～９５質量％がより好ましく、８０～９０質量％がさらに好ましい。
脱インキパルプの含有量が高いほど、古紙のリサイクルが促進される。フレッシュパルプを配合した場合には、表層の物性を上述した範囲にすることが容易になる。
通常、抄紙した表層のパルプ組成は、原料スラリーのパルプ組成と同等になる。
The content of the deinked pulp contained in the raw material slurry used when making the surface layer is, for example, preferably 60 to 100% by mass, preferably 70 to 95% by mass, based on the total mass of all pulp contained in the raw material slurry. is more preferred, and 80 to 90% by mass is even more preferred.
A higher content of deinked pulp facilitates waste paper recycling. When fresh pulp is blended, it becomes easy to make the physical properties of the surface layer within the ranges described above.
Usually, the pulp composition of the surface layer of the paper is the same as the pulp composition of the raw material slurry.
中層を抄紙する際に用いる原料スラリーに含まれる古紙パルプの含有量は、それぞれ独立に、該原料スラリーに含まれる全パルプの総質量に対して、例えば、６０～１００質量％が好ましく、７０～９５質量％がより好ましく、８０～９０質量％がさらに好ましい。
古紙パルプの含有量が高いほど、古紙のリサイクルが促進される。フレッシュパルプを配合した場合には、中層の物性を上述した範囲にすることが容易になる。通常、抄紙した中層のパルプ組成は、原料スラリーのパルプ組成と同等になる。
その他の層を構成するための原料スラリーのパルプ組成は、使用目的に応じて適宜調整する。
The content of the waste paper pulp contained in the raw material slurry used for making the middle layer is each independently based on the total mass of all pulp contained in the raw material slurry, for example, preferably 60 to 100% by mass, 95% by mass is more preferable, and 80 to 90% by mass is even more preferable.
Higher waste paper pulp content facilitates waste paper recycling. When fresh pulp is blended, it becomes easier to set the physical properties of the middle layer within the ranges described above. Usually, the pulp composition of the paper-making middle layer is the same as the pulp composition of the raw material slurry.
The pulp composition of the raw material slurry for forming the other layers is appropriately adjusted according to the purpose of use.
白板紙の抄紙方法は特に制限されず、例えば、トップワイヤー等を含む長網抄紙機、オントップフォーマー、ギャップフォーマー、丸網抄紙機、長網抄紙機と丸網抄紙機を併用した板紙抄紙機、ヤンキードライヤーマシン等を用いて行うことができる。
原料スラリーの抄紙時のｐＨは、酸性、中性、アルカリ性のいずれでもよいが、中性またはアルカリ性が好ましい。
The method of making white paperboard is not particularly limited, and for example, paperboard using a fourdrinier paper machine including a top wire, an on-top former, a gap former, a cylinder paper machine, and a fourdrinier paper machine and a cylinder paper machine. It can be carried out using a paper machine, a Yankee dryer machine, or the like.
The pH of the raw material slurry during papermaking may be acidic, neutral or alkaline, preferably neutral or alkaline.
抄紙後に乾燥させる方法は特に制限されず、例えば、蒸気加熱シリンダ、加熱熱風エアドライヤ、ガスヒータードライヤ、電気ヒータードライヤ、赤外線ヒータードライヤ等各種の方法が単独、もしくは併用して用いられる。 The drying method after paper making is not particularly limited, and for example, various methods such as a steam heating cylinder, a heated hot air dryer, a gas heater dryer, an electric heater dryer, and an infrared heater dryer can be used alone or in combination.
各層の原料スラリーには填料を内添してもよい。
填料は特に制限されず、例えば、ケイソウ土、タルク、カオリン、焼成カオリン、デラミネーティッドカオリン、重質炭酸カルシウム、軽質炭酸カルシウム、炭酸マグネシウム、炭酸バリウム、二酸化チタン、酸化亜鉛、酸化ケイ素、非晶質シリカ、亜硫酸カルシウム、石膏、ホワイトカーボン、水酸化アルミニウム、水酸化カルシウム、水酸化マグネシウム、水酸化亜鉛、製紙スラッジ、脱墨フロスからの再生無機粒子等の無機填料、尿素―ホルマリン樹脂、ポリスチレン樹脂、塩化ビニル樹脂、メラミン樹脂、フェノール樹脂、プラスチック微小中空粒子などの有機填料、さらには古紙やブロークに含まれている填料が挙げられる。
各層の原料スラリーに内添する填料の種類は、１種類でもよいし、２種類以上でもよい。
原料スラリーに填料を含有する場合、抄紙して乾燥した各層の総質量に対して、填料の含有量が、例えば１～２０質量％となるように添加することができる。
A filler may be internally added to the raw material slurry of each layer.
The filler is not particularly limited, and examples thereof include diatomaceous earth, talc, kaolin, calcined kaolin, delaminated kaolin, ground calcium carbonate, ground calcium carbonate, magnesium carbonate, barium carbonate, titanium dioxide, zinc oxide, silicon oxide, amorphous Inorganic fillers such as silica, calcium sulfite, gypsum, white carbon, aluminum hydroxide, calcium hydroxide, magnesium hydroxide, zinc hydroxide, papermaking sludge, inorganic particles recycled from deinked floss, urea-formalin resin, polystyrene resin , vinyl chloride resins, melamine resins, phenolic resins, organic fillers such as hollow plastic microparticles, and fillers contained in used paper and broken paper.
The type of filler internally added to the raw material slurry of each layer may be one type or two or more types.
When the raw material slurry contains a filler, it can be added so that the content of the filler is, for example, 1 to 20% by mass with respect to the total mass of each layer dried after papermaking.
各層の原料スラリーには、凝集助剤、紙力増強剤、染料、顔料、サイズ剤、歩留り向上剤、濾水向上剤、消泡剤を適宜配合してもよい。 The raw material slurry for each layer may optionally contain a flocculation aid, paper strength agent, dye, pigment, sizing agent, retention aid, drainage improver, and antifoaming agent.
≪塗工白板紙の製法≫
塗工白板紙は、白板紙の表層、又は表層及び裏層に対して、顔料塗工層になる顔料塗工液を塗工することにより製造することができる。好ましい塗工量は上述の通りである。
白板紙の表層、又は表層及び裏層に顔料塗工層を形成する塗工方法は特に制限されず、例えば、カーテン塗工、ブレード塗工、ウェットオンウェット塗工等の公知方法を適用できる。
≪Manufacturing method of coated white paperboard≫
Coated white paperboard can be produced by coating a pigment coating liquid to be a pigment coating layer on the surface layer of white paperboard, or on the surface layer and the back layer. Preferred coating amounts are as described above.
The coating method for forming the pigment coating layer on the surface layer or the surface and back layers of the white paperboard is not particularly limited, and known methods such as curtain coating, blade coating, and wet-on-wet coating can be applied.
白板紙の表層における顔料塗工層と、任意の裏面塗工層とを設けた後、適宜乾燥して水分量を調節することにより、塗工白板紙が得られる。また、必要に応じて、顔料塗工層及び裏面塗工層に対して、公知の平滑化処理を施してもよい。 After providing a pigment coating layer on the surface layer of the white paperboard and an optional back coating layer, the coated white paperboard is obtained by appropriately drying to adjust the water content. Further, if necessary, the pigment coating layer and the back coating layer may be subjected to a known smoothing treatment.
［実施例１］
＜白板紙の表層の作成＞
両面の３割が印刷部である色上古紙を縦×横＝３ｃｍ×３ｃｍに細かく裁断したものと、温水と、水酸化ナトリウムとを卓上離解機に投入して、４０℃、１０分間の離解処理を行い、パルプスラリーを得た。
離解処理に際して、パルプ濃度を２質量％に調整し、裁断物の重量に対して０．５質量％の水酸化ナトリウムを添加した。
上記パルプスラリーを濃縮して、パルプ濃度を２５質量％にした後、ＰＦＩミルを用いて１０００回のニーディング処理を行い、得られたパルプを１５０メッシュ金網の上で流水にて洗浄し、古紙パルプを得た。
上記古紙パルプを原料として、１５０メッシュワイヤーを用いてＪＩＳ８２２２：２０１５に従い、坪量３６．７ｇ／ｍ２で手抄き紙を作成し、白板紙の表層とした。
[Example 1]
<Creating the surface layer of the white paperboard>
Colored waste paper whose 30% of both sides is the printing part is finely cut into length x width = 3 cm x 3 cm, warm water, and sodium hydroxide are put into a tabletop disintegrator, and disintegration is performed at 40 ° C for 10 minutes. After treatment, a pulp slurry was obtained.
During the defibration treatment, the pulp concentration was adjusted to 2% by mass, and 0.5% by mass of sodium hydroxide was added to the weight of the shredded material.
After concentrating the pulp slurry to a pulp concentration of 25% by mass, kneading treatment is performed 1000 times using a PFI mill, and the obtained pulp is washed with running water on a 150 mesh wire mesh, and waste paper A pulp was obtained.
Using the waste paper pulp as a raw material, hand-made paper was prepared with a basis weight of 36.7 g/m 2 according to JIS8222:2015 using 150 mesh wire, and used as the surface layer of white paperboard.
＜表層のちり個数の測定＞
上記で作成した手抄き紙の表面に存在する「ちり個数」を下記の１）～６）のちりのサイズ毎に分けて測定した。
ちり個数の測定は、王子計測機器株式会社製の微細異物測定装置（型番：ＤＩＰ－２００）を用いて、スキャナの読み取り側に手抄き紙の表面をセットし、解像度１６００ｄｐｉで１０ｃｍ×１０ｃｍの画像を取り込み、付属のソフトウェアで解析して求めた。
１） 0.004mm2以上0.01m m2未満
２） 0.01m m2以上0.05m m2未満
３） 0.05m m2以上0.20m m2未満
４） 0.20mm2以上0.30m m2未満
５） 0.30m m2以上0.50m m2未満
６） 0.50m m2以上
<Measurement of the number of dust particles on the surface>
The "number of dust particles" present on the surface of the hand-made paper prepared above was measured for each dust size of 1) to 6) below.
To measure the number of dust particles, a fine foreign matter measuring device (model number: DIP-200) manufactured by Oji Scientific Instruments Co., Ltd. is used to set the surface of the hand-made paper on the reading side of the scanner, and a resolution of 1600 dpi and a size of 10 cm × 10 cm. Images were captured and analyzed by the attached software.
1) 0.004 mm 2 or more and less than 0.01 mm 2 2) 0.01 mm 2 or more and less than 0.05 mm 2 3) 0.05 mm 2 or more and less than 0.20 mm 2 4) 0.20 mm 2 or more and less than 0.30 mm 2 5) 0.30 mm 2 or more and less than 0.50 mm 2 6) 0.50mm2 or more
＜表層のＥＲＩＣ値の測定＞
上記で作成した手抄き紙について、ＪＩＳ Ｐ ８２５４：２０１３に準拠してＥＲＩＣ値を測定した。同規格では、試験シートとして用いる手抄き紙の坪量を６０ｇ／ｍ２とすることが規定されている。この規格に準拠するため、上記で作成した手抄き紙を２枚重ねたものを試験シートとして用いた。
<Measurement of ERIC value of surface layer>
The ERIC value of the handmade paper prepared above was measured according to JIS P 8254:2013. The standard stipulates that the basis weight of the hand-made paper used as the test sheet should be 60 g/m 2 . In order to comply with this standard, two sheets of hand-made paper prepared above were piled up and used as a test sheet.
＜表層の白色度の測定＞
上記で作成した手抄き紙について、ＪＩＳ Ｐ ８１４８：２００１年に準拠して、紫外線を含む測定における白色度を測定した。
<Measurement of whiteness of surface layer>
The hand-made paper prepared above was measured for whiteness in a measurement including ultraviolet rays in accordance with JIS P 8148:2001.
＜表層の比散乱係数・比吸収係数の測定＞
上記で作成した手抄き紙について、ＪＩＳ Ｐ ８１４９：２０００の方法に準拠して、波長457nmの単一シート視感反射率R0、固有視感反射率R∞を測定し、このR0、R∞及び紙の坪量W(g/m2)を用いて、前述した３つの式（１）により比吸収係数K、比散乱係数Sを求めた。
<Measurement of surface layer specific scattering coefficient/specific absorption coefficient>
For the handmade paper prepared above, the single sheet luminous reflectance R 0 and the intrinsic luminous reflectance R ∞ at a wavelength of 457 nm were measured according to the method of JIS P 8149 :2000. Using R ∞ and basis weight W (g/m 2 ) of the paper, the specific absorption coefficient K and the specific scattering coefficient S were obtained from the above-mentioned three equations (1).
＜表層の不透明度の測定＞
上記で作成した手抄き紙について、ＪＩＳ Ｐ ８１４９：２０００に準拠して不透明度を測定した。
<Measurement of opacity of surface layer>
The opacity of the handmade paper prepared above was measured according to JIS P 8149:2000.
＜表層の外観の目視評価＞
上記で作成した手抄き紙の表面を約１０ｃｍの距離から目視で観察し、下記の基準で表層の外観を評価した。
◎ ：ちり・くすみは確認できない。
○ ：ちり・くすみがわずかに確認できる。
× ：ちり・くすみが大量に確認できる。
<Visual evaluation of appearance of surface layer>
The surface of the handmade paper prepared above was visually observed from a distance of about 10 cm, and the appearance of the surface layer was evaluated according to the following criteria.
A: Dust and dullness cannot be observed.
○: Dust and dullness can be slightly observed.
x: A large amount of dust and dullness can be confirmed.
＜表層の隠蔽性の目視評価＞
上記で作成した手抄き紙に、市販の白板紙から剥離した脱インキパルプを含む中層を裏面に押し当てた状態で、手抄き紙の表面を約１０ｃｍの距離から目視で観察し、下記の基準で手抄き紙の隠蔽性を評価した。
◎ ：中層のちり・くすみは確認できず、中層の白色度の影響を殆ど受けない。
○ ：中層のちり・くすみは確認できないが、中層の白色度の影響を受ける。
× ：中層のちり・くすみが確認できるし、且つ、中層の白色度の影響を受ける。
<Visual evaluation of hiding property of surface layer>
The surface of the hand-made paper was visually observed from a distance of about 10 cm with the middle layer containing deinked pulp peeled off from the white paperboard on the market pressed against the back surface of the hand-made paper prepared above. The concealability of the hand-made paper was evaluated according to the criteria of
A: No dust or dullness in the middle layer was observed, and the whiteness of the middle layer was hardly affected.
◯: Dust and dullness in the middle layer cannot be confirmed, but are affected by the whiteness of the middle layer.
x: Dust and dullness in the middle layer can be confirmed, and the whiteness of the middle layer is affected.
以上の測定および評価の結果を表１に示す。
表１の結果を示す実施例１の表層にあっては、中層のちり・くすみが表層によって充分に隠蔽され、表層が良好な外観を呈していた。
Table 1 shows the results of the above measurements and evaluations.
In the surface layer of Example 1 showing the results in Table 1, dust and dullness in the middle layer were sufficiently hidden by the surface layer, and the surface layer exhibited a good appearance.
［実施例２］
原料古紙として、両面の９割が印刷部である色上古紙（縦×横＝３ｃｍ×３ｃｍ）を使用したこと以外は、実施例１と同様にして手抄き紙（表層）を作成し、測定及び評価を行ったその結果を表１に示す。
表１の結果において、実施例２が実施例１よりも高いＥＲＩＣ値を示す理由は、原料の古紙が有するインキが多いことによる。
表１の結果を示す実施例２の表層にあっては、中層のちり・くすみが表層によって充分に隠蔽され、表層が良好な外観を呈していた。
[Example 2]
As the raw material waste paper, hand-made paper (surface layer) was prepared in the same manner as in Example 1, except that colored waste paper (length x width = 3 cm x 3 cm) in which 90% of both sides were printed was used. Table 1 shows the results of measurement and evaluation.
The reason why Example 2 shows a higher ERIC value than Example 1 in the results of Table 1 is that the waste paper used as the raw material contains more ink.
In the surface layer of Example 2 showing the results in Table 1, dust and dullness in the middle layer were sufficiently hidden by the surface layer, and the surface layer exhibited a good appearance.
［比較例１］
原料として、古紙を用いず、広葉樹漂白パルプ（LBKP）を使用したこと以外は、実施例１と同様にして手抄き紙（表層）を作成し、測定及び評価を行ったその結果を表１に示す。
表１に示すように、比較例１のＥＲＩＣ値は１０未満であった。その結果、比較例１の表層にあっては、中層のちり・くすみの隠蔽が不十分であった。
[Comparative Example 1]
A hand-made paper (surface layer) was prepared in the same manner as in Example 1 except that bleached hardwood pulp (LBKP) was used instead of waste paper as a raw material, and the results were measured and evaluated. Table 1 shown in
As shown in Table 1, the ERIC value of Comparative Example 1 was less than 10. As a result, in the surface layer of Comparative Example 1, the concealment of dust and dullness in the middle layer was insufficient.
［比較例２］
ニーディング処理の回数を５００回に減じたこと以外は、実施例１と同様にして手抄き紙（表層）を作成し、測定及び評価を行ったその結果を表１に示す。
表１に示すように、比較例２の0.01mm2以上0.05mm2未満のちり個数は、１１万個以上であった。その結果、比較例２の表層にあっては、表層自体のちり・くすみの評価が悪かった。
[Comparative Example 2]
A hand-made paper (surface layer) was prepared in the same manner as in Example 1, except that the number of kneading treatments was reduced to 500. Table 1 shows the results of measurement and evaluation.
As shown in Table 1, the number of dust particles of 0.01 mm 2 or more and less than 0.05 mm 2 in Comparative Example 2 was 110,000 or more. As a result, in the surface layer of Comparative Example 2, the evaluation of dust and dullness of the surface layer itself was poor.
［比較例３］
ニーディング処理の回数を５００回に減じたこと以外は、実施例２と同様にして手抄き紙（表層）を作成し、測定及び評価を行ったその結果を表１に示す。
表１に示すように、比較例３のＥＲＩＣ値は６０超であった。その結果、比較例３の表層にあっては、表層自体のちり・くすみの評価が悪かった。
[Comparative Example 3]
A hand-made paper (surface layer) was prepared in the same manner as in Example 2, except that the number of kneading treatments was reduced to 500. Table 1 shows the results of measurement and evaluation.
As shown in Table 1, the ERIC value of Comparative Example 3 was greater than 60. As a result, in the surface layer of Comparative Example 3, the evaluation of dust and dullness of the surface layer itself was poor.
Claims (6)
前記表層は、古紙を原料とする脱インキパルプを含有し、
前記表層のＥＲＩＣ値が１０～６０であり、
前記表層の平面視における０．０１ｍｍ ２ 以上０．０５ｍｍ ２ 未満のちり個数が、０～４００００個／ｍ ２ であり、
前記表層の平面視における０．０５ｍｍ ２ 以上２ｍｍ ２ 未満のちり個数が、０～４０００個／ｍ ２ であり、
前記表層の平面視における０．００４ｍｍ ２ 以上０．０１ｍｍ ２ 未満のちり個数が、５０００～１０００００個／ｍ ２ である、白板紙。 A multi-layered white paperboard having a surface layer and a middle layer,
The surface layer contains deinked pulp made from waste paper,
The surface layer has an ERIC value of 10 to 60 ,
0.00 in plan view of the surface layer. The number of dust particles of 01 mm2 or more and less than 0.05 mm2 is 0 to 40000 / m2 ,
the number of dust particles of 0.05 mm 2 or more and less than 2 mm 2 in plan view of the surface layer is 0 to 4000/ m 2 ;
The white paperboard , wherein the surface layer has a dust count of 0.004 mm 2 or more and less than 0.01 mm 2 in plan view of 5,000 to 100,000/m 2 .