JP6933438B2 - 熱成形用シート及び食品用トレイ - Google Patents
熱成形用シート及び食品用トレイ Download PDFInfo
- Publication number
- JP6933438B2 JP6933438B2 JP2015171024A JP2015171024A JP6933438B2 JP 6933438 B2 JP6933438 B2 JP 6933438B2 JP 2015171024 A JP2015171024 A JP 2015171024A JP 2015171024 A JP2015171024 A JP 2015171024A JP 6933438 B2 JP6933438 B2 JP 6933438B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- tray
- polypropylene
- extruder
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1] 2以上の層が積層されてなる熱成形用シートであって、該熱成形用シートにおける一方の最外層が結晶性ポリエステルを含有し、且つ他方の最外層がポリプロピレンを含有する、熱成形用シート。
[2] 前記結晶性ポリエステルを含有する最外層の厚さが10μm以上であり、且つ前記熱成形用シートの厚さが200μm以上である、[1]に記載の熱成形用シート。
[3] 食品を収容するための食品用トレイであって、[1]又は[2]に記載の熱成形用シートを有し、且つ結晶性ポリエステルを含有する最外層が食品と接する面に位置する食品用トレイ。
[4] 前記結晶性ポリエステルにおける結晶化ピークのエンタルピーΔH(結晶化)と、融解ピークのエンタルピーΔH(融解)との比(ΔH(結晶化)/ΔH(融解))が0を超える、[3]に記載の食品用トレイ。
ジカルボン酸としては、テレフタル酸、イソフタル酸、オルトフタル酸、2,5−ナフタレンジカルボン酸、2,6−ナフタレンジカルボン酸、1,4−ナフタレンジカルボン酸、1,5−ナフタレンジカルボン酸、ジフェニルカルボン酸、ジフェノキシエタンジカルボン酸、ジフェニルスルホンカルボン酸、アントラセンジカルボン酸、1,3−シクロペンタンジカルボン酸、1,3−シクロヘキサンジカルボン酸、1,4−シクロヘキサンジカルボン酸、ヘキサヒドロテレフタル酸、ヘキサヒドロイソフタル酸、マロン酸、ジメチルマロン酸、コハク酸、3,3−ジエチルコハク酸、グルタル酸、2,2−ジメチルグルタル酸、アジピン酸、2−メチルアジピン酸、トリメチルアジピン酸、ピメリン酸、アゼライン酸、ダイマー酸、セバシン酸、スベリン酸、ドデカジカルボン酸等が挙げられる。
ジオールとしては、エチレングリコール、プロピレングリコール、ヘキサメチレングリコール、ネオペンチルグリコール、1,2−シクロヘキサンジメタノール、1,4−シクロヘキサンジメタノール、デカメチレングリコール、1,3−プロパンジオール、1,4−ブタンジオール、1,5−ペンタンジオール、1,6−ヘキサジオール、2,2−ビス(4−ヒドロキシフェニル)プロパン、ビス(4−ヒドロキシフェニル)スルホン等が挙げられる。
(A)マグネシウム、チタン及びハロゲンを必須成分とする固体触媒成分からなるTi−Mg系触媒、
(B)マグネシウム、チタン及びハロゲンを必須成分とする固体触媒成分に、有機アルミニウム化合物と、必要に応じて電子供与性化合物などの第三成分とを組み合わせた触媒系、
(C)メタロセン系触媒など。
このポリエチレンとしては、直鎖状低密度ポリエチレン、低密度ポリエチレン、高密度ポリエチレンなどの一般的なポリエチレンが使用できる。真空成型時の垂れを抑制するという観点からは、JIS K7210に準拠して190℃、2.16kg荷重で測定されるMFR値が、0.02〜4g/10分以下のポリエチレンが好ましく、さらに好ましくは、0.05〜2g/10分以下である。
さらに、高温時の剛性を持たせるために、造核剤としてではなく、タルクを5〜30重量%で含有することも好ましい。
a)溶融シート状の多層シート状物に静電気を付与し、表面状態が鏡面の冷却ロールに密着させて冷却する方法、
b)溶融シート状の多層シート状物を、表面状態が冷却ロールと表面状態がゴムロール(タッチロールともいう)との間で挟圧し、冷却ロールに密着させて冷却する方法、
c)溶融シート状の多層シート状物を冷却ロールに接触させるときに、エアチャンバー、あるいはエアナイフから吹き出されるエアによって冷却ロールに密着させて冷却する方法、などの公知の方法で実施できる。
上記のうち、b)の方法の場合は、ゴムの硬度が、60−100のシリコンゴム、ネオプレンゴムものなど一般的なものが使用できる。
上記の2つの方法を単独、あるいは両方適用しトレイを製造することにより、結晶化していない成分が多く、そのため、より配向の少ないトレイが製造でき、食品を入れて電子レンジ調理をしても問題が少なく、かつ、変形の少ないトレイが得られる。
食品と接する面に位置する最外層に含まれる結晶性ポリエステルを結晶化させることにより、トレイの穴開きをより効果的に抑制することができる。結晶化させることにより、トレイの耐熱性の上限が、結晶融点付近の温度となるためである。
(積層シート製造:ドライラミ)
未延伸ポリエチレンテレフタレートフィルム(東和化工株式会社製:厚み20μm、幅=500mm)をドライラミネーターの繰り出し機に取り付け、2液混合型脂肪族ポリエステル系接着剤を有機溶剤に希釈して調整した接着剤を含む溶液を、乾燥後の膜厚が2μmとなるようにグラビア塗布した。その後、120℃に温度制御したオーブン中に通し、有機溶剤を揮発させ、除去した。さらに、接着剤面に厚み550μmのポリプロピレンシート(融点=164℃)を重ね、ニップロールにて積層した。40℃で2日間エージングして積層シート1を得た。
積層シート1をバッチ式の真空成形機に取り付け、508℃に設定したヒーターで上下方向から12秒加熱し、シート表面温度が190℃となった時点でヒーターを離し、トレイ状(50mm×120mm×深さ40mm)にポリエステル面を内側として真空成形し、評価用トレイを得た。なお、シート表面温度は、温度表示が10℃刻みの市販のサーモラベルで異なる測定温度範囲のものを複数枚使用し計測した。
このトレイの内側のポリエステル層を剥離し、DSCを用いて昇温速度10℃/min、窒素フロー50ml/minで測定し、結晶化に伴うピーク、融解に伴うピークをそれぞれ求めた。
ついで、成形したトレイに市販のサラダ油を底部より10mm高さまで注ぎ、電子レンジ中に静置したのち、700Wで180秒加熱した。穴の有無を目視にて確認し、その後、サラダ油を廃棄し、水洗いを行った後、ポリエステル層を剥ぎとり、再びDSC測定を実施した。
成形した別のトレイに市販のサラダ油を底部より10mm高さまで注ぎ、電子レンジ中に静置したのち、1800Wでサラダ油が160℃となるまで加熱した。その後、トレイに変形が生じたか否かを目視で観察した。
積層シート1を用い、ヒーター温度550℃、加熱時間10秒、シート表面温度190℃とした以外は参考例1と同様にトレイを作製した。得られたトレイのDSCにより測定したエンタルピー比は0.50であった。この後、成形したトレイを150℃に加熱したギアオーブン中に設置し、15分間熱処理を行って結晶化させた以外は参考例1と同様に評価を行った。熱処理後のシートのDSC測定も行った。熱処理後のエンタルピー比が0であることから、トレイが結晶化していることがわかる。
積層体1と同じ未延伸ポリエチレンテレフタレートとポリプロピレンシートを用い、変性ポリオレフィン樹脂(三井化学株式会社製、アドマーSF731)を280℃に温度調節した50mmφ押出機に投入し、Tダイより厚み30μmとなる押出量で未延伸ポリエチレンテレフタレートとポリプロピレンシートの間に押し出した。その後、40℃に温調した金属ロールとゴムロール間でニップすることで積層シート2を得た。ヒーター温度530℃、加熱時間11秒、シート表面温度190℃とした以外は参考例1と同様に真空成形によりトレイを作製し、参考例1と同様に評価した。
270℃に設定した50mmΦ押出機(押出機A)に150℃で4時間乾燥させたポリエステル樹脂(PET:SHINKONG社製、SHINPETTM5522W)を、同じく260℃に設定した50mmΦ押出機(押出機B)に接着性樹脂(三井化学株式会社製アドマーSF731)を、さらに260℃に設定した40mmΦ押出機(押出機C)にポリプロピレン樹脂組成物(住友化学株式会社製ノーブレンWF836DG3/住友化学株式会社製エクセレンGH030=70/30)をそれぞれ投入し、270℃に設定した300mm幅マルチマニホールドダイより層比として押出機A/押出機B/押出機C=50/20/230μmとなるように各押出機のスクリュー回転数を調整した上で押し出し、15℃温調したゴムロールと20℃で温調した金属ロール間に挟み込み冷却することで積層シート3を得た。ヒーター温度530℃、加熱時間17秒、シート表面温度210℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。
270℃に設定した50mmΦ押出機(押出機A)に150℃で4時間乾燥させたポリエステル樹脂(PET:SHINKONG社製、SHINPETTM5522W)を、同じく260℃に設定した50mmΦ押出機(押出機C)に接着性樹脂(三井化学株式会社製アドマーSF731)を、さらに280℃に設定した65mmΦ押出機(押出機B)にポリプロピレン樹脂組成物(住友化学株式会社製ノーブレンAH1311/東ソー株式会社製ニポロンハード6300=85/15)をそれぞれ投入し、280℃に設定した1000mm幅マルチマニホールドダイより押出機A/押出機C/押出機Bの順に積層し押出した。層比は押出機A/押出機C/押出機B=10/20/270μmとなるように各押出機のスクリュー回転数を調整した上で押し出し、15℃温調したゴムロールと50℃で温調した金属ロール間に挟み込み冷却することで積層シート3を得た。ヒーター温度530℃、加熱時間14秒、シート表面温度220℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。ヒーター温度530℃、加熱時間14秒、シート表面温度220℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。
層比として押出機A/押出機B/押出機C=20/20/260μmとする以外は、実施例5と同様にして、積層シートを得た。ヒーター温度530℃、加熱時間10秒、シート表面温度210℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。
層比として押出機A/押出機B/押出機C=100/20/180μmとする以外は、実施例5と同様にして、積層シートを得た。ヒーター温度530℃、加熱時間17秒、シート表面温度200℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。
層比として押出機A/押出機B/押出機C=20/20/160μmとする以外は、実施例5と同様にして、積層シートを得た。ヒーター温度530℃、加熱時間17秒、シート表面温度210℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。
層比として押出機A/押出機B/押出機C=20/20/760μmとする以外は、実施例5と同様にして、積層シートを得た。ヒーター温度530℃、加熱時間14秒、シート表面温度210℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。
層比として押出機A/押出機B/押出機C=30/50/1120μmとする以外は、実施例5と同様にして、積層シートを得た。ヒーター温度530℃、加熱時間46秒、シート表面温度220℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。
層比として押出機A/押出機B/押出機C=20/20/260μmとする以外は、実施例5と同様にして、積層シートを得た。ヒーター温度380℃、加熱時間63秒、シート表面温度160℃とした以外は参考例1と同様にトレイを作製し、参考例1と同様に評価した。
比較対象として、積層シート1を製造するときに用いたポリプロピレンシートを用いて、参考例1と同様にしてトレイを成形し、参考例1と同様にサラダ油を用いて同様に電子レンジによる評価を行った。
Claims (2)
- 2以上の層の積層体を有する熱成形用シートであって、
該熱成形用シートにおける一方の最外層が結晶性ポリエステルを含有し、且つ他方の最外層がポリプロピレンを70質量%以上含有しポリエチレンを5〜30重量%含有し、
前記結晶性ポリエステルにおける結晶化ピークのエンタルピーΔH(結晶化)と、融解ピークのエンタルピーΔH(融解)との比(ΔH(結晶化)/ΔH(融解))が0.20以上であり、
前記結晶性ポリエステルを含有する最外層の厚さが10〜100μmであり、
前記ポリプロピレンを含有する最外層の厚さが160〜2000μmである、熱成形用シート(但し、前記最外層が、DSC法において、99.9℃/分の速度で昇温し、140℃に達した時点から該温度に保った場合に、結晶化ピークの現れるまでの時間が1分以上であるものを除く)。 - 食品を収容するための食品用トレイであって、
請求項1に記載の熱成形用シートを有し、且つ結晶性ポリエステルを含有する最外層が食品と接する面に位置する食品用トレイ。