JP6695685B2 - Optical laminate and image display device - Google Patents
Optical laminate and image display device Download PDFInfo
- Publication number
- JP6695685B2 JP6695685B2 JP2015235578A JP2015235578A JP6695685B2 JP 6695685 B2 JP6695685 B2 JP 6695685B2 JP 2015235578 A JP2015235578 A JP 2015235578A JP 2015235578 A JP2015235578 A JP 2015235578A JP 6695685 B2 JP6695685 B2 JP 6695685B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- base material
- polarizer
- film
- retardation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、光学積層体およびそれを用いた画像表示装置に関する。 The present invention relates to an optical laminate and an image display device using the same.
近年、薄型ディスプレイの普及と共に、有機ＥＬパネルを搭載したディスプレイ（有機ＥＬ表示装置）が提案されている。有機ＥＬパネルは反射性の高い金属層を有するため、外光反射や背景の映り込み等の問題を生じやすい。そこで、円偏光板を視認側に設けることにより、これらの問題を防ぐことが知られている。一方、表示セル（例えば、有機ＥＬセル）と偏光板との間にタッチセンサーが組み込まれた、いわゆるインナータッチパネル型入力表示装置の需要が高まっている。このような構成の入力表示装置は、画像表示セルとタッチセンサーとの距離が近いので、使用者に自然な入力操作感を与えることが可能となっている。また、上記構成の入力表示装置は、タッチセンサーに形成された導電パターンに起因する反射光の影響を低減することができる。 In recent years, with the spread of thin displays, a display (organic EL display device) equipped with an organic EL panel has been proposed. Since the organic EL panel has a highly reflective metal layer, problems such as external light reflection and background reflection are likely to occur. Therefore, it is known that these problems can be prevented by providing a circularly polarizing plate on the viewing side. On the other hand, there is an increasing demand for a so-called inner touch panel type input display device in which a touch sensor is incorporated between a display cell (for example, an organic EL cell) and a polarizing plate. In the input display device having such a configuration, since the distance between the image display cell and the touch sensor is short, it is possible to give the user a natural input operation feeling. Further, the input display device having the above configuration can reduce the influence of reflected light due to the conductive pattern formed on the touch sensor.
一般に、上記構成の入力表示装置におけるタッチセンサーは、基材と該基材上に形成された導電層とを備えるセンサーフィルムを備える。上記基材には、等方性基材が多用される。この等方性基材が、光学的に完全に等方性であれば、円偏光板による反射防止機能は十分に発揮される。しかしながら、実際には、導電層形成工程、基材の靭性を高める処理等の影響により、等方性を意図した基材においても、若干の異方性が発現する。その結果、円偏光板を配置しても、外光反射や背景の映り込み等の問題が解決しないという問題が生じる場合がある。 Generally, the touch sensor in the input display device having the above configuration includes a sensor film including a base material and a conductive layer formed on the base material. An isotropic substrate is often used as the substrate. If this isotropic substrate is optically isotropic, the antireflection function of the circularly polarizing plate will be sufficiently exerted. However, in reality, due to the influence of the conductive layer forming step, the treatment for increasing the toughness of the base material, etc., some anisotropy is exhibited even in the base material intended to be isotropic. As a result, even if the circularly polarizing plate is arranged, problems such as reflection of external light and reflection of the background may not be solved in some cases.
本発明は上記従来の課題を解決するためになされたものであり、その主たる目的は、光学的に異方性を有する基材（以下、異方性基材ともいう）を備えながらも、反射防止機能に優れる光学積層体を提供することにある。 The present invention has been made to solve the above conventional problems, and its main purpose is to provide an antireflection function while having a substrate having optical anisotropy (hereinafter, also referred to as an anisotropic substrate). The object is to provide an optical laminate excellent in
本発明の光学積層体は、偏光子と該偏光子の少なくとも片側に配置された保護層とを含む偏光板と、位相差層と、導電層と、基材とをこの順に有し、該基材の面内位相差Ｒｅ（５５０）が０ｎｍより大きく、 該基材の遅相軸と該位相差層の遅相軸とのなす角度が、−４０°〜−５０°または４０°〜５０°である。
１つの実施形態においては、上記偏光子の吸収軸と前記位相差層の遅相軸とのなす角度が３８°〜５２°である。
１つの実施形態においては、上記位相差層のＲｅ（４５０）／Ｒｅ（５５０）が、０．８以上１未満である。
１つの実施形態においては、上記位相差層のＲｅ（６５０）／Ｒｅ（５５０）が、１より大きく１．２以下である。
１つの実施形態においては、上記位相差層が、ポリカーボネート系で構成されている。
本発明の別の局面によれば、画像表示装置が提供される。この画像表示装置は、上記光学積層体を備える。
The optical layered body of the present invention has a polarizing plate including a polarizer and a protective layer disposed on at least one side of the polarizer, a retardation layer, a conductive layer, and a base material in this order, and The in-plane retardation Re (550) of the material is larger than 0 nm, and the angle between the slow axis of the base material and the slow axis of the retardation layer is −40 ° to −50 ° or 40 ° to 50 °. Is.
In one embodiment, the angle formed by the absorption axis of the polarizer and the slow axis of the retardation layer is 38 ° to 52 °.
In one embodiment, Re (450) / Re (550) of the retardation layer is 0.8 or more and less than 1.
In one embodiment, Re (650) / Re (550) of the retardation layer is more than 1 and 1.2 or less.
In one embodiment, the above-mentioned retardation layer comprises a polycarbonate system.
According to another aspect of the present invention, an image display device is provided. This image display device includes the optical layered body.
本発明によれば、異方性基材の遅相軸角度を最適化することにより、異方性基材を備えながらも、反射防止機能に優れる光学積層体を提供することができる。 According to the present invention, by optimizing the slow axis angle of the anisotropic base material, it is possible to provide an optical layered body having an excellent antireflection function even though the anisotropic base material is provided.
以下、本発明の実施形態について説明するが、本発明はこれらの実施形態には限定されない。 Hereinafter, embodiments of the present invention will be described, but the present invention is not limited to these embodiments.
（用語および記号の定義）
本明細書における用語および記号の定義は下記の通りである。
（１）屈折率（ｎｘ、ｎｙ、ｎｚ）
「ｎｘ」は面内の屈折率が最大になる方向（すなわち、遅相軸方向）の屈折率であり、「ｎｙ」は面内で遅相軸と直交する方向（すなわち、進相軸方向）の屈折率であり、「ｎｚ」は厚み方向の屈折率である。
（２）面内位相差（Ｒｅ）
「Ｒｅ（λ）」は、２３℃における波長λｎｍの光で測定した面内位相差である。例えば、「Ｒｅ（５５０）」は、２３℃における波長５５０ｎｍの光で測定した面内位相差である。Ｒｅ（λ）は、層（フィルム）の厚みをｄ（ｎｍ）としたとき、式：Ｒｅ（λ）＝（ｎｘ−ｎｙ）×ｄによって求められる。
（３）厚み方向の位相差（Ｒｔｈ）
「Ｒｔｈ（λ）」は、２３℃における波長λｎｍの光で測定した厚み方向の位相差である。例えば、「Ｒｔｈ（５５０）」は、２３℃における波長５５０ｎｍの光で測定した厚み方向の位相差である。Ｒｔｈ（λ）は、層（フィルム）の厚みをｄ（ｎｍ）としたとき、式：Ｒｔｈ（λ）＝（ｎｘ−ｎｚ）×ｄによって求められる。
（４）Ｎｚ係数
Ｎｚ係数は、Ｎｚ＝Ｒｔｈ／Ｒｅによって求められる。
(Definition of terms and symbols)
The definitions of terms and symbols in the present specification are as follows.
(1) Refractive index (nx, ny, nz)
“Nx” is the refractive index in the direction in which the in-plane refractive index is maximum (that is, the slow axis direction), and “ny” is the direction in the plane that is orthogonal to the slow axis (that is, the fast axis direction). , And “nz” is the refractive index in the thickness direction.
(2) In-plane retardation (Re)
“Re (λ)” is an in-plane retardation measured with light having a wavelength of λ nm at 23 ° C. For example, “Re (550)” is an in-plane retardation measured with light having a wavelength of 550 nm at 23 ° C. Re (λ) is calculated by the formula: Re (λ) = (nx−ny) × d when the thickness of the layer (film) is d (nm).
(3) Phase difference (Rth) in the thickness direction
“Rth (λ)” is a phase difference in the thickness direction measured with light having a wavelength of λ nm at 23 ° C. For example, “Rth (550)” is the phase difference in the thickness direction measured with light having a wavelength of 550 nm at 23 ° C. Rth (λ) is calculated by the formula: Rth (λ) = (nx−nz) × d when the thickness of the layer (film) is d (nm).
(4) Nz coefficient The Nz coefficient is calculated by Nz = Rth / Re.
Ａ．光学積層体の全体構成
図１は、本発明の1つの実施形態による光学積層体の概略断面図である。本実施形態の光学積層体１００は、偏光板１１と、位相差層１２と、導電層２１と、基材２２と、をこの順に有する。偏光板１１は、偏光子１と、偏光子１の一方の側に配置された第１の保護層２と、偏光子１のもう一方の側に配置された第２の保護層３とを含む。目的に応じて、第１の保護層２および第２の保護層３の一方は省略されてもよい。例えば、位相差層１２が偏光子１の保護層としても機能し得る場合には、第２の保護層３は省略されてもよい。導電層２１および基材２２は、それぞれが単一層として光学積層体１００の構成要素とされてもよく、基材２２と導電層２１との積層体として光学積層体１００に導入されてもよい。基材２２と導電層２１との積層体は、例えば、タッチセンサーのセンサーフィルム２０として機能し得る。なお、見やすくするために、図面における各層の厚みの比率は、実際とは異なっている。また、光学積層体を構成する各層は、任意の適切な接着層（接着剤層または粘着剤層：図示せず）を介して積層されていてもよい。一方、基材２２は、導電層２１に密着積層されていてもよい。本明細書において「密着積層」とは、２つの層が接着層（例えば、接着剤層、粘着剤層）を介在することなく直接かつ固着して積層されていることをいう。
A. Overall Structure of Optical Laminate FIG. 1 is a schematic sectional view of an optical laminate according to an embodiment of the present invention. The optical layered body 100 of this embodiment has a polarizing plate 11, a retardation layer 12, a conductive layer 21, and a base material 22 in this order. The polarizing plate 11 includes a polarizer 1, a first protective layer 2 arranged on one side of the polarizer 1, and a second protective layer 3 arranged on the other side of the polarizer 1. .. One of the first protective layer 2 and the second protective layer 3 may be omitted depending on the purpose. For example, when the retardation layer 12 can also function as a protective layer for the polarizer 1, the second protective layer 3 may be omitted. Each of the conductive layer 21 and the base material 22 may be a component of the optical layered body 100 as a single layer, or may be introduced into the optical layered body 100 as a layered body of the base material 22 and the conductive layer 21. The laminated body of the base material 22 and the conductive layer 21 can function as the sensor film 20 of the touch sensor, for example. It should be noted that the ratio of the thickness of each layer in the drawings is different from the actual ratio for the sake of clarity. Moreover, each layer which comprises an optical laminated body may be laminated | stacked through arbitrary suitable adhesive layers (adhesive layer or adhesive layer: not shown). On the other hand, the base material 22 may be closely adhered to the conductive layer 21. In the present specification, “adhesive lamination” means that two layers are directly and fixedly laminated without interposing an adhesive layer (for example, an adhesive layer or a pressure-sensitive adhesive layer).
偏光板１１と位相差層１２との積層体１０は、円偏光板として機能し得る。また、基材２２は、光学的に異方性であり得る。本発明においては、異方性基材２２を備えていても、該基材２２の遅相軸と、位相差層１２とのなす角度を特定の範囲（後述のように、−４０°〜−５０°または４０°〜５０°）とすることにより、円偏光板の反射防止機能が十分に発揮されて、外光反射や背景の映り込み等を有効に防止し得る光学積層体を提供することができる。基材２２は面内位相差を有する（例えば、面内位相差Ｒｅ（５５０）が０ｎｍより大きく１０ｎｍ以下）。詳細は後述する。 The laminated body 10 of the polarizing plate 11 and the retardation layer 12 can function as a circularly polarizing plate. Also, the substrate 22 can be optically anisotropic. In the present invention, even if the anisotropic substrate 22 is provided, the angle formed by the slow axis of the substrate 22 and the retardation layer 12 is within a specific range (-40 ° to -50 ° as described later). Or 40 ° to 50 °), the antireflection function of the circularly polarizing plate can be sufficiently exerted, and an optical layered body capable of effectively preventing reflection of external light, reflection of the background, and the like can be provided. .. The base material 22 has an in-plane retardation (for example, the in-plane retardation Re (550) is larger than 0 nm and 10 nm or less). Details will be described later.
光学積層体の総厚みは、好ましくは２２０μｍ以下であり、より好ましくは４０μｍ〜１８０μｍである。 The total thickness of the optical layered body is preferably 220 μm or less, more preferably 40 μm to 180 μm.
光学積層体は、長尺状（例えば、ロール状）であってもよく、枚葉状であってもよい。 The optical laminate may have a long shape (for example, a roll shape) or a sheet shape.
以下、光学積層体を構成する各層および光学フィルムについて、より詳細に説明する。 Hereinafter, each layer and the optical film constituting the optical laminate will be described in more detail.
Ｂ．偏光板
Ｂ−１．偏光子
偏光子１としては、任意の適切な偏光子が採用され得る。例えば、偏光子を形成する樹脂フィルムは、単層の樹脂フィルムであってもよく、二層以上の積層体であってもよい。
B. Polarizing plate B-1. Polarizer Any appropriate polarizer may be adopted as the polarizer 1. For example, the resin film forming the polarizer may be a single-layer resin film or a laminate of two or more layers.
単層の樹脂フィルムから構成される偏光子の具体例としては、ポリビニルアルコール（ＰＶＡ）系フィルム、部分ホルマール化ＰＶＡ系フィルム、エチレン・酢酸ビニル共重合体系部分ケン化フィルム等の親水性高分子フィルムに、ヨウ素や二色性染料等の二色性物質による染色処理および延伸処理が施されたもの、ＰＶＡの脱水処理物やポリ塩化ビニルの脱塩酸処理物等ポリエン系配向フィルム等が挙げられる。好ましくは、光学特性に優れることから、ＰＶＡ系フィルムをヨウ素で染色し一軸延伸して得られた偏光子が用いられる。 Specific examples of the polarizer composed of a single-layer resin film include hydrophilic polymer films such as polyvinyl alcohol (PVA) film, partially formalized PVA film, and ethylene / vinyl acetate copolymer partially saponified film. Examples thereof include polyene oriented films such as those subjected to dyeing treatment and stretching treatment with a dichroic substance such as iodine or dichroic dye, dehydrated PVA products and dehydrochlorinated polyvinyl chloride products. Preferably, a polarizer obtained by dyeing a PVA-based film with iodine and uniaxially stretching it is used because it has excellent optical properties.
上記ヨウ素による染色は、例えば、ＰＶＡ系フィルムをヨウ素水溶液に浸漬することにより行われる。上記一軸延伸の延伸倍率は、好ましくは３〜７倍である。延伸は、染色処理後に行ってもよいし、染色しながら行ってもよい。また、延伸してから染色してもよい。必要に応じて、ＰＶＡ系フィルムに、膨潤処理、架橋処理、洗浄処理、乾燥処理等が施される。例えば、染色の前にＰＶＡ系フィルムを水に浸漬して水洗することで、ＰＶＡ系フィルム表面の汚れやブロッキング防止剤を洗浄することができるだけでなく、ＰＶＡ系フィルムを膨潤させて染色ムラなどを防止することができる。 The dyeing with iodine is performed, for example, by immersing the PVA film in an iodine aqueous solution. The stretching ratio of the uniaxial stretching is preferably 3 to 7 times. Stretching may be performed after the dyeing treatment or may be performed while dyeing. Further, it may be stretched and then dyed. If necessary, the PVA film is subjected to swelling treatment, crosslinking treatment, washing treatment, drying treatment and the like. For example, by immersing a PVA-based film in water and washing it before dyeing, not only can the stains on the surface of the PVA-based film and the antiblocking agent be washed, but also the PVA-based film can be swollen to prevent uneven dyeing. Can be prevented.
積層体を用いて得られる偏光子の具体例としては、樹脂基材と当該樹脂基材に積層されたＰＶＡ系樹脂層（ＰＶＡ系樹脂フィルム）との積層体、あるいは、樹脂基材と当該樹脂基材に塗布形成されたＰＶＡ系樹脂層との積層体を用いて得られる偏光子が挙げられる。樹脂基材と当該樹脂基材に塗布形成されたＰＶＡ系樹脂層との積層体を用いて得られる偏光子は、例えば、ＰＶＡ系樹脂溶液を樹脂基材に塗布し、乾燥させて樹脂基材上にＰＶＡ系樹脂層を形成して、樹脂基材とＰＶＡ系樹脂層との積層体を得ること；当該積層体を延伸および染色してＰＶＡ系樹脂層を偏光子とすること；により作製され得る。本実施形態においては、延伸は、代表的には積層体をホウ酸水溶液中に浸漬させて延伸することを含む。さらに、延伸は、必要に応じて、ホウ酸水溶液中での延伸の前に積層体を高温（例えば、９５℃以上）で空中延伸することをさらに含み得る。得られた樹脂基材／偏光子の積層体はそのまま用いてもよく（すなわち、樹脂基材を偏光子の保護層としてもよく）、樹脂基材／偏光子の積層体から樹脂基材を剥離し、当該剥離面に目的に応じた任意の適切な保護層を積層して用いてもよい。このような偏光子の製造方法の詳細は、例えば特開２０１２−７３５８０号公報に記載されている。当該公報は、その全体の記載が本明細書に参考として援用される。 Specific examples of the polarizer obtained using the laminate include a laminate of a resin base material and a PVA-based resin layer (PVA-based resin film) laminated on the resin base material, or a resin base material and the resin. Examples thereof include a polarizer obtained by using a laminate with a PVA-based resin layer formed by coating on a base material. A polarizer obtained by using a laminate of a resin base material and a PVA-based resin layer formed by coating on the resin base material is, for example, a resin base material obtained by applying a PVA-based resin solution to the resin base material and drying the solution. A PVA-based resin layer is formed thereon to obtain a laminate of a resin substrate and a PVA-based resin layer; the laminate is stretched and dyed to form the PVA-based resin layer as a polarizer obtain. In the present embodiment, the stretching typically includes dipping the laminate in a boric acid aqueous solution and stretching. Further, the stretching may further include optionally stretching the laminate at high temperature (for example, 95 ° C. or higher) in the air before stretching in the boric acid aqueous solution. The resin base material / polarizer laminate thus obtained may be used as it is (that is, the resin base material may be used as a protective layer of the polarizer), and the resin base material is peeled from the resin base material / polarizer laminate. However, any appropriate protective layer may be laminated and used on the peeled surface depending on the purpose. The details of the method for manufacturing such a polarizer are described in, for example, JP 2012-73580 A. The entire description of the publication is incorporated herein by reference.
偏光子の厚みは、好ましくは１５μｍ以下であり、より好ましくは１μｍ〜１２μｍであり、さらに好ましくは３μｍ〜１２μｍであり、特に好ましくは５μｍ〜１２μｍである。 The thickness of the polarizer is preferably 15 μm or less, more preferably 1 μm to 12 μm, further preferably 3 μm to 12 μm, and particularly preferably 5 μm to 12 μm.
偏光子のホウ酸含有量は、好ましくは１８重量％以上であり、より好ましくは１８重量％〜２５重量％である。偏光子のホウ酸含有量がこのような範囲であれば、後述のヨウ素含有量との相乗的な効果により、貼り合わせ時のカール調整の容易性を良好に維持し、かつ、加熱時のカールを良好に抑制しつつ、加熱時の外観耐久性を改善することができる。ホウ酸含有量は、例えば、中和法から下記式を用いて、単位重量当たりの偏光子に含まれるホウ酸量として算出することができる。
偏光子のヨウ素含有量は、好ましくは２．１重量％以上であり、より好ましくは２．１重量％〜３．５重量％である。偏光子のヨウ素含有量がこのような範囲であれば、上記のホウ酸含有量との相乗的な効果により、貼り合わせ時のカール調整の容易性を良好に維持し、かつ、加熱時のカールを良好に抑制しつつ、加熱時の外観耐久性を改善することができる。本明細書において「ヨウ素含有量」とは、偏光子（ＰＶＡ系樹脂フィルム）中に含まれるすべてのヨウ素の量を意味する。より具体的には、偏光子中においてヨウ素はヨウ素イオン（Ｉ−）、ヨウ素分子（Ｉ２）、ポリヨウ素イオン（Ｉ３ −、Ｉ５ −）等の形態で存在するところ、本明細書におけるヨウ素含有量は、これらの形態をすべて包含したヨウ素の量を意味する。ヨウ素含有量は、例えば、蛍光Ｘ線分析の検量線法により算出することができる。なお、ポリヨウ素イオンは、偏光子中でＰＶＡ−ヨウ素錯体を形成した状態で存在している。このような錯体が形成されることにより、可視光の波長範囲において吸収二色性が発現し得る。具体的には、ＰＶＡと三ヨウ化物イオンとの錯体（ＰＶＡ・Ｉ３ −）は４７０ｎｍ付近に吸光ピークを有し、ＰＶＡと五ヨウ化物イオンとの錯体（ＰＶＡ・Ｉ５ −）は６００ｎｍ付近に吸光ピークを有する。結果として、ポリヨウ素イオンは、その形態に応じて可視光の幅広い範囲で光を吸収し得る。一方、ヨウ素イオン（Ｉ−）は２３０ｎｍ付近に吸光ピークを有し、可視光の吸収には実質的には関与しない。したがって、ＰＶＡとの錯体の状態で存在するポリヨウ素イオンが、主として偏光子の吸収性能に関与し得る。 The iodine content of the polarizer is preferably 2.1% by weight or more, more preferably 2.1% by weight to 3.5% by weight. When the iodine content of the polarizer is in such a range, the curl at the time of laminating is favorably maintained due to the synergistic effect with the above boric acid content, and the curl at the time of heating is maintained. It is possible to improve the appearance durability at the time of heating while suppressing the above. In the present specification, the “iodine content” means the amount of all iodine contained in the polarizer (PVA-based resin film). More specifically, iodine is present in the polarizer in the form of iodine ion (I − ), iodine molecule (I 2 ), polyiodine ion (I 3 − , I 5 − ), etc. The iodine content means the amount of iodine including all of these forms. The iodine content can be calculated, for example, by a calibration curve method of fluorescent X-ray analysis. In addition, the polyiodine ion exists in the state which formed the PVA-iodine complex in the polarizer. By forming such a complex, absorption dichroism can be exhibited in the wavelength range of visible light. Specifically, the complex of PVA and triiodide ion (PVA · I 3 − ) has an absorption peak near 470 nm, and the complex of PVA and pentaiodide ion (PVA · I 5 − ) is around 600 nm. Has an absorption peak at. As a result, polyiodine ions can absorb light in a wide range of visible light, depending on their morphology. On the other hand, iodine ion (I − ) has an absorption peak near 230 nm and does not substantially participate in absorption of visible light. Therefore, the polyiodine ion existing in the form of a complex with PVA may be mainly involved in the absorption performance of the polarizer.
偏光子は、好ましくは、波長３８０ｎｍ〜７８０ｎｍのいずれかの波長で吸収二色性を示す。偏光子の単体透過率は、上記のとおり４３．０％〜４６．０％であり、好ましくは４４．５％〜４６．０％である。偏光子の偏光度は、好ましくは９７．０％以上であり、より好ましくは９９．０％以上であり、さらに好ましくは９９．９％以上である。 The polarizer preferably exhibits absorption dichroism at any wavelength of 380 nm to 780 nm. The single transmittance of the polarizer is 43.0% to 46.0%, and preferably 44.5% to 46.0% as described above. The polarization degree of the polarizer is preferably 97.0% or more, more preferably 99.0% or more, and further preferably 99.9% or more.
Ｂ−２．第１の保護層
第１の保護層２は、偏光子の保護層として使用できる任意の適切なフィルムで形成される。当該フィルムの主成分となる材料の具体例としては、トリアセチルセルロース（ＴＡＣ）等のセルロース系樹脂や、ポリエステル系、ポリビニルアルコール系、ポリカーボネート系、ポリアミド系、ポリイミド系、ポリエーテルスルホン系、ポリスルホン系、ポリスチレン系、ポリノルボルネン系、ポリオレフィン系、（メタ）アクリル系、アセテート系等の透明樹脂等が挙げられる。また、（メタ）アクリル系、ウレタン系、（メタ）アクリルウレタン系、エポキシ系、シリコーン系等の熱硬化型樹脂または紫外線硬化型樹脂等も挙げられる。この他にも、例えば、シロキサン系ポリマー等のガラス質系ポリマーも挙げられる。また、特開２００１−３４３５２９号公報（ＷＯ０１／３７００７）に記載のポリマーフィルムも使用できる。このフィルムの材料としては、例えば、側鎖に置換または非置換のイミド基を有する熱可塑性樹脂と、側鎖に置換または非置換のフェニル基ならびにニトリル基を有する熱可塑性樹脂を含有する樹脂組成物が使用でき、例えば、イソブテンとＮ−メチルマレイミドからなる交互共重合体と、アクリロニトリル・スチレン共重合体とを有する樹脂組成物が挙げられる。当該ポリマーフィルムは、例えば、上記樹脂組成物の押出成形物であり得る。
B-2. First Protective Layer The first protective layer 2 is formed of any suitable film that can be used as a protective layer of a polarizer. Specific examples of the material that is the main component of the film include cellulose resins such as triacetyl cellulose (TAC), polyester resins, polyvinyl alcohol resins, polycarbonate resins, polyamide resins, polyimide resins, polyether sulfone resins, and polysulfone resins. , Polystyrene-based, polynorbornene-based, polyolefin-based, (meth) acrylic-based, acetate-based transparent resins and the like. Further, a thermosetting resin such as a (meth) acrylic resin, a urethane resin, a (meth) acrylic urethane resin, an epoxy resin, a silicone resin, or an ultraviolet curable resin can be used. In addition to these, for example, a glassy polymer such as a siloxane polymer may be used. Further, the polymer film described in JP 2001-343529 A (WO 01/37007) can also be used. As a material of this film, for example, a resin composition containing a thermoplastic resin having a substituted or unsubstituted imide group in the side chain and a thermoplastic resin having a substituted or unsubstituted phenyl group and a nitrile group in the side chain. Can be used, and examples thereof include a resin composition having an alternating copolymer of isobutene and N-methylmaleimide and an acrylonitrile / styrene copolymer. The polymer film can be, for example, an extruded product of the resin composition.
本発明の光学積層体は、後述するように代表的には画像表示装置の視認側に配置され、第１の保護層２は、代表的にはその視認側に配置される。したがって、第１の保護層２には、必要に応じて、ハードコート処理、反射防止処理、スティッキング防止処理、アンチグレア処理等の表面処理が施されていてもよい。さらに／あるいは、第１の保護層２には、必要に応じて、偏光サングラスを介して視認する場合の視認性を改善する処理（代表的には、（楕）円偏光機能を付与すること、超高位相差を付与すること）が施されていてもよい。このような処理を施すことにより、偏光サングラス等の偏光レンズを介して表示画面を視認した場合でも、優れた視認性を実現することができる。したがって、光学積層体は、屋外で用いられ得る画像表示装置にも好適に適用され得る。 As will be described later, the optical layered body of the present invention is typically arranged on the viewing side of the image display device, and the first protective layer 2 is typically arranged on the viewing side. Therefore, the first protective layer 2 may be subjected to surface treatment such as hard coat treatment, antireflection treatment, sticking prevention treatment, and antiglare treatment, if necessary. Further / or, if necessary, the first protective layer 2 is processed to improve the visibility when viewed through polarized sunglasses (typically, a (elliptical) circular polarization function is added, (Giving an ultrahigh phase difference) may be applied. By performing such processing, excellent visibility can be realized even when the display screen is viewed through a polarizing lens such as polarized sunglasses. Therefore, the optical laminate can be suitably applied to an image display device that can be used outdoors.
第１の保護層の厚みは、任意の適切な厚みが採用され得る。第１の保護層の厚みは、例えば１０μｍ〜５０μｍであり、好ましくは１５μｍ〜４０μｍである。なお、表面処理が施されている場合、第１の保護層の厚みは、表面処理層の厚みを含めた厚みである。 Any appropriate thickness can be adopted as the thickness of the first protective layer. The thickness of the first protective layer is, for example, 10 μm to 50 μm, preferably 15 μm to 40 μm. When the surface treatment is applied, the thickness of the first protective layer is the thickness including the thickness of the surface treatment layer.
Ｂ−３．第２の保護層
第２の保護層３もまた、偏光子の保護層として使用できる任意の適切なフィルムで形成される。当該フィルムの主成分となる材料は、第１の保護層に関して上記Ｂ−２項で説明したとおりである。第２の保護層３は、光学的に略等方性であることが好ましい。本明細書において「光学的に略等方性である」とは、面内位相差Ｒｅ（５５０）が０ｎｍ〜１０ｎｍであり、厚み方向の位相差Ｒｔｈ（５５０）が−１０ｎｍ〜＋１０ｎｍであることをいう。
B-3. Second Protective Layer The second protective layer 3 is also formed of any suitable film that can be used as a protective layer for the polarizer. The material serving as the main component of the film is as described in the section B-2 for the first protective layer. The second protective layer 3 is preferably optically isotropic. In the present specification, “optically substantially isotropic” means that the in-plane retardation Re (550) is 0 nm to 10 nm, and the thickness direction retardation Rth (550) is −10 nm to +10 nm. Say.
第２の保護層の厚みは、例えば１５μｍ〜３５μｍであり、好ましくは２０μｍ〜３０μｍである。第１の保護層の厚みと第２の保護層の厚みとの差は、好ましくは１５μｍ以下であり、より好ましくは１０μｍ以下である。厚みの差がこのような範囲であれば、貼り合わせ時のカールを良好に抑制することができる。第１の保護層の厚みと第２の保護層の厚みとは、同一であってもよく、第１の保護層の方が分厚くてもよく、第２の保護層の方が分厚くてもよい。代表的には、第２の保護層よりも第１の保護層の方が分厚い。 The thickness of the second protective layer is, for example, 15 μm to 35 μm, preferably 20 μm to 30 μm. The difference between the thickness of the first protective layer and the thickness of the second protective layer is preferably 15 μm or less, more preferably 10 μm or less. When the difference in thickness is within such a range, curling at the time of sticking can be favorably suppressed. The thickness of the first protective layer and the thickness of the second protective layer may be the same, the first protective layer may be thicker, and the second protective layer may be thicker. .. Typically, the first protective layer is thicker than the second protective layer.
Ｃ．位相差層
位相差層１２は、目的に応じて任意の適切な光学的特性および／または機械的特性を有し得る。位相差層１２は、代表的には遅相軸を有する。１つの実施形態においては、位相差層１２の遅相軸と偏光子１の吸収軸とのなす角度θは、好ましくは３８°〜５２°であり、より好ましくは４２°〜４８°であり、さらに好ましくは約４５°である。角度θがこのような範囲であれば、後述するように位相差層をλ／４板とすることにより、非常に優れた円偏光特性（結果として、非常に優れた反射防止特性）を有する光学積層体が得られ得る。
C. Retardation Layer The retardation layer 12 may have any appropriate optical property and / or mechanical property depending on the purpose. The retardation layer 12 typically has a slow axis. In one embodiment, the angle θ formed by the slow axis of the retardation layer 12 and the absorption axis of the polarizer 1 is preferably 38 ° to 52 °, more preferably 42 ° to 48 °, More preferably, it is about 45 °. When the angle θ is in such a range, an optical having very excellent circular polarization characteristics (as a result, very excellent antireflection characteristics) by using a λ / 4 plate as the retardation layer as described later. A laminate can be obtained.
位相差層は、好ましくは屈折率特性がｎｘ＞ｎｙ≧ｎｚの関係を示す。位相差層は、代表的には偏光板に反射防止特性を付与するために設けられ、１つの実施形態においてはλ／４板として機能し得る。この場合、位相差層の面内位相差Ｒｅ（５５０）は、好ましくは８０ｎｍ〜２００ｎｍ、より好ましくは１００ｎｍ〜１８０ｎｍ、さらに好ましくは１１０ｎｍ〜１７０ｎｍである。なお、ここで「ｎｙ＝ｎｚ」はｎｙとｎｚが完全に等しい場合だけではなく、実質的に等しい場合を包含する。したがって、本発明の効果を損なわない範囲で、ｎｙ＜ｎｚとなる場合があり得る。 The retardation layer preferably has a refractive index characteristic of nx> ny ≧ nz. The retardation layer is typically provided to impart antireflection characteristics to the polarizing plate, and can function as a λ / 4 plate in one embodiment. In this case, the in-plane retardation Re (550) of the retardation layer is preferably 80 nm to 200 nm, more preferably 100 nm to 180 nm, still more preferably 110 nm to 170 nm. Here, “ny = nz” includes not only the case where ny and nz are completely equal but also the case where they are substantially equal. Therefore, ny <nz may be satisfied as long as the effect of the present invention is not impaired.
位相差層のＮｚ係数は、好ましくは０．１〜３、より好ましくは０．２〜１．５、さらに好ましくは０．３〜１．３である。このような関係を満たすことにより、得られる光学積層体を画像表示装置に用いた場合に、非常に優れた反射色相を達成し得る。 The Nz coefficient of the retardation layer is preferably 0.1 to 3, more preferably 0.2 to 1.5, and further preferably 0.3 to 1.3. By satisfying such a relationship, a very excellent reflective hue can be achieved when the obtained optical laminate is used in an image display device.
位相差層は、位相差値が測定光の波長に応じて大きくなる逆分散波長特性を示してもよく、位相差値が測定光の波長に応じて小さくなる正の波長分散特性を示してもよく、位相差値が測定光の波長によってもほとんど変化しないフラットな波長分散特性を示してもよい。１つの実施形態においては、位相差層は、逆分散波長特性を示す。この場合、位相差層のＲｅ（４５０）／Ｒｅ（５５０）は、好ましくは０．８以上１未満であり、より好ましくは０．８以上０．９５以下である。また、位相差層のＲｅ（６５０）／Ｒｅ（５５０）は、好ましくは１より大きく１．２以下であり、より好ましくは１．０５以上１．２以下である。このような構成であれば、非常に優れた反射防止特性を実現することができる。また、このように逆波長分散特性を有する位相差層と、遅相軸角度が適切に調整された基材（後述）とを組み合わせることにより、当該効果は顕著となる。なお、位相差層の波長分散特性の制御は、例えば、後述のように樹脂フィルムとして、ポリカーボネート系樹脂フィルムを用い、該ポリカーボネート系樹脂を構成する構造単位の含有割合を調整して、行うことができる。 The retardation layer may exhibit an inverse dispersion wavelength characteristic in which the retardation value increases according to the wavelength of the measurement light, or may exhibit a positive wavelength dispersion characteristic in which the retardation value decreases according to the wavelength of the measurement light. It may well exhibit a flat wavelength dispersion characteristic in which the phase difference value hardly changes depending on the wavelength of the measurement light. In one embodiment, the retardation layer exhibits an inverse dispersion wavelength characteristic. In this case, Re (450) / Re (550) of the retardation layer is preferably 0.8 or more and less than 1, and more preferably 0.8 or more and 0.95 or less. Further, Re (650) / Re (550) of the retardation layer is preferably more than 1 and 1.2 or less, more preferably 1.05 or more and 1.2 or less. With such a configuration, it is possible to realize extremely excellent antireflection characteristics. Further, the effect becomes remarkable by combining the retardation layer having the reverse wavelength dispersion characteristic as described above and the substrate (described later) in which the slow axis angle is appropriately adjusted. The wavelength dispersion characteristics of the retardation layer can be controlled, for example, by using a polycarbonate resin film as the resin film as described below and adjusting the content ratio of the structural units constituting the polycarbonate resin. it can.
位相差層は、光弾性係数の絶対値が好ましくは２×１０−１１ｍ２／Ｎ以下、より好ましくは２．０×１０−１３ｍ２／Ｎ〜１．５×１０−１１ｍ２／Ｎ、さらに好ましくは１．０×１０−１２ｍ２／Ｎ〜１．２×１０−１１ｍ２／Ｎの樹脂を含む。光弾性係数の絶対値がこのような範囲であれば、加熱時の収縮応力が発生した場合に位相差変化が生じにくい。その結果、得られる画像表示装置の熱ムラが良好に防止され得る。 Retardation layer, the absolute value of photoelastic coefficient of preferably 2 × 10 -11 m 2 / N or less, more preferably 2.0 × 10 -13 m 2 /N~1.5×10 -11 m 2 / N, more preferably includes a resin of 1.0 × 10 -12 m 2 /N~1.2×10 -11 m 2 / N. When the absolute value of the photoelastic coefficient is in such a range, the phase difference change is unlikely to occur when contraction stress occurs during heating. As a result, heat unevenness of the obtained image display device can be favorably prevented.
位相差層の厚みは、好ましくは６０μｍ以下であり、好ましくは３０μｍ〜５５μｍである。位相差層の厚みがこのような範囲であれば、加熱時のカールを良好に抑制しつつ、貼り合わせ時のカールを良好に調整することができる。 The thickness of the retardation layer is preferably 60 μm or less, and preferably 30 μm to 55 μm. When the thickness of the retardation layer is in such a range, curling during heating can be suppressed well and curling during bonding can be adjusted well.
位相差層は、上記の特性を満足し得る任意の適切な樹脂フィルムで構成され得る。そのような樹脂の代表例としては、環状オレフィン系樹脂、ポリカーボネート系樹脂、セルロース系樹脂、ポリエステル系樹脂、ポリビニルアルコール系樹脂、ポリアミド系樹脂、ポリイミド系樹脂、ポリエーテル系樹脂、ポリスチレン系樹脂、アクリル系樹脂が挙げられる。位相差層が逆分散波長特性を示す樹脂フィルムで構成される場合、ポリカーボネート系樹脂が好適に用いられ得る。 The retardation layer may be composed of any appropriate resin film that can satisfy the above characteristics. Typical examples of such resins include cyclic olefin resins, polycarbonate resins, cellulose resins, polyester resins, polyvinyl alcohol resins, polyamide resins, polyimide resins, polyether resins, polystyrene resins, and acrylic resins. Examples include resin. When the retardation layer is composed of a resin film exhibiting reverse dispersion wavelength characteristics, a polycarbonate resin can be preferably used.
上記ポリカーボネート樹脂としては、本発明の効果が得られる限りにおいて、任意の適切なポリカーボネート樹脂を用いることができる。好ましくは、ポリカーボネート樹脂は、フルオレン系ジヒドロキシ化合物に由来する構造単位と、イソソルビド系ジヒドロキシ化合物に由来する構造単位と、脂環式ジオール、脂環式ジメタノール、ジ、トリまたはポリエチレングリコール、ならびに、アルキレングリコールまたはスピログリコールからなる群から選択される少なくとも１つのジヒドロキシ化合物に由来する構造単位と、を含む。好ましくは、ポリカーボネート樹脂は、フルオレン系ジヒドロキシ化合物に由来する構造単位と、イソソルビド系ジヒドロキシ化合物に由来する構造単位と、脂環式ジメタノールに由来する構造単位ならびに／あるいはジ、トリまたはポリエチレングリコールに由来する構造単位と、を含み；さらに好ましくは、フルオレン系ジヒドロキシ化合物に由来する構造単位と、イソソルビド系ジヒドロキシ化合物に由来する構造単位と、ジ、トリまたはポリエチレングリコールに由来する構造単位と、を含む。ポリカーボネート樹脂は、必要に応じてその他のジヒドロキシ化合物に由来する構造単位を含んでいてもよい。なお、本発明に好適に用いられ得るポリカーボネート樹脂の詳細は、例えば、特開２０１４−１０２９１号公報、特開２０１４−２６２６６号公報に記載されており、当該記載は本明細書に参考として援用される。 As the polycarbonate resin, any appropriate polycarbonate resin can be used as long as the effects of the present invention can be obtained. Preferably, the polycarbonate resin is a structural unit derived from a fluorene dihydroxy compound, a structural unit derived from an isosorbide dihydroxy compound, an alicyclic diol, an alicyclic dimethanol, di, tri or polyethylene glycol, and an alkylene. A structural unit derived from at least one dihydroxy compound selected from the group consisting of glycols or spiroglycols. Preferably, the polycarbonate resin is derived from a structural unit derived from a fluorene dihydroxy compound, a structural unit derived from an isosorbide dihydroxy compound, a structural unit derived from an alicyclic dimethanol and / or a di, tri or polyethylene glycol. And a structural unit derived from a fluorene-based dihydroxy compound, a structural unit derived from an isosorbide-based dihydroxy compound, and a structural unit derived from a di-, tri- or polyethylene glycol. The polycarbonate resin may contain structural units derived from other dihydroxy compounds, if necessary. The details of the polycarbonate resin that can be preferably used in the present invention are described in, for example, JP-A-2014-10291 and JP-A-2014-26266, and the description is incorporated herein by reference. It
上記ポリカーボネート樹脂のガラス転移温度は、１２０℃以上１９０℃以下であることが好ましく、より好ましくは１３０℃以上１８０℃以下である。ガラス転移温度が過度に低いと耐熱性が悪くなる傾向にあり、フィルム成形後に寸法変化を起こす可能性があり、又、得られる画像表示装置の画像品質を下げる場合がある。ガラス転移温度が過度に高いと、フィルム成形時の成形安定性が悪くなる場合があり、又フィルムの透明性を損なう場合がある。なお、ガラス転移温度は、ＪＩＳ Ｋ ７１２１（１９８７）に準じて求められる。 The glass transition temperature of the polycarbonate resin is preferably 120 ° C. or higher and 190 ° C. or lower, and more preferably 130 ° C. or higher and 180 ° C. or lower. If the glass transition temperature is excessively low, the heat resistance tends to deteriorate, the dimensions may change after the film is formed, and the image quality of the obtained image display device may deteriorate. If the glass transition temperature is excessively high, the molding stability during film molding may be deteriorated, and the transparency of the film may be impaired. The glass transition temperature is determined according to JIS K 7121 (1987).
上記ポリカーボネート樹脂の分子量は、還元粘度で表すことができる。還元粘度は、溶媒として塩化メチレンを用い、ポリカーボネート濃度を０．６ｇ／ｄＬに精密に調製し、温度２０．０℃±０．１℃でウベローデ粘度管を用いて測定される。還元粘度の下限は、通常０．３０ｄＬ／ｇが好ましく、より好ましは０．３５ｄＬ／ｇ以上である。還元粘度の上限は、通常１．２０ｄＬ／ｇが好ましく、より好ましくは１．００ｄＬ／ｇ、更に好ましくは０．８０ｄＬ／ｇである。還元粘度が前記下限値より小さいと成形品の機械的強度が小さくなるという問題が生じる場合がある。一方、還元粘度が前記上限値より大きいと、成形する際の流動性が低下し、生産性や成形性が低下するという問題が生じる場合がある。 The molecular weight of the polycarbonate resin can be represented by reduced viscosity. The reduced viscosity is measured using a Ubbelohde viscosity tube at a temperature of 20.0 ° C. ± 0.1 ° C. by precisely adjusting the polycarbonate concentration to 0.6 g / dL using methylene chloride as a solvent. The lower limit of the reduced viscosity is usually preferably 0.30 dL / g, more preferably 0.35 dL / g or more. The upper limit of the reduced viscosity is usually preferably 1.20 dL / g, more preferably 1.00 dL / g, further preferably 0.80 dL / g. If the reduced viscosity is smaller than the lower limit value, there may occur a problem that the mechanical strength of the molded product becomes small. On the other hand, when the reduced viscosity is higher than the upper limit value, the fluidity at the time of molding may be lowered, and the productivity and the moldability may be lowered.
ポリカーボネート系樹脂フィルムとして市販のフィルムを用いてもよい。市販品の具体例としては、帝人社製の商品名「ピュアエースＷＲ−Ｓ」、「ピュアエースＷＲ−Ｗ」、「ピュアエースＷＲ−Ｍ」、日東電工社製の商品名「ＮＲＦ」が挙げられる。 A commercially available film may be used as the polycarbonate resin film. Specific examples of commercially available products include Teijin's product names "Pure Ace WR-S", "Pure Ace WR-W", "Pure Ace WR-M", and Nitto Denko's product name "NRF". Be done.
位相差層は、例えば、上記ポリカーボネート系樹脂から形成されたフィルムを延伸することにより得られる。ポリカーボネート系樹脂からフィルムを形成する方法としては、任意の適切な成形加工法が採用され得る。具体例としては、圧縮成形法、トランスファー成形法、射出成形法、押出成形法、ブロー成形法、粉末成形法、ＦＲＰ成形法、キャスト塗工法（例えば、流延法）、カレンダー成形法、熱プレス法等が挙げられる。押出成形法またはキャスト塗工法が好ましい。得られるフィルムの平滑性を高め、良好な光学的均一性を得ることができるからである。成形条件は、使用される樹脂の組成や種類、位相差層に所望される特性等に応じて適宜設定され得る。なお、上記のとおり、ポリカーボネート系樹脂は、多くのフィルム製品が市販されているので、当該市販フィルムをそのまま延伸処理に供してもよい。 The retardation layer is obtained, for example, by stretching a film formed of the above polycarbonate resin. Any appropriate molding method can be adopted as a method of forming a film from the polycarbonate-based resin. Specific examples include compression molding method, transfer molding method, injection molding method, extrusion molding method, blow molding method, powder molding method, FRP molding method, cast coating method (for example, casting method), calender molding method, hot press. Law etc. are mentioned. An extrusion molding method or a cast coating method is preferable. This is because the smoothness of the obtained film can be improved and good optical uniformity can be obtained. The molding conditions can be appropriately set depending on the composition and type of the resin used, the characteristics desired for the retardation layer, and the like. As described above, since many film products of the polycarbonate-based resin are commercially available, the commercially available film may be directly subjected to the stretching treatment.
樹脂フィルム（未延伸フィルム）の厚みは、位相差層の所望の厚み、所望の光学特性、後述の延伸条件などに応じて、任意の適切な値に設定され得る。好ましくは５０μｍ〜３００μｍである。 The thickness of the resin film (unstretched film) can be set to any appropriate value depending on the desired thickness of the retardation layer, desired optical characteristics, stretching conditions described below, and the like. It is preferably 50 μm to 300 μm.
上記延伸は、任意の適切な延伸方法、延伸条件（例えば、延伸温度、延伸倍率、延伸方向）が採用され得る。具体的には、自由端延伸、固定端延伸、自由端収縮、固定端収縮などの様々な延伸方法を、単独で用いることも、同時もしくは逐次で用いることもできる。延伸方向に関しても、長さ方向、幅方向、厚さ方向、斜め方向等、様々な方向や次元に行なうことができる。延伸の温度は、樹脂フィルムのガラス転移温度（Ｔｇ）に対し、Ｔｇ−３０℃〜Ｔｇ＋６０℃であることが好ましく、Ｔｇ−３０℃〜Ｔｇ＋５０℃であることがより好ましく、Ｔｇ−１５℃〜Ｔｇ＋３０℃であることがさらに好ましい。 Any appropriate stretching method and stretching conditions (eg, stretching temperature, stretching ratio, stretching direction) can be adopted for the stretching. Specifically, various stretching methods such as free-end stretching, fixed-end stretching, free-end contraction, and fixed-end contraction can be used alone or simultaneously or sequentially. The stretching direction can also be performed in various directions and dimensions such as the length direction, the width direction, the thickness direction, and the oblique direction. The stretching temperature is preferably Tg-30 ° C to Tg + 60 ° C, more preferably Tg-30 ° C to Tg + 50 ° C, more preferably Tg-15 ° C to Tg + 30 with respect to the glass transition temperature (Tg) of the resin film. More preferably, it is ° C.
上記延伸方法、延伸条件を適宜選択することにより、上記所望の光学特性（例えば、屈折率特性、面内位相差、Ｎｚ係数）を有する位相差フィルムを得ることができる。 A retardation film having the desired optical characteristics (for example, refractive index characteristics, in-plane retardation, Nz coefficient) can be obtained by appropriately selecting the above stretching method and stretching conditions.
１つの実施形態においては、位相差フィルムは、樹脂フィルムを一軸延伸もしくは固定端一軸延伸することにより作製される。固定端一軸延伸の具体例としては、樹脂フィルムを長手方向に走行させながら、幅方向（横方向）に延伸する方法が挙げられる。延伸倍率は、好ましくは１．１倍〜３．５倍である。 In one embodiment, the retardation film is produced by uniaxially stretching or fixed-end uniaxially stretching a resin film. A specific example of the fixed-end uniaxial stretching is a method of stretching the resin film in the width direction (transverse direction) while running the resin film in the longitudinal direction. The draw ratio is preferably 1.1 times to 3.5 times.
別の実施形態においては、位相差フィルムは、長尺状の樹脂フィルムを長手方向に対して上記の角度θの方向に連続的に斜め延伸することにより作製され得る。斜め延伸を採用することにより、フィルムの長手方向に対して角度θの配向角（角度θの方向に遅相軸）を有する長尺状の延伸フィルムが得られ、例えば、偏光子との積層に際してロールトゥロールが可能となり、製造工程を簡略化することができる。なお、角度θは、位相差層付偏光板において偏光子の吸収軸と位相差層の遅相軸とがなす角度であり得る。角度θは、上記のとおり、好ましくは３８°〜５２°であり、より好ましくは４２°〜４８°であり、さらに好ましくは約４５°である。 In another embodiment, the retardation film can be produced by continuously obliquely stretching a long resin film in the direction of the angle θ with respect to the longitudinal direction. By adopting the oblique stretching, a long stretched film having an orientation angle of θ with respect to the longitudinal direction of the film (a slow axis in the direction of the angle θ) is obtained, and for example, when laminated with a polarizer. Roll-to-roll is possible, and the manufacturing process can be simplified. The angle θ may be an angle formed by the absorption axis of the polarizer and the slow axis of the retardation layer in the polarizing plate with the retardation layer. As described above, the angle θ is preferably 38 ° to 52 °, more preferably 42 ° to 48 °, and further preferably about 45 °.
斜め延伸に用いる延伸機としては、例えば、横および／または縦方向に、左右異なる速度の送り力もしくは引張り力または引き取り力を付加し得るテンター式延伸機が挙げられる。テンター式延伸機には、横一軸延伸機、同時二軸延伸機等があるが、長尺状の樹脂フィルムを連続的に斜め延伸し得る限り、任意の適切な延伸機が用いられ得る。 As a stretching machine used for oblique stretching, for example, a tenter type stretching machine capable of adding a feeding force or a pulling force or a pulling force at different speeds in the lateral and / or longitudinal directions can be mentioned. Examples of the tenter type stretching machine include a horizontal uniaxial stretching machine and a simultaneous biaxial stretching machine. Any appropriate stretching machine can be used as long as a long resin film can be continuously stretched obliquely.
上記延伸機において左右の速度をそれぞれ適切に制御することにより、上記所望の面内位相差を有し、かつ、上記所望の方向に遅相軸を有する位相差層（実質的には、長尺状の位相差フィルム）が得られ得る。 By appropriately controlling the left and right speeds in the stretching machine, respectively, the retardation layer having the desired in-plane retardation and having a slow axis in the desired direction (substantially long Phase retardation film) can be obtained.
上記フィルムの延伸温度は、位相差層に所望される面内位相差値および厚み、使用される樹脂の種類、使用されるフィルムの厚み、延伸倍率等に応じて変化し得る。具体的には、延伸温度は、Ｔｇ−３０℃〜Ｔｇ＋６０℃であることが好ましく、Ｔｇ−３０℃〜Ｔｇ＋５０℃であることがより好ましく、Ｔｇ−１５℃〜Ｔｇ＋３０℃であることがさらに好ましい。このような温度で延伸することにより、本発明において適切な特性を有する位相差層が得られ得る。なお、Ｔｇは、フィルムの構成材料のガラス転移温度である。 The stretching temperature of the film may vary depending on the in-plane retardation value and thickness desired for the retardation layer, the type of resin used, the thickness of the film used, the stretching ratio, and the like. Specifically, the stretching temperature is preferably Tg-30 ° C to Tg + 60 ° C, more preferably Tg-30 ° C to Tg + 50 ° C, and further preferably Tg-15 ° C to Tg + 30 ° C. By stretching at such a temperature, a retardation layer having suitable properties in the present invention can be obtained. Note that Tg is the glass transition temperature of the constituent material of the film.
Ｄ．導電層
導電層は、任意の適切な成膜方法（例えば、真空蒸着法、スパッタリング法、ＣＶＤ法、イオンプレーティング法、スプレー法等）により、任意の適切な基材上に、金属酸化物膜を成膜して形成され得る。成膜後、必要に応じて加熱処理（例えば、１００℃〜２００℃）を行ってもよい。加熱処理を行うことにより、非晶質膜が結晶化し得る。金属酸化物としては、例えば、酸化インジウム、酸化スズ、酸化亜鉛、インジウム−スズ複合酸化物、スズ−アンチモン複合酸化物、亜鉛−アルミニウム複合酸化物、インジウム−亜鉛複合酸化物が挙げられる。インジウム酸化物には２価金属イオンまたは４価金属イオンがドープされていてもよい。好ましくはインジウム系複合酸化物であり、より好ましくはインジウム−スズ複合酸化物（ＩＴＯ）である。インジウム系複合酸化物は、可視光領域（３８０ｎｍ〜７８０ｎｍ）で高い透過率（例えば、８０％以上）を有し、かつ、単位面積当たりの表面抵抗値が低いという特徴を有している。
D. Conductive Layer The conductive layer is a metal oxide film formed on any appropriate base material by any appropriate film formation method (eg, vacuum deposition method, sputtering method, CVD method, ion plating method, spray method, etc.). Can be formed into a film. After film formation, heat treatment (for example, 100 ° C. to 200 ° C.) may be performed if necessary. By performing heat treatment, the amorphous film can be crystallized. Examples of the metal oxide include indium oxide, tin oxide, zinc oxide, indium-tin composite oxide, tin-antimony composite oxide, zinc-aluminum composite oxide, and indium-zinc composite oxide. The indium oxide may be doped with divalent metal ions or tetravalent metal ions. An indium-based composite oxide is preferred, and an indium-tin composite oxide (ITO) is more preferred. The indium-based composite oxide has a feature that it has a high transmittance (for example, 80% or more) in the visible light region (380 nm to 780 nm) and has a low surface resistance value per unit area.
導電層が金属酸化物を含む場合、該導電層の厚みは、好ましくは５０ｎｍ以下であり、より好ましくは３５ｎｍ以下である。導電層の厚みの下限は、好ましくは１０ｎｍである。 When the conductive layer contains a metal oxide, the thickness of the conductive layer is preferably 50 nm or less, more preferably 35 nm or less. The lower limit of the thickness of the conductive layer is preferably 10 nm.
導電層の表面抵抗値は、好ましくは３００Ω／□以下であり、より好ましくは１５０Ω／□以下であり、さらに好ましくは１００Ω／□以下である。 The surface resistance value of the conductive layer is preferably 300Ω / □ or less, more preferably 150Ω / □ or less, and further preferably 100Ω / □ or less.
導電層は、必要に応じてパターン化され得る。パターン化によって、導通部と絶縁部とが形成され得る。パターニング方法としては、任意の適切な方法を採用し得る。パターニング方法の具体例としては、ウエットエッチング法、スクリーン印刷法が挙げられる。 The conductive layer can be patterned if desired. By patterning, conductive parts and insulating parts can be formed. Any appropriate method can be adopted as the patterning method. Specific examples of the patterning method include a wet etching method and a screen printing method.
Ｅ．基材
基材は、遅相軸を有する。本発明においては、遅相軸を有する基材、すなわち、異方性基材を用いても、円偏光板の反射防止機能が十分に発揮されて、外光反射や背景の映り込み等を有効に防止し得る光学積層体を提供することができる。したがって、本発明によれば、従来のように光学的な等方性を重視して基材を構成する材料を選択する必要がなく、所望の特性に応じて多様な材料を選択することができる。
E. Base material
The substrate has a slow axis. In the present invention, even if a substrate having a slow axis, that is, an anisotropic substrate is used, the antireflection function of the circularly polarizing plate is sufficiently exerted to effectively prevent the reflection of external light and the reflection of the background. It is possible to provide an optical laminate that can be obtained. Therefore, according to the present invention, it is not necessary to select a material that constitutes the base material by placing importance on optical isotropy as in the conventional case, and various materials can be selected according to desired characteristics. ..
また、上記基材は、光学的に等方性（面内位相差Ｒｅ（５５０）が０ｎｍ）であることをターゲットにして作製されながらも、不可避に遅相軸を有する基材であってもよい。基材上に導電層を成膜して形成する場合（すなわち、密着積層により基材と導電層が積層している場合）、成膜工程での加熱等により、基材に不要な遅相軸が生じる場合がある。このようにして生じた遅相軸は、円偏光板による反射防止機能を阻害する上、通常、その方向が制御しがたく、生産安定性低下の原因ともなる。本発明においては、上記遅相軸が生じた基材であっても、円偏光板の反射防止機能が十分に発揮される。このような本発明においては、遅相軸の発生を許容して、導電層を形成することができ、導電層成膜条件の制約を少なくすることができる。 Further, the above-mentioned base material may be a base material which is inevitably slow-axis although it is produced by targeting that it is optically isotropic (in-plane retardation Re (550) is 0 nm). Good. When the conductive layer is formed on the base material (that is, when the base material and the conductive layer are laminated by adhesion lamination), the slow axis that is unnecessary for the base material due to heating in the film formation process. May occur. The slow axis generated in this way impairs the antireflection function of the circularly polarizing plate, and its direction is usually difficult to control, which causes a decrease in production stability. In the present invention, the antireflection function of the circularly polarizing plate is sufficiently exerted even with the substrate having the slow axis. In the present invention as described above, it is possible to allow the generation of the slow axis to form the conductive layer, and it is possible to reduce restrictions on the conditions for forming the conductive layer.
上記効果は、基材の遅相軸と位相差層の遅相軸との角度を最適化することにより得られる。本発明は、基材の遅相軸がいかなる方向に生じても、円偏光板の反射防止機能が十分に発揮される点で特に有用である。 The above effect can be obtained by optimizing the angle between the slow axis of the base material and the slow axis of the retardation layer. The present invention is particularly useful in that the antireflection function of the circularly polarizing plate can be sufficiently exerted regardless of the direction of the slow axis of the substrate.
基材の遅相軸と位相差層の遅相軸とのなす角度は、−４０°〜−５０°または４０°〜５０°であり、好ましくは−４２°〜−４８°または４２°〜４８°であり、より好ましくは−４４°〜−４６°または４４°〜４６°であり、特に好ましくは−４５°または４５°である。このような範囲であれば、円偏光板の反射防止機能が十分に発揮されて、外光反射や背景の映り込み等を有効に防止し得る光学積層体を提供することができる。なお、本明細書において、基材の遅相軸を基準にして時計回り方向の角度を正の角度とし、反時計回り方向の角度を負の角度とする。 The angle formed by the slow axis of the base material and the slow axis of the retardation layer is −40 ° to −50 ° or 40 ° to 50 °, preferably −42 ° to −48 ° or 42 ° to 48. °, more preferably −44 ° to −46 ° or 44 ° to 46 °, and particularly preferably −45 ° or 45 °. Within such a range, it is possible to provide an optical laminate in which the antireflection function of the circularly polarizing plate is sufficiently exerted and external light reflection, background reflection, etc. can be effectively prevented. In this specification, a clockwise angle is a positive angle and a counterclockwise angle is a negative angle with reference to the slow axis of the substrate.
基材は、好ましくは屈折率特性がｎｘ＞ｎｙ≧ｎｚの関係を示す。基材の面内位相差Ｒｅ（５５０）は、０ｎｍより大きい。本発明によれば、面内位相差Ｒｅを有する基材を用いても、上記のように、円偏光板の反射防止機能が十分に発揮される光学積層体を得ることができる。１つの実施形態においては、基材の面内位相差Ｒｅ（５５０）は、３ｎｍ以上である。別の実施形態においては、基材の面内位相差Ｒｅ（５５０）は、５ｎｍ以上である。基材の面内位相差Ｒｅ（５５０）の上限は、例えば、１０ｎｍである。基材の面内位相差Ｒｅ（５５０）が１０ｎｍ以下（より好ましくは８ｎｍ以下、さらに好ましくは６ｎｍ以下）であれば、円偏光板の反射防止機能はより高くなる。 The substrate preferably has a refractive index characteristic of nx> ny ≧ nz. The in-plane retardation Re (550) of the substrate is larger than 0 nm. According to the present invention, even if a substrate having an in-plane retardation Re is used, it is possible to obtain an optical laminate in which the antireflection function of the circularly polarizing plate is sufficiently exerted as described above. In one embodiment, the in-plane retardation Re (550) of the substrate is 3 nm or more. In another embodiment, the in-plane retardation Re (550) of the substrate is 5 nm or more. The upper limit of the in-plane retardation Re (550) of the substrate is, for example, 10 nm. When the in-plane retardation Re (550) of the substrate is 10 nm or less (more preferably 8 nm or less, further preferably 6 nm or less), the antireflection function of the circularly polarizing plate will be higher.
基材としては、任意の適切な樹脂フィルムが用いられ得る。構成材料の具体例としては、環状オレフィン系樹脂、ポリカーボネート系樹脂、セルロース系樹脂、ポリエステル系樹脂、アクリル系樹脂が挙げられる。 Any appropriate resin film can be used as the substrate. Specific examples of the constituent material include a cyclic olefin resin, a polycarbonate resin, a cellulose resin, a polyester resin, and an acrylic resin.
基材の厚みは、好ましくは１０μｍ〜２００μｍであり、より好ましくは２０μｍ〜６０μｍである。 The thickness of the base material is preferably 10 μm to 200 μm, more preferably 20 μm to 60 μm.
必要に応じて、導電層２１と基材２２との間に、ハードコート層（図示せず）が設けられてもよい。ハードコート層としては、任意の適切な構成を有するハードコート層が用いられ得る。ハードコート層の厚みは、例えば０．５μｍ〜２μｍである。ヘイズが許容範囲であれば、ハードコート層にニュートンリング低減のための微粒子を添加してもよい。さらに、必要に応じて、導電層２１と基材２２（存在する場合にはハードコート層）との間に、導電層の密着性を高めるためのアンカーコート層、および／または、反射率を調整するための屈折率調整層が設けられてもよい。アンカーコート層および屈折率調整層としては、任意の適切な構成が採用され得る。アンカーコート層および屈折率調整層は数ｎｍ〜数十ｎｍの薄層であり得る。 A hard coat layer (not shown) may be provided between the conductive layer 21 and the base material 22 as needed. As the hard coat layer, a hard coat layer having any appropriate configuration can be used. The thickness of the hard coat layer is, for example, 0.5 μm to 2 μm. If the haze is within the allowable range, fine particles for reducing Newton's rings may be added to the hard coat layer. Further, if necessary, an anchor coat layer for enhancing adhesion of the conductive layer and / or a reflectance is adjusted between the conductive layer 21 and the base material 22 (hard coat layer if present). A refractive index adjusting layer for controlling may be provided. Any appropriate configuration can be adopted as the anchor coat layer and the refractive index adjusting layer. The anchor coat layer and the refractive index adjusting layer may be thin layers of several nm to several tens of nm.
必要に応じて、基材２２の導電層２１と反対側（光学積層体の最外側）に、別のハードコート層が設けられてもよい。当該ハードコート層は、代表的には、バインダー樹脂層と球状粒子とを含み、球状粒子がバインダー樹脂層から突出して凸部を形成している。このようなハードコート層の詳細は、特開２０１３−１４５５４７号公報に記載されており、当該公報の記載は本明細書に参考として援用される。 If necessary, another hard coat layer may be provided on the side of the base material 22 opposite to the conductive layer 21 (outermost side of the optical layered body). The hard coat layer typically includes a binder resin layer and spherical particles, and the spherical particles project from the binder resin layer to form convex portions. Details of such a hard coat layer are described in JP2013-145547A, and the description of the publication is incorporated herein by reference.
Ｆ．その他
本発明の実施形態による光学積層体は、その他の層をさらに含んでいてもよい。実用的には、基材２２の表面には、表示セルに貼り合わせるための粘着剤層（図示せず）が設けられている。当該粘着剤層の表面には、光学積層体が使用に供されるまで、剥離フィルムが貼り合わされていることが好ましい。
F. Others The optical layered body according to the embodiment of the present invention may further include other layers. Practically, the surface of the base material 22 is provided with a pressure-sensitive adhesive layer (not shown) for sticking to the display cell. A release film is preferably attached to the surface of the pressure-sensitive adhesive layer until the optical laminate is used.
Ｇ．画像表示装置
上記Ａ項からＦ項に記載の光学積層体は、画像表示装置に適用され得る。したがって、本発明は、そのような光学積層体を用いた画像表示装置を包含する。画像表示装置の代表例としては、液晶表示装置、有機ＥＬ表示装置が挙げられる。本発明の実施形態による画像表示装置は、その視認側に上記Ａ項からＧ項に記載の光学積層体を備える。光学積層体は、導電層が表示セル（例えば、液晶セル、有機ＥＬセル）側となるように（偏光子が視認側となるように）積層されている。すなわち、本発明の実施形態による画像表示装置は、表示セル（例えば、液晶セル、有機ＥＬセル）と偏光板との間にタッチセンサーが組み込まれた、いわゆるインナータッチパネル型入力表示装置であり得る。この場合、タッチセンサーは、導電層（または基材付導電層）と表示セルとの間に配置され得る。タッチセンサーの構成については業界で周知の構成が採用され得るので、詳細な説明は省略する。
G. Image Display Device The optical layered body described in the above items A to F can be applied to an image display device. Therefore, the present invention includes an image display device using such an optical laminate. Typical examples of the image display device include a liquid crystal display device and an organic EL display device. The image display device according to the embodiment of the present invention includes the optical layered body described in the above items A to G on the viewing side. The optical laminate is laminated so that the conductive layer is on the display cell (for example, liquid crystal cell or organic EL cell) side (the polarizer is on the viewing side). That is, the image display device according to the embodiment of the present invention may be a so-called inner touch panel type input display device in which a touch sensor is incorporated between a display cell (for example, a liquid crystal cell or an organic EL cell) and a polarizing plate. In this case, the touch sensor may be arranged between the conductive layer (or the conductive layer with the base material) and the display cell. As the configuration of the touch sensor, a configuration well known in the industry can be adopted, and thus detailed description thereof will be omitted.
以下、実施例によって本発明を具体的に説明するが、本発明はこれら実施例によって限定されるものではない。 Hereinafter, the present invention will be specifically described with reference to examples, but the present invention is not limited to these examples.
［実施例１］
下記表１に示す構成の光学積層体について、光学シミュレーター（Ｓｈｉｎｔｅｃ社製、商品名「ＬＣＤ Ｍａｓｔｅｒ Ｖ８」）を用い、正面色相ａ、ｂから、該光学積層体の反射特性を評価した。
なお、偏光板の位相差層とは反対側に、光源（「ＬＣＤ Ｍａｓｔｅｒ Ｖ８」に登録されているＤ６５光源）を配置し、基材の位相差層とは反対側に、反射板（「ＬＣＤ Ｍａｓｔｅｒ Ｖ８」に登録されている理想反射板Ｉｄｅａ−Ｒｅｆｌｅｃｔｏｒ）を配置する構成とした。
また、基材を含まないこと以外は表１と同様の構成にて、正面色相ａ、ｂを出し、その結果をリファレンスとした。
本評価は、後述のように基材の遅相軸角度を変えてシミュレーションを行い、リファレンスとの比較により、光学積層体の反射特性を評価するものである。
[Example 1]
With respect to the optical laminate having the configuration shown in Table 1 below, the reflection characteristics of the optical laminate were evaluated from the front hues a and b using an optical simulator (trade name “LCD Master V8” manufactured by Shintec).
A light source (D65 light source registered in “LCD Master V8”) is arranged on the side opposite to the retardation layer of the polarizing plate, and a reflection plate (“LCD An ideal reflector Idea-Reflector registered in "Master V8" is arranged.
Further, the front hues a and b were obtained in the same configuration as in Table 1 except that the base material was not included, and the results were used as a reference.
In this evaluation, the slow axis angle of the base material is changed to perform a simulation as described later, and the reflection characteristics of the optical laminate are evaluated by comparison with a reference.
［実施例１−１］
基材の遅相軸と偏光板の偏光子の吸収軸とのなす角度を９０°とした。すなわち、基材の遅相軸と位相差層の遅相軸とのなす角度を４５°とした。
[Example 1-1]
The angle formed by the slow axis of the substrate and the absorption axis of the polarizer of the polarizing plate was 90 °. That is, the angle formed by the slow axis of the substrate and the slow axis of the retardation layer was 45 °.
［実施例１−２］
基材の遅相軸と偏光板の偏光子の吸収軸とのなす角度を０°とした。すなわち、基材の遅相軸と位相差層の遅相軸とのなす角度を−４５°とした。
[Example 1-2]
The angle formed by the slow axis of the substrate and the absorption axis of the polarizer of the polarizing plate was set to 0 °. That is, the angle formed by the slow axis of the base material and the slow axis of the retardation layer was set to -45 °.
［実施例１−３］
基材の遅相軸と偏光板の偏光子の吸収軸とのなす角度を８５°とした。すなわち、基材の遅相軸と位相差層の遅相軸とのなす角度を４０°とした。
[Example 1-3]
The angle formed by the slow axis of the base material and the absorption axis of the polarizer of the polarizing plate was set to 85 °. That is, the angle formed by the slow axis of the base material and the slow axis of the retardation layer was set to 40 °.
［実施例１−４］
基材の遅相軸と偏光板の偏光子の吸収軸とのなす角度を９５°とした。すなわち、基材の遅相軸と位相差層の遅相軸とのなす角度を５０°とした。
[Example 1-4]
The angle formed by the slow axis of the base material and the absorption axis of the polarizer of the polarizing plate was set to 95 °. That is, the angle formed by the slow axis of the base material and the slow axis of the retardation layer was set to 50 °.
［実施例１−５］
基材の遅相軸と偏光板の偏光子の吸収軸とのなす角度を−５°とした。すなわち、基材の遅相軸と位相差層の遅相軸とのなす角度を−５０°とした。
[Example 1-5]
The angle formed by the slow axis of the base material and the absorption axis of the polarizer of the polarizing plate was set to -5 °. That is, the angle formed by the slow axis of the base material and the slow axis of the retardation layer was set to −50 °.
［実施例１−６］
基材の遅相軸と偏光板の偏光子の吸収軸とのなす角度を５°とした。すなわち、基材の遅相軸と位相差層の遅相軸とのなす角度を−４０°とした。
[Example 1-6]
The angle formed by the slow axis of the substrate and the absorption axis of the polarizer of the polarizing plate was set to 5 °. That is, the angle formed by the slow axis of the base material and the slow axis of the retardation layer was set to -40 °.
［比較例１］
基材の遅相軸と偏光板の偏光子の吸収軸とのなす角度を、１０°〜８０°および１００°〜１７０°の範囲内で変更し、各角度における、反射特性を評価した。
[Comparative Example 1]
The angle formed by the slow axis of the base material and the absorption axis of the polarizer of the polarizing plate was changed within the range of 10 ° to 80 ° and 100 ° to 170 °, and the reflection characteristics at each angle were evaluated.
実施例１および比較例１の結果について、正面色相ａ，ｂのプロットを図２示す。また、Δａｂの軸角度依存性を示すグラフ図を図３に示す。Δａｂは、Δａｂ＝｛（正面色相ａ−リファレンスの正面色相ａ）２＋（正面色相ｂ−リファレンスの正面色相ｂ）２｝１／２により算出される。Δａｂが、低いほど、等方性基材の影響が少なく、反射防止特性に優れることを示す。 FIG. 2 is a plot of front hues a and b for the results of Example 1 and Comparative Example 1. 3 is a graph showing the dependence of Δab on the axis angle. Δab is calculated by Δab = {(front hue a-reference front hue a) 2 + (front hue b-reference front hue b) 2 } 1/2 . The lower Δab, the less the influence of the isotropic base material and the better the antireflection property.
図２および図３から明らかなように、本発明の光学積層体は、優れた反射防止機能を有する。 As is clear from FIGS. 2 and 3, the optical layered body of the present invention has an excellent antireflection function.
［実施例２］
位相差層のＲｅ（５５０）を１３９ｎｍとし、位相差層の波長分散特性Ｒｅ（５５０）／Ｒｅ（４５０）を０．８５とし、波長分散特性Ｒｅ（６５０）／Ｒｅ（５５０）を１．０６としたこと以外は、実施例１（実施例１−１〜１−６）と同様にして、光学積層体の反射特性を評価した。
[Example 2]
Re (550) of the retardation layer is 139 nm, wavelength dispersion characteristic Re (550) / Re (450) of the retardation layer is 0.85, and wavelength dispersion characteristic Re (650) / Re (550) is 1.06. The reflection characteristics of the optical laminate were evaluated in the same manner as in Example 1 (Examples 1-1 to 1-6) except that the above was used.
［比較例２］
位相差層のＲｅ（５５０）を１３９ｎｍとし、位相差層の波長分散特性Ｒｅ（５５０）／Ｒｅ（４５０）を０．８５とし、波長分散特性Ｒｅ（６５０）／Ｒｅ（５５０）を１．０６としたこと以外は、比較例２と同様にして、光学積層体の反射特性を評価した。
[Comparative example 2]
Re (550) of the retardation layer is 139 nm, wavelength dispersion characteristic Re (550) / Re (450) of the retardation layer is 0.85, and wavelength dispersion characteristic Re (650) / Re (550) is 1.06. The reflection characteristics of the optical layered body were evaluated in the same manner as in Comparative Example 2 except for the above.
実施例２および比較例２の結果について、Δａｂの軸角度依存性を示すグラフ図を図４に示す。 With respect to the results of Example 2 and Comparative Example 2, a graph showing the axial angle dependence of Δab is shown in FIG.
［実施例３］
位相差層の波長分散特性Ｒｅ（５５０）／Ｒｅ（４５０）を０．８２とし、波長分散特性Ｒｅ（６５０）／Ｒｅ（５５０）を１．０８としたこと以外は、実施例１（実施例１−１〜１−６）と同様にして、光学積層体の反射特性を評価した。
[Example 3]
Example 1 (Examples) except that the wavelength dispersion characteristic Re (550) / Re (450) of the retardation layer was 0.82 and the wavelength dispersion characteristic Re (650) / Re (550) was 1.08. The reflection characteristics of the optical laminate were evaluated in the same manner as in 1-1 to 1-6).
［比較例３］
位相差層の波長分散特性Ｒｅ（５５０）／Ｒｅ（４５０）を０．８２とし、波長分散特性Ｒｅ（６５０）／Ｒｅ（５５０）を１．０８としたこと以外は、比較例２と同様にして、光学積層体の反射特性を評価した。
[Comparative Example 3]
Same as Comparative Example 2 except that the wavelength dispersion characteristic Re (550) / Re (450) of the retardation layer was 0.82 and the wavelength dispersion characteristic Re (650) / Re (550) was 1.08. Then, the reflection characteristics of the optical laminate were evaluated.
実施例３および比較例３の結果について、Δａｂの軸角度依存性を示すグラフ図を図５に示す。 With respect to the results of Example 3 and Comparative Example 3, a graph showing the axial angle dependence of Δab is shown in FIG.
本発明の光学積層体は、液晶表示装置および有機ＥＬ表示装置のような画像表示装置に好適に用いられ、特に有機ＥＬ表示装置の反射防止フィルムとして好適に用いられ得る。さらに、本発明の光学積層体は、インナータッチパネル型入力表示装置に好適に用いられ得る。 The optical layered body of the present invention is suitably used for an image display device such as a liquid crystal display device and an organic EL display device, and particularly preferably used as an antireflection film for an organic EL display device. Furthermore, the optical layered body of the present invention can be suitably used for an inner touch panel type input display device.
１ 偏光子
２ 第１の保護層
３ 第２の保護層
１１ 偏光板
１２ 位相差層
２１ 導電層
２２ 基材
１００ 光学積層体
DESCRIPTION OF SYMBOLS 1 Polarizer 2 1st protective layer 3 2nd protective layer 11 Polarizing plate 12 Retardation layer 21 Conductive layer 22 Base material 100 Optical laminated body
Claims (6)
該位相差層が、λ／４板であり、
該基材の面内位相差Ｒｅ（５５０）が０ｎｍより大きく１０ｎｍ以下であり、
該基材の遅相軸と該位相差層の遅相軸とのなす角度が、−４０°〜−５０°または４０°〜５０°である、
光学積層体。 A polarizing plate including a polarizer and a protective layer disposed on at least one side of the polarizer, a retardation layer, a conductive layer, and a base material in this order,
The retardation layer is a λ / 4 plate,
The in-plane retardation Re (550) of the substrate is more than 0 nm and 10 nm or less ,
The angle formed by the slow axis of the base material and the slow axis of the retardation layer is −40 ° to −50 ° or 40 ° to 50 °,
Optical stack.
An image display device comprising the optical laminate according to claim 1.