JP6662299B2 - 光学フィルタ及びこれを用いた装置 - Google Patents
光学フィルタ及びこれを用いた装置 Download PDFInfo
- Publication number
- JP6662299B2 JP6662299B2 JP2016564878A JP2016564878A JP6662299B2 JP 6662299 B2 JP6662299 B2 JP 6662299B2 JP 2016564878 A JP2016564878 A JP 2016564878A JP 2016564878 A JP2016564878 A JP 2016564878A JP 6662299 B2 JP6662299 B2 JP 6662299B2
- Authority
- JP
- Japan
- Prior art keywords
- optical filter
- transmittance
- filter according
- wavelength
- dye
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
しかし、この光学フィルタも、波長700nmの光の透過率が4〜7%程度であり、可視光に対する遮断性が不十分であり、高い感度の光センサは得られない。
(i)波長400〜730nmの光の平均透過率が2%以下である。
(ii)波長800〜1000nmの間に、平均透過率が80%以上となる連続する50nmの波長域を有する。
また、本発明の他の態様に係る装置は、上記光学フィルタを備えたことを特徴とする。
図1は、本発明の第1の実施形態による光学フィルタの構成を概略的に示す断面図である。本実施形態の光学フィルタは、可視光を遮断し、赤外光を選択的に透過させることが要求される用途、例えば、赤外線カメラ等の撮像装置、赤外線センサ、携帯電話やPC等に搭載される赤外線通信装置、テレビ、オーディオ、エアコン等の家電製品の赤外線リモコン装置、赤外光を用いた静脈認証や虹彩認証等の生体認証装置、モーションセンサ、3次元距離画像カメラ等の用途に有用な光学フィルタである。
ここで、「構造体1の一方の主面に、赤外光透過性基材2等の他の層を備える(または有する)」とは、構造体1に接触して他の層が備わる場合に限らず、構造体1と他の層との間に、他の機能層が備わっている場合も含むものと解釈し、以下の構成も同様である。
図3は、構造体1の両主面に赤外光透過性基材2を備える構成例である。
図4は、図3の光学フィルタにおいて、一方の赤外光透過性基材2を、接着剤層3を介して構造体1の一主面に備える構成例である。なお、図4の光学フィルタには不図示であるが、構造体1の両主面に接着剤層3を介して赤外光透過性基材2を備えてもよい。
図3及び図4に示す構成の光学フィルタにおいて、2つの赤外光透過性基材2を構成する材料や厚さ等は同一でも異なってもよい。
図5は、構造体1の一方の主面に機能層4を備える構成例である。
図6は、構造体1の両主面に機能層4を備える構成例である。2層の機能層4は同一でも異なってもよい。
図7は、構造体1の一方の主面に赤外光透過性基材2を備え、他方の主面に機能層4を備える構成例である。
構造体は、透明樹脂と、この透明樹脂中に分散または溶解された緑色色素、及び黒色色素を含む。
(i)波長400〜730nmの光の平均透過率が2%以下である。
平均透過率は、好ましくは1%以下、より好ましくは0.5%以下である。
(ii)波長800〜1000nmの間に、平均透過率が80%以上となる連続する50nmの波長域を有する。
該平均透過率は、好ましくは85%以上、より好ましくは90%以上である。
(iii)波長730〜860nmの間に、透過率が10%から80%に遷移する遷移波長域を有し、この遷移波長域における透過率の変化量が0.75%/nm以上である。
遷移波長域における透過率の変化量は、好ましくは1.00%/nm以上であり、より好ましくは1.25%nm以上であり、さらに好ましくは1.50%/nm以上、より一層好ましくは2.00%/nm以上である。なお、ここでいう「変化量」は、透過率が10%から80%に遷移するときの勾配(%/nm)の平均値に相当する。
上記遷移波長域における透過率の変化量は、次式で求められる値である。
D(%/nm)=[Tλ1(%)−Tλ2(%)]/[λ1(nm)−λ2(nm)]
(式中、Dは遷移波長域における透過率の変化量、λ1及びλ2はそれぞれ遷移波長域における長波長側端及び短波長側端の波長、Tλ1は分光透過率曲線の波長λ1における透過率であり、Tλ2は分光透過率曲線の波長λ2における透過率である)
すなわち、上記式において、Tλ1(%)=80(%)であり、Tλ2(%)=10%であるので、
D(%/nm)=70(%)/[λ1(nm)−λ2(nm)]
と表現できる。
(iv)波長400〜730nmの光の透過率が10%以下である。
透過率は、好ましくは5%以下、より好ましくは3%以下、さらに好ましくは1%以下、より一層好ましくは0.5%以下、特に好ましくは0.3%以下である。
(v)波長900〜1100nmの光の平均透過率が80%以上である。
平均透過率は、好ましくは85%以上、より好ましくは90%以上である。
(vi)波長900〜1100nmの光の透過率が80%以上である。
透過率は、好ましくは85%以上、より好ましくは90%以上である。
(vii)波長850〜950nmにおいて、入射光の光量に対する散乱光の光量の平均値(Save)が1%以下である。
該散乱光の光量の平均値(Save)は、好ましくは0.5%以下である。
ここで、上記の入射光の光量に対する散乱光の光量の平均値(Save)は、波長850〜950nmで発光する光源を用いて構造体に光を入射したときの入射光量をIin、全透過光量をIt、散乱光量をIdとしたとき、次式で求められる値である。
Save(%)=(散乱光透過率Td/全透過率Tt)×100
(式中、Td=(Id/Iin)×100
Tt=(It/Iin)×100)
緑色色素としては、例えば、スクアリリウム系色素、フタロシアニン系色素、シアニン系色素が挙げられる。これらの色素の中から、用途等に応じて1種以上を適宜選択して使用できる。緑色色素は、後述するように、透明樹脂中に分子が凝集して存在する顔料でもよいが、透明樹脂中に分子が溶解して存在する緑色染料が、散乱光発生の懸念が少ないことから好ましい。
スクアリリウム系色素は、透明樹脂中に分散して得られる樹脂膜を使用して測定される波長400〜1000nmの光の吸収スペクトルにおいて、波長600〜800nm内に吸収極大波長を有するものが好ましい。また、その吸収極大波長が発現する吸収ピークの赤外光側の傾きが急峻であることが好ましい。
このような吸収特性を有するスクアリリウム系色素を使用することにより、前述の要件に加えて、さらに下記要件も少なくとも1つを満たす構造体、さらには該構造体を含む光学フィルタが得られる。
・波長800〜900nmの光の平均透過率が80%である。該平均透過率は、好ましくは85%以上、より好ましくは90%以上である。
・波長730〜800nmの間に、透過率が10%から80%に遷移する遷移波長域を有し、前記遷移波長域の光の透過率の変化量が0.75%/nm以上である。該変化量は、好ましくは1.00%/nm以上であり、より好ましくは1.25%nm以上であり、さらに好ましくは1.50%/nm以上であり、より一層好ましくは2.00%/nm以上である。
・波長800〜900nmの光の透過率が80%以上である。該透過率は、好ましくは85%以上、より好ましくは90%以上である。
Xは、独立して1つ以上の水素原子が炭素数1〜12のアルキル基またはアルコキシ基で置換されていてもよい、式(1)または式(2)で示される2価の有機基である。
−(CH2)n1− …(1)
式(1)中n1は、2または3である。
−(CH2)n2−O−(CH2)n3− …(2)
式(2)中、n2とn3はそれぞれ独立して0〜2の整数であり、n2+n3は1または2である。
R1は、独立して飽和環構造を含んでもよく、分岐を有してもよい炭素数1〜12の飽和もしくは不飽和炭化水素基、炭素数3〜12の飽和環状炭化水素基、炭素数6〜12のアリール基または炭素数7〜13のアルアリール基を示す。
R2及びR3は、独立して水素原子、または、炭素数1〜10のアルキル基もしくはアルコキシ基を示す。
R4は、独立して1つ以上の水素原子が水酸基、カルボキシ基、スルホン基、またはシアノ基で置換されていてもよく、炭素原子間に不飽和結合、酸素原子、飽和もしくは不飽和の環構造を含んでよく、分岐を有してもよい炭素数1〜25の炭化水素基である。
また、アリール基は芳香族化合物が有する芳香環、例えば、ベンゼン環、ナフタレン環、ビフェニル、フラン環、チオフェン環、ピロール環等を構成する炭素原子を介して結合する基をいう。アルアリール基は、1以上のアリール基で置換された、飽和環構造を含んでもよい直鎖状もしくは分枝状の飽和もしくは不飽和炭化水素基または飽和環状炭化水素基をいう。
式(2)において、酸素原子の位置は、特に制限されない。すなわち、窒素原子と酸素原子が結合してもよく、ベンゼン環に酸素原子が直接結合してもよい。また、炭素原子に挟まれるように酸素原子が位置してもよい。
また、色素(A1)中、R2及びR3は、独立して、水素原子、または、炭素数1〜6のアルキル基もしくはアルコキシ基が好ましい。R2及びR3は、いずれも水素原子がより好ましい。
−CH3−mR13 m …(4)
ただし、式(4)中、mは1、2または3であり、R13は、それぞれ独立して、炭素原子間に不飽和結合、酸素原子、飽和もしくは不飽和の環構造を含んでもよい直鎖状または分枝状の炭化水素基(ただし、mが1のときは分枝状である。)を示し、かつm個のR13の炭素数の合計は4〜24である。透明樹脂への溶解性の観点から、mは2または3が好ましい。
フタロシアニン系色素は、透明樹脂中に分散して得られる樹脂膜を使用して測定される波長400〜1000nmの光の吸収スペクトルにおいて、波長700〜900nm内に吸収極大波長を有するものが好ましい。また、その吸収極大波長が発現する吸収ピークの赤外光側の傾きが急峻であることが好ましい。
このような吸収特性を有するフタロシアニン系色素を使用することにより、下記要件も少なくとも1つを満たす構造体、さらには該構造体を含む光学フィルタが得られる。
・波長860〜1000nmの光の平均透過率が80%以上である。該平均透過率は、好ましくは85%以上、より好ましくは90%以上である。
・波長760〜860nmの間に、透過率が10%から80%に遷移する遷移波長域を有し、前記遷移波長域の光の透過率の変化量が0.75%/nm以上である。該変化量は、好ましくは1.00%/nm以上であり、より好ましくは1.25%nm以上であり、さらに好ましくは1.50%/nm以上であり、より一層好ましくは2.00%/nm以上である。
・波長860〜1000nmの光の透過率が80%以上である。該透過率は、好ましくは85%以上、より好ましくは90%以上である。
また、式(B1)及び(B2)中、R5及びR6は、それぞれ独立して、1つ以上の水素原子が水酸基、カルボキシル基、フッ素原子、またはシアノ基で置換されていてもよく、炭素原子間に不飽和結合、酸素原子、飽和もしくは不飽和の環構造を含んでもよく、分岐を有してもよい炭素数1〜25の炭化水素基、あるいは式(B−a)、式(B−b)または式(B−c)で示される基である。
樹脂や溶媒に対する溶解性の観点から、R5及びR6は基(B−a)、(B−b)が好ましい。
シアニン系色素としては、式(C1)または(C2)で示されるシアニン系色素が特に好ましい。
R10及びR11は、それぞれ独立して水素原子、水酸基、カルボキシル基、メチル基、長鎖もしくは分岐アルキル基、アラルキル基、アミノ基、ニトロ基、長鎖アルキルアミン、アミド基またはイミド基を示す。式(C1)及び(C2)は、2置換の化合物を示しているが、3置換以上であってもよい。
Zは、ヨウ素原子、−NO3、−PF6または−N(SO2CF3)2を示す。
nは、1〜4の整数である。
黒色色素は、1種単独で黒色を呈する色素(狭義の黒色色素)のみならず、2種以上を混合して黒色を呈する混合物でもよい。混合物は、狭義の黒色色素と他の色の色素の混合物でもよい。なお、混合系黒色色素の場合、前述した緑色色素を除く。
黒色色素は、透明樹脂中に分子が凝集して存在する顔料でもよいが、透明樹脂中に分子が溶解して存在する黒色染料が、散乱光発生の懸念が少ないことから好ましい。
また、緑色色素と黒色色素の割合は、色素の種類等にもよるが、通常、質量基準で、黒色色素/緑色色素が1〜10となる範囲である。この混合比であれば、要件(i)及び(ii)を満たすことができる。
構造体を構成する透明樹脂は、ガラス転移温度(Tg)が、0〜380℃であることが好ましい。Tgの下限は、40℃以上がより好ましく、60℃以上がより一層好ましく、70℃以上がさらに好ましく、100℃以上が特に好ましい。また、Tgの上限は、370℃以下がより好ましく、360℃以下がより一層好ましい。透明樹脂のTgが0〜380℃の範囲であれば、本光学フィルタの製造プロセスや使用中において、熱による劣化や変形を抑制できる。
構造体には、緑色系色素及び黒色色素の他にさらに、本発明の効果を損なわない範囲で、この種の構造体が通常含有する各種任意成分を含有してもよい。任意成分としては、例えば、色調補正色素、レベリング剤、帯電防止剤、熱安定剤、光安定剤、酸化防止剤、分散剤、難燃剤、滑剤、可塑剤、透明ナノ粒子等が挙げられる。
シランカップリング剤としては、例えば、3−グリシドキシプロピルトリメトキシシラン、3−グリシドキシプロピルメチルジエトキシシラン、2−(3,4−エポキシシクロヘキシル)エチルトリメトキシシラン、3−(メタクリロプロピル)トリメトキシシラン、3−メルカプトプロピルトリメトキシシラン、3−メルカプトプロピルメチルジメトキシシラン、3−アミノプロピルトリエトキシシラン、3−ウレイドプロピルトリエトキシシラン、N−2−アミノエチル−3−アミノプロピルトリメトキシシラン、N−2−アミノエチル−3−アミノプロピルメチルジエトキシシラン、N−フェニル−3−アミノプロピルトリメトキシシラン、ビス(3−トリエトキシシリルプロピル)テトラスルファン、ビニルトリメトキシシラン等が挙げられる。
上記任意成分はいずれも1種を単独で使用してもよく、2種以上を混合して使用してもよい。
構造体は、例えば、緑色色素であるスクアリリウム系色素と、黒色色素と、透明樹脂または透明樹脂の原料成分と、必要に応じて配合される各成分とを、溶媒に溶解または分散させて塗工液を調製し、これを基材上に塗工し乾燥させ、さらに必要に応じて硬化させることにより形成できる。黒色色素として黒色染料を用いた場合には、黒色染料はスクアリリウム系色素とともに、透明樹脂及び塗工液に用いる溶媒の双方に溶解性が良好であるため、膜の均一性を確保でき、好ましい。
そのまま光学フィルタの構成部材となる基材としては、赤外光透過性基材が挙げられる。基材として構成部材となる基材を使用する場合、この基材には、構造体が形成される面にシランカップリング剤により予め表面処理を施して構造体と基材との密着性を高めてもよい。シランカップリング剤には、前述したシランカップリング剤を使用できる。
また、剥離性の基材は、剥離性を有するものであれば、形状、材料は特に限定されない。具体的には、ガラス板や、離型処理されたプラスチックフィルム、ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル樹脂、ポリエチレン、ポリプロピレン、エチレン酢酸ビニル共重合体等のポリオレフィン樹脂、ポリアクリレート、ポリメチルメタクリレート等のアクリル樹脂、ウレタン樹脂、塩化ビニル樹脂、フッ素樹脂、ポリカーボネート樹脂、ポリビニルブチラール樹脂、シクロオレフィン樹脂、ポリビニルアルコール樹脂等からなるフィルム、ステンレス鋼板等が使用できる。
まず、剥離性の基材上に、後述する塗工方法により構造体や必要に応じて機能層等を積層する。次に、後述する粘着層や市販の微粘着フィルム等を用いることにより、剥離性の基材から構造体を転写する。最後に、転写した構造体を別の部品に貼りつけることで、図1、図5、図6に示す光学フィルタが得られる。
このような方法で構造体を形成することで、本発明における光学フィルタは、赤外光透過性基材を含まず、薄型化を達成できる。この場合、光学フィルタの全体の厚さは、保護層等の機能層の有無に関わらず、50μm以下が好ましく、40μm以下がより好ましく、30μm以下がさらに好ましい。
塗工液の調製には、マグネチックスターラ、自転・公転式ミキサー、ビーズミル、遊星ミル、超音波ホモジナイザ等の攪拌装置を使用できる。撹拌は連続的に行ってもよく断続的に行ってもよい。
赤外光透過性基材は、赤外光を透過するものであれば、構成する材料は特に制限されず、ガラスや結晶等の無機材料や、樹脂等の有機材料が挙げられる。本光学フィルタは、特に赤外光に対する散乱光ができるだけ少ないことが求められることから、用いる基板についても散乱光の少ないものが好ましい。
強化ガラスはタッチパネル画面を保護する目的で、スマートフォンやタブレット端末のカバーガラスに用いられている。カバーガラスは、その外周部にはスクリーン印刷等で黒色や白色等の加飾印刷がなされている場合がある。その場合、予め加飾印刷が施される部分以外に開口部を設けておき、該開口部に上記塗工方法により塗工液を直接塗工できる。このように、塗工液を直接塗工することで、高い生産性が得られる。
機能層としては、反射防止層、パッシベーション機能を有する保護層、耐擦傷性を有する保護層、他の光学部品と接着させるための粘着層等のうち少なくとも1つを含む層が挙げられる。
反射防止層は、透過率を向上させ、効率良く入射光を利用する機能を有するもので、周知の材料及び方法により形成できる。具体的には、反射防止層は、スパッタリング法、真空蒸着法、プラズマCVD法等により形成したシリカ、チタニア、五酸化タンタル、フッ化マグネシウム、ジルコニア、アルミナ等の1層以上の膜や、ゾルゲル法、塗布法等により形成した1層以上の膜から構成される。ゾルゲル法を用いる材料としては、シリケート系材料が挙げられる。塗布法を用いる材料としては、シリコーン系樹脂、アクリル系樹脂、フッ素化アクリル系樹脂、シクロオレフィン樹脂、フッ素化シクロオレフィン樹脂等が挙げられる。また、シリカ微粒子や中空シリカ微粒子を加えることで、低屈折率化の実現や耐擦傷性を向上できる。なお、反射防止層の厚さは、通常、100〜2000nmである。
保護層は、無機膜または有機膜から構成される。保護層の厚さは、通常、0.2〜20μmである。
また、有機膜としては、ポリエチレンテレフタレート、ポリエチレンナフタレート等のポリエステル樹脂、ポリカーボネート樹脂、環状オレフィン樹脂等の熱可塑性樹脂、ポリイミド樹脂、ポリアミドイミド樹脂、ポリエーテルイミド樹脂等の熱硬化性樹脂、アクリル樹脂、エポキシ樹脂等のエネルギー線硬化性樹脂が挙げられる。熱硬化性樹脂及びエネルギー線硬化性樹脂を使用する場合、それらの重合性前駆体化合物を含む組成物を、例えば構造体の露出している主面に滴下し、その上に離型処理を施したガラス板を載せ、エネルギー線を照射する等して硬化させればよい。硬化後、ガラス板を離型すると、平滑で均一な厚さの有機膜を形成できる。平坦度は、好ましくは30nm以下であり、より好ましくは10nm以下である。高い平坦度を達成することで、ヘイズや収差を小さくできる。なお、ここでいう「平坦度」は、算術平均粗さRaのことを指す。有機膜からなる保護層には、前述した構造体に添加可能なその他の添加剤として挙げた成分を適宜添加できる。特に、赤外波長域で透明な無機酸化物材料のナノ粒子を用いることで、保護層の耐擦傷性を向上きる。
最表面粘着層の屈折率は、それを配置する面の材料の屈折率と略等しいことが好ましい。例えば、両者の屈折率差は好ましくは0.3以下、より好ましくは0.2以下である。2つの層の屈折率差を小さくすることで、界面反射を抑制でき、ノイズを低減できる。なお、ここでいう屈折率とは、波長589nmにおける屈折率をいう。
最表面粘着層としては液状接着剤も使用できる。液状接着剤としては、例えば、アクリル系、ウレタン系、エポキシ系、シリコーン系接着剤等が挙げられる。最表面粘着層が液状接着剤で構成される場合、光学フィルタを他の光学部品と接着した後、加熱、または紫外線等のエネルギー線を照射することにより、液状接着剤を硬化できる。
具体的には、波長400〜730nmの光の平均透過率が2%以下、波長800〜1000nmの間に、平均透過率が80%以上となる連続する50nmの波長域を有する分光透過率特性を具備できる。このように、平均透過率が80%以上となる連続する50nmの波長域を有することで、例えば、本実施形態の光学フィルタを用いて赤外波長域での送受信を行う場合において、一定の帯域で十分な感度を保つことができる。また、波長400〜730nmの光の透過率が10%以下、波長900〜1100nmの光の平均透過率が80%以上、あるいは波長900〜1100nmの光の透過率が80%以上という分光透過率特性を具備できる。
図8は、本発明の第2の実施形態による光学フィルタの構成を概略的に示す断面図である。本実施形態の光学フィルタは、可視光を遮断し、かつ所定波長以上の赤外光も遮断して、特定の波長域の赤外光のみを選択的に透過させることが要求される用途、例えば、赤外線レーザを用いて位置や距離等を測定する赤外線センサ等の用途に有用な光学フィルタである。本実施形態の説明にあたり、重複する説明を避けるため、第1の実施形態と共通する点については説明を省略し、相違点を中心に説明する。
本実施形態の光学フィルタは、赤外光透過性基材2を構造体1の両主面に有してもよく、赤外光透過性基材2及び赤外光反射層5を構造体1の両主面に有してもよい。
図10は、構造体1の一方の主面に赤外光透過性基材2及び赤外光反射層5を備え、他方の主面に赤外光透過性基材2及び機能層4を備える構成例である。
図11及び図12は、図9の光学フィルタにおいて、2つの赤外光透過性基材2のうちの一方を、接着剤層3を介して構造体1の一主面に備える構成例である。なお、図11、12の光学フィルタには不図示であるが、例えば、構造体1の両主面に接着剤層3を介して赤外光透過性基材2を備えてもよい。
図9〜12に示す構成の光学フィルタにおいて、2つの赤外光透過性基材2を構成する材料や厚さ等は同一でも異なってもよい。
赤外光反射層は、低屈折率の誘電体膜(低屈折率膜)と高屈折率の誘電体膜(高屈折率膜)とを交互に積層した誘電体多層膜から構成される。ここで、低屈折率と高屈折率とは、隣接する層の屈折率に対して低い屈折率と高い屈折率を有することを意味する。
高屈折率膜は、好ましくは、屈折率が1.6以上であり、より好ましくは2.2〜2.5である。高屈折率膜材料は、例えばTa2O5、TiO2、Nb2O5が挙げられる。このうち、成膜性、屈折率等における再現性、安定性等の点から、TiO2が好ましい。
一方、低屈折率膜は、好ましくは、屈折率1.6未満であり、より好ましくは1.35以上1.55未満であり、より一層好ましくは1.40〜1.50である。低屈折率膜材料は、例えばSiO2、SiOxNy等が挙げられる。成膜性における再現性、安定性、経済性等の点から、SiO2が好ましい。
具体的には、緑色色素としてスクアリリウム系色素(色素(A11−14))を用いた場合、波長400〜730nmの光の平均透過率が2%以下、波長800〜900nmの光の平均透過率が80%以上、波長900〜1100nmの間に透過率が5%以下に遷移する波長を有し、波長900nmより長波長側の透過率が、例えば1%以下という分光透過率特性を具備できる。また、波長400〜730nmの光の透過率が10%以下、あるいは波長800〜900nmの光の透過率が80%以上という分光透過率特性を具備できる。
このようなバンドパスフィルタは、例えば、波長800〜900nmの赤外光の透過感度を高め、かつ900nmよりも長波長側の光のノイズを遮断するように、特定の赤外光透過感度を高品質に高める光学フィルタとしての適用が期待できる。
図13は、本発明の第3の実施形態による撮像装置を概略的に示す断面図である。
本実施形態の撮像装置10は、固体撮像素子11と、本発明の光学フィルタ12と、撮像レンズ13と、これらを収容する筺体14とを有する。固体撮像素子11と、撮像レンズ13は、光軸xに沿って配置されている。固体撮像素子11は、撮像レンズ13を通過した光を電気信号に変換する、CCDやCMOS等が使用される。
また、光学フィルタ12は吸収波長に角度依存がないため広角でも可視光を十分に遮断できるため品質の良い画像となる。
さらに、光学フィルタ12が最表面粘着層を有する場合、光学フィルタ12は、最表面粘着層を介してカバーガラス等の他の光学部品に直接接着させて配置できる。光学フィルタ12が他の光学部品と直接接着できることで、光学フィルタ12が空気と接する界面を低減できるため、撮像装置全体の光利用効率を向上できる。
ポリエステル樹脂(大阪ガスケミカル(株)製 商品名「OKP850」)4.488g、黒色色素として、アゾ系色素(1)(C.I.ソルベントオレンジ7)0.473g、黒色色素として、アゾ系色素(2)(C.I.ソルベントブラック3)0.591g、緑色色素として、スクアリリウム系色素(色素(A11−14))0.213g、シランカップリング剤(信越化学工業(株)製 商品名「KBM403」)0.394g、紫外線吸収剤(BASFジャパン(株)製 商品名「TINUVIN(登録商標)405」)0.039g、光安定剤(BASFジャパン(株)製 商品名「TINUVIN(登録商標)123」)及び酸化防止剤((株)ADEKA製 商品名「アデカスタブ(登録商標) AO50」)0.016gをシクロヘキサノン8.5g及びN−メチル−2−ピロリドン8.5gの混合溶媒に溶解して溶液を調製した。
この溶液を、76mm×76mm×0.145mmのガラス(松波硝子工業(株)製 商品名「D263Teco」)板の一方の面にスピンコータ(ミカサ(株)製 スピンコータMS−A200)を用いて塗布し、150℃で1時間加熱して、厚さ3.5μmの構造体を形成し、光学フィルタを得た。
76mm×76mm×0.145mmのガラス(D263Teco)板の一方の面に、真空蒸着法により、SiO2層とTiO2層とを交互に積層して厚さ340nmの反射防止膜(7層)を形成した。
次いで、この反射防止膜を形成したガラス板の他方の面に、実施例1と同様にして厚さ3.5μmの構造体を形成し、光学フィルタを得た。
実施例1と同様にして、実施例2と同じガラス板の一方の面に厚さ3.5μmの構造体を形成した後、その構造体表面に、真空蒸着法により、SiO2層とTiO2層とを交互に積層して厚さ340nmのパッシベーション機能を併せ有する反射防止膜(7層)を形成し、光学フィルタを得た。
実施例1と同様にして、実施例2と同じガラス板の一方の面に厚さ3.5μmの構造体を形成した後、その構造体表面に、ジシクロペンタニルアクリレート6質量部、トリシクロデカンジメタノールジアクリレート4質量部及び光重合開始剤(1−ヒドロキシ−シクロヘキシルフェニルケトン)0.5質量部を混合して調製した紫外線硬化性アクリル樹脂組成物を滴下し、離型処理を施したガラス基材を被せた。この塗布層に100mW/cm2の照度で紫外線を照射して硬化させ、続いてガラスを離型し、厚さ2μmの保護層を形成し、光学フィルタを得た。
緑色色素として、スクアリリウム系色素に代えて、フタロシアニン系色素(山田化学工業(株)製 商品名「FDN−001」)0.66gを加えた以外は実施例1と同様に調製した溶液を用いて、実施例2と同じガラス板の一方の面に、実施例1と同様にして、厚さ4.0μmの構造体を形成し、光学フィルタを得た。
実施例2と同じガラス板の一方の面に、真空蒸着法により、SiO2層とTiO2層とを交互に積層して、厚さ約6μmの誘電体多層膜からなる赤外光反射層を形成した。図14に、光反射膜を形成したガラス板のシミュレーションによる分光透過率曲線(光入射角度0°)を示す。
次いで、上記赤外光反射層を形成したガラス板の他方の面に、実施例1と同様にして厚さ3.5μmの構造体を形成し、光学フィルタを得た。
実施例1で使用したガラス板の一方の面に、真空蒸着法により、SiO2層とTiO2層とを交互に積層して、厚さ約7μmの誘電体多層膜からなる赤外光反射層を形成した。図15は、赤外光反射層付きガラス板のシミュレーションによる分光透過率曲線(光入射角度0°)である。
次いで、上記赤外光反射層付きガラス板の他方の面に、実施例5と同様にして厚さ4.0μmの構造体を形成し、光学フィルタを得た。
スクアリリウム系色素(色素(A11−14))を未配合とした以外は実施例1と同様に調製した溶液を用いて、実施例2と同じガラス板の一方の面に、実施例1と同様にして、厚さ3.5μmの構造体を形成し、光学フィルタを得た。
緑色色素として、スクアリリウム系色素に代えて、フタロシアニン系色素(山田化学工業(株)製 商品名「FDR−005」)0.66gを加えた以外は実施例1と同様に調製した溶液を用いて、実施例1で使用したガラス板および構造体を備えた光学フィルタを得た。
緑色色素として、スクアリリウム系色素に代えて、シアニン系色素(Few chemicals社製 商品名「S0830」)0.66gを加えた以外は実施例1と同様に調製した溶液を用いて、実施例1で使用したガラス板および構造体を備えた光学フィルタを得た。
ポリエステル樹脂に代えて、ポリイミド樹脂(三菱ガス化学(株)製 商品名「C3450」)を用いた以外は実施例1と同様に調製した溶液を用いて、実施例1で使用したガラス板および構造体を備えた光学フィルタを得た。
ポリエステル樹脂に代えて、アクリル樹脂(ダイセルエボニック(株)製 商品名「TT50」)を用いた以外は実施例1と同様に調製した溶液を用いて、実施例1で使用したガラス板および構造体を備えた光学フィルタを得た。
ポリエステル樹脂(OKP850)4.488g、黒色色素として、アゾ系色素(1)(C.I.ソルベントオレンジ7)0.473g、黒色色素として、アゾ系色素(2)(C.I.ソルベントブラック3)0.591g、緑色色素として、スクアリリウム系色素(色素(A11−14))0.213g、シランカップリング剤(KBM403)0.394g、紫外線吸収剤(TINUVIN(登録商標)405)0.039g、光安定剤(TINUVIN(登録商標)123)及び酸化防止剤(アデカスタブ(登録商標)AO50」)0.016gをシクロペンタノン8.5g及びメチルエチルケトン8.5gの混合溶媒に溶解して溶液を調製した。
この溶液を、コロナ処理した250mm幅のポリイミドロールフィルム(三菱ガス化学(株)製 商品名「ネオプリム(登録商標)L―3450」;厚さ50μm)の一方の面にダイコーターを用いて塗布し、加熱乾燥させて、厚さ3.5μmの構造体を形成し、光学フィルタを得た。
赤外光透過性基材として、ポリイミドロールフィルムに代えて、シクロオレフィン系コポリマーフィルム(グンゼ(株)製 商品名「F1−EX」)を用いた以外は実施例11と同様にして光学フィルタを得た。
実施例12で得られた光学フィルタの構造体側外表面にコロナ処理を施した後、アクリロイルモルホリン(KJケミカルズ(株)製 商品名「ACMO(登録商標)」)60質量部、ジペンタエリスリトールヘキサアクリレート(日本化薬(株)製 商品名「KAYARAD(登録商標)−DPHA」)40質量部及び光重合開始剤2−メチル−1−[4−(メチルチオ)フェニル]−2−モルフォリノプロパン−1−オン(BASF社製 商品名「Irgacure(登録商標)907」)5質量部からなる組成物をダイコーターで塗布し、この塗布層に200mW/cm2の照度で紫外線を照射して硬化させ、厚さ3μmの保護層を形成し、光学フィルタを得た。
実施例14で得られた光学フィルタの赤外光透過性基材側外表面に実施例2と同様の反射防止膜を形成し、光学フィルタを得た。
本例は、赤外光透過性基材としてカバーガラスを用いた光学フィルタの例である。まず剥離性基材としてロールフィルム(日本ゼオン(株)製 商品名「ゼオノア(登録商標)ZF16」;厚さ100μm)を用意し、該基材の一方の面に実施例5と同様に調製した塗工液をダイコーターで塗布し、加熱乾燥させて、厚さ3.5μmの構造体を形成した。次に、該構造体の表面に、実施例14と同様の材料および製法で、厚さ3μmの保護層を形成した。次に、該保護層上に微粘着フィルム(日栄化工(株)製 商品名「PET75−H109(20)」を貼り合わせ、上記剥離性基材を剥離した。次に、剥離性基材が備えられていた側の構造体の表面に、OCAテープ(3M社製 商品名「3M(商標)OCAテープ8171CL」;厚さ25μm)を貼り合わせた。この後、強化ガラス(旭硝子社製 商品名「Dragontrail(登録商標)」;厚さ0.5mm)からなるカバーガラスに上記OCAテープを貼り合わせ、上記微粘着フィルムを剥離して、光学フィルタを得た。構造体、保護層、OCAテープの厚さの合計は、31.5μmであった。
本例は、周辺部に加飾印刷がなされたカバーガラス上に構造体を備える光学フィルタの例である。まず、直径2.5mmの円形状の開口部を有し、該開口部の周辺に、黒色顔料としてカーボンブラックを含む黒枠が印刷されたカバーガラスを用意し、その開口部に3−アミノプロピルトリエトキシシランによる表面処理を施した。次いで、表面処理した開口部に、実施例5と同様に調製した塗工液をキャストコーティングし、加熱乾燥させて、厚さ6.5μmの構造体を形成し、光学フィルタを得た。図16に本実施例で得られた光学フィルタを示す。図16において、1は構造体、21はカバーガラス、22は黒枠を示す。黒枠22に含まれるカーボンブラックは波長800〜1000nmの光を透過せず、構造体21は同波長域の光を透過するため、カバーガラス21上に波長800〜1000nmの光を透過する特定の領域を設けることができる。
これに対し、スクアリリウム系色素を用いなかった比較例では、透過率は、約670nmまでの波長域の光で約0%、約850nm以上の波長域の光で約90%以上、これらの間(約670〜約850nm)で緩やかに変化していた(比較例の、透過率が10%から80%に遷移する波長域(710〜779nm)での透過率の変位量Dは1.02%/nmであった)。このことから、波長730〜800nmの間で透過率を急峻に変化させるためには、スクアリリウム系色素が好ましく用いられることが示唆される。
なお、実施例12〜14、実施例15(0°)および実施例15(40°)における、透過率が10%から80%に遷移する波長域での透過率の変位量Dはそれぞれ、1.69%/nm、1.87%/nm、1.80%/nm、1.96%/nm、1.91%/nmであった。
Claims (27)
- 緑色色素、及び黒色色素を含有し、下記(i)及び(ii)の要件を満足する構造体を具備し、
前記構造体は、波長730〜860nmの間に、透過率が10%から80%に遷移する遷移波長域を有し、前記遷移波長域における透過率の変化量が0.75%/nm以上であることを特徴とする光学フィルタ。
(i)波長400〜730nmの光の平均透過率が2%以下である
(ii)波長800〜1000nmの間に、平均透過率が80%以上となる連続する50nmの波長域を有する - 前記構造体は、波長400〜730nmの光の透過率が10%以下である請求項1に記載の光学フィルタ。
- 前記構造体は透明樹脂を含み、該透明樹脂中に前記緑色色素及び黒色色素が分散または溶解している請求項1または2に記載の光学フィルタ。
- 前記緑色色素が、スクアリリウム系色素、フタロシアニン系色素、及びシアニン系色素から選ばれる少なくとも1種である請求項1〜3のいずれか1項に記載の光学フィルタ。
- 前記緑色色素がスクアリリウム系色素を含むとともに、前記構造体は波長800〜900nmの光の平均透過率が80%以上である請求項1〜4のいずれか1項に記載の光学フィルタ。
- 前記構造体は、波長730〜800nmの間に、透過率が10%から80%に遷移する遷移波長域を有し、前記遷移波長域における透過率の変化量が0.75%/nm以上である請求項5に記載の光学フィルタ。
- 前記構造体は、波長800〜900nmの光の透過率が80%以上である請求項5または6に記載の光学フィルタ。
- 前記スクアリリウム系色素は、式(A1)で表されるスクアリリウム系色素から選ばれる少なくとも1種である請求項4〜7のいずれか1項に記載の光学フィルタ。
Xは、独立して1つ以上の水素原子が炭素数1〜12のアルキル基またはアルコキシ基で置換されていてもよい、式(1)または式(2)で示される2価の有機基であり、
−(CH2)n1− …(1)
(式(1)中、n1は、2または3である。)
−(CH2)n2−O−(CH2)n3− …(2)
(式(2)中、n2とn3はそれぞれ独立して0〜2の整数であり、n2+n3は1または2である。)
R1は、独立して飽和環構造を含んでもよく、分岐を有してもよい炭素数1〜12の飽和もしくは不飽和炭化水素基、炭素数3〜12の飽和環状炭化水素基、炭素数6〜12のアリール基または炭素数7〜13のアルアリール基であり、
R2及びR3は、独立して水素原子、または、炭素数1〜10のアルキル基もしくはアルコキシ基であり、
R4は、独立して1つ以上の水素原子が水酸基、カルボキシ基、スルホ基、またはシアノ基で置換されていてもよく、炭素原子間に不飽和結合、酸素原子、飽和もしくは不飽和の環構造を含んでもよく、分岐を有してもよい炭素数1〜25の炭化水素基である。) - 前記スクアリリウム系色素は、透明樹脂中に分散して得られる樹脂膜を使用して測定される波長400〜1000nmの光の吸収スペクトルにおいて、波長600〜800nm内に吸収極大波長を有するスクアリリウム系色素である請求項4〜8のいずれか1項に記載の光学フィルタ。
- 前記緑色色素がフタロシアニン系色素を含むとともに、前記構造体は波長860〜1000nmの光の平均透過率が80%以上である請求項1〜4のいずれか1項に記載の光学フィルタ。
- 前記構造体は、波長760〜860nmの間に、透過率が10%から80%に遷移する遷移波長域を有し、前記遷移波長域における透過率の変化量が0.75%/nm以上である請求項10に記載の光学フィルタ。
- 前記構造体は、波長860〜1000nmにおける透過率が80%以上である請求項10または11に記載の光学フィルタ。
- 前記フタロシアニン系色素は、式(B1)または(B2)で表されるフタロシアニン系色素から選ばれる少なくとも1種である請求項10〜12のいずれか1項に記載の光学フィルタ。
Mは、2個の水素原子、2個の1価の金属原子、または3価もしくは4価の金属原子を含む置換金属原子であり、
R5及びR6は、それぞれ独立して、1つ以上の水素原子が水酸基、カルボキシル基、フッ素原子、またはシアノ基で置換されていてもよく、炭素原子間に不飽和結合、酸素原子、飽和もしくは不飽和の環構造を含んでもよく、分岐を有してもよい炭素数1〜25の炭化水素基、あるいは、式(B−a)、式(B−b)または式(B−c)で示される基である。
- 前記黒色色素は、アゾ系染料を含む請求項1〜13のいずれか1項に記載の光学フィルタ。
- 前記構造体の片側もしくは両側に赤外光透過性基材を備える請求項1〜14のいずれか1項に記載の光学フィルタ。
- 前記赤外光透過性基材は、開口部を有するカバーガラスを含む請求項15に記載の光学フィルタ。
- 前記構造体の片側もしくは両側に赤外光反射層を備え、
前記赤外光反射層は、入射角0°の分光透過率曲線において、波長800〜900nmの光の平均透過率が80%以上であり、波長900〜1100nmの間に透過率が5%以下となる波長を有する請求項1〜16のいずれか1項に記載の光学フィルタ。 - 前記構造体の片側もしくは両側に赤外光反射層を備え、
前記赤外光反射層は、入射角0°の分光透過率曲線において、波長900〜1000nmの光の平均透過率が80%以上であり、波長1000〜1100nmの間に透過率が5%以下となる波長を有する請求項1〜16のいずれか1項に記載の光学フィルタ。 - 前記構造体の片側もしくは両側に保護層を有する請求項1〜18のいずれか1項に記載の光学フィルタ。
- 前記保護層は、無機膜からなる請求項19に記載の光学フィルタ。
- 前記保護層は、有機膜からなる請求項19に記載の光学フィルタ。
- 外気と触れる最表面に、赤外光透過性を示す粘着層を有する請求項1〜21のいずれか1項に記載の光学フィルタ。
- 全体の厚さが50μm以下である請求項1〜22のいずれか1項に記載の光学フィルタ。
- 請求項1乃至23のいずれか1項に記載の光学フィルタを備えたことを特徴とする撮像装置。
- 請求項1乃至23のいずれか1項に記載の光学フィルタを備えたことを特徴とする赤外線センサ。
- 請求項1乃至23のいずれか1項に記載の光学フィルタを備えたことを特徴とする生体認証装置。
- 請求項1乃至23のいずれか1項に記載の光学フィルタを備えたことを特徴とする3次元距離画像カメラ。