JP6638277B2 - 樹脂組成物セット、樹脂シート、積層シート及び発泡壁紙、並びに樹脂シート及び発泡壁紙の製造方法 - Google Patents
樹脂組成物セット、樹脂シート、積層シート及び発泡壁紙、並びに樹脂シート及び発泡壁紙の製造方法 Download PDFInfo
- Publication number
- JP6638277B2 JP6638277B2 JP2015181973A JP2015181973A JP6638277B2 JP 6638277 B2 JP6638277 B2 JP 6638277B2 JP 2015181973 A JP2015181973 A JP 2015181973A JP 2015181973 A JP2015181973 A JP 2015181973A JP 6638277 B2 JP6638277 B2 JP 6638277B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- foaming agent
- resin composition
- sheet
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(i)1g/10分≦(A)≦10g/10分
(ii)1g/10分≦(B)≦16g/10分
(iii)−3g/10分≦(B)−(A)≦6g/10分
(i)1g/10分≦(A)≦10g/10分
(ii)1g/10分≦(B)≦16g/10分
(iii)−3g/10分≦(B)−(A)≦6g/10分
本実施形態に係る樹脂組成物セットは、第1の樹脂分と、充填剤と、発泡剤と、を含む発泡剤含有樹脂組成物と、第2の樹脂分を含み、発泡剤を含まない発泡剤非含有樹脂組成物と、を備える。
発泡剤含有樹脂組成物における第1の樹脂分は、ポリ塩化ビニル樹脂等のハロゲン系樹脂なども用いることができるが、燃焼時にダイオキシン等の有毒ガスの発生を防ぐ観点から、非ハロゲン系樹脂を含むことが好ましい。非ハロゲン系樹脂としては、例えば、エチレン単独重合体、エチレンと他のオレフィンとの共重合体、ポリオレフィン樹脂(ポリプロピレン、ポリブテン、ポリメチルペンテン等の単一オレフィン重合体、2種以上のオレフィンのランダム又はブロック共重合体など)、スチレン系樹脂(ポリスチレン、アクリロニトリル・スチレン共重合体(AS)、アクリロニトリル・ブタジエン・スチレン共重合体(ABS)等)、エチレンコポリマー(エチレン−酢酸ビニル共重合体、エチレン−メチルメタクリレート共重合体、エチレン−アクリル酸共重合体、エチレン−エチルアクリレート共重合体、エチレン−メチルアクリレート共重合体、エチレン−メタクリル酸共重合体等)などが挙げられる。これらは1種を単独で、又は2種以上を併用して用いることができる。
本実施形態に係る発泡剤非含有樹脂組成物は、第2の樹脂分を含み、発泡剤を含まない。
(i)1g/10分≦(A)≦10g/10分
(ii)1g/10分≦(B)≦16g/10分
(iii)−3g/10分≦(B)−(A)≦6g/10分
本実施形態に係る樹脂シートは、上述した樹脂組成物セットの発泡剤含有樹脂組成物及び発泡剤非含有樹脂組成物を共押出しすることにより得られるものであり、発泡剤含有樹脂組成物からなる第1層と、発泡剤非含有樹脂組成物からなる第2層との積層構造を含む。
本実施形態に係る積層シートは、基材と、基材上に設けられた上記樹脂シートと、を備える。当該積層シートは、樹脂シートを、基材上にラミネートして得ることができる。本発明の効果がより有効に得られる点から、積層シートは、樹脂シートにおける上記第1層を、基材上にラミネートして得られるものであることが好ましい。
本実施形態に係る発泡壁紙は、基材と、基材上に設けられた発泡樹脂層と、を備え、上記積層シートにおける第1層に含まれる発泡剤を発泡させることにより得ることができる。このような発泡壁紙は、基材上に、上述した本実施形態に係る樹脂シートの第1層側をラミネートして積層シートを得る積層シート形成工程と、積層シートにおける第1層に含まれる発泡剤を発泡させることにより発泡樹脂層を形成する発泡工程と、を備える、製造方法によって得ることができる。
同方向噛み合い型2軸押出機を用いて、発泡剤が分解しないように樹脂温度を130℃に制御しながら、表1の配合で発泡剤含有樹脂組成物のペレットを作製した。作製した発泡剤含有樹脂組成物のペレットをメルトインデクサー(株式会社東洋精機製作所製、G−01)を用いて、130℃、2.16kgf荷重におけるメルトマスフローレートを測定した。結果を表1に示す。
樹脂A:ペトロセン202(東ソー株式会社製、商品名、MFR=24(190℃)、密度=0.918g/cm3)
樹脂B:LJ902(日本ポリエチレン株式会社製、商品名、MFR=45(190℃)、密度=0.915g/cm3)
樹脂C:タフマー DF7350(三井化学株式会社製、商品名、MFR=35(190℃)、密度=0.870g/cm3)
樹脂D:リンクロン XCF710N(三菱化学株式会社製、商品名、低密度ポリエチレンベース、MFR=1.2(190℃)、密度=0.918g/cm3)
充填剤A:ソフトン1200(備北粉化工業株式会社製、商品名)
充填剤B:タイペークCR−60(石原産業株式会社製、商品名)
同方向噛み合い型2軸押出機を用いて、樹脂温度を130℃に制御しながら、表2の配合で発泡剤非含有樹脂組成物のペレットを作製した。作製した発泡剤非含有樹脂組成物のペレットをメルトインデクサー(東洋精機製作所製、G−01)を用いて、130℃、2.16kgf荷重におけるメルトマスフローレートを測定した。結果を表2に示す。
樹脂E:ニポロン−LM55(東ソー株式会社製、商品名)
樹脂F:ニポロン−LM65(東ソー株式会社製、商品名)
樹脂G:ニポロン−LM75(東ソー株式会社製、商品名)
(実施例1〜8、比較例1〜2)
上記で作製した発泡剤含有樹脂組成物1〜3及び発泡剤非含有樹脂組成物1〜5のペレットを、表3に示す組合せで用いて、樹脂シートを作製した。具体的には、スクリュー1(スクリュー径(D)65mm、L/D(スクリュー長をスクリュー径で除したもの)=28の単軸押出機)を用いて発泡剤含有樹脂組成物のペレットを押出し、スクリュー2(スクリュー径(D)50mm、L/D=28の単軸押出機)を用いて発泡剤非含有樹脂組成物のペレットを押出し、両者をフィードブロックタイプで合流させた後にTダイでシート製膜し、発泡剤含有樹脂組成物からなる第1層(厚さ75μm)と発泡剤非含有樹脂組成物からなる第2層(厚さ10μm)の2層からなる樹脂シートを得た。
作製した発泡壁紙について、下記の方法に従い、発泡倍率及び耐傷性を評価した。
発泡壁紙の厚みを厚み計で測定し、裏打紙の厚み(100μm)を差し引いて、発泡前の樹脂シートの厚み(85μm)で除した値を発泡倍率として算出した。結果を表3に示す。
コインスクラッチ試験機を用いて、耐傷性の評価を行った。具体的には、水平な面に発泡壁紙を置き、10円硬貨を用いて45°の角度で発泡壁紙を荷重100g、200g及び300gで引っ掻き、表面状態を観察した。以下の基準に基づき、耐傷性を評価した。A又はBであれば、耐傷性が十分なものと評価できる。結果を表3に示す。
A:試験体表面にキズなし。
B:表面にわずかにキズが残る。
C:発泡層にまでキズが入り込む。
Claims (14)
- 第1の樹脂分と、充填剤と、発泡剤と、を含む発泡剤含有樹脂組成物と、
第2の樹脂分を含み、発泡剤を含まない発泡剤非含有樹脂組成物と、を備え、
前記第1の樹脂分が、エチレン単独重合体又はエチレンと他のオレフィンとの共重合体を含み、
前記第2の樹脂分が、エチレン単独重合体又はエチレンと他のオレフィンとの共重合体を含み、
前記発泡剤含有樹脂組成物からなる第1層と前記発泡剤非含有樹脂組成物からなる第2層との積層構造を含む樹脂シートを形成するための樹脂組成物セットであって、
前記発泡剤含有樹脂組成物の130℃、2.16kgf荷重におけるメルトマスフローレート(A)及び前記発泡剤非含有樹脂組成物の130℃、2.16kgf荷重におけるメルトマスフローレート(B)が、以下の(i)、(ii)及び(iii)に示す条件を全て満たす、樹脂組成物セット。
(i)1g/10分≦(A)≦10g/10分
(ii)1g/10分≦(B)≦16g/10分
(iii)−3g/10分≦(B)−(A)≦6g/10分 - 前記第1の樹脂分が、低密度ポリエチレン及び超低密度ポリエチレンを含み、前記第2の樹脂分が、直鎖状低密度ポリエチレンを含む、請求項1に記載の樹脂組成物セット。
- 請求項1又は2に記載の樹脂組成物セットの前記発泡剤含有樹脂組成物及び前記発泡剤非含有樹脂組成物を共押出しすることにより得られ、
前記発泡剤含有樹脂組成物からなる第1層と、前記発泡剤非含有樹脂組成物からなる第2層との積層構造を含む、樹脂シート。 - 前記第1層に含まれる前記第1の樹脂分の一部又は全部が架橋している、請求項3に記載の樹脂シート。
- 前記第1の樹脂分がシラン架橋性樹脂を含む、請求項3又は4に記載の樹脂シート。
- 基材と、該基材上に設けられた、請求項3〜5のいずれか一項に記載の樹脂シートと、を備え、前記樹脂シートの前記第1層が前記基材側にある、積層シート。
- 基材と、該基材上に設けられた発泡樹脂層と、を備える発泡壁紙であって、
請求項6に記載の積層シートにおける前記第1層に含まれる発泡剤を発泡させて得られる、発泡壁紙。 - 第1の樹脂分と、充填剤と、発泡剤と、を含む発泡剤含有樹脂組成物と、第2の樹脂分を含み、発泡剤を含まない発泡剤非含有樹脂組成物と、を共押出しすることにより、前記発泡剤含有樹脂組成物からなる第1層と前記発泡剤非含有樹脂組成物からなる第2層との積層構造を含む樹脂シートを形成する樹脂シート形成工程を備え、
前記第1の樹脂分が、エチレン単独重合体又はエチレンと他のオレフィンとの共重合体を含み、
前記第2の樹脂分が、エチレン単独重合体又はエチレンと他のオレフィンとの共重合体を含み、
前記発泡剤含有樹脂組成物の130℃、2.16kgf荷重におけるメルトマスフローレート(A)及び前記発泡剤非含有樹脂組成物の130℃、2.16kgf荷重におけるメルトマスフローレート(B)が、以下の(i)、(ii)及び(iii)に示す条件を全て満たす、樹脂シートの製造方法。
(i)1g/10分≦(A)≦10g/10分
(ii)1g/10分≦(B)≦16g/10分
(iii)−3g/10分≦(B)−(A)≦6g/10分 - 前記第1の樹脂分が、低密度ポリエチレン及び超低密度ポリエチレンを含み、前記第2の樹脂分が、直鎖状低密度ポリエチレンを含む、請求項8に記載の樹脂シートの製造方法。
- 基材と、該基材上に設けられた発泡樹脂層と、を備える発泡壁紙の製造方法であって、
基材上に、請求項8又は9に記載の樹脂シートの製造方法により得られる樹脂シートの前記第1層側をラミネートして積層シートを得る積層シート形成工程と、
前記積層シートにおける前記第1層に含まれる前記発泡剤を発泡させることにより発泡樹脂層を形成する発泡工程と、
を備える、発泡壁紙の製造方法。 - 前記発泡工程が、前記積層シートを過熱水蒸気により加熱することを含む、請求項10に記載の発泡壁紙の製造方法。
- 前記発泡工程の前に、前記第1層に含まれる前記第1の樹脂分の一部又は全部を架橋する架橋工程を更に備える、請求項10又は11に記載の発泡壁紙の製造方法。
- 前記第1の樹脂分がシラン架橋性樹脂を含み、前記積層シートを過熱水蒸気により加熱して前記シラン架橋性樹脂の一部又は全部を架橋する、請求項12に記載の発泡壁紙の製造方法。
- 前記第1の樹脂分がシラン架橋性樹脂を含み、前記発泡工程において前記積層シートを過熱水蒸気により加熱して、前記シラン架橋性樹脂の一部又は全部を架橋しながら、前記発泡剤を発泡させる、請求項10に記載の発泡壁紙の製造方法。