JP6462266B2 - グローブ用布帛および繊維製品 - Google Patents
グローブ用布帛および繊維製品 Download PDFInfo
- Publication number
- JP6462266B2 JP6462266B2 JP2014163655A JP2014163655A JP6462266B2 JP 6462266 B2 JP6462266 B2 JP 6462266B2 JP 2014163655 A JP2014163655 A JP 2014163655A JP 2014163655 A JP2014163655 A JP 2014163655A JP 6462266 B2 JP6462266 B2 JP 6462266B2
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- glove
- filament yarn
- polyester filament
- sea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、グローブ用布帛には、高いグリップ力はもちろんのこと、吸水性、ソフト性、優れた耐久性なども要求されている。
前記ポリエステルフィラメント糸Aのフィラメント数が500本以上であり、前記ポリエステルフィラメント糸Aが、海成分と島成分とからなる海島型複合繊維の海成分を溶解除去して得られた糸条であり、前記樹脂が、発泡剤を含みかつ該発泡剤を発泡させた樹脂であり、布帛の表面および裏面のうち少なくともどちらか一方に、前記樹脂が、ドット状または文字で付着しており、布帛の厚さが0.2〜0.7mmの範囲内であり、布帛の表面および裏面のうち少なくともどちらか一方において、JIS L1096−1998 6.26.1滴下法で測定した吸水速度が10秒以下であることを特徴とするグローブ用布帛。」が提供される。
その際、単繊維繊度が2dtex以上のポリエステルフィラメント糸Bが含まれることが好ましい。
本発明のグローブ用布帛は、織物組織または編物組織を有するグローブ用布帛であって、該布帛が、単繊維径が10〜1500nmのポリエステルフィラメント糸Aを含み、かつ布帛の表面および裏面のうち少なくともどちらか一方に樹脂またはゴムが部分的に付着している。
前記樹脂またはゴムとしては特に限定されないが、アクリル酸エステル共重合樹脂、ウレタン樹脂、塩化ビニル樹脂、酢酸ビニル樹脂、スチレン−ブタジエン樹脂、天然ゴム、イソプレンゴム、シリコーンゴムなどが例示される。なかでも前記樹脂が、発泡剤を含みかつ該発泡剤を発泡させた樹脂であると高いグリップ力が得られ好ましい。また、前記樹脂がアクリル酸エステル共重合樹脂を含む樹脂であると、アクリル酸エステル共重合樹脂は接着性を有するため他のバインダーを必要とせず好ましい。
その際、ドット1個当たりの面積としては0.01〜25mm2が好ましい。また、下記に定義する付着比率としては10〜80%が好ましい。
付着比率=(付着部面積)/((付着部面積)+(非付着部面積))×100
ここで、吸水性としては、布帛の表面および裏面のうち少なくともどちらか一方において、JIS L1096−1998 6.26.1滴下法で測定した吸水速度が10秒以下であることが好ましい。
なお、かかる布帛において、布帛の厚さが0.2〜0.7mmの範囲内であることが好ましい。
乾燥処理後のポリマーを紡糸時のルーダー溶融温度に設定したオリフィスにセットして5分間溶融保持したのち、数水準の荷重をかけて押し出し、そのときのせん断速度と溶融粘度をプロットする。そのプロットをなだらかにつないで、せん断速度−溶融粘度曲線を作成し、せん断速度が1000秒−1の時の溶融粘度を見る。
海・島成分の各々0.3φ−0.6L×24Hの口金にて1000〜2000m/分の紡糸速度で糸を巻き取り、さらに残留伸度が30〜60%の範囲になるように延伸して、総繊度84dtex/24filのマルチフィラメントを作製する。これを各溶剤にて溶解しようとする温度で浴比100にて溶解時間と溶解量から、減量速度を算出した。
生地を電子顕微鏡で写真撮影した後、n数5で単繊維径を測定しその平均値を求めた。
JIS L 1096 8.5に従って測定した。
JIS L1096−1998 6.26.1滴下法に従って測定した。
JIS L1096 8.19.5 E法(マーチンデール法)に従って測定した。摩擦回数20000回で形状が維持(プリント樹脂が脱落したり、編地に穴が開いたりしない)していると良好とする。
下記式により算出した。
付着比率=(付着部面積)/((付着部面積)+(非付着部面積))×100
島成分としてポリエチレンテレフタレート(280℃における溶融粘度が1200ポイズ、艶消し剤の含有量:0重量%)、海成分として5−ナトリウムスルホイソフタル酸6モル%と数平均分子量4000のポリエチレングリコール6重量%を共重合したポリエチレンテレフタレート(280℃における溶融粘度が1750ポイズ)を用い(溶解速度比(海/島)=230)、海:島=30:70、島数=836の海島型複合未延伸繊維を、紡糸温度280℃、紡糸速度1500m/分で溶融紡糸して一旦巻き取った。
得られた未延伸糸を、延伸温度80℃、延伸倍率2.5倍でローラー延伸し、次いで150℃で熱セットして巻き取った。得られた海島型複合繊維(ポリエステルフィラメント糸A用繊維、延伸糸)は総繊度56dtex/10filであり、透過型電子顕微鏡TEMによる繊維横断面を観察したところ、島の形状は丸形状でかつ島の径は700nmであった。
一方、ポリエステルフィラメント糸Bとして、ポリエチレンテレフタレートフィラメント(総繊度33dtex/12fil、帝人(株)製)を用意した。
次いで、海島型複合繊維の海成分を除去するために編地を3.5%NaOH水溶液で、70℃にて30%アルカリ減量した。その後、130℃かつ30分間の高圧染色を行い、両面を起毛するためバフ加工を行い、170℃の乾熱セットを行った。
次いで、(株)村山化学研究所製の「SE BINDER FOAM 151ECO」(主成分:アクリル酸エステル共重合樹脂および発泡剤)重量比90に対し、水を10の割合で混合したプリント液を用意し、ロールスクリーン機で前記編地の片側表面にドット状にプリント液をプリントし(ドット1個当たりの面積0.5mm2、付着比率41%)、130℃で乾燥後、175℃で乾熱セットし発泡剤を発泡させ、グローブ用布帛を得た。
得られたグローブ用布帛において、ポリエステルフィラメント糸Aの単繊維径は700nmであり、ポリエステルフィラメント糸Bの単繊維径は16μmであった。
得られたグローブ用布帛は、厚さ0.4mm、吸水速度3.0秒、摩耗耐久性も良好であった。また、得られたグローブ用布帛を用いてゴルフグローブ製品を得て使用したところ、高い表面摩擦抵抗とグリップ力があり、ソフトでフィット感やしっとりした手持ち感を併せ持つものであった。なお、前記グローブ用布帛の樹脂プリント面がゴルフグローブ製品の外側(ゴルフクラブのグリップと接する側)になるように用いた。
実施例1において、海島複合繊維の代わりにポリエチレンテレフタレートフィラメント(56dtex/72fil、ポリエステルフィラメント糸C)を用い、これ以外は実施例1と同様にした。得られたグローブ用布帛において、ポリエステルフィラメント糸Cの単繊維径は8.5μmであった。
得られたグローブ用布帛は、厚さ0.5mm、吸水速度2.5秒と良好であったものの、摩耗耐久性はプリント樹脂が剥がれて不良であった。また、得られたグローブ用布帛を用いてゴルフグローブ製品を得て使用したところ、実施例1で得られたものと比較して、十分なグリップ力は得られず、また手持ち感も良くなかった。
実施例1において、同様に編地を得た後、(株)村山化学研究所製の「SE BINDER FOAM 151ECO」(主成分:アクリル酸エステル共重合樹脂および発泡剤)重量比90に対し、水を10の割合で混合したプリント液を用意し、グラビアコーターで前記編地の片側表面の全面にプリント液をプリントし、130℃で乾燥後、発泡剤を発泡させるために175℃で乾熱セットし、グローブ用布帛を得た。
得られたグローブ用布帛において、ポリエステルフィラメント糸Aの単繊維径は700nmであり、ポリエステルフィラメント糸Bの単繊維径は16μmであった。
得られたグローブ用布帛は、摩耗耐久性は良好であるものの、厚さ0.8mmと厚く、また、吸水しなかった。
得られたグローブ用布帛を用いてゴルフグローブ製品を得て使用したところ、実施例1で得られたものと比較して、十分なグリップ力は得られず、また手持ち感も良くなかった。
実施例1において、同様に編地を得た後、樹脂プリントせずに、そのまま編地をグローブ用布帛とした。得られたグローブ用布帛において、ポリエステルフィラメント糸Aの単繊維径は700nmであり、ポリエステルフィラメント糸Bの単繊維径は16μmであった。
得られたグローブ用布帛は、厚さ0.35mm、吸水速度2.0秒と良好であったが、得られたグローブ用布帛を用いてゴルフグローブ製品を得て使用したところ、実施例1で得られたものと比較して、十分なグリップ力は得られなかった。
2:非付着部
Claims (3)
- 編物組織を有するグローブ用布帛であって、該布帛が、単繊維径が10〜1500nmのポリエステルフィラメント糸Aを含み、かつ布帛の表面および裏面のうち少なくともどちらか一方にアクリル酸エステル共重合樹脂を含む樹脂が、1個あたりの面積0.01〜25mm2、付着比率10〜80%で部分的に付着しており、
前記ポリエステルフィラメント糸Aのフィラメント数が500本以上であり、前記ポリエステルフィラメント糸Aが、海成分と島成分とからなる海島型複合繊維の海成分を溶解除去して得られた糸条であり、前記樹脂が、発泡剤を含みかつ該発泡剤を発泡させた樹脂であり、布帛の表面および裏面のうち少なくともどちらか一方に、前記樹脂が、ドット状または文字で付着しており、布帛の厚さが0.2〜0.7mmの範囲内であり、布帛の表面および裏面のうち少なくともどちらか一方において、JIS L1096−1998 6.26.1滴下法で測定した吸水速度が10秒以下であることを特徴とするグローブ用布帛。 - 布帛に、さらに単繊維繊度が2dtex以上のポリエステルフィラメント糸Bが含まれる、請求項1に記載のグローブ用布帛。
- 請求項1または請求項2に記載のグローブ用布帛を用いてなる、スポーツ用グローブ、アウトドア用グローブ、バイク用グローブ、作業用グローブ、精密作業用グローブからなる群より選択されるいずれかの繊維製品。