JP6379039B2 - 回転成形組成物 - Google Patents
回転成形組成物 Download PDFInfo
- Publication number
- JP6379039B2 JP6379039B2 JP2014548920A JP2014548920A JP6379039B2 JP 6379039 B2 JP6379039 B2 JP 6379039B2 JP 2014548920 A JP2014548920 A JP 2014548920A JP 2014548920 A JP2014548920 A JP 2014548920A JP 6379039 B2 JP6379039 B2 JP 6379039B2
- Authority
- JP
- Japan
- Prior art keywords
- rotational molding
- molding composition
- propylene
- ethylene
- metal oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(a)約1.7〜約3.5のMw/Mn、少なくとも1つの融点Tm(℃)、および密度d(g/cm3)を有するが、このときTmおよびdの数値は、以下の関係式:
Tm>−2002.9+4538.5(d)−2422.2(d)2
に対応する;または
(b)約1.7〜約3.5のMw/Mnを有し、融解熱ΔH(J/g)、および最高DSCピークと最高CRYSTAFピークとの温度差であると規定されたデルタ量ΔT(℃)によって特徴付けられるが、このときΔTおよびΔHの数値は以下の関係式:
ゼロ超〜130J/gまでのΔHに対して、ΔT>−0.1299(ΔH)+62.81、
130J/g超のΔHに対して、ΔT≧48℃
を有し、このときCRYSTAFピークは少なくとも5%の累積ポリマーを使用して決定され、5%未満の該ポリマーが同定可能なCRYSTAFピークを有する場合は、該CRYSTAF温度は30℃である;または
(c)エチレン/α−オレフィン共重合体の圧縮成形フィルムを用いて測定された300%の歪みおよび1サイクルでの弾性回復率Re(%)によって特徴付けられ、密度d(g/cm3)を有するが、このときReおよびdの数値は、エチレン/α−オレフィン共重合体が実質的に架橋相を含んでいない場合に以下の関係式:
Re>1481−1629(d)
を満たす;または
(d)TREFを用いて分別した場合に40℃〜130℃で溶出する分子画分を有し、該画分が同一温度間で溶出する匹敵するランダムエチレン共重合体画分よりも少なくとも5%高いモルコモノマー含量を有することを特徴とするが、このとき該匹敵するランダムエチレン共重合体は同一コモノマーを有し、該エチレン/α−オレフィン共重合体の10%以内にあるメルトインデックス、密度およびモルコモノマー含量(全ポリマーに基づく)を有する;または
(e)25℃での貯蔵弾性率G’(25℃)および100℃での貯蔵弾性率G’(100℃)を有するが、このときG’(25℃)対G’(100℃)の比率は、約1:1〜約9:1の範囲内にある、エチレン/α−オレフィン共重合体であってよい。
(a)TREFを用いて分別した場合に40℃〜130℃の間で溶出する分子画分であって、少なくとも0.5〜約1までのブロックインデックスおよび約1.3より大きい分子量分布Mw/Mnを有することを特徴とする該分子画分を有していてよい;または
(b)0超〜約1.0までの平均ブロックインデックスおよび約1.3より大きい分子量分布Mw/Mnを有していてよい。
本発明の組成物1は、0.2重量%のMIOXならびにDow Chemical社から入手できる0.939g/cm3の密度および3.8g/10分のメルトインデックス(I2)を有するエチレン/α−オレフィンコポリマーである99.8重量%のDOWLEX(商標)NG2432.10UEを含んでいる。本発明の組成物1は、一辺が22cmの立方体形の試験用金型に形成した。1つの側壁の特性を試験し、結果は表1および2に報告した。
比較組成物1は、Dow Chemical社から入手できる0.939g/cm3の密度および3.8g/10分のメルトインデックス(I2)を有するエチレン/α−オレフィンコポリマーである100重量%のDOWLEX(商標)NG2432.10UEを含んでいる。比較組成物1は、一辺が22cmの立方体形の試験用金型に形成した。1つの側壁の特性を試験し、結果は表1および2に報告した。
試験方法には、以下が含まれる:
保持された伸び率(老化後)は、規格EN13341付属書A第A.1部およびA.2部にしたがって測定した。
圧縮成形試験は、ISO293:2005にしたがって実施した。
引張強さは、ISO527−2:1996によって測定した。
風化は、ISO4892−2にしたがって測定した。
衝撃強さは、ハンマーに潤滑油を適用せずにISO6603−2にしたがって測定した。
なお、本発明には以下の態様が包含される。
[1] 少なくとも95重量%の熱可塑性ポリマー、および
0.1〜3重量%の金属酸化物層板、
を含む回転成形組成物であって、
前記回転成形組成物は、以下:
(a)4,000時間の促進老化後に少なくとも85%の破断点伸び率の保持を有する特性、または
(b)前記金属酸化物層板を含んでいない類似組成物に比較して少なくとも50%の延性改善率を有する特性
のうちの少なくとも1つを特徴とする回転成形組成物。
[2] 前記金属酸化物は、酸化鉄である、[1]に記載の回転成形組成物。
[3]前記金属酸化物の小板は、99%を超える純度レベルを有する、[1]に記載の回転成形組成物。
[4]金属酸化物の小板は、2〜30μMの範囲内にある平均サイズ径(長軸)を有する、[1]に記載の回転成形組成物。
[5]金属酸化物の小板は、2〜30の範囲内にある平均アスペクト比(長軸/厚さ)を有する、[1]に記載の回転成形組成物。
[6]前記回転成形組成物は、前記金属酸化物層板を含んでいない類似組成物に比較して引張弾性率(2%)の少なくとも10%の改善率を有することをさらに特徴とする、[1]に記載の回転成形組成物。
[7]前記熱可塑性ポリマーは、エチレンをベースとするポリマーまたはプロピレンをベースとするポリマーである、[1]に記載の回転成形組成物。
Claims (5)
- 少なくとも95重量%の線状低密度ポリエチレン(LLDPE)、および
0.1〜1重量%の酸化鉄(III)(Fe2O3)で構成される金属酸化物層板、
を含む回転成形組成物であって、
前記回転成形組成物は、以下:
(a)少なくとも85%の破断点伸び率の保持を有する特性(ただし、前記破断点伸び率は、規格EN13341付属書A第A.1部およびA.2部にしたがって測定される)、または
(b)前記金属酸化物層板を含んでいない類似組成物に比較して少なくとも50%の延性改善率を有する特性(ただし、前記延性改善率は、ISO 527−2:1996にしたがって測定される)
のうちの少なくとも1つを特徴とする回転成形組成物。 - 前記金属酸化物層板は、99%を超える純度レベルを有する、請求項1に記載の回転成形組成物。
- 前記金属酸化物層板は、2〜30μMの範囲内にある平均サイズ径(長軸)を有する、請求項1に記載の回転成形組成物。
- 前記金属酸化物層板は、2〜30の範囲内にある平均アスペクト比(長軸/厚さ)を有する、請求項1に記載の回転成形組成物。
- 前記回転成形組成物は、前記金属酸化物層板を含んでいない類似組成物に比較して引張弾性率の少なくとも10%の改善率(ただし、前記引張弾性率は、ISO 527−2:1996にしたがって測定される)を有することをさらに特徴とする、請求項1に記載の回転成形組成物。