JP6310298B2 - 再剥離性シートの製造方法及び再剥離性シート - Google Patents
再剥離性シートの製造方法及び再剥離性シート Download PDFInfo
- Publication number
- JP6310298B2 JP6310298B2 JP2014068298A JP2014068298A JP6310298B2 JP 6310298 B2 JP6310298 B2 JP 6310298B2 JP 2014068298 A JP2014068298 A JP 2014068298A JP 2014068298 A JP2014068298 A JP 2014068298A JP 6310298 B2 JP6310298 B2 JP 6310298B2
- Authority
- JP
- Japan
- Prior art keywords
- base material
- adhesive
- overlapping surfaces
- overlapping
- adhesive composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このような再剥離性シートの代表的なものとしては、感圧圧着ハガキが例示でき、親展性を有するハガキシステムで汎用されている。
図4は、このような再剥離性シートの一例を示す図である。図1は、図4の再剥離性シートの表面展開図である。図4において、再剥離性シート(三つ折りハガキ)1は、領域A、領域B及び領域Cを備えている。そして、再剥離性シート1はZ折りに折り畳まれている。図4の再剥離性シートでは、図1における領域Bの表面と領域Cの表面が第1の重ね合わせ面を形成し、領域Aの裏面と領域Bの裏面が第2の重ね合わせ面を形成している。第1の重ね合わせ面同士及び第2の重ね合わせ面同士は、再剥離可能に接着される。
1実施形態に係る再剥離性シートとしての感圧圧着ハガキについて、以下、図面を引用しながら説明する。図1は再剥離性シート(三つ折りハガキ)の表面展開図、図2は図1に示すハガキの裏面展開図、図3は図1のX−X線における断面図、図4は図1に示すハガキを折り込む際の状態を説明する図である。
(接着剤基剤)
接着剤組成物は、接着剤基剤、溶媒、場合によりその他の成分を含む。接着剤基剤は公知のものでよく、具体的には、天然ゴム、天然ゴムを変性した変性ゴム、合成ゴム等が例示でき、より具体的には、有機溶媒を用いる有機溶媒系のもの、水を媒体とする水系のもの等が例示できる。なお、本明細書においては、特に断りのない限り「接着剤基剤」とは、前記天然ゴム等の固形のものを意味し、前記有機溶媒、水等の液状の媒体を含まないものとする。
これらの中でも、前記接着剤基剤は水系のものが好ましく、天然ゴム系水性エマルジョンタイプのものがより好ましい。水系の接着剤基剤である場合、これを用いたエマルジョン等の組成物は揮発性が低くなり、塗布量の調節が容易で、基材への塗布適性がより優れたものとなる。また、かかる組成物は媒体が水なので人体に無害であり、さらに引火性もなく、塗布工程や乾燥工程に防爆設備等の特殊設備が不要となる。
天然ゴムにメタクリル酸メチルをグラフト重合させて得られた変性ゴムで好ましいものとしては、天然ゴム100質量部に対して、メタクリル酸メチルを10〜40質量部グラフト重合させたものが例示できる。
天然ゴムにスチレンとメタクリル酸メチルとをグラフト重合させて得られた変性ゴムで好ましいものとしては、天然ゴム100質量部に対して、スチレン及びメタクリル酸メチルを合計で30〜70質量部重合させたものが例示できる。
溶媒としては、組成物の粘度調整に用いる各種溶媒が例示でき、より具体的には、水、各種有機溶媒が例示できる。
前記有機溶媒は、配合成分を劣化させないものであれば特に限定されないが、高極性の有機溶媒が好ましく、具体的には、メタノール、エタノール、2−プロパノール等のアルコール;アセトン、メチルエチルケトン、シクロヘキサノン等の鎖状又は環状ケトン;ジエチルエーテル、テトラヒドロフラン等の鎖状又は環状エーテル等が例示できる。
前記有機溶媒は一種を単独で用いてもよいし、二種以上を併用してもよい。二種以上を併用する場合には、それらの組み合わせ及び比率は、目的に応じて適宜選択すればよい。
その他の成分としては、微粒子、添加剤等が例示できる。前記微粒子の材質として、具体的には、フッ素樹脂、硬質微粒子、各種デンプン(スターチ)、ポリエチレン、シリカ、シラスバルーン、天然ゼオライト、合成ゼオライト、酸化亜鉛、酸化チタン、カオリン、活性白土等が例示できる。
前記微粒子は、平均粒子径が異なる二種以上を併用することが好ましい。このようにすることで、接着剤層表面に凹凸を形成し易くなり、その結果、接着剤層の接着力を損なうことなく再剥離性がより向上する。
前記組成物は、前記接着剤基剤、溶媒及び必要に応じてその他の成分を配合することで製造できる。
各成分の配合時には、すべての成分を添加してからこれらを混合してもよいし、一部の成分を順次添加しながら混合してもよく、すべての成分を順次添加しながら混合してもよい。また、固形の成分は、少なくともその一部を溶媒に分散させた分散物として添加してもよい。
混合方法は特に限定されず、撹拌子又は撹拌翼等を回転させて混合する方法、ミキサーを使用して混合する方法、超音波を加えて混合する方法等、公知の方法から適宜選択すればよい。そして、溶解していない成分が均一に分散するまで撹拌することが好ましい。
本発明に係る再剥離性シートは、基材の重ね合わせ面同士が、前記組成物を用いて形成された前記接着剤層で、再剥離可能に接着されてなるものである。
前記接着剤層は、例えば、基材の所定箇所に前記組成物を塗工し、乾燥させることで形成できる。
本発明において、基材は、少なくとも組成物の塗布面の材質が紙類であるものが好ましい。
本工程において、前記基材の表面における第1の重ね合わせ面又は/及び前記基材の裏面における第2の重ね合わせ面に印刷や印字を行い、印刷層を形成する。第1の重ね合わせ面のみに印刷や印字を行ってもよいし、第2の重ね合わせ面のみに印刷や印字を行ってもよいし、第1の重ね合わせ面及び第2の重ね合わせ面の双方に印刷や印字を行ってもよい。印刷方法は特に制限されず、例えば、グラビア印刷法やオフセット印刷法、スクリーン印刷法、フレキソ印刷法、静電印刷法、インクジェット印刷法等の従来公知の各種の印刷方法を使用することができる。
続いて、印刷済みの基材における前記第1の重ね合わせ面及び前記第2の重ね合わせ面上に接着剤組成物を塗布して接着剤層を形成する。より具体的には、図1に示す領域B及びCの表面に相当する基材の面上に接着剤組成物を塗布し、乾燥定着させて接着剤層を形成した後、更に図1の領域A及びBの裏面に相当する基材の面上に、接着剤組成物を塗布し、乾燥定着させて接着剤層を形成する。本製造方法は、印刷層の上に接着剤層が形成される、いわゆる後糊方式の製造方法である。
続いて、上述のようにして接着剤層が形成された前記基材を、前記第1の重ね合わせ面上の前記接着剤層同士及び前記第2の重ね合わせ面上の前記接着剤層同士が接触するようにZ折りに折り畳む。より具体的には、図1の折り線(折部)3a、3bに相当する基材上の線に沿って、基材を図4のようにZ型に折り畳む。基材の折り畳みは、通常の折り処理装置で行うことができる。
続いて、Z折りに折り畳まれた前記基材を加圧して再剥離可能に接着する。加圧は、例えば、対向する2個の金属ロールをロール面同志が非接触となるようにして備えたシール装置を用いて、折り畳んだ基材を、前記ロール面間を通過させることにより加圧することにより行うことができる。シール装置としては、例えば「プレッスルマルチ」(商品名、トッパン・フォームズ社製)を好適に使用できる。加圧は、例えば、加圧部位の加圧後の厚さが加圧前の厚さの70〜90%、例えば80%となるように行えばよい。加圧の圧力は、例えば、7〜20MPaである。
本発明の再剥離性シートの製造方法は、接着剤組成物の粘度と基材の透気度を所定の範囲に調整することを特徴とする。接着剤組成物の粘度は、例えば、B型粘度計のNo.2ローターを使用して、接着剤組成物の粘度に応じて60rpm又は6rpmで測定するとよい。また、透気度とは、基材が空気を透過させる度合いであり、基材が所定量の空気を透過させるのに要する時間である。透気度は、JIS P8117にしたがって測定することができる。
透気度が小さい基材と粘度が低い接着剤組成物を使用した場合、基材の透気度が小さいため、基材中に空隙が多く、基材中の空気が抜けやすいと考えられる。また、接着剤組成物の粘度が低いため、接着剤組成物が基材中に浸透しやすいと考えられる。
このため、図1の領域Bの表面に塗布した接着剤組成物は、基材中に比較的浸透すると考えられる。また、続いて領域Bの裏面に接着剤組成物を塗布した場合に、もともと基材中の空気が抜けやすいため、基材中の空気が障害となりにくく、接着剤組成物が基材中に比較的浸透すると考えられる。この結果、領域Bの表面と裏面に浸透せずに残った接着剤組成物により形成された接着剤層の厚さは同程度となり、上記の再剥離性シートの第1の重ね合わせ面同士の接着力と第2の重ね合わせ面同士の接着力の差も小さいものになると考えられる。
透気度が大きい基材と粘度が高い接着剤組成物を使用した場合、基材の透気度が大きいため、基材中に空隙が少なく、基材中の空気が抜けにくいと考えられる。また、接着剤組成物の粘度が高いため、接着剤組成物が基材中に浸透しにくいと考えられる。
このため、図1の領域Bの表面に塗布した接着剤組成物は、基材中にあまり浸透しないと考えられる。また、続いて領域Bの裏面に接着剤組成物を塗布した場合にも、接着剤組成物は、粘度が高いことから基材中にあまり浸透しないと考えられる。この結果、領域Bの表面と裏面に浸透せずに残った接着剤組成物により形成された接着剤層の厚さは同程度となり、上記の再剥離性シートの第1の重ね合わせ面同士の接着力と第2の重ね合わせ面同士の接着力の差も小さいものになると考えられる。
透気度が小さい基材と粘度が高い接着剤組成物を使用した場合、基材の透気度が小さいため、基材中に空隙が多く、基材中の空気が抜けやすいと考えられる。
このため、図1の領域Bの表面に塗布した接着剤組成物は、粘度が高いものの、ある程度基材中に浸透すると考えられる。
また、続いて領域Bの裏面に接着剤組成物を塗布した場合に、表面に塗布した接着剤組成物が蓋となって、基材の透気度は小さいものの基材中の空気が抜けにくくなり、障害となることと、接着剤組成物の粘度が高いことで基材中の空気が障害となりやすいことから、接着剤組成物が基材中に浸透しにくいと考えられる。この結果、領域Bの表面と裏面に浸透せずに残った接着剤組成物により形成された接着剤層の厚さに差が生じ、上記の再剥離性シートの第1の重ね合わせ面同士の接着力と第2の重ね合わせ面同士の接着力の差も大きいものになると考えられる。
透気度が大きい基材と粘度が低い接着剤組成物を使用した場合、基材の透気度が大きいため、基材中に空隙が少なく、基材中の空気が抜けにくいと考えられる。
しかしながら、図1の領域Bの表面に塗布した接着剤組成物は、粘度が低いため、ある程度基材中に浸透すると考えられる。
また、続いて領域Bの裏面に接着剤組成物を塗布した場合に、表面に塗布した接着剤組成物が蓋となって、基材中の空気が抜けにくくなり、障害となることから、接着剤組成物の粘度が低いものの、基材中にあまり浸透しないと考えられる。この結果、領域Bの表面と裏面に浸透せずに残った接着剤組成物により形成された接着剤層の厚さに差が生じ、上記の再剥離性シートの第1の重ね合わせ面同士の接着力と第2の重ね合わせ面同士の接着力の差も大きいものになると考えられる。
(再剥離性シートの製造)
表1に示す品質の基材及び表2に示す品質の接着剤組成物を使用して、再剥離性シートを作製した。表2において、実施例1、比較例2及び比較例4の接着剤組成物の粘度は、25℃においてB型粘度計(東機産業社製)No.2ローターを使用して6rpmで測定した。また、実施例2、比較例1及び比較例3の接着剤組成物の粘度は、25℃においてB型No.2ローターを使用して60rpmで測定した。
得られた再剥離性シートについて、JIS K6854に準じて、図1の領域B及びCの表面に相当する面からなる第1の重ね合わせ面同士(以下「表面」という場合がある。)の接着力を測定した。接着力は、剥離試験機(島津製作所社製「オートグラフAGSH」)を用いて、速度300mm/分、剥離角90°(すなわち、T字剥離)で再剥離性シートを剥離させたときの抵抗値により測定した。続いて、表面と同様の操作により、図1の領域A及びBの裏面に相当する面からなる第2の重ね合わせ面同士(以下「裏面」という場合がある。)の接着力を測定した。結果を表3に示す。
表1に示す品質の基材及び表2に示す品質の接着剤組成物を使用して、実施例1と同様にして実施例2及び比較例1〜4の再剥離性シートを作製した。続いて、実施例1と同様にして、表面及び裏面の接着力を測定した。結果を表3に示す。
Claims (3)
- 基材の表面における第1の重ね合わせ面同士、及び、前記基材の裏面における第2の重ね合わせ面同士が、折部を介してZ折りに折り畳まれて再剥離可能に接着された再剥離性シートの製造方法であって、
前記基材の前記第1の重ね合わせ面上又は/及び前記第2の重ね合わせ面上に印刷層を形成する工程と、
前記印刷層を形成する工程後の前記第1の重ね合わせ面上及び前記第2の重ね合わせ面上に接着剤組成物を塗布して接着剤層を形成する工程と、
前記接着剤層が形成された前記基材を、前記折部を介して前記第1の重ね合わせ面同士及び前記第2の重ね合わせ面同士が対向するようにZ折りに折り畳む工程と、
Z折りに折り畳まれた前記基材を加圧して、前記第1の重ね合わせ面同士及び前記第2の重ね合わせ面同士を再剥離可能に接着する工程と、を含み、
前記基材の透気度が200秒以下であり且つ前記接着剤組成物の粘度が300mPa・s以下であること、又は前記基材の透気度が2000秒以上であり且つ前記接着剤組成物の粘度が2000mPa・s以上であること、を特徴とし、
前記粘度は、B型粘度計のNo.2ローターを使用して、25℃において、前記接着剤組成物の粘度が2000mPa・s以上である場合には6rpmで測定し、前記接着剤組成物の粘度が300mPa・s以下である場合には60rpmで測定した場合のものである、再剥離性シートの製造方法。 - 基材の表面における第1の重ね合わせ面同士、及び、前記基材の裏面における第2の重ね合わせ面同士が、折部を介してZ折りに折り畳まれて再剥離可能に接着された再剥離性シートであって、請求項1に記載の製造方法により得られる、再剥離性シート。
- 前記第2の重ね合わせ面同士の接着力が、前記第1の重ね合わせ面同士の接着力の0.7〜1.3倍である、請求項2に記載の再剥離性シート。