JP6270750B2 - メルトブロー不織布、その製造方法および装置 - Google Patents
メルトブロー不織布、その製造方法および装置 Download PDFInfo
- Publication number
- JP6270750B2 JP6270750B2 JP2015009788A JP2015009788A JP6270750B2 JP 6270750 B2 JP6270750 B2 JP 6270750B2 JP 2015009788 A JP2015009788 A JP 2015009788A JP 2015009788 A JP2015009788 A JP 2015009788A JP 6270750 B2 JP6270750 B2 JP 6270750B2
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- melt
- melt blown
- blown nonwoven
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
例えば、メルトブロー用ダイのダイノーズ尖端部、ダイノーズ先端部とリップ板尖端部との距離等を特定の範囲にする方法(特許文献1:特開昭54−103466号公報)、リップ板尖端部間の幅(エアーナイフの間隔)が0.4〜0.8mmのダイを用いる方法(特許文献2:特開平4−91267号公報)、ノズルのオリフィス径を0.1〜0.5mm以下、単孔当たりの吐出量を0.05〜0.8g/分、好ましくは0.1〜0.5g/分の条件で製造する方法(特許文献3:特開平5−295645号公報)、牽引用流体流路の間隔(エアギャップ)、ダイノーズ先端部とリップ板尖端部との距離及びその比を特定の範囲にする方法(特許文献4:特開平11−200135号公報)あるいは平均繊維径を0.1〜5.0μmの範囲にする方法(特許文献5:特開平4−163353号公報)等、種々提案されている。
(i)平均繊維径が2.0μm以下、
(ii)繊維径分布CV値が60%以下、
(iii)繊維100本当たりの融着個数が15個以下、
であることを特徴とするメルトブロー不織布に関わる。
(i)平均繊維径が2.0μm以下、
(ii)繊維径分布CV値が60%以下、
(iii)繊維100本当たりの融着個数が15個以下、
(iv)α晶分率が0.9未満、
であることを特徴とするメルトブロー不織布に関わる。
また、本発明に係る製造装置は、構造が簡単でコンパクトであるとともに汎用の製造装置を大きく設計変更せずに構成することができる。
本発明のメルトブロー不織布を形成する極細繊維の原料となる熱可塑性樹脂は、種々公知の熱可塑性樹脂を用い得る。
前記熱可塑性樹脂の中でも、プロピレン系重合体が得られるメルトブロー不織布の耐薬品性が優れるので好ましい。
本発明のメルトブロー不織布の製造方法は、メルトブロー用ダイに圧送された溶融された熱可塑性樹脂(溶融樹脂)を、多数の小孔が並べられたノズルから紡出するとともに、小孔の列を挟むように設けたスリットから噴出される高温高速空気によって牽引細化させてなる繊維を移動する捕集板上に堆積してなるメルトブロー不織布の製造方法において、前記高温高速空気が噴出される前記スリットの出口部の両側面から30℃以下、好ましくは5〜25℃、より好ましくは5〜20℃の冷却流体を供給し、紡出された熱可塑性樹脂繊維を冷却することを特徴とするメルトブロー不織布の製造方法である。
本発明のメルトブロー不織布の製造方法によれば、紡出された熱可塑性樹脂繊維が、高温高速空気で牽引細化される際に、冷却流体との合流で空気流の温度が所定の温度以下に冷却されることにより、繊維間の融着を防止することができ、それにより、繊維同士の融着によって発生する太繊維〔融着個数〕を少なくすることができる。
本発明のメルトブロー不織布の製造装置は、メルトブロー用ダイに圧送された溶融樹脂を、多数の小孔が並べられたノズルから紡出するとともに、小孔の列を挟むように設けたスリットから噴出される高温高速空気によって牽引細化させてなる繊維を移動する捕集板上に堆積してなるメルトブロー不織布の製造装置において、前記メルトブロー用ダイの先端部に、紡出された熱可塑性樹脂繊維を冷却するための冷却流体、好ましくは冷却空気を導入するためのアタッチメントを着脱自在に取付けてなることを特徴とするメルトブロー不織布の製造装置である。
なお、この隙間無くとは、外部の空気が取り込まれる空気通路が形成されないとの意味である。
以下、上記プロピレン系重合体によるメルトブロー不織布の製造方法および製造装置について、更に、図面を参照しながら説明する。
このメルトブロー不織布の製造装置2は、メルトブロー用ダイ4の下方に、メッシュコンベア6からなる捕集板が配置され、このメッシュコンベア6の下方に、減圧手段により内部を吸引することのできるサクションボックス8が配置されている。
また、メルトブロー用ダイ30は、例えばヒーターにより、通常、280℃付近まで高温にされているので、温度差の大きい冷却空気を供給するためのアタッチメント32は、メルトブロー用ダイ30との間で熱伝播が生じないように設置する必要がある。そのため、例えば、ダイ30の下面に断熱材を介在させることが好ましい。あるいは、メルトブロー用ダイ30とアタッチメント32との間に若干隙間をあけて取り付けても良い。
よって、本発明によれば、冷却空気が高温空気に混ざり合った以後は、急冷されることにより、繊維間同士での熱融着を可及的に防止することができる。
本発明のメルトブロー不織布の製造方法および製造装置を用い、原料となる前記熱可塑性樹脂の内、ポリオレフィンを用いることにより、以下の特徴を有するメルトブロー不織布を製造することができる。
(i)平均繊維径が2.0μm以下
(ii)繊維径分布CV値が60%以下、好ましくは50%以下の範囲、
(iii)繊維100本当たりの融着個数が15個以下、好ましくは12個以下、さらに好ましくは10個以下、
であるメルトブロー不織布、である。
(i)平均繊維径が2.0μm以下の範囲、
(ii)繊維径分布CV値が60%以下、好ましくは50%以下の範囲、
(iii)繊維100本当たりの融着個数が15個以下、好ましくは12個以下、さらに好ましくは10個以下、
(iv)α晶分率が0.9未満、
であるメルトブロー不織布。
(i)平均繊維径
平均繊維径は通常2.0μm以下の範囲にあり、衛生材料用途には2μm以下、好ましくは1.8μm以下が適している。また、フィルタ用途には0.8μm以下、好ましくは、0.3〜0.6μmの範囲が適している。
具体的には、例えば、編布、織布、不織布、フィルム等を挙げることができる。本発明のメルトブロー不織布と他の層を積層する(貼り合せる)場合は、熱エンボス加工、超音波融着等の熱融着法、ニードルパンチ、ウォータージェット等の機械的交絡法、ホットメルト接着剤、ウレタン系接着剤等の接着剤による方法、押出しラミネート等をはじめ、種々公知の方法を採り得る。
本発明のフィルタは、前記メルトブロー不織布からなる層を含むフィルタであって、目付90g/cm2における0.5mm径の微粒子の捕集効率が99%以上である。
本発明の不織布積層体は、前記メルトブロー不織布の少なくとも片面にスパンボンド不織布が積層されている不織布積層体であって、メルトブロー不織布層の目付(g/m2)と積層体全体の目付(g/m2)の比〔メルトブロー不織布層の目付/積層体全体の目付〕が0.050以下、好ましくは0.040以下である。
目付比が0.050を超える不織布積層体は、メルトブロー不織布の目付が高いために柔軟性および通気性に劣る虞がある。
本発明の電池用セパレータは、前記メルトブロー不織布からなる層を含むセパレータであって、平均繊維径が、0.1〜2.0μm、好ましくは、0.2〜1.5μm、より好ましくは0.3〜1.0μmであるのが望ましく、また、目付量が3 〜 30g/m2、好ましくは4 〜 25g/m2 、より好ましくは5 〜 15g/m2であるのが望ましい。平均繊維径がこのような範囲にある場合には、微細な細孔を有する不織布が製造でき、かつ、メルトブローン法による紡糸および不織布の製造が円滑に生産性よく行えるため好ましい。目付量がこの範囲にあれば、電池として使用した場合にショートせず、内部抵抗が小さいので好ましい。
実施例及び比較例における物性値等は、以下の方法により測定した。
(1)平均繊維径(μm)、融着個数[本/100本]:
電子顕微鏡(日立製作所製S−3500N)を用いて、画面内に観察されるメルトブロー不織布の繊維本数が10本から20本の範囲となる倍率に調整したうえで表面写真を撮影する。直径の10倍以上の長さを有する場合を繊維とし、画面内の全ての繊維の幅(直径)を測定した。これを合計100本となるように繰り返して、得られた直径測定結果の平均を平均繊維径とした。なお、測定数の合計が100本を越える場合は下記式より平均繊維径を算出した。
平均繊維径=直径測定結果の平均×100/測定合計本数
さらに上記100本のなかで、その繊維径が平均繊維径の2倍を超える場合に糸同士が融着していると判定し、その個数を融着個数とした。
なお、測定数の合計が100本を越える場合は下記式より融着個数を算出した。
融着個数=融着個数合計×100/測定合計本数
目付90g/m2のメルトブロー不織布を調整し、JIS Z8703(試験場所の標準状態)に規定する温度20±2℃、湿度65±2%の恒温室内で、水処理用濾過材となる不織布積層体から採取した試験片をフッ素系不活性液体(3M社製 商品名:フロリナート)に浸漬し、Porous materials,Inc社製のキャピラリー・フロー・ポロメーター(Capillary Flow Porometer)「モデル:CFP-1200AE」を用いて目付90g/m2で測定した最大孔径(μm)、最小孔径(μm)及び平均孔径(μm)を測定した(表中、「最大孔径」、「最小孔径」及び「平均孔径」と示す)。
目付90g/m2のメルトブロー不織布を調整し、球状粒子径1.00μmのポリスチレンラテックス粒子を60容量%のイソプロピルアルコール(IPA)水溶液に0.01重量%の濃度で分散した試験液を用い、ろ過装置(ADVANTEC製TSU−90B)で0.3MPaの圧力のもとメルトブロー不織布(液体用フィルタ)を通過した濾液中の濃度:C1と原液の濃度:C0を測定し、次式で阻止率を求めた。
試験液および濾液の濃度は分光光度計(島津製UV3100)を使用し、波長500nmの吸光度を測定し、予め測定した検量線から求めた。
阻止率=〔(C0−C1)/C0〕×100(%)
流量(l/min)は、上記ろ過装置を用い0.3MPaの圧力のもと500ccの60容量%IPA水溶液がメルトブロー不織布(液体用フィルタ)を通過したときの時間を測定し求めた。
JIS L1092A法に準拠して、JIS Z8703(試験場所の標準状態)に規定する温度20±2℃、湿度65±2%の恒温室内で水処理用濾過材となる不織布積層体から採取した15×15cmの試験片10枚を採取し耐水圧試験機を用いて、水が漏れるときの圧力を測定しその平均値を求めた。
広角X線回折装置(リガク社製 RINT2500、付属装置:回転試料台、X線源:CuKα、出力:50kV 300mA、検出器:シンチレーションカウンター)を用いて、不織布を試料ホルダーに充填し、広角X線回折透過法により回折プロファイルを回転しながら測定した。
[α晶分率]=[α晶ピークの強度]/ [α晶ピークの強度+スメチカ晶のピーク強度]
評価者10人により手触りの評価を行った。以下の基準で評価結果を示す。
◎:手触りが良いと感じた人が、10人のうち10人の場合
○:手触りが良いと感じた人が、10人のうち9〜7人の場合
△:手触りが良いと感じた人が、10人のうち6〜3人の場合
×:手触りが良いと感じた人が、10人のうち2人以下の場合
<スパンボンド不織布の製造>
スパンボンド不織布製造装置(捕集面上の機械の流れ方向に垂直な方向の長さ:500mm)を用いて、プロピレン単独重合体(PP−1、MFR:60g/10分、融点:157℃)を240℃で溶融し、目付:7g/m2、繊維径:14μmのスパンボンド不織布を用意した。
上記方法で得たスパンボンド不織布に片面に、プロピレン単独重合体(PP−2、MFR:850g/10分、融点:159℃)をメルトブロー不織布製造装置のダイに供給し、設定温度:280℃のダイから、メルトブロー用ノズル(0.32mmφ、各ノズルの小孔の孔間の距離:0.20mm)を用いて、ノズル単孔あたりの吐出量:0.52g/分でノズルの両側から吹き出す高温高速空気(280℃、600m3/hr)と伴に吐出し、その後に冷却空気(温度:15℃、風量:6000m3/hr)にて冷却と分散を行い、DCD(紡糸口金の表面からコレクターまでの距離):120mmでメルトブロー不織布の目付が0.7g/m2となるように上記スパンボンド不織布の上に吹き付けて、スパンボンド不織布とメルトブロー不織布の積層体を得た。次いで、上記と同一条件で製造されるスパンボンド不織布をメルトブロー不織布上に積層して、総目付:14.7g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=7.0/0.7/7.0g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
実施例1で製造したメルトブロー不織布に替えて、スパンボンド不織布に積層するメルトブロー不織布として、メルトブロー用ノズル(0.32mmφ、各ノズルの小孔の孔間の距離:1.59mm)を用い、ノズル単孔あたりの吐出量を1.27g/分で製造した目付が0.5g/m2のメルトブロー不織布を用いる以外は、実施例1と同様に行い、総目付:14.5g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=7.0/0.5/7.0g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
プロピレン単独重合体(MFR:1500g/10分)をメルトブロー不織布製造装置のダイに供給し、設定温度:280℃のダイから、メルトブロー用ノズル(0.2mmφ、各ノズルの小孔の孔間の距離:2.62mm)を用いて、ノズル単孔あたりの吐出量:0.08g/分でノズルの両側から吹き出す高温高速空気(280℃、600m3/hr)と伴に吐出し、その後に冷却空気(温度:15℃、風量:6000m3/hr)にて冷却と分散を行い、DCD(紡糸口金の表面からコレクターまでの距離):120mmでコレクターの上に吹き付けて、目付:15g/m2のメルトブロー不織布を得た。
次いで、得られたメルトブロー不織布を6枚重ねて目付90g/m2の液体用フィルタとした。結果を表2に示す。
実施例1で製造したメルトブロー不織布に替えて、スパンボンド不織布に積層するメルトブロー不織布として、メルトブロー用ノズル(0.32mmφ、各ノズルの小孔の孔間の距離1.02mm)を用い、ノズル単孔あたりの吐出量を1.26g/分で製造した目付が0.7g/m2のメルトブロー不織布を用いること、スパンボンド不織布として、実施例1で製造したスパンボンド不織布の目付を6.15g/m2とすること、高温高速空気の量を1400m3/hrとすること、DCDを150mmとすること以外は、実施例1と同様に行い、総目付:13.0g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=6.15/0.7/6.15g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
スパンボンド不織布に積層するメルトブロー不織布として、メルトブロー用ノズル(0.32mmφ、各ノズルの小孔の孔間の距離0.33mm)を用い、ノズル単孔あたりの吐出量を0.63g/分で製造した目付が0.7g/m2のメルトブロー不織布を用いること、高温高速空気の量を1500m3/hrとすること以外は、実施例4と同様に行い、総目付:13.0g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=6.15/0.7/6.15g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
スパンボンド不織布に積層するメルトブロー不織布として、メルトブロー用ノズル(0.32mmφ、各ノズルの小孔の孔間の距離0.20mm)を用い、ノズル単孔あたりの吐出量を0.51g/分で製造した目付が0.7g/m2のメルトブロー不織布を用いること、高温高速空気の量を700m3/hrとすること以外は、実施例4と同様に行い、総目付:13.0g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=6.15/0.7/6.15g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
スパンボンド不織布に積層するメルトブロー不織布として、メルトブロー用ノズル(0.4mmφ、各ノズルの小孔の孔間の距離0.25mm)を用い、ノズル単孔あたりの吐出量を0.51g/分で製造した目付が0.7g/m2のメルトブロー不織布を用いること、高温高速空気の量を1200m3/hrとすること以外は、実施例4と同様に行い、総目付:13.0g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=6.15/0.7/6.15g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
実施例1において、メルトブロー不織布を製造する際に、冷却空気を使用せずに、目付が1.0g/m2のメルトブロー不織布を用いる以外は、実施例1と同様に行い、総目付:15.0g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=7.0/1.0/7.0g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
実施例1において、メルトブロー不織布を製造する際に、冷却空気を使用しなかった以外は実施例3と同様の方法にて、目付:15g/m2のメルトブロー不織布を得た。
次いで、得られたメルトブロー不織布を6枚重ねて目付90g/m2の液体用フィルタとした。結果を表2に示す。
比較例2において、メルトブロー用ノズル(0.2mmφ、各ノズルの小孔の孔間の距離0.68mm)を用いる以外は、比較例2と同様の方法で行い、目付:15g/m2のメルトブロー不織布を得た。
次いで、得られたメルトブロー不織布を6枚重ねて目付90g/m2の液体用フィルタとした。結果を表2に示す。
比較例2において、メルトブロー用ノズル(0.2mmφ、各ノズルの小孔の孔間の距離2.62mm)を用いる以外は、比較例2と同様の方法で行い、目付:15g/m2のメルトブロー不織布を得た。
次いで、得られたメルトブロー不織布を6枚重ねて目付90g/m2の液体用フィルタとした。結果を表2に示す。
目付が0.7g/m2のメルトブロー不織布を用いる以外は、比較例1と同様に行い、総目付:14.7g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=7.0/0.7/7.0g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
メルトブロー不織布を製造する際に、冷却空気に替えて、温度:50℃、風量:6000m3/hrの空気を使用すること、DCDを150mmとすること以外は、実施例1と同様に行い、総目付:14.7g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=7.0/0.7/7.0g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
メルトブロー不織布を製造する際に、冷却空気を使用しないこと、高温高速空気の量を1000m3/hrとすること以外は、実施例5と同様に行い、総目付:13.0g/m2(スパンボンド不織布/メルトブロー不織布/スパンボンド不織布=6.15/0.7/6.15g/m2)の不織布積層体を得た。
得られた不織布積層体の物性を上記記載の方法で測定した。結果を表1に示す。
4 メルトブロー用ダイ
6 メッシュコンベア
8 サクションボックス
10 繊維
12 ダイノーズ
14 小孔
16 ノズル
18 樹脂通路
20a、20b 空気通路
31 スリット
32 アタッチメント
Claims (5)
- プロピレン系重合体繊維からなり、
(i)平均繊維径が2.0μm以下、
(ii)繊維径分布CV値が60%以下、
(iii)繊維100本当たりの融着個数が15個以下、
(iv)α晶分率が0.9未満、
であることを特徴とするメルトブロー不織布。 - 請求項1記載のメルトブロー不織布からなる層を含み、目付90g/cm2における0.5mm径の微粒子の捕集効率が99%以上であるフィルタ。
- 請求項1記載のメルトブロー不織布の少なくとも片面にスパンボンド不織布が積層されている不織布積層体であって、メルトブロー不織布層の目付(g/m2)と積層体全体の目付(g/m2)の比が0.05以下であることを特徴とする不織布積層体。
- 請求項3記載の不織布積層体を含む衛生用品。
- 請求項1記載のメルトブロー不織布からなる層を含む電池用セパレータ。