JP5955623B2 - コンクリート - Google Patents
コンクリート Download PDFInfo
- Publication number
- JP5955623B2 JP5955623B2 JP2012100647A JP2012100647A JP5955623B2 JP 5955623 B2 JP5955623 B2 JP 5955623B2 JP 2012100647 A JP2012100647 A JP 2012100647A JP 2012100647 A JP2012100647 A JP 2012100647A JP 5955623 B2 JP5955623 B2 JP 5955623B2
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- expansion
- composition
- age
- alite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
〔1〕(A)低熱ポルトランドセメントと、(B)フライアッシュと、(C)遊離生石灰およびエーライトを含有するクリンカ粉砕物と石膏を含有してなる膨張性組成物と、(D)骨材とを含有するコンクリートであって、前記膨張性組成物中、遊離生石灰(c2)とエーライト(c1)との質量比(c2/c1)が0.7〜1.0であり、クリンカ粉砕物の粉末度が、ブレーン法による比表面積で1500〜5000cm 2 /gであることを特徴とするコンクリート。
〔2〕硬化体の材齢2日の圧縮強度に対する膨張ひずみの比が1.5〜5.5×104N/mm2である前記[1]のコンクリート。
〔3〕(C)膨張性組成物中、遊離生石灰の含有率が18〜30質量%、エーライトの含有率が20〜35質量%、石膏の含有率が20〜30質量%である前記〔1〕又は〔2〕記載のコンクリート。
フライアッシュの混和率(%)=FA÷P×100 (1)
〔実施例1・比較例1〕
表1に示す使用材料を用い、表2の膨張性組成物を調製した。膨張性組成物のEX1〜EX7は、焼成温度1400℃で、焼結させたクリンカ組成物を粉末度2600cm2/gに粉砕し、粉砕したクリンカ組成物に石膏をヘンシェルミキサーにて混合し、膨張性組成物を調製した。
実施例1の本発明のコンクリート(配合No.1および2)と比較例に当たる配合No.5及び8のコンクリートにおいて、環境温度10℃および30℃として、表3に示す使用材料を用いて表4に示す配合により、コンクリートミキサを用いて練り混ぜてコンクリートを製造した。製造したコンクリートを用いて、規格(JIS A 6202「コンクリート用膨張材」附属書2)に示される拘束膨張及び収縮試験方法(A法)に準拠し、拘束膨張試験を実施した。また、規格(JIS A 1108「コンクリートの圧縮強度試験方法」)に準拠し、圧縮強度試験を実施した。この結果を表6および表7に示した。
Claims (3)
- (A)低熱ポルトランドセメントと、
(B)フライアッシュと、
(C)遊離生石灰およびエーライトを含有するクリンカ粉砕物と石膏を含有してなる膨張性組成物と、
(D)骨材と
を含有するコンクリートであって、前記膨張性組成物中、遊離生石灰(c2)とエーライト(c1)との質量比(c2/c1)が0.7〜1.0であり、クリンカ粉砕物の粉末度が、ブレーン法による比表面積で1500〜5000cm 2 /gであることを特徴とするコンクリート。 - 硬化体の材齢2日における圧縮強度と膨張ひずみの比が1.5〜5.5×104N/mm2である請求項1記載のコンクリート。
- (C)膨張性組成物中、遊離生石灰の含有率が18〜30質量%、エーライトの含有率が20〜35質量%、石膏の含有率が20〜30質量%である請求項1又は2記載のコンクリート。