JP5897161B2 - 粘結剤コーテッド耐火物の製造方法、鋳型の製造方法 - Google Patents
粘結剤コーテッド耐火物の製造方法、鋳型の製造方法 Download PDFInfo
- Publication number
- JP5897161B2 JP5897161B2 JP2015002743A JP2015002743A JP5897161B2 JP 5897161 B2 JP5897161 B2 JP 5897161B2 JP 2015002743 A JP2015002743 A JP 2015002743A JP 2015002743 A JP2015002743 A JP 2015002743A JP 5897161 B2 JP5897161 B2 JP 5897161B2
- Authority
- JP
- Japan
- Prior art keywords
- binder
- phenol resin
- phenol
- coated
- refractory
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
反応容器に一価のフェノールを940質量部、37質量%濃度のホルマリンを665質量部、シュウ酸を5.6質量部仕込み、約60分を要して還流させ、そのまま180分間反応させた。この後、180℃まで昇温させて水と未反応のフェノールを留去し、軟化点が92℃の固形のノボラック型フェノール樹脂Dを得た。このフェノール樹脂Dには三価フェノールは含有されていない。
反応容器に一価のフェノールを799質量部、37質量%濃度のホルマリンを665質量部、シュウ酸を1.88質量部仕込み、約90分を要して還流させ、そのまま90分間反応させた。次に、水200質量部に三価のピロガロール141質量部を分散乃至溶解したピロガロール含有水を、発熱に注意しながら約30分を要して加え、還流させながら60分間反応させた。この後、180℃まで昇温させて水と未反応のフェノールを留去することによって、軟化点が95℃の固形のピロガロール含有ノボラック型フェノール樹脂Eを得た。このフェノール樹脂E中のピロガロールの含有量は15.4質量%であった。
反応容器に一価のフェノールを799質量部、37質量%濃度のホルマリンを665質量部、シュウ酸を1.88質量部仕込み、約90分を要して還流させ、そのまま90分間反応させた。次に、水200質量部に三価のフロログルシン141質量部を分散乃至溶解したフロログルシン含有水を、発熱に注意しながら約30分を要して加え、還流させながら60分間反応させた。この後、180℃まで昇温させて水と未反応のフェノールを留去することによって、軟化点が84℃の固形のフロログルシン含有ノボラック型フェノール樹脂Iを得た。このフェノール樹脂I中のフロログルシンの含有量は15.2質量%であった。
フラッタリー硅砂30kgを140℃に加熱してワールミキサーに仕込み、これにノボラック型フェノール樹脂E、Iを600g加え、30秒間混合した後、23℃の水を150g加えて混合することによって、フラッタリー硅砂を冷却した。そして冷却により110℃に温度が低下したフラッタリー硅砂に、ヘキサメチレンテトラミン90gを450gの水に溶解した水溶液を添加し、砂粒の塊が崩壊するまで混合した。次に滑剤としてステアリン酸カルシウム30gを加えて15秒間混練し、さらにエアレーションを行なうことによって、粘結剤コーテッド耐火物を得た。
フラッタリー硅砂30kgを140℃に加熱してワールミキサーに仕込み、これにノボラック型フェノール樹脂Dを600g加え、30秒間混合した後、23℃の水を150g加えて混合することによって、フラッタリー硅砂を冷却した。そして冷却により110℃に温度が低下したフラッタリー硅砂に、ヘキサメチレンテトラミン90gを450gの水に溶解した水溶液を添加し、砂粒の塊が崩壊するまで混合した。次に滑剤としてステアリン酸カルシウム30gを加えて15秒間混練し、さらにエアレーションを行なうことによって、粘結剤コーテッド耐火物を得た。
剛直率(%)=(熱間曲げ強さ/曲げ強さ)×100
上記の各結果を、表2に示す。
反応容器に一価のフェノールを680質量部、三価のカテコールを50質量部、水を400質量部仕込み、良く撹拌して溶解させた。ここに37質量%濃度のホルマリン220質量部を徐々に加え、その後、30℃で30分間反応させた。次に、水100質量部にヘキサメチレンテトラミン100質量部を分散乃至溶解させた水溶液を加えた。さらに37質量%濃度のホルマリンを460質量部加え、約60分を要して60℃まで昇温させ、そのまま4時間反応させた。次に反応容器の内容物をバットに払い出し、分離した水を傾斜法で除去した後、−20℃の冷凍庫に素早く入れて冷凍させた。24時間後に冷凍物を1mm以下の粒径に粗砕した後、流動床乾燥器にかけて凍結乾燥することによって、固形のカテコール含有レゾール型フェノール樹脂Kを得た。このレゾール型フェノール樹脂Kの軟化点は80℃であり、カテコールの含有量は6.5質量%であった。
反応容器に一価のフェノールを680質量部、37質量%濃度のホルマリンを679質量部、ヘキサメチレンテトラミンを101質量部仕込み、約60分を要して70℃まで昇温させ、そのまま5時間反応させた。次に反応容器の内容物をバットに払い出し、分離した水を傾斜法で除去した後、−20℃の冷凍庫に素早く入れて冷凍させた。24時間後に冷凍物を1mm以下の粒径に粗砕した後、流動床乾燥器にかけて凍結乾燥することによって、水分を1.1質量%含有する固形のレゾール型フェノール樹脂Lを得た。このレゾール型フェノール樹脂Lの軟化点は76℃であり、三価フェノールは含有されていない。
フラッタリー硅砂30kgを110℃に加熱してワールミキサーに仕込み、これにレゾール型フェノール樹脂K、Lを600g加え、30秒間混合した後、水350gを添加し、砂粒の塊が崩壊するまで混合した。次に滑剤としてステアリン酸カルシウム30gを加えて15秒間混練し、さらにエアレーションを行なうことによって、粘結剤コーテッド耐火物を得た。
2 粘結剤コーテッド耐火物
Claims (18)
- 三価フェノールが粘結剤の主成分であるフェノール樹脂に1〜60質量%含有されているフェノール樹脂粘結剤組成物を含有する固形の粘結剤層を耐火骨材の表面に被覆して形成される粘結剤コーテッド耐火物を製造するにあたって、フェノール類とアルデヒド類を反応させてフェノール樹脂を調製する際に、三価フェノールを添加することによって、この三価フェノールが含有されるフェノール樹脂粘結剤組成物を調製し、耐火骨材とこの三価フェノールが含有されるフェノール樹脂粘結剤組成物を混合することによって、上記のフェノール樹脂粘結剤組成物を含有する固形の粘結剤層を耐火骨材の表面に被覆することを特徴とする粘結剤コーテッド耐火物の製造方法。
- 三価フェノールが粘結剤の主成分であるフェノール樹脂に1〜60質量%含有されているフェノール樹脂粘結剤組成物を含有する固形の粘結剤層を耐火骨材の表面に被覆して形成される粘結剤コーテッド耐火物を製造するにあたって、フェノール類とアルデヒド類を反応させて調製されたフェノール樹脂と、三価フェノールを、耐火骨材と混合することによって、上記のフェノール樹脂粘結剤組成物を含有する固形の粘結剤層を耐火骨材の表面に被覆することを特徴とする粘結剤コーテッド耐火物の製造方法。
- 三価フェノールが粘結剤の主成分であるフェノール樹脂に1〜60質量%含有されているフェノール樹脂粘結剤組成物を含有する固形の粘結剤層を耐火骨材の表面に被覆して形成される粘結剤コーテッド耐火物を製造するにあたって、フェノール類とアルデヒド類を反応させてフェノール樹脂を調製し、このフェノール樹脂に三価フェノールを添加して溶融混合することによって、上記フェノール樹脂粘結剤組成物を調製し、耐火骨材とこの三価フェノールが含有されるフェノール樹脂粘結剤組成物を混合することによって、上記のフェノール樹脂粘結剤組成物を含有する固形の粘結剤層を耐火骨材の表面に被覆することを特徴とする粘結剤コーテッド耐火物の製造方法。
- 三価フェノールが粘結剤の主成分であるフェノール樹脂に1〜60質量%含有されているフェノール樹脂粘結剤組成物を含有する固形の粘結剤層を耐火骨材の表面に被覆して形成される粘結剤コーテッド耐火物を製造するにあたって、フェノール樹脂の溶融温度以上の温度に加熱した耐火骨材に固形のフェノール樹脂を混合して耐火骨材の表面に被覆し、次いで三価フェノールが反応しない温度以下に冷却した状態で、フェノール樹脂を表面に被覆した上記耐火骨材にこの三価フェノールを添加して混合することによって、上記のフェノール樹脂粘結剤組成物を含有する固形の粘結剤層を耐火骨材の表面に被覆することを特徴とする粘結剤コーテッド耐火物の製造方法。
- 三価フェノールが反応しない温度以下に冷却した状態で、フェノール樹脂を表面に被覆した耐火骨材に三価フェノールを添加して混合する他、フェノール樹脂用の硬化剤がフェノール樹脂と反応しない温度以下に冷却した状態で、フェノール樹脂を表面に被覆した耐火骨材にこの硬化剤を添加して混合することを特徴とする請求項4に記載の粘結剤コーテッド耐火物の製造方法。
- フェノール樹脂を被覆した耐火骨材を冷却する温度が、130℃未満であることを特徴とする請求項4又は5に記載の粘結剤コーテッド耐火物の製造方法。
- 水を加えることによって、フェノール樹脂を被覆した耐火骨材を冷却することを特徴とする請求項4乃至6のいずれかに記載の粘結剤コーテッド耐火物の製造方法。
- 三価フェノールがピロガロール、フロログルシンから選ばれるものであることを特徴とする請求項1乃至7のいずれかに記載の粘結剤コーテッド耐火物の製造方法。
- フェノール樹脂がノボラック型フェノール樹脂とレゾール型フェノール樹脂の少なくとも一方であることを特徴とする請求項1乃至8のいずれかに記載の粘結剤コーテッド耐火物の製造方法。
- 上記フェノール樹脂粘結剤組成物は、温度130℃で測定したときのゲル化時間が、100秒以下であることを特徴とする請求項1乃至9いずれかに記載の粘結剤コーテッド耐火物の製造方法。
- 上記粘結剤層には、フェノール樹脂用の硬化剤が含有されていることを特徴とする請求項1乃至10いずれかに記載の粘結剤コーテッド耐火物の製造方法。
- 請求項1乃至11のいずれかに記載の方法で製造した粘結剤コーテッド耐火物を加熱した型内に供給し、型の熱よって粘結剤コーテッド耐火物の粘結剤層のフェノール樹脂を硬化させることを特徴とする鋳型の製造方法。
- 請求項1乃至11のいずれかに記載の方法で製造した粘結剤コーテッド耐火物を型内に充填し、この型内に水蒸気を吹き込んで粘結剤コーテッド耐火物を加熱し、粘結剤層のフェノール樹脂を硬化させることを特徴とする鋳型の製造方法。
- 粘結剤コーテッド耐火物を充填した型内に水蒸気を吹き込んで、水蒸気の凝縮潜熱により粘結剤コーテッド耐火物の温度を上昇させ、次に加熱した気体を型内に吹き込んで、型内の凝縮水を蒸発させると共に粘結剤コーテッド耐火物の粘結剤層のフェノール樹脂が硬化する温度以上に加熱することを特徴とする請求項13に記載の鋳型の製造方法。
- 上記の加熱した気体が、加熱した空気であることを特徴とする請求項14に記載の鋳型の製造方法。
- 上記の加熱した気体が、水蒸気と空気との混合気体であることを特徴とする請求項14に記載の鋳型の製造方法。
- 上記の水蒸気が、過熱水蒸気であることを特徴とする請求項13乃至16のいずれかに記載の鋳型の製造方法。
- 予備加熱した粘結剤コーテッド耐火物を型内に充填することを特徴とする請求項13乃至17のいずれかに記載の鋳型の製造方法。