JP5809783B2 - ガスケット用樹脂組成物、その製造方法及び二次電池用ガスケット - Google Patents
ガスケット用樹脂組成物、その製造方法及び二次電池用ガスケット Download PDFInfo
- Publication number
- JP5809783B2 JP5809783B2 JP2010142585A JP2010142585A JP5809783B2 JP 5809783 B2 JP5809783 B2 JP 5809783B2 JP 2010142585 A JP2010142585 A JP 2010142585A JP 2010142585 A JP2010142585 A JP 2010142585A JP 5809783 B2 JP5809783 B2 JP 5809783B2
- Authority
- JP
- Japan
- Prior art keywords
- gasket
- group
- resin composition
- thermoplastic elastomer
- electrode plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
すなわち、近年、高い理論容量の活物質を電極物質として用いることによってリチウムイオン電池の高容量化が進んだ反面、充放電時に3〜4倍といった大きな体積変化を示すようになり、内部媒体の圧力が格段に高くなっている。さらには、ハイブリッド自動車(HV)や電気自動車(EV)といった車載用途の比重が高くなった結果、従来よりも高い安全性が要求され、高温・高湿の過酷な条件下でのガスケットの気密性や耐電解液性に対する信頼性が極めて高いレベルで必要となってきている。
このような環境変化のなかで、特に「Li/(CF)n系のコイン型電池」を主として想定し発明された上記樹脂組成物のガスケットでは、気密性及び耐電解質性が不十分なものとなっていた。
本発明が解決しようとする課題は、リチウムイオン二次電池等の密閉型二次電池(蓄電池)に用いられるガスケット用材料として、優れた耐電解液性及び気密性を兼備したガスケット用樹脂組成物及び二次電池用ガスケットを提供することである。
また本発明は、正極、負極、封口体、ガスケット、セパレータ及び電解液から構成される二次電池に用いられるガスケット用樹脂組成物であって、熱可塑性エラストマー(A)及びゲル浸透クロマトグラフィーにより求められる分子量分布のピーク分子量として28,000〜100,000であるポリアリーレンスルフィド樹脂(B)を含有することを特徴とするガスケット用樹脂組成物を提供する。
また本発明は、正極、負極、封口体、ガスケット、セパレータ及び電解液から構成される二次電池に用いられるガスケット用樹脂組成物の製造方法であって、熱可塑性エラストマー(A)及びゲル浸透クロマトグラフィーにより求められる分子量分布のピーク分子量として28,000〜100,000であるポリアリーレンスルフィド樹脂(B)を混合することを特徴とするガスケット用樹脂組成物の製造方法を提供する。
(1)N−メチルピロリドン、ジメチルアセトアミドなどのアミド系溶剤やスルホラン等のスルホン系溶媒中で硫化ナトリウムとp−ジクロロベンゼンを反応させる方法。
(2)p−ジクロロベンゼンを硫黄と炭酸ソーダの存在下で重合させる方法。
(3)p−ジクロロベンゼンを極性溶媒中で硫化ナトリウムあるいは水硫化ナトリウムと水酸化ナトリウム又は硫化水素と水酸化ナトリウムの存在下で重合させる方法。
(4)p−クロロチオフェノールの自己縮合による方法。
含水アルカリ金属硫化物、又は、含水アルカリ金属水硫化物及びアルカリ金属水酸化物と、N−メチルピロリドンと、非加水分解性有機溶媒とを、脱水させながら反応させて、スラリー(I)を製造する工程。
[工程2]
次いで、前記スラリー(I)中、ジクロロベンゼンと、前記アルカリ金属水硫化物と、前記N−メチルピロリドンの加水分解物のアルカリ金属塩とを、反応させて重合を行う工程。
装置:超高温ポリマー分子量分布測定装置(株式会社センシュー科学製「SSC−7000」)
カラム:UT−805L(昭和電工株式会社製)
カラム温度:210℃
溶媒:1−クロロナフタレン
測定方法:UV検出器(360nm)
で6種類の単分散ポリスチレンを校正に用いて分子量分布とピーク分子量を測定する。
本発明で用いるPAS樹脂(B)は、この方法により測定された非ニュートン指数が、1.0〜1.7のものを用いることができるが、特に、1.10〜1.70のものを用いることが好ましい。
(式中、Rは水素原子、有機基を表し、nは2以上の整数である。)
(式中、nは1以上の整数である。)
(式中、k、l、mは、0又は正の整数であり、l、mは同時に0でない整数をとる。また、R3は水素原子、アルキル基、アリール基、ハロゲン化アルキル基、シリルアルキル基及び後述する反応性官能基からなる群から選ばれる1種以上の置換基である。)
実施例1〜8及び比較例1〜4
表1及び表2に記載する配合量にしたがい、PAS樹脂であるポリフェニレンスルフィド、熱可塑性エラストマー及びその他配合材料をタンブラーで均一に混合した。その後、東芝機械株式会社製ベント付き2軸押出機「TEM−35B」に前記配合材料を投入し、樹脂成分吐出量25kg/hr、スクリュー回転数250rpm、樹脂成分の吐出量(kg/hr)とスクリュー回転数(rpm)との比率(吐出量/スクリュー回転数)=0.1(kg/hr・rpm)、設定樹脂温度330℃で溶融混練して樹脂組成物のペレットを得た。次いで、このペレットを用いて以下の各種評価試験を行った。試験及び評価の結果は、表1及び2に示す。
測定対象樹脂配合物の試験片をASTM4号ダンベル形状で作成し、ASTM D638に従って、株式会社島津製作所製「オートグラフ AG−5000C」にて測定し、引張破断伸びを測定した。
樹脂組成物ペレットを射出成形機を用いて成形し、射出成形機により縦8mm×横8mm×厚さ3mmの平板を成形し、図1に示すような圧縮応力緩和用試験片を作製した。この試験片を用い、恒温層を備えた株式会社島津製作所製「オートグラフ AG−50KNX」により10%歪み下(温度条件:23℃及び60℃)で圧縮応力緩和を測定し、100時間後の圧縮応力を求めた。
樹脂組成物ペレットを射出成形機を用いて成形し、形状が縦8mm×横8mm×高さ10mmで厚さ0.8mmの箱形成型品を作成した。次いで、この箱形成型品に電解液(1mol/LのLiPF6/エチレンカーボネート(EC):ジメチルカーボネート(DMC)(容量1:1混合溶液)溶液、キシダ化学株式会社製)を入れ、圧縮応力緩和試験で用いた縦8mm×横8mm×厚さ3mmの平板で一定応力(10%歪み下)で封をした気密試験用サンプルを作成する。これを60℃の乾熱下で放置し、液の漏れ具合について確認した。なお、評価結果は以下のように表示した。
◎:200時間後に液の漏れを生じない。
○:100時間後に液の漏れが生じない。
×:100時間後に液の漏れが生じる。
(1)PPS−1:ポリフェニレンスルフィド(DIC株式会社製「DSP LD−10G」;ピーク分子量 35,000、非ニュートン指数 1.56)
(2)PPS−2:ポリフェニレンスルフィド(DIC株式会社製「DSP ML−320」:ピーク分子量 41,000、非ニュートン指数 1.27)
(3)PPS−3:ポリフェニレンスルフィド(DIC株式会社製「DSP LR−2G」;ピーク分子量 34,000、非ニュートン指数 1.12)
(4)PPS−4:ポリフェニレンスルフィド(DIC株式会社製「DSP LR−100G」;ピーク分子量 20,000、非ニュートン指数 1.05)
(5)PPS−5:ポリフェニレンスルフィド(DIC株式会社製「DSP HC−270」;ピーク分子量 30,000、非ニュートン指数 1.62)
(6)PPS−6:ポリフェニレンスルフィド(DIC株式会社製「DSP LR−300G」;ピーク分子量 25,000、非ニュートン指数 1.08)
(7)ELA−1:エチレン−メタクリル酸グリシジル−アクリル酸メチル共重合体(住友化学工業株式会社製「ボンドファースト7L」)
(8)ELA−2:エチレン−無水マレイン酸−アクリル酸エチル共重合体(住友化学工業株式会社製「ボンダインAX8390」)
(9)Si−1:アミノ基含有シリコーン(信越化学工業株式会社製「KF−868」)
(10)PFA:テトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合体(ダイキン工業株式会社製の「ネオフロンAP−201」)
Claims (15)
- 正極板、負極板、セパレータ、電解液、電池ケース、及び封口体を含む二次電池に用いられるガスケットであって、前記ガスケットは、前記正極板と電気的に接続されている正極端子との接点又は前記負極板と電気的に接続されている負極端子との接点に設けられており、前記ガスケットが熱可塑性エラストマー(A)及びゲル浸透クロマトグラフィーにより求められる分子量分布のピーク分子量として28,000〜100,000であるポリアリーレンスルフィド樹脂(B)を含有するガスケット用樹脂組成物からなり、
前記熱可塑性エラストマー(A)の配合量が、前記熱可塑性エラストマー(A)及びポリアリーレンスルフィド樹脂(B)の合計100質量部に対して1〜30質量部であり、
前記樹脂組成物を射出成形して得られる試験片が、一定条件下(23℃、10%歪み、試験片厚さ3mm、圧縮面側表面積60mm2)での圧縮応力緩和試験において、100時間後圧縮応力の絶対値が10MPa以上であることを特徴とする二次電池用ガスケット。 - 前記樹脂組成物を射出成形して得られる試験片を用いた引張試験(ASTM D638)において、10%以上の引張破断伸びを有することを特徴とする請求項1記載のガスケット。
- 前記熱可塑性エラストマー(A)が、水酸基、カルボキシル基、アミノ基、メルカプト基、エポキシ基、酸無水物基、イソシアネート基、エステル基及びビニル基からなる群から選ばれる少なくとも1つの官能基を有するものである請求項1または2記載のガスケット。
- 前記熱可塑性エラストマー(A)が、α−オレフィン類、無水マレイン酸、(メタ)アクリル酸グリシジル及び(メタ)アクリル酸アルキルエステルからなる群から選ばれるモノマーを重合させた三元共重合体である請求項1〜3のいずれか一項記載のガスケット。
- 前記熱可塑性エラストマー(A)が、エチレン−メタクリル酸グリシジル−アクリル酸メチル共重合体又はエチレン−無水マレイン酸−アクリル酸エチル共重合体である請求項1〜4のいずれか一項記載のガスケット。
- 前記ガスケット用樹脂組成物が、熱可塑性エラストマー(A)及びポリアリーレンスルフィド樹脂(B)に加え、さらにシリコーン化合物(C)を含有する請求項1〜5のいずれか1項記載のガスケット。
- 前記シリコーン化合物(C)の配合量が、前記熱可塑性エラストマー(A)及びポリアリーレンスルフィド樹脂(B)、シリコーン化合物(C)の合計100質量部に対して0.1〜10質量部である請求項6記載のガスケット。
- 正極板、負極板、セパレータ、電解液、電池ケース、及び封口体を含む二次電池に用いられるガスケット用樹脂組成物であって、前記ガスケットは、前記正極板と電気的に接続されている正極端子との接点又は前記負極板と電気的に接続されている負極端子との接点に設けられており、前記ガスケット用樹脂組成物が、熱可塑性エラストマー(A)及びゲル浸透クロマトグラフィーにより求められる分子量分布のピーク分子量として28,000〜100,000であるポリアリーレンスルフィド樹脂(B)を含有すること、
前記熱可塑性エラストマー(A)の配合量が、前記熱可塑性エラストマー(A)及びポリアリーレンスルフィド樹脂(B)の合計100質量部に対して1〜30質量部であること、
前記樹脂組成物を射出成形して得られる試験片が、一定条件下(23℃、10%歪み、試験片厚さ3mm、圧縮面側表面積60mm2)での圧縮応力緩和試験において、100時間後圧縮応力の絶対値が10MPa以上であること、
を特徴とするガスケット用樹脂組成物。 - 前記樹脂組成物を射出成形して得られる試験片を用いた引張試験(ASTM D638)において、10%以上の引張破断伸びを有することを特徴とする請求項8記載のガスケット用樹脂組成物。
- 前記熱可塑性エラストマー(A)が、水酸基、カルボキシル基、アミノ基、メルカプト基、エポキシ基、酸無水物基、イソシアネート基、エステル基及びビニル基からなる群から選ばれる少なくとも1つの官能基を有するものである請求項8または9記載のガスケット用樹脂組成物。
- 前記熱可塑性エラストマー(A)が、α−オレフィン類、無水マレイン酸、(メタ)アクリル酸グリシジル及び(メタ)アクリル酸アルキルエステルからなる群から選ばれるモノマーを重合させた三元共重合体である請求項8〜10のいずれか一項記載のガスケット用樹脂組成物。
- 前記熱可塑性エラストマー(A)が、エチレン−メタクリル酸グリシジル−アクリル酸メチル共重合体又はエチレン−無水マレイン酸−アクリル酸エチル共重合体である請求項8〜11のいずれか一項記載のガスケット用樹脂組成物。
- 前記ガスケット用樹脂組成物が、熱可塑性エラストマー(A)及びポリアリーレンスルフィド樹脂(B)に加え、さらにシリコーン化合物(C)を含有する請求項8〜12のいずれか1項記載のガスケット用樹脂組成物。
- 前記シリコーン化合物(C)の配合量が、前記熱可塑性エラストマー(A)、ポリアリーレンスルフィド樹脂(B)及びシリコーン化合物(C)の合計100質量部に対して0.1〜10質量部である請求項13記載のガスケット用樹脂組成物。
- 正極板、負極板、セパレータ、電解液、電池ケース、及び封口体を含む二次電池に用いられるガスケット用樹脂組成物の製造方法であって、前記ガスケットは、前記正極板と電気的に接続されている正極端子との接点又は前記負極板と電気的に接続されている負極端子との接点に設けられており、前記ガスケット用樹脂組成物が、熱可塑性エラストマー(A)及びゲル浸透クロマトグラフィーにより求められる分子量分布のピーク分子量として28,000〜100,000であるポリアリーレンスルフィド樹脂(B)を混合すること、
前記熱可塑性エラストマー(A)の配合量が、前記熱可塑性エラストマー(A)及びポリアリーレンスルフィド樹脂(B)の合計100質量部に対して1〜30質量部であること、
前記樹脂組成物を射出成形して得られる試験片が、一定条件下(23℃、10%歪み、試験片厚さ3mm、圧縮面側表面積60mm2)での圧縮応力緩和試験において、100時間後圧縮応力の絶対値が10MPa以上であること、
を特徴とするガスケット用樹脂組成物の製造方法。