JP5715826B2 - 卓越した溶接性および耐食性を有するシームレス管用の高強度低合金鋼 - Google Patents
卓越した溶接性および耐食性を有するシームレス管用の高強度低合金鋼 Download PDFInfo
- Publication number
- JP5715826B2 JP5715826B2 JP2010547943A JP2010547943A JP5715826B2 JP 5715826 B2 JP5715826 B2 JP 5715826B2 JP 2010547943 A JP2010547943 A JP 2010547943A JP 2010547943 A JP2010547943 A JP 2010547943A JP 5715826 B2 JP5715826 B2 JP 5715826B2
- Authority
- JP
- Japan
- Prior art keywords
- steel
- mpa
- strength
- concentration
- steel pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
最小降伏強度Rp0.2:それぞれ620MPa(90ksi)および690MPa(100ksi)。
最小抗張力Rm:それぞれ690MPa(90ksi)および760MPa(100ksi)
切欠き衝撃強度Av(長手方向):−40℃にて90J
確実な一般溶接性
低いまたは制限されたNi濃度
H2Sを含むガス(酸性ガス)を輸送するときでも耐食性
0.030〜0.12%のC
最大0.40%のSi
1.30〜2.00%のMn
最大0.015%のP
最大0.005%のS
0.020〜0.050%のAl
0.20〜0.60%のNi
0.10〜0.40%のCu
0.20〜0.60%のMo
0.02〜0.10%のV
0.02〜0.06%のNb
最大0.0100%のN
と、溶融関連不純物を含む残りの鉄とを含み、Ti+Nb+Vの濃度の和が≧0.04%〜≦0.15%の値を有し、比Cu/Niが<1の値を有するという条件で任意にTiが添加される鋼が提案される。
0.10%のC
0.30%のSi
1.68%のMn
0.015%のP
0.002%のS
0.026%のAl
0.19%のCu
0.48%のNi
0.37%のMo
0.047%のV
0.042%のNb
0.003%のTi
0.006%のN
ならびにCu/Ni=0.40およびTi+Nb+V=0.092。
Claims (8)
- 620MPaの最小降伏強度および少なくとも690MPaの抗張力を有する、優れた溶接性および応力腐食亀裂に対する耐性を有するシームレス鋼管用の高強度低合金鋼であって、以下の化学組成(質量%):
0.030〜0.12%のC、
0.020〜0.050%のAl、
最大0.40%のSi、
1.30〜2.00%のMn、
最大0.015%のP、
最大0.005%のS、
0.20〜0.60%のNi、
0.10〜0.40%のCu、
0.20〜0.60%のMo、
0.02〜0.10%のV、
0.02〜0.06%のNb、
最大0.0100%のN、
と、残部鉄および不可避的不純物からなり、Ti+Nb+Vの濃度の和が≧0.043%〜≦0.15%の値を有し、比Cu/Niが<1の値を有するという条件でTiが添加され、Ti濃度の下限がTi≧0.003%であるシームレス鋼管用の高強度低合金鋼。 - Ti濃度が最大0.02%であることを特徴とする、請求項1に記載の鋼。
- 以下の化学組成(質量%):
0.080〜0.11%のC
0.020〜0.050%のAl、
0.25〜0.35%のSi、
1.65〜1.90%のMn、
最大0.015%のP、
最大0.005%のS、
0.45〜0.55%のNi、
0.15〜0.20%のCu、
0.35〜0.55%のMo、
0.04〜0.06%のV、
0.04〜0.05%のNb、
最大0.006%のNを含み、Ti+Nb+Vの濃度の和が≧0.083%〜≦0.15%の値であることを特徴とする、請求項1または2に記載の鋼。 - 鋼が690MPaの最小降伏強度および少なくとも760MPaの抗張力を有することを特徴とする、請求項1〜3のいずれか一項に記載の鋼。
- 620MPaの最小降伏強度および少なくとも690MPaの抗張力を有する、優れた溶接性および応力腐食亀裂に対する耐性を有する、熱間圧延と続いての焼戻しによって製造される高強度で溶接可能なシームレス鋼管であって、以下の合金組成:
0.030〜0.12%のC、
0.020〜0.050%のAl、
最大0.40%のSi、
1.30〜2.00%のMn、
最大0.015%のP、
最大0.005%のS、
0.20〜0.60%のNi、
0.10〜0.40%のCu、
0.20〜0.60%のMo、
0.02〜0.10%のV、
0.02〜0.06%のNb、
最大0.0100%のN、
と、残部鉄および不可避的不純物からなり、Tiが添加され、Ti濃度の下限がTi≧0.003%であり、ただしTi+Nb+V濃度の和が≧0.043%〜≦0.15%の値を有し、比Ni/Cuが≧1の値を有するという条件である鋼を含む、高強度で溶接性に優れたシームレス鋼管。 - 鋼が最大0.020%のチタン濃度を有することを特徴とする、請求項5に記載の鋼管。
- 鋼が以下の合金組成:
0.080〜0.11%のC
0.020〜0.050%のAl、
0.25〜0.35%のSi、
1.65〜1.90%のMn、
最大0.015%のP、
最大0.005%のS、
0.45〜0.55%のNi、
0.15〜0.20%のCu、
0.35〜0.55%のMo、
0.04〜0.06%のV、
0.04〜0.05%のNb、
最大0.006%のNを有し、Ti+Nb+Vの濃度の和が≧0.083%〜≦0.15%の値であることを特徴とする、請求項5または6に記載の鋼管。 - 鋼が690MPaの最小降伏強度および少なくとも760MPaの抗張力を有することを特徴とする、請求項5〜7のいずれか一項に記載の鋼管。