JP5610161B2 - Non-aqueous electrolyte secondary battery active material and non-aqueous electrolyte secondary battery - Google Patents

Non-aqueous electrolyte secondary battery active material and non-aqueous electrolyte secondary battery Download PDF

Info

Publication number
JP5610161B2
JP5610161B2 JP2011520950A JP2011520950A JP5610161B2 JP 5610161 B2 JP5610161 B2 JP 5610161B2 JP 2011520950 A JP2011520950 A JP 2011520950A JP 2011520950 A JP2011520950 A JP 2011520950A JP 5610161 B2 JP5610161 B2 JP 5610161B2
Authority
JP
Japan
Prior art keywords
active material
antioxidant
secondary battery
electrode
electrolyte secondary
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2011520950A
Other languages
Japanese (ja)
Other versions
JPWO2011002013A1 (en
Inventor
脇坂　康尋
康尋 脇坂
佳 小林
佳 小林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zeon Corp
Original Assignee
Zeon Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zeon Corp filed Critical Zeon Corp
Priority to JP2011520950A priority Critical patent/JP5610161B2/en
Publication of JPWO2011002013A1 publication Critical patent/JPWO2011002013A1/en
Application granted granted Critical
Publication of JP5610161B2 publication Critical patent/JP5610161B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、リチウムイオン二次電池などの非水電解質二次電池電極に用いられる活物質、それを含むスラリー組成物、非水電解質二次電池用電極及び非水電解質二次電池に関する。   The present invention relates to an active material used for a nonaqueous electrolyte secondary battery electrode such as a lithium ion secondary battery, a slurry composition containing the active material, a nonaqueous electrolyte secondary battery electrode, and a nonaqueous electrolyte secondary battery.

近年、ノート型パソコン、携帯電話、ＰＤＡなどの携帯端末の普及が著しい。これら携帯端末の電源に用いられている二次電池には、リチウムイオン二次電池等の非水電解質二次電池（以下、単に「電池」ということがある。）が多用されている。携帯端末は、より快適な携帯性が求められ、小型化、薄型化、軽量化、高性能化が急速に進んだ。その結果、携帯端末は様々な場で利用されるようになっている。携帯端末の利用範囲の増大に伴って、その電源である電池に対しても、携帯端末に対するのと同様に小型化、薄型化、軽量化、高性能化が要求されている。   In recent years, portable terminals such as notebook personal computers, mobile phones, and PDAs have become widespread. Non-aqueous electrolyte secondary batteries such as lithium ion secondary batteries (hereinafter sometimes simply referred to as “batteries”) are frequently used as secondary batteries used for the power sources of these portable terminals. Mobile terminals are required to have more comfortable portability, and have rapidly become smaller, thinner, lighter, and higher in performance. As a result, portable terminals are used in various places. As the usage range of mobile terminals increases, the battery as the power source is also required to be smaller, thinner, lighter, and higher in performance as with mobile terminals.

電池の性能向上のために、電極、電解液、その他の電池部材の改良が検討されている。通常、電極は次のように製造される。すなわち、結着剤と液状媒体とを混合しバインダー組成物を得、これに活物質を加えて電極用スラリー組成物とし、得られた電極用スラリー組成物を集電体上に塗布、乾燥することにより活物質層を形成し製造される。   In order to improve battery performance, improvements to electrodes, electrolytes, and other battery members have been studied. Usually, an electrode is manufactured as follows. That is, a binder and a liquid medium are mixed to obtain a binder composition, and an active material is added thereto to form an electrode slurry composition. The obtained electrode slurry composition is applied onto a current collector and dried. Thus, an active material layer is formed and manufactured.

例えば、特許文献１には、リチウムイオン二次電池の安全性に関する問題を解決すべく、酸化防止剤を含んだポリマー樹脂溶液に電極を含浸させることが開示されており、ヒンダードアミン系の酸化防止剤とポリフッ化ビニリデン等のポリマー樹脂との混合溶液中に上記のような方法で製造した電極をディップコーティングした後、乾燥して電極表面に酸化防止剤の被覆処理をしている。   For example, Patent Document 1 discloses that a polymer resin solution containing an antioxidant is impregnated with an electrode in order to solve a problem related to safety of a lithium ion secondary battery, and a hindered amine-based antioxidant is disclosed. The electrode manufactured by the above method is dip-coated in a mixed solution of polymer resin such as polyvinylidene fluoride and the like, and then dried to coat the surface of the electrode with an antioxidant.

また、特許文献２には、正極における酸化反応時のセパレータの劣化反応を抑制するために、酸化防止剤を含む重合体をセパレータ上にコーティングする方法が開示されている。   Patent Document 2 discloses a method of coating a separator with a polymer containing an antioxidant in order to suppress the deterioration reaction of the separator during the oxidation reaction in the positive electrode.

ところで、４．２５Ｖ以上の高電圧の電池では、電解液が強い酸化環境にさらされ、正極の活性点で過酸化物中間体が生成され、電解液や電解質の分解によるガスが発生し、電池が膨らむといった安全性に関する問題があった。特許文献３には、この問題を解決すべく電解質中に酸化防止剤を添加することが開示されている。   By the way, in a battery having a high voltage of 4.25 V or more, the electrolytic solution is exposed to a strong oxidizing environment, a peroxide intermediate is generated at the active point of the positive electrode, and gas is generated due to decomposition of the electrolytic solution and the electrolyte. There were safety issues such as bulges. Patent Document 3 discloses that an antioxidant is added to the electrolyte in order to solve this problem.

特開平１０−１０６５４６号公報JP-A-10-106546 特開２００４−２５３３９３号公報（米国特許出願公開第２００４／１６６４１５号明細書）JP 2004-253393 A (US Patent Application Publication No. 2004/166415) 特開２００６−２０９９９５号公報JP 2006-209995 A

しかしながら、本発明者らの検討によれば、特許文献１〜３に記載されているような、酸化防止剤を、電極にコートしたり、電解質や電解液に添加したとしても、反応場である活物質表面には酸化防止剤が少量しか存在し得ないことがわかった。そして、そのために、正極表面での酸化反応抑制などには、十分な効果が得られないことがあることがわかった。   However, according to the study by the present inventors, even if an antioxidant as described in Patent Documents 1 to 3 is coated on an electrode or added to an electrolyte or an electrolytic solution, it is a reaction field. It has been found that only a small amount of antioxidant can be present on the active material surface. For this reason, it has been found that sufficient effects may not be obtained for suppressing the oxidation reaction on the surface of the positive electrode.

とくに細孔面積が大きい活物質では、活物質の細孔内部が活性点となるため、充放電時に細孔部分での電解液の分解が顕著に起こり、炭酸リチウムなどの分解生成物が細孔内部に堆積する。この分解物によって活物質内部へのリチウムイオンの受入れが阻害され、とくに低温での受入性が顕著に悪化することもわかった。   Particularly in an active material having a large pore area, the inside of the pores of the active material becomes an active point, so that the electrolytic solution is significantly decomposed in the pores during charge and discharge, and decomposition products such as lithium carbonate are present in the pores. Deposits inside. It was also found that this decomposition product inhibited the acceptance of lithium ions into the active material, and the acceptability particularly at low temperatures was significantly deteriorated.

本発明は、上記のような従来技術の問題点に鑑みてなされたものであって、細孔の多い活物質における、低温でのリチウム受入性を向上させて、リチウムイオン二次電池の寿命特性の劣化を抑える非水電解質二次電池電極用活物質を提供することを目的としている。   The present invention has been made in view of the above-described problems of the prior art, and improves the lithium acceptability at a low temperature in an active material having many pores, thereby improving the life characteristics of the lithium ion secondary battery. It aims at providing the active material for nonaqueous electrolyte secondary battery electrodes which suppresses deterioration of this.

また、本発明は、前記活物質を含む非水電解質二次電池電極用スラリー組成物、それを塗布乾燥してなる非水電解質二次電池用電極、及び非水電解質二次電池を提供することも目的としている。   The present invention also provides a slurry composition for a non-aqueous electrolyte secondary battery electrode containing the active material, a non-aqueous electrolyte secondary battery electrode formed by applying and drying the slurry composition, and a non-aqueous electrolyte secondary battery. Also aimed.

本発明者らは、上記課題を解決すべく鋭意検討の結果、スラリー組成物を調製する際、予め酸化防止剤で表面処理した活物質を用いることにより、酸化防止剤が活物質の細孔内部に保持され、充放電時に細孔内部の活性点における電解液の分解が抑制されることにより、低温でのリチウム受入性が向上することを見出した。   As a result of intensive studies to solve the above problems, the present inventors have used an active material that has been previously surface-treated with an antioxidant when preparing a slurry composition, so that the antioxidant is inside the pores of the active material. It was found that the lithium acceptability at a low temperature is improved by suppressing the decomposition of the electrolyte solution at the active point inside the pore during charging and discharging.

すなわち、上記課題を解決する本発明は、下記事項を要旨として含む。
（１）酸化防止剤によって表面処理されてなる非水電解質二次電池電極用活物質。That is, this invention which solves the said subject contains the following matter as a summary.
(1) An active material for a nonaqueous electrolyte secondary battery electrode that is surface-treated with an antioxidant.

（２）活物質中の酸化防止剤の含有量が０．０１〜１質量％である（１）に記載の非水電解質二次電池電極用活物質。 (2) The active material for a nonaqueous electrolyte secondary battery electrode according to (1), wherein the content of the antioxidant in the active material is 0.01 to 1% by mass.

（３）酸化防止剤がアミン系酸化防止剤、フェノール系酸化防止剤である（１）または（２）に記載の非水電解質二次電池電極用活物質。 (3) The active material for a nonaqueous electrolyte secondary battery electrode according to (1) or (2), wherein the antioxidant is an amine-based antioxidant or a phenol-based antioxidant.

（４）水銀圧入細孔体積が、０．１cｍ３／ｇ〜２．０cｍ３／ｇである活物質を表面処理したものである（１）〜（３）のいずれかに記載の非水電解質二次電池電極用活物質。(4) mercury intrusion pore volume, 0.1cm 3 /g~2.0cm 3 / g active material is one in which surface-treated with (1) to a non-aqueous electrolyte according to any one of (3) Active material for secondary battery electrode.

（５）上記（１）に記載の非水電解質二次電池電極用活物質、バインダー及び溶媒を含む非水電解質二次電池電極用スラリー組成物。 (5) A slurry composition for a nonaqueous electrolyte secondary battery electrode, comprising the active material for a nonaqueous electrolyte secondary battery electrode according to (1) above, a binder, and a solvent.

（６）バインダーのガラス転移点温度が２５℃以下である（５）に記載の非水電解質二次電池電極用スラリー。 (6) The slurry for a nonaqueous electrolyte secondary battery electrode according to (5), wherein the binder has a glass transition temperature of 25 ° C. or lower.

（７）集電体上に、（５）〜（６）に記載のリチウムイオン二次電池電極用スラリー組成物を塗布乾燥してなる非水電解質二次電池用電極。 (7) A nonaqueous electrolyte secondary battery electrode obtained by applying and drying the slurry composition for a lithium ion secondary battery electrode according to (5) to (6) on a current collector.

（８）正極、負極、セパレーター及び電解液を有してなり、正極及び負極の少なくとも一方が、上記（７）に記載の電極である非水電解質二次電池。 (8) A nonaqueous electrolyte secondary battery comprising a positive electrode, a negative electrode, a separator, and an electrolytic solution, wherein at least one of the positive electrode and the negative electrode is the electrode according to (7).

本発明によれば、活物質を酸化防止剤で処理することにより、酸化防止剤を活物質の細孔内部に存在させ、活物質の細孔内部における活性点を非活性化し、電解液の分解を抑制することが出来る。この結果、電解液由来のガスの発生を抑制することができ、さらに電解液の分解による電池容量の低下を抑制することができる。その結果、サイクル特性が向上し、また電解液の分解由来の炭酸リチウムなどの発生を抑制されるため活物質のリチウムイオンの受入性が向上する。   According to the present invention, by treating the active material with the antioxidant, the antioxidant is present inside the pores of the active material, the active sites inside the pores of the active material are deactivated, and the electrolytic solution is decomposed. Can be suppressed. As a result, generation of gas derived from the electrolytic solution can be suppressed, and further, a decrease in battery capacity due to decomposition of the electrolytic solution can be suppressed. As a result, cycle characteristics are improved, and generation of lithium carbonate derived from decomposition of the electrolytic solution is suppressed, so that the acceptability of lithium ions of the active material is improved.

以下に本発明を記述する。
本発明の非水電解質二次電池電極用活物質は、酸化防止剤で表面処理されたものである（以下、酸化防止剤で表面処理された活物質を、「活物質“Ａ”」と記載することがある。）。本発明において、表面処理とは、活物質の表面が酸化防止剤で被覆されることをいう。この表面は、活物質の細孔表面も含む。The present invention is described below.
The active material for a non-aqueous electrolyte secondary battery electrode of the present invention is surface-treated with an antioxidant (hereinafter, the active material surface-treated with an antioxidant is referred to as “active material“ A ””). To do.) In the present invention, the surface treatment means that the surface of the active material is coated with an antioxidant. This surface also includes the pore surface of the active material.

（表面処理前の活物質）
本発明において表面処理して用いる非水電解質二次電池電極用活物質の表面処理される前の活物質（以下、「活物質“ａ”」と記載することがある。）としては、電解質中で電位をかける事により可逆的にリチウムイオンを挿入放出できるものであれば良く、無機化合物でも有機化合物でも用いることが出来る。(Active material before surface treatment)
The active material before surface treatment of the active material for a nonaqueous electrolyte secondary battery electrode used after surface treatment in the present invention (hereinafter sometimes referred to as “active material“ a ””) is used in the electrolyte. Any material can be used as long as it can reversibly insert and release lithium ions by applying a potential.

非水電解質二次電池正極用の電極活物質（正極活物質）は、リチウムイオンの吸蔵放出可能な活物質が用いられ、無機化合物からなるものと有機化合物からなるものとに大別される。   The electrode active material (positive electrode active material) for the positive electrode of the non-aqueous electrolyte secondary battery uses an active material capable of occluding and releasing lithium ions, and is broadly classified into an inorganic compound and an organic compound.

無機化合物からなる正極活物質としては、遷移金属酸化物、遷移金属硫化物、リチウムと遷移金属とからなるリチウム含有複合金属酸化物などが挙げられる。上記の遷移金属としては、Ｔｉ、Ｖ、Ｃｒ、Ｍｎ、Ｆｅ、Ｃｏ、Ｎｉ、Ｃｕ、Ｍｏ等が使用される。   Examples of the positive electrode active material made of an inorganic compound include transition metal oxides, transition metal sulfides, and lithium-containing composite metal oxides made of lithium and a transition metal. Examples of the transition metal include Ti, V, Cr, Mn, Fe, Co, Ni, Cu, and Mo.

遷移金属酸化物としては、ＭｎＯ、ＭｎＯ２、Ｖ２Ｏ５、Ｖ６Ｏ１３、ＴｉＯ２、Ｃｕ２Ｖ２Ｏ３、非晶質Ｖ２Ｏ−Ｐ２Ｏ５、ＭｏＯ３、Ｖ２Ｏ５、Ｖ６Ｏ１３等が挙げられ、中でもサイクル安定性と容量の観点からＭｎＯ、Ｖ２Ｏ５、Ｖ６Ｏ１３、ＴｉＯ２が好ましい。Examples of transition metal oxides include MnO, MnO 2 , V 2 O 5 , V 6 O 13 , TiO 2 , Cu 2 V 2 O 3 , amorphous V 2 O—P 2 O 5 , MoO 3 , V 2 O. 5 , V 6 O 13 and the like. Among them, MnO, V 2 O 5 , V 6 O 13 and TiO 2 are preferable from the viewpoint of cycle stability and capacity.

遷移金属硫化物としては、ＴｉＳ２、ＴｉＳ３、非晶質ＭｏＳ２、ＦｅＳ等が挙げられる。The transition metal sulfide, TiS 2, TiS 3, amorphous MoS 2, FeS, and the like.

リチウム含有複合金属酸化物の構造は、特に限定はされず、層状構造、スピネル構造あるいは、オリビン型構造などが挙げられる。   The structure of the lithium-containing composite metal oxide is not particularly limited, and examples thereof include a layered structure, a spinel structure, and an olivine structure.

層状構造を有するリチウム含有複合金属酸化物としてはリチウム含有コバルト酸化物（ＬｉＣｏＯ２）、リチウム含有ニッケル酸化物（ＬｉＮｉＯ２）、Ｃｏ−Ｎｉ−Ｍｎの複合酸化物を主構造とするリチウム含有複合酸化物、Ｎｉ−Ｍｎ−Ａｌの複合酸化物を主構造とするリチウム含有複合酸化物、Ｎｉ−Ｃｏ−Ａｌの複合酸化物を主構造とするリチウム含有複合酸化物等が挙げられる。As the lithium-containing composite metal oxide having a layered structure, lithium-containing composite oxide mainly composed of lithium-containing cobalt oxide (LiCoO 2 ), lithium-containing nickel oxide (LiNiO 2 ), and Co—Ni—Mn composite oxide. Products, lithium-containing composite oxides having a Ni-Mn-Al composite oxide as a main structure, lithium-containing composite oxides having a Ni-Co-Al composite oxide as a main structure, and the like.

スピネル構造を有するリチウム含有複合金属酸化物としてはマンガン酸リチウム(ＬｉＭｎ２Ｏ４）やＭｎの一部を他の遷移金属で置換したＬｉ［Ｍｎ３／２Ｍ１／２］Ｏ４（ここでＭは、Ｃｒ、Ｆｅ、Ｃｏ、Ｎｉ、Ｃｕ等）等が挙げられる。Examples of lithium-containing composite metal oxides having a spinel structure include lithium manganate (LiMn 2 O 4 ) and Li [Mn 3/2 M 1/2 ] O 4 in which a part of Mn is substituted with another transition metal (here M may be Cr, Fe, Co, Ni, Cu or the like.

オリビン型構造を有するリチウム含有複合金属酸化物としてはＬｉＸＭＰＯ４（式中、Ｍは、Ｍｎ，Ｆｅ，Ｃｏ，Ｎｉ，Ｃｕ，Ｍｇ，Ｚｎ，Ｖ，Ｃａ，Ｓｒ，Ｂａ，Ｔｉ，Ａｌ，Ｓｉ，Ｂ及びＭｏから選ばれる少なくとも1種、０≦Ｘ≦２）であらわされるオリビン型燐酸リチウム化合物が挙げられる。この中でもＬｉＦｅＰＯ４、ＬｉＣｏＰＯ4は導電性が低いために微粒化させて用いることが多いことから、多く細孔を有することより、老化防止剤の表面処理によるサイクル特性向上効果が高くみられる。Li X MPO 4 (wherein, M is Mn, Fe, Co, Ni, Cu, Mg, Zn, V, Ca, Sr, Ba, Ti, Al, Li X MPO 4 as the lithium-containing composite metal oxide having an olivine structure) An olivine-type lithium phosphate compound represented by at least one selected from Si, B and Mo, 0 ≦ X ≦ 2) may be mentioned. Among them, LiFePO 4 and LiCoPO 4 are often used after being atomized due to their low conductivity. Therefore, the effect of improving the cycle characteristics due to the surface treatment of the anti-aging agent is high because they have many pores.

有機化合物としては、例えば、ポリアセチレン、ポリ−ｐ−フェニレンなどの導電性高分子を用いることもできる。   As the organic compound, for example, a conductive polymer such as polyacetylene or poly-p-phenylene can be used.

電気伝導性に乏しい、鉄系酸化物は、還元焼成時に炭素源物質を存在させることで、炭素材料で覆われた電極活物質として用いてもよい。また、これら化合物は、部分的に元素置換したものであってもよい。リチウムイオン二次電池用の正極活物質は、上記の無機化合物と有機化合物の混合物であってもよい。   An iron-based oxide having poor electrical conductivity may be used as an electrode active material covered with a carbon material by allowing a carbon source material to be present during reduction firing. These compounds may be partially element-substituted. The positive electrode active material for a lithium ion secondary battery may be a mixture of the above inorganic compound and organic compound.

非水電解質二次電池負極用の電極活物質（負極活物質）は、リチウムイオンの吸蔵放出可能な活物質が用いられ、主に炭素系活物質と非炭素系活物質とに大別される。   As the electrode active material (negative electrode active material) for the negative electrode of the nonaqueous electrolyte secondary battery, an active material capable of occluding and releasing lithium ions is used, and is mainly classified into a carbon-based active material and a non-carbon-based active material. .

炭素系活物質としては、炭素質材料と黒鉛質材料が挙げられる。炭素質材料とは一般的に炭素前駆体を２０００℃以下で熱処理（炭素化）された黒鉛化度の低い(結晶性の低い)炭素材料を示し、黒鉛質材料とは易黒鉛性炭素を２０００℃以上で熱処理することによって得られた黒鉛に近い高い結晶性を有する黒鉛質材料を示す。   Examples of the carbon-based active material include carbonaceous materials and graphite materials. The carbonaceous material generally indicates a carbon material having a low graphitization degree (low crystallinity) obtained by heat-treating (carbonizing) a carbon precursor at 2000 ° C. or lower. A graphitic material having high crystallinity close to that of graphite obtained by heat-treating at a temperature of 0 ° C. or higher is shown.

炭素質材料としては、熱処理温度によって炭素の構造を容易に変える易黒鉛性炭素とガラス状炭素に代表される非晶質構造に近い構造を持つ難黒鉛性炭素が挙げられる。易黒鉛性炭素としては石油や石炭から得られるタールピッチを原料とした炭素材料が挙げられ、例えば、コークス、メソカーボンマイクロビーズ（ＭＣＭＢ）、メソフェーズピッチ系炭素繊維、熱分解気相成長炭素繊維などが挙げられる。ＭＣＭＢとはピッチ類を４００℃前後で加熱する過程で生成したメソフェーズ小球体を分離抽出した炭素微粒子であり、メソフェーズピッチ系炭素繊維とは、前記メソフェーズ小球体が成長、合体して得られるメソフェーズピッチを原料とする炭素繊維である。   Examples of the carbonaceous material include graphitizable carbon that easily changes the carbon structure depending on the heat treatment temperature, and non-graphitizable carbon having a structure close to an amorphous structure typified by glassy carbon. Examples of graphitizable carbon include carbon materials made from tar pitch obtained from petroleum and coal, such as coke, mesocarbon microbeads (MCMB), mesophase pitch-based carbon fibers, pyrolytic vapor-grown carbon fibers, etc. Is mentioned. MCMB is a carbon fine particle obtained by separating and extracting mesophase spherules produced in the process of heating pitches at around 400 ° C., and mesophase pitch-based carbon fiber is a mesophase pitch obtained by growing and coalescing the mesophase spherules. Is a carbon fiber made from a raw material.

難黒鉛性炭素としては、フェノール樹脂焼成体、ポリアクリロニトリル系炭素繊維、擬等方性炭素、フルフリルアルコール樹脂焼成体（ＰＦＡ）などが挙げられる。   Examples of the non-graphitizable carbon include phenol resin fired bodies, polyacrylonitrile-based carbon fibers, pseudo-isotropic carbon, and furfuryl alcohol resin fired bodies (PFA).

黒鉛質材料としては天然黒鉛、人造黒鉛が上げられる。人造黒鉛としては、主に２８００℃以上で熱処理した人造黒鉛、ＭＣＭＢを２０００℃以上で熱処理した黒鉛化ＭＣＭＢ、メソフェーズピッチ系炭素繊維を２０００℃以上で熱処理した黒鉛化メソフェーズピッチ系炭素繊維などが負極活物質として利用される。   Examples of the graphite material include natural graphite and artificial graphite. Artificial graphite mainly includes artificial graphite heat-treated at 2800 ° C. or higher, graphitized MCMB heat-treated at 2000 ° C. or higher, graphitized mesophase pitch-based carbon fiber heat-treated at 2000 ° C. or higher. Used as an active material.

非炭素系活物質としては、リチウム金属を用いることができ、またリチウムと合金を形成する単体金属およびそれらの合金、及びそれらの酸化物や硫化物等が用いられる。   As the non-carbon-based active material, lithium metal can be used, and simple metals and alloys thereof forming an alloy with lithium, oxides and sulfides thereof, and the like are used.

リチウム合金を形成する単体金属及び合金としては、Ａｇ、Ａｌ、Ｂａ、Ｂｉ、Ｃｕ、Ｇａ、Ｇｅ、Ｉｎ、Ｎｉ、Ｐ、Ｐｂ、Ｓｂ、Ｓｉ、Ｓｎ、Ｓｒ、Ｚｎ等の金属を含有する化合物が挙げられる。それらの中でもケイ素（Ｓｉ）、スズ（Ｓｎ）または鉛（Ｐｂ）の単体金属若しくはこれら原子を含む合金、または、それらの金属の化合物が用いられる。   Examples of single metals and alloys forming lithium alloys include compounds containing metals such as Ag, Al, Ba, Bi, Cu, Ga, Ge, In, Ni, P, Pb, Sb, Si, Sn, Sr, and Zn. Is mentioned. Among these, silicon (Si), tin (Sn) or lead (Pb) simple metals, alloys containing these atoms, or compounds of these metals are used.

酸化物や硫化物としては、酸化物、炭化物、窒化物、珪化物、硫化物、燐化物等が挙げられる。それらの中でも酸化スズ、酸化マンガン、酸化チタン、酸化ニオブ、酸化バナジウム等の酸化物、Ｓｉ、Ｓｎ、ＰｂおよびＴｉ原子よりなる群から選ばれる金属元素を含むリチウム含有金属複合酸化物材料が用いられている。   Examples of oxides and sulfides include oxides, carbides, nitrides, silicides, sulfides, and phosphides. Among these, lithium-containing metal composite oxide materials containing a metal element selected from the group consisting of oxides such as tin oxide, manganese oxide, titanium oxide, niobium oxide, vanadium oxide, Si, Sn, Pb and Ti atoms are used. ing.

リチウム含有金属複合酸化物としては、更にＬｉｘＴｉｙＭｚＯ４で示されるリチウムチタン複合酸化物（０．７≦ｘ≦１．５、１．５≦ｙ≦２．３、０≦ｚ≦１．６、Ｍは、Ｎａ、Ｋ、Ｃｏ、Ａｌ、Ｆｅ、Ｔｉ、Ｍｇ、Ｃｒ、Ｇａ、Ｃｕ、ＺｎおよびＮｂ）が挙げられ、中でもＬｉ４／３Ｔｉ５／３Ｏ４、Ｌｉ１Ｔｉ２Ｏ４、Ｌｉ４／５Ｔｉ１１／５Ｏ４が用いられる。As the lithium-containing metal composite oxide, a lithium titanium composite oxide represented by Li x Ti y M z O 4 (0.7 ≦ x ≦ 1.5, 1.5 ≦ y ≦ 2.3, 0 ≦ z ≦ 1.6, M includes Na, K, Co, Al, Fe, Ti, Mg, Cr, Ga, Cu, Zn, and Nb), among which Li 4/3 Ti 5/3 O 4 , Li 1 Ti 2 O 4 and Li 4/5 Ti 11/5 O 4 are used.

これらの活物質の中でも活物質表面、特に細孔内部における電解液による反応が起こりやすく、サイクル特性の劣化が激しいリチウムイオン二次電池用電極活物質において本発明の酸化防止剤に表面処理による効果が大きい。またその中でも非水電解質二次電池用負極活物質表面における効果が大きいことから、活物質“ａ”としては非水電解質二次電池用負極活物質が最も好適である。   Among these active materials, the effect of surface treatment on the antioxidant of the present invention in an electrode active material for lithium ion secondary batteries, which is prone to reaction by the electrolytic solution on the active material surface, particularly in the pores, and whose cycle characteristics are severely deteriorated Is big. Of these, the active material “a” is most preferably a negative electrode active material for a nonaqueous electrolyte secondary battery because it has a large effect on the surface of the negative electrode active material for a nonaqueous electrolyte secondary battery.

本発明において用いられる活物質“ａ”としては、圧力４ｋＰａから４００ＭＰａまでの昇圧時における水銀圧入細孔体積が、０．１ｃｍ３／ｇ〜２．０ｃｍ３／ｇの範囲内であるものが好ましく、０．４ｃｍ３／ｇ〜１．５ｃｍ３／ｇの範囲内であるものがより好ましい。水銀圧入細孔体積が上記範囲にある処理前活物質“ａ”は、通常は直径０．０１〜１０μｍの細孔を活物質内部に有している。活物質“ａ”として、水銀圧入細孔体積が前記範囲内にあるものを用いることにより、活物質“ａ”を酸化防止剤で表面処理する際に、細孔内部へ酸化防止剤が入り込みやすくなり、活物質の細孔内部の活性点を非活性化し、低温リチウム受け入れ性が大幅に向上する。更には、後述するスラリー組成物を調製する際のバインダー量を少なくすることができ、電池の容量の低下を抑制できると共に、スラリー組成物を、塗布するのに適正な粘度に調製することが容易になる。前記細孔体積は水銀圧入法による細孔径分布測定により求めることができる。The active material "a" used in the present invention, mercury intrusion pore volume in the voltage step-up from the pressure 4kPa to 400MPa is, preferably has in the range of 0.1cm 3 /g~2.0cm 3 / g , it is more preferable in a range of 0.4cm 3 /g~1.5cm 3 / g. The pre-treatment active material “a” whose mercury intrusion pore volume is in the above range usually has pores having a diameter of 0.01 to 10 μm inside the active material. By using the active material “a” having a mercury intrusion pore volume within the above range, when the active material “a” is surface-treated with an antioxidant, the antioxidant easily enters the pores. Thus, the active sites inside the pores of the active material are deactivated, and the low-temperature lithium acceptability is greatly improved. Furthermore, it is possible to reduce the amount of binder when preparing a slurry composition to be described later, to suppress a decrease in the capacity of the battery, and to easily prepare the slurry composition to have an appropriate viscosity for application. become. The pore volume can be determined by measuring pore size distribution by mercury porosimetry.

本発明において、用いられる活物質“ａ”の粒子形状は、従来用いられるような、塊状、多面体状、球状、楕円球状、板状、針状、柱状等が用いられるが、中でも活物質内部に多く細孔が存在し、酸化防止剤を用いた表面処理によるリチウム受け入れ性向上効果が大きいことから、塊状、または一次粒子が凝集して、二次粒子を形成して成るものが好ましい。   In the present invention, the particle shape of the active material “a” used may be a lump shape, polyhedron shape, spherical shape, elliptical spherical shape, plate shape, needle shape, columnar shape, etc., as used conventionally. Since there are many pores and the effect of improving lithium acceptability by surface treatment using an antioxidant is large, it is preferable that the particles are agglomerated or formed by agglomerating primary particles to form secondary particles.

本発明において用いられる活物質“ａ”の比表面積は、０．１〜２０ｍ２/ｇの範囲内であるものが好ましく、０．５〜１０ｍ２/ｇの範囲内であるものがより好ましい。活物質“ａ”の比表面積が上記範囲であるものを用いることにより、酸化防止剤の添加効果が大きく見られる。更には、後述するスラリー組成物の作製時におけるバインダー量を少なくすることができ、電池容量の低下を抑制できると共に、後述するスラリー組成物を、塗布するのに適正な粘度に調製することが容易になる。The specific surface area of the active material "a" used in the present invention is preferably one in the range of 0.1 to 20 m 2 / g, it is more preferable in the range of 0.5 to 10 m 2 / g. By using a material having a specific surface area of the active material “a” within the above range, the effect of adding an antioxidant can be greatly seen. Furthermore, the amount of binder at the time of preparation of the slurry composition described later can be reduced, the decrease in battery capacity can be suppressed, and the slurry composition described later can be easily prepared to have an appropriate viscosity for application. become.

本発明において用いられる活物質“ａ”の粒子径は、通常１〜５０μｍ、好ましくは２〜３０μｍである。活物質“ａ”の粒子径が上記範囲にあることにより、後述するスラリー組成物を調製する際のバインダー量を少なくすることができ、電池の容量の低下を抑制できると共に、スラリー組成物を、塗布するのに適正な粘度に調製することが容易になる。   The particle diameter of the active material “a” used in the present invention is usually 1 to 50 μm, preferably 2 to 30 μm. When the particle diameter of the active material “a” is in the above range, the amount of the binder when preparing a slurry composition to be described later can be reduced, the decrease in battery capacity can be suppressed, It becomes easy to adjust the viscosity to be appropriate for application.

本発明においては、活物質“ａ”として、機械的改質法により表面に導電付与材を付着させたものも使用できる。   In the present invention, as the active material “a”, a material obtained by attaching a conductivity imparting material to the surface by a mechanical modification method can also be used.

（酸化防止剤）
本発明で用いる酸化防止剤としては、アミン系酸化防止剤、フェノール系酸化防止剤、キノン系酸化防止剤、有機リン系酸化防止剤、硫黄系酸化防止剤、フェノチアジン系酸化防止剤等が挙げられる。(Antioxidant)
Examples of the antioxidant used in the present invention include amine-based antioxidants, phenol-based antioxidants, quinone-based antioxidants, organic phosphorus-based antioxidants, sulfur-based antioxidants, and phenothiazine-based antioxidants. .

前記アミン系酸化防止剤としては、例えば、ビス（４−ｔ−ブチルフェニル）アミン、ポリ（２，２，４−トリメチル−１，２−ジヒドロキノリン）、６−エトキシ−１，２−ジヒドロ−２，２，４−トリメチルキノリン、ジフェニルアミンとアセトンとの反応物、１−（Ｎ−フェニルアミノ）−ナフタレン、ジフェニルアミン誘導体、ジアルキルジフェニルアミン類、Ｎ，Ｎ’−ジフェニル−ｐ−フェニレンジアミン、混合ジアリル−ｐ−フェニレンジアミン、Ｎ−フェニル−Ｎ’−イソプロピル−ｐ−フェニレンジアミン、Ｎ，Ｎ’−ジ−２−ナフチル−ｐ−フェニレンジアミン化合物等が挙げられる。   Examples of the amine-based antioxidant include bis (4-t-butylphenyl) amine, poly (2,2,4-trimethyl-1,2-dihydroquinoline), 6-ethoxy-1,2-dihydro- 2,2,4-trimethylquinoline, reaction product of diphenylamine and acetone, 1- (N-phenylamino) -naphthalene, diphenylamine derivative, dialkyldiphenylamines, N, N′-diphenyl-p-phenylenediamine, mixed diallyl- Examples thereof include p-phenylenediamine, N-phenyl-N′-isopropyl-p-phenylenediamine, and N, N′-di-2-naphthyl-p-phenylenediamine compound.

前記フェノール系酸化防止剤としては、３，５−ジ−ｔ−ブチル−４−ヒドロキシトルエン、ジブチルヒドロキシトルエン、２，２’−メチレンビス（６−ｔ−ブチル−４−メチルフェノール）、４，４’−ブチリデンビス（３−ｔ−ブチル−３−メチルフェノール）、４，４’−チオビス（６−ｔ−ブチル−３−メチルフェノール）、α−トコフェノール、２，２，４−トリメチル−６−ヒドロキシ−７−ｔ−ブチルクロマン、または分子量の比較的高いポリマー型フェノール等が挙げられる。   Examples of the phenolic antioxidant include 3,5-di-t-butyl-4-hydroxytoluene, dibutylhydroxytoluene, 2,2′-methylenebis (6-t-butyl-4-methylphenol), 4,4. '-Butylidenebis (3-t-butyl-3-methylphenol), 4,4'-thiobis (6-t-butyl-3-methylphenol), α-tocophenol, 2,2,4-trimethyl-6- Examples thereof include hydroxy-7-t-butylchroman and polymer type phenol having a relatively high molecular weight.

前記キノン系酸化防止剤としては、２，５−ジ−ｔ−ブチルハイドロキノン、２，５−ジ−ｔ−オクチルハイドロキノン、２，６−ジ−ｎ−ドデシルハイドロキノン、２−ｎ−ドデシル−５−クロロハイドロキノン、２−ｔ−オクチル−５−メチルハイドロキノンなどのハイドロキノン化合物が挙げられる。   Examples of the quinone antioxidant include 2,5-di-t-butylhydroquinone, 2,5-di-t-octylhydroquinone, 2,6-di-n-dodecylhydroquinone, 2-n-dodecyl-5 Examples include hydroquinone compounds such as chlorohydroquinone and 2-t-octyl-5-methylhydroquinone.

前記リン系酸化防止剤としては、例えば、トリフェニルホスファイト、ジフェニルイソデシルホスファイト、フェニルジイソデシルホスファイト、４，４’−ブチリデン−ビス（３−メチル−６−ｔ−ブチルフェニルジトリデシル）ホスファイト、サイクリックネオペンタンテトライルビス（オクタデシルホスファイト）、トリス（ノニルフェニルホスファイト）、トリス（モノ（またはジ）ノニルフェニル）ホスファイト、ジイソデシルペンタエリスリトールジホスファイト、９，１０−ジヒドロ−９−オキサ−１０−ホスファフェナントレン−１０−オキサイド、１０−（３，５−ジ−ｔ−ブチル−４−ヒドロキシベンジル）−９，１０−ジヒドロ−９−オキサ−１０−ホスファフェナントレン−１０−オキサイド、１０−デシロキシ−９，１０−ジヒドロ−９−オキサ−１０−ホスファフェナントレン−１０−オキサイド、トリス（２，４−ジ−ｔ−ブチルフェニル）ホスファイト、サイクリックネオペンタンテトライルビス（２，４−ジ−ｔ−ブチルフェニル）ホスファイト、サイクリックネオペンタンテトライルビス（２，６−ジ−ｔ−ブチル−４−メチルフェニル）ホスファイト、２，２−メチレンビス（４，６−ジ−ｔ−ブチルフェニル）オクチルホスファイト等が挙げられる。   Examples of the phosphorus antioxidant include triphenyl phosphite, diphenylisodecyl phosphite, phenyl diisodecyl phosphite, and 4,4′-butylidene-bis (3-methyl-6-tert-butylphenylditridecyl) phos. Phyto, cyclic neopentanetetrayl bis (octadecyl phosphite), tris (nonylphenyl phosphite), tris (mono (or di) nonylphenyl) phosphite, diisodecyl pentaerythritol diphosphite, 9,10-dihydro-9 -Oxa-10-phosphaphenanthrene-10-oxide, 10- (3,5-di-t-butyl-4-hydroxybenzyl) -9,10-dihydro-9-oxa-10-phosphaphenanthrene-10- Oxide, 10-decyloxy- , 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, tris (2,4-di-t-butylphenyl) phosphite, cyclic neopentanetetraylbis (2,4-di-t -Butylphenyl) phosphite, cyclic neopentanetetraylbis (2,6-di-t-butyl-4-methylphenyl) phosphite, 2,2-methylenebis (4,6-di-t-butylphenyl) Examples include octyl phosphite.

硫黄系酸化防止剤としては、ジラウリル−３，３’−チオジプロピオネート、ジステアリル−３，３’−トリジプロピオネートなどが挙げられる。
前記フェノチアジン系酸化防止剤としては、例えば、フェノチアジン、１０−メチルフェノチアジン、２−メチルフェノチアジン、２−トリフルオロメチルフェノチアジン等が挙げられる。Examples of the sulfur-based antioxidant include dilauryl-3,3′-thiodipropionate and distearyl-3,3′-tridipropionate.
Examples of the phenothiazine antioxidant include phenothiazine, 10-methylphenothiazine, 2-methylphenothiazine, and 2-trifluoromethylphenothiazine.

これらの酸化防止剤の中でも、電池のサイクル特性向上効果が大きいこと、また電池内部における電解液溶媒やリチウム塩、電極活物質の表面官能基等との反応が起こりにくいために表面処理による大幅な低温リチウム受け入れ性向上が見られること、などの観点により、アミン系酸化防止剤、フェノール系酸化防止剤、ハイドロキノン系酸化防止剤、又は有機リン系酸化防止剤が好ましい。さらに、電解液に対する溶解性が低く、電池内部においても電極活物質表面や細孔内部に存在し、活物質表面を非活性化させて、寿命特性及び低温リチウム受け入れ性のいずれの向上効果も非常に大きいことから、アミン系酸化防止剤又はフェノール系酸化防止剤がより好ましい。さらにその中でも、特に電解液への溶解性が非常に低く、また、活物質表面に吸着安定化し、電極内部に存在しやすいことからジフェニルアミン誘導体が特に好ましく、電解液に溶解しにくいという点で、電気吸引基、例えばイミド骨格を側鎖に持つジフェニルアミン誘導体が最も好ましい。また酸化防止剤は、これらを単独で用いても、２種類以上を混合して用いてもよい。   Among these antioxidants, the effect of improving the cycle characteristics of the battery is great, and the reaction with the electrolyte solvent, lithium salt, surface active group of the electrode active material, etc. hardly occurs in the battery, so that the surface treatment significantly increases. An amine antioxidant, a phenolic antioxidant, a hydroquinone antioxidant, or an organic phosphorus antioxidant is preferred from the viewpoint of improving low-temperature lithium acceptability. In addition, the solubility in the electrolyte is low, and it exists on the surface of the electrode active material and in the pores even inside the battery. By deactivating the active material surface, both the life characteristics and the low-temperature lithium acceptability are greatly improved. Therefore, an amine-based antioxidant or a phenol-based antioxidant is more preferable. Among them, in particular, the solubility in the electrolytic solution is very low, and the diphenylamine derivative is particularly preferable because it is adsorbed and stabilized on the active material surface and easily exists inside the electrode, and is difficult to dissolve in the electrolytic solution. Most preferred are electrophenyl groups, for example, diphenylamine derivatives having an imide skeleton in the side chain. Moreover, these antioxidants may be used alone or in combination of two or more.

（活物質の表面処理方法）
本発明では、酸化防止剤で表面処理された活物質“Ａ”を用いる。
酸化防止剤による活物質“ａ”の表面処理方法としては、気体状態にした酸化防止剤を活物質“ａ”の表面に接触させる気相処理法；溶媒に溶解又は分散させた酸化防止剤を活物質“ａ”の表面に接触させる液相処理法；活物質“ａ”に対して固体状の、好ましくは粉末状の酸化防止剤を接触させて表面処理を行う固相処理法等、様々な方法が挙げられる。(Surface treatment method of active material)
In the present invention, an active material “A” surface-treated with an antioxidant is used.
As a surface treatment method of the active material “a” with an antioxidant, a gas phase treatment method in which an antioxidant in a gaseous state is brought into contact with the surface of the active material “a”; an antioxidant dissolved or dispersed in a solvent is used. Various liquid phase treatment methods for bringing the surface of the active material “a” into contact; solid phase treatment methods in which a solid, preferably powdered, antioxidant is brought into contact with the active material “a” for surface treatment The method is mentioned.

気相処理法としては例えば、ＣＶＤ法などを応用して活物質表面に酸化防止剤の層を形成する方法が挙げられる。   Examples of the gas phase treatment method include a method of forming an antioxidant layer on the active material surface by applying a CVD method or the like.

液相処理法としては例えば、酸化防止剤及び活物質を溶媒に溶解又は分散させて活物質表面に酸化防止剤の層を形成させる湿式法、その他にスプレードライング法、真空蒸着法などが挙げられる。   Examples of the liquid phase treatment method include a wet method in which an antioxidant and an active material are dissolved or dispersed in a solvent to form an antioxidant layer on the surface of the active material, as well as a spray drying method and a vacuum deposition method. .

固相処理法としては例えば、活物質と酸化防止剤を分散機内に共存させ、これらに機械的力を加えて活物質表面に酸化防止剤を付着させるメカノケミカル法などが挙げられる。  Examples of the solid phase treatment method include a mechanochemical method in which an active material and an antioxidant coexist in a disperser, and a mechanical force is applied thereto to attach the antioxidant to the active material surface.

これらの方法の中でも、最も簡易な方法であり、また酸化防止剤を活物質の細孔内部に存在させることができ、かつ細孔内部の活性点を非活性化させることにより低温時のリチウム受け入れ性を向上させられることから、液相処理法が好ましく、その中でも酸化防止剤及び活物質を溶媒に溶解又は分散させて活物質表面に酸化防止剤の層を形成させる湿式法がさらに好ましい。   Among these methods, it is the simplest method, and an antioxidant can be present inside the pores of the active material, and the lithium accepts lithium at a low temperature by deactivating the active sites inside the pores. From the viewpoint of improving the properties, a liquid phase treatment method is preferable, and among them, a wet method in which an antioxidant and an active material are dissolved or dispersed in a solvent to form an antioxidant layer on the surface of the active material is more preferable.

液相処理法としては、１）溶媒中に、酸化防止剤及び活物質“ａ”を添加して分散させ、得られた分散液を乾燥する方法；２）溶媒中に、酸化防止剤を添加して分散させ、得られた分散液に活物質“ａ”を加え混合し、乾燥する方法；３）溶媒中に、活物質“ａ”を添加して分散させ、得られた分散液に酸化防止剤を加え混合し、乾燥する方法；４）酸化防止剤と活物質“ａ”と溶媒を一括で混合し、噴霧乾燥を行う方法などが挙げられる。   As the liquid phase treatment method, 1) a method in which an antioxidant and an active material “a” are added and dispersed in a solvent, and the resulting dispersion is dried; 2) an antioxidant is added in the solvent. The active material “a” is added to the resulting dispersion, mixed and dried; 3) The active material “a” is added and dispersed in the solvent, and the resulting dispersion is oxidized. A method of adding an inhibitor and mixing and drying; 4) a method of mixing the antioxidant, the active material “a” and a solvent in a lump and performing spray drying.

酸化防止剤と活物質“ａ”とを分散させる方法としては、特に制限されず、ホモジナイザー、ボールミル、サンドミル、ロールミル、および遊星式混練機などの分散混練装置を用いることができる。   The method for dispersing the antioxidant and the active material “a” is not particularly limited, and a dispersion kneader such as a homogenizer, a ball mill, a sand mill, a roll mill, and a planetary kneader can be used.

液相処理法により活物質“ａ”を表面処理する場合において、前記分散液中の固形分濃度は４０〜８０質量％であることが好ましく、５０〜７０質量％であることがより好ましい。前記分散液中の固形分濃度が前記範囲であることにより、活物質が良好に分散するので、酸化防止剤を活物質表面に均一に被覆させることができる。また、前記分散液中の酸化防止剤の濃度は、溶媒に対して固形分濃度で０．１〜１０質量％であることが好ましく、０．５〜５質量％であることが好ましく、１〜２質量％であることがより好ましい。酸化防止剤の濃度が前記範囲であることにより、酸化防止剤が溶媒に均一溶解するので、活物質表面に均一に被覆させることができる。   When surface-treating the active material “a” by the liquid phase treatment method, the solid content concentration in the dispersion is preferably 40 to 80% by mass, and more preferably 50 to 70% by mass. When the solid content concentration in the dispersion is within the above range, the active material is well dispersed, so that the surface of the active material can be uniformly coated with the antioxidant. Further, the concentration of the antioxidant in the dispersion is preferably 0.1 to 10% by mass, preferably 0.5 to 5% by mass in terms of solid content with respect to the solvent. It is more preferable that it is 2 mass%. When the concentration of the antioxidant is within the above range, the antioxidant is uniformly dissolved in the solvent, so that the active material surface can be uniformly coated.

乾燥温度と乾燥時間は、溶媒を完全に除去することができ、活物質の構造変化を起こさず、酸化防止剤を分解させない温度及び時間が好ましい。使用する溶媒の種類によって決まるが、乾燥温度は、酸化防止剤の分解温度未満が好ましく、５０〜３００℃が好ましく、１００〜２５０℃がより好ましい。乾燥時間は、１〜４８時間が好ましく、５〜２４時間が好ましい。乾燥は、常圧で行ってもよく、減圧下で行ってもよい。   The drying temperature and the drying time are preferably a temperature and a time at which the solvent can be completely removed, the structure of the active material is not changed, and the antioxidant is not decomposed. Although it depends on the type of solvent used, the drying temperature is preferably less than the decomposition temperature of the antioxidant, preferably 50 to 300 ° C, more preferably 100 to 250 ° C. The drying time is preferably 1 to 48 hours, more preferably 5 to 24 hours. Drying may be performed under normal pressure or under reduced pressure.

溶媒としては、酸化防止剤が溶解可能であれば特に制限はない。溶媒としては、水および有機溶媒のいずれも使用できる。有機溶媒としては、シクロペンタン、シクロヘキサンなどの環状脂肪族炭化水素類；トルエン、キシレン、エチルベンゼンなどの芳香族炭化水素類；アセトン、エチルメチルケトン、ジソプロピルケトン、シクロヘキサノン、メチルシクロヘキサン、エチルシクロヘキサンなどのケトン類；メチレンクロライド、クロロホルム、四塩化炭素など塩素系脂肪族炭化水素；酢酸エチル、酢酸ブチル、γ−ブチロラクトン、ε−カプロラクトンなどのエステル類；アセトニトリル、プロピオニトリルなどのアシロニトリル類；テトラヒドロフラン、エチレングリコールジエチルエーテルなどのエーテル類：メタノール、エタノール、イソプロパノール、エチレングリコール、エチレングリコールモノメチルエーテルなどのアルコール類；Ｎ−メチルピロリドン、Ｎ，Ｎ−ジメチルホルムアミドなどのアミド類があげられる。これらの溶媒は、単独で使用しても、これらを２種以上混合して混合溶媒として使用してもよい。これらの中でも特に、本発明に用いる酸化防止剤の溶解性に優れ、沸点が低く揮発性が高い溶媒が、短時間でかつ低温で除去できるので好ましい。アセトン、トルエン、シクロヘキサノン、シクロペンタン、テトラヒドロフラン、シクロヘキサン、キシレン、若しくはＮ−メチルピロリドン、またはこれらの混合溶媒が好ましく、特に活物質に濡れ易く、酸化防止剤が活物質に浸透しやすいため、Ｎ−メチルピロリドンが好ましい。   The solvent is not particularly limited as long as the antioxidant can be dissolved. As the solvent, either water or an organic solvent can be used. Examples of organic solvents include cycloaliphatic hydrocarbons such as cyclopentane and cyclohexane; aromatic hydrocarbons such as toluene, xylene, and ethylbenzene; acetone, ethyl methyl ketone, disopropyl ketone, cyclohexanone, methylcyclohexane, and ethylcyclohexane. Ketones; chlorinated aliphatic hydrocarbons such as methylene chloride, chloroform and carbon tetrachloride; esters such as ethyl acetate, butyl acetate, γ-butyrolactone and ε-caprolactone; acylonitriles such as acetonitrile and propionitrile; tetrahydrofuran; Ethers such as ethylene glycol diethyl ether: alcohols such as methanol, ethanol, isopropanol, ethylene glycol and ethylene glycol monomethyl ether; Amides such as loridone and N, N-dimethylformamide are exemplified. These solvents may be used alone, or two or more of these may be mixed and used as a mixed solvent. Among these, a solvent having excellent solubility of the antioxidant used in the present invention and having a low boiling point and high volatility is preferable because it can be removed in a short time and at a low temperature. Acetone, toluene, cyclohexanone, cyclopentane, tetrahydrofuran, cyclohexane, xylene, or N-methylpyrrolidone, or a mixed solvent thereof is preferable, and particularly N- is preferred because it easily wets the active material and the antioxidant easily penetrates the active material. Methyl pyrrolidone is preferred.

表面処理された活物質“Ａ”中の酸化防止剤の含有量は、好ましくは０．０１〜１．０質量％であり、更に好ましくは０．０１〜０．５質量％、特に好ましくは０．０１〜０．２質量％である。活物質“Ａ”中の酸化防止剤の含有量が前記範囲内であることにより、電池内部において酸化防止剤が電解液中に遊離することなく、活物質の細孔内部にも酸化防止剤を存在させることができ、細孔内部の活性点を非活性化させることによる低温時のリチウム受け入れ性の向上が大きい。   The content of the antioxidant in the surface-treated active material “A” is preferably 0.01 to 1.0% by mass, more preferably 0.01 to 0.5% by mass, and particularly preferably 0. 0.01 to 0.2% by mass. When the content of the antioxidant in the active material “A” is within the above range, the antioxidant is not released into the electrolyte inside the battery, and the antioxidant is also added inside the pores of the active material. The lithium acceptability at a low temperature can be greatly improved by deactivating the active sites inside the pores.

本発明の活物質“Ａ”中の酸化防止剤の含有量は、ガスクロマトグラフと質量分析装置を直結したＧＣ−ＭＳにより測定が可能である。活物質“Ａ”を、酸化防止剤と活物質“ａ”とに分離し、上記ＧＣ−ＭＳより、それぞれの質量を分析して比を出すことで活物質中の酸化防止剤の含有量を測定できる。   The content of the antioxidant in the active material “A” of the present invention can be measured by GC-MS in which a gas chromatograph and a mass spectrometer are directly connected. The active material “A” is separated into the antioxidant and the active material “a”, and the content of the antioxidant in the active material is determined by analyzing the mass of each from the GC-MS and calculating the ratio. It can be measured.

上記測定は、まず、酸化防止剤により表面処理された所定量の活物質“Ａ”と、該酸化防止剤を溶解しうる溶媒、例えばＮ−メチルピロリドンとを混合して混合液を得る。次に、これをろ過して、活物質“ａ”と、酸化防止剤を含む溶液とに分離する。そして、酸化防止剤を含む溶液中の酸化防止剤量をＧＣ−ＭＳにより検出する。前記検出に際しては、数種類の濃度で酸化防止剤を溶解させたＮ−メチルピロリドン溶液を準備しておき、これを用いて検量線を作成しておく。検出された溶液中の酸化防止剤量とろ過により分離された活物質“ａ”の重量比から、表面処理された活物質“Ａ”中の酸化防止剤の含有量を算出する。   In the measurement, first, a predetermined amount of the active material “A” surface-treated with an antioxidant and a solvent capable of dissolving the antioxidant, for example, N-methylpyrrolidone, are mixed to obtain a mixed solution. Next, this is filtered and separated into an active material “a” and a solution containing an antioxidant. Then, the amount of the antioxidant in the solution containing the antioxidant is detected by GC-MS. For the detection, an N-methylpyrrolidone solution in which an antioxidant is dissolved at several concentrations is prepared, and a calibration curve is prepared using this solution. The content of the antioxidant in the surface-treated active material “A” is calculated from the detected weight ratio of the antioxidant in the solution and the active material “a” separated by filtration.

（非水電解質二次電池電極用スラリー組成物）
本発明の非水電解質二次電池電極用スラリー組成物は、予め酸化防止剤で表面処理された非水電解質二次電池電極用活物質“Ａ”、バインダー及び溶媒を含む。(Slurry composition for non-aqueous electrolyte secondary battery electrode)
The slurry composition for a non-aqueous electrolyte secondary battery electrode of the present invention contains an active material “A” for a non-aqueous electrolyte secondary battery electrode that has been surface-treated with an antioxidant in advance, a binder, and a solvent.

（バインダー）
バインダーは、結着性を有するバインダー（重合体）粒子が水または有機溶媒に溶解または分散された溶液または分散液である（以下、これらを総称して「バインダー分散液」と記載することがある）。バインダー分散液は非水系であっても、水系であってもよい。バインダー分散液が水系の場合は、通常、水を分散媒とした重合体粒子分散液であり、例えば、後述するジエン系重合体粒子分散液、アクリル系重合体粒子分散液、フッ素系重合体粒子分散液、シリコン系重合体粒子分散液などが挙げられる。この中でも、活物質との結着性および得られる電極の強度や柔軟性に優れるため、ジエン系重合体粒子分散液又はアクリル系重合体粒子分散液が好ましい。活物質との結着性が高い為、電極の剥がれ等を生じにくい。その結果、長期サイクル時においても活物質表面の酸化防止剤が表面から脱離せずに、表面に酸化防止剤が存在していることにより、活物質表面の活性点を非活性化させリチウム受け入れ性を向上させる効果が持続する。その結果高いサイクル特性を示すことが出来る。(binder)
The binder is a solution or dispersion in which binder (polymer) particles having binding properties are dissolved or dispersed in water or an organic solvent (hereinafter, these may be collectively referred to as “binder dispersion”). ). The binder dispersion may be non-aqueous or aqueous. When the binder dispersion is aqueous, it is usually a polymer particle dispersion using water as a dispersion medium. For example, a diene polymer particle dispersion, an acrylic polymer particle dispersion, or a fluorine polymer particle described later. Examples thereof include a dispersion and a silicon-based polymer particle dispersion. Among these, a diene polymer particle dispersion or an acrylic polymer particle dispersion is preferable because it has excellent binding properties to the active material and the strength and flexibility of the obtained electrode. Because of its high binding properties with the active material, it is difficult for the electrode to peel off. As a result, the antioxidant on the surface of the active material does not desorb from the surface even during long-term cycles, and the presence of the antioxidant on the surface deactivates the active sites on the surface of the active material, thereby accepting lithium. The effect of improving is sustained. As a result, high cycle characteristics can be exhibited.

またバインダー分散液が非水系（分散媒として有機溶媒を用いたもの）の場合は、通常、ポリエチレン、ポリプロピレン、ポリイソブチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリフッ化ビニリデン、ポリテトラフルオロエチレン、ポリ酢酸ビニルポリビニルアルコールポリビニル、イソブチルエーテル、ポリアクリロニトリル、ポリメタアクリロニトリル、ポリメタクリル酸メチル、ポリアクリル酸メチル、ポリメタクリル酸エチル、ポリ酢酸アリル、ポリスチレンなどのビニル系重合体；ポリブタジエン、ポリイソプレンなどのジエン系重合体；ポリオキシメチレン、ポリオキシエチレン、ポリ環状チオエーテル、ポリジメチルシロキサンなど主鎖にヘテロ原子を含むエーテル系重合体；ポリラクトン、ポリ環状無水物、ポリエチレンテレフタレート、ポリカーボネートなどの縮合エステル系重合体；ナイロン６、ナイロン６６、ポリ−ｍ−フェニレンイソフタラミド、ポリ−ｐ−フェニレンテレフタラミド、ポリピロメリットイミドなどの縮合アミド系重合体などをＮ−メチルピロリドン（ＮＭＰ）に溶解させたものが挙げられる。   When the binder dispersion is non-aqueous (using an organic solvent as a dispersion medium), usually polyethylene, polypropylene, polyisobutylene, polyvinyl chloride, polyvinylidene chloride, polyvinylidene fluoride, polytetrafluoroethylene, polyacetic acid Vinyl-polyvinyl alcohol, vinyl, isobutyl ether, polyacrylonitrile, polymethacrylonitrile, polymethyl methacrylate, polymethyl acrylate, polyethyl methacrylate, polyallyl acetate, polystyrene and other vinyl polymers; polybutadiene, polyisoprene, and other diene polymers Polymer: Polyoxymethylene, polyoxyethylene, polycyclic thioether, polydimethylsiloxane, and other ether-based polymers containing a hetero atom in the main chain; polylactone, polycyclic anhydride, polyethylene N-terephthalate, polycarbonate, and other condensed ester polymers; Nylon 6, nylon 66, poly-m-phenylene isophthalamide, poly-p-phenylene terephthalamide, polypyromellitimide, and other condensed amide polymers -What was melt | dissolved in methylpyrrolidone (NMP) is mentioned.

ジエン系重合体粒子分散液とは、ブタジエン、イソプレンなどの共役ジエンを重合体してなる単量体単位を含む重合体の水分散液である。ジエン系重合体中の共役ジエンを重合してなる単量体単位の割合は通常４０重量％以上、好ましくは５０重量％以上、より好ましくは６０重量％以上である。重合体としては、ポリブタジエンやポリイソプレンなどの共役ジエンの単独重合体；共役ジエンと共重合可能な単量体との共重合体が挙げられる。前記共重合可能な単量体としては、アクリロニトリル、メタクリロニトリルなどのα，β−不飽和ニトリル化合物；アクリル酸、メタクリル酸などの不飽和カルボン酸類；スチレン、クロロスチレン、ビニルトルエン、ｔ−ブチルスチレン、ビニル安息香酸、ビニル安息香酸メチル、ビニルナフタレン、クロロメチルスチレン、ヒドロキシメチルスチレン、α−メチルスチレン、ジビニルベンゼン等のスチレン系単量体；エチレン、プロピレン等のオレフィン類；ブタジエン、イソプレン等のジエン系単量体；塩化ビニル、塩化ビニリデン等のハロゲン原子含有単量体； 酢酸ビニル、プロピオン酸ビニル、酪酸ビニル、安息香酸ビニル等のビニルエステル類；メチルビニルエーテル、エチルビニルエーテル、ブチルビエルエーテル等のビニルエーテル類；メチルビニルケトン、エチルビニルケトン、ブチルビニルケトン、ヘキシルビニルケトン、イソプロペニルビニルケトン等のビニルケトン類； Ｎ−ビニルピロリドン、ビニルピリジン、ビニルイミダゾール等の複素環含有ビニル化合物が挙げられる。   The diene polymer particle dispersion is an aqueous dispersion of a polymer containing monomer units formed by polymerizing a conjugated diene such as butadiene or isoprene. The proportion of monomer units obtained by polymerizing conjugated diene in the diene polymer is usually 40% by weight or more, preferably 50% by weight or more, more preferably 60% by weight or more. Examples of the polymer include homopolymers of conjugated dienes such as polybutadiene and polyisoprene; and copolymers of monomers that are copolymerizable with conjugated dienes. Examples of the copolymerizable monomer include α, β-unsaturated nitrile compounds such as acrylonitrile and methacrylonitrile; unsaturated carboxylic acids such as acrylic acid and methacrylic acid; styrene, chlorostyrene, vinyltoluene, and t-butyl. Styrene monomers such as styrene, vinyl benzoic acid, methyl vinyl benzoate, vinyl naphthalene, chloromethyl styrene, hydroxymethyl styrene, α-methyl styrene, divinylbenzene; olefins such as ethylene, propylene; butadiene, isoprene, etc. Diene monomers; halogen atom-containing monomers such as vinyl chloride and vinylidene chloride; vinyl esters such as vinyl acetate, vinyl propionate, vinyl butyrate, vinyl benzoate; methyl vinyl ether, ethyl vinyl ether, butyl vinyl ether, etc. Vinylue Ethers; vinyl ketones such as methyl vinyl ketone, ethyl vinyl ketone, butyl vinyl ketone, hexyl vinyl ketone, and isopropenyl vinyl ketone; and heterocyclic ring-containing vinyl compounds such as N-vinyl pyrrolidone, vinyl pyridine, and vinyl imidazole.

アクリル系重合体粒子分散液とは、アクリル酸エステルおよび／またはメタクリル酸エステルを重合してなる単量体単位を含む重合体の水分散液である。アクリル酸エステルおよび／またはメタクリル酸エステルを重合してなる単量体単位の割合は、通常４０重量％以上、好ましくは５０重量％以上、より好ましくは６０重量％以上である。重合体としては、アクリル酸エステル及び／又はメタクリル酸エステルの単独重合体、これと共重合可能な単量体との共重合体が挙げられる。前記共重合可能な単量体としては、アクリル酸、メタクリル酸、イタコン酸、フマル酸などの不飽和カルボン酸類；エチレングリコールジメタクリレート、ジエチレングリコールジメタクリレート、トリメチロールプロパントリアクリレートなどの２つ以上の炭素−炭素二重結合を有するカルボン酸エステル類；スチレン、クロロスチレン、ビニルトルエン、ｔ−ブチルスチレン、ビニル安息香酸、ビニル安息香酸メチル、ビニルナフタレン、クロロメチルスチレン、ヒドロキシメチルスチレン、α−メチルスチレン、ジビニルベンゼン等のスチレン系単量体；アクリルアミド、Ｎ−メチロールアクエイルアミド、アクリルアミド−２−メチルプロパンスルホン酸などのアミド系単量体；アクリロニトリル、メタクリロニトリルなどのα，β−不飽和ニトリル化合物；エチレン、プロピレン等のオレフィン類；ブタジエン、イソプレン等のジエン系単量体；塩化ビニル、塩化ビニリデン等のハロゲン原子含有単量体； 酢酸ビニル、プロピオン酸ビニル、酪酸ビニル、安息香酸ビニル等のビニルエステル類；メチルビニルエーテル、エチルビニルエーテル、ブチルビエルエーテル等のビニルエーテル類；メチルビニルケトン、エチルビニルケトン、ブチルビニルケトン、ヘキシルビニルケトン、イソプロペニルビニルケトン等のビニルケトン類； Ｎ−ビニルピロリドン、ビニルピリジン、ビニルイミダゾール等の複素環含有ビニル化合物が挙げられる。   The acrylic polymer particle dispersion is an aqueous dispersion of a polymer containing monomer units obtained by polymerizing an acrylic ester and / or a methacrylic ester. The proportion of monomer units obtained by polymerizing acrylic acid ester and / or methacrylic acid ester is usually 40% by weight or more, preferably 50% by weight or more, more preferably 60% by weight or more. Examples of the polymer include homopolymers of acrylic acid esters and / or methacrylic acid esters, and copolymers with monomers copolymerizable therewith. Examples of the copolymerizable monomer include unsaturated carboxylic acids such as acrylic acid, methacrylic acid, itaconic acid, and fumaric acid; two or more carbons such as ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, and trimethylolpropane triacrylate. -Carboxylic acid ester having a carbon double bond; styrene, chlorostyrene, vinyl toluene, t-butyl styrene, vinyl benzoic acid, vinyl benzoate methyl, vinyl naphthalene, chloromethyl styrene, hydroxymethyl styrene, α-methyl styrene, Styrene monomers such as divinylbenzene; Amide monomers such as acrylamide, N-methylol aquaylamide, and acrylamide-2-methylpropanesulfonic acid; α, β- such as acrylonitrile and methacrylonitrile Saturated nitrile compounds; olefins such as ethylene and propylene; diene monomers such as butadiene and isoprene; monomers containing halogen atoms such as vinyl chloride and vinylidene chloride; vinyl acetate, vinyl propionate, vinyl butyrate, vinyl benzoate Vinyl esters such as methyl vinyl ether, ethyl vinyl ether, and butyl vinyl ether; vinyl ketones such as methyl vinyl ketone, ethyl vinyl ketone, butyl vinyl ketone, hexyl vinyl ketone, and isopropenyl vinyl ketone; N-vinyl pyrrolidone, Heterocycle-containing vinyl compounds such as vinylpyridine and vinylimidazole can be mentioned.

正極用バインダーとしては、充電における耐酸化性に優れる点、バインダー自身の分解等が起こらずサイクル特性の低下等が見られないことと、バインダーが電解液に適度に膨潤し、Ｌｉイオンが伝導しやすくなり、Ｌｉの受入特性に優れる点で、重合体主鎖に不飽和結合を有しない飽和型重合体の分散体であるアクリル系重合体粒子分散液が最も好ましい。   As the binder for the positive electrode, it is excellent in oxidation resistance during charging, the binder itself is not decomposed and the cycle characteristics are not deteriorated, the binder is appropriately swollen in the electrolyte, and Li ions are conducted. An acrylic polymer particle dispersion, which is a dispersion of a saturated polymer that does not have an unsaturated bond in the polymer main chain, is most preferable in that it is easy to obtain and has excellent Li acceptance characteristics.

バインダー分散液は、水を分散媒とした水系バインダーであってもよく、また有機溶剤を分散媒とした非水系バインダーであってもよいが、非水系バインダーを用いると活物質に表面処理された酸化防止剤が溶解し、本発明の効果が得られない場合があるため、水系バインダーが好ましく用いられる。   The binder dispersion may be an aqueous binder using water as a dispersion medium, or may be a non-aqueous binder using an organic solvent as a dispersion medium. However, when a non-aqueous binder is used, the active material is surface-treated. Since the antioxidant is dissolved and the effects of the present invention may not be obtained, an aqueous binder is preferably used.

水系バインダーは、例えば、上記単量体を水中で乳化重合することにより製造できる。また、非水系バインダーは、前記水系バインダーを有機溶媒で置換することにより製造できる。バインダー分散液中のバインダー粒子の平均粒径は、５０ｎｍ〜５００ｎｍが好ましく、７０ｎｍ〜４００ｎｍがさらに好ましい。平均粒径がこの範囲であると得られる電極の強度および柔軟性が良好となる。   The aqueous binder can be produced, for example, by emulsion polymerization of the monomer in water. The non-aqueous binder can be produced by replacing the aqueous binder with an organic solvent. The average particle size of the binder particles in the binder dispersion is preferably 50 nm to 500 nm, and more preferably 70 nm to 400 nm. When the average particle size is within this range, the strength and flexibility of the obtained electrode are good.

本発明において、バインダーのガラス転移温度は、２５℃以下であることが好ましく、より好ましくは−１００℃〜＋２５℃、更に好ましくは−８０℃〜＋１０℃、最も好ましくは−８０℃〜０℃である。バインダーのガラス転移温度が、前記範囲であることにより、電極の柔軟性、結着性及び捲回性、活物質層と集電体層との密着性などの特性が高度にバランスされ好適であり、また活物質表面がバインダーに被覆されている状態を保持できるため、極板プレス工程における活物質からの酸化防止剤及びバインダーの剥がれを抑制することができる。   In the present invention, the glass transition temperature of the binder is preferably 25 ° C. or less, more preferably −100 ° C. to + 25 ° C., still more preferably −80 ° C. to + 10 ° C., and most preferably −80 ° C. to 0 ° C. is there. When the glass transition temperature of the binder is within the above range, characteristics such as flexibility, binding and winding properties of the electrode, and adhesion between the active material layer and the current collector layer are highly balanced and suitable. Moreover, since the state in which the active material surface is coated with the binder can be maintained, peeling of the antioxidant and the binder from the active material in the electrode plate pressing step can be suppressed.

本発明の電極用スラリー組成物における、表面処理されてなる活物質“Ａ”及びバインダーの合計含有量は、スラリー１００質量部に対して、好ましくは１０〜９０質量部であり、さらに好ましくは３０〜８０質量部である。また表面処理されてなる活物質“Ａ”に対するバインダーの含有量（固形分相当量）は、活物質“Ａ”１００質量部に対して、好ましくは０．１〜５質量部であり、さらに好ましくは０．５〜２質量部である。電極用スラリー組成物における表面処理されてなる活物質“Ａ”及びバインダーの合計含有量およびバインダーの含有量が、前記範囲であると得られるスラリー組成物の粘度が適正化され、塗工を円滑に行えるようになり、また得られた極板の抵抗が高くなることなく、十分な密着強度が得られる。その結果、極板プレス工程における活物質からの酸化防止剤及びバインダーの剥がれを抑制することができる。   In the slurry composition for an electrode of the present invention, the total content of the surface-treated active material “A” and the binder is preferably 10 to 90 parts by mass, more preferably 30 with respect to 100 parts by mass of the slurry. ~ 80 parts by mass. Further, the binder content (solid content equivalent) relative to the surface-treated active material “A” is preferably 0.1 to 5 parts by mass, more preferably 100 parts by mass of the active material “A”. Is 0.5-2 parts by mass. If the total content of the active material “A” subjected to the surface treatment in the electrode slurry composition and the binder content and the binder content are within the above ranges, the viscosity of the resulting slurry composition is optimized, and the coating is smoothly performed. In addition, sufficient adhesion strength can be obtained without increasing the resistance of the obtained electrode plate. As a result, peeling of the antioxidant and binder from the active material in the electrode plate pressing step can be suppressed.

（溶媒）
電極用スラリーに用いる溶媒としては、上記固形分（酸化防止剤で表面処理された非水電解質二次電池電極用活物質“Ａ”、バインダー）、を均一に分散し得るものであれば特に制限されないが、酸化防止剤を溶解しない溶媒が好ましく用いられる。(solvent)
The solvent used for the electrode slurry is not particularly limited as long as it can uniformly disperse the above-described solid content (active material “A” for non-aqueous electrolyte secondary battery electrode surface-treated with an antioxidant, binder). Although not used, a solvent that does not dissolve the antioxidant is preferably used.

電極用スラリーに用いる溶媒としては、水および有機溶媒のいずれも使用できる。有機溶媒としては、シクロペンタン、シクロヘキサンなどの環状脂肪族炭化水素類；トルエン、キシレン、エチルベンゼンなどの芳香族炭化水素類；アセトン、エチルメチルケトン、ジソプロピルケトン、シクロヘキサノン、メチルシクロヘキサン、エチルシクロヘキサンなどのケトン類；メチレンクロライド、クロロホルム、四塩化炭素など塩素系脂肪族炭化水素；酢酸エチル、酢酸ブチル、γ−ブチロラクトン、ε−カプロラクトンなどのエステル類；アセトニトリル、プロピオニトリルなどのアシロニトリル類；テトラヒドロフラン、エチレングリコールジエチルエーテルなどのエーテル類：メタノール、エタノール、イソプロパノール、エチレングリコール、エチレングリコールモノメチルエーテルなどのアルコール類；Ｎ−メチルピロリドン、Ｎ，Ｎ−ジメチルホルムアミドなどのアミド類があげられる。   As the solvent used for the electrode slurry, either water or an organic solvent can be used. Examples of organic solvents include cycloaliphatic hydrocarbons such as cyclopentane and cyclohexane; aromatic hydrocarbons such as toluene, xylene, and ethylbenzene; acetone, ethyl methyl ketone, disopropyl ketone, cyclohexanone, methylcyclohexane, and ethylcyclohexane. Ketones; chlorinated aliphatic hydrocarbons such as methylene chloride, chloroform and carbon tetrachloride; esters such as ethyl acetate, butyl acetate, γ-butyrolactone and ε-caprolactone; acylonitriles such as acetonitrile and propionitrile; tetrahydrofuran; Ethers such as ethylene glycol diethyl ether: alcohols such as methanol, ethanol, isopropanol, ethylene glycol and ethylene glycol monomethyl ether; Amides such as loridone and N, N-dimethylformamide are exemplified.

これらの溶媒は、単独で使用しても、これらを２種以上混合して混合溶媒として使用してもよい。これらの中でも沸点が低く揮発性が高い溶媒が、短時間でかつ低温で除去できるので好ましい。具体的には、アセトン、トルエン、シクロヘキサノン、シクロペンタン、テトラヒドロフラン、シクロヘキサン、キシレン、水、若しくはＮ−メチルピロリドン、またはこれらの混合溶媒が好ましい。更に、活物質の表面処理に用いた酸化防止剤を溶解せずに、活物質中の酸化防止剤量を維持する観点から、特に水が好ましい。   These solvents may be used alone, or two or more of these may be mixed and used as a mixed solvent. Among these, a solvent having a low boiling point and high volatility is preferable because it can be removed at a low temperature in a short time. Specifically, acetone, toluene, cyclohexanone, cyclopentane, tetrahydrofuran, cyclohexane, xylene, water, N-methylpyrrolidone, or a mixed solvent thereof is preferable. Furthermore, water is particularly preferable from the viewpoint of maintaining the amount of antioxidant in the active material without dissolving the antioxidant used for the surface treatment of the active material.

（増粘剤）
本発明の電極用スラリー組成物においては、さらに増粘剤を含有してもよい。増粘剤としては、カルボキシメチルセルロース、メチルセルロース、ヒドロキシプロピルセルロースなどのセルロース系ポリマーおよびこれらのアンモニウム塩並びにアルカリ金属塩；（変性）ポリ（メタ）アクリル酸およびこれらのアンモニウム塩並びにアルカリ金属塩；（変性）ポリビニルアルコール、アクリル酸又はアクリル酸塩とビニルアルコールの共重合体、無水マレイン酸又はマレイン酸もしくはフマル酸とビニルアルコールの共重合体などのポリビニルアルコール類；ポリエチレングリコール、ポリエチレンオキシド、ポリビニルピロリドン、変性ポリアクリル酸、酸化スターチ、リン酸スターチ、カゼイン、各種変性デンプンなどが挙げられ、好ましくはカルボキシメチルセルロースのアンモニウム塩並びにアルカリ金属塩が用いられる。これは上記増粘剤がスラリー作製時に活物質の表面を均一に覆いやすいため、活物質表面の酸化防止剤の脱離を防ぐという効果があるためである。(Thickener)
The slurry composition for electrodes of the present invention may further contain a thickener. Examples of thickeners include cellulosic polymers such as carboxymethylcellulose, methylcellulose, hydroxypropylcellulose, and ammonium salts and alkali metal salts thereof; (modified) poly (meth) acrylic acid and ammonium salts and alkali metal salts thereof; ) Polyvinyl alcohols such as polyvinyl alcohol, copolymers of acrylic acid or acrylate and vinyl alcohol, maleic anhydride or copolymers of maleic acid or fumaric acid and vinyl alcohol; polyethylene glycol, polyethylene oxide, polyvinyl pyrrolidone, modified Examples include polyacrylic acid, oxidized starch, phosphoric acid starch, casein, various modified starches, and preferably ammonium salts and alkali metal salts of carboxymethyl cellulose. Used. This is because the above thickener tends to uniformly cover the surface of the active material at the time of slurry preparation, and thus has an effect of preventing the removal of the antioxidant on the surface of the active material.

増粘剤の配合量は、酸化防止剤で表面処理された活物質“Ａ”１００質量部に対して、０．５〜２．０質量部が好ましい。増粘剤の配合量がこの範囲であると、塗工性、集電体との密着性が良好である。本発明において、「（変性）ポリ」は「未変性ポリ」又は「変性ポリ」を意味し、「（メタ）アクリル」は、「アクリル」又は「メタアクリル」を意味する。   The blending amount of the thickener is preferably 0.5 to 2.0 parts by mass with respect to 100 parts by mass of the active material “A” surface-treated with the antioxidant. When the blending amount of the thickener is within this range, the coating property and the adhesion with the current collector are good. In the present invention, “(modified) poly” means “unmodified poly” or “modified poly”, and “(meth) acryl” means “acryl” or “methacryl”.

（導電材）
本発明の電極用スラリー組成物においては、導電材を含有してもよい。導電材としては、アセチレンブラック、ケッチェンブラック、カーボンブラック、グラファイト、気相成長カーボン繊維、およびカーボンナノチューブ等の導電性カーボンを使用することができる。導電材を用いることにより、活物質同士の電気的接触を向上させることができ、リチウムイオン二次電池に用いる場合に放電レート特性を改善することができる。導電材の配合量は、酸化防止剤で表面処理された活物質“Ａ”１００質量部に対して通常０〜２０質量部、好ましくは１〜１０質量部である。(Conductive material)
In the slurry composition for electrodes of the present invention, a conductive material may be contained. As the conductive material, conductive carbon such as acetylene black, ketjen black, carbon black, graphite, vapor-grown carbon fiber, and carbon nanotube can be used. By using the conductive material, the electrical contact between the active materials can be improved, and the discharge rate characteristics can be improved when used for a lithium ion secondary battery. The amount of the conductive material is usually 0 to 20 parts by mass, preferably 1 to 10 parts by mass with respect to 100 parts by mass of the active material “A” surface-treated with the antioxidant.

本発明の電極用スラリー組成物には、上記成分のほかに、さらに補強材、分散剤、レベリング剤、電解液分解抑制等の機能を有する電解液添加剤等の、他の成分が含まれていてもよく、後述の二次電池電極中に含まれていてもよい。これらは電池反応に影響を及ぼさないものであれば特に限られない。   In addition to the above-mentioned components, the electrode slurry composition of the present invention further contains other components such as a reinforcing material, a dispersing agent, a leveling agent, and an electrolyte additive having a function of inhibiting electrolyte decomposition. It may be included in a secondary battery electrode described later. These are not particularly limited as long as they do not affect the battery reaction.

補強材としては、各種の無機および有機の球状、板状、棒状または繊維状のフィラーが使用できる。補強材を用いることにより強靭で柔軟な電極を得ることができ、優れた長期サイクル特性を示すことができる。電極用スラリー組成物における導電性付与材や補強剤の使用量は、酸化防止剤で表面処理された活物質“Ａ”１００質量部に対して通常０．０１〜２０質量部、好ましくは１〜１０質量部である。前記範囲に含まれることにより、高い容量と高い負荷特性を示すことができる。   As the reinforcing material, various inorganic and organic spherical, plate-like, rod-like or fibrous fillers can be used. By using a reinforcing material, a tough and flexible electrode can be obtained, and excellent long-term cycle characteristics can be exhibited. The usage-amount of the electroconductivity imparting material and the reinforcing agent in the slurry composition for electrodes is usually 0.01 to 20 parts by mass, preferably 1 to 100 parts by mass with respect to 100 parts by mass of the active material “A” surface-treated with the antioxidant. 10 parts by mass. By being included in the range, high capacity and high load characteristics can be exhibited.

分散剤としてはアニオン性化合物、カチオン性化合物、非イオン性化合物、高分子化合物が例示される。分散剤は用いる電極活物質や導電剤に応じて選択される。電極用スラリー組成物中の分散剤の含有割合は、酸化防止剤で表面処理された活物質“Ａ”１００質量部に対して０．０１〜１０質量部であることが好ましい。分散剤量が上記範囲であることによりスラリーの安定性に優れ、平滑な電極を得ることができ、高い電池容量を示すことができる。   Examples of the dispersant include an anionic compound, a cationic compound, a nonionic compound, and a polymer compound. A dispersing agent is selected according to the electrode active material and electrically conductive agent to be used. It is preferable that the content rate of the dispersing agent in the slurry composition for electrodes is 0.01-10 mass parts with respect to 100 mass parts of active material "A" surface-treated with antioxidant. When the amount of the dispersant is in the above range, the slurry has excellent stability, a smooth electrode can be obtained, and a high battery capacity can be exhibited.

レベリング剤としてはアルキル系界面活性剤、シリコン系界面活性剤、フッ素系界面活性剤、金属系界面活性剤などの界面活性剤が挙げられる。前記界面活性剤を混合することにより、塗工時に発生するはじきを防止したり、電極の平滑性を向上させることができる。電極用スラリー組成物中のレベリング剤の含有割合は、酸化防止剤で表面処理された活物質“Ａ”１００質量部に対して、好ましくは０．０１〜１０質量部である。レベリング剤が上記範囲であることにより電極作製時の生産性、平滑性及び電池特性に優れる。   Examples of the leveling agent include surfactants such as alkyl surfactants, silicon surfactants, fluorine surfactants, and metal surfactants. By mixing the surfactant, it is possible to prevent the repelling that occurs during coating or to improve the smoothness of the electrode. The content ratio of the leveling agent in the electrode slurry composition is preferably 0.01 to 10 parts by mass with respect to 100 parts by mass of the active material “A” surface-treated with the antioxidant. When the leveling agent is within the above range, the productivity, smoothness, and battery characteristics during electrode production are excellent.

電解液添加剤としては、電極用スラリー組成物中及び電解液中に使用されるビニレンカーボネートなどを用いることができる。電極用スラリー組成物中の電解液添加剤の含有割合は、酸化防止剤で表面処理された活物質“Ａ”１００質量部に対して、好ましくは０．０１〜１０質量部である。電解液添加剤が、上記範囲であることによりサイクル特性及び高温特性に優れる。その他には、フュームドシリカやフュームドアルミナなどのナノ微粒子が挙げられる。前記ナノ微粒子を混合することにより電極形成用スラリーのチキソ性をコントロールすることができ、さらにそれにより得られる電極のレベリング性を向上させることができる。電極用スラリー組成物中のナノ微粒子の含有割合は、酸化防止剤で表面処理された活物質“Ａ”１００質量部に対して、好ましくは０．０１〜１０質量部である。ナノ微粒子が上記範囲であることによりスラリー安定性、生産性に優れ、高い電池特性を示す。   As the electrolytic solution additive, vinylene carbonate used in the slurry composition for electrodes and in the electrolytic solution can be used. The content ratio of the electrolytic solution additive in the electrode slurry composition is preferably 0.01 to 10 parts by mass with respect to 100 parts by mass of the active material “A” surface-treated with the antioxidant. When the electrolytic solution additive is in the above range, the cycle characteristics and the high temperature characteristics are excellent. Other examples include nanoparticles such as fumed silica and fumed alumina. By mixing the nanoparticles, the thixotropy of the electrode forming slurry can be controlled, and the leveling property of the resulting electrode can be improved. The content ratio of the nano fine particles in the electrode slurry composition is preferably 0.01 to 10 parts by mass with respect to 100 parts by mass of the active material “A” surface-treated with the antioxidant. When the nanoparticles are in the above range, the slurry stability and productivity are excellent, and high battery characteristics are exhibited.

（非水電解質二次電池電極用スラリー組成物の製造方法）
非水電解質二次電池電極用スラリー組成物は、上記バインダー、酸化防止剤により表面処理されてなる活物質“Ａ”、溶媒および必要に応じ用いられる増粘剤、導電材等とを混合して得られる。(Method for producing slurry composition for nonaqueous electrolyte secondary battery electrode)
The slurry composition for a non-aqueous electrolyte secondary battery electrode is prepared by mixing the binder, the active material “A” surface-treated with an antioxidant, a solvent, a thickener used as necessary, a conductive material, and the like. can get.

混合法は特に限定はされないが、例えば、撹拌式、振とう式、および回転式などの混合装置を使用した方法が挙げられる。また、ホモジナイザー、ボールミル、サンドミル、ロールミル、および遊星式混練機などの分散混練装置を使用した方法が挙げられる。   The mixing method is not particularly limited, and examples thereof include a method using a mixing apparatus such as a stirring type, a shaking type, and a rotary type. Further, a method using a dispersion kneader such as a homogenizer, a ball mill, a sand mill, a roll mill, and a planetary kneader can be used.

（電極）
本発明の非水電解質二次電池用電極は、集電体上に、本発明の電極用スラリー組成物を塗布乾燥してなる活物質層が結着してなる。(electrode)
The electrode for a non-aqueous electrolyte secondary battery of the present invention is formed by binding an active material layer formed by applying and drying the electrode slurry composition of the present invention on a current collector.

本発明の電極の製造方法は、特に限定されないが、例えば、前記電極用スラリー組成物を集電体の少なくとも片面、好ましくは両面に塗布、乾燥し、活物質層を形成する方法が挙げられる。   Although the manufacturing method of the electrode of this invention is not specifically limited, For example, the method of apply | coating and drying the said slurry composition for electrodes on at least one surface of an electrical power collector, Preferably both surfaces and forming an active material layer is mentioned.

電極用スラリー組成物を集電体上に塗布する方法は特に限定されない。例えば、ドクターブレード法、ディップ法、リバースロール法、ダイレクトロール法、グラビア法、エクストルージョン法、およびハケ塗り法などの方法が挙げられる。   The method for applying the electrode slurry composition onto the current collector is not particularly limited. Examples of the method include a doctor blade method, a dip method, a reverse roll method, a direct roll method, a gravure method, an extrusion method, and a brush coating method.

乾燥方法としては、例えば、温風、熱風、低湿風による乾燥、真空乾燥、（遠）赤外線や電子線などの照射による乾燥法が挙げられる。乾燥時間は通常５〜３０分であり、乾燥温度は通常４０〜１８０℃である。   Examples of the drying method include drying by warm air, hot air, low-humidity air, vacuum drying, and drying by irradiation with (far) infrared rays or electron beams. The drying time is usually 5 to 30 minutes, and the drying temperature is usually 40 to 180 ° C.

本発明の電極を製造するに際して、集電体上に上記電極用スラリー組成物を塗布乾燥後、金型プレスやロールプレスなどを用い、加圧処理により活物質層の空隙率を低くする工程を有することが好ましい。空隙率の好ましい範囲は５％〜１５％、より好ましくは７％〜１３％である。空隙率が高すぎると充電効率や放電効率が悪化する。空隙率が低すぎる場合は、電池の体積容量が低くなったり、活物質層が集電体から剥がれ易くなり電池の不良が発生し易いといった問題を生じる。   When manufacturing the electrode of the present invention, after applying and drying the slurry composition for an electrode on a current collector, a step of lowering the porosity of the active material layer by pressure treatment using a die press or a roll press, etc. It is preferable to have. The preferable range of the porosity is 5% to 15%, more preferably 7% to 13%. If the porosity is too high, charging efficiency and discharging efficiency are deteriorated. When the porosity is too low, there arises a problem that the volume capacity of the battery is lowered, or the active material layer is easily peeled off from the current collector, and the battery is liable to be defective.

さらに、バインダーとして硬化性の重合体を用いる場合は、硬化させることが好ましい。   Further, when a curable polymer is used as the binder, it is preferably cured.

本発明において、非水電解質二次電池用電極の活物質層の厚みは、正極、負極とも、通常５〜３００μｍであり、好ましくは３０〜２５０μｍである。電極厚みが上記範囲にあることにより、負荷特性及びサイクル特性共に高い特性を示す。   In the present invention, the thickness of the active material layer of the electrode for a nonaqueous electrolyte secondary battery is usually 5 to 300 μm, preferably 30 to 250 μm, for both the positive electrode and the negative electrode. When the electrode thickness is in the above range, both load characteristics and cycle characteristics are high.

（集電体）
本発明で用いる集電体は、電気導電性を有しかつ電気化学的に耐久性のある材料であれば特に制限されないが、耐熱性を有するため金属材料が好ましく、例えば、鉄、銅、アルミニウム、ニッケル、ステンレス鋼、チタン、タンタル、金、白金などが挙げられる。中でも、リチウムイオン二次電池の正極用としてはアルミニウムが特に好ましく、負極用としては銅が特に好ましい。集電体の形状は特に制限されないが、厚さ０．００１〜０．５ｍｍ程度のシート状のものが好ましい。集電体は、活物質層との接着強度を高めるため、予め粗面化処理して使用するのが好ましい。粗面化方法としては、機械的研磨法、電解研磨法、化学研磨法などが挙げられる。機械的研磨法においては、研磨剤粒子を固着した研磨布紙、砥石、エメリバフ、鋼線などを備えたワイヤーブラシ等が使用される。また、合剤の接着強度や導電性を高めるために、集電体表面に中間層を形成してもよい。(Current collector)
The current collector used in the present invention is not particularly limited as long as it is an electrically conductive and electrochemically durable material. However, a metal material is preferable because it has heat resistance. For example, iron, copper, aluminum Nickel, stainless steel, titanium, tantalum, gold, platinum and the like. Among these, aluminum is particularly preferable for the positive electrode of the lithium ion secondary battery, and copper is particularly preferable for the negative electrode. The shape of the current collector is not particularly limited, but a sheet shape having a thickness of about 0.001 to 0.5 mm is preferable. In order to increase the adhesive strength with the active material layer, the current collector is preferably used after roughening in advance. Examples of the roughening method include a mechanical polishing method, an electrolytic polishing method, and a chemical polishing method. In the mechanical polishing method, an abrasive cloth paper with a fixed abrasive particle, a grindstone, an emery buff, a wire brush provided with a steel wire or the like is used. Further, an intermediate layer may be formed on the current collector surface in order to increase the adhesive strength and conductivity of the mixture.

（非水電解質二次電池）
本発明の非水電解質二次電池は、正極、負極、セパレーター及び電解液を有してなり、正極及び負極の少なくとも一方が、前記非水電解質二次電池用電極である。(Non-aqueous electrolyte secondary battery)
The non-aqueous electrolyte secondary battery of the present invention includes a positive electrode, a negative electrode, a separator, and an electrolytic solution, and at least one of the positive electrode and the negative electrode is the non-aqueous electrolyte secondary battery electrode.

（電解液）
本発明に用いられる電解液は、特に限定されないが、例えば、非水系の溶媒に支持電解質としてリチウム塩を溶解したものが使用できる。リチウム塩としては、例えば、ＬｉＰＦ６、ＬｉＡｓＦ６、ＬｉＢＦ４、ＬｉＳｂＦ６、ＬｉＡｌＣｌ４、ＬｉＣｌＯ４、ＣＦ３ＳＯ３Ｌｉ、Ｃ４Ｆ９ＳＯ３Ｌｉ、ＣＦ３ＣＯＯＬｉ、（ＣＦ３ＣＯ）２ＮＬｉ、（ＣＦ３ＳＯ２）２ＮＬｉ、（Ｃ２Ｆ５ＳＯ２）ＮＬｉなどのリチウム塩が挙げられる。特に溶媒に溶けやすく高い解離度を示すＬｉＰＦ６、ＬｉＣｌＯ４、ＣＦ３ＳＯ３Ｌｉは好適に用いられる。これらは、単独、または２種以上を混合して用いることができる。支持電解質の量は、電解液に対して、通常１質量％以上、好ましくは５質量％以上、また通常は３０質量％以下、好ましくは２０質量％以下である。支持電解質の量が少なすぎても多すぎてもイオン導電度は低下し電池の充電特性、放電特性が低下する。(Electrolyte)
The electrolytic solution used in the present invention is not particularly limited. For example, a solution obtained by dissolving a lithium salt as a supporting electrolyte in a non-aqueous solvent can be used. Examples of the lithium salt include LiPF 6 , LiAsF 6 , LiBF 4 , LiSbF 6 , LiAlCl 4 , LiClO 4 , CF 3 SO 3 Li, C 4 F 9 SO 3 Li, CF 3 COOLi, (CF 3 CO) 2 NLi , (CF 3 SO 2 ) 2 NLi, (C 2 F 5 SO 2 ) NLi, and other lithium salts. In particular, LiPF 6 , LiClO 4 , and CF 3 SO 3 Li that are easily soluble in a solvent and exhibit a high degree of dissociation are preferably used. These can be used alone or in admixture of two or more. The amount of the supporting electrolyte is usually 1% by mass or more, preferably 5% by mass or more, and usually 30% by mass or less, preferably 20% by mass or less, with respect to the electrolytic solution. If the amount of the supporting electrolyte is too small or too large, the ionic conductivity is lowered, and the charging characteristics and discharging characteristics of the battery are degraded.

電解液に使用する溶媒としては、支持電解質を溶解させるものであれば特に限定されないが、通常、ジメチルカーボネート（ＤＭＣ）、エチレンカーボネート（ＥＣ）、ジエチルカーボネート（ＤＥＣ）、プロピレンカーボネート（ＰＣ）、ブチレンカーボネート（ＢＣ）、およびメチルエチルカーボネート（ＭＥＣ）などのアルキルカーボネート類；γ−ブチロラクトン、ギ酸メチルなどのエステル類、１，２−ジメトキシエタン、およびテトラヒドロフランなどのエーテル類；スルホラン、およびジメチルスルホキシドなどの含硫黄化合物類；が用いられる。特に高いイオン伝導性が得易く、使用温度範囲が広いため、ジメチルカーボネート、エチレンカーボネート、プロピレンカーボネート、ジエチルカーボネート、メチルエチルカーボネートが好ましい。これらは、単独、または２種以上を混合して用いることができる。   The solvent used in the electrolytic solution is not particularly limited as long as it can dissolve the supporting electrolyte. Usually, dimethyl carbonate (DMC), ethylene carbonate (EC), diethyl carbonate (DEC), propylene carbonate (PC), butylene. Alkyl carbonates such as carbonate (BC) and methyl ethyl carbonate (MEC); esters such as γ-butyrolactone and methyl formate; ethers such as 1,2-dimethoxyethane and tetrahydrofuran; sulfolane and dimethyl sulfoxide Sulfur-containing compounds are used. In particular, dimethyl carbonate, ethylene carbonate, propylene carbonate, diethyl carbonate, and methyl ethyl carbonate are preferable because high ion conductivity is easily obtained and the use temperature range is wide. These can be used alone or in admixture of two or more.

また前記電解液には添加剤を含有させて用いることも可能である。添加剤としてはビニレンカーボネート（ＶＣ）などのカーボネート系の化合物が好ましい。   Moreover, it is also possible to use the electrolyte solution by containing an additive. As the additive, carbonate compounds such as vinylene carbonate (VC) are preferable.

上記以外の電解液としては、ポリエチレンオキシド、ポリアクリロニトリルなどのポリマー電解質に電解液を含浸したゲル状ポリマー電解質や、硫化リチウム、ＬｉＩ、Ｌｉ３Ｎなどの無機固体電解質を挙げることができる。Examples of the electrolytic solution other than the above include a gel polymer electrolyte obtained by impregnating a polymer electrolyte such as polyethylene oxide and polyacrylonitrile with an electrolytic solution, and an inorganic solid electrolyte such as lithium sulfide, LiI, and Li 3 N.

（セパレーター）
セパレーターは気孔部を有する多孔性基材であって、使用可能なセパレーターとしては、（ａ）気孔部を有する多孔性セパレーター、（ｂ）片面または両面上に高分子コート層が形成された多孔性セパレーター、または（ｃ）無機セラミック粉末を含む多孔質の樹脂コート層が形成された多孔性セパレーターがあり、これらの非制限的な例としては、ポリプロピレン系、ポリエチレン系、ポリオレフィン系、またはアラミド系多孔性セパレーター、ポリビニリデンフルオリド、ポリエチレンオキシド、ポリアクリロニトリルまたはポリビニリデンフルオリドヘキサフルオロプロピレン共重合体などの固体高分子電解質用またはゲル状高分子電解質用の高分子フィルム、ゲル化高分子コート層がコートされたセパレーター、または無機フィラー、無機フィラー用分散剤からなる多孔膜層がコートされたセパレーターなどがある。(separator)
The separator is a porous substrate having pores, and usable separators include (a) a porous separator having pores, and (b) a porous material having a polymer coating layer formed on one or both sides. There is a separator or (c) a porous separator on which a porous resin coat layer containing an inorganic ceramic powder is formed. Non-limiting examples of these include polypropylene, polyethylene, polyolefin, or aramid porous Polymer film for solid polymer electrolyte or gel polymer electrolyte such as conductive separator, polyvinylidene fluoride, polyethylene oxide, polyacrylonitrile, or polyvinylidene fluoride hexafluoropropylene copolymer, and gelled polymer coating layer Coated separator or inorganic filler And the like porous membrane layer made of an inorganic filler dispersant is coated separator.

（電池の製造方法）
本発明の非水電解質二次電池の製造方法は、特に限定されない。例えば、負極と正極とをセパレータを介して重ね合わせ、これを電池形状に応じて巻く、折るなどして電池容器に入れ、電池容器に電解液を注入して封口する。さらに必要に応じてエキスパンドメタルや、ヒューズ、ＰＴＣ素子などの過電流防止素子、リード板などを入れ、電池内部の圧力上昇、過充放電の防止をすることもできる。電池の形状は、ラミネートセル型、コイン型、ボタン型、シート型、円筒型、角形、扁平型などいずれであってもよい。(Battery manufacturing method)
The method for producing the nonaqueous electrolyte secondary battery of the present invention is not particularly limited. For example, the negative electrode and the positive electrode are overlapped via a separator, and this is wound or folded according to the shape of the battery and placed in the battery container, and the electrolytic solution is injected into the battery container and sealed. Further, if necessary, an expanded metal, an overcurrent prevention element such as a fuse or a PTC element, a lead plate and the like can be inserted to prevent an increase in pressure inside the battery and overcharge / discharge. The shape of the battery may be any of a laminated cell type, a coin type, a button type, a sheet type, a cylindrical type, a square type, a flat type, and the like.

（実施例）
以下に、実施例を挙げて本発明を説明するが、本発明はこれに限定されるものではない。尚、本実施例における部および％は、特記しない限り質量基準である。実施例および比較例において、各種物性は以下のように評価した。(Example)
Hereinafter, the present invention will be described with reference to examples, but the present invention is not limited thereto. In addition, unless otherwise indicated, the part and% in a present Example are a mass reference | standard. In the examples and comparative examples, various physical properties were evaluated as follows.

（表面処理前の活物質の水銀圧入細孔体積の測定）
表面処理前の活物質“ａ”の細孔体積の測定は、水銀ポロシメーター（マイクロメリティクス製 オートポアＩＶ９５１０型）を使用して行った。表面処理前の活物質“ａ”０．２ｇをパウダー用セルに注入し、室温、真空下にて１０分間脱気して前処理をおこない、減圧下にて水銀を導入して圧力を変えて水銀圧入量を測定した。得られた水銀圧入曲線より表面処理前の活物質“ａ”の水銀圧入細孔体積を算出した。(Measurement of mercury intrusion pore volume of active material before surface treatment)
The pore volume of the active material “a” before the surface treatment was measured using a mercury porosimeter (Autopore IV9510 manufactured by Micromeritics). Inject 0.2 g of active material “a” before surface treatment into a powder cell, perform pretreatment by degassing for 10 minutes at room temperature under vacuum, introduce mercury under reduced pressure and change pressure The amount of mercury intrusion was measured. The mercury intrusion pore volume of the active material “a” before the surface treatment was calculated from the obtained mercury intrusion curve.

（表面処理された活物質“Ａ”中の酸化防止剤の含有量）
表面処理された活物質“Ａ”とＮ−メチルピロリドンとを混合して固形分濃度１０％の混合液を得る。次に、これをろ過して、活物質“ａ”と、酸化防止剤を含む溶液とに分離する。そして、ＧＣ−ＭＳにより、酸化防止剤を含む溶液中の酸化防止剤量を検出する。検出された溶液中の酸化防止剤量とろ過により分離された活物質“ａ”の重量比から、表面処理された活物質“Ａ”中の酸化防止剤の量を算出した。なお、前記検出に際しては、数種類の濃度で酸化防止剤を溶解させた溶液を準備しておき、これらを用いて検量線を作成した。(Content of antioxidant in the surface-treated active material “A”)
The surface-treated active material “A” and N-methylpyrrolidone are mixed to obtain a mixed solution having a solid content concentration of 10%. Next, this is filtered and separated into an active material “a” and a solution containing an antioxidant. Then, the amount of the antioxidant in the solution containing the antioxidant is detected by GC-MS. The amount of antioxidant in the surface-treated active material “A” was calculated from the weight ratio of the detected amount of antioxidant in the solution and the active material “a” separated by filtration. In the detection, a solution in which an antioxidant was dissolved at several concentrations was prepared, and a calibration curve was prepared using these solutions.

（ピール強度）
電極を、それぞれ、幅１ｃｍ×長さ１０ｃｍの矩形に切って試験片とし、電極活物質層面を上にして固定する。試験片の電極活物質層表面にセロハンテープを貼り付けた後、試験片の一端からセロハンテープを５０ｍｍ／分の速度で１８０°方向に引き剥がしたときの応力を測定した。測定を１０回行い、その平均値を求めてこれをピール強度とし、下記基準にて判定を行った。ピール強度が大きいほど、極板の密着性が良好であることを示す。
Ａ：６Ｎ／ｍ以上
Ｂ：５Ｎ／ｍ以上〜６Ｎ／ｍ未満
Ｃ：４Ｎ／ｍ以上〜５Ｎ／ｍ未満
Ｄ：３Ｎ／ｍ以上〜４Ｎ／ｍ未満
Ｅ：２Ｎ／ｍ以上〜３Ｎ／ｍ未満
Ｆ：２Ｎ／ｍ未満(Peel strength)
Each electrode is cut into a rectangular shape having a width of 1 cm and a length of 10 cm to form a test piece, which is fixed with the electrode active material layer surface facing up. After applying the cellophane tape to the surface of the electrode active material layer of the test piece, the stress was measured when the cellophane tape was peeled off from one end of the test piece in the 180 ° direction at a speed of 50 mm / min. The measurement was performed 10 times, the average value was obtained, and this was used as the peel strength. It shows that the adhesiveness of an electrode plate is so favorable that peel strength is large.
A: 6 N / m or more B: 5 N / m or more to less than 6 N / m C: 4 N / m or more to less than 5 N / m D: 3 N / m or more to less than 4 N / m E: 2 N / m or more to less than 3 N / m F: Less than 2 N / m

（充放電特性）
（１）リチウム受け入れ特性
得られたラミネートセル型電池を用いて、それぞれ２５℃で充放電レートを０．１Ｃとし、定電流定電圧充電法にて、４．２Ｖになるまで定電流で充電し、定電圧で充電する。充電後に３Ｖまで放電する充放電を各２回繰り返し、その後０℃に設定した恒温槽内で０．１Ｃで定電流定電圧充電を行った。この定電流定電圧充電における定電流時に得られた電池容量をリチウム受け入れ性の指標とし、下記の基準で判定した。この値が大きいほど、リチウム受入性のよい電池であることを示す。
Ａ：２２０ｍＡｈ／ｇ以上
Ｂ：２００ｍＡｈ／ｇ以上２２０ｍＡｈ／ｇ未満
Ｃ：１８０ｍＡｈ／ｇ以上２００ｍＡｈ／ｇ未満
Ｄ：１６０ｍＡｈ／ｇ以上１８０ｍＡｈ／ｇ未満
Ｅ：１４０ｍＡｈ／ｇ以上１６０ｍＡｈ／ｇ未満
Ｅ：１４０ｍＡｈ／ｇ未満(Charge / discharge characteristics)
(1) Lithium-accepting characteristics Using the obtained laminated cell type battery, the charge / discharge rate was set to 0.1 C at 25 ° C., respectively, and the battery was charged at a constant current until it reached 4.2 V by the constant current constant voltage charging method. Charge at a constant voltage. Charging / discharging to 3V after charging was repeated twice, and then constant current / constant voltage charging was performed at 0.1 C in a thermostat set to 0 ° C. The battery capacity obtained at the time of constant current in this constant current and constant voltage charge was used as an index of lithium acceptability, and the determination was made according to the following criteria. The larger this value, the better the battery.
A: 220 mAh / g or more B: 200 mAh / g or more and less than 220 mAh / g C: 180 mAh / g or more and less than 200 mAh / g D: 160 mAh / g or more and less than 180 mAh / g E: 140 mAh / g or more and less than 160 mAh / g E: 140 mAh / less than g

（２）充放電サイクル特性
得られたラミネートセル型電池を用いて、それぞれ２５℃で０．５Ｃの定電流定電圧充電法という方式で、４．２Ｖになるまで定電流で充電、その後定電圧で充電し、また０．５Ｃの定電流で３．０Ｖまで放電する充放電サイクルを行った。充放電サイクルは５０サイクルまで行い、初期放電容量に対する５０サイクル目の放電容量の比を容量維持率とし、下記の基準で判定した。この値が大きいほど繰り返し充放電による容量減が少ないことを示す。
Ａ：６０％以上
Ｂ：５５％以上６０％未満
Ｃ：５０％以上５５％未満
Ｄ：４５％以上５０％未満
Ｅ：４０％以上４５％未満
Ｅ：４０％未満(2) Charging / discharging cycle characteristics Using the obtained laminate cell type battery, charging at a constant current until reaching 4.2V by a method of constant current constant voltage charging at 25C at 25C, respectively, and then constant voltage And a charge / discharge cycle in which the battery was discharged to 3.0 V with a constant current of 0.5 C. The charge / discharge cycle was performed up to 50 cycles, and the ratio of the discharge capacity at the 50th cycle to the initial discharge capacity was defined as the capacity maintenance rate, and the following criteria were used. It shows that the capacity | capacitance reduction by repeated charging / discharging is so small that this value is large.
A: 60% or more B: 55% or more and less than 60% C: 50% or more and less than 55% D: 45% or more and less than 50% E: 40% or more and less than 45% E: Less than 40%

（充放電時ガス発生量）
得られたラミネートセル型電池を用いて上記方法と同様に、０．１Ｃで充電と放電を繰り返した後、もう一度０．１Ｃで充電したセルを８０℃の恒温槽に入れ、３０時間静置した。恒温槽にて３０時間静置後のセル厚み（ａ）と恒温槽に入れる前のセルの厚み（ｂ）を測定し、{（ａ）−（ｂ）}／（ａ）×１００（％）の値をセルの膨らみ率とし、下記の基準により判定する。このセルの膨らみ率をガス発生量の指標であり、セルの膨らみ率が小さいほど、ガス発生量が少ないことを示す。
Ａ：１０％未満
Ｂ：１０％以上２０％未満
Ｃ：２０％以上３０％未満
Ｄ：３０％以上４０％未満
Ｅ：４０％以上(Gas generation during charging / discharging)
In the same manner as in the above method, using the obtained laminated cell type battery, charging and discharging were repeated at 0.1 C, and then the cell charged at 0.1 C was again placed in a thermostatic bath at 80 ° C. and allowed to stand for 30 hours. . Measure the cell thickness (a) after standing for 30 hours in a thermostat and the thickness (b) of the cell before entering the thermostat, and {(a)-(b)} / (a) × 100 (%) Is determined by the following criteria. The expansion rate of the cell is an indicator of the amount of gas generation, and the smaller the expansion rate of the cell, the smaller the amount of gas generation.
A: Less than 10% B: 10% or more and less than 20% C: 20% or more and less than 30% D: 30% or more and less than 40% E: 40% or more

（実施例１）
（活物質の酸化防止剤による表面処理）
下記化学式１に示すジフェニルアミン誘導体の酸化防止剤０．０２部を、Ｎ−メチルピロリドン５０部に溶解させ、混合溶液を作製した。容器に、処理前の活物質“ａ”として水銀圧入細孔体積が０．９５cｍ３／ｇ、比表面積が３．８ｍ２／ｇである人造黒鉛１００部をいれ、次いで前記混合溶液を加えて、プラネタリーミキサーで１時間攪拌し、得られた混合物を１００℃で２４時間真空乾燥し、人造黒鉛の表面処理をおこなった。Example 1
(Surface treatment with active material antioxidant)
A mixed solution was prepared by dissolving 0.02 part of an antioxidant of a diphenylamine derivative represented by the following chemical formula 1 in 50 parts of N-methylpyrrolidone. Into a container, 100 parts of artificial graphite having a mercury intrusion pore volume of 0.95 cm 3 / g and a specific surface area of 3.8 m 2 / g as an active material “a” before treatment is added, and then the mixed solution is added. The mixture was stirred for 1 hour with a planetary mixer, and the resulting mixture was vacuum-dried at 100 ° C. for 24 hours to subject the artificial graphite to a surface treatment.

Figure 0005610161
Figure 0005610161

（負極の製造）
１％水溶液粘度が２０００ｍＰａ・ｓであるカルボキシメチルセルロース（ダイセル化学工業株式会社製「Ｄａｉｃｅｌ２２００」）を用いて、１％水溶液を調整した。(Manufacture of negative electrode)
A 1% aqueous solution was prepared using carboxymethylcellulose (“Daicel 2200” manufactured by Daicel Chemical Industries, Ltd.) having a 1% aqueous solution viscosity of 2000 mPa · s.

ディスパー付きのプラネタリーミキサーに、酸化防止剤で表面処理された人造黒鉛１００部を入れ、これに上記水溶液１００部を加え、イオン交換水で固形分濃度５３．５％に調整した後、２５℃で６０分間混合した。次に、イオン交換水で固形分濃度４４％に調整した後、さらに２５℃で１５分間混合した。   Into a planetary mixer with a disper, 100 parts of artificial graphite surface-treated with an antioxidant was added, and 100 parts of the aqueous solution was added thereto, and the solid content concentration was adjusted to 53.5% with ion-exchanged water. For 60 minutes. Next, after adjusting to 44% of solid content concentration with ion-exchange water, it mixed for 15 minutes at 25 degreeC.

次に、固形分濃度が４０％、ガラス転移温度が−１５℃であるスチレン−ブタジエン重合体粒子の分散液２．５部を入れ、さらに１０分間混合した。これを減圧下で脱泡処理して流動性の良い電極用スラリー組成物を得た。   Next, 2.5 parts of a dispersion of styrene-butadiene polymer particles having a solid content concentration of 40% and a glass transition temperature of −15 ° C. was added and further mixed for 10 minutes. This was defoamed under reduced pressure to obtain a slurry composition for electrodes with good fluidity.

上記電極用スラリー組成物を、コンマコーターで、厚さ２０μｍの銅箔の上に、乾燥後の膜厚が２００μｍ程度になるように塗布し、０．５ｍ／ｍｉｎの速度で６０℃で２分間乾燥、１２０℃で２分間加熱処理して電極原反を得た。この電極原反をロールプレスで圧延して活物質層の厚みが８０μｍの負極用電極を得た。   The electrode slurry composition was applied on a copper foil having a thickness of 20 μm with a comma coater so that the film thickness after drying was about 200 μm, and the speed was 0.5 m / min at 60 ° C. for 2 minutes. The electrode raw material was obtained by drying and heat treatment at 120 ° C. for 2 minutes. This electrode fabric was rolled with a roll press to obtain a negative electrode having an active material layer thickness of 80 μm.

（正極の製造）
正極活物質であるスピネル構造を有するＬｉＭｎ２Ｏ４ １００部に、バインダーとしてポリフッ化ビニリデンを固形分相当量が２部となるように加え、さらに、アセチレンブラック２部、Ｎ−メチルピロリドン２０部を加えて、プラネタリーミキサーで混合して正極用スラリーを得た。この正極用スラリーを厚さ１８μｍのアルミニウム箔に塗布し、１５０℃で３時間乾燥した後、ロールプレスして活物質層の厚みが１００μｍの正極用電極を得た。(Manufacture of positive electrode)
Polyvinylidene fluoride was added as a binder to 100 parts of LiMn 2 O 4 having a spinel structure as a positive electrode active material so that the solid content equivalent amount was 2 parts, and further 2 parts of acetylene black and 20 parts of N-methylpyrrolidone were added. In addition, the slurry for positive electrodes was obtained by mixing with a planetary mixer. This positive electrode slurry was applied to an aluminum foil having a thickness of 18 μm, dried at 150 ° C. for 3 hours, and then roll-pressed to obtain a positive electrode having an active material layer thickness of 100 μm.

（リチウムイオン二次電池の製造）
アルミニウムシートの両面がポリプロピレンからなる樹脂で被覆されたラミネートフィルムを用いて電池容器を作成した。次いで、上記正極および負極を用い、それぞれ端部から活物質層を除去して、除去した箇所に正極はＮｉタブを、負極はＣｕタブを溶接させた。得られた正極及び負極を、両極の活物質層面が対向するようにしてポリエチレン製の微多孔膜からなるセパレータを挟み、捲回して上記の電池容器に収納した。続いてここに、エチレンカーボネートとジエチルカーボネートを２５℃で体積比で１：２で混合した混合溶媒に、ＬｉＰＦ６を１モル／リットルの濃度になるように溶解させた電解液を注入した。次いで、ラミネートフィルムを封止させてラミネートセル型のリチウムイオン二次電池を作製した。この電池の性能の評価結果を表１に示す。(Manufacture of lithium ion secondary batteries)
A battery container was prepared using a laminate film in which both surfaces of an aluminum sheet were coated with a resin made of polypropylene. Next, using the positive electrode and the negative electrode, the active material layer was removed from each end, and the Ni tab was welded to the removed portion and the Cu tab was welded to the negative electrode. The obtained positive electrode and negative electrode were wound with a separator made of a polyethylene microporous membrane so that the active material layer surfaces of both electrodes were opposed, and wound and stored in the battery container. Subsequently, an electrolytic solution in which LiPF 6 was dissolved to a concentration of 1 mol / liter was injected into a mixed solvent in which ethylene carbonate and diethyl carbonate were mixed at a volume ratio of 1: 2 at 25 ° C. Next, the laminate film was sealed to produce a laminate cell type lithium ion secondary battery. Table 1 shows the evaluation results of the performance of this battery.

（実施例２）
活物質の表面処理において、混合溶液としてジフェニルアミン誘導体の酸化防止剤０．１部を、Ｎ−メチルピロリドン５０部に溶解させたものを使用した事以外は、実施例１と同様の操作を行って、負極用電極及びラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。結果を表１に示す。(Example 2)
In the surface treatment of the active material, the same operation as in Example 1 was performed except that 0.1 part of a diphenylamine derivative antioxidant was dissolved in 50 parts of N-methylpyrrolidone as a mixed solution. Then, a negative electrode and a laminate cell type lithium ion secondary battery were prepared, and the performance of the battery was evaluated. The results are shown in Table 1.

（実施例３）
活物質の表面処理において、混合溶液としてジフェニルアミン誘導体の酸化防止剤１．０部を、Ｎ−メチルピロリドン５０部に溶解させたものを使用した事以外は、実施例１と同様の操作を行って、負極用電極及びラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。結果を表１に示す。(Example 3)
In the surface treatment of the active material, the same operation as in Example 1 was performed except that 1.0 part of a diphenylamine derivative antioxidant was dissolved in 50 parts of N-methylpyrrolidone as a mixed solution. Then, a negative electrode and a laminate cell type lithium ion secondary battery were prepared, and the performance of the battery was evaluated. The results are shown in Table 1.

（実施例４）
活物質の表面処理において、処理前の活物質“ａ”として水銀圧入細孔体積が０．３cｍ３／ｇである人造黒鉛１００部を使用した事以外は、実施例１と同様の操作を行って、負極用電極及びラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。結果を表１に示す。Example 4
In the surface treatment of the active material, the same operation as in Example 1 was performed except that 100 parts of artificial graphite having a mercury intrusion pore volume of 0.3 cm 3 / g was used as the active material “a” before the treatment. Then, a negative electrode and a laminate cell type lithium ion secondary battery were prepared, and the performance of the battery was evaluated. The results are shown in Table 1.

（実施例５）
活物質の表面処理において、混合溶液として、下記化学式２に示すジフェニルアミン誘導体の酸化防止剤（ノクラック ＤＰ 大内新興化学工業社製）０．０２部を、Ｎ−メチルピロリドン５０部に溶解させたものを使用した事以外は、実施例１と同様の操作を行って、負極用電極及びラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。結果を表１に示す。(Example 5)
In the surface treatment of the active material, 0.02 part of a diphenylamine derivative antioxidant (NOCRAK DP manufactured by Ouchi Shinsei Chemical Co., Ltd.) represented by the following chemical formula 2 is dissolved in 50 parts of N-methylpyrrolidone as a mixed solution A negative electrode and a laminate cell type lithium ion secondary battery were produced by performing the same operation as in Example 1 except that the battery was evaluated, and the performance of this battery was evaluated. The results are shown in Table 1.

Figure 0005610161
Figure 0005610161

（実施例６）
活物質の表面処理において、混合溶液として、下記化学式３に示すフェノール系の酸化防止剤０．０２部を用いた事以外は、実施例１と同様の操作を行って、負極用電極及びラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。結果を表１に示す。(Example 6)
In the surface treatment of the active material, the same operation as in Example 1 was carried out except that 0.02 part of the phenolic antioxidant represented by the following chemical formula 3 was used as the mixed solution, and the negative electrode and laminate cell type A lithium ion secondary battery was manufactured and the performance of this battery was evaluated. The results are shown in Table 1.

Figure 0005610161
Figure 0005610161

（実施例７）
スラリー組成物作製の際に、固形分濃度が４０％、ガラス転移点温度が−１５℃であるスチレン−ブタジエン重合体粒子の分散液のかわりに、固形分濃度が４０％、ガラス転移温度が１７℃であるスチレン−ブタジエン重合体粒子分散液を２．５部用いた事以外は、実施例１と同様の操作を行って、負極用電極及びラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。結果を表１に示す。(Example 7)
In the preparation of the slurry composition, instead of the dispersion of styrene-butadiene polymer particles having a solid content concentration of 40% and a glass transition temperature of −15 ° C., the solid content concentration is 40% and the glass transition temperature is 17 Except for using 2.5 parts of a styrene-butadiene polymer particle dispersion at ℃, the same operation as in Example 1 was performed to produce a negative electrode and a laminate cell type lithium ion secondary battery. The battery performance was evaluated. The results are shown in Table 1.

（比較例１）
酸化防止剤による表面処理を行わず、活物質“ａ”として水銀圧入細孔体積が０．９５cｍ３／ｇである人造黒鉛１００部を用いた事以外は、実施例１と同様の操作を行って、負極用電極及びラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。結果を表１に示す。(Comparative Example 1)
The same operation as in Example 1 was performed except that 100 parts of artificial graphite having a mercury intrusion pore volume of 0.95 cm 3 / g was used as the active material “a” without performing surface treatment with an antioxidant. Then, a negative electrode and a laminate cell type lithium ion secondary battery were prepared, and the performance of the battery was evaluated. The results are shown in Table 1.

（比較例２）
ディスパー付きのプラネタリーミキサーに、人造黒鉛１００部と化学式１に示すジフェニルアミン誘導体の酸化防止剤０．０２部を入れ、これにカルボキシメチルセルロース水溶液１００部を加え、イオン交換水で固形分濃度５３．５％に調整した後、２５℃で６０分間混合した。次に、イオン交換水で固形分濃度４４％に調整した後、さらに２５℃で１５分間混合し、負極用スラリー組成物を調製した。負極用スラリー組成物として、前記スラリー組成物を用いた事以外は、実施例１と同様の操作を行って、負極用電極及びラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。このとき得られた極板の表面には斑点状のものが確認された。結果を表１に示す。(Comparative Example 2)
Into a planetary mixer with a disper, 100 parts of artificial graphite and 0.02 part of an antioxidant of a diphenylamine derivative represented by the chemical formula 1 are added, and 100 parts of a carboxymethylcellulose aqueous solution is added thereto, and the solid content concentration is 53.5 with ion-exchanged water. % And then mixed at 25 ° C. for 60 minutes. Next, after adjusting to 44% of solid content concentration with ion-exchange water, it mixed for 15 minutes at 25 degreeC, and the slurry composition for negative electrodes was prepared. Except that the slurry composition was used as the negative electrode slurry composition, the same operation as in Example 1 was performed to produce a negative electrode and a laminate cell type lithium ion secondary battery. Evaluation was performed. The surface of the electrode plate obtained at this time was spotted. The results are shown in Table 1.

（比較例３）
比較例１で得られた負極用電極を、電極中の活物質量１００部に対して化学式１に示すジフェニルアミン誘導体の酸化防止剤０．０２部をＮ−メチルピロリドン５０部に溶解させた溶液中に１時間浸漬し、その後乾燥後して得られた極板を負極用電極として用いた事以外は、実施例１と同様の操作を行って、ラミネートセル型のリチウムイオン二次電池を作製し、この電池の性能の評価を行った。結果を表１に示す。(Comparative Example 3)
The negative electrode obtained in Comparative Example 1 was dissolved in 50 parts of N-methylpyrrolidone in which 0.02 part of the antioxidant of the diphenylamine derivative represented by Chemical Formula 1 was dissolved in 100 parts of the active material amount in the electrode. The laminate cell type lithium ion secondary battery was manufactured by performing the same operation as in Example 1 except that the electrode plate obtained by immersing in 1 hour and then drying was used as the negative electrode. The performance of this battery was evaluated. The results are shown in Table 1.

Figure 0005610161
Figure 0005610161

表１の結果から、以下のことがわかる。
本発明によれば、実施例１〜実施例７に示すように、活物質として酸化防止剤で予め表面処理したものを用いることにより、ピール強度、リチウム受入特性、充放電時ガス発生量に優れるリチウムイオン二次電池を得ることができる。また、実施例の中でも、アミン系の酸化防止剤の含有量が０．０１〜０．２質量％で、表面処理に供される活物質“ａ”の水銀圧入細孔体積が０．４ｃｍ３／ｇ〜１．５ｃｍ３／ｇの範囲にあり、且つガラス転移点温度が０℃以下のバインダーを併用している実施例１や実施例２は、ピール強度、充放電特性、充放電時ガス発生量のすべてに優れている。From the results in Table 1, the following can be understood.
According to the present invention, as shown in Examples 1 to 7, by using an active material that has been surface-treated with an antioxidant in advance, it is excellent in peel strength, lithium acceptance characteristics, and gas generation during charging and discharging. A lithium ion secondary battery can be obtained. Further, among the examples, the content of the amine-based antioxidant is 0.01 to 0.2% by mass, and the mercury intrusion pore volume of the active material “a” used for the surface treatment is 0.4 cm 3. Example 1 and Example 2 in which a binder having a glass transition temperature of 0 ° C. or lower is used in combination with peel strength, charge / discharge characteristics, and charge / discharge gas, in the range of / g to 1.5 cm 3 / g. Excellent in all of the amount generated.

一方、活物質として酸化防止剤で予め表面処理をしていないものを用いたもの（比較例１）、活物質の表面処理を行わず、電極用スラリー組成物を調製する際に酸化防止剤を添加したもの（比較例２）、活物質の表面処理を行わず、電極を酸化防止剤を含んだポリマー溶液に含浸させたもの（比較例３）は、ピール強度、リチウム受入特性、充放電時ガス発生量の少なくとも一つが著しく劣る。   On the other hand, an active material that has not been surface-treated with an antioxidant in advance (Comparative Example 1), an active material that is not subjected to a surface treatment, and an antioxidant is prepared when preparing a slurry composition for an electrode. What was added (Comparative Example 2), and the surface treatment of the active material was not performed, and the electrode was impregnated with a polymer solution containing an antioxidant (Comparative Example 3) was peel strength, lithium receiving characteristics, charging / discharging At least one of the gas generation amounts is significantly inferior.

Claims (7)

酸化防止剤で黒鉛質材料を表面処理されてなり、
前記黒鉛質材料中の酸化防止剤の含有量が、０．０１〜１質量％であり、
水銀圧入細孔体積が、０．１ｃｍ ３ ／ｇ〜２．０ｃｍ ３ ／ｇである黒鉛質材料を表面処理したものを含む非水電解質二次電池電極用活物質。 Ri Na been surface-treated graphite material with an antioxidant,
The content of the antioxidant in the graphite material is 0.01 to 1% by mass,
Mercury intrusion pore volume, 0.1cm 3 /g~2.0cm 3 / g non-aqueous electrolyte secondary battery electrode active material, including those of the graphite material was treated surface is. 前記黒鉛質材料が人造黒鉛である請求項１に記載の非水電解質二次電池電極用活物質。The active material for a nonaqueous electrolyte secondary battery electrode according to claim 1, wherein the graphite material is artificial graphite. 前記酸化防止剤が、アミン系酸化防止剤又はフェノール系酸化防止剤である請求項１又は２に記載の非水電解質二次電池電極用活物質。   The active material for a nonaqueous electrolyte secondary battery electrode according to claim 1, wherein the antioxidant is an amine-based antioxidant or a phenol-based antioxidant. 請求項１に記載の非水電解質二次電池電極用活物質、バインダー及び溶媒を含む非水電解質二次電池電極用スラリー組成物。   The slurry composition for nonaqueous electrolyte secondary battery electrodes containing the active material for nonaqueous electrolyte secondary battery electrodes of Claim 1, a binder, and a solvent. 前記バインダーのガラス転移温度が２５℃以下である請求項４に記載の非水電解質二次電池電極用スラリー組成物。 The slurry composition for a nonaqueous electrolyte secondary battery electrode according to claim 4 , wherein the binder has a glass transition temperature of 25 ° C. or lower. 集電体上に、請求項４又は５に記載の非水電解質二次電池電極用スラリー組成物を塗布乾燥してなる非水電解質二次電池用電極。 A nonaqueous electrolyte secondary battery electrode obtained by applying and drying the slurry composition for a nonaqueous electrolyte secondary battery electrode according to claim 4 or 5 on a current collector. 正極、負極、セパレーター及び電解液を有してなり、
正極及び負極の少なくとも一方が、請求項６に記載の電極である、
非水電解質二次電池。 Comprising a positive electrode, a negative electrode, a separator and an electrolyte,
At least one of the positive electrode and the negative electrode is the electrode according to claim 6 ,
Non-aqueous electrolyte secondary battery.
JP2011520950A 2009-06-30 2010-06-30 Non-aqueous electrolyte secondary battery active material and non-aqueous electrolyte secondary battery Expired - Fee Related JP5610161B2 (en)