JP5573303B2 - 熱転写記録媒体 - Google Patents
熱転写記録媒体 Download PDFInfo
- Publication number
- JP5573303B2 JP5573303B2 JP2010082260A JP2010082260A JP5573303B2 JP 5573303 B2 JP5573303 B2 JP 5573303B2 JP 2010082260 A JP2010082260 A JP 2010082260A JP 2010082260 A JP2010082260 A JP 2010082260A JP 5573303 B2 JP5573303 B2 JP 5573303B2
- Authority
- JP
- Japan
- Prior art keywords
- thermal transfer
- layer
- recording medium
- transfer recording
- polyvinyl acetal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
さらに具体的には、基材フィルムと、該基材フィルムの一方の面に、バインダー樹脂と滑剤を有する熱転写層と、該基材フィルムのもう一方の面に、バインダー樹脂と無機粒子を有する耐熱滑性層からなる熱転写記録媒体に関するものである。
本発明の具体的な構成を以下に示す。
[請求項1]
基材フィルムと、該基材フィルムの一方の面に、少なくともバインダー樹脂と滑剤を有する熱転写層と、該基材フィルムのもう一方の面に、少なくともバインダー樹脂と無機粒子を有する耐熱滑性層からなる熱転写記録媒体において、
該熱転写層に用いるバインダー樹脂が、重合度1000以上且つガラス転移温度100℃以上のポリビニルアセタール樹脂(A)と、重合度1000未満且つガラス転移温度100℃未満のポリビニルアセタール樹脂(B)の2種のポリビニルアセタール樹脂と多価イソシアネートの反応物であって、且つ2種のポリビニルアセタール樹脂の比が、A:B=70〜90:30〜10重量%であって、且つ多価イソシアネートの添加量がNCO/OHの比で0.5以上であり、
該耐熱滑性層に用いるバインダー樹脂が水酸基価100mgKOH/g以上の熱可塑性樹脂と多価イソシアネートの反応物で、且つ多価イソシアネートの添加量がNCO/OHの比で0.8以上である事を特徴とする熱転写記録媒体。
[請求項2]
該熱転写層で使用される滑剤がシリコーン系の滑剤である事を特徴とする請求項1に記載の熱転写記録媒体。
[請求項3]
耐熱滑性層で使用される熱可塑性樹脂のガラス転移温度が40℃以上である事を特徴とする請求項1または2に記載の熱転写記録媒体。
[請求項4]
該耐熱滑性層で使用される無機粒子が、比重3.0×10 3 kg/m 3 以上である事を特徴とする請求項1乃至3のいずれか1項に記載の熱転写記録媒体。
重合度が1000以上且つガラス転移温度100℃以上のポリビニルアセタール樹脂を用いる事により熱転写層が被熱転写体に融着する危険性を減らす事ができた。
しかし、一方で、ポリビニルアセタール樹脂の重合度が高すぎると、樹脂の流動性が低く、塗工性が低下する為、均一な塗工面が得られないといった欠点が生じていた。
そこで本発明では重合度が1000以上且つガラス転移温度100℃以上のポリビニルアセタール樹脂に加えて、重合度が1000未満、好ましくは700未満のポリビニルアセタール樹脂を併せて使用する。これにより熱転写層が被転写体に融着せず、且つバインダー樹脂の塗工性が向上し均一な塗工面を得る事ができたのである。
<実施例1>
下記組成の耐熱滑性層形成用塗布液−1を調製し、基材フィルムである厚み4.5μmのポリエチレンテレフタレートフィルムの一方の面に塗布、乾燥させた後、50℃で24時間加熱することで硬化処理を行い、膜厚1.0μmの耐熱滑性層を形成した。
<耐熱滑性層形成用塗布液−1>
アクリルポリオール樹脂(KOH=150mgKOH/g、Tg=37℃) 25重量部
トリレンジイソシアネート 10重量部(NCO/OH=1.0)
水酸化マグネシウム(比重:2.4×10 3 kg/m 3 )0.2重量部
トルエン 45.5重量部
メチルエチルケトン 19.5重量部
<熱昇華転写層形成用塗布液−1>
ポリビニルアセタール樹脂(A)(平均重合度約2100、Tg110℃)4.0重量部
ポリビニルアセタール樹脂(B)(平均重合度約約600、Tg70℃ 1.0重量部
トリレンジイソシアネート 0.6重量部(NCO/OH=1.2)
C.I.ソルベントブルー63 5.0重量部
リン酸エステル系界面活性剤 0.04重量部
トルエン 45重量部
メチルエチルケトン 45重量部
〔受容層用インキ〕
・塩化ビニル−酢酸ビニル系共重合体 50部
・シリコーンオイル 2部
・メチルエチルケトン 25部
・トルエン 25部
実施例1において、熱昇華転写層形成用塗布液で使用されているリン酸エステル系界面活性剤の代わりに、ポリエーテル変性シリコーンオイルを使用した以外は実施例1と同様にして、実施例3の熱転写記録媒体を得た。
実施例2において、耐熱滑性層形成用塗布液−1で使用されている水酸基価150mgKOH/g、Tg=37℃のアクリルポリオール樹脂の代わりに、水酸基価150mgKOH/g、Tg=43℃のアクリルポリオール樹脂を使用した以外は実施例2と同様にして、実施例3の熱転写記録媒体を得た。
実施例3において、耐熱滑性層形成用塗布液で使用されている水酸化マグネシウムの代わりに、酸化マグネシウム(比重:3.3×10 3 kg/m 3 )を使用した以外は実施例3と同様にして、実施例4の熱転写記録媒体を得た。
実施例5において、熱昇華転写層形成用塗布液で使用されている平均重合度約2100、Tg110℃のポリビニルアセタール樹脂4.0重量部及び平均重合度約600、Tg70℃のポリビニルアセタール樹脂1.0重量部の代わりに、平均重合度2100、Tg110℃のポリビニルアセタール樹脂5.0重量部を使用した以外は実施例5と同様にして、比較例1の熱転写記録媒体を得た。
実施例5において、熱昇華転写層形成用塗布液で使用されている平均重合度約2100、Tg110℃のポリビニルアセタール樹脂4.0重量部及び平均重合度約約600、Tg70℃のポリビニルアセタール樹脂1.0重量部の代わりに、平均重合度約600、Tg70℃のポリビニルアセタール樹脂5.0重量部を使用した以外は実施例5と同様にして、比較例2の熱転写記録媒体を得た。
実施例5において、熱昇華転写層形成用塗布液で使用されているトリレンジイソシアネート0.6重量部の代わりに、0.2重量部使用した以外は実施例5と同様にして、比較例2の熱転写記録媒体を得た。
実施例5において、耐熱滑性層形成用塗布液で使用されている水酸基価150mgKOH/g、Tg=43℃のアクリルポリオール樹脂の代わりに、水酸基価80mgKOH/g、Tg=43℃のアクリルポリオール樹脂を使用した以外は実施例5と同様にして、比較例4の熱転写記録媒体を得た。
実施例5において、耐熱滑性層形成用塗布液で使用されているトリレンジイソシアネート10重量部の代わりに、4重量部使用した以外は実施例5と同様にして、比較例5の熱転写記録媒体を得た。
[熱転写層の塗工面]
◎:スジ、ムラなし
○:スジ、ムラあり(印画物に影響なし)
×:スジ、ムラあり(印画物に影響あり)
[基材フィルムの状態]
◎:ちぎれ、裂けなし
○:ちぎれ、裂けが2%未満(以後の印画に影響なし)
×:ちぎれ、裂けが2%以上(以後の印画に影響あり)
[ヘッドのカス付着]
◎:汚れなし
○:僅かに汚れあり(以後の印画に影響なし)
[熱転写層と被転写体の融着]
◎:融着なし(印画時の剥離音なし)
○:融着なし(印画時の剥離音あり)
×:融着がひどく、印画停止(以後の印画に影響あり)
[印画物の状態]
○:欠陥なく、良好
×:ムラ、スジ抜けあり
2・・・基材フィルム
3・・・熱転写層
4・・・耐熱滑性層
Claims (4)
- 基材フィルムと、該基材フィルムの一方の面に、少なくともバインダー樹脂と滑剤を有する熱転写層と、該基材フィルムのもう一方の面に、少なくともバインダー樹脂と無機粒子を有する耐熱滑性層からなる熱転写記録媒体において、
該熱転写層に用いるバインダー樹脂が、重合度1000以上且つガラス転移温度100℃以上のポリビニルアセタール樹脂(A)と、重合度1000未満且つガラス転移温度100℃未満のポリビニルアセタール樹脂(B)の2種のポリビニルアセタール樹脂と多価イソシアネートの反応物であって、且つ2種のポリビニルアセタール樹脂の比が、A:B=70〜90:30〜10重量%であって、且つ多価イソシアネートの添加量がNCO/OHの比で0.5以上であり、
該耐熱滑性層に用いるバインダー樹脂が水酸基価100mgKOH/g以上の熱可塑性樹脂と多価イソシアネートの反応物で、且つ多価イソシアネートの添加量がNCO/OHの比で0.8以上である事を特徴とする熱転写記録媒体。 - 該熱転写層で使用される滑剤がシリコーン系の滑剤である事を特徴とする請求項1に記載の熱転写記録媒体。
- 耐熱滑性層で使用される熱可塑性樹脂のガラス転移温度が40℃以上である事を特徴とする請求項1または2に記載の熱転写記録媒体。
- 該耐熱滑性層で使用される無機粒子が、比重3.0×10 3 kg/m 3 以上である事を特徴とする請求項1乃至3のいずれか1項に記載の熱転写記録媒体。