JP5457492B2 - タイヤ用ゴム組成物及び空気入りタイヤ - Google Patents
タイヤ用ゴム組成物及び空気入りタイヤ Download PDFInfo
- Publication number
- JP5457492B2 JP5457492B2 JP2012099161A JP2012099161A JP5457492B2 JP 5457492 B2 JP5457492 B2 JP 5457492B2 JP 2012099161 A JP2012099161 A JP 2012099161A JP 2012099161 A JP2012099161 A JP 2012099161A JP 5457492 B2 JP5457492 B2 JP 5457492B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- wax
- parts
- rubber composition
- tire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記タイヤ用ゴム組成物は、タイヤ外層用ゴム組成物であることが好ましい。
本発明はまた、前記ゴム組成物を用いて作製した空気入りタイヤに関する。
BR1:日本ゼオン(株)製のBR1250H(スズ変性BR)
BR2:宇部興産(株)製のVCR617(SPB含有BR)
NR:TSR20
IR:IR2200
カーボンブラック(N550):キャボットジャパン(株)製のショウブラックN550(N2SA:42m2/g、DBP吸油量:115ml/100g)
シリカ:エボニック社製のULTRASIL VN3(N2SA:175m2/g)
石油系C5レジン:丸善石油化学(株)製のマルカレッツT−100AS(軟化点:102℃)
混合レジン:シルアンドザイラリー社製のストラクトール40MS(芳香族炭化水素系樹脂と脂肪族炭化水素系樹脂の混合物)
C10レジン:Rutgers Chemicals社製のNOVARES C10(液状クマロンインデン樹脂、軟化点:5〜15℃)
SP1068レジン:(株)日本触媒製のSP1068(アルキルフェノール樹脂)
プロセスオイル:H&R社製のvivatec500(TDAE)
ステアリン酸:日油(株)製のステアリン酸「椿」
酸化亜鉛:東邦亜鉛(株)製の銀嶺R
10%オイル含有不溶性硫黄:日本乾溜工業(株)セイミサルファー(2硫化炭素による不溶分60%、オイル分10%)
加硫促進剤TBBS:大内新興化学工業(株)製のノクセラーNS(N−tert−ブチル−2−ベンゾチアゾリルスルフェンアミド)
石油由来ワックス1:試作品(ノルマルアルカン分:平均85質量%)
石油由来ワックス2:日本精鑞(株)製のパラフィンワックス−125(PW−125)(ノルマルアルカン分:平均88質量%)
天然由来ワックス1:横関油脂工業(株)製の精製ライスワックスS−100(軟化点分布:77〜83℃、エステル成分:95質量%、遊離脂肪酸:4質量%、遊離アルコール:1質量%、炭化水素:1質量%)
天然由来ワックス2:東亜化成(株)製の精製ライスワックスTOWAX 37F(軟化点分布:75〜81℃、エステル成分:90質量%以上、遊離脂肪酸:5質量%、遊離アルコール:2質量%、炭化水素:1質量%)
天然由来ワックス3:横関油脂工業(株)製の精製キャンデリラワックスMK−2(軟化点分布:42〜73℃、エステル成分:22質量%、遊離脂肪酸:10質量%、遊離アルコール:10質量%、炭化水素:40質量%、樹脂:18質量%)
天然由来ワックス4:横関油脂工業(株)製の精製ミツロウBEESWAXCO−100(軟化点分布:0〜75℃、エステル成分:70質量%、遊離脂肪酸:14質量%、遊離アルコール:2質量%、炭化水素:14質量%)
天然由来ワックス5:下記製造例で調製した精製砂糖きびワックス(軟化点分布:73〜79℃、エステル成分:61.4質量%、遊離脂肪酸:13質量%、遊離アルコール:4質量%、炭化水素:22質量%)
6PPD:住友化学(株)製のアンチゲン6C(N−(1,3−ジメチルブチル)−N’−フェニル−p−フェニレンジアミン)
77PD:LANXESS社製のVulkanox4030(N,N’−ビス−(1,4−ジメチルペンチル)−p−フェニレンジアミン)
6QDI:フレキシス社製の6QDI(N−(1,3−ジメチルブチル)−N’−フェニルキノンジイミン)
TMQ:大内新興化学工業(株)製ノクラック224(2,2,4−トリメチル−1,2−ジヒドロキノリン重合体)
粗糖製造工程で砂糖きびを圧搾して絞り取った砂糖ジュースを静置し、ジュース上部に浮上してくる主として繊維分と油脂分からなる浮遊物を濾過分離して得られるフィルターケーキを真空恒温槽で乾燥し、乾燥ケーキを得た。この乾燥ケーキを、撹拌機と還流冷却器、そして加熱ヒーターを備えた容器に入れ、抽出溶媒を加え、撹拌しながら加熱して溶媒の還流温度で抽出した。抽出が終了した後直ちに濾過を行い、フィルターケーキを分離除去した。濾過液を静置して下層の水層を分離した後、溶媒層を蒸留し、溶媒を除去して深緑色の砂糖きび粗ワックスを得た。得られた砂糖きび粗ワックスを常法に従って溶剤精製し、溶媒を蒸留で除去した後、更にこれを常法に従い漂白、脱臭処理して精製砂糖きびワックスを得た。
測定装置としてキャピラリーGC、カラムとしてアルミニウムコーティングされたキャピラリーカラムを用い、キャリアガスヘリウム、流量4ml/分、カラム温度180〜390℃、昇温速度15℃/分の条件にて測定した。
表1〜4の上段に示す配合処方にしたがい、(株)神戸製鋼製1.7Lバンバリーミキサーを用いて、硫黄及び加硫促進剤以外の薬品を混練りした。次に、オープンロールを用いて、得られた混練り物に硫黄及び加硫促進剤を添加して練り込み、未加硫ゴム組成物を得た。得られた未加硫ゴム組成物を用いて、サイドウォール、クリンチエイペックスの形状に合わせて成形し、他のタイヤ部材とともに貼り合わせて未加硫タイヤを作製し、170℃で加硫して試験用タイヤ(205/65R15)を得た。得られた試験用タイヤの性能を以下の試験により評価した。なお、表の下段は、各実施例、比較例で配合した石油由来ワックスの軟化点分布を示す。
高温地域は中近東アラブ首長国連邦で約1年間(夏を含む)、亜寒冷地域は北海道で約1年間(冬を含む)ロードテストを行い、発生したクラックの度合いを、以下の基準にしたがって評価した。数字が大きいほど、耐クラック性能に優れている。
1:3mm以上の亀裂または切断が見られる。
2:1mm以上3mm未満の深い亀裂が見られる。
3:1mm未満の深くて比較的大きな亀裂が見られる。
4:肉眼では、やっとのことで亀裂または切断が確認できる。
5:肉眼では確認できないが、拡大鏡(10倍)では亀裂または切断が確認できる。
(1)屋外:茶変色評価
神戸にて、タイヤを屋外の日の当たる場所に6カ月間(冬〜夏)放置し、色差度計を用いて、a*、b*を測定し、その値により、以下の基準にしたがって5段階に分けて評価した。数字が大きいほど、茶変色の度合いが小さい。
(基準)
1:−(a*+b*)×10≦−30
2:−30<−(a*+b*)×10≦−20
3:−20<−(a*+b*)×10≦−10
4:−10<−(a*+b*)×10≦0
5:−(a*+b*)×10>0
神戸にて、タイヤを屋内の倉庫に6カ月間(冬〜夏)放置し、色差度計を用いて、L*を測定し、その値により、以下の基準にしたがって5段階に分けて評価した。数字が大きいほど、白変色の度合いが小さい。
(基準)
1:100−L*≦60
2:60<100−L*≦65
3:65<100−L*≦70
4:70<100−L*≦75
5:100−L*>75
Claims (4)
- エステル成分含有量が40〜98質量%の天然由来ワックスと、炭素数20〜32の各ノルマルアルカンを含む石油由来ワックスと、フェニレンジアミン系及び/又はキノン系老化防止剤とを含み、
ゴム成分100質量部に対して、前記天然由来ワックスの含有量が0.05〜2質量部、前記炭素数20〜32の各ノルマルアルカンの合計含有量が0.3〜1.5質量部、前記フェニレンジアミン系及び前記キノン系老化防止剤の合計含有量が1.4〜6.0質量部であるタイヤ用ゴム組成物。 - 前記天然由来ワックスは、イネ科植物から抽出され、軟化点60〜90℃の成分からなるものである請求項1記載のタイヤ用ゴム組成物。
- タイヤ外層用ゴム組成物である請求項1又は2記載のタイヤ用ゴム組成物。
- 請求項1〜3のいずれかに記載のゴム組成物を用いて作製した空気入りタイヤ。