JP6347646B2 - 空気入りタイヤ - Google Patents
空気入りタイヤ Download PDFInfo
- Publication number
- JP6347646B2 JP6347646B2 JP2014077088A JP2014077088A JP6347646B2 JP 6347646 B2 JP6347646 B2 JP 6347646B2 JP 2014077088 A JP2014077088 A JP 2014077088A JP 2014077088 A JP2014077088 A JP 2014077088A JP 6347646 B2 JP6347646 B2 JP 6347646B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- less
- rubber
- wax
- grip performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、該精製キャンデリラワックスにおいて、炭素数28〜33の炭化水素中に占める炭素数31の炭化水素の割合は、60質量%以上が好ましく、65質量%以上がより好ましい。
なお、軟化点とは、JIS K 6220に規定される軟化点を環球式軟化点測定装置で測定し、球が降下した温度である。
なお、カーボンブラックの窒素吸着比表面積は、JIS K 6217のA法によって求められる。
なお、シリカのBET法による窒素吸着比表面積は、ASTM D3037−81に準拠した方法により測定することができる。
以下に、実施例で用いた各種薬品について説明する。
SBR:旭化成(株)製のタフデン4350(結合スチレン量:40質量%、ゴム固形分100質量部に対してオイル分50質量部含有)
BR:宇部興産(株)製のBR150B(シス1,4結合量97%、ML1+4(100℃)40、25℃における5%トルエン溶液粘度48cps、Mw/Mn3.3)
NR:RSS#3
カーボンブラック:新日化カーボン(株)製のニテロン#55S(石炭系重質油を原料としたカーボンブラック、N2SA:28×103m2/kg)
α−メチルスチレン系樹脂:アリゾナケミカル社製のSA85(軟化点:85℃、Tg:43℃、Mw:1000、α−メチルスチレンとスチレンとの共重合体)
シリカ:Degussa社製のウルトラジルVN3(N2SA:175m2/g)
シランカップリング剤:Degussa社製のSi69(ビス(3−トリエトキシシリルプロピル)テトラスルフィド)
老化防止剤6C:大内新興化学工業(株)製のノクラック6C(N−(1,3−ジメチルブチル)−N−フェニル−p−フェニレンジアミン)
老化防止剤224:フレキシス社製のノクラック224(2,2,4−トリメチル−1,2−ジヒドロキノリン重合体)
ステアリン酸:日油(株)製のステアリン酸「桐」
酸化亜鉛:三井金属鉱業(株)製の酸化亜鉛2種
ワックス1:サンノックN(大内新興化学製石油系ワックス)
ワックス2:横関油脂工業(株)製の精製キャンデリラワックスMK−2(構成成分:エステル22質量%、遊離脂肪酸10質量%、遊離アルコール10質量%、炭化水素40質量%、樹脂18質量%)(軟化点分布:42〜73℃)(40℃におけるヒートフロー/ピーク温度のヒートフロー×100=0)
ワックス3:横関油脂工業(株)製の精製キャンデリラワックスMD−21(構成成分:エステル3質量%、遊離脂肪酸5質量%、遊離アルコール5質量%、炭素数28〜33の炭化水素82質量%(該炭化水素のうち炭素数31の占める割合約70質量%)、樹脂5質量%)(軟化点分布:35〜75℃)(40℃におけるヒートフロー/ピーク温度のヒートフロー×100=0.6)
ワックス4:晒しミツロウ(構成成分:エステル66.5質量%、遊離脂肪酸18質量%、遊離アルコール2.5質量%、炭化水素13質量%)(軟化点分布:20〜70℃)(40℃におけるヒートフロー/ピーク温度のヒートフロー×100=9)
ワックス5:横関油脂工業(株)製の精製ミツロウBEESWAXCO−100(化粧品仕様)(構成成分:エステル70質量%、遊離脂肪酸14質量%、遊離アルコール2質量%、炭化水素14質量%)(軟化点分布:0〜75℃)(40℃におけるヒートフロー/ピーク温度のヒートフロー×100=13)
アロマスオイル:(株)ジャパンエナジー製のJOMOプロセスX140
硫黄:鶴見化学工業(株)製の粉末硫黄
加硫促進剤DPG:大内新興化学工業社製のノクセラーD
加硫促進剤CZ:大内新興化学工業社製のノクセラーCZ
バンバリーミキサーを用いて、表1の工程1に示す配合量の薬品を投入して、排出温度が約150℃となるように5分間混練し、排出した。更に、表1の工程2に示す配合量の硫黄および加硫促進剤を加え、バンバリーミキサーを用いて、排出温度が100℃となるように約3分間混練して、未加硫ゴム組成物を得た。得られた未加硫ゴム組成物を、170℃で12分間加硫することにより、加硫ゴムシートを作製した。
「ラボテストにおける初期・後期グリップ性能評価」
加硫ゴムシートからサンプルを作製し、日邦産業(株)製DFテスターSタイプに取り付け、繰り返し測定を行い、2回目、10回目の摩擦係数を示した。
初期グリップ性能:2回目の摩擦係数(滑り速度7km/h)
後期グリップ性能:10回目の摩擦係数(滑り速度7km/h)
更に実施例の配合は、耐オゾン性、屋外暴露試験での耐変色性にも優れていた。
Claims (6)
- ゴム成分、非石油系ワックス、及びα−メチルスチレン系樹脂を含有し、
前記ゴム成分100質量%中、スチレンブタジエンゴムの含有量が50〜90質量%であるゴム組成物を用いて作製したトレッドを有する空気入りタイヤ。 - 前記非石油系ワックスは、非石油系ワックスに、遊離脂肪酸、遊離アルコール及び樹脂からなる群より選択される少なくとも1種を除去する処理を施して得られる精製非石油系ワックスである請求項1記載の空気入りタイヤ。
- 前記非石油系ワックスは、炭素数28〜33の炭化水素を65質量%以上含有し、かつ該炭化水素中に占める炭素数31の炭化水素の割合が60質量%以上の精製キャンデリラワックスである請求項1又は2記載の空気入りタイヤ。
- 前記非石油系ワックスは、遊離脂肪酸含有量が17質量%以下、遊離アルコール含有量が2.5質量%未満の精製ミツロウである請求項1又は2記載の空気入りタイヤ。
- 前記ゴム組成物は、前記ゴム成分100質量部に対する前記非石油系ワックスの含有量が0.1〜8質量部である請求項1〜4のいずれかに記載の空気入りタイヤ。
- 前記ゴム組成物は、アミン系の老化防止剤及びキノリン系の老化防止剤を更に含有する請求項1〜5のいずれかに記載の空気入りタイヤ。