JP5443539B2 - 濡れすべり抵抗が改良されたエラストマーコンパウンド及び濡れすべり抵抗を改良する方法 - Google Patents
濡れすべり抵抗が改良されたエラストマーコンパウンド及び濡れすべり抵抗を改良する方法 Download PDFInfo
- Publication number
- JP5443539B2 JP5443539B2 JP2012108769A JP2012108769A JP5443539B2 JP 5443539 B2 JP5443539 B2 JP 5443539B2 JP 2012108769 A JP2012108769 A JP 2012108769A JP 2012108769 A JP2012108769 A JP 2012108769A JP 5443539 B2 JP5443539 B2 JP 5443539B2
- Authority
- JP
- Japan
- Prior art keywords
- silica
- composition
- elastomer
- surface area
- elastomer composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
(a)少なくとも1種のエラストマー成分、
(b)モース硬さが約4.5超且つBET表面積が約100m2/g未満の、少なくとも1種の濡れすべり促進充填材、
(c)BET表面積が約80m2/g又はそれよりも大きい、少なくとも1種の強化充填材、及び
(d)表面積が約100m2/g未満の、少なくとも1種の充填材、
を含有する組成物に関し、ここで(b)、(c)及び(d)は互いに異なっている。
(a)少なくとも1種のエラストマー成分、
(b)モース硬さが約4.5超且つBET表面積が約100m2/g未満の、非アルミニウム含有充填材である少なくとも1種の濡れすべり促進充填材、及び
(c)BET表面積が少なくとも約80m2/gの、少なくともシリカを含む少なくとも1種の強化充填材、
を含有する組成物に関する。
(a)少なくとも1種のエラストマー成分、
(b)モース硬さが約4.5超且つBET表面積が約100m2/g未満の、少なくとも1種の濡れすべり促進充填材、並びに
(c)(1)ケイ素含有種相及び炭素相を有する結合体、(2)金属含有種相及び炭素相を有する結合体、(3)少なくとも1つの有機基が結合した炭素生成物、若しくは(4)シリカをコーティングされたカーボンブラック、又はそれらの組み合わせから選択される、少なくとも1種の充填材、
を含有する組成物に関する。
(a)少なくとも1種のエラストマー成分、
(b)BET表面積が約40m2/g未満の、少なくとも1つのタイプのシリカ、及び
(c)BET表面積が少なくとも約80m2/gの、少なくとも1種の強化充填材、
を含有する組成物に関する。
(a)少なくとも1種のエラストマー成分、
(b)モース硬さが約4.5超且つBET表面積が約100m2/g未満の、アルミニウム及びシリカを含有しない少なくとも1種の濡れすべり促進充填材、並びに
(c)BET表面積が少なくとも約80m2/gの、少なくとも1種の強化充填材、
を含有する組成物に関する。
(a)少なくとも1種のエラストマー成分、
(b)モース硬さが約4.5超且つBET表面積が約100m2/g未満の、少なくとも1種の濡れすべり促進充填材、
(c)BET表面積が約80m2/g又はそれよりも大きい、少なくとも1種の強化充填材、及び
(d)表面積が約100m2/g未満の、少なくとも1種の充填材、
を含有している。ここで(b)、(c)及び(d)は互いに異なっている。
(a)少なくとも1種のエラストマー成分、
(b)モース硬さが約4.5超且つBET表面積が約100m2/g未満の、非アルミニウム含有充填材である少なくとも1種の濡れすべり促進充填材、及び
(c)BET表面積が少なくとも約80m2/gの、少なくともシリカを含む少なくとも1種の強化充填材、
を含有する。
(a)少なくとも1種のエラストマー成分、
(b)モース硬さが約4.5超且つBET表面積が約100m2/g未満の、少なくとも1種の濡れすべり促進充填材、並びに
(c)(1)ケイ素含有種相及び炭素相を有する結合体、(2)金属含有種相及び炭素相を有する結合体、(3)少なくとも1つの有機基が結合した炭素生成物、若しくは(4)シリカをコーティングされたカーボンブラック、又はそれらの組み合わせから選択される、少なくとも1種の充填材、
を含有する。
(a)少なくとも1種のエラストマー成分、
(b)BET表面積が約40m2/g未満の、少なくとも1つのタイプのシリカ、及び
(c)BET表面積が少なくとも約80m2/gの、少なくとも1種の強化充填材、
を含有する。
(a)少なくとも1種のエラストマー成分、
(b)モース硬さが約4.5超且つBET表面積が約100m2/g未満の、アルミニウム及びシリカを含有しない少なくとも1種の濡れすべり促進充填材、並びに
(c)BET表面積が少なくとも約80m2/gの、少なくとも1種の強化充填材、
を含有する。
以下の例では、表1で示されている組成に従って、エラストマー組成物を調製した。全ての例において、与えられている数値は、特に示している場合を除いて重量部である。
Claims (16)
- (a)天然ゴム、スチレン−ブタジエンゴム、ポリイソブチレン、ポリブタジエン、ポリイソプレン、ポリクロロプレン、そのようなエラストマーの油展誘導体、並びにそれらの配合、混合及びコポリマーからなる群より選択される、少なくとも1種のエラストマー成分、
(b)モース硬さが4.5超且つBET表面積が40m2/g未満の、少なくとも1種のシリカ、
(c)BET表面積が80m2/g又はそれよりも大きい、少なくとも1種のカーボンブラック又はカーボンブラックとシリカの配合、及び
(d)表面積が100m2/g未満の、少なくとも1種の充填材、
を含有し、前記充填材(b)、(c)及び(d)が互いに異なっている、タイヤ用の組成物。 - 前記充填材(b)、(c)及び(d)が充填材のタイプに関して異なっている、請求項1に記載の組成物。
- 前記充填材(b)、(c)及び(d)が表面積に関して異なっている、請求項1に記載の組成物。
- (a)天然ゴム、スチレン−ブタジエンゴム、ポリイソブチレン、ポリブタジエン、ポリイソプレン、ポリクロロプレン、そのようなエラストマーの油展誘導体、並びにそれらの配合、混合及びコポリマーからなる群より選択される、少なくとも1種のエラストマー成分、
(b)モース硬さが4.5超且つBET表面積が40m2/g未満の、少なくとも1種のシリカ、並びに
(c)(1)ケイ素含有種相及び炭素相を有する結合体、(2)金属含有種相及び炭素相を有する結合体、(3)少なくとも1つの有機基が結合した炭素生成物、若しくは(4)シリカをコーティングされたカーボンブラック、又はそれらの組み合わせから選択される、少なくとも1種の充填材、
を含有する、タイヤ用の組成物。 - (a)天然ゴム、スチレン−ブタジエンゴム、ポリイソブチレン、ポリブタジエン、ポリイソプレン、ポリクロロプレン、そのようなエラストマーの油展誘導体、並びにそれらの配合、混合及びコポリマーからなる群より選択される、少なくとも1種のエラストマー成分、
(b)モース硬さが4.5超且つBET表面積が40m2/g未満の、少なくとも1つのタイプのシリカ、及び
(c)BET表面積が少なくとも80m2/gの、少なくとも1種のカーボンブラック又はカーボンブラックとシリカの配合、
を含有する、タイヤ用の組成物。 - 前記カーボンブラックとシリカの配合が、5:95〜95:5の重量比を有する、請求項1又は5に記載の組成物。
- 請求項1又は5に記載の組成物を含有するタイヤ部品。
- 前記エラストマー成分が、ブタジエンモノマー、イソプレンモノマー、クロロプレンモノマー、それらの組み合わせ、又はそれらの反応生成物から選択される少なくとも1種のモノマーを含有する、請求項1又は5に記載の組成物。
- (a)天然ゴム、スチレン−ブタジエンゴム、ポリイソブチレン、ポリブタジエン、ポリイソプレン、ポリクロロプレン、そのようなエラストマーの油展誘導体、並びにそれらの配合、混合及びコポリマーからなる群より選択される、少なくとも1種のエラストマー成分、
(b)モース硬さが4.5超且つBET表面積が40m2/g未満の、少なくとも1種のシリカ、
(c)BET表面積が80m2/g又はそれよりも大きい、少なくとも1種のカーボンブラック又はカーボンブラックとシリカの配合、及び
(d)表面積が100m2/g未満の、少なくとも1種の充填材、
を組み合わせて、濡れすべり抵抗性エラストマー組成物を作ることを含み、前記充填材(b)、(c)及び(d)が互いに異なっている、エラストマー組成物の濡れすべり抵抗性を改良する方法であって、ここで前記(b)のシリカを伴わない前記エラストマー組成物と比較して、前記濡れすべり抵抗性エラストマー組成物の濡れすべり抵抗性が増加しており、かつ前記エラストマー組成物はタイヤ用の組成物である、エラストマー組成物の濡れすべり抵抗性を改良する方法。 - (a)天然ゴム、スチレン−ブタジエンゴム、ポリイソブチレン、ポリブタジエン、ポリイソプレン、ポリクロロプレン、そのようなエラストマーの油展誘導体、並びにそれらの配合、混合及びコポリマーからなる群より選択される、少なくとも1種のエラストマー成分、
(b)モース硬さが4.5超且つBET表面積が40m2/g未満の、少なくとも1種のシリカ、及び
(c)BET表面積が少なくとも80m2/gの、少なくとも1種のカーボンブラックとシリカの配合、
を共に組み合わせることを含む、エラストマー組成物の濡れすべり抵抗性を改良する方法であって、ここで前記(b)のシリカを伴わない前記エラストマー組成物と比較して、前記濡れすべり抵抗性エラストマー組成物の濡れすべり抵抗性が増加しており、かつ前記エラストマー組成物はタイヤ用の組成物である、エラストマー組成物の濡れすべり抵抗性を改良する方法。 - (a)天然ゴム、スチレン−ブタジエンゴム、ポリイソブチレン、ポリブタジエン、ポリイソプレン、ポリクロロプレン、そのようなエラストマーの油展誘導体、並びにそれらの配合、混合及びコポリマーからなる群より選択される、少なくとも1種のエラストマー成分、
(b)モース硬さが4.5超且つBET表面積が40m2/g未満の、少なくとも1種のシリカ、並びに
(c)(1)ケイ素含有種相及び炭素相を有する結合体、(2)金属含有種相及び炭素相を有する結合体、(3)少なくとも1つの有機基が結合した炭素生成物、若しくは(4)シリカをコーティングされたカーボンブラック、又はそれらの組み合わせから選択される、少なくとも1種の充填材、
を共に組み合わせることを含む、エラストマー組成物の濡れすべり抵抗性を改良する方法であって、ここで前記(b)のシリカを伴わない前記エラストマー組成物と比較して、前記濡れすべり抵抗性エラストマー組成物の濡れすべり抵抗性が増加しており、かつ前記エラストマー組成物はタイヤ用の組成物である、エラストマー組成物の濡れすべり抵抗性を改良する方法。 - (a)天然ゴム、スチレン−ブタジエンゴム、ポリイソブチレン、ポリブタジエン、ポリイソプレン、ポリクロロプレン、そのようなエラストマーの油展誘導体、並びにそれらの配合、混合及びコポリマーからなる群より選択される、少なくとも1種のエラストマー成分、
(b)モース硬さが4.5超且つBET表面積が40m2/g未満の、少なくとも1つのタイプのシリカ、及び
(c)BET表面積が少なくとも80m2/gの、少なくとも1種のカーボンブラック又はカーボンブラックとシリカの配合、
を共に組み合わせることを含む、エラストマー組成物の濡れすべり抵抗性を改良する方法であって、ここで前記(c)のカーボンブラック又はカーボンブラックとシリカの配合を伴わない前記エラストマー組成物と比較して、前記濡れすべり抵抗性エラストマー組成物の濡れすべり抵抗性が増加しており、前記エラストマー組成物はタイヤ用の組成物である、エラストマー組成物の濡れすべり抵抗性を改良する方法。 - 前記濡れすべり抵抗性が、前記成分を伴わないエラストマー組成物と比較して、少なくとも2%大きい、請求項9、11及び12のいずれかに記載の方法。
- 前記濡れすべり抵抗性が、前記成分を伴わないエラストマー組成物と比較して、少なくとも10%大きい、請求項9、11及び12のいずれかに記載の方法。
- 前記濡れすべり抵抗性エラストマー組成物を製造品に成形すること、及びその後で前記濡れすべり抵抗性エラストマー組成物を加硫することを更に含む、請求項9〜12のいずれかに記載の方法。
- 前記成形工程が、前記濡れすべり抵抗性エラストマー組成物をタイヤ部品に成形することを含む、請求項9〜12のいずれかに記載の方法。