JP5432841B2 - 作業服用織編物 - Google Patents
作業服用織編物 Download PDFInfo
- Publication number
- JP5432841B2 JP5432841B2 JP2010149102A JP2010149102A JP5432841B2 JP 5432841 B2 JP5432841 B2 JP 5432841B2 JP 2010149102 A JP2010149102 A JP 2010149102A JP 2010149102 A JP2010149102 A JP 2010149102A JP 5432841 B2 JP5432841 B2 JP 5432841B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- knitted fabric
- woven
- work clothes
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)セルロース繊維を65〜100重量%含有しかつポリエステル繊維を0〜35重量%含有する作業服用織編物であって、フルオロアルキル系ビニルモノマー(A)とポリアルキレングリコール含有親水性ビニルモノマー(B1)と非ポリアルキレングリコール系ビニルモノマー(B2)とからなるアクリレート系共重合体が0.5〜10重量%付着されていること、及び前記アクリレート系共重合体中のモノマーのモル比がA:(B1+B2)=1.0:0.5〜1.0:3.5であり、かつB1:B2=1.0:1.0〜1.0:4.0であることを特徴とする作業服用織編物。
(2)導電性繊維が0.2〜3.0重量%含有され、JIS−L1094の摩擦帯電電荷量が7μc/m2以下であることを特徴とする(1)に記載の作業服用織編物。
(3)銀、アルミニウム、カリウム、鉄、チタンまたは亜鉛の塩または酸化物からなる金属系抗菌剤が0.0001〜3重量%含有されていることを特徴とする(1)または(2)に記載の作業服用織編物。
(4)液体アンモニア加工またはシルケット加工が施され、バリウム活性数が130〜190であることを特徴とする(1)〜(3)のいずれかに記載の作業服用織編物。
(5)導電性繊維以外の構成繊維が全て綿であることを特徴とする(1)〜(4)のいずれかに記載の作業服用織編物。
具体的には、一般式(I):
Rf−XOCOCR1=CH2 (I)
[式中、Rfはフルオロアルキル基であり、R1は水素原子またはメチル基であり、Xはアルキレン基、下記一般式:
−SO2、NR2−R3−
(式中、R2は水素原子またはアルキル基であり、R3はアルキレン基である)で表される基、又は下記一般式:
−CH2CH(OR4)CH2−
(式中、R4は水素原子またはアシル基である)で表される基である]
CyF2y+1−
(式中、yは3〜20の整数である)で表される直鎖状又は分岐状のパーフルオロアルキル基又は該基の一部のフッ素原子が水素原子もしくは塩素原子で置換されたフルオロアルキル基が挙げられ、特に代表的なものは、炭素数が3〜20のパーフルオロアルキル基である。このようなRfの具体例としては、例えば、CF3(CF2)4−、CF3(CF2)5−、CF2(CF2)6−、CF2(CF2)7−、CF2(CF2)8−、CF2(CF2)9−、(CF3)2CFCF2−、(CF3)2CF(CF2)2−、(CF3)2CF(CF2)3−、(CF3)2CF(CF2)5−、(CF3)2CF(CF2)6−、(CF3)2CF(CF2)8−、(CF3)CF(CF2)10−、H(CF2)10−、CF2Cl(CF2)10−などが挙げられる。
CF3(CF2)7(CH2)8OCOCH=CH2
CF3(CF2)6CH2OCOC(CH3)=CH2
(CF3)2CF(CF2)8(CH2)2OCOCH=CH2
CF3(CF2)7(CH2)2OCOCH=CH2
CF3(CF2)7(CH2)2OCOC(CH3)=CH2
CF3(CF2)9(CH2)2OCOCH=CH2
CF3(CF2)7SO2NCH3(CH2)2OCOCH=CH2
CF3(CF2)7SO2NCH3(CH2)2OCOCCH3=CH2
(CF3)2CF(CF2)8CH2CHOCOCH2CH2OCOCCH3=CH2
H(CF2)10CH2OCOCH=CH2
CF2Cl(CF2)10CH2OCOC(CH3)=CH2
などが挙げられる。これらの化合物は単独でも二種以上の併用でもよい。
下記一般式(II):
CH2=CR1CO−(OR3)n−R5 (II)
(式中、R1は水素原子又はメチル基、R3はアルキレン基、R5はヒドロキシル基又はアルコキシ基であり、nは3〜50の整数である)で表される(メタ)アクリル酸エステル、または、一般式(III):
CH2=CR1CO−(OR3)n−OCOCR1=CH2 (III)
(式中、R1は水素原子か又はメチル基で、R2はアルキレン基であり、nは3〜50の整数である)で表されるジ(メタ)アクリル酸エステルを言う。
CH2=CHCOO(CH2CH2O)10H
CH2=CHCOO(CH2CH2)9CH3
CH2=CHCOO(CH2CH2O)23H
CH2=CHCOO(CH2CH2O)30H
CH2=CCH3COO(CH2CH2O)8H
CH2=CCH3COO(CH2CH2O)23H
CH2=CCH3COO(CH2CH2O)40H
CH2=CHCOO(CH2CH2O)10OCOCH=CH2
CH2=CHCOO(CH2CH2O)23OCOCH=CH2
CH2=CHCOO(CH2CH2O)36OCOCH=CH2
CH2=CCH3COO(CH2CH2O)10OCOCH3C=CH2
CH2=CCH3COO(CH2CH2O)23OCOCH3C=CH2
CH2=CCH3COO(CH2CH2O)36OCOCH3C=CH2
などの化合物が挙げられる。これらの化合物は単独でも二種以上の併用でもよい。
一般式(IV):
CH2=CR1CO−(OR3)m−R5 (IV)
(式中、R1、R3、R5は前記と同様であり、mは0もしくは1の整数である)で表される(メタ)アクリル酸エステルを言う。
CH2=CHCOOCH2CH2OH
CH2=CCH3COOCH2CH2OH
CH2=CHCONH2
CH2=CCH3CONH2
CH2=CHCONH・CH2OH
CH2=CCH3CONH・CH2OH
CH2=CHCOOH
CH2=CCH3COOH
などの化合物が挙げられる。これらの化合物は単独でも二種以上の併用でもよい。
JIS−L1907の滴下法に準拠して評価した。
AATCC TM−188(1997)に準拠して評価した。
JIS−L1094 5.3の摩擦帯電電荷量測定法に準拠して評価した。
JIS−L1902の黄色ぶどう球菌を使用した菌液吸収法に準拠して静菌活性値(抗菌性)を評価した。
AATCC 124−1984の5段階レプリカ法に基づいて判定を行った。洗濯機はパナソニック製の2槽式洗濯機NA−W40G2を用いて、JIS−L0217 103法に従って洗濯して、吊り干し乾燥とした。判定は5段階で5級(良好)〜1級(不良)とした。評価結果はn=3回の評価の平均値とした。
防汚性は、汚れ物質とともに生地を洗濯したときに、生地がどれだけ汚れたかを判定する。具体的には、AATCC Test Method 61−1996を基にして下記のように行った。
試料から10cm×5cmの試験片を2枚採取する。Launder Ometerに付属する標準瓶(canister)1個に対して下記処方の汚染液100ccを入れて、40℃×10分間42rpmで攪拌し、汚染液の温度を安定させる。その後、標準瓶1個に対して上記試験片2枚とステンレス球10個を入れて42rpmで40℃×30分間処理する。汚染液を捨て、浴比1:100の割合で常温水を入れて2回(1分+2分)水洗いして、濾紙で脱水後風乾する。そして、JIS−L0805汚染用グレースケールを用いて汚れ具合を級判定する。
汚染母液の処方と汚染液
下記処方の汚染母液を作成して、それをイオン交換水で100倍に希釈したものを汚染液とした。
カーボンブラック(三菱チャンネルブラック♯100) 1重量部
牛脂硬化脂肪酸(mp.51℃ 日本油脂製) 15重量部
石鹸(JIS−K3302のU) 10重量部
水(常温のイオン交換水) 74重量部
―――――――――――――――――――――――――――――――――
合計 100重量部
但し、母液を作成する際、温浴中で85℃に暖めながら、しっかり攪拌して、牛脂、石鹸、カーボンブラックを完全に溶かした後、攪拌しながら30℃になるまで冷却する。
撚係数(K)3.7(撚数23.4T/inch)40′sのアメリカ産スーピマ綿100重量%紡績糸をリング式の撚糸機を用いて英式番手で40番双糸(40/2)を作成した。そのときの双糸撚数は16.5T/inchであった。また、前記双糸を作る時に、クラレ社製ポリエステル導電糸(クラカーボ(R))28デシテックス2フィラメントを合撚することで導電糸入り紡績糸を作成した。
(A)2−パーフルオロオクチルエチルアクリレート、(B1)メトキシポリエチレングリコール(PEG400)アクリレート、(B2)2−ヒドロキシエチルアクリレートの各モノマーを下記モル比で共重合反応させ、親水撥油剤1〜4を調製した。
A:B1:B2=1.00:0.75:1.75(親水撥油剤1)
A:B1:B2=1.0:1.0:2.0(親水撥油剤2)
A:B1:B2=1.0:0.5:1.5(親水撥油剤3)
A:B1:B2=1.0:3.0:4.0(親水撥油剤4)
変性エタノール溶媒として、攪拌しながら温度を60℃に設定した後、アゾビス2、4−ジメチルバレロニトリル2.0gを入れ、70〜75℃で7時間重合反応を行い、冷却後イオン交換水を580g加えて、共重合体を22重量%含有する水溶液1000gを得た。
試料1を液体アンモニア処理した後、下記の配合の処理液1に浸漬し、ピックアップ率100%でパッド処理し、120℃で1分間の乾燥の後、更に150℃で2.5分間キュアした。アクリレート系共重合体の付着量は2.2重量%であった。
〈処理液1〉
親水撥油剤1の水溶液 10.0重量%
鉄、アルミニウム、及びカリウムの全てを含む触媒機能を有する
金属組成物(東洋興業(株)製TC−42) 0.5重量%
ポリエチレン系柔軟剤(日華化学(株)製PE713) 2.0重量%
親水性シリコーン系柔軟剤(第一工業製薬(株)製S1515) 0.5重量%
試料1を液体アンモニア処理した後、下記の配合の処理液2に浸漬し、ピックアップ率100%でパッド処理し、120℃で1分間の乾燥の後、更に150℃で2.5分間キュアした。アクリレート系共重合体の付着量は2.2重量%であった。
〈処理液2〉
親水撥油剤2の水溶液 10.0重量%
鉄、アルミニウム、及びカリウムの全てを含む触媒機能を有する
金属組成物(東洋興業(株)製TC−42) 0.5重量%
ポリエチレン系柔軟剤(日華化学(株)製PE713) 2.0重量%
親水性シリコーン系柔軟剤(第一工業製薬(株)製S1515) 0.5重量%
試料1を液体アンモニア処理した後、下記の配合の処理液3に浸漬し、ピックアップ率100%でパッド処理し、120℃で1分間の乾燥の後、更に150℃で2.5分間キュアした。アクリレート系共重合体の付着量は2.2重量%であった。
〈処理液3〉
親水撥油剤3の水溶液 10.0重量%
鉄、アルミニウム、及びカリウムの全てを含む触媒機能を有する
金属組成物(東洋興業(株)製TC−42) 0.5重量%
ポリエチレン系柔軟剤(日華化学(株)製PE713) 2.0重量%
親水性シリコーン系柔軟剤(第一工業製薬(株)製S1515) 0.5重量%
試料1を液体アンモニア処理した後、下記の配合の処理液4に浸漬し、ピックアップ率100%でパッド処理し、120℃で1分間の乾燥の後、更に150℃で2.5分間キュアした。アクリレート系共重合体の付着量は1.1重量%であった。
〈処理液4〉
親水撥油剤1の水溶液 5.0重量%
鉄、アルミニウム、及びカリウムの全てを含む触媒機能を有する
金属組成物(東洋興業(株)製TC−42) 0.5重量%
ポリエチレン系柔軟剤(日華化学(株)製PE713) 2.0重量%
親水性シリコーン系柔軟剤(第一工業製薬(株)製S1515) 0.5重量%
試料1を液体アンモニア処理した後、下記の配合の処理液5に浸漬し、ピックアップ率100%でパッド処理し、120℃で1分間の乾燥の後、更に150℃で2.5分間キュアした。アクリレート系共重合体の付着量は3.3重量%であった。
〈処理液5〉
親水撥油剤1の水溶液 15.0重量%
鉄、アルミニウム、及びカリウムの全てを含む触媒機能を有する
金属組成物(東洋興業(株)製TC−42) 0.5重量%
ポリエチレン系柔軟剤(日華化学(株)製PE713) 2.0重量%
親水性シリコーン系柔軟剤(第一工業製薬(株)製S1515) 0.5重量%
試料2に対して実施例1と同様の処理を行った。
試料1を液体アンモニア処理した後、下記の配合の処理液6に浸漬し、ピックアップ率100%でパッド処理し、120℃で1分間の乾燥の後、更に150℃で2.5分間キュアした。アクリレート系共重合体の付着量は2.2重量%であった。
〈処理液6〉
親水撥油剤4の水溶液 10.0重量%
鉄、アルミニウム、及びカリウムの全てを含む触媒機能を有する
金属組成物(東洋興業(株)製TC−42) 0.5重量%
ポリエチレン系柔軟剤(日華化学(株)製PE713) 2.0重量%
親水性シリコーン系柔軟剤(第一工業製薬(株)製S1515) 0.5重量%
試料1を液体アンモニア処理した後、下記の配合の処理液7に浸漬し、ピックアップ率100%でパッド処理し、120℃で1分間の乾燥の後、更に150℃で2.5分間キュアした。
〈処理液7〉
ポリエステル系親水加工剤(高松油脂(株)製SR1000) 2.0重量%
親水性シリコーン系柔軟剤(一方社油脂(株)製ESN741) 1.0重量%
親水性シリコーン系柔軟剤(第一工業製薬(株)製S1515) 0.5重量%
試料1を液体アンモニア処理した後、下記の配合の処理液8に浸漬し、ピックアップ率100%でパッド処理し、120℃で1分間の乾燥の後、更に150℃で2.5分間キュアした。
〈処理液8〉
フッ素系撥水撥油剤(明成化学(株)製AG7600) 5.0重量%
イソシアネート系架橋剤(明成化学(株)製MF) 1.0重量%
鉄、アルミニウム、及びカリウムの全てを含む触媒機能を有する
金属組成物(東洋興業(株)製TC−42) 0.5重量%
ポリエチレン系柔軟剤(日華化学(株)製PE713) 2.0重量%
親水性シリコーン柔軟剤(第一工業製薬(株)製S1515) 0.5重量%
試料3に対して実施例1と同様の処理を行った。
Claims (5)
- セルロース繊維を65〜100重量%含有しかつポリエステル繊維を0〜35重量%含有する作業服用織編物であって、フルオロアルキル系ビニルモノマー(A)とポリアルキレングリコール含有親水性ビニルモノマー(B1)と非ポリアルキレングリコール系ビニルモノマー(B2)とからなるアクリレート系共重合体が0.5〜10重量%付着されていること、及び前記アクリレート系共重合体中のモノマーのモル比がA:(B1+B2)=1.0:0.5〜1.0:3.5であり、かつB1:B2=1.0:1.0〜1.0:4.0であることを特徴とする作業服用織編物。
- 導電性繊維が0.2〜3.0重量%含有され、JIS−L1094の摩擦帯電電荷量が7μc/m2以下であることを特徴とする請求項1に記載の作業服用織編物。
- 銀、アルミニウム、カリウム、鉄、チタンまたは亜鉛の塩または酸化物からなる金属系抗菌剤が0.0001〜3重量%含有されていることを特徴とする請求項1または2に記載の作業服用織編物。
- 液体アンモニア加工またはシルケット加工が施され、バリウム活性数が130〜190であることを特徴とする請求項1〜3のいずれかに記載の作業服用織編物。
- 導電性繊維以外の構成繊維が全て綿であることを特徴とする請求項1〜4のいずれかに記載の作業服用織編物。