JP5424716B2 - ポリアミド樹脂組成物及びその製造方法並びに冷媒輸送用ホース - Google Patents
ポリアミド樹脂組成物及びその製造方法並びに冷媒輸送用ホース Download PDFInfo
- Publication number
- JP5424716B2 JP5424716B2 JP2009126712A JP2009126712A JP5424716B2 JP 5424716 B2 JP5424716 B2 JP 5424716B2 JP 2009126712 A JP2009126712 A JP 2009126712A JP 2009126712 A JP2009126712 A JP 2009126712A JP 5424716 B2 JP5424716 B2 JP 5424716B2
- Authority
- JP
- Japan
- Prior art keywords
- polyamide resin
- resin composition
- metal compound
- polyolefin
- elastomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
例えば、エアコンシステム内に微量でも酸性成分が存在する場合、高温/高圧の実使用条件下では、ポリアミド樹脂組成物がこの酸性成分により著しく劣化し、使用に耐えなくなる場合がある。この酸性成分としては冷媒と共に封入されるコンプレッサーオイルに含まれる極圧剤などが考えられる。このため、エアコンに使用されるオイルの種類や環境条件によっては、従来の冷媒輸送用ホースでは実用的な耐久性が得られず、使用不可能となる場合もある。
この特定の金属化合物による、ポリアミド樹脂組成物の冷媒やコンプレッサーオイルによる劣化防止効果の作用機構の詳細は明らかではないが、ポリアミド樹脂組成物に配合された金属化合物が受酸剤、受ハロゲン剤等として機能し、冷媒やオイルに含まれる酸成分やハロゲン成分等の劣化要因物質を金属化合物がトラップすることにより、ポリアミド樹脂組成物の劣化防止効果が発現されることによるものと推定される。
本発明はまた、このポリアミド樹脂組成物よりなるガスバリア層を有する耐久性能に優れた冷媒輸送用ホースを提供することを課題とする。
本発明に従って、ポリアミド樹脂に予め金属化合物を混練した後ポリオレフィン系エラストマーを混練することにより得られる樹脂組成物では、金属化合物が主としてポリアミド樹脂相に存在するものとなり、金属化合物によるポリアミド樹脂の劣化防止作用、即ち、冷媒やオイルに含まれる酸成分やハロゲン成分等のポリアミド樹脂の劣化要因物質を金属化合物がトラップする作用がポリアミド樹脂相内で直接的に有効に機能するようになる。
先願においては、ポリアミド樹脂組成物中の金属化合物の含有量はポリマー成分と金属化合物との合計に対して1〜15重量%とされているが、本発明においては、ポリアミド樹脂に予め金属化合物を混練した後ポリオレフィン系エラストマーを混練する2段階混練を行うことによるポリアミド樹脂に対する金属化合物の添加効果の向上により、先願に比べて比較的少ない金属化合物配合量で良好な添加効果を得ることができる。しかして、本発明では、このように金属化合物の配合量を低減することにより、耐久性のより一層の向上を図ることができる。即ち、樹脂組成物に配合された金属化合物は、組成物中で分散不良が生じた場合、破壊の起点ともなり得るものであり、その観点からは、添加効果が得られる範囲内でなるべく配合量を少なくすることが望まれる。
本発明によれば、製造時の混練工程の改良により、少ない金属化合物配合量でその添加効果を確実に発揮させて、耐久性の改善を図ることができる。
まず、本発明のポリアミド樹脂組成物の製造方法とこのポリアミド樹脂組成物の製造方法により製造される本発明のポリアミド樹脂組成物について説明する。
本発明で用いられるポリアミド樹脂は、アミノ酸、ラクタムあるいはジアミンとジカルボン酸を主たる構成成分とするポリアミド樹脂である。これらの構成成分の具体例を挙げるとε−カプロラクタム、エナントラクタム、ω−ラウロラクタムなどのラクタム、ε−アミノカプロン酸、11−アミノウンデカン酸、12−アミノドデカン酸などのアミノ酸、テトラメチレンジアミン、ヘキサメチレンジアミン、ウンデカメチレンジアミン、ドデカメチレンジアミン、2,2,4−/2,4,4−トリメチルヘキサメチレンジアミン、5−メチルノナメチレンジアミン、m−キシリレンジアミン、p−キシリレンジアミン、1,3−ビスアミノメチルシクロヘキサン、1,4−ビスアミノメチルシクロヘキサン、ビス−p−アミノシクロヘキシルメタン、ビス−p−アミノシクロヘキシルプロパン、イソホロンジアミンなどのジアミン、アジピン酸、スベリン酸、アゼライン酸、ゼバシン酸、ドデカン2酸、1,4−シクロヘキサンジカルボン酸、1,3−シクロヘキサンジカルボン酸、テレフタル酸、イソフタル酸、ナフタレンジカルボン酸、ダイマー酸などのジカルボン酸がある。これらの構成成分は単独あるいは2種以上の混合物の形で重合に供され、得られるポアミド樹脂はホモポリマー、コポリマーのいずれであっても良い。
本発明のポリアミド樹脂組成物は、ポリオレフィン系エラストマーを含む。ポリオレフィン系エラストマーを含有することにより、このポリアミド樹脂組成物で構成されるガスバリア層の柔軟性、耐久性を付与することができる。
特に、本発明では、ポリアミド樹脂組成物中のポリオレフィン系エラストマーのうちの40〜100重量%を酸変性エラストマーとしたものが好ましい。
本発明のポリアミド樹脂組成物に含まれる金属化合物は、2価もしくは3価の金属の水酸化物、酸化物、及び炭酸塩から選ばれるものである。
ここで、2価もしくは3価の金属としては、マグネシウム、鉄、亜鉛、カルシウム、ニッケル、コバルト、銅などの2価金属、アルミニウム、鉄、マンガン等の3価金属が挙げられる。
これらの金属の水酸化物、酸化物、炭酸塩としては、具体的には、ハイドロタルサイト、酸化マグネシウム、水酸化マグネシウム、水酸化アルミニウム、酸化カルシウム、炭酸カルシウムなどが挙げられ、特に、優れた受酸効果を持つことが考えられることから、ハイドロタルサイトが好適である。
これらの金属化合物は1種を単独で用いても良く、2種以上を任意の組み合わせ及び比率で併用しても良い。
M1 8−xM2 x(OH)16CO2・nH2O …(I)
本発明のポリアミド樹脂組成物は、樹脂成分としてポリアミド樹脂以外の樹脂成分を含んでいても良いが、その場合において、冷媒輸送用ホース中の全ポリマー成分のうちの70重量%以上がポリアミド樹脂であることが、ガスバリア性の確保のために好ましい。
前述の如く、本発明においては、ポリアミド樹脂組成物の製造に当たり、(a)ポリアミド樹脂と(c)金属化合物とをまず混練し、得られた混練物に、(b)ポリオレフィン系エラストマーを混練してポリマーアロイとする2段階混練を行う。
この混練は、ポリアミド樹脂中に金属化合物が十分に均一に分散される程度であれば良く、混練時間等には特に制限はない。
次に、このような本発明の製造方法により製造される本発明のポリアミド樹脂組成物をガスバリア層の構成材料として用いる本発明の冷媒輸送用ホースについて、図面を参照して説明する。
ガスバリア層2は、本発明のポリアミド樹脂組成物よりなる。
従ってガスバリア層2の膜厚は、50〜400μm、特に100〜300μmであることが好ましい。
内層ゴム層3及び外被ゴム層7を構成するゴムとしては、一般にブチルゴム(IIR)、塩素化ブチルゴム(C1−IIR)、塩素化ポリエチレン、クロロスルホン化ポリエチレン、臭素化ブチルゴム(Br−IIR)、イソブチレン−ブロモパラメチルスチレン共重合体、EPR(エチレン−プロピレン共重合体)、EPDM(エチレン−プロピレン−ジエン三元共重合体)、NBR(アクリロニトリルブタジエンゴム)、CR(クロロプレンゴム)、水素添加NBR、アクリルゴム、エチレンアクリルゴム(AEM)、これらのゴムの2種以上のブレンド物、或いは、これらのゴムを主成分とするポリマーとのブレンド物、好ましくはブチル系ゴム、EPDM系ゴムが用いられる。これらのゴムには、通常用いられる充填剤、加工助剤、老化防止剤、加硫剤、加硫促進剤等の配合処方を適用できる。
第1補強糸層4は、補強糸をスパイラル状に巻き付けたものであり、第2補強糸層6は、この第1補強糸層4とは逆方向にスパイラル状に補強糸を巻き付けたものである。
このような本発明の冷媒輸送用ホースは、常法に従って、マンドレル上にガスバリア層2と内層ゴム層3の材料を所定の厚さに押し出して積層し、補強糸層4を巻き付け、中間ゴム層5を押し出して積層し、補強糸層6を巻きつけ、次いで外被ゴム層7を押し出して積層し、その後140〜170℃で30〜120分間加硫することにより製造することができる。
表1に示す配合にて各材料を混練して試験用ポリアミド系樹脂片を製造した。なお、混練に際しては、東洋精機社製二軸混練り機を用い、ポリアミド樹脂の融点(220℃)以上の温度である230℃にて混練りを行った。
エラストマー:三井化学社製 α−オレフィンポリマー(エチレン・ブテン共重合体
)「タフマーA−1050S」
マレイン酸変性エラストマー:三井化学社製マレイン酸変性α−オレフィンポリマー
(エチレン・ブテン共重合体)「タフマーMH7010」
ハイドロタルサイト:協和化学社製「ハイドロタルサイトDHT−4A」
組成式:Mg4.5Al2(OH)13CO3・3.5H2O
電子顕微鏡(SEM)を用い、リンタングステン酸で表面処理した試験用ポリアミド系樹脂片を観察してエラストマーの分散粒径を調べ、エラストマーの分散粒径が3μm以下をOK、3μmを超えるものをNGとした。
東洋精機社製引張り試験機を用い、各試験用ポリアミド系樹脂片について、引張り速度50mm/minで伸長して弾性率を測定し、比較例5の試験用ポリアミド系樹脂片(100)に対する指数で表記した。
GTRテック社製ガス透過試験機を用い、各試験用ポリアミド系樹脂片について、100℃絶対差圧226cmHgでHeガス透過係数を測定し、比較例5の試験用ポリアミド系樹脂片(100)に対する指数で表記した。
東洋精機社製引張り試験機を用い、以下の老化試験前後の各試験用ポリアミド系樹脂片について、引張り速度50mm/minで伸長して破断強力を測定し、老化試験前の値に対する老化試験後の値の百分率で表記した。
東洋精機社製引張り試験機を用い、以下の老化試験前後の各試験用ポリアミド系樹脂片について、引張り速度50mm/minで伸長して破断伸びを測定し、老化試験前の値に対する老化試験後の値の百分率で表記した。
以下の1〜7の手順で行なった。
1 耐圧容器に1ccの水を入れる。
2 巾10×長さ50mm×厚み0.1mmサイズの試験用ポリアミド系樹脂片を入れ
る。
3 ポリアルキレングリコールオイルを100cc入れる。
4 耐圧容器を15分冷凍した後、5分間耐圧容器を真空引きする。
5 冷媒としてR−134aを100cc入れる。
6 高温槽に150℃で8週間放置する。
7 容器から試験用ポリアミド系樹脂片を取出し、評価測定に供する。
2 ガスバリア層
3 内層ゴム層
4,6 補強糸層
5 中間ゴム層
7 外被ゴム層
Claims (7)
- (a)ポリアミド樹脂と、(b)ポリオレフィン系エラストマーと、(c)2価もしくは3価の金属の水酸化物、酸化物及び炭酸塩よりなる群から選ばれる1種又は2種以上の金属化合物と含むポリアミド樹脂組成物を製造する方法において、
(c)金属化合物と(a)ポリアミド樹脂とを混練する第1の混練工程と、
該第1の混練工程で得られた混練物と(b)ポリオレフィン系エラストマーとを混練する第2の混練工程と
を含むポリアミド樹脂組成物の製造方法であって、
前記ポリアミド樹脂組成物中のポリマー成分と(c)金属化合物との合計に対する(c)金属化合物の割合が1〜10重量%であり、
前記ポリオレフィン系エラストマーの少なくとも一部が酸変性されていることを特徴とするポリアミド樹脂組成物の製造方法。 - 請求項1において、前記(c)金属化合物がハイドロタルサイトであることを特徴とするポリアミド樹脂組成物の製造方法。
- 請求項1又は2において、前記ポリアミド樹脂組成物のポリオレフィン系エラストマーの含有量がポリアミド樹脂組成物の総重量に対して10〜45重量%であることを特徴とするポリアミド樹脂組成物の製造方法。
- 請求項1ないし3のいずれか1項に記載のポリアミド樹脂組成物の製造方法により製造されたポリアミド樹脂組成物。
- 請求項4において、冷媒輸送用ホースのガスバリア層形成用ポリアミド樹脂組成物であることを特徴とするポリアミド樹脂組成物。
- ポリアミド樹脂組成物よりなるガスバリア層を有する冷媒輸送用ホースにおいて、該ポリアミド樹脂組成物が請求項4又は5に記載のポリアミド樹脂組成物であることを特徴とする冷媒輸送用ホース。
- 請求項6において、前記ガスバリア層の外周側に、補強糸よりなる補強層と外被ゴム層とが設けられていることを特徴とする冷媒輸送用ホース。