JP5376327B2 - 吸湿性積層体 - Google Patents
吸湿性積層体 Download PDFInfo
- Publication number
- JP5376327B2 JP5376327B2 JP2010008548A JP2010008548A JP5376327B2 JP 5376327 B2 JP5376327 B2 JP 5376327B2 JP 2010008548 A JP2010008548 A JP 2010008548A JP 2010008548 A JP2010008548 A JP 2010008548A JP 5376327 B2 JP5376327 B2 JP 5376327B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- moisture
- hygroscopic
- layer
- release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記吸湿フィルムが、バインダ樹脂と水分吸着性物質とからなる吸湿層と、該吸湿層の片面または両面に設けられた粘着層とからなり、前記剥離フィルムが、基材と、該基材の少なくとも一方の面に設けられた珪素酸化物の連続薄膜よりなる離型層とからなり、該連続薄膜が、炭素、水素、珪素および酸素からなる群から選択される1種または2種以上の元素からなる化合物の少なくとも1種以上を含有し、該連続薄膜の炭素原子含有量が5原子%以上であり、かつ、前記吸湿フィルムと前記剥離フィルムとが、前記吸湿層または前記粘着層と前記離型層との間で、擬似接着されていることを特徴とするものである。
図1に、本発明の吸湿性積層体の一構成例を示す模式的断面図を示す。図示するように、本発明の吸湿性積層体10は、吸湿フィルム1と、これを挟持する一対の剥離フィルム2とからなる。
剥離フィルム2に用いる基材5としては、これが剥離フィルム2を構成する基本素材となること、および、これに離型層6を構成する珪素酸化物の連続薄膜を設けることから、機械的、物理的、化学的等において優れた性質を有し、強度が高く強靱であって、かつ、耐熱性を有する樹脂のフィルムないしシートを使用することが好ましい。具体的には例えば、ポリエチレン系樹脂、ポリプロピレン系樹脂、環状ポリオレフィン系樹脂、フッ素系樹脂、ポリスチレン系樹脂、アクリロニトリル−スチレン共重合体(AS樹脂)、アクリロニトリル−ブタジエン−スチレン共重合体(ABS樹脂)、ポリ塩化ビニル系樹脂、フッ素系樹脂、ポリ(メタ)アクリル系樹脂、ポリカーボネート系樹脂、ポリエチレンテレフタレート(PET)、ポリエチレンナフタレート(PEN)等のポリエステル系樹脂、各種のナイロン等のポリアミド系樹脂、ポリイミド系樹脂、ポリアミドイミド系樹脂、ポリアリールフタレート系樹脂、シリコ−ン系樹脂、ポリスルホン系樹脂、ポリフェニレンスルフィド系樹脂、ポリエーテルスルホン系樹脂、ポリウレタン系樹脂、アセタール系樹脂、セルロース系樹脂、その他等の各種の樹脂のフィルムないしシートを挙げることができる。中でも特に、ポリプロピレン系樹脂、ポリエステル系樹脂またはポリアミド系樹脂のフィルムないしシートを使用することが好ましく、より好ましくは、吸湿フィルム1と擬似接着させることを考慮して、耐熱性の高い、2軸延伸ポリエステル系樹脂フィルムまたは2軸延伸ポリアミド系樹脂フィルムを用いることが好ましい。
<実施例1>
下記に従い、図1に示す層構成の吸湿性積層体を作製した。
まず、基材5として、厚さ25μmの2軸延伸ポリエチレンテレフタレート(PET)フィルムを使用し、これをプラズマ化学気相成長装置の送り出しロールに装着した。次に、下記に示す蒸着条件に従い、上記2軸延伸PETフィルムの片側のコロナ処理面に、厚み500Åの珪素酸化物の連続薄膜からなる離型層6を形成して、剥離フィルム2を製造した。
蒸着面;コロナ処理面,
導入ガス量;ヘキサメチルジシロキサン:酸素ガス:ヘリウム=10:1:10(単位:slm),
パワ−;3kW,
成膜速度;300m/min,
成膜圧力;2×10−2torr
層構成を、基材(25μm)/離型層(500Å)/粘着層(10μm)/吸湿層(30μm)/粘着層(10μm)/離型層(500Å)/基材(25μm)とした以外は実施例1と同様にして、実施例2の吸湿性積層体を作製した。
吸湿フィルム1の粘着層4形成用の材料として、アクリル系熱可塑性エラストマー(クラレ(株)製,LAポリマー LA2140e,MFR=31(190℃,2.16kg))95質量部と、ロジン系タッキファイヤー(荒川化学工業(株)製,スーパーエステルA100,軟化温度100℃)5質量部とを混合したものを用いた以外は実施例1と同様にして、実施例3の吸湿性積層体を作製した。この吸湿性積層体の層構成は、基材(25μm)/離型層(500Å)/吸湿層(30μm)/粘着層(10μm)/離型層(500Å)/基材(25μm)であった。
基材5として、厚さ15μmの2軸延伸ナイロン6(ONy)フィルムを使用し、これをプラズマ化学気相成長装置の送り出しロールに装着した。次に、下記に示す蒸着条件に従い、上記2軸延伸ナイロン6フィルムの片面に、厚さ500Åの珪素酸化物の連続薄膜からなる離型層6を形成して、剥離フィルム2を製造した。それ以外は実施例1と同様にして、実施例4の吸湿性積層体を作製した。この吸湿性積層体の層構成は、基材(12μm)/離型層(500Å)/吸湿層(30μm)/粘着層(10μm)/離型層(500Å)/基材(12μm)であった。
蒸着面;コロナ処理面,
導入ガス量;ヘキサメチルジシロキサン:酸素ガス:ヘリウム=10:1:10(単位:slm),
パワ−;3kW,
成膜速度;300m/min,
成膜圧力;2×10−2torr
層構成を、基材(12μm)/離型層(500Å)/粘着層(10μm)/吸湿層(30μm)/粘着層(10μm)/離型層(500Å)/基材(12μm)とした以外は実施例4と同様にして、実施例5の吸湿性積層体を作製した。
剥離フィルム2に離型層6を設けない以外は実施例1と同様にして、比較例1の吸湿性積層体を作製した。この吸湿性積層体の層構成は、基材(25μm)/吸湿層(30μm)/粘着層(10μm)/基材(25μm)であった。
剥離フィルム2に離型層6を設けない以外は実施例4と同様にして、比較例2の吸湿性積層体を作製した。この吸湿性積層体の層構成は、基材(12μm)/吸湿層(30μm)/粘着層(10μm)/基材(12μm)であった。
吸湿層3におけるバインダ樹脂と水分吸着性物質との重量比率を、バインダ樹脂:水分吸着性物質=100:0とした以外は実施例1と同様にして、比較例3の吸湿性積層体を作製した。この吸湿性積層体の層構成は、基材(25μm)/離型層(500Å)/吸湿層(30μm)/粘着層(10μm)/離型層(500Å)/基材(25μm)であった。
剥離フィルム2の炭素原子含有量を2原子%とした以外は実施例1と同様にして、比較例4の吸湿性積層体を作製した。この吸湿性積層体の層構成は、基材(25μm)/離型層(500Å)/吸湿層(30μm)/粘着層(10μm)/離型層(500Å)/基材(25μm)であった。
(1)製造直後からの重量変化
上記実施例1〜5および比較例1〜4において作製した吸湿性積層体の寸法10×10cmのサンプルについて、製造直後および25℃75%RHの恒温恒湿槽に1日放置した後の重量を測定し、重量の差異を変化量として記載した。
(2)室温下で3日間放置後の重量変化
上記実施例1〜5および比較例1〜4において作製した吸湿性積層体の寸法10×10cmのサンプルについて、室温下で3日間放置後、剥離層を剥離し、剥離直後および25℃75%RHの恒温恒湿槽に10日放置後の重量変化を測定し、重量の差異を変化量として記載した。
上記の測定結果を、室温下で3日間放置後における剥離層剥離後の吸湿の状況と併せて、下記表2中に示す。
2 剥離フィルム
3 吸湿層
4 粘着層
5 基材
6 離型層
10 吸湿性積層体
11 プラズマ化学気相成長装置
12 真空チャンバー
13 巻き出しロール
14 補助ロール
15 冷却・電極ドラム
16,17 ガス供給装置
18 原料揮発供給装置
19 原料供給ノズル
20 グロー放電プラズマ
21 電源
22 マグネット
23 補助ロール
24 巻き取りロール
25 真空ポンプ
Claims (9)
- 吸湿フィルムと、該吸湿フィルムを挟持する一対の剥離フィルムとからなる吸湿性積層体であって、
前記吸湿フィルムが、バインダ樹脂と水分吸着性物質とからなる吸湿層と、該吸湿層の片面または両面に設けられた粘着層とからなり、前記剥離フィルムが、基材と、該基材の少なくとも一方の面に設けられた珪素酸化物の連続薄膜よりなる離型層とからなり、該連続薄膜が、炭素、水素、珪素および酸素からなる群から選択される1種または2種以上の元素からなる化合物の少なくとも1種以上を含有し、該連続薄膜の炭素原子含有量が5原子%以上であり、かつ、前記吸湿フィルムと前記剥離フィルムとが、前記吸湿層または前記粘着層と前記離型層との間で、擬似接着されていることを特徴とする吸湿性積層体。 - 前記剥離フィルムの前記基材が、2軸延伸ポリエステル系樹脂フィルムまたは2軸延伸ポリアミド系樹脂フィルムからなる請求項1記載の吸湿性積層体。
- 前記剥離フィルムの前記離型層の膜厚が、50〜2000Åである請求項1または2記載の吸湿性積層体。
- 前記吸湿フィルムの前記吸湿層のバインダ樹脂が、温度190℃、荷重2.16kgの条件で測定したMFRが5〜40g/10minであるアクリル系熱可塑性エラストマーである請求項1〜3のうちいずれか一項記載の吸湿性積層体。
- 前記吸湿フィルムの前記吸湿層の水分吸着性物質が、アルカリ金属酸化物、アルカリ土類金属酸化物、硫酸塩、金属ハロゲン化物、過塩素酸および有機物からなる群から選択される少なくとも1種からなる化学的水分吸着性物質である請求項1〜4のうちいずれか一項記載の吸湿性積層体。
- 前記吸湿フィルムの前記吸湿層におけるバインダ樹脂と水分吸着性物質との重量比率が、バインダ樹脂20〜60質量部に対し、水分吸着性物質80〜40質量部である請求項1〜5のうちいずれか一項記載の吸湿性積層体。
- 前記吸湿フィルムの前記粘着層が、アクリル系熱可塑性エラストマーからなる請求項1〜6のうちいずれか一項記載の吸湿性積層体。
- 前記吸湿フィルムの前記粘着層が、アクリル系熱可塑性エラストマーを主成分とし、かつ、ロジン系タッキファイヤーを含む請求項1〜7のうちいずれか一項記載の吸湿性積層体。
- 前記吸湿フィルムの前記粘着層の厚みが、5〜20μmである請求項1〜8のうちいずれか一項記載の吸湿性積層体。