JP5322500B2 - 光学用フィルムおよび偏光板 - Google Patents
光学用フィルムおよび偏光板 Download PDFInfo
- Publication number
- JP5322500B2 JP5322500B2 JP2008136357A JP2008136357A JP5322500B2 JP 5322500 B2 JP5322500 B2 JP 5322500B2 JP 2008136357 A JP2008136357 A JP 2008136357A JP 2008136357 A JP2008136357 A JP 2008136357A JP 5322500 B2 JP5322500 B2 JP 5322500B2
- Authority
- JP
- Japan
- Prior art keywords
- optical film
- carbon atoms
- acrylic resin
- glutarimide
- film according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)以下の成分(A)、(B)を含有する樹脂組成物からなることを特徴とする光学用フィルム。
(A)ガラス転移温度が120℃以上であり、屈折率が1.50以上であるアクリル系樹脂99.5〜70重量%、
(B)エポキシ基含有オレフィン系共重合体0.5〜30重量%
(請求項1)。
(4)アクリル系樹脂が下記一般式(3)で表される単位をさらに含むことを特徴とする請求項3に記載の光学用フィルム。
(5)溶融押出法により得られるフィルムであることを特徴とする請求項1〜4に記載の光学用フィルム。(請求項5)
(6)延伸されたフィルムであることを特徴とする請求項5に記載の光学用フィルム。(請求項6)
(7) 面内位相差が10nm以下であり、かつ厚み方向位相差が50nm以下であることを特徴とする請求項5または6のいずれかに記載の光学用フィルム。(請求項7)
(8)請求項5〜7のいずれかに記載の光学用フィルムを用いた偏光子保護フィルム。(請求項8)
(9)請求項5または6のいずれかに記載の光学用フィルムを用いたことを特徴とする位相差フィルム。(請求項9)
(10)請求項8または9に記載されたフィルムを用いたことを特徴とする偏光板。(請求項10)
(11)以下の成分(A)に成分(B)を混合する際に触媒を用いることを特徴とする光学用フィルムの製造方法。
(A)ガラス転移温度が120℃以上であり、屈折率が1.50以上であるアクリル系樹脂99.5〜70重量%、
(B)エポキシ基含有オレフィン系共重合体0.5〜30重量%。(請求項11)
で表される単位(以下、「グルタルイミド単位」ともいう)と、
下記一般式(2)
で表される単位(以下、「(メタ)アクリル酸エステル単位」ともいう)とを含むグルタルイミド樹脂を好適に用いることができる。
で表される単位(以下、「芳香族ビニル単位」ともいう)をさらに含んでいてもよい。
Rth=|(nx+ny)/2−nz|×d
なお、上記式中において、nx、ny、およびnzは、それぞれ、面内屈折率が最大となる方向をX軸、X軸に垂直な方向をY軸、フィルムの厚さ方向をZ軸とし、それぞれの軸方向の屈折率を表す。また、dはフィルムの厚さ、||は絶対値を表す。
ただし、本発明において、光弾性係数はセナルモン法により、波長515nmにて、23℃、50%RHにおいて測定した値である。
原料の樹脂としてメタクリル酸メチル−スチレン共重合体(スチレン量11モル%)、イミド化剤としてモノメチルアミンを用いて、イミド化樹脂を製造した。
口径30mmの噛合い型同方向回転式二軸押出機を用い、押出機の温度調整ゾーンの設定温度を240℃、スクリュー回転数250rpmとし、グルタルイミドアクリル樹脂(A−1)およびボンドファースト7L(住友化学株式会社製)および触媒テトラ−n−ブチルホスホニウムブロミドを、10kg/hrの割合で供給した。押出機出口に設けられたダイスからストランドとして出てきた樹脂を水槽で冷却し、ペレタイザでペレット化した。
Claims (11)
- 以下のアクリル系樹脂(A)およびエポキシ基含有オレフィン系共重合体(B)を含有する樹脂組成物並びに触媒からなることを特徴とする光学用フィルム。
(A)グルタルイミド構造、無水グルタル酸構造またはラクトン構造を分子中の単位とし、且つガラス転移温度が120℃以上であり、屈折率が1.50以上であるアクリル系樹脂99.5〜70重量%、
(B)エポキシ基含有オレフィン系共重合体0.5〜30重量%。 - アクリル系樹脂(A)の屈折率が、1.52〜1.56であることを特徴とする請求項1に記載の光学用フィルム。
- アクリル系樹脂(A)が、下記一般式(1)で表される単位と、下記一般式(2)で表される単位とを有するグルタルイミドアクリル樹脂であることを特徴とする請求項1または2に記載の光学用フィルム。
- アクリル系樹脂(A)が下記一般式(3)で表される単位をさらに含むことを特徴とする請求項3に記載の光学用フィルム。
- 溶融押出法により得られるフィルムであることを特徴とする請求項1〜4のいずれかに記載の光学用フィルム。
- 延伸されたフィルムであることを特徴とする請求項5に記載の光学用フィルム。
- 面内位相差が10nm以下であり、かつ厚み方向位相差が50nm以下であることを特徴とする請求項5または6に記載の光学用フィルム。
- 請求項5〜7のいずれかに記載の光学用フィルムを用いた偏光子保護フィルム。
- 請求項5または6に記載の光学用フィルムを用いたことを特徴とする位相差フィルム。
- 請求項8または9に記載のフィルムを用いたことを特徴とする偏光板。
- 以下のアクリル系樹脂(A)にエポキシ基含有オレフィン系共重合体(B)を混合する際に触媒を用いることを特徴とする光学用フィルムの製造方法。
(A)グルタルイミド構造、無水グルタル酸構造またはラクトン構造を分子中の単位とし、且つガラス転移温度が120℃以上であり、屈折率が1.50以上であるアクリル系樹脂99.5〜70重量%、
(B)エポキシ基含有オレフィン系共重合体0.5〜30重量%。