JP5313455B2 - 表面保護フィルム - Google Patents
表面保護フィルム Download PDFInfo
- Publication number
- JP5313455B2 JP5313455B2 JP2007054090A JP2007054090A JP5313455B2 JP 5313455 B2 JP5313455 B2 JP 5313455B2 JP 2007054090 A JP2007054090 A JP 2007054090A JP 2007054090 A JP2007054090 A JP 2007054090A JP 5313455 B2 JP5313455 B2 JP 5313455B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- protective film
- resin
- surface protective
- acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ポリエステルフィルムの片面に、ポリエステル樹脂、アクリル樹脂、アクリル変性ポリエステル樹脂およびウレタン樹脂の群から選択される少なくとも1種の樹脂成分、帯電防止剤および濡れ調整剤の含有量が下記式(1)〜(3)を満足する塗液から表面層を形成するに際して、
該濡れ調整剤が、炭素数が12以上のアルキル側鎖を持つアルキルアクリレートとアクリル酸との共重合体、または、ポリビニルアルコールまたはポリエチレンイミンを塩素化アルキロイルまたはアルキルイソシアネートで長鎖アルキル化した共重合体であり、
該塗液は、沸点150℃以上の水溶性または水混和性の液体を該塗液中の溶媒総重量を基準として0.2〜3.0重量%含有する
ことを特徴とする表面保護フィルムの製造方法が提供される。
(1)7≦A≦40
(2)0≦B≦3
(3)57≦C≦93
(式中、Aは帯電防止剤の含有量(重量%)、Bは濡れ調整剤の含有量(重量%)、Cはポリエステル樹脂、アクリル樹脂、アクリル変性ポリエステル樹脂およびウレタン樹脂の群から選択される少なくとも1種の樹脂成分の含有量(重量%)を表す。ここで含有量(重量%)は、塗液中の有効成分(溶媒を除いた成分)重量を基準とした含有量である。)
・帯電防止剤が下記一般式で表される単位を主たる繰返し単位とするポリチオフェンからなる導電性ポリマーであり、かつ表面保護フィルムの表面層の膜厚が0.03〜0.10μmであり、表面固有抵抗率が1×10 5 〜1×10 12 Ω/□であること、
・濡れ調整剤が、ポリビニルアルコールまたはポリエチレンイミンを塩素化アルキロイルまたはアルキルイソシアネートで長鎖アルキル化した共重合体であって、表面保護フィルムの表面層の水の接触角が70°以下であること、
・表面保護フィルムの表面層のアクリル系粘着テープに対する剥離強度が5N/25mm以上であること、
・表面保護フィルムが、ポリエステルフィルムと表面層との間に、主成分としてシランカップリング剤を含有する塗液から形成されたプライマー層を有すること、
・表面保護フィルムの粘着剤層の粘着力が0.03〜0.50N/25mmであること、
・表面保護フィルムが、偏光板、位相差板または視野角拡大フィルムの表面保護に用いられること、
の少なくともひとつの要件を具備する表面保護フィルムの製造方法が提供される。
本発明の表面保護フィルムは、ポリエステルフィルムの片側の面に、ポリエステル樹脂、アクリル樹脂、アクリル変性ポリエステル樹脂およびウレタン樹脂の群から選択される少なくとも1種の樹脂成分(以下単に樹脂成分と称することがある)、好ましくはケトン系溶剤を含有するインキに対する印字性を有する樹脂成分、帯電防止剤、および、必要に応じてさらに濡れ調整剤を含有する塗液から形成された表面層を有し、他方の面に粘着剤層を有している必要がある。
かかるアクリル樹脂の重量平均分子量は表面層塗膜の耐削れ性および耐ブロッキング性の点から10,000〜500,000の範囲であることが好ましい。
表面層の膜厚は0.02〜0.20μmの範囲が好ましく、さらに好ましくは0.03〜0.10μmの範囲である。
なかでも、ポリエチレンテレフタレートまたはポリエチレン−2,6−ナフタレートが特に好ましい。
アドバンテスト社製抵抗率計を使用し、測定温度23℃、測定湿度65%RHの雰囲気で、印加電圧100Vで1分後の表面固有抵抗率を測定した。なお、表面固有抵抗率としては、1×1012Ω/□以下であること好ましい。
LINX社製インクジェットプリンター(16ドット仕様)で、赤インク1018(MEKとして75〜85重量%含有)を使用し、表面保護フィルムの粘着剤層面をガラス板に貼り合せ、表面層側を上にして30m/分のコンベアに流し、「0」を印字して評価用サンプルを得た。得られた評価用サンプルを使い、(i)ドットの観察と(ii)セロハンテープでの印字部分密着性を評価した。
(i)ドット観察
コロナ処理をしたポリエステルフィルムに印字した時のドットの平均直径を1.00とした場合の、測定サンプルのドットの平均直径の比率より、下記基準で判定し、△以上を合格とした。
○:0.85以上、1.20未満
△:0.60以上、0.85未満又は1.20以上、1.50未満
×:0.60未満
(ii)印字部分の密着性
印字部分にセロハンテープ(ニチバン製エルパック18mm幅または24mm幅)をゴムロールで貼合せ、ついで5kgの圧着ローラーで圧着して5分後に、180°剥離して印字部分をルーペで観察し、下記の基準で判定した。△以上を合格とした。
○:印字部分の脱落が殆ど認められない。
△:印字部分の脱落が部分的に認められる。
×:印字部分の殆どが表面層とインキの界面で剥がれている。
イオン交換水に1分間浸漬した後、イオン交換水を含ませたベンコットに500g/cm2となるように重りをのせ、一方方向に5回擦って表面層の脱落度合を目視観察し、下記基準で判定。
◎:擦る回数を10回にしても変化がない。
○:全く変化しないか、薄くキズが残る。
△:擦った後が薄く変色する。
×:擦った部分の50%以上が完全にポリエステルフィルムの地肌が現れる。または白く濁る。
エルマ接触角測定画像解析装置を用いて、水を滴下後10秒後の接触角を測定した。
表面保護フィルムの表面層側にアクリル系粘着テープ(ニットー31B)をゴムロールで貼合せ、5kgの圧着ローラーで圧着し1時間放置後、表面保護フィルムの粘着剤層側に積層されている離型フィルムを剥離除去して粘着剤面をアルミ支持板に両面テープで固定し、該アクリル系粘着テープを180°に折り返し、引張試験機にて剥離強度を測定した。なお、剥離強度の好ましい範囲は5N/25mm以上である。剥離強度が5N/25mm未満であると表面保護フィルムを剥離する粘着テープの貼り付きが悪く、表面保護フィルムを剥離できないといった不具合を生じるため好ましくない。
洗浄されたステンレス板の上に、表面保護フィルムを直接ゴムローラー(軽荷重)で貼りつけ、その上から荷重2kgのゴムローラーにて1往復し、密着させる。そのまま温度23℃、湿度50〜60%RHの条件下で1日放置し、その後25mm幅の短冊状に切り取る。これを引張試験機(東洋精機(株)製ストログラフ)に取り付けステンレス板を固定し、積層フィルムの方を、300mm/分で180°にて引張り、その強度をもって粘着力とする。
厚みが38μmの2軸配向ポリエチレンテレフタレートフィルムの両面にコロナ処理を行い、ぬれ張力試験用混合液でぬれ張力が54mN/m以上にしたポリエステルフィルムの片面に表1に記載の表面層組成1〜6を有効成分として濃度が2重量%になるように作成した塗工液を、リバースロールコーターを用いて塗布量を4g/m2で塗工し、ドライヤーゾーン140℃下で1分間の乾燥により、表面層を設けたポリエステルフィルムを得た。次に、アクリル系粘着剤として、2−エチルヘキシルアクリレート(主モノマー)、n−ブチルアクリレート(主モノマー)、酢酸ビニル(コモノマー)、2−ヒドロキシエチルメタクリレート(官能基含有モノマー)が5:2:2:1の重量比で混合された組成物と、エポキシ変性ステアリルアクリレートからなる添加剤とを、前者の組成物10重量部に対し後者の添加物0.5重量部となるように加え、酢酸エチルの溶剤下で反応触媒としてアゾビスイソブチロニトリルを用い溶液重合した。得られた粘着剤用ポリマーの重量平均分子量は約35万であった。この粘着剤用ポリマーに、TDI系イソシアネート架橋剤(日本ポリウレタン社製コロネートL)を固形分比で粘着剤用ポリマー100重量部に対し、架橋剤7重量部の割合で添加した後、25μmのポリエステルフィルムの片面にシリコーン離型層を持つ剥離フィルムの離型層側面に乾燥後の厚みが15μmとなるように塗布し、100℃2分乾燥した後、前記表面層を設けたポリエステルフィルムの表面層とは反対側の面と該粘着剤面とを貼り合せた、45℃で1週間のエージング処理を行い実施例1、2と比較例1〜4の表面保護フィルムを得た。得られた表面保護フィルムの物性を表2にまとめた。
縦延伸終了後のフィルムの片面に、プライマー層として下記の塗布液を、乾燥横延伸後の厚みが40nmとなるように塗布し、同じ条件で製膜した2軸配向ポリエステルフィルムを使用したこと以外、実施例2と同じ条件で表面保護フィルムを作成した。得られた表面保護フィルムの物性を表2にまとめた。
バイトロンP スタルク株式会社
レザムM643 中京油脂株式会社
DMSO 和光純薬工業株式会社
エマルゲン420 花王株式会社
Claims (7)
- ポリエステルフィルムの片面に表面層、他面に粘着剤層を有する表面保護フィルムの製造方法であって、
ポリエステルフィルムの片面に、ポリエステル樹脂、アクリル樹脂、アクリル変性ポリエステル樹脂およびウレタン樹脂の群から選択される少なくとも1種の樹脂成分、帯電防止剤および濡れ調整剤の含有量が下記式(1)〜(3)を満足する塗液から表面層を形成するに際して、
該濡れ調整剤が、炭素数が12以上のアルキル側鎖を持つアルキルアクリレートとアクリル酸との共重合体、または、ポリビニルアルコールまたはポリエチレンイミンを塩素化アルキロイルまたはアルキルイソシアネートで長鎖アルキル化した共重合体であり、
該塗液は、沸点150℃以上の水溶性または水混和性の液体を該塗液中の溶媒総重量を基準として0.2〜3.0重量%含有する
ことを特徴とする表面保護フィルムの製造方法。
(1)7≦A≦40
(2)0≦B≦3
(3)57≦C≦93
(式中、Aは帯電防止剤の含有量(重量%)、Bは濡れ調整剤の含有量(重量%)、Cはポリエステル樹脂、アクリル樹脂、アクリル変性ポリエステル樹脂およびウレタン樹脂の群から選択される少なくとも1種の樹脂成分の含有量(重量%)を表す。ここで含有量(重量%)は、塗液中の有効成分(溶媒を除いた成分)重量を基準とした含有量である。) - 濡れ調整剤が、ポリビニルアルコールまたはポリエチレンイミンを塩素化アルキロイルまたはアルキルイソシアネートで長鎖アルキル化した共重合体であって、表面保護フィルムの表面層の水の接触角が70°以下である請求項1または2記載の表面保護フィルムの製造方法。
- 表面保護フィルムの表面層のアクリル系粘着テープに対する剥離強度が5N/25mm以上である請求項1〜3のいずれか1項に記載の表面保護フィルムの製造方法。
- 表面保護フィルムが、ポリエステルフィルムと表面層との間に、主成分としてシランカップリング剤を含有する塗液から形成されたプライマー層を有する請求項1〜4のいずれか1項に記載の表面保護フィルムの製造方法。
- 表面保護フィルムの粘着剤層の粘着力が0.03〜0.50N/25mmである請求項1〜5のいずれか1項に記載の表面保護フィルムの製造方法。
- 表面保護フィルムが、偏光板、位相差板または視野角拡大フィルムの表面保護に用いられる請求項1〜6のいずれか1項に記載の表面保護フィルムの製造方法。