JP5300173B2 - 樹脂組成物およびそれを成形してなる成形体 - Google Patents
樹脂組成物およびそれを成形してなる成形体 Download PDFInfo
- Publication number
- JP5300173B2 JP5300173B2 JP2005517742A JP2005517742A JP5300173B2 JP 5300173 B2 JP5300173 B2 JP 5300173B2 JP 2005517742 A JP2005517742 A JP 2005517742A JP 2005517742 A JP2005517742 A JP 2005517742A JP 5300173 B2 JP5300173 B2 JP 5300173B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- mass
- biodegradable polyester
- resin composition
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(1)架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とし、樹脂(A)〜(C)の合計量100質量部あたりさらにシリコーン化合物(D)0.05〜10質量部を含んでいることを特徴とする樹脂組成物。
(2)架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とし、樹脂(A)〜(C)の合計量100質量部あたり、さらに変性されたオレフィン重合体又はオレフィン共重合体(E)0.1〜20質量部を含んでいることを特徴とする樹脂組成物。
(3)架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とした樹脂組成物であり、架橋生分解性ポリエステル樹脂(A)が、生分解性ポリエステル樹脂100質量部あたり、0.01〜20質量部の(メタ)アクリル酸エステル化合物と0.01〜20質量部の過酸化物とを反応させて得られたものであり、(メタ)アクリル酸エステル化合物が分子内に2個以上の(メタ)アクリル基を有する化合物であることを特徴とする樹脂組成物。
(4)架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とした樹脂組成物であり、架橋生分解性ポリエステル樹脂(A)の生分解性ポリエステル樹脂がポリ乳酸あるいはポリ乳酸を主成分とするものであることを特徴とする樹脂組成物。
(5)架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とした樹脂組成物であり、樹脂(A)〜(C)の合計量100質量部に対し、さらに末端基としてイソシアネートを有するカルボジイミド化合物0.01〜5質量部を含んでいることを特徴とする樹脂組成物。
(6)樹脂(B)と樹脂(C)との質量比が(B)/{(B)+(C)}≧0.3の関係
をみたす(1)から(5)までのいずれかの樹脂組成物。
(7)架橋生分解性ポリエステル樹脂(A)の生分解性ポリエステル樹脂が、植物由来原料から製造されたものである(1)から(6)までのいずれかの樹脂組成物。
(8)(1)から(7)までいずれかに記載の樹脂組成物を成形してなる成形体。
本発明の樹脂組成物は、架橋生分解性ポリエステル樹脂(A)と、ポリカーボネート樹脂(B)と、必要に応じさらにアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)とが混合されたものである。
1.評価項目
(1)メルトフローレート(MFR):
JIS規格K−7210(試験条件4)に従い、190℃、荷重21.2Nで測定した。
(2)極限粘度(IV):
フェノール/1,1,2,2−テトラクロロエタン混合溶媒(質量比6/4)を用い、温度20℃で測定した。
(3)熱変形温度(DTUL):
ASTM規格D−648に従い、荷重0.45MPaで測定した。試験片は次のように作成した。すなわち、射出成形機(東芝機械社製IS−80G型)を用い、シリンダ温度210〜240℃で樹脂を溶融して、射出圧力100MPa、射出時間15秒で70℃の金型に充填し、30秒間冷却した。
(4)衝撃強度(IZOD衝撃強度):
ASTM規格D−256に従い、ノッチ(V字型切込み)付き試験片を用いて測定した。試験片は(3)と同様の成形方法により得た。
(5)曲げ弾性率:
ASTM規格D−790に従い、変形速度1mm/分で荷重をかけて測定した。試験片は(3)と同様の成形方法により得た。
(6)曲げ強度:
ASTM規格D−790に従い、変形速度1mm/分で荷重をかけて測定した。試験片は(3)と同様の成形方法により得た。
(7)耐湿熱性:
(6)で得られた曲げ強度試験片を温度60℃、湿度95%RHの環境下で800時間処理した後、曲げ強度を測定して、処理時間0の値に対する強度保持率によって表した。
(8)流動性:
厚み1mmのバー状金型を使用し、射出成形機(東芝機械社製IS−80G型)によって、シリンダ温度220℃、金型温度70℃、射出圧力100MPaで成形をおこない、流動長(mm)を測定した。ポリ乳酸、架橋ポリ乳酸または架橋ポリ乳酸/ポリブチレンサクシネート樹脂の成形条件は、(3)に準じた。流動長が大きいほど流動性に優れている。
(9)反り量:
正方形平板の成形試験を実施した(正方形の一辺がフィルムゲートで60.0mm×60.0mm×厚み1mmの金型を使用)。成形温度は220℃、金型温度は70℃に、それぞれ設定した。ポリ乳酸、架橋ポリ乳酸または架橋ポリ乳酸/ポリブチレンサクシネート樹脂の成形条件は、(3)に準じた。射出速度・射出圧力は、成形収縮率が0.2%となるように設定した。得られた平板成形品を凸側を上にして水平な台の上に置き、その高さを測定した。反り量は、(反り高さ)/(平板対角線長さ)×100(%)で評価した。この値が0.5%以下であれば成形品の実用上問題ない範囲と判断できる。
(10)コンパウンド操業性:
コンパウンド時の状態を観察して、下記のように評価した。
(11)成形品外観:
成形品の外観を観察して、下記のよう分類し、○を合格とした。
×:ムラが非常に目立つ。
2.原料
(1)ポリ乳酸樹脂:
カーギルダウ社製 Nature Works 6201DK;MFR=10g/10分、融点168℃(以下、「PLA」と略称する)。
(2)架橋ポリ乳酸樹脂:
次の通りに作製した。
(3)架橋ポリ乳酸/ポリブチレンサクシネート樹脂:
次の通りに作製した。
(4)PC樹脂:
住友ダウ社製200−13(IV=0.49)。
(5)PC樹脂/ABS樹脂の混合体(PC樹脂比率約40質量%):
住友ダウ社製IM−6100(以下、「PC/ABS」と略称する)。
(6)ポリメタクリル酸メチルがグラフト共重合されたエチレングリシジルメタクリレート共重合体:
日本油脂社製モディパーA4200(以下、「EGMA−gf−PMMA」と略称する)。
(7)シリコーン化合物:
・GE東芝シリコーン社製メチルフェニルシリコーンオイル TSF−433
・信越シリコーン社製メチルフェニルシリコーンオイル KF−54
・GE東芝シリコーン社製アミノ変性シリコーンオイル TSF4707
・GE東芝シリコーン社製エポキシ変性シリコーンオイル TSF4730
・GE東芝シリコーン社製ヒドロキシ末端メチルフェニルシリコーン YF3804
(8)カルボジイミド化合物:
・日清紡社製LA−1;イソシアネート基含有率1〜3%
・日清紡社製HMV−8CA;イソシアネート基封止品
実施例1〜34
各原料を、表1、3、4に示す割合で二軸押出機(東芝機械社製TEM−37BS)に供給し、加工温度220℃〜240℃で溶融混練押出しをおこない、吐出された樹脂をペレット状にカッティングして、樹脂組成物A〜HHを得た。なおカルボジイミド化合物を添加する場合にサイドフィードで供給した他は、全ての原料をトップフィード口から同時に供給した。
比較例1〜13
各原料を、表2〜4に示す割合で二軸押出機(東芝機械社製TEM−37BS)に供給し、加工温度210℃〜230℃で溶融混練押出しをおこない、吐出された樹脂をペレット状にカッティングして、樹脂組成物II〜UUを得た。この場合に、比較例1、2、4、8、12、13では、ノズルから溶融樹脂が脈動しながら吐出されて、ペレット化が困難であった。なお、比較例6、7では樹脂原料をそのまま各種試験片作成の射出成形に供した。
Claims (8)
- 架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とし、樹脂(A)〜(C)の合計量100質量部あたり、さらにシリコーン化合物(D)0.05〜10質量部を含んでいることを特徴とする樹脂組成物。
- 架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とし、樹脂(A)〜(C)の合計量100質量部あたり、さらに変性されたオレフィン重合体又はオレフィン共重合体(E)0.1〜20質量部を含んでいることを特徴とする樹脂組成物。
- 架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とした樹脂組成物であり、架橋生分解性ポリエステル樹脂(A)が、生分解性ポリエステル樹脂100質量部あたり、0.01〜20質量部の(メタ)アクリル酸エステル化合物と0.01〜20質量部の過酸化物とを反応させて得られたものであり、(メタ)アクリル酸エステル化合物が分子内に2個以上の(メタ)アクリル基を有する化合物であることを特徴とする樹脂組成物。
- 架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とした樹脂組成物であり、架橋生分解性ポリエステル樹脂(A)の生分解性ポリエステル樹脂がポリ乳酸あるいはポリ乳酸を主成分とするものであることを特徴とする樹脂組成物。
- 架橋生分解性ポリエステル樹脂(A)30〜90質量%、ポリカーボネート樹脂(B)10〜70質量%およびアクリロニトリル/ブタジエン/スチレン系共重合樹脂(C)0〜50質量%を含み、樹脂(A)〜(C)の合計を100質量%とした樹脂組成物であり、樹脂(A)〜(C)の合計量100質量部に対し、さらに末端基としてイソシアネートを有するカルボジイミド化合物0.01〜5質量部を含んでいることを特徴とする樹脂組成物。
- 樹脂(B)と樹脂(C)との質量比が(B)/{(B)+(C)}≧0.3の関係をみたすことを特徴とする請求項1から5までのいずれか1項に記載の樹脂組成物。
- 架橋生分解性ポリエステル樹脂(A)の生分解性ポリエステル樹脂が、植物由来原料から製造されたものであることを特徴とする請求項1から6までのいずれか1項に記載の樹脂組成物。
- 請求項1から7までのいずれか1項に記載の樹脂組成物を成形してなる成形体。