JP4876790B2 - Light emitting device and white conversion sheet - Google Patents

Light emitting device and white conversion sheet Download PDF

Info

Publication number
JP4876790B2
JP4876790B2 JP2006230310A JP2006230310A JP4876790B2 JP 4876790 B2 JP4876790 B2 JP 4876790B2 JP 2006230310 A JP2006230310 A JP 2006230310A JP 2006230310 A JP2006230310 A JP 2006230310A JP 4876790 B2 JP4876790 B2 JP 4876790B2
Authority
JP
Japan
Prior art keywords
light
ultraviolet
ultraviolet led
resin layer
phosphor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2006230310A
Other languages
Japanese (ja)
Other versions
JP2008053590A (en
Inventor
大輔 松浦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Priority to JP2006230310A priority Critical patent/JP4876790B2/en
Publication of JP2008053590A publication Critical patent/JP2008053590A/en
Application granted granted Critical
Publication of JP4876790B2 publication Critical patent/JP4876790B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide a light-emitting device that is less apt to color variations and a sheet for conversion to white that is used therefor. <P>SOLUTION: The light-emitting device comprises a plurality of ultraviolet LED light sources, having an ultraviolet LED chip; and the sheet for conversion to white that is provided on the plurality of ultraviolet LED light sources, disposed at a space that allows ultraviolet light emitted from the ultraviolet LED chip to be converted into a visible light, contains a plural kinds of fluorescent substances for converting the ultraviolet light into visible lights that differ in wavelength from each other, and has a resin layer capable of substantially obtaining white color light through color mixture of the light emitted from the plural kinds of fluorescent substances. <P>COPYRIGHT: (C)2008,JPO&amp;INPIT

Description

本発明は、紫外発光ダイオード（紫外ＬＥＤ）を備え、白色光を発光する発光装置、およびそれに用いる白色変換シートに関するものである。   The present invention relates to a light emitting device that includes an ultraviolet light emitting diode (ultraviolet LED) and emits white light, and a white conversion sheet used therefor.

従来、紫外光を放射する紫外ＬＥＤチップと、この紫外ＬＥＤチップが放射する紫外光を吸収して、青色光、緑色光、赤色光等を発光する蛍光体を含有する色変換部とを備え、白色光を発光する紫外ＬＥＤが知られている（例えば、特許文献１参照）。   Conventionally, an ultraviolet LED chip that emits ultraviolet light, and a color conversion unit that contains a phosphor that absorbs ultraviolet light emitted by this ultraviolet LED chip and emits blue light, green light, red light, and the like, An ultraviolet LED that emits white light is known (see, for example, Patent Document 1).

一般に、紫外ＬＥＤにおいて、色変換部は、ＬＥＤ実装部に設けられ、紫外ＬＥＤチップ上に直接形成される。
紫外ＬＥＤにおけるＬＥＤ実装部は微小なサイズであるので、ＬＥＤ実装部に色変換部を設ける際には、蛍光体の量を制御するのが困難である。そのため、個々の紫外ＬＥＤによって色のばらつき（色温度のばらつき）が生じやすくなる。例えば、白色光を発光する発光装置を得たい場合に、紫外ＬＥＤ毎に蛍光体の量にばらつきがあると、個々の紫外ＬＥＤによって得られる発光色の色調が変化する。これは、色変換部に含有される各色の蛍光体が発光する光の比率によって色調が決定されるためである。このような色調のばらつきは、特に複数個の紫外ＬＥＤを面状に設けた場合には、色むらとして容易に判別されてしまう。 Generally, in an ultraviolet LED, the color conversion part is provided in the LED mounting part and is directly formed on the ultraviolet LED chip.
Since the LED mounting part in the ultraviolet LED has a very small size, it is difficult to control the amount of the phosphor when the color conversion part is provided in the LED mounting part. For this reason, color variations (color temperature variations) are easily caused by individual ultraviolet LEDs. For example, when it is desired to obtain a light emitting device that emits white light, if there is a variation in the amount of phosphor for each ultraviolet LED, the color tone of the emission color obtained by each ultraviolet LED changes. This is because the color tone is determined by the ratio of the light emitted by the phosphors of each color contained in the color conversion unit. Such variation in color tone is easily determined as color unevenness, particularly when a plurality of ultraviolet LEDs are provided in a planar shape.

一般に、紫外ＬＥＤにおける色変換部は、樹脂中に蛍光体を分散させたものである。上述したように、色変換部は紫外ＬＥＤチップ上に直接形成されるので、色変換部に含まれる樹脂は、高エネルギーの紫外光や、紫外ＬＥＤチップの発熱による熱に晒されることになり、劣化する。また、色変換部に含まれる蛍光体も、高エネルギーの紫外光や、紫外ＬＥＤチップの発熱による熱に晒されて、劣化したり、温度消光が生じたりする。   In general, the color conversion part in an ultraviolet LED is obtained by dispersing a phosphor in a resin. As described above, since the color conversion part is directly formed on the ultraviolet LED chip, the resin contained in the color conversion part is exposed to high energy ultraviolet light and heat generated by the ultraviolet LED chip, to degrade. Further, the phosphor contained in the color conversion unit is also exposed to heat of high energy ultraviolet light or heat generated by the ultraviolet LED chip, and deteriorates or temperature quenching occurs.

このような問題を解決するために、紫外光ＬＥＤチップと、この紫外光ＬＥＤチップに対して距離おいて配置された色変換部とを備える紫外光ＬＥＤが提案されている（例えば、特許文献１参照）。   In order to solve such a problem, an ultraviolet LED including an ultraviolet LED chip and a color conversion unit disposed at a distance from the ultraviolet LED chip has been proposed (for example, Patent Document 1). reference).

特開２００５−１３６００６号公報JP 2005-136006 A

しかしながら、複数個の上記紫外光ＬＥＤを設ける場合には、紫外光ＬＥＤ毎に色変換部を形成するため、やはりＬＥＤ光源毎に色のばらつきが生じると考えられる。
本発明は、上記問題点に鑑みてなされたものであり、色のばらつきが生じにくい発光装置、およびそれに用いられる白色変換シートを提供することを主目的とする。 However, in the case where a plurality of the ultraviolet light LEDs are provided, a color conversion portion is formed for each ultraviolet light LED, so that it is considered that color variation also occurs for each LED light source.
The present invention has been made in view of the above problems, and a main object of the present invention is to provide a light-emitting device in which color variations are unlikely to occur and a white conversion sheet used therefor.

上記目的を達成するために、本発明は、紫外ＬＥＤチップを有する複数個の紫外ＬＥＤ光源と、上記複数個の紫外ＬＥＤ光源に対して設けられ、かつ上記紫外ＬＥＤチップに対して、上記紫外ＬＥＤチップから放射される紫外光を可視光に変換し得る間隙をおいて配置され、上記紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有し、上記複数種の蛍光体からの発光の混色により実質的に白色光を得ることが可能な樹脂層を有する白色変換シートとを備えることを特徴とする発光装置を提供する。   In order to achieve the above object, the present invention provides a plurality of ultraviolet LED light sources having ultraviolet LED chips, the plurality of ultraviolet LED light sources, and the ultraviolet LED chips. It is arranged with a gap that can convert ultraviolet light emitted from the chip into visible light, and contains a plurality of types of phosphors that convert the ultraviolet light into visible light of different wavelengths. And a white conversion sheet having a resin layer capable of obtaining substantially white light by mixing the emitted light.

本発明によれば、白色変換シートが複数個の紫外ＬＥＤ光源に対して設けられ、白色変換シートおよび紫外ＬＥＤ光源が別の部材として設けられているので、白色変換シートを構成する樹脂層では、層中に蛍光体を均一に分散させることができる。これにより、色のばらつきを抑制することが可能である。さらに、本発明によれば、紫外ＬＥＤ光源の紫外ＬＥＤチップと白色変換シートとが所定の間隙をおいて配置されているので、紫外ＬＥＤチップの発熱や紫外ＬＥＤチップからの紫外光の高エネルギーにより、樹脂および蛍光体の劣化や、蛍光体の温度消光を抑制することが可能である。これにより、色むらのない均質な白色光を得ることができる。
さらに、白色変換シートを構成する樹脂層は、樹脂中に蛍光体が分散されたものであり、成形性に優れているので、種々の形状を有する発光装置を得ることが可能である。
また、従来のように紫外ＬＥＤ光源毎に蛍光体を含有する色変換部を設ける場合と比較して、白色変換シートの大面積化が可能であるので、蛍光体の含有量の制御、および、樹脂層全体で蛍光体の含有量を均一にするのが容易である。 According to the present invention, since the white conversion sheet is provided for a plurality of ultraviolet LED light sources, and the white conversion sheet and the ultraviolet LED light source are provided as separate members, in the resin layer constituting the white conversion sheet, The phosphor can be uniformly dispersed in the layer. Thereby, it is possible to suppress color variation. Furthermore, according to the present invention, since the ultraviolet LED chip of the ultraviolet LED light source and the white color conversion sheet are arranged with a predetermined gap, the heat generated by the ultraviolet LED chip and the high energy of the ultraviolet light from the ultraviolet LED chip. It is possible to suppress degradation of the resin and the phosphor and temperature quenching of the phosphor. Thereby, uniform white light without color unevenness can be obtained.
Furthermore, since the resin layer constituting the white conversion sheet is obtained by dispersing the phosphor in the resin and has excellent moldability, it is possible to obtain light emitting devices having various shapes.
In addition, compared with the conventional case where a color conversion part containing a phosphor is provided for each ultraviolet LED light source, the white conversion sheet can be increased in area, so the control of the phosphor content, and It is easy to make the phosphor content uniform throughout the resin layer.

上記発明においては、上記蛍光体が、上記紫外光を青色光に変換する青色蛍光体、上記紫外光を緑色光に変換する緑色蛍光体、および、上記紫外光を赤色光に変換する赤色蛍光体であってもよい。このような構成とすることにより、白色光を発光する発光装置を得ることができ、また演色性を高めることができるからである。   In the above invention, the phosphor is a blue phosphor that converts the ultraviolet light into blue light, a green phosphor that converts the ultraviolet light into green light, and a red phosphor that converts the ultraviolet light into red light. It may be. This is because with such a configuration, a light-emitting device that emits white light can be obtained, and color rendering can be improved.

また本発明においては、上記白色変換シートが、上記樹脂層上に形成された光導入層をさらに有していてもよい。白色変換シートに光導入層が形成されていることにより、紫外ＬＥＤ光源からの紫外光を樹脂層に効率的に入射させたり、光取り出し効率を高めたりすることができるからである。   In the present invention, the white conversion sheet may further include a light introduction layer formed on the resin layer. This is because the light introduction layer is formed on the white conversion sheet, so that the ultraviolet light from the ultraviolet LED light source can be efficiently incident on the resin layer and the light extraction efficiency can be increased.

本発明は、また、上述の発光装置に用いられ、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射される紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有し、上記複数種の蛍光体からの発光の混色により実質的に白色光を得ることが可能な樹脂層を有することを特徴とする白色変換シートを提供する。   The present invention also includes a plurality of types of phosphors that are used in the above-described light emitting device and convert ultraviolet light emitted from an ultraviolet LED chip of an ultraviolet LED light source into visible light having different wavelengths. Provided is a white conversion sheet having a resin layer capable of obtaining substantially white light by mixing colors of light emitted from a phosphor.

本発明の白色変換シートは、上述の発光装置に用いられるものであるので、所定の発光装置に用いた場合には、上述したように、色のばらつき、樹脂および蛍光体の劣化、蛍光体の温度消光を抑制することが可能である。また、樹脂層は、樹脂中に蛍光体が分散されたものであり、成形性に優れているので、本発明の白色変換シートを用いて発光装置を作製する場合には、種々の形状を有する発光装置を得ることが可能である。さらに、本発明の白色変換シートは大面積化が可能であるので、蛍光体の含有量の制御、および、樹脂層中に蛍光体を均一に分散させるのが容易である。   Since the white conversion sheet of the present invention is used in the above-described light emitting device, when used in a predetermined light emitting device, as described above, color variation, resin and phosphor degradation, phosphor phosphor It is possible to suppress temperature quenching. In addition, since the resin layer is obtained by dispersing the phosphor in the resin and has excellent moldability, the resin layer has various shapes when the light-emitting device is produced using the white conversion sheet of the present invention. A light emitting device can be obtained. Furthermore, since the white conversion sheet of the present invention can have a large area, it is easy to control the phosphor content and to uniformly disperse the phosphor in the resin layer.

本発明によれば、白色変換シートが、複数個の紫外ＬＥＤ光源に対して設けられ、かつ紫外ＬＥＤ光源の紫外ＬＥＤチップに対して所定の間隙をおいて配置されているので、色のばらつき、樹脂および蛍光体の劣化、ならびに蛍光体の温度消光を抑制することができるという効果を奏する。また、白色変換シートは成形性に優れているので、発光装置の設計の自由度が増すという効果を奏する。   According to the present invention, since the white color conversion sheet is provided for a plurality of ultraviolet LED light sources and is arranged with a predetermined gap with respect to the ultraviolet LED chip of the ultraviolet LED light source, color variation, There is an effect that the deterioration of the resin and the phosphor and the temperature quenching of the phosphor can be suppressed. In addition, since the white conversion sheet is excellent in moldability, there is an effect that the degree of freedom in designing the light emitting device is increased.

以下、本発明の発光装置および白色変換シートについて詳細に説明する。   Hereinafter, the light emitting device and the white color conversion sheet of the present invention will be described in detail.

Ａ．発光装置
まず、本発明の発光装置について説明する。
本発明の発光装置は、紫外ＬＥＤチップを有する複数個の紫外ＬＥＤ光源と、上記紫外ＬＥＤチップに対して設けられ、かつ上記紫外ＬＥＤチップに対して、上記紫外ＬＥＤチップから放射される紫外光を可視光に変換し得る間隙をおいて配置され、上記紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有し、上記複数種の蛍光体からの発光の混色により実質的に白色光を得ることが可能な樹脂層を有する白色変換シートとを備えることを特徴とするものである。 A. First, the light emitting device of the present invention will be described.
The light emitting device of the present invention includes a plurality of ultraviolet LED light sources having an ultraviolet LED chip, and ultraviolet light emitted from the ultraviolet LED chip to the ultraviolet LED chip. It is arranged with a gap that can be converted into visible light, contains a plurality of types of phosphors that convert the ultraviolet light into visible light of different wavelengths, and is substantially due to a color mixture of light emitted from the plurality of types of phosphors. And a white conversion sheet having a resin layer capable of obtaining white light.

本発明の発光装置について、図面を参照しながら説明する。
図１は、本発明の発光装置の一例を示す概略平面図であり、図２は、図１のＡ−Ａ線断面図である。図１および図２に例示する発光装置１は、基板２と、この基板２上にアレイ状に配列された複数個の紫外ＬＥＤ光源３と、この複数個の紫外ＬＥＤ光源３の紫外ＬＥＤチップに対して、所定の間隙をおいて配置された白色変換シート５とを有するものである。白色変換シート５は、紫外ＬＥＤ光源３の紫外ＬＥＤチップから放射される紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有する樹脂層４から構成されている。なお、図１において、白色変換シートの一部は省略されている。 The light emitting device of the present invention will be described with reference to the drawings.
FIG. 1 is a schematic plan view showing an example of the light-emitting device of the present invention, and FIG. 2 is a cross-sectional view taken along line AA of FIG. The light emitting device 1 illustrated in FIGS. 1 and 2 includes a substrate 2, a plurality of ultraviolet LED light sources 3 arranged in an array on the substrate 2, and an ultraviolet LED chip of the plurality of ultraviolet LED light sources 3. On the other hand, it has the white conversion sheet 5 arrange | positioned at predetermined intervals. The white conversion sheet 5 is composed of a resin layer 4 containing a plurality of types of phosphors that convert ultraviolet light emitted from the ultraviolet LED chip of the ultraviolet LED light source 3 into visible light having different wavelengths. In FIG. 1, a part of the white conversion sheet is omitted.

上記の発光装置において、例えば、白色変換シートの樹脂層に含まれる複数種の蛍光体が、紫外光を青色光に変換する青色蛍光体と、紫外光を緑色光に変換する緑色蛍光体と、紫外光を赤色光に変換する赤色蛍光体とである場合、紫外ＬＥＤ光源の紫外ＬＥＤチップから紫外光が放射されると、この紫外光が樹脂層に含有される各色の蛍光体に吸収されて、青色光、緑色光および赤色光が発生する。これらの青色光と緑色光と赤色光との混色によって、白色光を得ることができる。   In the above light-emitting device, for example, a plurality of types of phosphors included in the resin layer of the white conversion sheet, a blue phosphor that converts ultraviolet light into blue light, a green phosphor that converts ultraviolet light into green light, In the case of a red phosphor that converts ultraviolet light into red light, when ultraviolet light is emitted from the ultraviolet LED chip of the ultraviolet LED light source, the ultraviolet light is absorbed by the phosphors of each color contained in the resin layer. Blue light, green light and red light are generated. White light can be obtained by mixing these blue light, green light, and red light.

本発明によれば、白色変換シートが、紫外ＬＥＤ光源毎ではなく、複数個の紫外ＬＥＤ光源に対して設けられており、白色変換シートと紫外ＬＥＤ光源とが別の部材となっている。そのため、白色変換シートを構成する樹脂層では、層中に蛍光体を均一に分散させることができる。これにより、蛍光体の含有量の差異による色のばらつきを抑制することが可能である。   According to the present invention, the white conversion sheet is provided not for each ultraviolet LED light source but for a plurality of ultraviolet LED light sources, and the white conversion sheet and the ultraviolet LED light source are separate members. Therefore, in the resin layer constituting the white conversion sheet, the phosphor can be uniformly dispersed in the layer. Thereby, it is possible to suppress color variation due to a difference in phosphor content.

さらに、本発明によれば、紫外ＬＥＤチップから放射された紫外光のうち、白色変換シートに対して垂直な方向への光だけでなく、斜め方向への光も、白色変換シートに入射する。同一の紫外ＬＥＤチップから、白色変換シートに対して垂直な方向に放射された紫外光と、白色変換シートに対して斜め方向に放射された紫外光とでは、白色変換シートに入射する部分が異なる。そのため、例えば個々の紫外ＬＥＤチップによって輝度が異なる場合であっても、紫外ＬＥＤチップ毎の輝度のばらつきを低減することができる。   Further, according to the present invention, not only light in a direction perpendicular to the white conversion sheet but also light in an oblique direction among the ultraviolet light emitted from the ultraviolet LED chip is incident on the white conversion sheet. The ultraviolet light emitted in the direction perpendicular to the white conversion sheet from the same ultraviolet LED chip and the ultraviolet light emitted in the oblique direction with respect to the white conversion sheet differ in the portion incident on the white conversion sheet. . Therefore, for example, even when the luminance differs depending on the individual ultraviolet LED chip, it is possible to reduce the variation in luminance for each ultraviolet LED chip.

このように本発明によれば、従来のような個々の紫外ＬＥＤ光源による違いを平均化することが可能であり、色むらのない均質な白色光を得ることができる。   As described above, according to the present invention, it is possible to average the differences due to the individual ultraviolet LED light sources as in the prior art, and obtain uniform white light without color unevenness.

また、本発明によれば、紫外ＬＥＤ光源の紫外ＬＥＤチップと白色変換シートとが所定の間隙をおいて配置されているので、紫外ＬＥＤチップの発熱による温度の影響や、紫外ＬＥＤチップからの紫外光の高いエネルギーの影響を受けて、白色変換シートの樹脂層に含まれる樹脂や蛍光体が劣化したり、蛍光体の温度消光が生じたりするのを抑制することが可能である。特に、従来のように紫外ＬＥＤ光源の一部に蛍光体を含有する色変換部を設ける場合と比較して、紫外ＬＥＤチップと白色変換シートとの距離を長くすることができるので、効果的に樹脂や蛍光体の劣化および蛍光体の温度消光を抑制することが可能である。   Further, according to the present invention, the ultraviolet LED chip of the ultraviolet LED light source and the white color conversion sheet are arranged with a predetermined gap, so that the influence of the temperature due to the heat generated by the ultraviolet LED chip and the ultraviolet light from the ultraviolet LED chip can be reduced. Under the influence of high energy of light, it is possible to suppress the deterioration of the resin and phosphor contained in the resin layer of the white conversion sheet and the occurrence of temperature quenching of the phosphor. In particular, since the distance between the ultraviolet LED chip and the white conversion sheet can be increased compared to the conventional case where a color conversion part containing a phosphor is provided in a part of the ultraviolet LED light source, it is effective. It is possible to suppress deterioration of the resin or phosphor and temperature quenching of the phosphor.

さらに、本発明における樹脂層は、樹脂中に蛍光体が分散されたものであるので、成形性に優れている。そのため、樹脂層を有する白色変換シートの形状を、筒状、球状、半筒状など、種々の形状にすることができる。すなわち、白色変換シートが成形性に優れているので、種々の形状を有する発光装置を得ることが可能である。例えば、図３に示すように、基板２上に配列された複数個の紫外ＬＥＤ光源３と、複数個の紫外ＬＥＤ光源３を覆うように配置された円筒状の白色変換シート５とを備える発光装置１とすることができる。なお、図３において、白色変換シートの一部は省略されている。
一方、従来のように紫外ＬＥＤ光源毎に蛍光体を含有する色変換部が設けられている場合には、色変換部が紫外ＬＥＤ光源の一部を構成しているため、本発明における白色変換シートのように、種々の形状とすることは困難である。また、従来の場合では、発光装置においては複数個の紫外ＬＥＤ光源がドット状に配置されるため、本発明のように種々の形状を有する発光装置とすることも困難である。 Furthermore, the resin layer in the present invention is excellent in moldability because the phosphor is dispersed in the resin. Therefore, the shape of the white conversion sheet having the resin layer can be various shapes such as a cylindrical shape, a spherical shape, and a semi-cylindrical shape. That is, since the white conversion sheet is excellent in moldability, it is possible to obtain light emitting devices having various shapes. For example, as shown in FIG. 3, light emission including a plurality of ultraviolet LED light sources 3 arranged on a substrate 2 and a cylindrical white conversion sheet 5 arranged so as to cover the plurality of ultraviolet LED light sources 3. The device 1 can be obtained. In FIG. 3, a part of the white conversion sheet is omitted.
On the other hand, when a color conversion unit containing a phosphor is provided for each ultraviolet LED light source as in the prior art, the color conversion unit constitutes a part of the ultraviolet LED light source. It is difficult to make various shapes like a sheet. In the conventional case, since a plurality of ultraviolet LED light sources are arranged in a dot shape in the light emitting device, it is difficult to obtain a light emitting device having various shapes as in the present invention.

また、本発明によれば、従来のように紫外ＬＥＤ光源毎に蛍光体を含有する色変換部を設ける場合と比較して、樹脂層の面積を格段に大きくすることができる。したがって、蛍光体の含有量を樹脂層全体で均一にすることが容易であり、さらに蛍光体の含有量の制御も容易である。また、このような比較的大面積の樹脂層は、例えば、樹脂に蛍光体を混練して成形することにより得ることができ、容易に形成可能である。
以下、本発明の発光装置の各構成について説明する。 Moreover, according to this invention, compared with the case where the color conversion part containing a fluorescent substance is provided for every ultraviolet LED light source like the past, the area of a resin layer can be enlarged greatly. Therefore, it is easy to make the phosphor content uniform throughout the resin layer, and the phosphor content can be easily controlled. Such a relatively large area resin layer can be obtained, for example, by kneading and molding a phosphor in a resin and can be easily formed.
Hereinafter, each structure of the light-emitting device of this invention is demonstrated.

１．白色変換シート
本発明に用いられる白色変換シートは、複数個の紫外ＬＥＤ光源に対して設けられ、かつ紫外ＬＥＤ光源の紫外ＬＥＤチップに対して、この紫外ＬＥＤチップから放射される紫外光を可視光に変換し得る間隙をおいて配置されるものである。また、白色変換シートは、紫外ＬＥＤチップから放射される紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有し、この複数種の蛍光体からの発光の混色により実質的に白色光を得ることが可能な樹脂層を有するものである。 1. White conversion sheet The white conversion sheet used in the present invention is provided for a plurality of ultraviolet LED light sources, and for the ultraviolet LED chips of the ultraviolet LED light sources, ultraviolet light emitted from the ultraviolet LED chips is visible light. It is arranged with a gap that can be converted into The white conversion sheet contains a plurality of types of phosphors that convert the ultraviolet light emitted from the ultraviolet LED chip into visible light having different wavelengths, and is substantially due to a color mixture of light emitted from the plurality of types of phosphors. It has a resin layer capable of obtaining white light.

紫外ＬＥＤ光源の紫外ＬＥＤチップおよび白色変換シートの配置としては、白色変換シートが、紫外ＬＥＤ光源の紫外ＬＥＤチップに対して、紫外ＬＥＤチップから放射される紫外光を可視光に変換し得る間隙をおいて配置されていれば特に限定されるものではない。
なお、紫外ＬＥＤチップとは、紫外光を放射する部材、いわゆる発光層のことをいう。本発明においては、紫外ＬＥＤチップと白色変換シートとが所定の間隙をおいて配置されているので、紫外ＬＥＤチップと白色変換シートとが直接接触することがなく、樹脂や蛍光体の劣化、および蛍光体の温度消光を抑制することができる。紫外ＬＥＤチップと白色変換シートとが所定の間隙をおいて配置されていれば、紫外ＬＥＤ光源と白色変換シートとが接触していてもかまわない。 As an arrangement of the ultraviolet LED chip and the white conversion sheet of the ultraviolet LED light source, the white conversion sheet has a gap that can convert the ultraviolet light emitted from the ultraviolet LED chip into visible light with respect to the ultraviolet LED chip of the ultraviolet LED light source. It is not particularly limited as long as it is arranged.
The ultraviolet LED chip refers to a member that emits ultraviolet light, a so-called light emitting layer. In the present invention, since the ultraviolet LED chip and the white conversion sheet are arranged with a predetermined gap, the ultraviolet LED chip and the white conversion sheet are not in direct contact with each other, deterioration of the resin or phosphor, and Temperature quenching of the phosphor can be suppressed. If the ultraviolet LED chip and the white conversion sheet are arranged with a predetermined gap, the ultraviolet LED light source and the white conversion sheet may be in contact with each other.

白色変換シートは、少なくとも樹脂層を有するものであればよいが、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射される紫外光を平行光にしたり拡散させたりする光導入層をさらに有していてもよい。また、樹脂層が自己支持性をもたない場合には、基材上に樹脂層が形成されていてもよい。
以下、白色変換シートの各構成について説明する。 The white conversion sheet may have at least a resin layer, but may further have a light introduction layer that makes the ultraviolet light emitted from the ultraviolet LED chip of the ultraviolet LED light source parallel light or diffuses it. . Moreover, when the resin layer does not have self-supporting property, the resin layer may be formed on the base material.
Hereinafter, each configuration of the white color conversion sheet will be described.

（１）樹脂層
本発明に用いられる樹脂層は、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射される紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有するものであり、この複数種の蛍光体からの発光の混色により実質的に白色光を得ることが可能なものである。 (1) Resin layer The resin layer used in the present invention contains plural kinds of phosphors that convert ultraviolet light emitted from an ultraviolet LED chip of an ultraviolet LED light source into visible light having different wavelengths. It is possible to obtain substantially white light by mixing colors of light emitted from a plurality of kinds of phosphors.

複数種の蛍光体は、紫外光を吸収して可視光を放射する。また、紫外光は高いエネルギーをもつため、樹脂層は紫外光をそのまま透過しない方が好ましい。したがって、樹脂層は、紫外光を吸収し、可視光を透過するものであることが好ましい。   Plural types of phosphors absorb ultraviolet light and emit visible light. Moreover, since ultraviolet light has high energy, it is preferable that the resin layer does not transmit ultraviolet light as it is. Therefore, the resin layer preferably absorbs ultraviolet light and transmits visible light.

樹脂層の膜厚としては、樹脂層中の蛍光体の含有量、樹脂層の紫外光線透過率および可視光線透過率、ならびに、目的とする発光スペクトル等に応じて適宜選択される。   The film thickness of the resin layer is appropriately selected according to the phosphor content in the resin layer, the ultraviolet light transmittance and visible light transmittance of the resin layer, the target emission spectrum, and the like.

また、樹脂層は、複数種の蛍光体を含有する単一層であってもよく、各色の蛍光体をそれぞれ含有する層が積層されたものであってもよい。   The resin layer may be a single layer containing a plurality of types of phosphors, or may be a layer in which layers containing phosphors of the respective colors are laminated.

樹脂層は、複数種の蛍光体が樹脂中に分散されたものである。以下、蛍光体および樹脂について説明する。   The resin layer is obtained by dispersing a plurality of types of phosphors in a resin. Hereinafter, the phosphor and the resin will be described.

（ｉ）蛍光体
本発明に用いられる蛍光体は、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射される紫外光を可視光に変換するものである。樹脂層は、紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有しており、この複数種の蛍光体からの発光の混色により実質的に白色光を得ることができる。 (I) Phosphor The phosphor used in the present invention converts ultraviolet light emitted from an ultraviolet LED chip of an ultraviolet LED light source into visible light. The resin layer contains a plurality of kinds of phosphors that convert ultraviolet light into visible light having different wavelengths, and substantially white light can be obtained by mixing colors of light emitted from the plurality of kinds of phosphors.

複数種の蛍光体が紫外ＬＥＤ光源の紫外ＬＥＤチップから放射される紫外光を吸収してそれぞれ放射する光が補色関係にある場合には、これらの複数種の蛍光体からの発光を混色させることにより、白色光を得ることができる。白色光を得るには、例えば、青色光、緑色光および赤色光を混色すればよい。すなわち、複数種の蛍光体としては、例えば、紫外光を青色光に変換する青色蛍光体と、紫外光を緑色光に変換する緑色蛍光体と、紫外光を赤色光に変換する赤色蛍光体とを用いることができる。中でも、複数種の蛍光体のひとつとして、赤色蛍光体を用いる場合には、演色性を高めることができる。   When multiple types of phosphors absorb ultraviolet light emitted from the ultraviolet LED chip of the ultraviolet LED light source and the emitted light has a complementary color relationship, the light emission from these multiple types of phosphors is mixed. Thus, white light can be obtained. In order to obtain white light, for example, blue light, green light, and red light may be mixed. That is, as the plurality of types of phosphors, for example, a blue phosphor that converts ultraviolet light into blue light, a green phosphor that converts ultraviolet light into green light, and a red phosphor that converts ultraviolet light into red light; Can be used. In particular, when a red phosphor is used as one of a plurality of types of phosphors, color rendering can be improved.

本発明に用いられる青色蛍光体としては、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射された紫外光で励起されて青色光を発光するものであれば特に限定されるものではない。具体的には、青色蛍光体は、波長２５０ｎｍ〜４２０ｎｍの光で励起されて、波長４２０ｎｍ〜５００ｎｍの光を発光するものであることが好ましい。このような青色蛍光体としては、例えば、ユーロピウムで付活されたバリウム・アルミニウム酸化物（ＢＡＭ：Ｅｕ２＋）、（Ｃａ，Ｓｒ，Ｂａ）５（ＰＯ４）３Ｃｌ：Ｅｕ２＋などを挙げることができる。 The blue phosphor used in the present invention is not particularly limited as long as it is excited by ultraviolet light emitted from an ultraviolet LED chip of an ultraviolet LED light source and emits blue light. Specifically, the blue phosphor is preferably one that is excited by light having a wavelength of 250 nm to 420 nm and emits light having a wavelength of 420 nm to 500 nm. Examples of such blue phosphors include barium aluminum oxide (BAM: Eu 2+ ) and (Ca, Sr, Ba) 5 (PO 4 ) 3 Cl: Eu 2+ activated by europium. Can do.

また、本発明に用いられる緑色蛍光体としては、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射された紫外光で励起されて緑色光を発光するものであれば特に限定されるものではない。具体的には、緑色蛍光体は、波長２５０ｎｍ〜４２０ｎｍの光で励起されて、波長５００ｎｍ〜６００ｎｍの光を発光するものであることが好ましい。このような緑色蛍光体としては、例えば、（Ｃａ，Ｓｒ，Ｂａ）２ＳｉＯ４：Ｅｕ２＋、ユーロピウムおよびマンガンで付活されたバリウム・アルミニウム酸化物（ＢＡＭ：Ｅｕ２＋，Ｍｎ２＋）、α−ＳｉＡｌＯＮ：Ｅｕ２＋などを挙げることができる。 The green phosphor used in the present invention is not particularly limited as long as it is excited by ultraviolet light emitted from the ultraviolet LED chip of the ultraviolet LED light source and emits green light. Specifically, the green phosphor is preferably one that is excited by light having a wavelength of 250 nm to 420 nm and emits light having a wavelength of 500 nm to 600 nm. Examples of such green phosphors include (Ca, Sr, Ba) 2 SiO 4 : Eu 2+ , barium aluminum oxide activated with europium and manganese (BAM: Eu 2+ , Mn 2+ ), α− SiAlON: Eu < 2+ > etc. can be mentioned.

さらに、本発明に用いられる赤色蛍光体としては、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射された紫外光で励起されて赤色光を発光するものであれば特に限定されるものではない。具体的には、赤色蛍光体は、波長２５０ｎｍ〜４２０ｎｍの光で励起されて、波長６００ｎｍ〜７００ｎｍの光を発光するものであることが好ましい。このような赤色蛍光体としては、例えば、Ｙ２Ｏ２Ｓ：Ｅｕ３＋、Ｌａ２Ｏ２Ｓ：Ｅｕ３＋、（Ｃａ，Ｓｒ，Ｂａ）２Ｓｉ５Ｎ８：Ｅｕ２＋、ＣａＡｌＳｉＮ３：Ｅｕ２＋、ＬｉＥｕＷ２Ｏ８Ｃａ（Ｅｕ，Ｌａ）４Ｓｉ３Ｏ１３、Ｅｕ２Ｗ２Ｏ９系、（Ｌａ，Ｅｕ）２Ｗ３Ｏ１２、（Ｃａ，Ｓｒ，Ｂａ）３ＭｇＳｉ２Ｏ８：Ｅｕ２＋，Ｍｎ２＋、ＣａＴｉＯ３：Ｐｒ３＋，Ｂｉ３＋などを挙げることができる。 Furthermore, the red phosphor used in the present invention is not particularly limited as long as it is excited by ultraviolet light emitted from the ultraviolet LED chip of the ultraviolet LED light source and emits red light. Specifically, the red phosphor is preferably one that is excited by light having a wavelength of 250 nm to 420 nm and emits light having a wavelength of 600 nm to 700 nm. As such a red phosphor, for example, Y 2 O 2 S: Eu 3+ , La 2 O 2 S: Eu 3+ , (Ca, Sr, Ba) 2 Si 5 N 8 : Eu 2+ , CaAlSiN 3 : Eu 2+ LiEuW 2 O 8 Ca (Eu, La) 4 Si 3 O 13 , Eu 2 W 2 O 9 series, (La, Eu) 2 W 3 O 12 , (Ca, Sr, Ba) 3 MgSi 2 O 8 : Eu 2+, Mn 2+, CaTiO 3: Pr 3+, and the like Bi 3+.

樹脂中の蛍光体の含有量としては、樹脂層の膜厚、樹脂層の紫外光線透過率および可視光線透過率、樹脂層の成形性、ならびに、目的とする発光スペクトル等に応じて適宜選択される。   The content of the phosphor in the resin is appropriately selected according to the film thickness of the resin layer, the ultraviolet light transmittance and the visible light transmittance of the resin layer, the moldability of the resin layer, the target emission spectrum, and the like. The

（ii）樹脂
本発明に用いられる樹脂としては、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射される紫外光を吸収し、蛍光体から放射される可視光を透過するものであれば特に限定されるものではないが、高エネルギーの紫外光に対して劣化しにくいものであることが好ましい。 (Ii) Resin The resin used in the present invention is particularly limited as long as it absorbs ultraviolet light emitted from the ultraviolet LED chip of the ultraviolet LED light source and transmits visible light emitted from the phosphor. However, it is preferable that the material is not easily deteriorated against high-energy ultraviolet light.

また、樹脂は、自己支持性を有していてもよく、有さなくてもよい。樹脂が自己支持性を有さない、すなわち樹脂層が自己支持性を有さない場合には、後述するように、基材上に樹脂層が形成されていることが好ましい。   Further, the resin may or may not have a self-supporting property. When the resin does not have self-supporting property, that is, when the resin layer does not have self-supporting property, it is preferable that the resin layer is formed on the substrate as described later.

このような樹脂としては、熱硬化性樹脂、熱可塑性樹脂、光硬化性樹脂などを用いることができ、例えば、シクロオレフィン系樹脂、ポリメチルメタクリレート等のアクリル樹脂、ポリビニルアルコール、ポリイミド、ポリアリレート、ポリエチレンテレフタレート、ポリスルホン、ポリエーテルスルホン、アモルファスポリオレフィン、変性アクリル系ポリマー、ポリスチレン、セルロース誘導体、エポキシ樹脂、ユリア樹脂、シリコーン樹脂、ポリカーボネート、ポリエステル類などを挙げることができる。   As such a resin, a thermosetting resin, a thermoplastic resin, a photocurable resin, or the like can be used. For example, an acrylic resin such as a cycloolefin resin or polymethyl methacrylate, polyvinyl alcohol, polyimide, polyarylate, Examples thereof include polyethylene terephthalate, polysulfone, polyethersulfone, amorphous polyolefin, modified acrylic polymer, polystyrene, cellulose derivatives, epoxy resins, urea resins, silicone resins, polycarbonates, and polyesters.

（iii）その他
本発明における樹脂層は、蛍光体を樹脂に分散させた樹脂組成物を固化させることにより得ることができる。
樹脂層の成膜方法としては、例えば、上記樹脂組成物を用いてシート状に成形する方法や、上記樹脂組成物を基材上に塗布する方法を用いることができる。また、樹脂組成物の固化方法としては、用いる樹脂の種類に応じて適宜選択され、例えば、加熱、乾燥、光照射等の方法が用いられる。 (Iii) Others The resin layer in the present invention can be obtained by solidifying a resin composition in which a phosphor is dispersed in a resin.
As a method for forming the resin layer, for example, a method of forming the resin composition into a sheet shape or a method of applying the resin composition on a substrate can be used. Moreover, as a solidification method of a resin composition, it selects suitably according to the kind of resin to be used, for example, methods, such as a heating, drying, and light irradiation, are used.

本発明においては、蛍光体の種類、樹脂層中の蛍光体の含有量、樹脂層の膜厚等を調整することにより、得られる発光スペクトルを調整することができる。すなわち、白色光はもちろん、可視光領域の発光色うち、任意の発光色を得ることが可能な発光装置とすることができる。   In the present invention, the emission spectrum to be obtained can be adjusted by adjusting the type of phosphor, the content of the phosphor in the resin layer, the film thickness of the resin layer, and the like. That is, it is possible to obtain a light emitting device capable of obtaining an arbitrary emission color among emission colors in the visible light region as well as white light.

（２）光導入層
本発明においては、樹脂層上に光導入層が形成されていてもよい。この光導入層としては、例えば、点光源（紫外ＬＥＤ光源）からの光（紫外光）を平行光にするものであってもよく、紫外ＬＥＤ光源からの紫外光を拡散させるものであってもよい。光導入層が紫外ＬＥＤ光源からの紫外光を平行光にするものである場合には、紫外ＬＥＤ光源から全方位に放射される紫外光を光導入層によって平行光にし、紫外光を樹脂層に効率良く入射させることができる。また、光導入層が紫外ＬＥＤ光源からの紫外光を拡散させるものである場合には、樹脂層表面での光の反射を抑制し、紫外光を樹脂層に効率良く入射させたり、樹脂層から白色光を効率良く取り出したりすることができる。 (2) Light Introducing Layer In the present invention, a light introducing layer may be formed on the resin layer. As this light introduction layer, for example, light (ultraviolet light) from a point light source (ultraviolet LED light source) may be made parallel light, or ultraviolet light from an ultraviolet LED light source may be diffused. Good. When the light introduction layer is to convert the ultraviolet light from the ultraviolet LED light source into parallel light, the ultraviolet light emitted from the ultraviolet LED light source in all directions is converted into parallel light by the light introduction layer, and the ultraviolet light is converted into the resin layer. It can be incident efficiently. Further, when the light introduction layer diffuses ultraviolet light from the ultraviolet LED light source, reflection of light on the surface of the resin layer is suppressed, and ultraviolet light is efficiently incident on the resin layer, or from the resin layer. White light can be taken out efficiently.

紫外ＬＥＤ光源からの紫外光を平行光にする光導入層としては、例えば、凸レンズ、レンチキュラーレンズ、プリズム等の形状を有するものを用いることができる。光導入層が凸レンズやプリズムの形状を有する場合には、凸レンズやプリズムがアレイ状に形成されたものであることが好ましい。   As the light introducing layer for converting the ultraviolet light from the ultraviolet LED light source into parallel light, for example, a layer having a shape such as a convex lens, a lenticular lens, or a prism can be used. When the light introduction layer has a convex lens or prism shape, the convex lens or prism is preferably formed in an array.

光導入層が紫外ＬＥＤ光源からの紫外光を平行光にするものである場合は、通常、図４に例示するように、光導入層６ａが樹脂層４の紫外ＬＥＤ光源３側の面に形成される。   In the case where the light introduction layer converts the ultraviolet light from the ultraviolet LED light source into parallel light, the light introduction layer 6a is usually formed on the surface of the resin layer 4 on the ultraviolet LED light source 3 side as illustrated in FIG. Is done.

また、紫外ＬＥＤ光源からの紫外光を拡散させる光導入層としては、例えば、樹脂層と、白色変換シートおよび紫外ＬＥＤ光源の間に介在する媒体とに対して屈折率が調整された層や、光を拡散する微粒子を含有する層などを用いることができる。   In addition, as a light introduction layer for diffusing ultraviolet light from an ultraviolet LED light source, for example, a layer whose refractive index is adjusted with respect to a resin layer and a medium interposed between the white conversion sheet and the ultraviolet LED light source, A layer containing fine particles that diffuse light can be used.

光導入層が紫外ＬＥＤ光源からの紫外光を拡散させるものである場合、光導入層の形成位置としては、樹脂層上であれば特に限定されるものではない。例えば、図５に示すように光導入層６ｂが樹脂層４の紫外ＬＥＤ光源３側の面に形成されていてもよく、図示しないが光導入層が樹脂層の紫外ＬＥＤ光源に対向している面とは反対側の面に形成されていてもよい。   In the case where the light introduction layer diffuses ultraviolet light from the ultraviolet LED light source, the formation position of the light introduction layer is not particularly limited as long as it is on the resin layer. For example, as shown in FIG. 5, the light introduction layer 6b may be formed on the surface of the resin layer 4 on the side of the ultraviolet LED light source 3, and although not shown, the light introduction layer faces the ultraviolet LED light source of the resin layer. You may form in the surface on the opposite side to a surface.

また、紫外ＬＥＤ光源からの紫外光を平行光にする光導入層、および、紫外ＬＥＤ光源からの紫外光を拡散させる光導入層の両方が形成されていてもよい。   Moreover, both the light introduction layer which makes the ultraviolet light from an ultraviolet LED light source parallel light, and the light introduction layer which diffuses the ultraviolet light from an ultraviolet LED light source may be formed.

このような光導入層は、樹脂層の紫外ＬＥＤ光源側の面に形成されている場合は、紫外光ＬＥＤ光源からの紫外光を透過するものであることが好ましく、樹脂層の紫外ＬＥＤ光源側の面とは反対側の面に形成されている場合は、蛍光体から放射される可視光を透過するものであることが好ましい。   When such a light introducing layer is formed on the surface of the resin layer on the side of the ultraviolet LED light source, it is preferable to transmit ultraviolet light from the ultraviolet LED light source, and the resin layer on the side of the ultraviolet LED light source In the case of being formed on the surface opposite to the surface, it is preferable to transmit visible light emitted from the phosphor.

（３）基材
本発明においては、樹脂層が基材上に形成されていてもよい。特に、樹脂層が自己支持性をもたない場合には、基材上に樹脂層が形成されていることが好ましい。 (3) Base material In this invention, the resin layer may be formed on the base material. In particular, when the resin layer does not have self-supporting properties, it is preferable that the resin layer is formed on the base material.

基材は、蛍光体から放射される可視光を透過するものであれば特に限定されるものではない。このような基材としては、例えば、石英ガラス、パイレックス（登録商標）、合成石英板等の可撓性を有さないリジットな基材、または、樹脂フィルム、光学用樹脂板等の可撓性を有するフレキシブルな基材を挙げることができる。
中でも、基材は、樹脂フィルム等のフレキシブルな基材であることが好ましい。樹脂フィルムは、成形性に優れており、曲面への適用等の種々のアプリケーションへの適用可能性が広がるからである。 A base material will not be specifically limited if the visible light radiated | emitted from fluorescent substance is permeate | transmitted. Examples of such a base material include rigid base materials such as quartz glass, Pyrex (registered trademark), and synthetic quartz plates, or flexible materials such as resin films and optical resin plates. A flexible base material having
Especially, it is preferable that a base material is flexible base materials, such as a resin film. This is because the resin film is excellent in moldability and can be applied to various applications such as application to curved surfaces.

基材の形成位置としては、通常、樹脂層の紫外ＬＥＤ光源に対向している面とは反対側の面とされる。   As a formation position of a base material, it is a surface on the opposite side to the surface facing the ultraviolet LED light source of a resin layer normally.

２．紫外ＬＥＤ光源
本発明に用いられる紫外ＬＥＤ光源は、紫外ＬＥＤチップを有するものである。この紫外ＬＥＤ光源としては、特に限定されるものではなく、一般的に使用される紫外ＬＥＤ光源を用いることができる。例えば、ＬＥＤの種類としては、砲弾型、表面実装（ＳＭＤ）型、Chip On Board（ＣＯＢ）型、パワーＬＥＤ Face Up（ＦＵ）型、パワーＬＥＤ Face Down（ＦＤ）型などのいずれであってもよい。 2. Ultraviolet LED light source The ultraviolet LED light source used in the present invention has an ultraviolet LED chip. The ultraviolet LED light source is not particularly limited, and a commonly used ultraviolet LED light source can be used. For example, the LED type may be any of a bullet type, a surface mount (SMD) type, a chip on board (COB) type, a power LED Face Up (FU) type, a power LED Face Down (FD) type, and the like. Good.

図６は、本発明に用いられる紫外ＬＥＤ光源の一例を示す概略断面図である。図６に例示する紫外ＬＥＤ光源３においては、基体１２上にパターン状に配線１３および１４が形成され、配線の一部（配線１４）の上に紫外ＬＥＤチップ１５が形成されており、封止枠１７および樹脂からなる凸レンズ状の封止材１８により封止されている。また、紫外ＬＥＤチップ１５は、導電性ワイヤー１６を介して配線１３に接続されている。   FIG. 6 is a schematic cross-sectional view showing an example of an ultraviolet LED light source used in the present invention. In the ultraviolet LED light source 3 illustrated in FIG. 6, wirings 13 and 14 are formed in a pattern on the substrate 12, and an ultraviolet LED chip 15 is formed on a part of the wiring (wiring 14). It is sealed with a frame 17 and a convex lens-shaped sealing material 18 made of resin. The ultraviolet LED chip 15 is connected to the wiring 13 through the conductive wire 16.

紫外ＬＥＤチップとしては、紫外光領域の光を放射するものであれば特に限定されるものではなく、一般的に紫外ＬＥＤに使用されるものを用いることができる。紫外ＬＥＤチップの構成材料としては、例えば、ＡｌＧａＮ等の窒化ガリウム系化合物半導体などが挙げられる。半導体の構造としては、例えば、ＭＩＳ接合、ＰＩＮ接合、ＰＮ接合等を有するホモ構造、ヘテロ構造、ダブルへテロ構造、単一量子井戸構造、多重量子井戸構造を挙げることができる。   The ultraviolet LED chip is not particularly limited as long as it emits light in the ultraviolet region, and those generally used for ultraviolet LEDs can be used. Examples of the constituent material of the ultraviolet LED chip include a gallium nitride compound semiconductor such as AlGaN. Examples of the semiconductor structure include a homo structure having a MIS junction, a PIN junction, and a PN junction, a hetero structure, a double hetero structure, a single quantum well structure, and a multiple quantum well structure.

紫外ＬＥＤチップの発光波長としては、紫外光領域であれば特に限定されるものではなく、励起発光効率等を考慮して適宜選択される。この紫外ＬＥＤチップの発光波長は、構成材料や混晶度等を適宜選択することにより、調整することができる。   The emission wavelength of the ultraviolet LED chip is not particularly limited as long as it is in the ultraviolet light region, and is appropriately selected in consideration of the excitation light emission efficiency and the like. The emission wavelength of the ultraviolet LED chip can be adjusted by appropriately selecting a constituent material, a mixed crystal degree, and the like.

また、基体としては、一般的にＬＥＤに用いられるものであれば特に限定されるものではなく、例えば、金属板および絶縁層が積層されたものや、セラミックス、ガラス、サファイア、エポキシ樹脂等の樹脂などからなる基体を用いることができる。
上記金属板の構成材料としては、熱伝導性のよい金属が用いられ、例えば、アルミニウム、銅などが挙げられる。 The substrate is not particularly limited as long as it is generally used for LEDs. For example, a substrate in which a metal plate and an insulating layer are laminated, a resin such as ceramics, glass, sapphire, and epoxy resin. A substrate made of such as can be used.
As a constituent material of the metal plate, a metal having good thermal conductivity is used, and examples thereof include aluminum and copper.

導電性ワイヤーとしては、配線とのオーミック性、機械的接続性、電気伝導性および熱伝導性がよいものであれば特に限定されるものではない。このような導電性ワイヤーの構成材料としては、例えば、金、銅、白金、アルミニウム等の金属、およびそれらの合金などが挙げられる。   The conductive wire is not particularly limited as long as it has good ohmic properties with wiring, mechanical connectivity, electrical conductivity, and thermal conductivity. Examples of the constituent material of the conductive wire include metals such as gold, copper, platinum, and aluminum, and alloys thereof.

また、配線としては、一般的にＬＥＤに用いられるものであれば特に限定されるものではない。   Moreover, as wiring, it will not specifically limit if it is generally used for LED.

封止材は、紫外ＬＥＤチップ、導電性ワイヤーなどを外部から保護するために設けられるものである。
封止材の構成材料としては、通常、樹脂が用いられる。樹脂としては、例えば、エポキシ樹脂、ユリア樹脂、シリコーン樹脂等が挙げられる。これらは、耐候性に優れているため、好適に用いられる。 The sealing material is provided to protect the ultraviolet LED chip, the conductive wire, and the like from the outside.
As the constituent material of the sealing material, a resin is usually used. Examples of the resin include an epoxy resin, a urea resin, and a silicone resin. Since these are excellent in weather resistance, they are preferably used.

紫外ＬＥＤ光源が設けられる基板としては、一般的にＬＥＤに用いられるものであれば特に限定されるものではなく、上記基体が基板を兼ねていてもよい。   The substrate on which the ultraviolet LED light source is provided is not particularly limited as long as it is generally used for LEDs, and the substrate may also serve as the substrate.

本発明においては、複数個の紫外ＬＥＤ光源が配列される。この複数個の紫外ＬＥＤ光源は、規則的に所定の間隔で配列されていることが好ましい。また、紫外ＬＥＤ光源の数としては、２個以上であれば特に限定されるものではない。   In the present invention, a plurality of ultraviolet LED light sources are arranged. The plurality of ultraviolet LED light sources are preferably regularly arranged at a predetermined interval. The number of ultraviolet LED light sources is not particularly limited as long as it is two or more.

３．用途
本発明の発光装置は、例えば、信号機、広告等の表示用光源、照明装置等の照明用光源、液晶表示装置のバックライト等の表示装置用光源などに適用することができる。
特に、本発明における白色変換シートは成形性に優れているので、種々の形状を有する発光装置を得ることができる。 3. Applications The light-emitting device of the present invention can be applied to, for example, traffic lights, display light sources for advertisements, illumination light sources such as illumination devices, and light sources for display devices such as backlights of liquid crystal display devices.
In particular, since the white conversion sheet in the present invention is excellent in moldability, light emitting devices having various shapes can be obtained.

４．その他
紫外ＬＥＤ光源と白色変換シートとの間に充填される媒体としては、特に限定されるものではない。 4). Others The medium filled between the ultraviolet LED light source and the white conversion sheet is not particularly limited.

Ｂ．白色変換シート
本発明の白色変換シートは、上述の発光装置に用いられ、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射される紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有し、上記複数種の蛍光体からの発光の混色により実質的に白色光を得ることが可能な樹脂層を有することを特徴とするものである。
なお、白色変換シートについては、上記「Ａ．発光装置」の項に詳しく記載したので、ここでの説明は省略する。 B. White conversion sheet The white conversion sheet of the present invention is used in the above-described light-emitting device, and contains a plurality of kinds of phosphors that convert ultraviolet light emitted from an ultraviolet LED chip of an ultraviolet LED light source into visible light having different wavelengths. And a resin layer capable of obtaining substantially white light by mixing colors of light emitted from the plurality of types of phosphors.
The white conversion sheet has been described in detail in the above section “A. Light-emitting device”, and thus description thereof is omitted here.

なお、本発明は、上記実施形態に限定されるものではない。上記実施形態は、例示であり、本発明の特許請求の範囲に記載された技術的思想と実質的に同一な構成を有し、同様な作用効果を奏するものは、いかなるものであっても本発明の技術的範囲に包含される。   The present invention is not limited to the above embodiment. The above-described embodiment is an exemplification, and the present invention has substantially the same configuration as the technical idea described in the claims of the present invention, and any device that exhibits the same function and effect is the present invention. It is included in the technical scope of the invention.

以下、実施例を用いて本発明を具体的に説明する。
［実施例］
１．白色変換シートの作製
青色蛍光体（ＢａＭｇＡｌ１０Ｏ１７：Ｅｕ２＋）と、緑色蛍光体（（Ｃａ，Ｓｒ，Ｂａ）２ＳｉＯ４：Ｅｕ２＋）と、赤色蛍光体（ＣａＡｌＳｉＮ３：Ｅｕ２＋）とを、ＰＭＭＡ樹脂ペレットに混練させ、蛍光体および樹脂が混合したペレットを作製した。この蛍光体・樹脂混合ペレットを３００μｍの厚さのシート状に加工し、１０ｃｍ×１０ｃｍの白色変換シートを作製した。 Hereinafter, the present invention will be specifically described with reference to examples.
[Example]
1. Production of white conversion sheet Blue phosphor (BaMgAl 10 O 17 : Eu 2+ ), green phosphor ((Ca, Sr, Ba) 2 SiO 4 : Eu 2+ ), and red phosphor (CaAlSiN 3 : Eu 2+ ) Were kneaded into PMMA resin pellets to produce pellets in which phosphor and resin were mixed. This phosphor / resin mixed pellet was processed into a sheet having a thickness of 300 μm to prepare a 10 cm × 10 cm white conversion sheet.

２．発光装置の作製
紫外ＬＥＤ光源が９個配列されたものを準備した。これらの紫外ＬＥＤ光源の紫外ＬＥＤチップに対して、上記の白色変換シートを３ｍｍ程度の間隙をおいて配置した。 2. Production of Light Emitting Device A device in which nine ultraviolet LED light sources were arranged was prepared. With respect to the ultraviolet LED chip of these ultraviolet LED light sources, the above white conversion sheet was disposed with a gap of about 3 mm.

３．評価
得られた白色変換シートについて、紫外ＬＥＤ（４０５ｎｍ）の光励起による発光色を観察した。紫外ＬＥＤチップからの紫外光により励起されて発生した、ＢａＭｇＡｌ１０Ｏ１７：Ｅｕ２＋の青色蛍光と、（Ｃａ，Ｓｒ，Ｂａ）２ＳｉＯ４：Ｅｕ２＋の緑色蛍光と、ＣａＡｌＳｉＮ３：Ｅｕ２＋の赤色蛍光とが混色されて、白色光が観測された。 3. Evaluation About the obtained white conversion sheet, the luminescent color by the photoexcitation of ultraviolet LED (405 nm) was observed. BaMgAl 10 O 17 : Eu 2+ blue fluorescence, (Ca, Sr, Ba) 2 SiO 4 : Eu 2+ green fluorescence and CaAlSiN 3 : Eu 2+ generated by being excited by ultraviolet light from an ultraviolet LED chip. Red light was mixed and white light was observed.

本発明の発光装置の一例を示す概略平面図である。It is a schematic plan view which shows an example of the light-emitting device of this invention. 図１のＡ−Ａ線断面図である。It is the sectional view on the AA line of FIG. 本発明の発光装置の他の例を示す概略斜視図である。It is a schematic perspective view which shows the other example of the light-emitting device of this invention. 本発明の発光装置の他の例を示す概略断面図である。It is a schematic sectional drawing which shows the other example of the light-emitting device of this invention. 本発明の発光装置の他の例を示す概略断面図である。It is a schematic sectional drawing which shows the other example of the light-emitting device of this invention. 本発明に用いられる紫外ＬＥＤ光源の一例を示す概略断面図である。It is a schematic sectional drawing which shows an example of the ultraviolet LED light source used for this invention.

符号の説明Explanation of symbols

１ …発光装置
２ … 基板
３ … 紫外ＬＥＤ光源
４ … 樹脂層
５ … 白色変換シート
６ａ、６ｂ … 光導入層 DESCRIPTION OF SYMBOLS 1 ... Light-emitting device 2 ... Board | substrate 3 ... Ultraviolet LED light source 4 ... Resin layer 5 ... White conversion sheet 6a, 6b ... Light introduction layer

Claims (5)

紫外ＬＥＤチップを有する複数個の紫外ＬＥＤ光源と、
前記複数個の紫外ＬＥＤ光源に対して設けられ、かつ前記紫外ＬＥＤチップに対して、前記紫外ＬＥＤチップから放射される紫外光を可視光に変換し得る間隙をおいて配置され、前記紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有し、前記複数種の蛍光体からの発光の混色により実質的に白色光を得ることが可能な樹脂層および前記樹脂層の前記紫外ＬＥＤ光源側に形成され、前記紫外ＬＥＤ光源からの前記紫外光を平行光にする光導入層を有する白色変換シートと、
を備えることを特徴とする光発光装置。 A plurality of ultraviolet LED light sources having ultraviolet LED chips;
It is provided for the plurality of ultraviolet LED light sources, and is disposed with a gap capable of converting ultraviolet light emitted from the ultraviolet LED chip into visible light with respect to the ultraviolet LED chip. A resin layer containing a plurality of types of phosphors that convert visible light having different wavelengths from each other, and capable of obtaining substantially white light by mixing colors of light emitted from the plurality of types of phosphors, and the ultraviolet of the resin layer A white color conversion sheet formed on the LED light source side, and having a light introduction layer for making the ultraviolet light from the ultraviolet LED light source parallel light ;
A light-emitting device comprising: 前記複数種の蛍光体が、前記紫外光を青色光に変換する青色蛍光体、前記紫外光を緑色光に変換する緑色蛍光体、および、前記紫外光を赤色光に変換する赤色蛍光体であることを特徴とする請求項１に記載の発光装置。 The plurality of types of phosphors are a blue phosphor that converts the ultraviolet light into blue light, a green phosphor that converts the ultraviolet light into green light, and a red phosphor that converts the ultraviolet light into red light. The light-emitting device according to claim 1. 前記樹脂層が、前記複数種の蛍光体をそれぞれ含有する層が積層されたものであることを特徴とする請求項１または請求項２に記載の発光装置。 The light emitting device according to claim 1 , wherein the resin layer is formed by laminating layers each containing the plurality of types of phosphors . 前記樹脂層中の前記蛍光体が均一に分散していることを特徴とする請求項１から請求項３までのいずれかの請求項に記載の発光装置。  The light emitting device according to any one of claims 1 to 3, wherein the phosphors in the resin layer are uniformly dispersed. 請求項１から請求項４までのいずれかに記載の発光装置に用いられ、紫外ＬＥＤ光源の紫外ＬＥＤチップから放射される紫外光を互いに異なる波長の可視光に変換する複数種の蛍光体を含有し、前記複数種の蛍光体からの発光の混色により実質的に白色光を得ることが可能な樹脂層と、前記樹脂層の前記紫外ＬＥＤ光源側に形成され、前記紫外ＬＥＤ光源からの前記紫外光を平行光にする光導入層と、を有することを特徴とする白色変換シート。 A plurality of kinds of phosphors that are used in the light-emitting device according to any one of claims 1 to 4 and that convert ultraviolet light emitted from an ultraviolet LED chip of an ultraviolet LED light source into visible light having different wavelengths. And a resin layer capable of obtaining substantially white light by mixing light emitted from the plurality of kinds of phosphors, and the ultraviolet LED light source side of the resin layer. A white conversion sheet comprising: a light introduction layer that converts light into parallel light .
JP2006230310A 2006-08-28 2006-08-28 Light emitting device and white conversion sheet Active JP4876790B2 (en)