JP4296244B2 - S−eb−sブロックコポリマー/可塑剤水性分散液及び物品の成形におけるその使用 - Google Patents
S−eb−sブロックコポリマー/可塑剤水性分散液及び物品の成形におけるその使用 Download PDFInfo
- Publication number
- JP4296244B2 JP4296244B2 JP50986798A JP50986798A JP4296244B2 JP 4296244 B2 JP4296244 B2 JP 4296244B2 JP 50986798 A JP50986798 A JP 50986798A JP 50986798 A JP50986798 A JP 50986798A JP 4296244 B2 JP4296244 B2 JP 4296244B2
- Authority
- JP
- Japan
- Prior art keywords
- dispersion
- styrene
- block copolymer
- aqueous dispersion
- butylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明は、S−EB−Sブロックコポリマーの水性分散液及びそのような水性分散液の物品成形、好ましくは浸漬成形における使用に関する。
薄壁の延伸性物品、例えば手袋、コンドームや他の製品は、これまで天然ゴムから製造されてきた。通常の製法では、そのような物品は、安定剤及び加硫成分を加えた天然ゴムラテックス、すなわちゴムと水との天然のエマルジョンから製造される。場合により予め凝固溶液により被覆された適当な形状の型を、ラテックス混合物に一回または数回浸漬し、所望厚さの層を形成する。水は蒸発させ、固体ゴムフィルムを残す。適当な機械的及び物理的特性を与えるために、フィルムは加硫しなければならない。
天然ゴムは、このような用途では多くの利点を有している。すなわち、天然ゴムは、強く、かつ高弾性であり、使用者にとって良好な「触質性」又は感触を有している。天然ゴムは、いくつかの欠点、例えば「ピンホール」ができやすく、分断クラックを生じるオゾンによる急激な攻撃、及びクラックを生じ製品の物理的一体性を損なう貯蔵中の酸化的攻撃を受けやすいという欠点を有している。天然ゴムは、ゴム中の残留界面活性剤、加硫剤、安定剤、酸化防止剤、及び/または蛋白質の故に、低アレルギー誘発性ではない。特に刺激または感作に感受性の強い人、または長期間ゴム製品を使用する人は、アレルギー反応を起こすかもしれない。
浸漬成形により薄い物品を製造するのに用いるため、種々の合成弾性ポリマー製品が開発されている。合成ゴム組成物は、ピンホールを非常にできにくくするように真の溶液を形成するために溶媒に溶解され得る。入手できる多くの合成ゴム組成物は、許容できない触質性を含め多くの他の欠点を有している。そのような組成物のそれぞれは、いくつかの要求は満足するが、ほとんどの組成物は、強さ、触質性、環境攻撃に対する耐性、及び多くの製品(例えば、試験及び手術用手袋、コンドーム、並びに人体に接触する他の医療用製品)に要求される低アレルギー誘発性を所望通りに組み合わせて有していない。
合成弾性ポリマー製品の分野での重要な進歩は、米国特許第5112900号及び同第5407715号に記載されている。これらの特許は、特定のスチレン−エチレン/ブチレン−スチレン(S−EB−S)ブロックコポリマー溶液と、物品の浸漬成形におけるその使用を開示している。得られる物品は、手袋、コンドーム、及び他の製品に使用するための優れた弾性特性を有している。これらのコポリマーは、ピンホールの発生率が低く、酸化またはオゾン化のような環境攻撃に対する耐性が高く、低アレルギー誘発性である。
しかしながら、そのような組成物から製造される物品の生産性及び方法の経済性を更に改良する必要性が常に存在している。本発明は、この必要性を満足するものであり、関連した利点をもたらす。
発明の概要
本発明は、S−EB−S水性分散液、及び薄い弾性物品の製造におけるこの水性分散液の利用を提供する。物品は、S−EB−S溶液から製造される対応する物品の、優れた弾性特性、低ピンホール発生、酸化またはオゾン化のような環境攻撃に対する良好な耐性及び低アレルギー誘発性を含む所望の特性を有している。本発明は、物品の利用性を高めるための粉体または非粉体技術の使用のような関連する技術に匹敵する。加えて、分散体系浸漬成形製造方法は、従来のS−EB−S溶液からの浸漬成形に比べて、改良された方法経済性となるように高い速度で機能する。より厚い層または物品を、各浸漬段階で作ることができる。この製造方法は、浸漬成形工程で有害な溶媒を用いないので、より安全でもある。
本発明によれば、水性分散液は、水及び界面活性剤の混合物を含む分散媒体、並びに分散媒体中に分散された複数の粒子を含んでいる。各粒子は、S−EB−S(スチレン−エチレン/ブチレン−スチレン)ブロックコポリマー、および鉱油のような可塑剤(以下、「油」とも称する)を含んでいる。最も好ましくは、粒子は、約2μmを越えない平均寸法を有する。S−EB−Sブロックコポリマーは、実質的に同じ分子量の分子、又は2またはそれ以上の分子量の混合物であってもよいが、好ましくは、末端ブロックそれぞれは約15000ダルトン以上の平均末端ブロック分子量を有している。
水性分散液は、薄壁物品を製造する浸漬成形において用いることができる。本発明のこの形態によれば、弾性物品の製造方法は、記述した種類の水性分散液を供給し、水性分散液に型を浸し、水性分散液から型を引き上げ、型の上に分散液の膜を残し、型上の分散液から水を蒸発させ、残留したポリマーを溶融し、型の上に凝集延伸性フィルムを残す工程を含んでなる。浸漬成形方法において使用される水性分散液は、非水性溶媒を実質的に含まないが、存在するごく少量の溶媒は、浸漬成形方法にとって不利ではなく、ある場合には凝集性フィルムの形成に有益なことがある。
水性分散液は、他の加工技術と合わせて使用することができる。例えば、水性分散液は、天然ラテックスゴムコンパウンドに採用される凝固剤浸漬法に使用することができる。水性分散液は、例えば噴霧コーティング、又はスラッシ成形方法においても使用することができる。
得られる物品は、米国特許第5112900号及び同第5407715号に記載されているようなS−EB−Sブロックコポリマーに関連する望ましい特徴を有する。更に、物品は、先行特許に記載されている溶液を用いた技術により可能なよりも非常に早く製造することができる。製造操作において、通常分散液は、分散液の調製時に発生する潜在的毒性溶媒蒸気を処理する装置を備えた場所で作られる。浸漬成形操作は、他の場所で行ってよい。浸漬成形操作では潜在的毒性溶媒は放出されないので、浸漬成形及び乾燥ラインで作業者に危害を与える危険はほとんどない。
本発明の他の特徴及び利点は、以下において添付図面を参照して行う好ましい態様のより詳細な説明から明らかになるであろう。以下の説明は、例として本発明の原理を説明するものである。本発明の範囲は、これら好ましい態様に限定されるものではない。
【図面の簡単な説明】
図1は、本発明を実施するための好ましい方法のブロックフロー図である。
図2Aは、(水/界面活性剤)中(S−EB−S/油)水性分散液の模式的ミクロ構造図である。
図2Bは、(S−EB−S/油)中(水/界面活性剤)水性分散液の模式的ミクロ構造図である。
図3は、手袋用型の斜視図である。
図4は、コンドーム用型の斜視図である。
発明の詳細な説明
図1は、本発明に従って水性分散液を製造し、次いでその水性分散液を浸漬成形により物品を製造するために使用する好ましい方法を示すブロックフロー図である。
スチレン−エチレン/ブチレン−スチレン(S−EB−S)ブロックコポリマーは、20で示されているように、供給される。S−EB−Sブロックコポリマーは、エチレン−ブチレンコポリマー中央ブロックとポリスチレン末端ブロックとから形成される。各ポリスチレン末端ブロックは、少なくとも約15000ダルトン、より好ましくは約18000〜約20000ダルトンの重量平均分子量を有する。浸漬成形液中には比較的大量の油が含まれているので、S−EB−Sブロックコポリマーが、このような末端ブロック分子量により達成される高い末端ブロックポリスチレン含有量を有することは有利である。
末端ブロックそれぞれの重量平均分子量が約15000未満であると、浸漬成形により物品を形成することはできるが、その強度は低下し、ある用途には許容できないほど低くなる。そのような物品は、低い機械的特性を有する。約15000未満の末端ブロック分子量を有するS−EB−Sブロックコポリマー用いて浸漬成形された物品は、恐らく高温での低い機械強度故に、乾燥および溶融中にひび割れる傾向がある。一方、ポリスチレン末端ブロックの重量平均分子量が約15000を越え、好ましくは18000〜20000の範囲にあると、フィルムは優れた強度特性を有し、乾燥及び溶融中にひび割れない。この場合、少なくとも約150000ダルトンを越える重量平均分子量を有するS−EB−Sブロックコポリマー成分を1つ有するのが望ましい。ポリスチレン末端ブロックの重量平均分子量が約24000ダルトンを越える場合、分散液は浸漬成形において良好なフィルム形成性を有するが、物理的性質は、18000〜20000の範囲の重量平均分子量の場合ほど良好ではない。
ポリスチレン末端ブロックは、典型的には、全分子の約25〜35重量%を占める。コポリマーの全分子量は、典型的に、約50000〜約300000ダルトンである。
S−EB−Sブロックコポリマーは、場合により、ポリスチレン末端ブロックに付加された末端ブロック適合性樹脂を有していてよい。付加された末端ブロック適合性樹脂は、S−EB−Sブロックコポリマーのガラス転移点(Tg)を上昇させる。上昇したTgにより、製品はTgおよびそれより高い温度において幾分粘着性になる傾向があるので、他の場合に可能なよりも高い温度で最終物品を使用することが可能になる。そのような末端ブロック適合性樹脂の例は、ポリ−α−メチルスチレンである。
S−EB−Sブロックコポリマーは、時々合成ゴム組成物に使用されている他のブロックコポリマー、例えばスチレン−イソプレン−スチレン(S−I−S)およびスチレン−ポリブタジエン−スチレン(S−B−S)ブロックコポリマーからは区別されるべきである。S−I−SおよびS−B−Sブロックコポリマーから薄いゴム状物品を製造することは知られている(例えば、米国特許第3933723号参照)。このようなS−I−SおよびS−B−Sブロックコポリマーの使用は、物品を加硫する必要性をなくするが、物品は、酸化およびオゾン化による損傷を受けやすい。
S−EB−Sブロックコポリマーは、他の種類とは異なり、2つの理由から本発明の成功にとって不可欠である。第1に、S−EB−Sブ弾性トリブロックコポリマー系エラストマーは、オゾンまたは酸化条件による攻撃に耐性を示すが、S−I−SおよびS−B−Sエラストマーは、オゾンに暴露されると急速にひび割れし、酸化条件ではひび割れし、または硬くなる。後者のコポリマー両方は、医療及び他の用途では有害である抗オゾン剤または酸化防止剤のような特定の添加剤により保護されている場合でも、損傷される。このような特別の添加剤は、ある人ではアレルギー反応を引き起こすことがあるので、使用することは望ましくない。本発明の弾性組成物は、低アレルギー誘発性であり、長期間使用者の皮膚に触れてもよい。加えて、特別の添加剤にもかかわらず、特に物品が折り畳んだ状態で貯蔵され、その後使用前又は使用中に伸ばされた場合、S−I−SおよびS−B−S組成物から製造された物品のオゾンクラックによる分断クラックが、早期の破壊を招くことがある。
第2に、S−EB−Sトリブロックコポリマーの機械的性質は、引張強さ、弾性伸び及び触質性の望ましい組み合わせを提供するように選択できる。S−EB−S弾性トリブロックコポリマーは、S−I−SおよびS−B−Sトリブロックエラストマーよりも、高い引張強さ、小さい弾性伸び、および50〜500%伸びにおける高い応力を有している。
いくつかのS−EB−Sエラストマーの構造、特性及びいくつかの用途は、米国特許第3485787号、同3830767号及び同4006116号、同40396289号、同4041103号、同4386179号、同4481323号、同4511354号及び同4613640号に記載されている。
S−EB−Sブロックコポリマーは、ある範囲の溶液粘度/コポリマー濃度値で、市販されている。溶液粘度/コポリマー濃度値は、特定の水準で溶媒中に予め溶解されたコポリマーの粘度を測定することにより決定される。溶液粘度/コポリマー濃度値は、中央及び末端ブロック含有量がそれらの種類および相対量により特定されたブロックコポリマーの性質を独自に規定する通常の方法である。例えば、S−EB−Sブロックコポリマーは、ポリスチレン末端ブロック及びポリ(エチレン−ブチレン)中央ブロックの定まった組成、末端ブロック及び中央ブロックの相対量、及び溶液粘度/コポリマー濃度により、特定される。従って、ブロックコポリマーは、S−EB−Sタイプであり、ポリスチレン末端ブロックの割合は例えば全コポリマーの28重量%であり、77°Fにおけるトルエン中20重量%溶液のブルックフィールド粘度は1500cpsであると記載することで特定できる。
市販S−EB−Sブロックコポリマーは、市販製品それぞれがそのような基準に合致するように厳密に制御されるように、精密な方法で製造されている。Shell Kraton G1650は、28/72のスチレン/中央ブロック比、および1500の77°Fでのブルックフィールド粘度(濃度20重量%のトルエン溶液)を有しているS−EB−Sブロックコポリマーである。Shell Kraton G1651は、33/67のスチレン/中央ブロック比、および2000の77°Fでのブルックフィールド粘度(濃度20重量%のトルエン溶液)を有しているS−EB−Sブロックコポリマーである。Shell Kraton G1652は、29/71のスチレン/中央ブロック比、および550の77°Fでのブルックフィールド粘度(濃度20重量%のトルエン溶液)を有しているS−EB−Sブロックコポリマーである。
S−EB−Sブロックコポリマーは、実質的に同じ分子量の分子からなっていてよい。あるいは、2つ又はそれ以上の異なる分子量の分子の混合物からなっていてよい。分子量及び/又は分子量の混合物は、最終製品において所望の機械的性質を達成するのに寄与するように選択される。例えば、1つの好ましい形態では、ASTM規格を満たすような所望の機械的性質を達成するように、米国特許第5112900号及び同5407715号に開示されたようなS−EB−S分子の混合物を利用する。本発明にいたる研究により、単一市販ポリマーは少なくともある種の用途には適しているものの、S−EB−Sポリマーブレンド組成物は、ほとんどの場合、典型的な単一市販ポリマーよりも優れたフィルム特性を示すことが明らかになった。特に、高重量平均分子量を有するポリマー(例えば、Shell Kraton G1651)の少なくとも1種を含むS−EB−Sポリマーブレンドは、他のS−EB−Sブレンドよりも優れた性能を示す。
油(ある場合には、「可塑剤」とも称される。)は、22で示されているように、供給される。油は、好ましくは、Merck Index,第8版、Entries6971及び6972に記載されている精製石油パラフィン炭化水素油である鉱油である。好ましい鉱油は、0.87の比重(77°F)、170センチストークスの粘度(77°F)、及び492のHirschler分子量を有している。選択された油は、ポリスチレン末端セグメントを膨潤または可溶化してはならない。高水準の油を含む組成物は、他の組成物より界面活性剤が少なくても、より安定な分散液を形成する。
S−EB−Sブロックコポリマーは、製造業者からは固体で供給される。適当な分散液を調製できる混合物を形成するために、24で示されているように、溶媒(トルエン又はシクロヘキサンが好ましい)が供給される。S−EB−Sブロックコポリマー及び鉱油可塑剤は、26において混合され、共通の溶媒、好ましくはトルエン又はシクロヘキサンに溶解される。
分散媒体は、水28及び界面活性剤30から調製される。界面活性剤は、アニオン性又はカチオン性、若しくはイオン性とノニオン性との混合物であってよい。適当な界面活性剤は、米国特許第3360599号、同第3305917号及び同5120765号に記載されている。好ましい界面活性剤は、アニオン性界面活性剤である。カチオン性界面活性剤は、機能するが、アレルギー誘発性であり得るので好ましさは劣る。なお、ほとんどのアニオン性界面活性剤は、低アレルギー誘発性である。界面活性剤及びその残渣の大部分は、製造操作中に浸出され、除かれるが、少量は残り、界面活性剤が低アレルギー誘発性でなければ、製品の使用者にアレルギー反応を引き起こす。界面活性剤30は、約1〜約5容量%の量で、水32と混合される。界面活性剤30は、界面活性剤形成性化合物を添加して反応させることにより、その場で製造することもできる。例えば、油相(S−EB−S溶液)に添加したオレイン酸と水相に添加した水酸化カリウムが混合により反応して、界面活性剤オレイン酸カリウムを形成する。
場合により、増粘剤、抑泡剤、又は緩衝剤のような改質用添加剤31も供給して、水性分散媒質に添加することができる。
S−EB−S、油及び溶媒の混合物26を、34において、水と界面活性剤との混合物32と混合する。混合34は、分散液を製造するように設計された混合機を用いて高速高剪断速度条件で行う。好ましい混合機は、ローター/ステーター混合機(例えば、Charles Ross & Coから販売されているXシリーズ410−X6、又はMicrofluidies Coから販売されているMicrofluidizer M210)である。所望の粒子サイズを得るには、高剪断混合を数回行う必要がある。
分散段階34の後、36において、溶媒(好ましくはトルエン又はシクロヘキサン)を分散液から除去する。この段階は、しばしば「ストリッピング」と呼ばれる。ストリッピングは、いかなる操作可能な方法でも行え、熱/真空ストリッピング及び水蒸気ストリッピングが好ましい。溶媒は、あらゆる成分の中で最も高い蒸気圧を有しており、従って、分散液から蒸発され、抜き出される。付加的な水を、段階36で加えてもよく、あるいは濃縮段階37において加熱又は他の方法で水を除去してもよい。所望により、殺生物剤を段階37で加えてもよい。
段階20〜36に関して説明した手順と同等に、他の順序又は経路で成分を混合して分散液を調製することができる。例えば、S−EB−Sブロックコポリマー、溶媒及び一部分の水を、高剪断条件で混合して第1分散液を形成し、油及び残りの水を高剪断条件で混合して第2分散液を形成する。改質剤は、いずれの分散液に分散させてもよい。第1分散液から溶媒を除去する。その後、溶媒除去した第1分散液と第2分散液とを混合して、第3分散液を形成する。
図2A及び図2Bにより、上記方法の段階20〜36により製造した分散液の2つの可能な種類を説明する。すなわち、(水/界面活性剤)中(S−EB−S/油)水性分散液(図2A)及び(S−EB−S/油)中(水/界面活性剤)水性分散液である。分散液の種類は、ストリッピング36の後に残っている混合物26と混合物32との相対量、並びに界面活性剤(相の表面エネルギーを変える)の種類と量に依存する。(水/界面活性剤)混合物の量に比べて相対的に少量の(S−EB−S/油)−溶媒混合物が存在する場合、分散液は、図2Aに示されているように、(水/界面活性剤)連続相52中に(S−EB−S/油)−溶媒混合物の不連続液滴50が存在する構造を有する。図2Aの分散液の場合、(S−EB−S/油)液滴50は、一般に、約2μmを越えない平均寸法を有する球形である。もし粒がもっと大きければ、分離する傾向を示し、分散液は不安定になる。(S−EB−S/油)−溶媒混合物が(水/界面活性剤)混合物の量に比べて比較的多量に存在する場合、分散液は、図2Bに示されているように、(S−EB−S/油)−溶媒混合物連続相56中に(水/界面活性剤)相の不連続液滴54が存在する構造を有する。(本明細書中、水/界面活性剤相は、それが連続相、又は加工の中間段階で分散相を形成していても、「分散媒体」と称する。)
図2Aの(水/界面活性剤)中(S−EB−S/油)水性分散液は、浸漬成型方法に有用である。(S−EB−S/油)中(水/界面活性剤)水性分散液(図2B)は、浸漬成型方法で使用される水性分散液の製造中にのみ存在する一時的な系である。
図2A及び2Bの分散液の両方は、段階20〜34の分散液調製中、異なる時点で存在し得る(同時には存在しない)。例えば、米国特許第2872427号及び同3867321号並びにカナダ特許第876153号に記載されているような、好ましい反転分散法では、混合物26は、S−EB−S/油/溶媒混合物26の体積が、水/界面活性剤混合物32の体積に比べて大きくなるように、比較的高い溶媒含有量で調製されてよい。高剪断速度混合段階34により、S−EB−S/油/溶媒中水/界面活性剤混合物分散液が製造される。しかしながら、段階36で溶媒を減圧で除去し、場合によりさらに水を加えると、残留している(S−EB−S/油)混合物の相対体積がずっと小さくなり、分散液は転相し、図2Aの(水/界面活性剤)中(S−EB−S/油)水性分散液が生成する。従って、加工中に分散液の性質を判断する時点は、ストリッピング段階36の後であって、それより前の段階ではない。
分散液を製造する他の実施可能な方法も使用できる。そのような方法の例は、米国特許第3238173号、同第3503917号及び同第5120765号に開示されている。
段階20〜36により製造された分散液は、好ましくは浸漬成形方法において使用される。(もちろん、先に述べたように、他の種類の成形及び適用方法において用いることもできる。)浸漬成形方法は、他の用途について一般に知られているので、ここでは簡単に説明する。
型を供給する(38)。操作できる型ならいずれも使用でき、そのような型の最も興味ある例は、図3の人の手の型60、及び図4の閉鎖末端を有する円筒62である。手の型60は、弾性手袋を作るのに用いられ、円筒型62は、コンドームを作るのに用いられる。
物品は、最初に型を分散液に漬け(40)、次いで水を蒸発させ(すなわち乾燥し)、フィルムを溶融し、場合によりフィルムを浸出する(42)ことにより製造される。好ましい乾燥温度は、約30℃〜約100℃の範囲、最も好ましくは約70℃〜約90℃である。溶融は、典型的には、S−EB−Sブロックコポリマーの末端ブロックの軟化点より高い温度で一定時間、物品を加熱することにより行われる。通常のS−EB−Sブロックコポリマーについては、溶融処理は、好ましくは約120℃〜約150℃、最も好ましくは約130℃から140℃の範囲において、いずれの場合も25分を越えない時間、行われる。高温により、良好な機械的性質を得るのが促進される。S−EB−Sブロックコポリマーは、このような温度で安定である。このような条件は、天然ゴム浸漬成形用に設計された浸漬成形ラインにより物品を製造するのを可能にする。しかしながら、本明細書に記載しているように、S−EB−Sブロックコポリマーは、そのガラス転移点を上昇させるように変性でき、それに従って、溶融温度も上昇し得る。溶融処理の時間及び温度は、変えることができ、より高い温度ではより短い時間が、より低い温度ではより長い時間が採用される。
所望により、最終製品を水により浸出して、残留している界面活性剤を除去する。好ましい浸出時間は10分間又はそれ以下、好ましくは5分間又はそれ以下である。より長い時間及びより高い温度の改良された浸出条件により、改良されたフィルム特性が得られる。好ましい浸出温度は、約30℃〜約90℃である。
そのような物品を製造するには、記載した方法で十分大量の分散液を調製し、室温で浸漬槽に入れる。所望物品の形状を有する型(典型的には、アルミ、ガラス、プラスチック、又は磁器から作られる)に、離型剤(例えば、炭酸カルシウムスラリー又はステアリン酸カルシウム)を塗布する。その後、型を槽に漬け、ゆっくり引き上げ、型に付着した分散液の均一な薄層を残す。この操作は、型を塗料容器に浸漬して塗料の層を型に付着させるのとほとんど同じである。浸漬中、分散液は、型に適用される回転及び波動運動の組み合わせにより、型の表面に均一に分配される。型及びその上の分散液層は、室温又は高温において空気流中で乾燥され、薄いエラストマー層中の水は蒸発される。各浸漬乾燥層の厚さは、典型的に、約0.03〜0.20mmである。必要な厚さの完成した層が形成されるのに必要なだけ浸漬工程を繰り返す。本発明の浸漬成形方法に従って製造される薄い物品は、各層の厚さ及び層の数に依存して、0.03から1.0mmの厚さを有する。約0.03mm未満の厚さの層の完全性を保持するのは困難である。浸漬成形により約1.0mmを越える厚さの物品を製造するのは困難である。フイルムの乾燥及び溶融の後、物品を型からはずし、型は再使用する。物品は、本発明の方法と矛盾しない方法で、改質又は処理することができ、例えば、身体により簡単に装着できるように粉を振りかけ、あるいは、容易な着用を可能にするように適合性非粉末表面層を供給することができる。
本発明の方法により物品を商業的に浸漬成形する際には、いくつかの考慮事項がある。型を浸漬する分散液中の固形分含量は、約30〜約65重量%、最も好ましくは約55〜約63重量%である。約55重量%の固形分含量では、ASTM規格を満足する所望の手袋厚さを達成するには、多数回の浸漬が必要である。約60〜約63重量%の固形分含量では、0.25〜0.3mmの厚さの満足できるフィルムを2〜3回の浸漬で得ることができる。先の温度及び引上げ速度のような浸漬条件は、所望の厚さが得られるように変化させ得る。均一なフィルムは、型の回転及び波動運動により達成できる。より厚いフィルムは、分散液のより低い固形分含量、又は増粘剤の添加による分散液の粘度の調整により、形成できる。好ましい浸漬方法では、型上に凝固剤を用いない。他の浸漬方法も使用できる。ビードは、フィルムが熱い内に、好ましくは溶融炉を出た後に、容易に形成できる。
以下の実施例により、本発明の用途及び実用例を説明する。これらの実施例は、説明のために示されるのであって、本発明をいかなる意味においても限定するものと解釈してはならない。
実施例1
56phrの油を含む、Kraton G1650(40重量部)、Kraton G1651(40重量部)及びKraton G1652(10重量部)S−EB−Sブロックコポリマーの16重量%トルエン溶液(約150g)を、Witco Chemical製Emcol K-8300界面活性剤(1g)を含む水(約100g)に分散させた。分散は、ローター/ステーターアッセンブリを用い、高剪断条件で2分間行った。
加熱及び減圧下、ロトヴァップ(rotovap)により溶媒をストリップし、溶液は、水を添加して希釈した。分散液は、エラストマーフィルムを製造するための浸漬成形操作において用いた。
実施例2
48phrの油を含む、Kraton G1650(40重量部)、Kraton G1651(40重量部)及びKraton G1652(10重量部)S−EB−Sブロックコポリマーのシクロヘキサン溶液(約150g)を、スルホスクシネート界面活性剤(0.67g)を含む水(約150g)に分散させた。分散は、ローター/ステーターアッセンブリを用い、高剪断条件で2分間行った。
シクロヘキサンをストリップし、分散液を濃縮して、S−EB−Sブロックコポリマー及び油の水性分散液を得た。分散液を浸漬成形操作に用いて、エラストマーフィルムを形成し、このフィルムを、80〜95℃で10〜20分間、乾燥し溶融した。得られたフィルムは、優れた機械的強度特性を示した。
実施例3
最終分散液がEmcol K-8300界面活性剤を2.5重量%含有していた以外は実施例1と同様に分散液を調製した。浸漬成形により製造したフィルムを、80〜95℃で10〜20分間溶融した。得られたフィルムは、優れた機械的強度特性を示した。
実施例4
Kraton G1651(103.13g)、Kraton G1650(154.69g)及び鉱油(154.69g)をトルエン(2088g)に溶解して、S−EB−Sポリマーブレンド組成物を調製した。ポリスチレン末端ブロックの重量平均分子量は、約18000ダルトンと評価された。この溶液(600g)、並びにEmcol K-8300(3.25g)及びカリウムロジン石鹸(3.25g)を含む水(466g)を用いて水性分散液を調製した。トルエンをストリップした後、加熱及び減圧下にロトヴァップ中で分散液を濃縮した。得られた水性分散液の固形分含量は、約54重量%であった。
温かいガラス製コンドーム型を用い、複数回浸漬して、この分散液から浸漬成形によりフィルムを形成した。厚さは、0.05〜0.09mmであった。各浸漬後、フィルムを約70〜80℃で乾燥した。最終浸漬後、フィルムを130℃で5分間加熱し、次いで、温水により5分間浸出した。次に、フィルムを130℃で25分間加熱し、冷却し、粉を適用した後、型からはずした。このようにして製造したコンドームは、22.37MPaの引張強さ、2.69MPaの500%モジュラス、及び812%の破断時伸びを有していた。
実施例5
ブレンドがKraton G1651(127.74g)、Kraton G1650(151.68g)、Kraton G1652(31.94g)及び鉱油(175.64g)を含んでいた以外は実施例4と同様に、S−EB−Sブレンドを調製した。ブレンドのポリスチレン末端ブロックの重量平均分子量は、17800ダルトンと評価された。
実施例4と同様にして水性分散液を調製し、63.23重量%の固形分含量まで濃縮した。実施例4と同様に、厚さ0.1〜0.16mmのコンドームを製造した。フィルムは、23.78MPaの引張強さ、2.94MPaの500%モジュラス、及び839%の破断時伸びを有していた。
コンドームサンプルを、29.9〜39.1KGyの線量でガンマ線により滅菌した。これらサンプルは、20.61MPaの引張強さ、2.64MPaの弾性率(500%伸び)、及び897%の破断時伸びを有していた。
実施例6
70phrの鉱油を含んでいた以外は実施例4と同様に、S−EB−Sブレンドを調製した。ポリスチレン末端ブロックの重量平均分子量は、実施例4と同じく、18000ダルトンと評価された。
ブレンド溶液(600g)、並びにEmcol K-8300(3.25g)及びArizona Chemical Co.製DRS42界面活性剤(4g)を含む水(466g)を用いて、実施例4と同様にして水性分散液及びフィルムを製造した。分散液を濃縮し、この分散液から浸漬成形により、厚さ約0.04〜0.06mmのコンドームを製造した。フィルムは、18.8MPaの引張強さ、2MPaの500%モジュラス、及び884%の破断時伸びを有していた。この分散液浸漬成形コンドームは、溶液浸漬成形フィルムと同等の破裂体積及び破裂圧力を示した。
上記分散液及びセラミック型を用いて手袋を浸漬成形した。
実施例7
トルエン(2087.5g)中でKraton G1652(242.65g)及び鉱油(169.9g)を混合してS−EB−S溶液を調製した。実施例4と同様に分散液を調製した。末端ブロックの重量平均分子量は7250ダルトンと評価された。この分散液から浸漬成形された厚さ0.05〜0.07mmのコンドームは、フィルムの乾燥及び溶融中にフィルムクラックの兆候を示した。フィルムの引張強さは4.36MPaであり、500%モジュラスは約4.36MPaであった。
実施例8
トルエン中のKraton G1651、Kraton G1652及び70phrの鉱油を用いてS−EB−Sブレンド溶液を調製した。実施例4と同様にして分散液を作成した。ブレンドのポリスチレン末端ブロックの重量平均分子量は、24000ダルトンと評価された。分散液を、固形分含量63.5%まで濃縮し、この分散液からコンドームを浸漬成形した。分散液は、優れたフィルム形成特性及び中程度の強さを有していた。
実施例9
実施例5に記載したS−EB−Sブレンド組成物を、約21重量%の固形分含量で調製した。分散液は、溶液(3kg)、並びにEmcol K-8300(30g)及びカリウムロジン石鹸(70g)を含む水(4kg)を用い、2200ポンド/インチ2でMicrofluidizerに3回通して製造した。Microfluidizerに通す前に、予備分散液を作った。分散液は、0.47μmの平均粒子寸法を有していた。分散液をストリップし、濃縮した。分散液は、優れたフィルム形成特性及び良好なフィルム強度特性を示した。
実施例10
実施例5と同様にS−EB−S溶液を調製し、Ross X-Seriesミキサーを用いて分散液を作成した。分散液を、固形分含量61重量%まで濃縮した。分散液は、実施例5と同じく、良好な安定性及び良好なフィルム形成性を示した。
本発明は、水性分散液から優れた性質のフィルムを形成する技術を提供する。フィルムは、米国特許第5112900号及び同第5407715号に開示されているような有利な性質を有しているが、浸漬成形方法は、これら特許に記載されている方法よりも経済的である。本発明の特定の形態を説明のために詳細に記載してきたが、本発明の精神及び範囲を逸脱することなく、種々の変更及び改良を行うことができよう。従って、本発明は、以下の請求の範囲以外のものによって限定されない。
Claims (10)
- 水及び界面活性剤の混合物を含む分散媒体、並びに
分散媒体に分散された粒子を含んでなり、各粒子は、
15000ダルトンよりも大きい重量平均分子量をそれぞれ有する末端ブロックを持つスチレン−エチレン/ブチレン−スチレンブロックコポリマー、及び
可塑剤
の混合物を含んでなる、水性分散液。 - 粒子は、2μm以下の平均寸法を有する請求の範囲1に記載の水性分散液。
- スチレン−エチレン/ブチレン−スチレンブロックコポリマーは、実質的に同じ分子量のブロックコポリマーからなる請求の範囲1又は2に記載の水性分散液。
- スチレン−エチレン/ブチレン−スチレンブロックコポリマーは、異なる分子量の少なくとも2つのスチレン−エチレン/ブチレン−スチレンブロックコポリマーからなる請求の範囲1又は2に記載の水性分散液。
- スチレン−エチレン/ブチレン−スチレンブロックコポリマー成分の少なくとも1つは、少なくとも150000ダルトンを越える総重量平均分子量を有する請求の範囲4に記載の水性分散液。
- 水及び界面活性剤から本質的になる分散媒体、並びに
分散媒体に分散された粒子を含んでなり、各粒子は、
15000ダルトンよりも大きい重量平均分子量をそれぞれ有する末端ブロックを持つスチレン−エチレン/ブチレン−スチレンブロックコポリマー、及び
可塑剤
の混合物を含んでなる水性分散液を供給し、
水性分散液に型を浸し、水性分散液から型を引き上げ、型の上に分散液の膜を残し、
型上の分散液から水を蒸発させ、形成されたフィルム加熱してフィルムを溶融し、型の上に凝集延伸性フィルムを残す
工程を含んでなる、弾性物品の製造方法。 - 水性分散液を供給する工程は、
スチレン−エチレン/ブチレン−スチレンブロックコポリマーが実質的に同じ分子量のブロックコポリマーからなる水性分散液を供給すること
を含む請求の範囲6に記載の方法。 - 水性分散液を供給する工程は、
スチレン−エチレン/ブチレン−スチレンブロックコポリマーが異なる分子量の少なくとも2つのスチレン−エチレン/ブチレン−スチレンブロックコポリマーからなる水性分散液を供給すること
を含む請求の範囲6に記載の方法。 - 供給する工程は、
スチレン−エチレン/ブチレン−スチレンブロックコポリマー、可塑剤及び溶媒を含む第1混合物を調製し、
水及び界面活性剤を含む第2混合物を調製し、
第1混合物及び第2混合物を、高剪断条件で混合して分散液を形成し、
分散液から溶媒をストリップする
工程を含んでなる請求の範囲6〜8のいずれかに記載の方法。 - 供給する工程は、
スチレン−エチレン/ブチレン−スチレンブロックコポリマー、溶媒及び水を含む第1分散液を調製し、
第1分散液から溶媒をストリップし、
可塑剤及び水を含む第2分散液を調製し、
ストリップされた第1分散液及び第2分散液を混合して第3分散液を形成する工程を含んでなる請求の範囲6〜8のいずれかに記載の方法。