JP2022530507A - カルボン酸変性ニトリル系共重合体ラテックス、これを含むディップ成形用ラテックス組成物およびこれより成形された成形品 - Google Patents
カルボン酸変性ニトリル系共重合体ラテックス、これを含むディップ成形用ラテックス組成物およびこれより成形された成形品 Download PDFInfo
- Publication number
- JP2022530507A JP2022530507A JP2021563711A JP2021563711A JP2022530507A JP 2022530507 A JP2022530507 A JP 2022530507A JP 2021563711 A JP2021563711 A JP 2021563711A JP 2021563711 A JP2021563711 A JP 2021563711A JP 2022530507 A JP2022530507 A JP 2022530507A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- latex
- carboxylic acid
- dip molding
- modified nitrile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
[実施例1]
<カルボン酸変性ニトリル系共重合体ラテックスの製造>
以下、重量%は、カルボン酸変性ニトリル系共重合体の主鎖を形成するために投入される全単量体含量に対して記載したものであり、重量部は、投入される単量体の全100重量部に対して記載したものである。
前記取得したカルボン酸変性ニトリル系共重合体ラテックス100重量部(固形分基準)に、硫黄1重量部、ジ-n-ブチルジチオカルバメート亜鉛(ZDBC、zinc di-n-butyldithiocarbamate)1.0重量部、酸化亜鉛1.3重量部および酸化チタン1重量部と水酸化カリウム溶液および2次蒸留水を加えて、固形分濃度30重量%およびpH10.2のディップ成形用ラテックス組成物を取得した。
18重量%のカルシウムナイトレート、81.5重量%の水、0.5重量%の湿潤剤(Huntsman Corporation、Teric 320)を混合して凝固剤溶液を製造し、この溶液に手形状のセラミックモールドを13秒間浸漬し、取り出した後、120℃で3分間乾燥し、凝固剤を手形状のモールドに塗布した。
撹拌機が取り付けられた重合反応器にアクリロニトリル18重量%およびメタクリル酸4.5重量%を投入した後、撹拌を開始して混合し、t-ドデシルメルカプタン0.3重量部、ナトリウムドデシルベンゼンスルホネート3.0重量部、70℃の水130重量部を投入した後、1,3-ブタジエン77.5重量%を投入し、2.7kgf/cm2の圧力および40℃の温度で重合開始剤である過硫酸カリウム0.25重量部を投入し、乳化重合を開始した。
撹拌機が取り付けられた重合反応器にアクリロニトリル28重量%およびメタクリル酸2.5重量%を投入した後、撹拌を開始して混合し、t-ドデシルメルカプタン0.8重量部、ナトリウムドデシルベンゼンスルホネート3.0重量部、50℃の水110重量部を投入した後、1,3-ブタジエン69.5重量%を投入し、2.2kgf/cm2の圧力および37℃の温度で重合開始剤である過硫酸カリウム0.35重量部を投入し、乳化重合を開始した。
撹拌機が取り付けられた重合反応器にアクリロニトリル25重量%およびメタクリル酸4.1重量%を投入した後、撹拌を開始して混合し、t-ドデシルメルカプタン0.3重量部、ナトリウムドデシルベンゼンスルホネート2.5重量部、55℃の水140重量部を投入した後、1,3-ブタジエン70.9重量%を投入し、2.4kgf/cm2の圧力および40℃の温度で重合開始剤である過硫酸カリウム0.2重量部を投入し、乳化重合を開始した。
撹拌機が取り付けられた重合反応器にアクリロニトリル21重量%およびメタクリル酸2.9重量%を投入した後、撹拌を開始して混合し、t-ドデシルメルカプタン0.6重量部、ナトリウムドデシルベンゼンスルホネート3.5重量部、75℃の水110重量部を投入した後、1,3-ブタジエン76.1重量%を投入し、2.6kgf/cm2の圧力および39℃の温度で重合開始剤である過硫酸カリウム0.3重量部を投入し、乳化重合を開始した。
撹拌機が取り付けられた重合反応器にアクリロニトリル28重量%およびメタクリル酸4.5重量%を投入した後、撹拌を開始して混合し、t-ドデシルメルカプタン0.25重量部、ナトリウムドデシルベンゼンスルホネート3.0重量部、60℃の水110重量部を投入した後、1,3-ブタジエン67.5重量%を投入し、2.0kgf/cm2の圧力および36℃の温度で重合開始剤である過硫酸カリウム0.45重量部を投入し、乳化重合を開始した。
撹拌機が取り付けられた重合反応器にアクリロニトリル18重量%およびメタクリル酸2.5重量%を投入した後、撹拌を開始して混合し、t-ドデシルメルカプタン0.5重量部、ナトリウムドデシルベンゼンスルホネート3.5重量部、65℃の水120重量部を投入した後、1,3-ブタジエン79.5重量%を投入し、2.8kgf/cm2の圧力および41℃の温度で重合開始剤である過硫酸カリウム0.15重量部を投入し、乳化重合を開始した。
撹拌機が取り付けられた重合反応器にアクリロニトリル26重量%およびメタクリル酸4重量%を投入した後、撹拌を開始して混合し、t-ドデシルメルカプタン0.6重量部、ナトリウムドデシルベンゼンスルホネート3.5重量部、60℃の水120重量部を投入した後、イソプレン70重量%を投入し、2.4kgf/cm2の圧力および41℃の温度で重合開始剤である過硫酸カリウム0.3重量部を投入し、乳化重合を開始した。
前記実施例1でディップ成形用ラテックス組成物の製造時に、酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート1重量部を投入した以外は、実施例1と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記実施例1でディップ成形用ラテックス組成物の製造時に、硫黄1重量部、ジ-n-ブチルジチオカルバメート亜鉛1.0重量部および酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート2重量部を投入した以外は、実施例1と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記実施例6でディップ成形用ラテックス組成物の製造時に、酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート1重量部を投入した以外は、実施例6と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記実施例6でディップ成形用ラテックス組成物の製造時に、硫黄1重量部、ジ-n-ブチルジチオカルバメート亜鉛1.0重量部および酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート2重量部を投入した以外は、実施例6と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記実施例7でディップ成形用ラテックス組成物の製造時に、酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート1重量部を投入した以外は、実施例7と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記実施例7でディップ成形用ラテックス組成物の製造時に、硫黄1重量部、ジ-n-ブチルジチオカルバメート亜鉛1.0重量部および酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート2重量部を投入した以外は、実施例7と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
[比較例1]
撹拌機が取り付けられた重合反応器にアクリロニトリル31重量%およびメタクリル酸6重量%を投入し、t-ドデシルメルカプタン0.6重量部、ナトリウムドデシルベンゼンスルホネート4.0重量部、60℃の水120重量部を投入した後、1,3-ブタジエン63重量%を投入し、2.5kgf/cm2の圧力および39℃の温度で重合開始剤である過硫酸カリウム0.3重量部を投入し、撹拌を開始しながら乳化重合を開始した。
撹拌機が取り付けられた重合反応器にt-ドデシルメルカプタン0.25重量部、ナトリウムドデシルベンゼンスルホネート3.0重量部、60℃の水110重量部を投入した後、撹拌を開始して混合し、アクリロニトリル28重量%、メタクリル酸4.5重量%および1,3-ブタジエン67.5重量%を投入し、2.0kgf/cm2の圧力および36℃の温度で重合開始剤である過硫酸カリウム0.45重量部を投入して、乳化重合を開始した。
撹拌機が取り付けられた重合反応器にアクリロニトリル18重量%およびメタクリル酸1重量%を投入し、t-ドデシルメルカプタン0.25重量部、ナトリウムドデシルベンゼンスルホネート4.0重量部、70℃の水110重量部を投入した後、1,3-ブタジエン81重量%を投入し、2.8kgf/cm2の圧力および40℃の温度で重合開始剤である過硫酸カリウム0.45重量部を投入し、撹拌を開始しながら乳化重合を開始した。
撹拌機が取り付けられた重合反応器にアクリロニトリル31重量%およびメタクリル酸2.5重量%を投入し、t-ドデシルメルカプタン0.6重量部、ナトリウムドデシルベンゼンスルホネート4.0重量部、50℃の水120重量部を投入した後、1,3-ブタジエン66.5重量%を投入し、2.2kgf/cm2の圧力および37℃の温度で重合開始剤である過硫酸カリウム0.3重量部を投入し、撹拌を開始しながら乳化重合を開始した。
撹拌機が取り付けられた重合反応器にt-ドデシルメルカプタン0.25重量部、ナトリウムドデシルベンゼンスルホネート4重量部、65℃の水130重量部を投入し、アクリロニトリル14重量%、メタクリル酸6重量%および1,3-ブタジエン80重量%を投入した後、撹拌を開始して混合し、2.4kgf/cm2の圧力および41℃の温度で重合開始剤である過硫酸カリウム0.45重量部を投入して、乳化重合を開始した。
前記比較例1でディップ成形用ラテックス組成物の製造時に、酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート1重量部を投入した以外は、比較例1と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記比較例1でディップ成形用ラテックス組成物の製造時に、硫黄1重量部、ジ-n-ブチルジチオカルバメート亜鉛1.0重量部および酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート2重量部を投入した以外は、比較例1と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記比較例2でディップ成形用ラテックス組成物の製造時に、酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート1重量部を投入した以外は、比較例2と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記比較例2でディップ成形用ラテックス組成物の製造時に、硫黄1重量部、ジ-n-ブチルジチオカルバメート亜鉛1.0重量部および酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート2重量部を投入した以外は、比較例2と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記比較例4でディップ成形用ラテックス組成物の製造時に、酸化亜鉛1.3重量部アルミニウムシトレート1重量部を投入した以外は、比較例4と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記比較例4でディップ成形用ラテックス組成物の製造時に、硫黄1重量部、ジ-n-ブチルジチオカルバメート亜鉛1.0重量部および酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート2重量部を投入した以外は、比較例4と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記比較例5でディップ成形用ラテックス組成物の製造時に、酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート1重量部を投入した以外は、比較例5と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
前記比較例5でディップ成形用ラテックス組成物の製造時に、硫黄1重量部、ジ-n-ブチルジチオカルバメート亜鉛1.0重量部および酸化亜鉛1.3重量部の代わりに、アルミニウムシトレート2重量部を投入した以外は、比較例5と同じ方法でディップ成形用ラテックス組成物および成形品を製造した。
[実験例1]
前記実施例1~8 および比較例1~5で製造されたカルボン酸変性ニトリル系共重合体ラテックスの物性を下記のような方法で測定し、下記表1に示した。
前記実施例1~8および比較例1~5で製造された成形品の物性を下記のような方法で測定し、下記表2に示した。
架橋剤の変化による成形品の物性の変化を示すための前記実施例9~14および比較例6~13で製造された成形品の物性を、前記実験例2と同じ方法で測定し、下記表3に示した。
Claims (16)
- 前記カルボン酸変性ニトリル系共重合体は、エチレン性不飽和ニトリル系単量体由来の単位18重量%~28重量%を含む、請求項1に記載のディップ成形用ラテックス組成物。
- 前記カルボン酸変性ニトリル系共重合体は、共役ジエン系単量体由来の単位67.5重量%~79.5重量%を含む、請求項1に記載のディップ成形用ラテックス組成物。
- 前記共役ジエン系単量体は、1,3-ブタジエン、2,3-ジメチル-1,3-ブタジエン、2-エチル-1,3-ブタジエン、1,3-ペンタジエンおよびイソプレンからなる群から選択される1種以上を含む、請求項1に記載のディップ成形用ラテックス組成物。
- 前記エチレン性不飽和ニトリル系単量体は、アクリロニトリル、メタクリロニトリル、フマロニトリル、α-クロロニトリルおよびα-シアノエチルアクリロニトリルからなる群から選択される1種以上を含む、請求項1に記載のディップ成形用ラテックス組成物。
- 前記エチレン性不飽和酸単量体は、アクリル酸、メタクリル酸、イタコン酸、マレイン酸、フマル酸、無水マレイン酸、無水シトラコン酸、スチレンスルホン酸、フマル酸モノブチル、マレイン酸モノブチルおよびマレイン酸モノ-2-ヒドロキシプロピルからなる群から選択される1種以上を含む、請求項1に記載のディップ成形用ラテックス組成物。
- 前記共役ジエン系単量体は、1,3-ブタジエンまたはイソプレンであり、
前記エチレン性不飽和ニトリル系単量体は、アクリロニトリルであり、
前記エチレン性不飽和酸単量体は、メタクリル酸である、請求項1に記載のディップ成形用ラテックス組成物。 - 前記カルボン酸変性ニトリル系共重合体は、エチレン性不飽和単量体由来の単位をさらに含む、請求項1に記載のディップ成形用ラテックス組成物。
- 前記ディップ成形用ラテックス組成物は、架橋剤組成物をさらに含む、請求項1に記載のディップ成形用ラテックス組成物。
- 前記架橋剤組成物は、加硫剤、加硫促進剤、2価陽イオン金属酸化物および多価金属陽イオン化合物からなる群から選択される1種以上を含む、請求項11に記載のディップ成形用ラテックス組成物。
- 前記架橋剤組成物は、加硫剤、加硫促進剤および多価金属陽イオン化合物を含む、請求項12に記載のディップ成形用ラテックス組成物。
- 前記架橋剤組成物は、多価金属陽イオン化合物を含む、請求項12に記載のディップ成形用ラテックス組成物。
- 請求項1に記載のディップ成形用ラテックス組成物由来の層を含む、成形品。
- 前記成形品は、伸び率が580%~800%であり、500%モジュラスが4~20.5である、請求項15に記載の成形品。