JP2021004857A - Method for inspecting welded part - Google Patents
Method for inspecting welded part Download PDFInfo
- Publication number
- JP2021004857A JP2021004857A JP2019120156A JP2019120156A JP2021004857A JP 2021004857 A JP2021004857 A JP 2021004857A JP 2019120156 A JP2019120156 A JP 2019120156A JP 2019120156 A JP2019120156 A JP 2019120156A JP 2021004857 A JP2021004857 A JP 2021004857A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- coated steel
- welded
- layer side
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、溶着部の検査方法に関する。 The present invention relates to a method for inspecting a welded portion.
一般に、住宅等の建物において、防水性が必要とされる所定の箇所には、防水層が設けられている。この防水層は、樹脂で被膜された鋼板（以下、適宜「樹脂被膜鋼板」と称す。）又は複数の樹脂製の防水シート（以下、適宜「防水シート」と称す。）を含んで構成されることがある。 Generally, in a building such as a house, a waterproof layer is provided at a predetermined place where waterproofness is required. This waterproof layer is configured to include a resin-coated steel sheet (hereinafter, appropriately referred to as "resin-coated steel sheet") or a plurality of resin-made waterproof sheets (hereinafter, appropriately referred to as "waterproof sheet"). Sometimes.
このように、防水層が複数の樹脂被膜鋼板又は防水シートを含んで構成される場合には、これらのつなぎ目において、下層側の樹脂被膜鋼板又は防水シートに対して、上層側の防水シートが溶着されている。このとき、防水層の防水性及び耐久性は、当該つなぎ目の溶着品質によって左右される。 In this way, when the waterproof layer is composed of a plurality of resin-coated steel sheets or waterproof sheets, the upper-layer waterproof sheet is welded to the lower-layer resin-coated steel sheet or waterproof sheet at these joints. Has been done. At this time, the waterproofness and durability of the waterproof layer depend on the welding quality of the joint.
従来、溶着部の溶着状態を検査する方法として、上層側の防水シートの小口に、棒状又は扁平状の工具を当てる方法が知られている。この方法では、当該工具の入り込みの有無によって、溶着部の溶着状態を検査する。 Conventionally, as a method of inspecting the welded state of the welded portion, a method of applying a rod-shaped or flat-shaped tool to the edge of the waterproof sheet on the upper layer side is known. In this method, the welded state of the welded portion is inspected depending on the presence or absence of the tool.
また、特許文献１には、上層側の防水シートのうち、溶着されていない部分に吸盤を吸着させて、該吸盤を引き上げることで、溶着された部分と溶着されていない部分の境界を検査する方法が開示されている。 Further, in Patent Document 1, the suction cup is adsorbed on the non-welded portion of the upper layer side waterproof sheet, and the suction cup is pulled up to inspect the boundary between the welded portion and the non-welded portion. The method is disclosed.
しかしながら、上記いずれの方法を用いても、溶着状態を検査できるのは、溶着作業が行われた部分（溶着部）のうち、実際に溶着された部分（以下、適宜「正規溶着部」と称す。）の外側端部のみである。つまり、これらの方法では、溶着部において周囲を正規溶着部に囲まれて内部に空気が溜まってしまった未溶着の部分（以下、適宜「未溶着部」と称す。）が存在する場合、これを特定することができない。 However, using any of the above methods, the welded state can be inspected only in the portion where the welding work has been performed (welded portion), which is actually welded (hereinafter, appropriately referred to as "normal welded portion"). .) Only at the outer end. That is, in these methods, when there is an unwelded portion (hereinafter, appropriately referred to as "unwelded portion") in the welded portion, which is surrounded by a normal welded portion and air is accumulated inside, this is applied. Cannot be identified.
防水層の溶着部に未溶着部が存在すると、防水性及び耐久性の確保に必要な溶着幅を確保できない場合がある。したがって、溶着後には、未溶着部を特定する検査を行い、必要に応じて当該部分を補修することが望ましい。 If there is an unwelded portion in the welded portion of the waterproof layer, it may not be possible to secure the welding width required for ensuring waterproofness and durability. Therefore, after welding, it is desirable to carry out an inspection to identify the unwelded portion and repair the portion as necessary.
本発明は上記事実を考慮し、溶着部において、未溶着部を特定可能な溶着部の検査方法を提供することを目的とする。 In consideration of the above facts, an object of the present invention is to provide a method for inspecting a welded portion in which an unwelded portion can be identified.
第１の態様に係る溶着部の検査方法は、建物に設けられた防水層において、下層側に設けられた樹脂被膜鋼板又は樹脂製の防水シートと上層側に設けられた樹脂製の防水シートとの溶着部を、前記下層側の樹脂被膜鋼板、前記下層側の防水シート及び前記上層側の防水シートが溶融しない範囲で、前記上層側から加熱する工程と、前記溶着部において加熱前の状態よりも***された部分を未溶着部として判定する工程と、を有している。 The method for inspecting the welded portion according to the first aspect is that, in the waterproof layer provided in the building, a resin-coated steel plate or a resin waterproof sheet provided on the lower layer side and a resin waterproof sheet provided on the upper layer side are used. From the step of heating the welded portion from the upper layer side to the extent that the resin-coated steel plate on the lower layer side, the tarpaulin on the lower layer side, and the tarpaulin on the upper layer side do not melt, and the state before heating in the welded portion. Also has a step of determining the raised portion as an unwelded portion.
第１の態様によれば、まず、溶着部において、上層側に設けられた防水シートが上層側から加熱される。 According to the first aspect, first, in the welded portion, the waterproof sheet provided on the upper layer side is heated from the upper layer side.
次に、溶着部に未溶着部が存在する場合には、該加熱によって未溶着部の内部の空気が膨張し、未溶着部の内圧が高まる。これにより、上層側の防水シートのうち、未溶着部の上層側を構成する部分が押し上げられて***される。これに対して、正規溶着部を加熱しても、防水シートのうち、正規溶着部の上層側を構成する部分は***されない。 Next, when there is an unwelded portion in the welded portion, the air inside the unwelded portion expands due to the heating, and the internal pressure of the unwelded portion increases. As a result, of the waterproof sheet on the upper layer side, the portion constituting the upper layer side of the unwelded portion is pushed up and raised. On the other hand, even if the normal welded portion is heated, the portion of the waterproof sheet that constitutes the upper layer side of the regular welded portion is not raised.
つまり、溶着部を加熱することで、上層側の防水シートのうち、未溶着部の上層側を構成する部分のみが***され、正規溶着部の上層側を構成する部分は***されない。よって、溶着部において、加熱後に加熱前の状態よりも***された部分が、未溶着部として判定される。 That is, by heating the welded portion, only the portion of the waterproof sheet on the upper layer side that constitutes the upper layer side of the unwelded portion is raised, and the portion that constitutes the upper layer side of the normal welded portion is not raised. Therefore, in the welded portion, the portion raised after heating from the state before heating is determined as the unwelded portion.
第２の態様に係る溶着部の検査方法は、第１の態様において、前記溶着は、設定温度及び風量の少なくとも一方を調節可能な熱風ガンによる熱風溶着とされ、前記加熱は、前記熱風ガンの設定温度及び風量の少なくとも一方を、前記熱風溶着時よりも下げて行う。 The method for inspecting the welded portion according to the second aspect is that, in the first aspect, the welding is hot air welding by a hot air gun capable of adjusting at least one of a set temperature and an air volume, and the heating is performed on the hot air gun. At least one of the set temperature and the air volume is set lower than that at the time of hot air welding.
第２の態様によれば、熱風溶着時に使用した熱風ガンを用いて、熱風溶着後に溶着部が加熱される。 According to the second aspect, the welded portion is heated after the hot air welding by using the hot air gun used at the time of hot air welding.
第３の態様に係る溶着部の検査方法は、第１又は第２の態様において、前記溶着部において、前記上層側の防水シートの上に金属製の薄板を置き、前記薄板を介して前記溶着部を加熱する。 In the method for inspecting the welded portion according to the third aspect, in the first or second aspect, in the welded portion, a thin metal plate is placed on the waterproof sheet on the upper layer side, and the welded portion is placed through the thin plate. Heat the part.
第３の態様によれば、金属製の薄板において熱が拡散され、この薄板からの伝熱によって防水シートが加熱される。これにより、溶着部において薄板と接する範囲が一度に加熱される。 According to the third aspect, heat is diffused in the thin metal plate, and the heat transfer from the thin plate heats the waterproof sheet. As a result, the area of the welded portion in contact with the thin plate is heated at once.
第４の態様に係る溶着部の検査方法は、第１〜第３のいずれかの態様において、前記下層側の樹脂被膜鋼板は、平部及び立ち上がり部を含んで構成され、前記平部と前記立ち上がり部との間には湾曲されたコーナー部が形成されており、前記上層側の防水シートは、前記コーナー部を含む範囲で前記下層側の樹脂被膜鋼板に溶着されている。 In the method for inspecting the welded portion according to the fourth aspect, in any one of the first to third aspects, the resin-coated steel sheet on the lower layer side is configured to include a flat portion and a rising portion, and the flat portion and the above-mentioned flat portion. A curved corner portion is formed between the rising portion and the rising portion, and the waterproof sheet on the upper layer side is welded to the resin-coated steel plate on the lower layer side in a range including the corner portion.
第４の態様によれば、コーナー部に未溶着部が存在する場合、上層側の防水シートのうち、該未溶着部の上層側を構成する部分が***される。 According to the fourth aspect, when the unwelded portion is present at the corner portion, the portion of the waterproof sheet on the upper layer side that constitutes the upper layer side of the unwelded portion is raised.
第５の態様に係る溶着部の検査方法は、第１〜第４のいずれかの態様において、前記建物は住宅とされ、前記防水層は、当該住宅のバルコニー又はベランダに設けられている。 In the method for inspecting the welded portion according to the fifth aspect, in any one of the first to fourth aspects, the building is a house, and the waterproof layer is provided on a balcony or a veranda of the house.
第５の態様によれば、住宅のバルコニー又はベランダに設けられている防水層において、溶着部に形成された未溶着部が特定される。 According to the fifth aspect, in the waterproof layer provided on the balcony or veranda of the house, the unwelded portion formed in the welded portion is specified.
以上説明したように、第１の態様に係る溶着部の検査方法は、溶着部において未溶着部を特定できるという優れた効果を有する。 As described above, the method for inspecting a welded portion according to the first aspect has an excellent effect that an unwelded portion can be identified in the welded portion.
第２の態様に係る溶着部の検査方法は、溶着に使用した機材を用いて、効率よく簡便に溶着部の溶着状態を検査できるという優れた効果を有する。 The method for inspecting the welded portion according to the second aspect has an excellent effect that the welded state of the welded portion can be inspected efficiently and easily by using the equipment used for welding.
第３の態様に係る溶着部の検査方法は、溶着部の広い範囲を効率よく検査できるという優れた効果を有する。 The method for inspecting a welded portion according to the third aspect has an excellent effect that a wide range of the welded portion can be efficiently inspected.
第４の態様に係る溶着部の検査方法は、コーナー部に形成された未溶着部を特定できるという優れた効果を有する。 The method for inspecting the welded portion according to the fourth aspect has an excellent effect that the unwelded portion formed in the corner portion can be identified.
第５の態様に係る溶着部の検査方法は、雨水にさらされる住宅のバルコニーやベランダにおいて、高い防水性及び耐久性を確保し、住宅を漏水から守ることができるという優れた効果を有する。 The method for inspecting a welded portion according to a fifth aspect has an excellent effect that high waterproofness and durability can be ensured and the house can be protected from water leakage on a balcony or a veranda of a house exposed to rainwater.
（第１実施形態）
以下、図１〜図５を用いて、第１実施形態に係る溶着部の検査方法について説明する。本実施形態では、住宅のバルコニー１０（図２参照）に設けられた防水層１２に、本発明に係る検査方法を適用した場合について説明する。なお、各図に適宜示される矢印ＵＰは鉛直上向きを示す。また、以下の説明で特記なく上下の方向を用いる場合は、鉛直上下方向の上下を示すものとする。また、上層側とは、防水層１２の上層側を示し、下層側とは、防水層１２の下層側を示すものとする。
(First Embodiment)
Hereinafter, a method for inspecting the welded portion according to the first embodiment will be described with reference to FIGS. 1 to 5. In the present embodiment, a case where the inspection method according to the present invention is applied to the waterproof layer 12 provided on the balcony 10 of the house (see FIG. 2) will be described. The arrow UP shown in each figure indicates a vertically upward direction. In addition, when the vertical direction is used in the following description without special mention, it shall indicate the vertical vertical vertical direction. Further, the upper layer side means the upper layer side of the waterproof layer 12, and the lower layer side means the lower layer side of the waterproof layer 12.
図１には、住宅のバルコニー１０に設けられた防水層１２の概略斜視図が示されている。バルコニー１０には、床材の上に断熱材、絶縁シートが順に敷設されている（いずれも図示しない）。防水層１２は、バルコニー１０においてこれらの上に設けられている。また、防水層１２は平面視で略矩形状に形成されており、住宅の部屋とバルコニー１０との出入り口側（以下、適宜「屋内側」と称す。）に一方の長辺を有し、屋内側とは反対側（以下、適宜「屋外側」と称す。）に他方の長辺を有する。 FIG. 1 shows a schematic perspective view of the waterproof layer 12 provided on the balcony 10 of the house. On the balcony 10, a heat insulating material and an insulating sheet are laid in order on the floor material (neither is shown). The waterproof layer 12 is provided on the balcony 10 above them. Further, the waterproof layer 12 is formed in a substantially rectangular shape in a plan view, and has one long side on the entrance / exit side (hereinafter, appropriately referred to as "indoor side") between the room of the house and the balcony 10. It has the other long side on the side opposite to the inside (hereinafter, appropriately referred to as the "outdoor side").
＜樹脂被膜鋼板＞
防水層１２は、樹脂被膜鋼板１４、１６、１８、２０、２２、２４、２６、２８を含んで構成されている。
<Resin coated steel sheet>
The waterproof layer 12 includes resin-coated steel sheets 14, 16, 18, 20, 22, 24, 26, and 28.
各樹脂被膜鋼板１４、１６、１８、２０、２２、２４、２６、２８は、めっき鋼板の表側の面に、塩化ビニル樹脂を被膜した所謂塩ビ鋼板とされる。一例として、図３に示されるように、樹脂被膜鋼板２０では、めっき鋼板２１の表側の面に、塩化ビニル樹脂製の樹脂層２３が形成されている。樹脂被膜鋼板２０の詳細については後述する。 Each of the resin-coated steel sheets 14, 16, 18, 20, 22, 24, 26, and 28 is a so-called vinyl chloride steel sheet in which the front surface of the plated steel sheet is coated with a vinyl chloride resin. As an example, as shown in FIG. 3, in the resin-coated steel sheet 20, a resin layer 23 made of vinyl chloride resin is formed on the front surface of the plated steel sheet 21. Details of the resin-coated steel sheet 20 will be described later.
図１に示されるように、樹脂被膜鋼板１４、１６、１８、２０は、防水層１２の屋内側において、一端側から他端側へ順に敷設されている。一方で、樹脂被膜鋼板２２、２４、２６、２８は、防水層１２の屋外側において、一端側から他端側へ順に敷設されている。以下、「一端側」とは、防水層１２において、平面視で樹脂被膜鋼板１４及び樹脂被膜鋼板２２が設けられている側を示すものとし、「他端側」とは、防水層１２において、平面視で樹脂被膜鋼板２０及び樹脂被膜鋼板２８が設けられている側を示すものとする。 As shown in FIG. 1, the resin-coated steel sheets 14, 16, 18, and 20 are laid in order from one end side to the other end side on the indoor side of the waterproof layer 12. On the other hand, the resin-coated steel plates 22, 24, 26, and 28 are laid in order from one end side to the other end side on the outdoor side of the waterproof layer 12. Hereinafter, the "one end side" is defined as the side of the waterproof layer 12 where the resin-coated steel plate 14 and the resin-coated steel plate 22 are provided in a plan view, and the "other end side" is the waterproof layer 12. It is assumed that the side on which the resin-coated steel sheet 20 and the resin-coated steel sheet 28 are provided is shown in a plan view.
樹脂被膜鋼板１４は、略水平に形成された平部１４Ａと、平部１４Ａの屋内側の端部から略上向きに延出された立ち上がり部１４Ｂとを含んで構成されている。さらに樹脂被膜鋼板１４には、防水層１２の一端側の短辺に沿って、平部１４Ａから略上向きに延出された立ち上がり部１４Ｃが形成されている。 The resin-coated steel sheet 14 includes a flat portion 14A formed substantially horizontally and a rising portion 14B extending substantially upward from an indoor end portion of the flat portion 14A. Further, the resin-coated steel sheet 14 is formed with a rising portion 14C extending substantially upward from the flat portion 14A along the short side on one end side of the waterproof layer 12.
樹脂被膜鋼板１６は、略水平に形成された平部１６Ａと、平部１６Ａの屋内側の端部から略上向きに延出された立ち上がり部１６Ｂとを含んで構成されている。同様に、樹脂被膜鋼板１８は、平部１８Ａと立ち上がり部１８Ｂとを含んで構成されている。 The resin-coated steel plate 16 includes a flat portion 16A formed substantially horizontally and a rising portion 16B extending substantially upward from an indoor end portion of the flat portion 16A. Similarly, the resin-coated steel sheet 18 is configured to include a flat portion 18A and a rising portion 18B.
また同様に、樹脂被膜鋼板２０は、平部２０Ａと立ち上がり部２０Ｂとを含んで構成されている。さらに樹脂被膜鋼板２０には、防水層１２の他端側の短辺に沿って、平部２０Ａから略上向きに延出された立ち上がり部２０Ｃが形成されている。樹脂被膜鋼板１４の立ち上がり部１４Ｃと樹脂被膜鋼板２０の立ち上がり部２０Ｃとは互いに対向している。 Similarly, the resin-coated steel sheet 20 includes a flat portion 20A and a rising portion 20B. Further, the resin-coated steel sheet 20 is formed with a rising portion 20C extending substantially upward from the flat portion 20A along the short side on the other end side of the waterproof layer 12. The rising portion 14C of the resin-coated steel sheet 14 and the rising portion 20C of the resin-coated steel sheet 20 face each other.
なお、樹脂被膜鋼板１４、１６、１８、２０の各平部１４Ａ、１６Ａ、１８Ａ、２０Ａは、それぞれ平面視で防水層１２の長手方向に長辺を有し、防水層１２の短手方向に短辺を有する略矩形状の薄い板とされる。樹脂被膜鋼板１４、１６、１８、２０の平面視における長手方向の長さは、互いに略同一である。また、これらの平面視における短手方向の長さも、互いに略同一である。 The flat portions 14A, 16A, 18A, and 20A of the resin-coated steel sheets 14, 16, 18, and 20 each have a long side in the longitudinal direction of the waterproof layer 12 in a plan view, and are oriented in the lateral direction of the waterproof layer 12. It is a thin plate with a short side and a substantially rectangular shape. The lengths of the resin-coated steel sheets 14, 16, 18, and 20 in the longitudinal direction in a plan view are substantially the same as each other. Further, the lengths in the lateral view in these plan views are also substantially the same as each other.
樹脂被膜鋼板２２は、樹脂被膜鋼板１４の屋外側の端部において、防水層１２の一端部から樹脂被膜鋼板１４の長手方向中央部にかけて、樹脂被膜鋼板１４に隣接して配置されている。 The resin-coated steel sheet 22 is arranged adjacent to the resin-coated steel sheet 14 at the outdoor end of the resin-coated steel sheet 14 from one end of the waterproof layer 12 to the central portion in the longitudinal direction of the resin-coated steel sheet 14.
同様に、樹脂被膜鋼板２４は、樹脂被膜鋼板１４、１６、１８の屋外側の端部において、樹脂被膜鋼板１４の長手方向中央部から樹脂被膜鋼板１８の長手方向中央部にかけて、これらの樹脂被膜鋼板１４、１６、１８に隣接して配置されている。 Similarly, the resin-coated steel sheet 24 has these resin coatings at the outdoor end portions of the resin-coated steel sheets 14, 16 and 18 from the longitudinal center portion of the resin-coated steel sheet 14 to the longitudinal center portion of the resin-coated steel sheet 18. It is arranged adjacent to the steel plates 14, 16 and 18.
また同様に、樹脂被膜鋼板２６は、樹脂被膜鋼板１８、２０の屋外側の端部において、樹脂被膜鋼板１８の長手方向中央部から樹脂被膜鋼板２０の長手方向中央部にかけて隣接して配置されている。さらに同様に、樹脂被膜鋼板２８は、樹脂被膜鋼板２０の屋外側の端部において、樹脂被膜鋼板２０の長手方向中央部から防水層１２の他端部にかけて隣接して配置されている。 Similarly, the resin-coated steel sheets 26 are arranged adjacent to each other at the outdoor-side ends of the resin-coated steel sheets 18 and 20 from the central portion in the longitudinal direction of the resin-coated steel sheets 18 to the central portion in the longitudinal direction of the resin-coated steel sheets 20. There is. Further, similarly, the resin-coated steel sheet 28 is arranged adjacent to the resin-coated steel sheet 20 at the outdoor end portion from the central portion in the longitudinal direction of the resin-coated steel sheet 20 to the other end of the waterproof layer 12.
樹脂被膜鋼板２２は、略水平に形成された平部２２Ａと、平部２２Ａの屋外側の端部から略上向きに延出された立ち上がり部２２Ｂとを含んで構成されている。さらに、樹脂被膜鋼板２２には、防水層１２の平面視における一端側の短辺に沿って、平部２２Ａから略上向きに延出された立ち上がり部２２Ｃが形成されている。樹脂被膜鋼板２２の立ち上がり部２２Ｃと樹脂被膜鋼板１４の立ち上がり部１４Ｃとは、略同一平面をなしている。 The resin-coated steel plate 22 includes a flat portion 22A formed substantially horizontally and a rising portion 22B extending substantially upward from an end portion of the flat portion 22A on the outdoor side. Further, the resin-coated steel plate 22 is formed with a rising portion 22C extending substantially upward from the flat portion 22A along the short side on one end side in the plan view of the waterproof layer 12. The rising portion 22C of the resin-coated steel sheet 22 and the rising portion 14C of the resin-coated steel plate 14 form substantially the same plane.
また、樹脂被膜鋼板２４は、略水平に形成された平部２４Ａと、平部２４Ａの屋外側の端部から略上向きに延出された立ち上がり部２４Ｂとを含んで構成されている。同様に、樹脂被膜鋼板２６は、平部２６Ａと立ち上がり部２６Ｂとを含んで構成されており、樹脂被膜鋼板２８は、平部２８Ａと立ち上がり部２８Ｂとを含んで構成されている。樹脂被膜鋼板２８にはさらに、防水層１２の平面視における他端側の短辺に沿って、平部２８Ａから略上向きに延出された立ち上がり部２８Ｃが形成されている。 Further, the resin-coated steel plate 24 includes a flat portion 24A formed substantially horizontally and a rising portion 24B extending substantially upward from the end portion of the flat portion 24A on the outdoor side. Similarly, the resin-coated steel sheet 26 is configured to include a flat portion 26A and a rising portion 26B, and the resin-coated steel plate 28 is configured to include a flat portion 28A and a rising portion 28B. Further, the resin-coated steel plate 28 is formed with a rising portion 28C extending substantially upward from the flat portion 28A along the short side on the other end side in the plan view of the waterproof layer 12.
樹脂被膜鋼板２２の立ち上がり部２２Ｃと樹脂被膜鋼板２８の立ち上がり部２８Ｃとは、互いに対向している。また、樹脂被膜鋼板２８の立ち上がり部２８Ｃと樹脂被膜鋼板２０の立ち上がり部２０Ｃとは、略同一平面をなしている。 The rising portion 22C of the resin-coated steel sheet 22 and the rising portion 28C of the resin-coated steel plate 28 face each other. Further, the rising portion 28C of the resin-coated steel sheet 28 and the rising portion 20C of the resin-coated steel sheet 20 form substantially the same plane.
なお、樹脂被膜鋼板２２、２４、２６、２８の各平部２２Ａ、２４Ａ、２６Ａ、２８Ａは、それぞれ平面視で防水層１２の長手方向に長辺を有し、短手方向に短辺を有する略矩形状の薄い板とされる。樹脂被膜鋼板２２、２４、２６、２８の短手方向の長さは略同一とされ、これらの長さは、前述した樹脂被膜鋼板１４、１６、１８、２０の短手方向の長さよりも短い。また、樹脂被膜鋼板１４、１６、１８、２０、２２、２４、２６、２８の立ち上がり部１４Ｂ、１４Ｃ、１６Ｂ、１８Ｂ、２０Ｂ、２０Ｃ、２２Ｂ、２２Ｃ、２４Ｂ、２６Ｂ、２８Ｂ、２８Ｃは、略同一の高さで形成されている。 The flat portions 22A, 24A, 26A, and 28A of the resin-coated steel sheets 22, 24, 26, and 28 each have a long side in the longitudinal direction and a short side in the lateral direction of the waterproof layer 12 in a plan view. It is a thin plate with a substantially rectangular shape. The lengths of the resin-coated steel sheets 22, 24, 26, and 28 in the lateral direction are substantially the same, and these lengths are shorter than the lengths of the resin-coated steel sheets 14, 16, 18, and 20 in the lateral direction described above. .. Further, the rising portions 14B, 14C, 16B, 18B, 20B, 20C, 22B, 22C, 24B, 26B, 28B and 28C of the resin-coated steel sheets 14, 16, 18, 20, 22, 24, 26 and 28 are substantially the same. It is formed at the height of.
＜防水シート＞
樹脂被膜鋼板１４と樹脂被膜鋼板１６とが隣接する部分（以下、樹脂被膜鋼板１４、１６、１８、２０、２２、２４、２６、２８同士が隣接する部分を適宜「つなぎ目」と称す。）には、上層側に帯状の防水シート３０が設けられている。
<Waterproof sheet>
In the portion where the resin-coated steel sheet 14 and the resin-coated steel sheet 16 are adjacent to each other (hereinafter, the portion where the resin-coated steel sheets 14, 16, 18, 20, 22, 24, 26, 28 are adjacent to each other is appropriately referred to as a "joint"). Is provided with a strip-shaped waterproof sheet 30 on the upper layer side.
樹脂被膜鋼板１４の平部１４Ａと樹脂被膜鋼板１６の平部１６Ａとは、防水シート３０の平部３０Ａによって連結されている。また、樹脂被膜鋼板１４の立ち上がり部１４Ｂと樹脂被膜鋼板１６の立ち上がり部１６Ｂとは、防水シート３０の立ち上がり部３０Ｂによって連結されている。 The flat portion 14A of the resin-coated steel plate 14 and the flat portion 16A of the resin-coated steel plate 16 are connected by the flat portion 30A of the waterproof sheet 30. Further, the rising portion 14B of the resin-coated steel plate 14 and the rising portion 16B of the resin-coated steel plate 16 are connected by the rising portion 30B of the waterproof sheet 30.
同様に、樹脂被膜鋼板１６と樹脂被膜鋼板１８とのつなぎ目及び樹脂被膜鋼板１８と樹脂被膜鋼板２０とのつなぎ目には、それぞれ上層側に防水シート３０が設けられている。これらのつなぎ目は、上記樹脂被膜鋼板１４と樹脂被膜鋼板１６とのつなぎ目における連結態様と同様に、防水シート３０の平部３０Ａ及び立ち上がり部３０Ｂによって連結されている。各防水シート３０は、防水層１２の短手方向に沿って延在されている。 Similarly, a waterproof sheet 30 is provided on the upper layer side of each of the joint between the resin-coated steel plate 16 and the resin-coated steel plate 18 and the joint between the resin-coated steel plate 18 and the resin-coated steel plate 20. These joints are connected by the flat portion 30A and the rising portion 30B of the waterproof sheet 30 in the same manner as in the connection mode at the joint between the resin-coated steel plate 14 and the resin-coated steel plate 16. Each waterproof sheet 30 extends along the lateral direction of the waterproof layer 12.
これに対して、樹脂被膜鋼板１４と樹脂被膜鋼板２２とのつなぎ目及び樹脂被膜鋼板１４と樹脂被膜鋼板２４とのつなぎ目には、長手方向に沿って延在された１枚の帯状の防水シート３２が上層側に設けられている。 On the other hand, at the joint between the resin-coated steel plate 14 and the resin-coated steel plate 22 and the joint between the resin-coated steel plate 14 and the resin-coated steel plate 24, one strip-shaped waterproof sheet 32 extending along the longitudinal direction Is provided on the upper layer side.
樹脂被膜鋼板１４の平部１４Ａ、樹脂被膜鋼板２２の平部２２Ａ及び樹脂被膜鋼板２４の平部２４Ａは、防水シート３２の平部３２Ａによって連結されている。また、樹脂被膜鋼板１４の立ち上がり部１４Ｃと樹脂被膜鋼板２２の立ち上がり部２２Ｃとは、防水シート３２の立ち上がり部３２Ｂによって連結されている。 The flat portion 14A of the resin-coated steel plate 14, the flat portion 22A of the resin-coated steel plate 22, and the flat portion 24A of the resin-coated steel plate 24 are connected by the flat portion 32A of the waterproof sheet 32. Further, the rising portion 14C of the resin-coated steel sheet 14 and the rising portion 22C of the resin-coated steel plate 22 are connected by the rising portion 32B of the waterproof sheet 32.
防水シート３２と同様に、樹脂被膜鋼板１６と樹脂被膜鋼板２４とのつなぎ目には、防水シート３４が設けられており、樹脂被膜鋼板１６の平部１６Ａと樹脂被膜鋼板２４の平部２４Ａとは、防水シート３４によって連結されている。 Similar to the waterproof sheet 32, the waterproof sheet 34 is provided at the joint between the resin-coated steel plate 16 and the resin-coated steel plate 24, and the flat portion 16A of the resin-coated steel plate 16 and the flat portion 24A of the resin-coated steel plate 24 are , Are connected by a tarpaulin 34.
また同様に、樹脂被膜鋼板１８と樹脂被膜鋼板２４とのつなぎ目及び樹脂被膜鋼板１８と樹脂被膜鋼板２６とのつなぎ目には、防水シート３６が設けられている。樹脂被膜鋼板１８の平部１８Ａ、樹脂被膜鋼板２４の平部２４Ａ及び樹脂被膜鋼板２６の平部２６Ａは、防水シート３６によって連結されている。 Similarly, a waterproof sheet 36 is provided at the joint between the resin-coated steel plate 18 and the resin-coated steel plate 24 and at the joint between the resin-coated steel plate 18 and the resin-coated steel plate 26. The flat portion 18A of the resin-coated steel plate 18, the flat portion 24A of the resin-coated steel plate 24, and the flat portion 26A of the resin-coated steel plate 26 are connected by a waterproof sheet 36.
さらに同様に、樹脂被膜鋼板２０と樹脂被膜鋼板２６とのつなぎ目及び樹脂被膜鋼板２０と樹脂被膜鋼板２８とのつなぎ目には、防水シート３８が設けられている。樹脂被膜鋼板２０の平部２０Ａ、樹脂被膜鋼板２６の平部２６Ａ、及び樹脂被膜鋼板２８の平部２８Ａは、防水シート３８の平部３８Ａによって連結されている。また、樹脂被膜鋼板２０の立ち上がり部２０Ｃと樹脂被膜鋼板２８の立ち上がり部２８Ｃとは、防水シート３８の立ち上がり部３８Ｂによって連結されている。 Similarly, a waterproof sheet 38 is provided at the joint between the resin-coated steel sheet 20 and the resin-coated steel sheet 26 and at the joint between the resin-coated steel sheet 20 and the resin-coated steel sheet 28. The flat portion 20A of the resin-coated steel sheet 20, the flat portion 26A of the resin-coated steel sheet 26, and the flat portion 28A of the resin-coated steel plate 28 are connected by the flat portion 38A of the waterproof sheet 38. Further, the rising portion 20C of the resin-coated steel sheet 20 and the rising portion 28C of the resin-coated steel plate 28 are connected by the rising portion 38B of the waterproof sheet 38.
樹脂被膜鋼板２２と樹脂被膜鋼板２４とのつなぎ目には、上層側に帯状の防水シート４０が設けられている。樹脂被膜鋼板２２の平部２２Ａと樹脂被膜鋼板２４の平部２４Ａとは、防水シート４０の平部４０Ａによって連結されている。また、樹脂被膜鋼板２２の立ち上がり部２２Ｂと樹脂被膜鋼板２４の立ち上がり部２４Ｂとは、防水シート４０の立ち上がり部４０Ｂによって連結されている。 A strip-shaped waterproof sheet 40 is provided on the upper layer side at the joint between the resin-coated steel plate 22 and the resin-coated steel plate 24. The flat portion 22A of the resin-coated steel plate 22 and the flat portion 24A of the resin-coated steel plate 24 are connected by the flat portion 40A of the waterproof sheet 40. Further, the rising portion 22B of the resin-coated steel plate 22 and the rising portion 24B of the resin-coated steel plate 24 are connected by the rising portion 40B of the waterproof sheet 40.
同様に、樹脂被膜鋼板２４と樹脂被膜鋼板２６とのつなぎ目及び樹脂被膜鋼板２６と樹脂被膜鋼板２８とのつなぎ目にも、それぞれ防水シート４０が設けられている。これらのつなぎ目は、上記樹脂被膜鋼板２２と樹脂被膜鋼板２４とのつなぎ目における連結態様と同様に、防水シート４０の平部４０Ａ及び立ち上がり部４０Ｂによって連結されている。 Similarly, the waterproof sheet 40 is also provided at the joint between the resin-coated steel plate 24 and the resin-coated steel plate 26 and at the joint between the resin-coated steel plate 26 and the resin-coated steel plate 28, respectively. These joints are connected by the flat portion 40A and the rising portion 40B of the waterproof sheet 40 in the same manner as in the connection mode at the joint between the resin-coated steel plate 22 and the resin-coated steel plate 24.
本実施形態では、防水シート３０、３２、３４、３６、３８、４０は、いずれも塩化ビニル樹脂製のシート（所謂塩ビシート）とされる。 In the present embodiment, the waterproof sheets 30, 32, 34, 36, 38, and 40 are all vinyl chloride resin sheets (so-called vinyl chloride sheets).
＜つなぎ目＞
図２には、図１で示された防水層の一部を拡大して示す拡大平面図が示されている。
<Seam>
FIG. 2 shows an enlarged plan view showing a part of the waterproof layer shown in FIG. 1 in an enlarged manner.
（樹脂被膜鋼板同士の重なり）
樹脂被膜鋼板１８の平部１８Ａは、他端側かつ屋内側の角部及び他端側かつ屋外側の角部が切り欠かれている。これにより、樹脂被膜鋼板１８の平部１８Ａには、樹脂被膜鋼板２０の平部２０Ａと隣接する側（他端側）の端部に、略矩形状の重なり片Ｐが形成されている。樹脂被膜鋼板２０の平部２０Ａにおける一端側の端部は、樹脂被膜鋼板１８の重なり片Ｐの上に重ねられている。
(Overlapping of resin-coated steel sheets)
The flat portion 18A of the resin-coated steel sheet 18 is notched at a corner portion on the other end side and the indoor side and a corner portion on the other end side and the outdoor side. As a result, the flat portion 18A of the resin-coated steel sheet 18 is formed with a substantially rectangular overlapping piece P at the end on the side (the other end side) adjacent to the flat portion 20A of the resin-coated steel plate 20. One end of the resin-coated steel sheet 20 on the flat portion 20A is overlapped on the overlapping piece P of the resin-coated steel sheet 18.
また、樹脂被膜鋼板１８の平部１８Ａの屋外側の端部には、略矩形状の重なり片Ｑが形成されている。樹脂被膜鋼板２４の平部２４Ａ及び樹脂被膜鋼板２６の平部２６Ａにおける屋内側の各端部は、樹脂被膜鋼板１８の重なり片Ｑの上に重ねられている。 Further, a substantially rectangular overlapping piece Q is formed at the outdoor end of the flat portion 18A of the resin-coated steel plate 18. Each end of the flat portion 24A of the resin-coated steel sheet 24 and the flat portion 26A of the resin-coated steel plate 26 on the indoor side is overlapped on the overlapping piece Q of the resin-coated steel plate 18.
樹脂被膜鋼板１８と同様に、樹脂被膜鋼板１６の平部１６Ａには、他端側の端部に重なり片Ｐが形成されており、屋外側の端部に重なり片Ｑが形成されている。 Similar to the resin-coated steel sheet 18, the flat portion 16A of the resin-coated steel sheet 16 has an overlapping piece P formed at the end on the other end side and an overlapping piece Q formed at the end on the outdoor side.
なお、図示されていないが、図１に示される樹脂被膜鋼板１４の平部１４Ａにも、他端側の端部に重なり片Ｐと同様の重なり片が形成されている。また、平部１４Ａの屋外側の端部にも、重なり片Ｑと同様の重なり片が形成されている。 Although not shown, the flat portion 14A of the resin-coated steel sheet 14 shown in FIG. 1 also has an overlapping piece similar to the overlapping piece P formed at the end on the other end side. Further, an overlapping piece similar to the overlapping piece Q is also formed at the outdoor end of the flat portion 14A.
上記の通り樹脂被膜鋼板１４及び樹脂被膜鋼板１６については、樹脂被膜鋼板１８と同様のため、樹脂被膜鋼板同士の重なり方についての説明を省略する。 As described above, since the resin-coated steel sheet 14 and the resin-coated steel sheet 16 are the same as the resin-coated steel sheet 18, the description of how the resin-coated steel sheets overlap each other will be omitted.
また、樹脂被膜鋼板２８の平部２８Ａは屋内側かつ他端側の角部が切り欠かれている。これにより、樹脂被膜鋼板２８の平部２８Ａには、屋内側の端部に略矩形状の重なり片Ｒが形成されている。当該重なり片Ｒは、樹脂被膜鋼板２０の平部２０Ａにおける屋外側の端部の上に重ねられている。 Further, the flat portion 28A of the resin-coated steel sheet 28 has notches at the corners on the indoor side and the other end side. As a result, the flat portion 28A of the resin-coated steel plate 28 is formed with a substantially rectangular overlapping piece R at the end portion on the indoor side. The overlapping piece R is overlapped on the outdoor side end portion of the flat portion 20A of the resin-coated steel sheet 20.
なお、図示されていないが、図１に示される樹脂被膜鋼板２２の平部２２Ａにも、屋内側の端部に重なり片Ｒと同様の図示しない重なり片が形成されている。樹脂被膜鋼板２２については、樹脂被膜鋼板２８と同様のため、樹脂被膜鋼板同士の重なり方についての説明を省略する。 Although not shown, the flat portion 22A of the resin-coated steel sheet 22 shown in FIG. 1 also has an overlapping piece (not shown) similar to the overlapping piece R formed at the end portion on the indoor side. Since the resin-coated steel sheet 22 is the same as the resin-coated steel sheet 28, the description of how the resin-coated steel sheets are overlapped with each other will be omitted.
また、図２に示されるように、樹脂被膜鋼板２４の平部２４Ａにおける屋内側の端部は、樹脂被膜鋼板１６及び樹脂被膜鋼板１８における屋外側の各端部の上に重ねられている。同様に、樹脂被膜鋼板２６の平部２６Ａにおける屋内側の端部は、樹脂被膜鋼板１８及び樹脂被膜鋼板２０における屋外側の各端部の上に重ねられている。なお、図示されていないが、樹脂被膜鋼板２４の平部２４Ａにおける屋内側の端部は、図１に示される樹脂被膜鋼板１４における屋外側の端部の上にも重ねられている。 Further, as shown in FIG. 2, the indoor end of the flat portion 24A of the resin-coated steel sheet 24 is overlapped on each of the outdoor-side ends of the resin-coated steel sheet 16 and the resin-coated steel sheet 18. Similarly, the indoor end of the flat portion 26A of the resin-coated steel sheet 26 is overlapped on each of the outdoor-side ends of the resin-coated steel sheet 18 and the resin-coated steel sheet 20. Although not shown, the indoor end of the flat portion 24A of the resin-coated steel sheet 24 is also overlapped on the outdoor-side end of the resin-coated steel sheet 14 shown in FIG.
（樹脂被膜鋼板と防水シートとの重なり）
図２に示されるように、樹脂被膜鋼板１８の重なり片Ｐと樹脂被膜鋼板２０の平部２０Ａとが重ねられた部分は、上層側に設けられた防水シート３０の平部３０Ａに覆われている。また、樹脂被膜鋼板１８の平部１８Ａと樹脂被膜鋼板２０の平部２０Ａとは、当該重ねられた部分以外では、互いに突き合わされている。このように突き合わされた部分も、上層側に設けられた防水シート３０の平部３０Ａに覆われている。
(Overlap of resin-coated steel sheet and tarpaulin)
As shown in FIG. 2, the portion where the overlapping piece P of the resin-coated steel plate 18 and the flat portion 20A of the resin-coated steel plate 20 are overlapped is covered with the flat portion 30A of the waterproof sheet 30 provided on the upper layer side. There is. Further, the flat portion 18A of the resin-coated steel sheet 18 and the flat portion 20A of the resin-coated steel sheet 20 are butted against each other except for the overlapped portion. The abutted portion is also covered with the flat portion 30A of the waterproof sheet 30 provided on the upper layer side.
さらに、図１に示される樹脂被膜鋼板１８の立ち上がり部１８Ｂと樹脂被膜鋼板２０の立ち上がり部２０Ｂとは、互いに突き合わされている。図示されていないが、当該突き合わされた部分も、上層側に設けられた防水シート３０の立ち上がり部３０Ｂに覆われている。 Further, the rising portion 18B of the resin-coated steel sheet 18 and the rising portion 20B of the resin-coated steel sheet 20 shown in FIG. 1 are butted against each other. Although not shown, the abutted portion is also covered with a rising portion 30B of the waterproof sheet 30 provided on the upper layer side.
このように、樹脂被膜鋼板１８と樹脂被膜鋼板２０とのつなぎ目は、樹脂被膜鋼板１８と樹脂被膜鋼板２０とが互いに重ねられた部分と互いに突き合わされた部分とを含んで、上層側に設けられた防水シート３０に覆われている。図１に示された防水層１２における他のつなぎ目については、上記のつなぎ目と同様の構造であるため、個々のつなぎ目についての説明は省略する。 As described above, the joint between the resin-coated steel sheet 18 and the resin-coated steel sheet 20 is provided on the upper layer side including the portion where the resin-coated steel sheet 18 and the resin-coated steel sheet 20 are overlapped with each other and the portion where the resin-coated steel sheet 20 is abutted against each other. It is covered with a waterproof sheet 30. Since the other joints in the waterproof layer 12 shown in FIG. 1 have the same structure as the above-mentioned joints, the description of each joint will be omitted.
（防水シート同士の重なり）
図２に示されるように、樹脂被膜鋼板１８の平部１８Ａと樹脂被膜鋼板２０の平部２０Ａとを連結する防水シート３０の平部３０Ａは、その屋外側の端部において、防水シート３６及び防水シート３８と重ねられている。詳細には、平部３０Ａの屋外側かつ一端側の端部の上には、防水シート３６が重ねて設けられている。一方、平部３０Ａの屋外側かつ他端側の端部は、防水シート３８の上に重ねて設けられている。
(Overlap of waterproof sheets)
As shown in FIG. 2, the flat portion 30A of the waterproof sheet 30 connecting the flat portion 18A of the resin-coated steel plate 18 and the flat portion 20A of the resin-coated steel plate 20 has the waterproof sheet 36 and the flat portion 30A on the outdoor side thereof. It is overlapped with the waterproof sheet 38. Specifically, a waterproof sheet 36 is provided on the outdoor side and one end side of the flat portion 30A. On the other hand, the outdoor side and the other end side of the flat portion 30A is provided so as to be overlapped on the waterproof sheet 38.
＜溶着部＞
（樹脂被膜鋼板と防水シートとの溶着部）
図３（Ａ）には、図２の３Ａ−３Ａ線に沿って切断した樹脂被膜鋼板２０と防水シート３０との溶着部４８における拡大断面図が示されている。
<Welding part>
(Welded part between resin coated steel plate and waterproof sheet)
FIG. 3A shows an enlarged cross-sectional view of the welded portion 48 of the resin-coated steel sheet 20 and the waterproof sheet 30 cut along the line 3A-3A of FIG.
下層側の樹脂被膜鋼板２０には、前述した平部２０Ａと立ち上がり部２０Ｂとの間に、湾曲されたコーナー部２０Ｄが形成されている。 The resin-coated steel sheet 20 on the lower layer side is formed with a curved corner portion 20D between the flat portion 20A and the rising portion 20B described above.
防水シート３０の平部３０Ａは、樹脂被膜鋼板２０の平部２０Ａに溶着されており、防水シート３０の立ち上がり部３０Ｂは、樹脂被膜鋼板２０の立ち上がり部２０Ｂに溶着されている。防水シート３０において、平部３０Ａと立ち上がり部３０Ｂとの間をコーナー部３０Ｃとすると、防水シート３０のコーナー部３０Ｃは、樹脂被膜鋼板２０のコーナー部２０Ｄに沿って溶着されている（図示しない）。換言すると、上層側に設けられた防水シート３０は、コーナー部２０Ｄを含む範囲で下層側に設けられた樹脂被膜鋼板２０に溶着されている。 The flat portion 30A of the waterproof sheet 30 is welded to the flat portion 20A of the resin-coated steel sheet 20, and the rising portion 30B of the waterproof sheet 30 is welded to the rising portion 20B of the resin-coated steel plate 20. Assuming that the corner portion 30C is between the flat portion 30A and the rising portion 30B in the waterproof sheet 30, the corner portion 30C of the waterproof sheet 30 is welded along the corner portion 20D of the resin-coated steel plate 20 (not shown). .. In other words, the waterproof sheet 30 provided on the upper layer side is welded to the resin-coated steel plate 20 provided on the lower layer side in a range including the corner portion 20D.
ここで、下層側の樹脂被膜鋼板２０は、めっき鋼板２１と、該めっき鋼板２１の表側の面に設けられた塩化ビニル樹脂製の樹脂層２３とを含んで構成されている。防水シート３０は、樹脂被膜鋼板２０の樹脂層２３に溶着されている。 Here, the resin-coated steel sheet 20 on the lower layer side includes a plated steel sheet 21 and a resin layer 23 made of vinyl chloride resin provided on the front surface of the plated steel sheet 21. The waterproof sheet 30 is welded to the resin layer 23 of the resin-coated steel sheet 20.
図３（Ａ）に示されるように、樹脂被膜鋼板２０の平部２０Ａと防水シート３０の平部３０Ａとの溶着部４８Ａには、該平部２０Ａと該平部３０Ａとの間に、空気だまり５０が形成されている。 As shown in FIG. 3A, the welded portion 48A between the flat portion 20A of the resin-coated steel plate 20 and the flat portion 30A of the waterproof sheet 30 has air between the flat portion 20A and the flat portion 30A. A tarpaulin 50 is formed.
同様に、樹脂被膜鋼板２０の立ち上がり部２０Ｂと防水シート３０の立ち上がり部３０Ｂとの溶着部４８Ｂには、空気だまり５２が形成されている。さらに、樹脂被膜鋼板２０のコーナー部２０Ｄと防水シート３０のコーナー部３０Ｃとの溶着部４８Ｃには、空気だまり５４が形成されている。 Similarly, an air pool 52 is formed in the welded portion 48B between the rising portion 20B of the resin-coated steel plate 20 and the rising portion 30B of the waterproof sheet 30. Further, an air pool 54 is formed in the welded portion 48C between the corner portion 20D of the resin-coated steel sheet 20 and the corner portion 30C of the waterproof sheet 30.
なお、本実施形態では説明の便宜上、溶着部４８に３つの空気だまり５０、５２、５４が形成されているものとして説明したが、空気だまりの数はこれに限らず、例えば溶着部に１つも空気だまりが形成されていなくてもよい。 In the present embodiment, for convenience of explanation, it has been described that three air pools 50, 52, and 54 are formed in the welded portion 48, but the number of air pools is not limited to this, and for example, one in the welded portion. The air pool does not have to be formed.
（防水シート同士の溶着部）
図３（Ｂ）には、図２の３Ｂ−３Ｂ線に沿って切断した防水シート３０の平部３０Ａと防水シート３６との溶着部４９における拡大断面図が示されている。
(Welding part between waterproof sheets)
FIG. 3B shows an enlarged cross-sectional view of the welded portion 49 between the flat portion 30A of the waterproof sheet 30 and the waterproof sheet 36 cut along the line 3B-3B of FIG.
下層側の樹脂被膜鋼板２６は、めっき鋼板２７と、該めっき鋼板２７の表側の面に設けられた塩化ビニル樹脂製の樹脂層２９とを含んで構成されている。 The resin-coated steel sheet 26 on the lower layer side includes a plated steel sheet 27 and a resin layer 29 made of vinyl chloride resin provided on the front surface of the plated steel sheet 27.
防水シート３０の平部３０Ａは、下層側に設けられた樹脂被膜鋼板２６の樹脂層２９に溶着されている。なお、溶着部４８、４９に限らず、図１に示される防水層１２の他の溶着部において、上層側に設けられた防水シート３０、３２、３４、３６、３８、４０は、それぞれ下層側に設けられた樹脂被膜鋼板１４、１６、１８、２０、２２、２４、２６、２８のいずれかの樹脂層に溶着されている（図示しない）。 The flat portion 30A of the waterproof sheet 30 is welded to the resin layer 29 of the resin-coated steel plate 26 provided on the lower layer side. Not limited to the welded portions 48 and 49, in the other welded portions of the waterproof layer 12 shown in FIG. 1, the waterproof sheets 30, 32, 34, 36, 38 and 40 provided on the upper layer side are on the lower layer side, respectively. It is welded to any of the resin layers 14, 16, 18, 20, 22, 24, 26, and 28 provided in (not shown).
図３（Ｂ）に示されるように、樹脂被膜鋼板２６に溶着された防水シート３０のさらに上層側には、防水シート３６が溶着されている。ここで、図３（Ｂ）に示されるように、溶着部４９において、防水シート３０の平部３０Ａと防水シート３６との間には、空気だまり５４が形成されている。なお、溶着部４９に限らず、図１に示される防水層１２において、防水シート同士が重なる部分では、上層側に設けられた防水シートは、それぞれ下層側に設けられた防水シートに溶着されている。 As shown in FIG. 3B, the waterproof sheet 36 is welded to the upper layer side of the waterproof sheet 30 welded to the resin-coated steel plate 26. Here, as shown in FIG. 3 (B), in the welded portion 49, an air pool 54 is formed between the flat portion 30A of the waterproof sheet 30 and the waterproof sheet 36. In the waterproof layer 12 shown in FIG. 1, not limited to the welded portion 49, in the portion where the waterproof sheets overlap each other, the waterproof sheets provided on the upper layer side are welded to the waterproof sheets provided on the lower layer side, respectively. There is.
（本実施形態の作用・効果）
次に、溶着部の検査方法について説明し、その説明を通して本実施形態の作用及び効果について説明する。
(Action / effect of this embodiment)
Next, a method for inspecting the welded portion will be described, and the operation and effect of the present embodiment will be described through the description.
＜溶着部の検査方法＞
本実施形態では、一例として、図３（Ａ）に示された溶着部４８Ａ及び溶着部４８Ｃの検査方法について説明する。上層側の防水シート３０は、設定温度を調節可能な熱風ガン１００（図４参照）を用いた熱風溶着によって、下層側の樹脂被膜鋼板２０に溶着されたものとする。なお、以下の説明において、熱風ガン１００の設定温度等の条件は一例であり、これらの条件に限定されず、加熱対象の材質や厚さ等に応じて適宜変更される。
<Inspection method for welded parts>
In this embodiment, as an example, an inspection method of the welded portion 48A and the welded portion 48C shown in FIG. 3A will be described. It is assumed that the waterproof sheet 30 on the upper layer side is welded to the resin-coated steel plate 20 on the lower layer side by hot air welding using a hot air gun 100 (see FIG. 4) whose set temperature can be adjusted. In the following description, the conditions such as the set temperature of the hot air gun 100 are examples, and are not limited to these conditions, and are appropriately changed according to the material and thickness of the heating target.
ここでは、作業員が熱風ガン１００の設定温度を４２０℃に設定して、熱風ガン１００の先端を、溶着面から５ｍｍ〜１ｃｍ程度離して、これを秒速２ｃｍ〜３ｃｍ程度の速度で水平移動しながら、溶着部４８Ａ、４８Ｃを溶着したものとする。 Here, the worker sets the set temperature of the hot air gun 100 to 420 ° C., separates the tip of the hot air gun 100 from the welding surface by about 5 mm to 1 cm, and moves it horizontally at a speed of about 2 cm to 3 cm per second. However, it is assumed that the welded portions 48A and 48C are welded.
（加熱工程）
図４及び図５に示されるように、まず、熱風ガン１００を用いて上層側から溶着部４８Ａ、４８Ｃを加熱する。検査員は、溶着時に使用した熱風ガン１００の設定温度を４００℃に下げて、この先端を防水シート３０の表側の面から３ｃｍ程度離して、これを秒速２ｃｍ〜３ｃｍ程度の速度で水平移動させながら、溶着部４８Ａ、４８Ｃを加熱するものとする。当該条件は、下層側の樹脂被膜鋼板２０の樹脂層２３及び上層側の防水シート３０が溶融しない範囲とされる。なお、検査員は作業員と同一人物であってもよい。
(Heating process)
As shown in FIGS. 4 and 5, first, the welded portions 48A and 48C are heated from the upper layer side using the hot air gun 100. The inspector lowered the set temperature of the hot air gun 100 used at the time of welding to 400 ° C., separated the tip of the hot air gun 100 from the front surface of the waterproof sheet 30 by about 3 cm, and moved it horizontally at a speed of about 2 cm to 3 cm per second. However, it is assumed that the welded portions 48A and 48C are heated. The condition is such that the resin layer 23 of the resin-coated steel sheet 20 on the lower layer side and the waterproof sheet 30 on the upper layer side do not melt. The inspector may be the same person as the worker.
図４（Ａ）には、加熱前における防水シート３０の平部３０Ａの状態が実線で表されており、加熱後における該平部３０Ａの状態が二点鎖線で表されている。熱風ガン１００からの熱風によって、溶着部４８Ａに形成された空気だまり５０の空気が加熱される。このとき、空気だまり５０の空気が膨張し、未溶着部の内圧が高まる。これにより、上層側に設けられた防水シート３０の平部３０Ａのうち、未溶着部の上層側を構成する部分が押し上げられて***部６０が形成される。 In FIG. 4A, the state of the flat portion 30A of the waterproof sheet 30 before heating is represented by a solid line, and the state of the flat portion 30A after heating is represented by a two-dot chain line. The hot air from the hot air gun 100 heats the air in the air pool 50 formed in the welded portion 48A. At this time, the air in the air pool 50 expands, and the internal pressure of the unwelded portion increases. As a result, of the flat portion 30A of the waterproof sheet 30 provided on the upper layer side, the portion constituting the upper layer side of the unwelded portion is pushed up to form the raised portion 60.
（判定工程）
このように、上記加熱工程で溶着部４８Ａを加熱することによって、上層側に設けられた防水シート３０における平部３０Ａの一部が加熱前の状態よりも***された場合に、当該***された部分（***部６０）を未溶着部として判定する。
(Judgment process)
In this way, by heating the welded portion 48A in the heating step, when a part of the flat portion 30A of the waterproof sheet 30 provided on the upper layer side is raised from the state before heating, the raised portion is raised. The portion (raised portion 60) is determined as an unwelded portion.
これに対して、図４（Ｂ）に示されるように、防水シート３０の平部３０Ａのうち、正規溶着部の上層側を構成する部分は、加熱しても***されない。よって、加熱しても***されなかった部分については、空気だまりのない正規溶着部であるとみなす。 On the other hand, as shown in FIG. 4B, the portion of the flat portion 30A of the waterproof sheet 30 that constitutes the upper layer side of the normal welding portion is not raised even when heated. Therefore, the part that is not raised even after heating is regarded as a normal welded part without air pool.
同様に、図５（Ａ）には、加熱前における防水シート３０のコーナー部３０Ｃの状態が実線で表されており、加熱後における該コーナー部３０Ｃの状態が二点鎖線で表されている。加熱によって溶着部４８Ｃに形成された空気だまり５４の空気が膨張し、***部６４が形成される。このように、加熱によってコーナー部３０Ｃに形成された***部６４を未溶着部として判定する。 Similarly, in FIG. 5A, the state of the corner portion 30C of the waterproof sheet 30 before heating is represented by a solid line, and the state of the corner portion 30C after heating is represented by a two-dot chain line. The air in the air pool 54 formed in the welded portion 48C expands by heating, and the raised portion 64 is formed. In this way, the raised portion 64 formed in the corner portion 30C by heating is determined as an unwelded portion.
一方で、図５（Ｂ）に示されるように、コーナー部３０Ｃにおいても平部３０Ａ（図４Ｂ参照）と同様に、正規溶着部の上層側を構成する部分は***されないため、当該部分については正規溶着部であるとみなす。 On the other hand, as shown in FIG. 5B, even in the corner portion 30C, as in the flat portion 30A (see FIG. 4B), the portion forming the upper layer side of the normal welding portion is not raised, so that the portion is not raised. Considered to be a regular weld.
図４に示される溶着部４８Ａ及び図５に示される溶着部４８Ｃにおいて、防水シート３０の一部が***されたか否かについては、上層側から防水シート３０を目視して又はこれに触れて判定する。 Whether or not a part of the waterproof sheet 30 is raised in the welded portion 48A shown in FIG. 4 and the welded portion 48C shown in FIG. 5 is determined by visually observing or touching the waterproof sheet 30 from the upper layer side. To do.
なお、本実施形態では溶着部４８Ａ及び溶着部４８Ｃの検査方法について説明したが、これに限らず、他の溶着部にも本発明に係る検査方法を適用してもよい。例えば、図３（Ａ）に示された立ち上がり部２０Ｂと立ち上がり部３０Ｂとの溶着部４８Ｂに本発明に係る検査方法を適用してもよく、図３（Ｂ）に示された防水シート３０と防水シート３６との溶着部４９にこれを適用してもよい。 In the present embodiment, the inspection method of the welded portion 48A and the welded portion 48C has been described, but the present invention is not limited to this, and the inspection method according to the present invention may be applied to other welded portions. For example, the inspection method according to the present invention may be applied to the welded portion 48B between the rising portion 20B and the rising portion 30B shown in FIG. 3 (A), and the waterproof sheet 30 shown in FIG. 3 (B). This may be applied to the welded portion 49 with the waterproof sheet 36.
以上説明したように、本実施形態に係る検査方法によれば、平部２０Ａと平部３０Ａとの溶着部４８Ａ及びコーナー部２０Ｄとコーナー部３０Ｃとの溶着部４８Ｃにおいて、未溶着部を特定できる。 As described above, according to the inspection method according to the present embodiment, the unwelded portion can be identified in the welded portion 48A between the flat portion 20A and the flat portion 30A and the welded portion 48C between the corner portion 20D and the corner portion 30C. ..
また、未溶着部を特定することで、当該部分の補修が可能となるため、補修によって必要な溶着幅を確保することができる。一方、溶着部４８Ａ、４８Ｃを加熱しても***部６０、６４が形成されない場合には、溶着部４８Ａ、４８Ｃの全範囲が溶着されていることを確認できる。この結果、防水層において高い防水性及び耐久性を確保できる。 Further, by specifying the unwelded portion, it is possible to repair the portion, so that the required welding width can be secured by the repair. On the other hand, if the raised portions 60 and 64 are not formed even when the welded portions 48A and 48C are heated, it can be confirmed that the entire range of the welded portions 48A and 48C is welded. As a result, high waterproofness and durability can be ensured in the waterproof layer.
さらにまた、本実施形態に係る検査方法によれば、熱風溶着時に使用した熱風ガン１００を用いて、熱風溶着後の溶着部４８Ａ及び溶着部４８Ｃが加熱される。したがって、溶着時に使用した機材を用いて、効率よく簡便に溶着部の溶着状態を検査できる。 Furthermore, according to the inspection method according to the present embodiment, the welded portion 48A and the welded portion 48C after the hot air welding are heated by using the hot air gun 100 used at the time of hot air welding. Therefore, the welded state of the welded portion can be inspected efficiently and easily by using the equipment used at the time of welding.
また、本実施形態に係る溶着部の検査方法によれば、住宅のバルコニー１０に設けられた防水層１２において、空気だまり５０及び空気だまり５４が形成された未溶着部を特定することができる。このため、雨水にさらされるバルコニー１０において高い防水性及び耐久性を確保し、住宅を漏水から守ることができる。 Further, according to the method for inspecting the welded portion according to the present embodiment, it is possible to identify the unwelded portion in which the air pool 50 and the air pool 54 are formed in the waterproof layer 12 provided on the balcony 10 of the house. Therefore, the balcony 10 exposed to rainwater can ensure high waterproofness and durability, and can protect the house from water leakage.
さらに、本実施形態に係る溶着部の検査方法によれば、上層側に設けられた防水シートが小さい場合やその全範囲にわたって溶着されている場合でも、溶着部の溶着状態を検査することができる。また、正規溶着部を引きはがす方向に力をかけることなく、溶着部の溶着状態を検査することができる。 Further, according to the method for inspecting the welded portion according to the present embodiment, the welded state of the welded portion can be inspected even when the waterproof sheet provided on the upper layer side is small or welded over the entire range. .. In addition, the welded state of the welded portion can be inspected without applying force in the direction of peeling off the regular welded portion.
（第２実施形態）
以下、図６を用いて、第２実施形態に係る溶着部の検査方法について説明する。なお、前述した第１実施形態と同一の部分については、同一の符号を付してその説明を省略する。
(Second Embodiment)
Hereinafter, a method for inspecting the welded portion according to the second embodiment will be described with reference to FIG. The same parts as those in the first embodiment described above are designated by the same reference numerals, and the description thereof will be omitted.
本実施形態では、図６（Ａ）に示されるように、溶着部４８Ａに複数の空気だまり５０が形成されているものとして説明する。図６（Ｂ）には、図６（Ａ）の６Ｂ−６Ｂ線に沿って切断した断面を拡大して示す溶着部４８Ａの拡大断面図が示されている。 In the present embodiment, as shown in FIG. 6A, a plurality of air pools 50 are formed in the welded portion 48A. FIG. 6B shows an enlarged cross-sectional view of the welded portion 48A showing an enlarged cross section cut along the line 6B-6B of FIG. 6A.
図６（Ａ）及び図６（Ｂ）に示されるように、加熱工程の前工程として、溶着部４８Ａにおいて上層側に設けられた防水シート３０の平部３０Ａの上に、アルミニウム合金製の薄板７０（以下、適宜「アルミ板７０」と称す。）を置く。 As shown in FIGS. 6 (A) and 6 (B), as a pre-process of the heating step, a thin plate made of aluminum alloy is placed on the flat portion 30A of the waterproof sheet 30 provided on the upper layer side of the welded portion 48A. 70 (hereinafter, appropriately referred to as "aluminum plate 70") is placed.
アルミ板７０は、溶着部４８Ａにおいて上記の複数の空気だまり５０を含む範囲で防水シート３０の平部３０Ａの上に置かれる。なお、本実施形態では、説明の便宜上、溶着部４８Ａに複数の空気だまり５０が形成されているものとして説明するが、これに限らず、溶着部に１つだけ空気だまりが形成されていてもよく、溶着部に空気だまりが形成されていなくてもよい。 The aluminum plate 70 is placed on the flat portion 30A of the waterproof sheet 30 in the welded portion 48A within the range including the plurality of air pools 50 described above. In the present embodiment, for convenience of explanation, it is assumed that a plurality of air pools 50 are formed in the welded portion 48A, but the present invention is not limited to this, and even if only one air pool is formed in the welded portion. Often, no air pool may be formed in the welded portion.
加熱工程では、防水シート３０の上に置いたアルミ板７０へ熱風ガン１００の熱風を当てて、下層側の樹脂被膜鋼板２０及び上層側の防水シート３０が溶融しない範囲で、アルミ板７０を介して溶着部４８Ａを加熱する。 In the heating step, the hot air of the hot air gun 100 is applied to the aluminum plate 70 placed on the waterproof sheet 30, and the resin-coated steel plate 20 on the lower layer side and the waterproof sheet 30 on the upper layer side are not melted through the aluminum plate 70. The welded portion 48A is heated.
続いて判定工程では、図示されていないが、アルミ板７０を撤去した後に、防水シート３０の平部３０Ａのうち、アルミ板７０が置かれていた部分において、加熱前の状態よりも***された部分を未溶着部として判定する。 Subsequently, in the determination step, although not shown, after the aluminum plate 70 was removed, the portion of the flat portion 30A of the waterproof sheet 30 on which the aluminum plate 70 was placed was raised from the state before heating. The portion is determined as an unwelded portion.
（本実施形態の作用・効果）
次に、本実施形態の作用及び効果を説明する。
(Action / effect of this embodiment)
Next, the operation and effect of this embodiment will be described.
本実施形態に係る溶着部の検査方法によれば、熱伝導率の高いアルミ板７０において熱が拡散され、アルミ板７０全体が略均等に加熱される。 According to the method for inspecting the welded portion according to the present embodiment, heat is diffused in the aluminum plate 70 having high thermal conductivity, and the entire aluminum plate 70 is heated substantially evenly.
また、アルミ板７０からの伝熱によって、アルミ板７０と接する上層側の防水シート３０の平部３０Ａが加熱される。このとき、溶着部４８Ａにおけるアルミ板７０と接する範囲が一度に加熱される。 Further, the heat transfer from the aluminum plate 70 heats the flat portion 30A of the waterproof sheet 30 on the upper layer side in contact with the aluminum plate 70. At this time, the area of the welded portion 48A in contact with the aluminum plate 70 is heated at once.
本実施形態で説明したように溶着部４８Ａに複数の空気だまり５０が形成されている場合には、上層側の防水シート３０の平部３０Ａのうち、未溶着部の上層側を構成する複数の部分が一度に***される。 When a plurality of air pools 50 are formed in the welded portion 48A as described in the present embodiment, a plurality of flat portions 30A of the waterproof sheet 30 on the upper layer side constituting the upper layer side of the unwelded portion. The parts are raised at once.
したがって、本実施形態に係る溶着部の検査方法によれば、溶着部４８Ａの広い範囲を効率よく検査できる。なお、溶着部に１つだけ空気だまりが形成されている場合や溶着部に空気だまりが形成されていない場合であっても、溶着部の広い範囲を効率よく検査できる。 Therefore, according to the method for inspecting the welded portion according to the present embodiment, a wide range of the welded portion 48A can be efficiently inspected. Even when only one air pool is formed in the welded portion or when no air pool is formed in the welded portion, a wide range of the welded portion can be efficiently inspected.
さらに、本実施形態に係る溶着部の検査方法によれば、アルミ板７０の全体が略均等に加熱されるため、防水シート３０において一部に熱が集中するのを抑制することができる。よって、防水シート３０の一部に熱が集中した場合に当該部分に不要な光沢や焦げが生じるのを抑制することができる。また、アルミ板７０の全体が略均等に加熱されるため、加熱ムラが生じにくく、検査の質が検査員の習熟度に左右されにくい。 Further, according to the method for inspecting the welded portion according to the present embodiment, since the entire aluminum plate 70 is heated substantially evenly, it is possible to prevent the heat from concentrating on a part of the waterproof sheet 30. Therefore, when heat is concentrated on a part of the waterproof sheet 30, it is possible to prevent unnecessary gloss and charring from occurring in the part. Further, since the entire aluminum plate 70 is heated substantially evenly, uneven heating is less likely to occur, and the quality of inspection is less likely to be affected by the proficiency level of the inspector.
ここで、図６（Ｂ）に示されるように、溶着部４８Ａに空気だまり５０が存在する場合、防水シート３０の平部３０Ａのうち空気だまり５０が形成されている部分（未溶着部）は、加熱前の状態でも、正規溶着部よりもわずかに***している。このため、未溶着部は、正規溶着部よりもアルミ板７０に密着している。これにより、アルミ板７０から未溶着部に熱が伝わりやすく、未溶着部の上層側を構成する部分が効率よく***される。このことから、正規溶着部が必要以上に加熱されるのを抑制できる。 Here, as shown in FIG. 6B, when the air pool 50 is present in the welded portion 48A, the portion (unwelded portion) in which the air pool 50 is formed in the flat portion 30A of the waterproof sheet 30 is Even in the state before heating, it is slightly raised from the normal welded part. Therefore, the unwelded portion is in closer contact with the aluminum plate 70 than the regular welded portion. As a result, heat is easily transferred from the aluminum plate 70 to the unwelded portion, and the portion forming the upper layer side of the unwelded portion is efficiently raised. From this, it is possible to prevent the normal welded portion from being heated more than necessary.
〔上記各実施形態の補足説明〕
なお、上記各実施形態に係る検査方法は、住宅のバルコニー１０における防水層１２に適用されるとしたが、これに限らず、本発明に係る検査方法は、建物に設けられた他の防水層に適用されてもよい。例えば、本発明に係る検査方法は、ビルに設けられた防水層に適用されてもよいし、ベランダ、屋上、テラス、屋根、プール等に設けられた防水層に適用されてもよい。
[Supplementary explanation of each of the above embodiments]
The inspection method according to each of the above embodiments is applied to the waterproof layer 12 on the balcony 10 of the house, but the inspection method according to the present invention is not limited to this, and the inspection method according to the present invention is another waterproof layer provided in the building. May be applied to. For example, the inspection method according to the present invention may be applied to a waterproof layer provided in a building, or may be applied to a waterproof layer provided in a balcony, a rooftop, a terrace, a roof, a pool, or the like.
また、上記各実施形態では、８つの樹脂被膜鋼板を含んで構成された防水層１２について説明したが、これに限らない。例えば、樹脂被膜鋼板を用いずに防水層１２が形成されていてもよい。すなわち、複数の防水シートがバルコニーに敷設され、これらの端部同士が重ね合わさることで防水層１２が形成されていてもよい。 Further, in each of the above embodiments, the waterproof layer 12 including the eight resin-coated steel sheets has been described, but the present invention is not limited to this. For example, the waterproof layer 12 may be formed without using the resin-coated steel sheet. That is, a plurality of waterproof sheets may be laid on the balcony, and the waterproof layer 12 may be formed by overlapping the ends thereof.
また、上記各実施形態では、熱風ガン１００を用いて熱風溶着された溶着部を検査する方法について説明したが、これに限らない。例えば、溶着剤を用いて溶着された溶着部に対して、本発明に係る検査方法を適用してもよい。さらに、上記各実施形態では、熱風ガン１００を用いて検査する方法について説明したが、これに限らず、樹脂被膜鋼板及び防水シートが溶融しない範囲で溶着部を加熱する方法であれば、他の方法を用いて検査してもよい。例えば、熱風ガン１００以外の機材を用いて溶着部を加熱してもよい。 Further, in each of the above embodiments, the method of inspecting the welded portion welded by hot air using the hot air gun 100 has been described, but the present invention is not limited to this. For example, the inspection method according to the present invention may be applied to a welded portion welded by using a welding agent. Further, in each of the above embodiments, the method of inspecting using the hot air gun 100 has been described, but the method is not limited to this, as long as it is a method of heating the welded portion within a range in which the resin-coated steel plate and the waterproof sheet do not melt. It may be inspected using a method. For example, the welded portion may be heated using equipment other than the hot air gun 100.
さらに、上記各実施形態では、熱風ガン１００の設定温度を、溶着時よりも下げて検査を行う検査方法について説明したが、これに限らない。例えば、風量を調節可能な熱風ガンを用いて、溶着時よりも当該熱風ガンの風量を下げて検査を行ってもよい。また、設定温度及び風量の両方を調節可能な熱風ガンを用いて、溶着時よりも当該熱風ガンの設定温度及び風量を下げて検査を行ってもよい。さらに、検査時における熱風ガンの設定温度及び風量を、溶着時における熱風ガンの設定温度及び風量と同一にしたまま検査を行ってもよい。この場合、熱風ガンの吹き出し口と上層側の防水シートとの距離を溶着時より離すか、又は熱風ガンを水平移動させる速度を溶着時よりも速くすればよい。 Further, in each of the above embodiments, the inspection method in which the set temperature of the hot air gun 100 is lowered from that at the time of welding has been described, but the present invention is not limited to this. For example, using a hot air gun whose air volume can be adjusted, the air volume of the hot air gun may be lower than that at the time of welding for inspection. Further, using a hot air gun capable of adjusting both the set temperature and the air volume, the inspection may be performed at a lower set temperature and air volume of the hot air gun than at the time of welding. Further, the inspection may be performed while keeping the set temperature and air volume of the hot air gun at the time of inspection the same as the set temperature and air volume of the hot air gun at the time of welding. In this case, the distance between the outlet of the hot air gun and the waterproof sheet on the upper layer side may be separated from that at the time of welding, or the speed at which the hot air gun is moved horizontally may be made faster than at the time of welding.
また、上記各実施形態では、溶着部４８Ａ及び溶着部４８Ｃを加熱し、当該部分について判定を行う検査方法について説明したが、これに限らず、本発明に係る検査方法は、防水層において溶着作業が行われた部分（溶着部）に広く適用できる。例えば、溶着部４８Ｂ、４９を含む防水層１２における他の溶着部に対して、本発明に係る検査方法を適用してもよい。また、本実施形態では、樹脂被膜鋼板が重ねられていない部分の上に防水シートが設けられた溶着部４８Ａ、４８Ｃ、４９について説明したが、これに限らず、樹脂被膜鋼板同士が重ねられた部分の上に防水シートが溶着された溶着部に、本発明に係る検査方法を適用してもよい。 Further, in each of the above embodiments, an inspection method in which the welded portion 48A and the welded portion 48C are heated to determine the welded portion 48C has been described, but the inspection method according to the present invention is not limited to this, and the inspection method according to the present invention is a welding operation in the waterproof layer. It can be widely applied to the part (welded part) where For example, the inspection method according to the present invention may be applied to other welded portions in the waterproof layer 12 including the welded portions 48B and 49. Further, in the present embodiment, the welded portions 48A, 48C, 49 in which the waterproof sheet is provided on the portion where the resin-coated steel sheets are not overlapped have been described, but the present invention is not limited to this, and the resin-coated steel sheets are overlapped with each other. The inspection method according to the present invention may be applied to a welded portion in which a waterproof sheet is welded on the portion.
上記第２実施形態では、アルミ板７０を用いる方法について説明したが、これに限らず、他の金属製の薄板を用いてもよい。 In the second embodiment, the method of using the aluminum plate 70 has been described, but the present invention is not limited to this, and other thin metal plates may be used.
また、上記第２実施形態では、熱風ガン１００を用いてアルミ板７０を加熱する方法について説明したが、これに限らず、他の方法で金属製の薄板を加熱してもよい。例えば、誘導加熱によって薄板を加熱してもよい。 Further, in the second embodiment, the method of heating the aluminum plate 70 using the hot air gun 100 has been described, but the present invention is not limited to this, and the thin metal plate may be heated by another method. For example, the thin plate may be heated by induction heating.
１０ バルコニー
１２ 防水層
１４、１６、１８、２０、２２、２４、２６、２８ 樹脂被膜鋼板
１４Ａ、１６Ａ、１８Ａ、２０Ａ、２２Ａ、２４Ａ、２６Ａ、２８Ａ 平部
１４Ｂ、１６Ｂ、１８Ｂ、２０Ｂ、２２Ｂ、２４Ｂ、２６Ｂ、２８Ｂ 立ち上がり部
１４Ｃ、２０Ｃ、２２Ｃ、２８Ｃ 立ち上がり部
２０Ｄ コーナー部
３０、３２、３４、３６、３８、４０ 防水シート
４８、４９ 溶着部
６０、６４ ***部（***された部分）
７０ アルミ板（金属製の薄板）
１００ 熱風ガン
10 Balcony 12 Waterproof layer 14, 16, 18, 20, 22, 24, 26, 28 Resin coated steel plate 14A, 16A, 18A, 20A, 22A, 24A, 26A, 28A Flat part 14B, 16B, 18B, 20B, 22B, 24B, 26B, 28B Rising part 14C, 20C, 22C, 28C Rising part 20D Corner part 30, 32, 34, 36, 38, 40 Waterproof sheet 48, 49 Welding part 60, 64 Raised part (raised part)
70 Aluminum plate (thin metal plate)
100 hot air gun
Claims (5)
前記溶着部において加熱前の状態よりも***された部分を未溶着部として判定する工程と、
を有する溶着部の検査方法。 In the waterproof layer provided in the building, the welded portion between the resin-coated steel plate or the resin-made waterproof sheet provided on the lower layer side and the resin-made waterproof sheet provided on the upper layer side is formed by forming the resin-coated steel plate on the lower layer side. A step of heating from the upper layer side within a range where the lower layer side waterproof sheet and the upper layer side waterproof sheet do not melt.
A step of determining a portion of the welded portion that is raised from the state before heating as an unwelded portion, and
A method for inspecting a welded portion having.
前記防水層は、当該住宅のバルコニー又はベランダに設けられている請求項１〜請求項４のいずれか１項に記載の溶着部の検査方法。 The building is considered a residence
The method for inspecting a welded portion according to any one of claims 1 to 4, wherein the waterproof layer is provided on the balcony or veranda of the house.