JP2020503176A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2020503176A5 JP2020503176A5 JP2019534156A JP2019534156A JP2020503176A5 JP 2020503176 A5 JP2020503176 A5 JP 2020503176A5 JP 2019534156 A JP2019534156 A JP 2019534156A JP 2019534156 A JP2019534156 A JP 2019534156A JP 2020503176 A5 JP2020503176 A5 JP 2020503176A5
- Authority
- JP
- Japan
- Prior art keywords
- component
- phenol
- weight
- hydrocarbon group
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000005011 phenolic resin Substances 0.000 claims 16
- 125000001931 aliphatic group Chemical group 0.000 claims 13
- 125000001183 hydrocarbyl group Chemical group 0.000 claims 12
- 229920005862 polyol Polymers 0.000 claims 12
- 150000003077 polyols Chemical class 0.000 claims 12
- ISWSIDIOOBJBQZ-UHFFFAOYSA-N phenol Chemical compound OC1=CC=CC=C1 ISWSIDIOOBJBQZ-UHFFFAOYSA-N 0.000 claims 11
- 229920001568 phenolic resin Polymers 0.000 claims 10
- 239000000178 monomer Substances 0.000 claims 9
- IQPQWNKOIGAROB-UHFFFAOYSA-N [N-]=C=O Chemical compound [N-]=C=O IQPQWNKOIGAROB-UHFFFAOYSA-N 0.000 claims 8
- 239000002904 solvent Substances 0.000 claims 8
- 150000002989 phenols Chemical group 0.000 claims 7
- MHDVGSVTJDSBDK-UHFFFAOYSA-N dibenzyl ether Chemical compound C=1C=CC=CC=1COCC1=CC=CC=C1 MHDVGSVTJDSBDK-UHFFFAOYSA-N 0.000 claims 6
- 239000000203 mixture Substances 0.000 claims 6
- 239000012454 non-polar solvent Substances 0.000 claims 6
- 125000000217 alkyl group Chemical group 0.000 claims 5
- 238000000465 moulding Methods 0.000 claims 5
- 125000001797 benzyl group Chemical group [H]C1=C([H])C([H])=C(C([H])=C1[H])C([H])([H])* 0.000 claims 3
- 239000000463 material Substances 0.000 claims 3
- JOLVYUIAMRUBRK-UTOQUPLUSA-N 3-[(8Z,11Z)-pentadeca-8,11,14-trienyl]phenol Chemical compound OC1=CC=CC(CCCCCCC\C=C/C\C=C/CC=C)=C1 JOLVYUIAMRUBRK-UTOQUPLUSA-N 0.000 claims 2
- KVVSCMOUFCNCGX-UHFFFAOYSA-N Adipostatin A Chemical group CCCCCCCCCCCCCCCC1=CC(O)=CC(O)=C1 KVVSCMOUFCNCGX-UHFFFAOYSA-N 0.000 claims 2
- KWKXNDCHNDYVRT-UHFFFAOYSA-N Dodecylbenzene Chemical group CCCCCCCCCCCCC1=CC=CC=C1 KWKXNDCHNDYVRT-UHFFFAOYSA-N 0.000 claims 2
- 125000003118 aryl group Chemical group 0.000 claims 2
- 150000001896 cresols Chemical class 0.000 claims 2
- 150000001990 dicarboxylic acid derivatives Chemical class 0.000 claims 2
- 150000002513 isocyanates Chemical class 0.000 claims 2
- DNIAPMSPPWPWGF-UHFFFAOYSA-N propylene glycol Chemical compound CC(O)CO DNIAPMSPPWPWGF-UHFFFAOYSA-N 0.000 claims 2
- CQRYARSYNCAZFO-UHFFFAOYSA-N salicyl alcohol Chemical compound OCC1=CC=CC=C1O CQRYARSYNCAZFO-UHFFFAOYSA-N 0.000 claims 2
- FYGHSUNMUKGBRK-UHFFFAOYSA-N 1,2,3-Trimethylbenzene Chemical compound CC1=CC=CC(C)=C1C FYGHSUNMUKGBRK-UHFFFAOYSA-N 0.000 claims 1
- 239000004215 Carbon black (E152) Substances 0.000 claims 1
- 229940095070 TETRAPROPYL ORTHOSILICATE Drugs 0.000 claims 1
- BOTDANWDWHJENH-UHFFFAOYSA-N Tetraethyl orthosilicate Chemical group CCO[Si](OCC)(OCC)OCC BOTDANWDWHJENH-UHFFFAOYSA-N 0.000 claims 1
- 150000001335 aliphatic alkanes Chemical class 0.000 claims 1
- -1 alkyl / alkoxy silanes Chemical class 0.000 claims 1
- 239000011230 binding agent Substances 0.000 claims 1
- 125000004432 carbon atoms Chemical group C* 0.000 claims 1
- 239000006184 cosolvent Substances 0.000 claims 1
- 230000001808 coupling Effects 0.000 claims 1
- 238000010168 coupling process Methods 0.000 claims 1
- 238000005859 coupling reaction Methods 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- ODLMAHJVESYWTB-UHFFFAOYSA-N propylbenzene Chemical compound CCCC1=CC=CC=C1 ODLMAHJVESYWTB-UHFFFAOYSA-N 0.000 claims 1
- 239000003586 protic polar solvent Substances 0.000 claims 1
- ZQZCOBSUOFHDEE-UHFFFAOYSA-N tetrapropyl silicate Chemical compound CCCO[Si](OCCC)(OCCC)OCCC ZQZCOBSUOFHDEE-UHFFFAOYSA-N 0.000 claims 1
Claims (20)
- − ベンジルエーテル型フェノール樹脂および溶媒を含有する、ポリオール成分、
− 1分子あたり少なくとも2個のイソシアネート基を有する1種または複数のイソシアネート化合物からなる、イソシアネート成分、
を少なくとも有する成形材料混合物を硬化させるための成分系であって、前記ポリオール成分と前記イソシアネート成分とは互いに空間的に離れており、
前記ベンジルエーテル型フェノール樹脂が、モノマー成分として少なくとも1種のフェノールを有し、前記フェノールは、脂肪族炭化水素基で置換されており、炭化水素原子数11〜26で0〜4個の二重結合を有する前記脂肪族炭化水素基で芳香環が置換されており、該フェノール樹脂中の該炭化水素基で置換された前記フェノールの部分が、0.5〜20重量%であり、
前記ポリオール成分が、少なくとも95重量%の非極性溶媒を含む溶媒を含有し、非極性溶媒が、炭化水素、アルキル/アルコキシシラン、アルキル/アルコキシシロキサン、およびこれらの混合物から選択され、
前記ベンジルエーテル型フェノール樹脂が、前記溶媒に溶解する、成分系。 - 前記ベンジルエーテル型フェノール樹脂の−CH 2 −OH基の最大で25モル%が、C 1 〜C 12 炭化水素基、特にC 1 〜C 4 炭化水素基でエステル化されている、請求項1に記載の成分系。
- 前記溶媒が、前記ポリオール成分に対して、10〜70重量%、特に好ましくは26〜55重量%、とりわけ好ましくは41〜50重量%の量で使用される、請求項1または2に記載の成分系。
- 該フェノール樹脂が、2.5重量%未満、好ましくは2重量%未満の遊離フェノールを含有する、請求項1〜3のいずれか一項に記載の成分系。
- 前記ポリオール成分が、遊離サリゲニンも含有し、遊離フェノールと前記遊離サリゲニンの重量比が、1:1超である、請求項1〜4のいずれか一項に記載の成分系。
- 前記非極性溶媒が、アルキルベンゼン、好ましくは、炭素原子数7〜13のアルキルベンゼン、特にトリメチルベンゼンおよびプロピルベンゼンである、請求項1〜5のいずれか一項に記載の成分系。
- 前記非極性溶媒が、C 6 〜C 22 アルカンである、請求項1〜6のいずれか一項に記載の成分系。
- 前記アルキル/アルコキシシランが、オルトケイ酸テトラエチルまたはオルトケイ酸テトラプロピル、これらのオリゴマー、およびこれらの混合物である、請求項1〜7のいずれか一項に記載の成分系。
- 前記非極性溶媒が、35未満のE T (30)値を有する、請求項1〜8のいずれか一項に記載の成分系。
- 前記溶媒が、共溶媒として、ジカルボン酸のジエステル、好ましくは、分枝ジカルボン酸のジエステルを含有する、請求項1〜9のいずれか一項に記載の成分系。
- 前記ベンジルエーテル型フェノール樹脂が、モノマー成分として、フェノールおよびクレゾールを含有し、該フェノール樹脂に組み込まれた前記クレゾールのモル占有率が、該フェノール樹脂に組み込まれた前記フェノールのモル占有率以下である、請求項1〜10のいずれか一項に記載の成分系。
- 前記ポリオール成分が、
a)1.5重量%未満、特に好ましくは1.0重量%未満、とりわけ好ましくは0.8重量%未満の水を含有する、
請求項1〜11のいずれか一項に記載の成分系。 - 前記ポリオール成分が、
a)2重量%未満、特に好ましくは1.5重量%未満、とりわけ好ましくは1.0重量%未満の脂肪族アルコールを含有するか、あるいは
b)アルキル/アルコキシシラン、アルキル/アルコキシシロキサン、またはこれらの混合物が使用される場合、1.5重量%未満、好ましくは1.0重量%未満、とりわけ好ましくは0.8重量%未満の脂肪族アルコールを含有する、
請求項1〜12のいずれか一項に記載の成分系。 - 該フェノール樹脂が、DIN 5567−1に従って測定して、600〜1200g/モル、特に600〜1,000g/モルの平均分子量(Mw)を有する請求項1〜13のいずれか一項に記載の成分系。
- 空間的に離れた別の成分として、耐熱性の成形ベース材料をさらに含有する、請求項1〜14のいずれか一項に記載の成分系。
- 前記脂肪族炭化水素基で置換された前記フェノールが、モノマー成分として、
a)前記脂肪族炭化水素基が、0〜3個の二重結合を有すること、
b)前記脂肪族炭化水素基で置換された前記フェノールが、モノマーとして、前記ベンジルエーテル型フェノール樹脂中に、0.5〜15重量%、好ましくは2〜12重量%、組み込まれていること、
c)前記脂肪族炭化水素基が、前記フェノールのモノマー成分の、メタ位またはパラ位で、好ましくはメタ位で結合していること、
d)前記脂肪族炭化水素基で置換された前記フェノールが、カルドールおよび/またはカルダノールであること
のうちの1つまたは複数の特徴によってさらに特徴付けられる、請求項1〜15のいずれか一項に記載の成分系。 - 請求項1〜16のいずれか一項に記載のポリオール成分およびイソシアネート成分、ならびに耐熱性の成形ベース材料を組み合わせることによって製造される、成形材料混合物。
- 請求項1〜16のいずれか一項に記載のポリオール成分およびイソシアネート成分、ならびに耐熱性の成形ベース材料を組み合わせること、ならびにPU非焼成法およびPUコールドボックス法に従って硬化させることによる、型、中子またはライザーを製造するための方法。
- イソシアネートバインダーの要素としてのポリオール成分の使用であって、前記ポリオール成分が、ベンジルエーテル型フェノール樹脂および溶媒を含有し、
− イソシアネート成分が、1分子あたり少なくとも2個のイソシアネート基を有する1種または複数のイソシアネート化合物からなり、
該フェノール樹脂が、モノマー成分として少なくとも1種の炭化水素置換フェノールを有し、該フェノールは、炭化水素原子数11〜26で0〜4個の二重結合を有する脂肪族炭化水素基で芳香環が置換されており、前記フェノール樹脂中の該炭化水素基で置換された前記フェノールの部分が、0.5〜20重量%であり、
前記ポリオール成分が、少なくとも95重量%の非極性溶媒を含む溶媒を含有し、前記非極性溶媒が、炭化水素、アルキル/アルコキシシラン、アルキル/アルコキシシロキサン、およびこれらの混合物から選択され、
前記ベンジルエーテル型フェノール樹脂が、前記溶媒に溶解する、使用。 - 前記脂肪族炭化水素基で置換された前記フェノールが、モノマー成分として、
a)前記脂肪族炭化水素基が、0〜3個の二重結合を有すること、
b)前記脂肪族炭化水素基で置換された前記フェノールが、モノマーとして、前記ベンジルエーテル型フェノール樹脂中に、0.5〜15重量%、好ましくは2〜12重量%まで、組み込まれていること、
c)前記脂肪族炭化水素基が、前記フェノールのモノマー成分の、メタ位またはパラ位で、好ましくはメタ位で結合していること、
d)前記脂肪族炭化水素基で置換された前記フェノールが、カルドールおよび/またはカルダノールであること、
のうちの1つまたは複数の特徴によってさらに特徴付けられる、請求項19に記載の使用。