JP2019142598A - bag - Google Patents

bag Download PDF

Info

Publication number
JP2019142598A
JP2019142598A JP2019107607A JP2019107607A JP2019142598A JP 2019142598 A JP2019142598 A JP 2019142598A JP 2019107607 A JP2019107607 A JP 2019107607A JP 2019107607 A JP2019107607 A JP 2019107607A JP 2019142598 A JP2019142598 A JP 2019142598A
Authority
JP
Japan
Prior art keywords
film
layer
bag
resin
back seal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2019107607A
Other languages
Japanese (ja)
Other versions
JP6971443B2 (en
Inventor
知宏 上杉
Tomohiro Uesugi
知宏 上杉
松永　伸二
Shinji Matsunaga
伸二 松永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kyoraku Co Ltd
Original Assignee
Kyoraku Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2015039052A external-priority patent/JP6536878B2/en
Application filed by Kyoraku Co Ltd filed Critical Kyoraku Co Ltd
Priority to JP2019107607A priority Critical patent/JP6971443B2/en
Publication of JP2019142598A publication Critical patent/JP2019142598A/en
Application granted granted Critical
Publication of JP6971443B2 publication Critical patent/JP6971443B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

To provide a bag excellent in easy opening applicable for bag-in-box use and like.SOLUTION: A bag in accordance with the present invention is a multiple bag 1 excellent in easy opening allowing multiple film 2 including a back seal part 6 integrated with four piece of film to be easily torn because a tear starting part 51 arranged in a joined part 5 of the multiple bag 1 configured with the multiple film 2 including an outer film 3 and an inner film is formed to reach from an outer edge 52 of the joined part at least to the back seal part 6. Also, at least the outer film 3 having a middle layer made of mixed resin with cyclic olefin resin and polyolefin resin provides the multiple bag 1 excellent in easy opening by allowing the multi film 2 to be easily torn.SELECTED DRAWING: Figure 1

Description

本発明は、袋に関する。さらに詳しくは、いわゆるバックインボックス等に用いられ、材料、食品等、所定の内容物を包装、運搬等することが可能な袋に関する。   The present invention relates to a bag. More specifically, the present invention relates to a bag that can be used for a so-called back-in box or the like and can wrap or carry a predetermined content such as a material or food.

業務用に使用される液体、半流動体、粉体、固形、ペースト体等の材料、食品等は、従来は金属製の容器に充填して運搬、保管、販売等に供されていた。一方、金属製の容器は使用後の容器が嵩張ること、内容物を取出しにくいことや、使用後の容器処理の困難性や、容器の重量が重い等の問題があった。   Conventionally, materials such as liquids, semi-fluids, powders, solids, pastes, foods, etc. used for business use have been packed in metal containers for transportation, storage, and sales. On the other hand, a metal container has problems such as a bulky container after use, difficulty in taking out contents, difficulty in processing the container after use, and heavy container weight.

近年、かかる内容物を合成樹脂製のフィルムからなる袋に充填した状態で段ボール製の箱やパレット等に収納して流通させる、いわゆるバッグインボックスと呼ばれる包装方法が広く実用化されている。このようなバッグインボックスにおいては、袋用のフィルムの機械的強度が高いことを要し、ナイロン、ポリエステル等の高強度フィルムに熱融着性を有する層を積層したフィルムが用いられている。また、機械的強度をさらに高めるべく前記以外のフィルムを積層したり、厚みを厚くする試みがなされていたのであるが、現実にはフィルムの厚みの増加だけでは解決し得ない現状であった。   In recent years, a so-called bag-in-box packaging method in which such contents are stored in a cardboard box, pallet, or the like in a state in which the contents are filled in a bag made of a synthetic resin film has been widely put into practical use. In such a bag-in-box, it is required that the bag film has high mechanical strength, and a film obtained by laminating a layer having heat-fusibility on a high-strength film such as nylon or polyester is used. In addition, attempts have been made to laminate films other than the above or to increase the thickness in order to further increase the mechanical strength. However, in reality, this cannot be solved only by increasing the thickness of the film.

そこで、袋を形成する２枚のフィルムが完全にラミネートされず、相互に移動ができる自由度が存在する多重袋が提案されている（例えば、特許文献１を参照。）。この多重袋（二重袋とも呼ばれる。）は、外側に現れる外側フィルムと、内容物と接する内側フィルムからなり、１枚のフィルムにピンホールが生じても他のフィルムの損傷を防ぐことができる。また、屈曲応力に対しても、内容物を支えている内側フィルムと、段ボール箱等と接して多重袋を支持する外側フィルムとの間で、ある程度の滑りを生じさせることができるため、衝撃等が吸収され、極度の屈曲応力が加わることを抑制し、袋を形成するフィルムにおけるピンホールの発生ないしは袋の破裂が生じることを防止している。   In view of this, there has been proposed a multiple bag in which the two films forming the bag are not completely laminated, and there is a degree of freedom of mutual movement (see, for example, Patent Document 1). This multiple bag (also called double bag) consists of an outer film that appears on the outside and an inner film that contacts the contents, and can prevent damage to other films even if pinholes occur in one film. . In addition, even against bending stress, a certain amount of slip can be generated between the inner film supporting the contents and the outer film supporting the multiple bag in contact with the cardboard box or the like. Is absorbed and an excessive bending stress is prevented from being applied, and the occurrence of pinholes in the film forming the bag or the rupture of the bag is prevented.

特許第４４９００４５号公報Japanese Patent No. 4490045

多重袋は、充填された内容物を取り出す際に、背シール部から引き裂いて開封することが多いが、例えば、合掌部での貼り合わせとして、かかる合掌部に背シール部を形成した場合には、合掌部に集められる４枚のシールを引き裂く必要があり、外側フィルムと内側フィルムが相互に移動ができる自由度が存在する等も含め、易開封性が良好でないという問題があり、改善が望まれていた。   When taking out the filled contents, the multiple bag is often torn from the back seal part and opened, but for example, when the back seal part is formed at the joint part as a pasting at the joint part It is necessary to tear the four seals collected at the joint part, and there is a problem that the easy-opening property is not good, including the freedom to move the outer film and the inner film relative to each other. It was rare.

本発明は、前記の課題に鑑みてなされたものであり、例えば、バックインボックス等に使用可能であり、易開封性に優れた袋を提供することにある。   This invention is made | formed in view of the said subject, For example, it can be used for a back-in box etc., It is providing the bag excellent in easy-opening property.

前記の課題を解決するために、本発明の第１発明に係る袋は、フィルムの両端を前記フィルム同士が対向するように重ね合わせて合掌部が形成され、前記合掌部に所定の幅で、重ね合わされる前記フィルム同士を溶着して一体化した背シール部が形成されるとともに、前記背シール部と直交する側の両端縁付近を所定の幅で溶着した横シール部が形成されることで内容物が充填密封された袋が形成され、前記合掌部には前記横シール部に対して略平行に引裂くように開封するための、前記横シール部に対して略平行に形成される引裂開始部を有し、前記引裂開始部は前記合掌部の外縁から少なくとも前記背シール部まで達するように形成されることを特徴とする。   In order to solve the above-mentioned problem, the bag according to the first invention of the present invention has a palm portion formed by overlapping both ends of the film so that the films face each other, and with a predetermined width in the palm portion, By forming a back seal part in which the films to be superimposed are integrated to form a back seal part, and a lateral seal part in which the vicinity of both end edges on the side orthogonal to the back seal part is welded with a predetermined width is formed. A bag is formed which is filled and sealed with the contents, and the tearing portion is formed substantially parallel to the lateral seal portion for opening the joint portion so as to tear substantially parallel to the lateral seal portion. The tear start portion is formed so as to reach at least the back seal portion from an outer edge of the palm portion.

本発明の第１発明に係る袋は、前記した第１発明において、前記背シール部は前記合掌部に対して細幅線状に複数形成され、前記引裂開始部は前記複数の背シール部のうち少なくとも前記合掌部の外縁側に形成された前記背シール部に達するように形成されていることを特徴とする。   The bag according to a first aspect of the present invention is the bag according to the first aspect, wherein the back seal portion is formed in a plurality of narrow lines with respect to the palm portion, and the tear start portion is formed of the plurality of back seal portions. Of these, it is formed so as to reach at least the back seal portion formed on the outer edge side of the palm portion.

本発明の第２発明に係る多重袋は、フィルムの両端を前記フィルム同士が対向するように重ね合わせて合掌部が形成され、前記合掌部に所定の幅で、重ね合わされる前記フィルム同士を溶着して一体化した背シール部が形成されるとともに、前記背シール部と直交する側の両端縁付近を所定の幅で溶着した横シール部が形成されることで内容物が充填密封された袋が形成され、前記合掌部には前記横シール部に対して略平行に引裂くように開封するための、前記横シール部に対して略平行に形成される引裂開始部を有し、少なくとも前記フィルムは環状ポリオレフィン樹脂とポリオレフィン系樹脂との混合樹脂からなる中間層を有する多層構成であることを特徴とする。   In the multiple bag according to the second aspect of the present invention, a palm portion is formed by overlapping both ends of the film so that the films face each other, and the films to be overlapped with each other at a predetermined width are welded to the palm portion. A bag in which the contents are filled and sealed by forming an integrated back seal part and forming a horizontal seal part welded with a predetermined width near both end edges on the side orthogonal to the back seal part And the tearing portion has a tear start portion formed substantially parallel to the lateral seal portion for opening so as to tear substantially parallel to the lateral seal portion, and at least the The film has a multilayer structure having an intermediate layer made of a mixed resin of a cyclic polyolefin resin and a polyolefin-based resin.

本発明の第２発明に係る袋は、前記した第２発明において、前記混合樹脂は、前記環状ポリオレフィン樹脂を前記混合樹脂全体に対して３〜９９質量％含有することを特徴とする。   The bag according to the second invention of the present invention is characterized in that, in the second invention described above, the mixed resin contains 3 to 99% by mass of the cyclic polyolefin resin with respect to the total of the mixed resin.

本発明の第１発明に係る袋は、袋の合掌部に形成される引裂開始部が合掌部の外縁から少なくとも背シール部まで達するように形成されているので、多重フィルムを容易に引き裂くことができる、易開封性に優れた袋となる。   Since the bag according to the first aspect of the present invention is formed so that the tear start portion formed at the palm portion of the bag reaches at least the back seal portion from the outer edge of the palm portion, the multiple film can be easily torn. A bag that is easy to open.

また、本発明の第２発明に係る袋は、袋のフィルムが環状オレフィン系樹脂とポリオレフィン系樹脂との混合樹脂からなる中間層を有するので、フィルムを容易に引き裂くことができる、易開封性に優れた袋となる。   Further, the bag according to the second invention of the present invention has an intermediate layer made of a mixed resin of a cyclic olefin resin and a polyolefin resin, so that the film can be easily torn and easily opened. An excellent bag.

本発明に係る多重袋を示した斜視図である。It is the perspective view which showed the multiple bag based on this invention. 本発明に係る多重袋を示した正面図である。It is the front view which showed the multiple bag which concerns on this invention. 多重フィルム（チューブ状フィルム）を筒状に湾曲し、重ね合わせて合掌部を形成した状態を示した概略図である。It is the schematic which showed the state which curved the multiple film (tubular film) in the cylinder shape, and overlapped and formed the palm part. チューブ状フィルムを用いた場合の背シール部の拡大図である。It is an enlarged view of the back seal part at the time of using a tubular film. 多重フィルム（ブロッキング接着フィルム）を筒状に湾曲し、重ね合わせて合掌部を形成した状態を示した概略図である。It is the schematic which showed the state which curved the multilayer film (blocking adhesive film), and overlapped and formed the palm part. ブロッキング接着フィルムを用いた場合の背シール部の拡大図である。It is an enlarged view of the back seal part at the time of using a blocking adhesive film. 本発明に係る多重袋の他の態様を示した正面図である。It is the front view which showed the other aspect of the multiple bag which concerns on this invention. チューブ状フィルムにおいて、内側フィルム及び外側フィルムを３層とした場合の層構成を示した断面図である。In a tubular film, it is sectional drawing which showed the layer structure at the time of making an inner film and an outer film into 3 layers. ブロッキング接着フィルムにおいて、外側フィルムを３層とした場合の層構成を示した断面図である。In a blocking adhesive film, it is sectional drawing which showed the layer structure at the time of making an outer film into 3 layers.

以下、本発明に係る多重袋１の一態様について説明する。   Hereinafter, an aspect of the multiple bag 1 according to the present invention will be described.

（Ａ）多重袋１の構成（第１実施形態（第１発明）、第２実施形態（第２発明）共通）：
以下、本発明に係る多重袋１について説明する。図１は、本発明に係る多重袋１を示した斜視図、図２は、本発明に係る多重袋１を示した正面図、図３は、多重フィルム２（チューブ状フィルム２１）を筒状に湾曲し、重ね合わせて合掌部５を形成した状態を示した概略図、図４は、チューブ状フィルム２１を用いた場合の背シール部６の拡大図、をそれぞれ示す。図中、１は多重袋、２は多重フィルム、３は外側フィルム、４は内側フィルム、５は合掌部、５１は引裂開始部、５２は合掌部の外縁、６は背シール部、６１は合掌部の外縁５２側に形成された背シール部、７は横シール部、をそれぞれ示す。 (A) Configuration of the multiplex bag 1 (common to the first embodiment (first invention) and the second embodiment (second invention)):
Hereinafter, the multiple bag 1 according to the present invention will be described. FIG. 1 is a perspective view showing a multiplex bag 1 according to the present invention, FIG. 2 is a front view showing the multiplex bag 1 according to the present invention, and FIG. 3 shows a multiplex film 2 (tubular film 21) in a cylindrical shape. FIG. 4 is an enlarged view of the back seal portion 6 when the tube-shaped film 21 is used. In the figure, 1 is a multiple bag, 2 is a multiple film, 3 is an outer film, 4 is an inner film, 5 is a palm portion, 51 is a tear start portion, 52 is an outer edge of the palm portion, 6 is a back seal portion, and 61 is a palm. A back seal part formed on the outer edge 52 side of the part, and 7 a horizontal seal part.

図１及び図２に示される多重袋１は、外側フィルム３と内側フィルム４からなる多重フィル２により構成される。なお、外側フィルム３及び内側フィルム４については、多重袋１として製袋化した場合に、多重袋１の外側に現れる（図示しない段ボール箱等と接する）フィルムを外側フィルム３、多重袋１の内側に現れる（図示しない内容物と接する）フィルムを内側フィルム４とする。   The multiple bag 1 shown in FIGS. 1 and 2 is constituted by a multiple fill 2 composed of an outer film 3 and an inner film 4. As for the outer film 3 and the inner film 4, when the bag is made as the multiple bag 1, the film that appears outside the multiple bag 1 (in contact with a cardboard box or the like not shown) is the inner film of the outer film 3 or the multiple bag 1. The film appearing at (in contact with the contents not shown) is referred to as the inner film 4.

図３に示すように、多重袋１を構成する合掌部５は、多重フィルム２を筒状に湾曲させ、多重フィルム２の両端を内側フィルム４同士が対向するように重ね合わせることにより形成される。   As shown in FIG. 3, the palm portion 5 constituting the multiplex bag 1 is formed by bending the multiplex film 2 into a cylindrical shape and overlapping the both ends of the multiplex film 2 so that the inner films 4 face each other. .

多重袋１は、使用する際に所定の内容物が充填されるとともに、背シール部６と横シール部７が形成されることにより、内容物が充填密封される。図１や図２に示すように、背シール部６は、合掌部５に対して所定の幅（概ね、２〜２０ｍｍ程度。以下同じ。）で帯状に溶着（ヒートシール、熱融着のこと。以下同じ。）することにより形成される。また、横シール部７は、かかる背シール部６と直交する側の両端縁付近を所定の幅（概ね２〜２０ｍｍ程度。以下同じ。）で帯状に溶着することにより形成される。なお、横シール部７は、細幅線状の複数のシール部からなるようにしてもよい。   The multiplex bag 1 is filled with a predetermined content when used, and the back seal portion 6 and the lateral seal portion 7 are formed, whereby the content is filled and sealed. As shown in FIG. 1 and FIG. 2, the back seal portion 6 is welded in a band shape with a predetermined width (generally about 2 to 20 mm; the same shall apply hereinafter) with respect to the palm portion 5 (that is, heat sealing or heat sealing). The same shall apply hereinafter). Further, the lateral seal portion 7 is formed by welding the vicinity of both end edges on the side orthogonal to the back seal portion 6 with a predetermined width (approximately 2 to 20 mm; the same applies hereinafter) in a band shape. In addition, you may make it the horizontal seal | sticker part 7 consist of a some narrow width | variety seal part.

背シール部６、横シール部７とも、多重フィルム２の内側フィルム４同士を平坦状に接した状態とした上で、外部から図示しない所定の幅のシールバー等で挟み込むことにより形成される。図４は背シール部６の拡大図を示しているが、接している内側フィルム４同士のほか、外側フィルム３も含め、重ね合わされる全てのフィルム（外側フィルム２枚、内側フィルム２枚の計４枚。）が溶着されて一体化している。また、これは、横シール部７についても同様である。   Both the back seal portion 6 and the lateral seal portion 7 are formed by sandwiching the inner films 4 of the multiple film 2 in a flat state and sandwiching them with a seal bar having a predetermined width (not shown) from the outside. FIG. 4 shows an enlarged view of the back seal portion 6. In addition to the inner films 4 that are in contact with each other, the outer film 3 as well as all the films that are superposed (total of two outer films and two inner films) are shown. 4) are welded and integrated. This also applies to the lateral seal portion 7.

なお、図３及び図４は、多重フィルム２の構成として、後記する（Ｂ）（１）や（Ｃ）（１）で説明するチューブ状フィルム２１を用いた態様を示している。チューブ状フィルム２１は、外側フィルム３と内側フィルム４が一体化されており、外側フィルム３と内側フィルム４の両側端縁が互いに連続している。   3 and 4 show an embodiment in which the tubular film 21 described later in (B) (1) and (C) (1) is used as the configuration of the multiple film 2. In the tubular film 21, the outer film 3 and the inner film 4 are integrated, and both side edges of the outer film 3 and the inner film 4 are continuous with each other.

一方、多重フィルム２の構成として、後記する（Ｂ）（２）や（Ｃ）（２）で説明するブロッキング接着フィルム２２を用いた場合にあっては、次のようになる。図５は、多重フィルム２（ブロッキング接着フィルム２２）を筒状に湾曲させ、重ね合わせて合掌部５を形成した状態を示した概略図であり、図６は、ブロッキング接着フィルム２２を用いた場合における背シール部６の拡大図である。このように、ブロッキング接着フィルム２２は、チューブ状フィルム２１と異なり、外側フィルム３と内側フィルム４が一体化されておらず、外側フィルム３と内側フィルム４の両側端縁も互いに連続していない。   On the other hand, when the blocking adhesive film 22 described in (B) (2) and (C) (2) described later is used as the configuration of the multiple film 2, the following is obtained. FIG. 5 is a schematic view showing a state in which the multiple film 2 (blocking adhesive film 22) is bent into a cylindrical shape and overlapped to form the palm portion 5, and FIG. 6 shows a case where the blocking adhesive film 22 is used. It is an enlarged view of the back seal part 6 in FIG. Thus, unlike the tubular film 21, the blocking adhesive film 22 is not integrated with the outer film 3 and the inner film 4, and both side edges of the outer film 3 and the inner film 4 are not continuous with each other.

（Ｂ）第１実施形態に係る多重袋１：
以下、第１実施形態に係る多重袋１の構成を説明する。本発明の第１実施形態に係る多重袋１は、図１及び図２に示すように、多重フィルム２の両端を内側フィルム４同士が対向するように重ね合わせた合掌部５に対して、引裂開始部５１が形成されている。引裂開始部５１は、横シール部７に対して略平行に開封するために形成され、例えば、横シール部７に対して略平行となるように形成すれば、使用者が横シール部７に対して略平行に開封しやすくなる。 (B) Multiple bag 1 according to the first embodiment 1:
Hereinafter, the configuration of the multiple bag 1 according to the first embodiment will be described. As shown in FIGS. 1 and 2, the multiple bag 1 according to the first embodiment of the present invention is torn against the palm portion 5 in which both ends of the multiple film 2 are overlapped so that the inner films 4 face each other. A start portion 51 is formed. The tear start portion 51 is formed to open substantially parallel to the lateral seal portion 7. For example, if the tear start portion 51 is formed so as to be substantially parallel to the lateral seal portion 7, the user can contact the lateral seal portion 7. On the other hand, it becomes easy to open it substantially parallel.

合掌部５に形成される引裂開始部５１は、初期の引き裂き強度を弱め、易開封性を向上させる。引裂開始部５１は、スリット（切れ目）、Ｖノッチ、Ｉノッチ、ミシン目、微多孔の集合体等の任意の形状とすることができる。   The tear start part 51 formed in the palm part 5 weakens the initial tear strength and improves easy-openability. The tear start portion 51 can have an arbitrary shape such as a slit (cut), a V notch, an I notch, a perforation, or a microporous aggregate.

引裂開始部５１は、図１及び図２に示すように、合掌部の外縁５２から少なくとも背シール部６まで達するように形成されている。引裂開始部５１が背シール部６まで達しているため、開封時の引き裂きの繰り出しをスムースに行うことができ、４枚のフィルム（２枚の多重フィルム２）が集まった背シール部６を容易に引き裂くことができる、易開封性に優れた多重袋１となる。また、引裂開始部５１の長さとしては、前記のように背シール部６まで達していれば特に制限はないが、概ね５〜２０ｍｍであればよい。   As shown in FIGS. 1 and 2, the tear start portion 51 is formed so as to reach at least the back seal portion 6 from the outer edge 52 of the palm portion. Since the tear start portion 51 reaches the back seal portion 6, the tear can be smoothly drawn out at the time of opening, and the back seal portion 6 in which four films (two multiplex films 2) gather can be easily obtained. It becomes the multiple bag 1 excellent in easy-opening property that can be torn. In addition, the length of the tear start portion 51 is not particularly limited as long as it reaches the back seal portion 6 as described above, but may be approximately 5 to 20 mm.

図７は、多重袋１の他の態様を示した正面図である。図７にあっては、背シール部６が合掌部５に対して細幅線状に２本形成されている態様を示している。このように、細幅線状の背シール部６を複数形成した場合にあっては、引裂開始部５１は複数の細幅線状の背シール部６のうち少なくとも合掌部の外縁５２側に形成された背シール部６１に達するように形成されている。なお、本発明にあって、細幅線状の背シール部６，６１は、ヒートシール（溶着）により、概ね２〜１０ｍｍ程度の幅からなる略直線状に形成された背シール部６を指す。また、複数の背シール部６，６１の数は、概ね２〜５とすればよい。   FIG. 7 is a front view showing another aspect of the multiple bag 1. FIG. 7 shows an aspect in which two back seal portions 6 are formed in a narrow line shape with respect to the palm portion 5. As described above, when a plurality of narrow line-shaped back seal portions 6 are formed, the tear start portion 51 is formed on the outer edge 52 side of at least the palm portion of the plurality of narrow line-shaped back seal portions 6. It is formed so as to reach the back seal portion 61 made. In addition, in this invention, the narrow line-shaped back seal parts 6 and 61 point out the back seal part 6 formed in the substantially linear form which has a width | variety about 2-10 mm by heat sealing (welding). . Moreover, what is necessary is just to make the number of the some back seal parts 6 and 61 into 2-5 in general.

（１）多重フィルム２の構成（チューブ状フィルム２１）：
次に、多重袋１を構成する多重フィルム２について説明する。多重フィルム２については、外側フィルム３と内側フィルム４を２枚重ねとしたものであるが、例えば、筒状のフィルムを扁平状にして２枚重ねにした両端が袋状に閉じた対面する２枚のフィルム（チューブ状フィルム２１）とすることができる。多重フィルム２であるチューブ状フィルム２１は、図３及び図４からもわかるように、外側フィルム３と内側フィルム４の両側端縁が互いに連続しているものであり、外側フィルム３と内側フィルム４が一体化されている。よって、外側フィルム３と内側フィルム４は、共通する樹脂で構成されることになる。 (1) Configuration of multiple film 2 (tubular film 21):
Next, the multiple film 2 constituting the multiple bag 1 will be described. As for the multiple film 2, the outer film 3 and the inner film 4 are stacked in two layers. For example, the two ends of the cylindrical film that are flattened and stacked in two layers face each other closed in a bag shape 2 It can be set as a sheet of film (tube-shaped film 21). As can be seen from FIG. 3 and FIG. 4, the tubular film 21 that is the multiple film 2 is one in which both side edges of the outer film 3 and the inner film 4 are continuous with each other, and the outer film 3 and the inner film 4. Are integrated. Therefore, the outer film 3 and the inner film 4 are made of a common resin.

チューブ状フィルム２１は、多層構成とすることが好ましい。以下、外側フィルム３及び内側フィルム４を共通する３層構成としたチューブ状フィルム２１を例に挙げて説明する。   The tube-shaped film 21 preferably has a multilayer structure. Hereinafter, the tubular film 21 having a three-layer configuration in which the outer film 3 and the inner film 4 are shared will be described as an example.

図８は、チューブ状フィルム２１において、外側フィルム３及び内側フィルム４を３層とした場合の層構成を示した断面図である。図８中、３は外側フィルム、４は内側フィルム、３１，４１は内層、３２，４２は中間層、３３，４３は外層、Ｃは隙間、をそれぞれ示す。   FIG. 8 is a cross-sectional view showing the layer structure of the tubular film 21 when the outer film 3 and the inner film 4 have three layers. In FIG. 8, 3 is an outer film, 4 is an inner film, 31 and 41 are inner layers, 32 and 42 are intermediate layers, 33 and 43 are outer layers, and C is a gap.

図８に一例を示すように、外側フィルム３及び内側フィルム４を多層とする場合は、外側フィルム３と内側フィルム４は、外側フィルム３と内側フィルム４の間に形成されている隙間Ｃからみて対称の関係となり、多重袋１の外側から多重袋１の内側までは、多重袋１の外側／外層３３／中間層３２／内層３１（以上が外側フィルム３の層。）／隙間Ｃ／内層４１／中間層４２／外層４３（以上が内側フィルム４の層。）／多重袋１の内側、となる。そして、外層３３，４３に該当する層が、背シール部６や横シール部７を形成する際に、重ね合わされて、直接接して溶着されることになる。   As shown in FIG. 8, when the outer film 3 and the inner film 4 are multilayered, the outer film 3 and the inner film 4 are viewed from a gap C formed between the outer film 3 and the inner film 4. From the outer side of the multiple bag 1 to the inner side of the multiple bag 1, the outer side of the multiple bag 1 / outer layer 33 / intermediate layer 32 / inner layer 31 (the above is the layer of the outer film 3) / gap C / inner layer 41. / Intermediate layer 42 / outer layer 43 (the above is the layer of the inner film 4) / inner side of the multiple bag 1. Then, when the back seal portion 6 and the lateral seal portion 7 are formed, the layers corresponding to the outer layers 33 and 43 are overlapped and welded in direct contact with each other.

前記した層のうち、背シール部６や横シール部７を形成する際に直接接して溶着される外層３３，４３は、その層自体にヒートシール性があることが好ましく、例えば、ポリオレフィン系樹脂が挙げられ、具体的には、高密度ポリエチレン（ＨＤＰＥ）、中密度ポリエチレン（ＭＤＰＥ）、低密度ポリエチレン（ＬＤＰＥ）、直鎖状（線状）低密度ポリエチレン（ＬＬＤＰＥ）、直鎖状超低密度ポリエチレン（ＶＬＤＰＥ）、また、エチレンと共重合可能なビニル化合物との共重合体、例えば、エチレン−酢酸ビニル共重合体（ＥＶＡ）、アイオノマー、エチレン−アクリル酸またはエチレン−アクリル酸エステル共重合体、エチレンメタアクリル酸またはメタアクリル酸エステル共重合体、エチレン−プロピレン共重合体等のポリエチレン系樹脂や、ポリプロピレン系樹脂や、ポリエチレン、ポリプロピレン等のポリオレフィン系樹脂をアクリル酸、メタアクリル酸、無水マレイン酸、フマール酸、その他の不飽和カルボン酸で変成した酸変性ポレオレフィン樹脂等のポリオレフィン系樹脂が挙げられる。これらの樹脂は、その１種を単独で使用してもよく、２種以上を組み合わせて使用するようにしてもよい。   Of the layers described above, the outer layers 33 and 43 that are welded in direct contact with each other when the back seal portion 6 and the lateral seal portion 7 are formed preferably have heat sealability. For example, polyolefin resin Specifically, high density polyethylene (HDPE), medium density polyethylene (MDPE), low density polyethylene (LDPE), linear (linear) low density polyethylene (LLDPE), linear ultra-low density Polyethylene (VLDPE), and copolymers of vinyl compounds copolymerizable with ethylene, such as ethylene-vinyl acetate copolymer (EVA), ionomers, ethylene-acrylic acid or ethylene-acrylic ester copolymers, Polyethylene such as ethylene methacrylic acid or methacrylic acid ester copolymer, ethylene-propylene copolymer Polyolefin resins such as resins, polypropylene resins, and acid-modified polyolefin resins obtained by modifying polyolefin resins such as polyethylene and polypropylene with acrylic acid, methacrylic acid, maleic anhydride, fumaric acid, and other unsaturated carboxylic acids Is mentioned. One of these resins may be used alone, or two or more thereof may be used in combination.

これらの樹脂のうち、ヒートシール性等が優れた、低密度ポリエチレン（ＬＤＰＥ）を使用することが好ましく、低密度ポリエチレンの中でも、耐ピンホール性を有し、タフで丈夫なため機械的強度等にも優れた直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を使用することが特に好ましい。   Of these resins, it is preferable to use low-density polyethylene (LDPE), which has excellent heat-sealing properties, etc. Among low-density polyethylene, it has pinhole resistance, is tough and strong, and has mechanical strength, etc. In particular, it is particularly preferable to use linear low density polyethylene (LLDPE).

なお、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を用いた場合の物性、機械的強度やヒートシール強度等は、共重合させるα−オレフィンの炭素数により調整される。一般に、炭素数３〜１３個、好ましくは炭素数４〜８個のα−オレフィン、例えばブテン−１、オクテン−１、ヘキセン−１、４−メチルペンテン−１、へプテン−１等が好ましく用いられる。   The physical properties, mechanical strength, heat seal strength, and the like when linear low density polyethylene (LLDPE) is used are adjusted by the number of carbon atoms of the α-olefin to be copolymerized. In general, α-olefins having 3 to 13 carbon atoms, preferably 4 to 8 carbon atoms, such as butene-1, octene-1, hexene-1, 4-methylpentene-1, heptene-1, etc. are preferably used. It is done.

低密度ポリエチレン（直鎖状低密度ポリエチレンを含む。）の密度は、０．８７０〜０．９３５ｇ／ｃｍ３であることが好ましい。密度がかかる範囲の低密度ポリエチレンを用いることにより、ヒートシール性等の諸特性が維持される。低密度ポリエチレンの密度は、０．８８０〜０．９２０ｇ／ｃｍ３であることが特に好ましい。なお、１９０℃におけるメルトフローレート（ＭＦＲ）は、０．１〜３０．０ｇ／１０分とすることが好ましく、０．５〜４．０ｇ／１０分とすることが特に好ましい。   The density of the low density polyethylene (including the linear low density polyethylene) is preferably 0.870 to 0.935 g / cm 3. Various characteristics such as heat sealability are maintained by using low density polyethylene in a range where the density is high. The density of the low density polyethylene is particularly preferably from 0.880 to 0.920 g / cm 3. The melt flow rate (MFR) at 190 ° C. is preferably 0.1 to 30.0 g / 10 minutes, and particularly preferably 0.5 to 4.0 g / 10 minutes.

図８における外側フィルム３及び内側フィルム４を構成する内層３１，４１や中間層３２，４２は、多重フィルム２に耐ピンホール性や機械的特性を付与すべく、前記したポリエチレン系樹脂、ポリプロピレン系樹脂等のポリオレフィン系樹脂のほか、ポリアミド系樹脂（ナイロン）、ポリエステル系樹脂（ＰＥＴ、ＰＢＴ）、エチレン−ビニルアルコール共重合体等を使用することができる。   The inner layers 31 and 41 and the intermediate layers 32 and 42 constituting the outer film 3 and the inner film 4 in FIG. 8 are provided with the above-described polyethylene-based resin and polypropylene-based resin so as to impart pinhole resistance and mechanical properties to the multiple film 2. In addition to polyolefin resins such as resins, polyamide resins (nylon), polyester resins (PET, PBT), ethylene-vinyl alcohol copolymers, and the like can be used.

なお、中間層３２，４２として、易引裂樹脂からなる易引裂樹脂層とするようにしてもよい。易引裂樹脂を中間層３２，４２として介することにより、多重フィルム２にさらなる易開封性を付与することができる。また、外側フィルム３や内側フィルム４を図８に示した３層の構成とする場合、外側フィルム３は、多重袋１の外側から順に、直鎖状低密度ポリエチレンからなる層（直鎖状低密度ポリエチレン層）／易引裂樹脂層／ポリオレフィン系樹脂からなる層（ポリオレフィン系樹脂層）、内側フィルム４は、多重袋１の外側（前記した隙間Ｃ）から順に、ポリオレフィン系樹脂層／易引裂樹脂層／直鎖状低密度ポリエチレン層とすることが好ましい。外側フィルム３及び内側フィルム４をかかる構成とすることにより、ヒートシール性、耐ピンホール性等を維持した状態で、易開封性（易引裂性）を付与することができる。   The intermediate layers 32 and 42 may be easily tearable resin layers made of easily tearable resin. By using the easy tear resin as the intermediate layers 32 and 42, it is possible to impart further easy opening to the multiple film 2. When the outer film 3 and the inner film 4 have the three-layer configuration shown in FIG. 8, the outer film 3 is a layer made of linear low density polyethylene (linear Density polyethylene layer) / easy tear resin layer / polyolefin resin layer (polyolefin resin layer), inner film 4 is polyolefin resin layer / easy tear resin in order from the outer side of the multiple bag 1 (the aforementioned gap C). Layer / linear low density polyethylene layer is preferred. By setting the outer film 3 and the inner film 4 as such a configuration, easy-openability (easy tearing property) can be imparted while maintaining heat sealability, pinhole resistance, and the like.

易引裂樹脂層を構成する樹脂としては、例えば、環状ポリオレフィン樹脂を含有する混合樹脂を用いるようにしてもよい。かかる環状ポリオレフィン樹脂を含有する層を中間層３２，４２として介在させることにより、多重フィルム２の易開封性（易引裂性）が向上する。   As the resin constituting the easily tearable resin layer, for example, a mixed resin containing a cyclic polyolefin resin may be used. By interposing the layer containing the cyclic polyolefin resin as the intermediate layers 32 and 42, the easy-openability (easy tearing property) of the multiple film 2 is improved.

環状ポリオレフィン樹脂は、一般に、環状オレフィンを重合単位として重合される樹脂の総称であり、例えば、特開平１−２４０５１７号公報、特開平３−１４８８２号公報、特開平３−１２２１３７号公報等に記載されている。本発明にあっては、環状オレフィンをメタセシス開環重合反応によって重合した開環メタセシス重合体（シクロオレフィンポリマー（ＣＯＰ：Ｃｙｃｌｏ−Ｏｌｅｆｉｎ Ｐｏｌｙｍｅｒ）とも呼ばれる。）はもちろんのこと、環状オレフィンとα−オレフィン（鎖状オレフィン）等との共重合体である、いわゆる環状オレフィンコポリマー（シクロオレフィンコポリマー（ＣＯＣ：Ｃｙｃｌｏ−Ｏｌｅｆｉｎ Ｃｏｐｏｌｙｍｅｒ）とも呼ばれる。）や、これらを不飽和カルボン酸やその誘導体で変性したグラフト重合体、並びに、それらの水素化物等を含むものとする。   The cyclic polyolefin resin is a general term for resins that are polymerized with a cyclic olefin as a polymerization unit, and is described in, for example, JP-A-1-240517, JP-A-3-14882, JP-A-3-122137, and the like. Has been. In the present invention, a ring-opening metathesis polymer obtained by polymerizing a cyclic olefin by a metathesis ring-opening polymerization reaction (also referred to as a cycloolefin polymer (COP)), as well as a cyclic olefin and an α-olefin. So-called cyclic olefin copolymers (also called cycloolefin copolymers (COC)), which are copolymers with (chain olefins), etc., and graft weights modified with unsaturated carboxylic acids or their derivatives Including coalescence and hydrides thereof.

環状オレフィンとしては、エチレン系不飽和結合及びビシクロ環を有する任意の環状炭化水素を使用することができ、ノルボルネン系モノマー等が広く知られており、ビシクロ［２.２.１］ヘプタ−２−エン（ノルボルネン）骨格を有するものが好ましい。   As the cyclic olefin, any cyclic hydrocarbon having an ethylenically unsaturated bond and a bicyclo ring can be used, and norbornene monomers and the like are widely known. Bicyclo [2.2.1] hept-2- Those having an ene (norbornene) skeleton are preferred.

具体的には、ビシクロ［２．２．１］ヘプタ−２−エン及びその誘導体、トリシクロ［４．３．０．１２．５］−３−デセン及びその誘導体、トリシクロ［４．４．０．１２．５］−３−ウンデセン及びその誘導体、テトラシクロ［４．４．０．１２．５．１７．１０］−３−ドデセン及びその誘導体、ペンタシクロ［６．５．１．１３．６．０２．７．０９．１３］−４−ペンタデセン及びその誘導体、ペンタシクロ［７．４．０．１２．５.１９．１２.０８．１３］−３−ペンタデセン及びその誘導体、ペンタシクロ［６．５．１．１３．６．０２．７．０９．１３］−４，１０−ペンタデカジエン及びその誘導体、ペンタシクロ［８．４．０．１２．５.１９．１２．０８．１３］−３−ヘキサデセン及びその誘導体等が挙げられるが、これらに限定されない。   Specifically, bicyclo [2.2.1] hept-2-ene and derivatives thereof, tricyclo [4.3.0.12.5] -3-decene and derivatives thereof, and tricyclo [4.4.0. 12.5] -3-undecene and derivatives thereof, tetracyclo [4.4.0.12.5.17.10] -3-dodecene and derivatives thereof, pentacyclo [6.5.1.13.6.02. 7.09.13] -4-pentadecene and its derivatives, pentacyclo [7.4.0.12.5.19.12.2.08.13] -3-pentadecene and its derivatives, pentacyclo [6.5.1. 13.6.0.2.7.09.13] -4,10-pentadecadiene and its derivatives, pentacyclo [8.4.0.12.5.19.12.08.13] -3-hexadecene and its derivatives Derivatives and the like, But it is not limited to these.

また、環状オレフィンは、置換基として、例えば、カルボキシル基、カルボン酸無水物等の酸無水物基、エポキシ基、アミノ基、アミド基、エステル基、ヒドロキシル基、スルホ基、ホスホノ基、ホスフィノ基等の極性基を有していてもよい。また、（メタ）アクリル酸、マレイン酸、無水マレイン酸、無水イタコン酸、グリシジル（メタ）アクリレート、（メタ）アクリル酸アルキル（例えば、炭素数１〜１０）エステル、マレイン酸アルキル（例えば、炭素数１〜１０）エステル、（メタ）アクリルアミド、（メタ）アクリル酸−２−ヒドロキシエチル等を挙げることができ、好ましくは、カルボキシル基、酸無水物基、エポキシ基、アミノ基、アミド基、エステル基、ヒドロキシル基、スルホ基、ホスホノ基、ホスフィノ基等の極性基を有する不飽和化合物を有していてもよい。   In addition, the cyclic olefin has, for example, a carboxyl group, an acid anhydride group such as a carboxylic acid anhydride, an epoxy group, an amino group, an amide group, an ester group, a hydroxyl group, a sulfo group, a phosphono group, a phosphino group, etc. May have a polar group. Moreover, (meth) acrylic acid, maleic acid, maleic anhydride, itaconic anhydride, glycidyl (meth) acrylate, alkyl (meth) acrylate (for example, carbon number 1-10) ester, alkyl maleate (for example, carbon number) 1-10) ester, (meth) acrylamide, (meth) acrylic acid-2-hydroxyethyl and the like can be mentioned, preferably carboxyl group, acid anhydride group, epoxy group, amino group, amide group, ester group And an unsaturated compound having a polar group such as a hydroxyl group, a sulfo group, a phosphono group, or a phosphino group.

例えば、環状オレフィンコポリマーとして、環状オレフィンと共重合するα−オレフィンとしては、例えば、エチレン、炭素数３〜２０のα−オレフィンを使用することができ、具体的には、エチレン、プロピレン、１−ブテン、１−ペンテン、３−メチル−１−ブテン、１−ヘキセン、４−メチル−１−ペンテン等が挙げられ、エチレン等が広く用いられる。   For example, as the α-olefin copolymerized with the cyclic olefin as the cyclic olefin copolymer, for example, ethylene and an α-olefin having 3 to 20 carbon atoms can be used. Specifically, ethylene, propylene, 1- Examples include butene, 1-pentene, 3-methyl-1-butene, 1-hexene, 4-methyl-1-pentene, and ethylene is widely used.

環状ポリオレフィン樹脂と組み合わせられる樹脂（後記）としてポリエチレン系樹脂を用いる場合、ポリエチレンに対する分散性が良好となるという等の理由で、環状オレフィンコポリマー（ＣＯＣ）を用いることが好ましく、共重合するα−オレフィンをエチレンとした、エチレン−環状オレフィン共重合体とすることが特に好ましい。   When a polyethylene resin is used as a resin (described later) to be combined with a cyclic polyolefin resin, it is preferable to use a cyclic olefin copolymer (COC) for reasons such as good dispersibility in polyethylene. It is particularly preferable to use an ethylene-cycloolefin copolymer in which is used as ethylene.

本発明において、開環メタセシス重合体の製造は、公知の開環メタセシス重合反応であれば特に限定されず、前記した環状オレフィンを、重合触媒を用いて開環重合させることによって製造することができる。   In the present invention, the production of the ring-opening metathesis polymer is not particularly limited as long as it is a known ring-opening metathesis polymerization reaction, and can be produced by ring-opening polymerization of the above-mentioned cyclic olefin using a polymerization catalyst. .

また、環状オレフィンコポリマーの製造は、例えば、所定のモル比としたα−オレフィンと環状オレフィンとを、メタロセン触媒等のシングルサイト系触媒やマルチサイト系触媒を用いてランダム重合させることによりなされる。   The cyclic olefin copolymer is produced by, for example, randomly polymerizing an α-olefin and a cyclic olefin having a predetermined molar ratio using a single site catalyst such as a metallocene catalyst or a multisite catalyst.

また、環状オレフィンモノマーの開環重合体等の水素添加物は、開環重合体を公知の水素化触媒により水素化することにより得ることができる。   A hydrogenated product such as a ring-opened polymer of a cyclic olefin monomer can be obtained by hydrogenating the ring-opened polymer with a known hydrogenation catalyst.

環状ポリオレフィン樹脂は、ガラス転移温度（Ｔｇ）（例えば、ＪＩＳ Ｋ７１２１等。）が６０℃以上のものを使用することが好ましい。ガラス転移温度がかかる範囲の環状ポリオレフィン樹脂を用いることにより、優れた耐熱性を維持することができる。環状ポリオレフィン樹脂は、ガラス転移温度（Ｔｇ）は、７０℃以上とすることが特に好ましい。   It is preferable to use a cyclic polyolefin resin having a glass transition temperature (Tg) (for example, JIS K7121 etc.) of 60 ° C. or higher. By using a cyclic polyolefin resin having a glass transition temperature in such a range, excellent heat resistance can be maintained. As for cyclic polyolefin resin, it is especially preferable that the glass transition temperature (Tg) shall be 70 degreeC or more.

また、環状ポリオレフィン樹脂のメルトフローレート（ＭＦＲ）は、３．０〜３０．０ｇ／１０分とすることが好ましい。ＭＦＲがかかる範囲の環状ポリオレフィン樹脂を用いることにより、優れた耐熱性を維持することができる。環状ポリオレフィン樹脂のＭＦＲは、ＩＳＯ １１３３やＡＳＴＭ Ｄ−１２３８（例えば、２８０℃。２１．１８Ｎ）に準拠して測定した値を用いればよい。環状ポリオレフィン樹脂のＭＦＲは、５．０〜２０．０ｇ／１０分とすることが特に好ましい。   Moreover, it is preferable that the melt flow rate (MFR) of cyclic polyolefin resin shall be 3.0-30.0 g / 10min. By using a cyclic polyolefin resin in such a range that MFR is applied, excellent heat resistance can be maintained. As the MFR of the cyclic polyolefin resin, a value measured in accordance with ISO 1133 or ASTM D-1238 (for example, 280 ° C., 21.18N) may be used. The MFR of the cyclic polyolefin resin is particularly preferably 5.0 to 20.0 g / 10 min.

中間層３２，４２を前記の混合樹脂とする場合、環状ポリオレフィン樹脂と組み合わせて用いることができる樹脂としては、前記したポリエチレン系樹脂や、ポリプロピレン系樹脂等のポリオレフィン系樹脂を用いることができる。この中でも、ポリエチレン系樹脂が好ましく、低密度ポリエチレン（ＬＤＰＥ）がさらに好ましく、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）が特に好ましい。   When the intermediate layers 32 and 42 are made of the mixed resin, as the resin that can be used in combination with the cyclic polyolefin resin, the above-described polyethylene resins and polyolefin resins such as polypropylene resins can be used. Among these, polyethylene resins are preferable, low density polyethylene (LDPE) is more preferable, and linear low density polyethylene (LLDPE) is particularly preferable.

易引裂樹脂層を構成する混合樹脂における環状ポリオレフィン樹脂の含有量は、混合樹脂全体（環状ポリオレフィン樹脂及び当該環状ポリオレフィン樹脂と組み合わせて用いられる樹脂との合計を指す。）に対して３〜９９質量％とすることが好ましい。環状ポリオレフィン樹脂の含有量をかかる範囲とすることにより、易引裂性が良好に実施されることになる。環状ポリオレフィン樹脂の含有量は、混合樹脂全体に対して６０〜９０質量％とすることがさらに好ましく、６０〜８０質量％とすることが特に好ましい。   The content of the cyclic polyolefin resin in the mixed resin constituting the easily tearable resin layer is 3 to 99 mass with respect to the entire mixed resin (the total of the cyclic polyolefin resin and the resin used in combination with the cyclic polyolefin resin). % Is preferable. By setting the content of the cyclic polyolefin resin within such a range, the easy tearability is favorably implemented. The content of the cyclic polyolefin resin is more preferably 60 to 90% by mass, and particularly preferably 60 to 80% by mass with respect to the entire mixed resin.

なお、前記した混合樹脂で構成されるような、環状ポリオレフィン樹脂を含有する層は、多層の外側フィルム３及び内側フィルム４において、中間層３２，４２とすることが好ましいが、外側フィルム３や内側フィルム４を多層とする場合に、中間層３２，４２以外の層としても問題はない。   In addition, although the layer containing cyclic polyolefin resin which is comprised with the above-mentioned mixed resin is preferably the intermediate layers 32 and 42 in the multilayer outer film 3 and the inner film 4, the outer film 3 and the inner film When the film 4 is a multilayer, there is no problem even if it is a layer other than the intermediate layers 32 and 42.

多重フィルム２であるチューブ状フィルム２１を製造するには、例えば、インフレーションフィルム法で得るのが好ましい。インフレーションフィルムは、あらかじめチューブ状（筒状）となっており、製造されたままの状態で使用でき、後工程でフィルムを筒状にする必要がなく継ぎ目も生じないというメリットもある。加えて、インフレーションフィルムは厚さが薄いフィルムはもちろんのこと、厚さが比較的厚いフィルムを容易に製造可能である。   In order to manufacture the tube-shaped film 21 which is the multiple film 2, it is preferable to obtain by the inflation film method, for example. The inflation film is in the form of a tube (cylinder) in advance, and can be used as manufactured, and there is an advantage that the film does not need to be formed into a cylinder in the subsequent process and no seam is produced. In addition, it is possible to easily produce a relatively thick film as well as a thin film.

一般的なインフレーションフィルム法としては、例えば、押出機からダイを経てチューブ状に押し出された溶融樹脂を垂直方向に引き上げ、かかる溶融樹脂を垂直方向に引き上げられる過程で供給される空気により膨らませてチューブ状とし、空冷しながらフラットなフィルムにして巻取装置に巻き取ることで、チューブ状フィルム２１を扁平状に巻いたロールを得ることができる。   As a general inflation film method, for example, a molten resin extruded in a tube shape from a extruder through a die is pulled up in the vertical direction, and the molten resin is expanded by air supplied in the process of being pulled up in the vertical direction. It is possible to obtain a roll in which the tubular film 21 is wound in a flat shape by forming a flat film while air cooling and winding it on a winding device.

なお、多重フィルム２をチューブ状フィルム２１とした場合にあっては、外側フィルム３及び内側フィルム４における外側に現れず接触する層（前記した図８における内層３１，４１）については、相互にブロッキング接着していることが好ましい。ここで、「相互にブロッキング接着している」とは、接触しているフィルム同士が接着剤等の他の媒体や熱融着により接着されて完全に一体化されているものではなく、接触しているフィルム同士が疑似接着して柔軟な状態であることを指す。ブロッキング接着は、フィルムの全面にわたって発生していてもよいし、フィルムの一部に部分的に発生していてもよい。ブロッキング接着させることにより、製袋等の際に外側フィルム３と内側フィルム４が一体化し、取り扱い性が良好となる。   In the case where the multiple film 2 is a tube-shaped film 21, the outer film 3 and the inner film 4 that do not appear on the outer side and contact with each other (the inner layers 31 and 41 in FIG. 8 described above) block each other. It is preferable to adhere. Here, “blocking to each other” means that the films in contact with each other are not completely integrated by being bonded by another medium such as an adhesive or by heat-sealing. It means that the films are in a flexible state by pseudo-bonding. Blocking adhesion may occur over the entire surface of the film, or may occur partially on a part of the film. By carrying out blocking adhesion, the outer film 3 and the inner film 4 are integrated during bag making or the like, and the handleability is improved.

チューブ状フィルム２１をブロッキング接着させるためには、例えば、前記したインフレーションフィルム法によって製膜されたポリオレフィン系のチューブ状フィルムを折畳みニップロール等で加圧して重ね合わせたフィルム間の空気を押出しながら１つ折りの扁平な２層フィルムとして巻き取ることによって、簡便に製造することができる。   In order to block-bond the tube-shaped film 21, for example, the polyolefin-based tube-shaped film formed by the above-described inflation film method is folded and pressed with a nip roll or the like, and folded while extruding air between the overlapped films. It can manufacture simply by winding up as a flat 2 layer film.

（２）多重フィルム２の構成（ブロッキング接着フィルム２２）：
次に、多重フィルム２の他の構成について説明する。多重フィルム２としては、別途独立した外側フィルム３と内側フィルム４がブロッキング接着している構成のもの（ブロッキング接着フィルム２２）を使用することができる。 (2) Configuration of multiple film 2 (blocking adhesive film 22):
Next, another configuration of the multiple film 2 will be described. As the multiple film 2, it is possible to use a film (blocking adhesive film 22) having a structure in which an independent outer film 3 and inner film 4 are bonded to each other by blocking.

ここで、「ブロッキング接着」については、前記した通りであり、接触しているフィルム同士が接着剤等の他の媒体や熱融着により接着されて完全に一体化されているものではなく、フィルム接触しているフィルム同士が疑似接着して柔軟な状態であることを指す。ブロッキング接着は、フィルムの全面にわたって発生していてもよいし、フィルムの一部に部分的に発生していてもよい。ブロッキング接着させることにより、製袋等の際に外側フィルム３と内側フィルム４が一体化し、取り扱い性が良好となる。   Here, “blocking adhesion” is as described above, and the films in contact with each other are not completely integrated by being bonded by another medium such as an adhesive or by heat fusion. It means that the films in contact are pseudo-bonded and in a flexible state. Blocking adhesion may occur over the entire surface of the film, or may occur partially on a part of the film. By carrying out blocking adhesion, the outer film 3 and the inner film 4 are integrated during bag making or the like, and the handleability is improved.

多重フィルム２となるブロッキング接着フィルム２２は、ブロッキング接着している外側フィルム３及び内側フィルム４からなる層（以下、「ブロッキング接着層」とする場合もある。）からなるフィルムのほか、かかるブロッキング接着層に外側フィルム３としてさらに他の層を積層したフィルムも含む。   The blocking adhesive film 22 to be the multiple film 2 is not only a film composed of a layer composed of the outer film 3 and the inner film 4 (hereinafter, may be referred to as “blocking adhesive layer”) which are blocking-adhered, and such blocking adhesive. The film which laminated | stacked another layer as the outer film 3 on the layer is also included.

図９は、ブロッキング接着フィルム２２において、外側フィルム３を３層とした場合の層構成を示した断面図である。図９中、３は外側フィルム、４は内側フィルム、３１は内層、３２は中間層、３３は外層、Ｂはブロッキング接着されている面、をそれぞれ示す。図９に示すように、ブロッキング接着フィルム２２にあっては、内側フィルム４における外側フィルム３に接する面と、外側フィルム３を構成する層で内側フィルム４と接する面（内層３１の面）がブロッキング接着することになる。また、ブロッキング接着フィルム２２にあっては、内側フィルム４が、背シール部６や横シール部７を構成する際に、重ね合わされて、直接接して溶着されることになる。   FIG. 9 is a cross-sectional view showing the layer structure of the blocking adhesive film 22 when the outer film 3 has three layers. In FIG. 9, 3 is an outer film, 4 is an inner film, 31 is an inner layer, 32 is an intermediate layer, 33 is an outer layer, and B is a surface that is blocking-bonded. As shown in FIG. 9, in the blocking adhesive film 22, the surface in contact with the outer film 3 in the inner film 4 and the surface in contact with the inner film 4 in the layer constituting the outer film 3 (the surface of the inner layer 31) are blocking. It will be glued. Moreover, in the blocking adhesive film 22, when the inner film 4 comprises the back seal | sticker part 6 and the horizontal seal | sticker part 7, it will overlap and will be welded in direct contact.

ブロッキング接着フィルム２２におけるブロッキング接着層を構成する樹脂（内側フィルム４と、外側フィルム３における内層３１）としては、ヒートシール性を有することが好ましく、例えば、前記した（１）で挙げたポリエチレン系樹脂や、ポリプロピレン系樹脂等のポリオレフィン系樹脂を使用することができる。また、かかるポリオレフィン系樹脂のうち、ポリエチレン系樹脂を用いることが好ましく、この中でも、ヒートシール性等に優れた、低密度ポリエチレン（ＬＤＰＥ）を用いることがさらに好ましく、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を用いることが特に好ましい。   The resin constituting the blocking adhesive layer in the blocking adhesive film 22 (the inner film 4 and the inner layer 31 in the outer film 3) preferably has heat-sealing properties. For example, the polyethylene resin mentioned in the above (1) Alternatively, a polyolefin resin such as a polypropylene resin can be used. Of these polyolefin resins, polyethylene resins are preferably used, and among them, it is more preferable to use low density polyethylene (LDPE) excellent in heat sealability and the like, and linear low density polyethylene (LLDPE). ) Is particularly preferred.

また、外側フィルム３における外層３３や中間層３２を構成する樹脂としては、多重フィルム２に耐ピンホール性や機械的特性を付与すべく、例えば、前記した（１）で挙げたポリエチレン系樹脂や、ポリプロピレン系樹脂等のポリオレフィン系樹脂のほか、例えば、ポリアミド系樹脂（ナイロン）、ポリエステル系樹脂（ＰＥＴ、ＰＢＴ）、エチレン−ビニルアルコール共重合体等を使用することができる。   Moreover, as resin which comprises the outer layer 33 and the intermediate | middle layer 32 in the outer side film 3, in order to provide pinhole resistance and mechanical characteristics to the multiplex film 2, for example, the polyethylene-type resin mentioned above (1), In addition to polyolefin resins such as polypropylene resins, for example, polyamide resins (nylon), polyester resins (PET, PBT), ethylene-vinyl alcohol copolymers, and the like can be used.

また、前記したチューブ状フィルム２１と同様、外側フィルム３の中間層３２として易引裂樹脂からなる易引裂樹脂層を形成することが好ましい。易引裂樹脂層としては、例えば、環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる層を用いるようにしてもよい。かかる環状ポリオレフィン樹脂を含有する層を中間層３２として介在させることにより、多重フィルム２の易開封性（易引裂性）が向上する。使用可能な環状ポリオレフィン樹脂、ポリオレフィン系樹脂や環状ポリオレフィン樹脂の含有量等については、前記した（１）で説明した環状ポリオレフィン樹脂を含んだ混合樹脂等と共通するので、説明を省略する。   Moreover, it is preferable to form the easy tear resin layer which consists of easy tear resin as the intermediate | middle layer 32 of the outer side film 3 similarly to the above-mentioned tube-shaped film 21. FIG. As the easily tearable resin layer, for example, a layer made of a mixed resin of a cyclic polyolefin resin and a polyolefin resin may be used. By interposing the layer containing the cyclic polyolefin resin as the intermediate layer 32, the easy-openability (easy tearing property) of the multiple film 2 is improved. The content of the cyclic polyolefin resin, polyolefin resin, and cyclic polyolefin resin that can be used is the same as that of the mixed resin including the cyclic polyolefin resin described in the above (1), and thus the description thereof is omitted.

ブロッキング接着フィルム２２を用いるにあたり、外側フィルム３を図９に示した３層の構成とする場合、外側フィルム３は、多重袋１の外側から順に、ポリオレフィン系樹脂からなる層（ポリオレフィン系樹脂層）／環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる層（混合樹脂層）／直鎖状低密度ポリエチレンからなる層（直鎖状低密度ポリエチレン層）、内側フィルムは、直鎖状低密度ポリエチレン層とすることが好ましい。外側フィルム３及び内側フィルム４をかかる構成とすることにより、ヒートシール性、耐ピンホール性等を維持した状態で、易開封性（易引裂性）を付与することができる。   In using the blocking adhesive film 22, when the outer film 3 has a three-layer structure shown in FIG. 9, the outer film 3 is a layer made of a polyolefin resin (polyolefin resin layer) in order from the outside of the multiple bag 1. / Layer made of mixed resin of cyclic polyolefin resin and polyolefin resin (mixed resin layer) / Layer made of linear low density polyethylene (linear low density polyethylene layer), inner film is linear low density polyethylene layer It is preferable that By setting the outer film 3 and the inner film 4 as such a configuration, easy-openability (easy tearing property) can be imparted while maintaining heat sealability, pinhole resistance, and the like.

また、環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる層は、多層の外側フィルム３において、中間層３２以外の層としても問題はなく、チューブ状フィルムと２１同様である。   In addition, the layer made of the mixed resin of the cyclic polyolefin resin and the polyolefin-based resin has no problem even if it is a layer other than the intermediate layer 32 in the multilayer outer film 3 and is the same as the tubular film 21.

ブロッキング接着されるブロッキング接着層の形成方法は、特に制限はなく、従来公知の技術を用いることができるが、例えば、単層押出インフレーション法によりインフレーションフィルムを製造するときに押し出したチューブ状フィルムを折り畳んで重ね、引取り用ニップロールまたは引取り用ニップロールの後に新たに設けた圧着ロールで、オンラインで圧接してフィルムの内面同士をブロッキングさせてロール状に捲き取る方法等により製造することができる。また、別の方法としては、ブロッキングさせることなく別々に巻き取ったフィルムをオフラインで捲出してブロッキングさせる層同士を重ね合わせて引揃え、加熱した加圧ロール間を通して熱圧着してブロッキングさせる方法等があるが、操作の簡便性、コスト等の点から、前記したインフレーション成形と同時に圧着させてブロッキンクさせる方法を用いることが好ましい。   The method for forming the blocking adhesive layer to be blocked is not particularly limited, and a conventionally known technique can be used. For example, a tubular film extruded when a blown film is produced by a single-layer extrusion inflation method is folded. It is possible to manufacture by a method such as a method in which the inner surfaces of the film are blocked by online pressure-contacting with an on-line press and a take-up nip roll or a pressure-bonding roll newly provided after the take-up nip roll, and then wound into a roll. In addition, as another method, a film wound up separately without blocking is rolled off and the layers to be blocked are overlapped and aligned, and the film is blocked by thermocompression bonding between heated pressure rolls, etc. However, from the viewpoint of ease of operation, cost, and the like, it is preferable to use a method in which the above-described inflation molding is pressure-bonded and blocked.

ここで、ブロッキング接着のし易さは、使用される樹脂（ポリオレフィン系樹脂等）の種類や密度、滑剤やアンチブロッキング剤等の添加剤の種類や量等によって適宜変更される。一般に、樹脂の密度が高く、添加剤の量が多くなるほどブロッキングし難くなる。また、インフレーション法により製膜して折畳んだフィルムのブロッキング接着強度を調整するために、折畳んだチューブ状フィルムがニップロールや圧着ロール、エンボスロール、加熱ロール等のロールを通過する前に、フィルムを遠赤外線ランプやニクロム線ヒーターなどの加熱手段を用いて加熱してもよい。   Here, the ease of blocking adhesion is appropriately changed depending on the type and density of the resin (polyolefin resin, etc.) used, the type and amount of additives such as lubricants and antiblocking agents, and the like. Generally, the higher the density of the resin and the greater the amount of additive, the more difficult it becomes to block. In addition, in order to adjust the blocking adhesive strength of the film that has been formed and folded by the inflation method, the folded tube-shaped film is passed through a roll such as a nip roll, a pressure-bonding roll, an embossing roll, or a heating roll. May be heated using a heating means such as a far-infrared lamp or a nichrome wire heater.

なお、ブロッキング接着する２層の接着強度は、少なくともフィルム積層工程やスリット工程、製袋あるいは自動充填製袋工程でブロッキングの意図しない剥離が生じて機械適性を損なわない程度の強さであればよい。これについては前記（１）チューブ状フィルムで内層３１，４１同士をブロッキング接着させる場合も同様である。   In addition, the adhesive strength of the two layers to be bonded to the blocking layer only needs to be strong enough not to impair mechanical suitability due to unintentional blocking peeling in the film laminating step, slitting step, bag making or automatic filling bag making step. . The same applies to the case (1) where the inner layers 31 and 41 are subjected to blocking adhesion with the tubular film.

ブロッキング接着層と他の層を積層するには、例えば、所定の接着剤や接着性樹脂を介して接着するドライラミネーション法、無溶剤ラミネーション法、ホットメルトラミネーション法、押出ラミネーション法等が用いられる。例えば、ドライラミネーション法による場合、１液性または２液性のポリウレタン系接着剤を用いるのが一般的であるが、これには制限されず、ラミネートする層を構成する樹脂の種類等に応じて、接着剤の種類を適宜選択するようにすればよい。接着性樹脂としては、ＥＶＡ、アイオノマーＰＥ、ＥＡＡ、ＥＭＡＡ、各種変性樹脂等の公知の接着性樹脂を使用するようにしてもよい。   In order to laminate the blocking adhesive layer and the other layers, for example, a dry lamination method, a solventless lamination method, a hot melt lamination method, an extrusion lamination method, or the like, which is bonded through a predetermined adhesive or adhesive resin, is used. For example, in the case of the dry lamination method, it is common to use a one-component or two-component polyurethane adhesive, but this is not a limitation, and depending on the type of resin constituting the layer to be laminated, etc. The type of the adhesive may be selected as appropriate. As the adhesive resin, known adhesive resins such as EVA, ionomer PE, EAA, EMAA, and various modified resins may be used.

なお、ラミネートするフィルム間の貼合せ接着力を向上するために、ラミネーションに先だって（あるいはラミネーションと同時に）、ラミネートする層のいずれか一方、あるいは両方の貼合接着する面に対して、コロナ放電処理、オゾン処理、アンカーコート剤塗布等による表面処理を施すようにしてもよい。   In order to improve the adhesive strength between the films to be laminated, prior to lamination (or at the same time as the lamination), one or both of the layers to be laminated are subjected to corona discharge treatment. Surface treatment by ozone treatment, anchor coating agent application, or the like may be performed.

（Ｃ）第２実施形態に係る多重袋１：
次に、第２実施形態に係る多重袋１の特徴を説明する。第２実施形態に係る多重袋１は、多重袋１を構成する外側フィルム３と内側フィルム４からなる多重フィルム２のうち、少なくとも外側フィルム３は環状オレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる中間層３２，４２（図８、図９参照。）を有する多層構成である。かかる混合樹脂からなる中間層３２，４２を形成することにより、中間層３２，４２が易引裂樹脂層となり、４枚のフィルム（２枚の多重フィルム２）が集まった背シール部６を容易に引き裂くことができる。以下、多重フィルム２の構成がチューブ状フィルム２１の場合とブロッキング接着フィルム２２の場合に分けて説明する。 (C) Multiple bag 1 according to second embodiment 1:
Next, features of the multiple bag 1 according to the second embodiment will be described. The multiplex bag 1 according to the second embodiment is an intermediate film made of a mixed resin of a cyclic olefin resin and a polyolefin resin among the multiplex film 2 composed of the outer film 3 and the inner film 4 constituting the multiplex bag 1. This is a multilayer structure having layers 32 and 42 (see FIGS. 8 and 9). By forming the intermediate layers 32 and 42 made of such a mixed resin, the intermediate layers 32 and 42 become easily tearable resin layers, and the back seal portion 6 where four films (two multiple films 2) are gathered can be easily formed. Can be torn. Hereinafter, the case where the structure of the multiple film 2 is the tube-shaped film 21 and the case of the blocking adhesive film 22 will be described separately.

（１）多重フィルム２の構成（チューブ状フィルム２１）：
チューブ状フィルム２１は、筒状のフィルムを扁平状にして２枚重ねにした両端が袋状に閉じた対面する２枚のフィルムである。多重フィルム２であるチューブ状フィルム２１は、図３及び図４からもわかるように、外側フィルム３と内側フィルム４の両側端縁が互いに連続しているものであり、外側フィルム３と内側フィルム４が一体化されており、外側フィルム３と内側フィルム４は、共通する樹脂で構成される。 (1) Configuration of multiple film 2 (tubular film 21):
The tube-shaped film 21 is two films facing each other with both ends of a cylindrical film flattened in a flat shape and closed in a bag shape. As can be seen from FIG. 3 and FIG. 4, the tubular film 21 that is the multiple film 2 is one in which both side edges of the outer film 3 and the inner film 4 are continuous with each other, and the outer film 3 and the inner film 4. Are integrated, and the outer film 3 and the inner film 4 are made of a common resin.

図８は、チューブ状フィルム２１において、外側フィルム３及び内側フィルム４を３層とした場合の層構成を示した断面図である。図８中、３は外側フィルム、４は内側フィルム、３１，４１は内層、３２，４２は中間層、３３，４３は外層、Ｃは隙間、をそれぞれ示す。   FIG. 8 is a cross-sectional view showing the layer structure of the tubular film 21 when the outer film 3 and the inner film 4 have three layers. In FIG. 8, 3 is an outer film, 4 is an inner film, 31 and 41 are inner layers, 32 and 42 are intermediate layers, 33 and 43 are outer layers, and C is a gap.

図８に示すように、本実施形態にあって、多重フィルム２をチューブ状フィルム２１とした場合にあっては、外側フィルム３及び内側フィルム４の両方が、環状オレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる中間層３２，４２を有する多層構成となる。かかる環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる層を中間層３２，４２として介在させることにより、中間層３２，４２が易引裂樹脂層となり、多重フィルムの易開封性（易引裂性）が向上する。   As shown in FIG. 8, in this embodiment, when the multiple film 2 is a tube-shaped film 21, both the outer film 3 and the inner film 4 are a mixture of a cyclic olefin resin and a polyolefin resin. A multilayer structure having intermediate layers 32 and 42 made of resin is formed. By interposing a layer composed of a mixed resin of the cyclic polyolefin resin and the polyolefin resin as the intermediate layers 32 and 42, the intermediate layers 32 and 42 become easy tear resin layers, and the easy-openability (easy tearability) of the multiple film is achieved. improves.

図８に一例を示すように、外側フィルム３及び内側フィルム４を多層とする場合は、外側フィルム３及び内側フィルム４は、外側フィルム３及び内側フィルム４の間に形成されている隙間Ｃからみて対称の関係となり、多重袋１の外側から多重袋１の内側までは、多重袋１の外側／外層３３／中間層３２／内層３１（以上が外側フィルム３の層）／隙間Ｃ／内層４１／中間層４２／外層４３（以上が内側フィルム４の層）／多重袋１の内側、となる。そして、外層３３，４３に該当する層が、背シール部６や横シール部７を形成する際に、重ね合わされて、直接接して溶着されることになる。   As shown in an example in FIG. 8, when the outer film 3 and the inner film 4 are multilayered, the outer film 3 and the inner film 4 are viewed from the gap C formed between the outer film 3 and the inner film 4. From the outer side of the multiple bag 1 to the inner side of the multiple bag 1, the outer side of the multiple bag 1 / outer layer 33 / intermediate layer 32 / inner layer 31 (the above is the layer of the outer film 3) / gap C / inner layer 41 / The intermediate layer 42 / the outer layer 43 (the above is the layer of the inner film 4) / the inner side of the multiple bag 1. Then, when the back seal portion 6 and the lateral seal portion 7 are formed, the layers corresponding to the outer layers 33 and 43 are overlapped and welded in direct contact with each other.

チューブ状フィルム２１を構成する樹脂として、中間層３２，４２以外の層を構成する樹脂として、図８において外層３３，４３に相当する層は、その層自体にヒートシール性があることが好ましく、例えば、ポリオレフィン系樹脂が挙げられ、具体的には、高密度ポリエチレン（ＨＤＰＥ）、中密度ポリエチレン（ＭＤＰＥ）、低密度ポリエチレン（ＬＤＰＥ）、直鎖状（線状）低密度ポリエチレン（ＬＬＤＰＥ）、直鎖状超低密度ポリエチレン（ＶＬＤＰＥ）、また、エチレンと共重合可能なビニル化合物との共重合体、例えば、エチレン−酢酸ビニル共重合体（ＥＶＡ）、アイオノマー、エチレン−アクリル酸またはエチレン−アクリル酸エステル共重合体、エチレンメタアクリル酸またはメタアクリル酸エステル共重合体、エチレン−プロピレン共重合体等のポリエチレン系樹脂や、ポリプロピレン系樹脂や、ポリエチレン、ポリプロピレン等のポリオレフィン系樹脂をアクリル酸、メタアクリル酸、無水マレイン酸、フマール酸、その他の不飽和カルボン酸で変成した酸変性ポレオレフィン樹脂等のポリオレフィン系樹脂が挙げられる。これらの樹脂は、その１種を単独で使用してもよく、２種以上を組み合わせて使用するようにしてもよい。   As a resin constituting the layers other than the intermediate layers 32 and 42 as a resin constituting the tubular film 21, the layers corresponding to the outer layers 33 and 43 in FIG. 8 preferably have heat sealability in the layers themselves, For example, polyolefin resin can be mentioned. Specifically, high density polyethylene (HDPE), medium density polyethylene (MDPE), low density polyethylene (LDPE), linear (linear) low density polyethylene (LLDPE), straight Linear very low density polyethylene (VLDPE), and copolymers with vinyl compounds copolymerizable with ethylene, such as ethylene-vinyl acetate copolymer (EVA), ionomers, ethylene-acrylic acid or ethylene-acrylic acid Ester copolymer, ethylene methacrylic acid or methacrylic ester copolymer, ethylene Acid modification by modifying polyethylene resins such as propylene copolymer, polypropylene resins, and polyolefin resins such as polyethylene and polypropylene with acrylic acid, methacrylic acid, maleic anhydride, fumaric acid, and other unsaturated carboxylic acids. Examples include polyolefin resins such as polyolefin resins. One of these resins may be used alone, or two or more thereof may be used in combination.

これらの樹脂のうち、ヒートシール性等が優れた、低密度ポリエチレン（ＬＤＰＥ）を使用することが好ましく、低密度ポリエチレンの中でも、耐ピンホール性を有し、タフで丈夫なため機械的強度等にも優れた直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を使用することが特に好ましい。   Of these resins, it is preferable to use low-density polyethylene (LDPE), which has excellent heat-sealing properties, etc. Among low-density polyethylene, it has pinhole resistance, is tough and strong, and has mechanical strength, etc. In particular, it is particularly preferable to use linear low density polyethylene (LLDPE).

なお、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を用いた場合の物性、機械的強度やヒートシール強度等は、共重合させるα−オレフィンの炭素数により調整される。一般に、炭素数３〜１３個、好ましくは炭素数４〜８個のα−オレフィン、例えばブテン−１、オクテン−１、ヘキセン−１、４−メチルペンテン−１、へプテン−１等が好ましく用いられる。   The physical properties, mechanical strength, heat seal strength, and the like when linear low density polyethylene (LLDPE) is used are adjusted by the number of carbon atoms of the α-olefin to be copolymerized. In general, α-olefins having 3 to 13 carbon atoms, preferably 4 to 8 carbon atoms, such as butene-1, octene-1, hexene-1, 4-methylpentene-1, heptene-1, etc. are preferably used. It is done.

低密度ポリエチレン（直鎖状低密度ポリエチレンを含む。）の密度は、０．８７０〜０．９３５ｇ／ｃｍ３であることが好ましい。密度がかかる範囲の低密度ポリエチレンを用いることにより、ヒートシール性等の諸特性が維持される。低密度ポリエチレンの密度は、０．８８０〜０．９２０ｇ／ｃｍ３であることが特に好ましい。なお、１９０℃におけるメルトフローレート（ＭＦＲ）は、０．１〜３０．０ｇ／１０分とすることが好ましく、０．５〜４．０ｇ／１０分とすることが特に好ましい。   The density of the low density polyethylene (including the linear low density polyethylene) is preferably 0.870 to 0.935 g / cm 3. Various characteristics such as heat sealability are maintained by using low density polyethylene in a range where the density is high. The density of the low density polyethylene is particularly preferably from 0.880 to 0.920 g / cm 3. The melt flow rate (MFR) at 190 ° C. is preferably 0.1 to 30.0 g / 10 minutes, and particularly preferably 0.5 to 4.0 g / 10 minutes.

また、図８において、内層３１，４１に相当する層を構成する樹脂としては、多重フィルム２に耐ピンホール性や機械的特性を付与すべく、前記したポリエチレン系樹脂、ポリプロピレン系樹脂等のポリオレフィン系樹脂のほか、ポリアミド系樹脂（ナイロン）、ポリエステル系樹脂（ＰＥＴ、ＰＢＴ）、エチレン−ビニルアルコール共重合体等を使用することができる。   Further, in FIG. 8, as the resin constituting the layers corresponding to the inner layers 31 and 41, polyolefins such as the above-described polyethylene resins and polypropylene resins are provided so as to give the multiple film 2 pinhole resistance and mechanical properties. In addition to resin, polyamide resin (nylon), polyester resin (PET, PBT), ethylene-vinyl alcohol copolymer and the like can be used.

中間層３２，４２となる混合樹脂を構成する環状ポリオレフィン樹脂は、前記（Ｂ）（１）等で説明した環状ポリオレフィン樹脂と共通するので、説明を省略する。   Since the cyclic polyolefin resin constituting the mixed resin to be the intermediate layers 32 and 42 is the same as the cyclic polyolefin resin described in (B) (1) and the like, description thereof is omitted.

混合樹脂において、環状ポリオレフィン樹脂と組み合わせて用いる樹脂としては、前記したポリエチレン系樹脂や、ポリプロピレン系樹脂等のポリオレフィン系樹脂を用いることができる。この中でも、ポリエチレン系樹脂が好ましく、低密度ポリエチレン（ＬＤＰＥ）がさらに好ましく、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）が特に好ましい。   In the mixed resin, as the resin used in combination with the cyclic polyolefin resin, the above-described polyethylene resins and polyolefin resins such as polypropylene resins can be used. Among these, polyethylene resins are preferable, low density polyethylene (LDPE) is more preferable, and linear low density polyethylene (LLDPE) is particularly preferable.

混合樹脂における環状ポリオレフィン樹脂の含有量は、混合樹脂全体（環状ポリオレフィン樹脂及び当該環状ポリオレフィン樹脂と組み合わせて用いられる樹脂との合計を指す。）に対して３〜９９質量％とすることが好ましい。環状ポリオレフィン樹脂の含有量をかかる範囲とすることにより、易引裂性が良好に実施されることになる。環状ポリオレフィン樹脂の含有量は、混合樹脂全体に対して６０〜９０質量％とすることがさらに好ましく、６０〜８０質量％とすることが特に好ましい。   The content of the cyclic polyolefin resin in the mixed resin is preferably 3 to 99% by mass with respect to the entire mixed resin (the total of the cyclic polyolefin resin and the resin used in combination with the cyclic polyolefin resin). By setting the content of the cyclic polyolefin resin within such a range, the easy tearability is favorably implemented. The content of the cyclic polyolefin resin is more preferably 60 to 90% by mass, and particularly preferably 60 to 80% by mass with respect to the entire mixed resin.

外側フィルム３や内側フィルム４を図８に示した３層の構成とする場合、外側フィルム３は、多重袋１の外側から順に、直鎖状低密度ポリエチレンからなる層（直鎖状低密度ポリエチレン層）／環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる層（混合樹脂層）／ポリオレフィン系樹脂からなる層（ポリオレフィン系樹脂層）、内側フィルムは、多重袋１の外側（前記した隙間Ｃ）から順に、ポリオレフィン系樹脂層／混合樹脂層／直鎖状低密度ポリエチレン層とすることが好ましい。外側フィルム及び内側フィルムをかかる構成とすることにより、ヒートシール性、耐ピンホール性等を維持した状態で、易開封性（易引裂性）を付与することができる。   When the outer film 3 and the inner film 4 have the three-layer configuration shown in FIG. 8, the outer film 3 is a layer made of linear low-density polyethylene in order from the outside of the multiple bag 1 (linear low-density polyethylene). Layer) / layer made of mixed resin of cyclic polyolefin resin and polyolefin resin (mixed resin layer) / layer made of polyolefin resin (polyolefin resin layer), inner film is the outer side of the multiple bag 1 (the aforementioned gap C) It is preferable that the polyolefin resin layer / mixed resin layer / linear low-density polyethylene layer be used in this order. By setting the outer film and the inner film as such, easy-opening property (easy tearing property) can be imparted while maintaining heat sealability, pinhole resistance and the like.

多重フィルム２であるチューブ状フィルム２１を製造するには、例えば、インフレーションフィルム法で得るのが好ましい。インフレーションフィルムは、あらかじめチューブ状（筒状）となっており、製造されたままの状態で使用でき、後工程でフィルムを筒状にする必要がなく継ぎ目も生じないというメリットもある。加えて、インフレーションフィルムは厚さが薄いフィルムはもちろんのこと、厚さが比較的厚いフィルムを容易に製造可能である。   In order to manufacture the tube-shaped film 21 which is the multiple film 2, it is preferable to obtain by the inflation film method, for example. The inflation film is in the form of a tube (cylinder) in advance, and can be used as manufactured, and there is an advantage that the film does not need to be formed into a cylinder in the subsequent process and no seam is produced. In addition, it is possible to easily produce a relatively thick film as well as a thin film.

一般的なインフレーションフィルム法としては、例えば、押出機からダイを経てチューブ状に押し出された溶融樹脂を垂直方向に引き上げ、かかる溶融樹脂を垂直方向に引き上げられる過程で供給される空気により膨らませてチューブ状とし、空冷しながらフラットなフィルムにして巻取装置に巻き取ることで、チューブ状フィルム２１を扁平状に巻いたロールを得ることができる。   As a general inflation film method, for example, a molten resin extruded in a tube shape from a extruder through a die is pulled up in the vertical direction, and the molten resin is expanded by air supplied in the process of being pulled up in the vertical direction. It is possible to obtain a roll in which the tubular film 21 is wound in a flat shape by forming a flat film while air cooling and winding it on a winding device.

なお、多重フィルム２をチューブ状フィルム２１とした場合にあっては、外側フィルム３及び内側フィルム４における外側に現れず接触する層（前記した図８における内層３１，４１）については、相互にブロッキング接着していることが好ましい。ここで、「相互にブロッキング接着している」とは、接触しているフィルム同士が接着剤等の他の媒体や熱融着により接着されて完全に一体化されているものではなく、接触しているフィルム同士が疑似接着して柔軟な状態であることを指す。ブロッキング接着は、フィルムの全面にわたって発生していてもよいし、フィルムの一部に部分的に発生していてもよい。ブロッキング接着させることにより、製袋等の際に外側フィルム３と内側フィルム４が一体化し、取り扱い性が良好となる。   In the case where the multiple film 2 is a tube-shaped film 21, the outer film 3 and the inner film 4 that do not appear on the outer side and contact with each other (the inner layers 31 and 41 in FIG. 8 described above) block each other. It is preferable to adhere. Here, “blocking to each other” means that the films in contact with each other are not completely integrated by being bonded by another medium such as an adhesive or by heat-sealing. It means that the films are in a flexible state by pseudo-bonding. Blocking adhesion may occur over the entire surface of the film, or may occur partially on a part of the film. By carrying out blocking adhesion, the outer film 3 and the inner film 4 are integrated during bag making or the like, and the handleability is improved.

チューブ状フィルム２１をブロッキング接着させるためには、例えば、前記したインフレーションフィルム法によって製膜されたポリオレフィン系のチューブ状フィルムを折畳みニップロール等で加圧して重ね合わせたフィルム間の空気を押出しながら１つ折りの扁平な２層フィルムとして巻き取ることによって、簡便に製造することができる。   In order to block-bond the tube-shaped film 21, for example, the polyolefin-based tube-shaped film formed by the above-described inflation film method is folded and pressed with a nip roll or the like, and folded while extruding air between the overlapped films. It can manufacture simply by winding up as a flat 2 layer film.

（２）多重フィルム２の構成（ブロッキング接着フィルム２２）：
次に、多重フィルム２をブロッキング接着フィルム２２とした場合について説明する。多重フィルム２としては、別途独立した外側フィルム３と内側フィルム４がブロッキング接着している構成のもの（ブロッキング接着フィルム）を使用することができる。 (2) Configuration of multiple film 2 (blocking adhesive film 22):
Next, the case where the multiple film 2 is the blocking adhesive film 22 will be described. As the multiple film 2, it is possible to use a film (blocking adhesive film) in which an independent outer film 3 and an inner film 4 are blocking-bonded.

ここで、「ブロッキング接着」については、前記した通りであり、接触しているフィルム同士が接着剤等の他の媒体や熱融着により接着されて完全に一体化されているものではなく、フィルム接触しているフィルム同士が疑似接着して柔軟な状態であることを指す。ブロッキング接着は、フィルムの全面にわたって発生していてもよいし、フィルムの一部に部分的に発生していてもよい。ブロッキング接着させることにより、製袋等の際に外側フィルム３と内側フィルム４が一体化し、取り扱い性が良好となる。   Here, “blocking adhesion” is as described above, and the films in contact with each other are not completely integrated by being bonded by another medium such as an adhesive or by heat fusion. It means that the films in contact are pseudo-bonded and in a flexible state. Blocking adhesion may occur over the entire surface of the film, or may occur partially on a part of the film. By carrying out blocking adhesion, the outer film 3 and the inner film 4 are integrated during bag making or the like, and the handleability is improved.

多重フィルム２となるブロッキング接着フィルム２２は、本実施形態にあっては、ブロッキング接着している外側フィルム３（図９の内層３１）及び内側フィルム４からなる層（以下、「ブロッキング接着層」とする場合もある。）と、外側フィルム３として、さらに環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる中間層３２、及び外層３３を積層した構成となる。   In the present embodiment, the blocking adhesive film 22 to be the multiple film 2 is a layer composed of the outer film 3 (inner layer 31 in FIG. 9) and the inner film 4 (hereinafter referred to as “blocking adhesive layer”). The outer film 3 has a structure in which an intermediate layer 32 made of a mixed resin of a cyclic polyolefin resin and a polyolefin resin and an outer layer 33 are further laminated.

図９は、ブロッキング接着フィルム２２において、外側フィルム３を３層とした場合の層構成を示した断面図である。図９中、３は外側フィルム、４は内側フィルム、３１は内層、３２は中間層、３３は外層、Ｂはブロッキング接着されている面、をそれぞれ示す。図９に示すように、ブロッキング接着フィルム２２にあっては、内側フィルム４における外側フィルム３（の内層３１）に接する面と、外側フィルム３を構成する内層３１における内側フィルム４と接する面がブロッキング接着することになる。また、ブロッキング接着フィルム２２にあっては、内側フィルム４が、背シール部６や横シール部７を構成する際に、重ね合わされて、直接接して溶着されることになる。   FIG. 9 is a cross-sectional view showing the layer structure of the blocking adhesive film 22 when the outer film 3 has three layers. In FIG. 9, 3 is an outer film, 4 is an inner film, 31 is an inner layer, 32 is an intermediate layer, 33 is an outer layer, and B is a surface that is blocking-bonded. As shown in FIG. 9, in the blocking adhesive film 22, the surface in contact with the outer film 3 (inner layer 31 thereof) in the inner film 4 and the surface in contact with the inner film 4 in the inner layer 31 constituting the outer film 3 are blocked. It will be glued. Moreover, in the blocking adhesive film 22, when the inner film 4 comprises the back seal | sticker part 6 and the horizontal seal | sticker part 7, it will overlap and will be welded in direct contact.

外側フィルム３における環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる中間層３２を構成する環状ポリオレフィン樹脂やポリオレフィン系樹脂、混合樹脂における環状ポリオレフィン樹脂の含有量等については、前記した（１）チューブ状フィルムを構成する環状ポリオレフィン樹脂やポリオレフィン系樹脂、混合樹脂における環状ポリオレフィン樹脂の含有量等と共通するので（前記（Ｂ）でも説明。）、説明を省略する。   The content of the cyclic polyolefin resin, the polyolefin resin, and the cyclic polyolefin resin in the mixed resin constituting the intermediate layer 32 composed of the mixed resin of the cyclic polyolefin resin and the polyolefin resin in the outer film 3 is as described in (1) Tubular Since it is the same as the content of the cyclic polyolefin resin, the polyolefin-based resin, and the content of the cyclic polyolefin resin in the mixed resin (described in the above (B)), the description is omitted.

ブロッキング接着フィルム２２におけるブロッキング接着層を構成する樹脂（内側フィルム４と、外側フィルム３における内層３１）としては、例えば、前記した（１）で挙げたポリオレフィン系樹脂を使用することができる。また、かかるポリオレフィン系樹脂のうち、ポリエチレン系樹脂を用いることが好ましく、低密度ポリエチレン（ＬＤＰＥ）を用いることがさらに好ましく、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を用いることが特に好ましい。   As the resin constituting the blocking adhesive layer in the blocking adhesive film 22 (the inner film 4 and the inner layer 31 in the outer film 3), for example, the polyolefin resin mentioned in the above (1) can be used. Of such polyolefin resins, polyethylene resins are preferably used, low density polyethylene (LDPE) is more preferably used, and linear low density polyethylene (LLDPE) is particularly preferably used.

また、外側フィルム３における外層３３を構成する樹脂としては、多重フィルム２に耐ピンホール性や機械的特性を付与すべく、前記したポリエチレン系樹脂、ポリプロピレン系樹脂等のポリオレフィン系樹脂のほか、ポリアミド系樹脂（ナイロン）、ポリエステル系樹脂（ＰＥＴ、ＰＢＴ）、エチレン−ビニルアルコール共重合体等を使用することができる。   Further, as the resin constituting the outer layer 33 in the outer film 3, in order to impart pinhole resistance and mechanical characteristics to the multiple film 2, in addition to polyolefin resins such as polyethylene resins and polypropylene resins, polyamide Resin (nylon), polyester resin (PET, PBT), ethylene-vinyl alcohol copolymer, etc. can be used.

ブロッキング接着フィルム２２を用いるにあたり、外側フィルム３を図９に示した３層の構成とする場合、外側フィルム３は、多重袋１の外側から順に、ポリオレフィン系樹脂からなる層（ポリオレフィン系樹脂層）／環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる層（混合樹脂層）／直鎖状低密度ポリエチレンからなる層（直鎖状低密度ポリエチレン層）、内側フィルムは、直鎖状低密度ポリエチレン層とすることが好ましい。外側フィルム３及び内側フィルム４をかかる構成とすることにより、ヒートシール性、耐ピンホール性等を維持した状態で、易開封性（易引裂性）を付与することができる。   In using the blocking adhesive film 22, when the outer film 3 has a three-layer structure shown in FIG. 9, the outer film 3 is a layer made of a polyolefin resin (polyolefin resin layer) in order from the outside of the multiple bag 1. / Layer made of mixed resin of cyclic polyolefin resin and polyolefin resin (mixed resin layer) / Layer made of linear low density polyethylene (linear low density polyethylene layer), inner film is linear low density polyethylene layer It is preferable that By setting the outer film 3 and the inner film 4 as such a configuration, easy-openability (easy tearing property) can be imparted while maintaining heat sealability, pinhole resistance, and the like.

ブロッキング接着されるブロッキング接着層は、例えば、単層押出インフレーション法によりインフレーションフィルムを製造するときに押し出したチューブ状フィルムを折畳んで重ね、引取り用ニップロールまたは引取り用ニップロールの後に新たに設けた圧着ロールで、オンラインで圧接してフィルムの内面同士をブロッキングさせてロール状に捲き取る方法等により製造することができる。また、別の方法としては、ブロッキングさせることなく別々に巻き取ったフィルムをオフラインで捲出してブロッキングさせる層同士を重ね合わせて引揃え、加熱した加圧ロール間を通して熱圧着してブロッキングさせる方法等があるが、操作の簡便性、コスト等の点から、前記したインフレーション成形と同時に圧着させてブロッキンクさせる方法を用いることが好ましい。   The blocking adhesive layer to be blocking-adhered is, for example, a tubular film extruded when a blown film is produced by a single-layer extrusion inflation method, folded and overlapped, and newly provided after the take-up nip roll or the take-up nip roll. It can be manufactured by a method such as a method in which a pressure roll is pressed online to block the inner surfaces of the film and are wound up into a roll. In addition, as another method, a film wound up separately without blocking is rolled off and the layers to be blocked are overlapped and aligned, and the film is blocked by thermocompression bonding between heated pressure rolls, etc. However, from the viewpoint of ease of operation, cost, and the like, it is preferable to use a method in which the above-described inflation molding is pressure-bonded and blocked.

重ね合わせるフィルムのブロッキング接着のし易さは、使用される樹脂（ポリオレフィン系樹脂等）の種類や密度、滑剤やアンチブロッキング剤等の添加剤の種類や量等によって適宜変更される。一般に、樹脂の密度が高く、添加剤の量が多くなるほどブロッキングし難くなる。また、インフレーション法により製膜して折畳んだフィルムのブロッキング接着強度を調整するために、折畳んだチューブ状フィルムがニップロールや圧着ロール、エンボスロール、加熱ロール等のロールを通過する前に、フィルムを遠赤外線ランプやニクロム線ヒーターなどの加熱手段を用いて加熱してもよい。   The ease of blocking adhesion of the films to be overlaid is appropriately changed depending on the type and density of the resin (polyolefin resin, etc.) used, the type and amount of additives such as lubricants and antiblocking agents, and the like. Generally, the higher the density of the resin and the greater the amount of additive, the more difficult it becomes to block. In addition, in order to adjust the blocking adhesive strength of the film that has been formed and folded by the inflation method, the folded tube-shaped film is passed through a roll such as a nip roll, a pressure-bonding roll, an embossing roll, or a heating roll. May be heated using a heating means such as a far-infrared lamp or a nichrome wire heater.

なお、ブロッキング接着する２層の接着強度は、少なくともフィルム積層工程やスリット工程、製袋あるいは自動充填製袋工程でブロッキングの意図しない剥離が生じて機械適性を損なわない程度の強さであればよい。これについては前記（１）で内層３１，４１同士をブロッキング接着させる場合も同様である。   In addition, the adhesive strength of the two layers to be bonded to the blocking layer only needs to be strong enough not to impair mechanical suitability due to unintentional blocking peeling in the film laminating step, slitting step, bag making or automatic filling bag making step. . The same applies to the case where the inner layers 31 and 41 are subjected to blocking adhesion in the above (1).

ブロッキング接着層と他の層を積層するには、例えば、所定の接着剤を介して接着するドライラミネーション法、無溶剤ラミネーション法、ホットメルトラミネーション法、押出ラミネーション法等が用いられる。例えば、ドライラミネーション法による場合、１液性または２液性のポリウレタン系接着剤を用いるのが一般的であるが、これには制限されず、ラミネートする層を構成する樹脂の種類等に応じて、接着剤の種類を適宜選択するようにすればよい。   In order to laminate the blocking adhesive layer and the other layers, for example, a dry lamination method, a solventless lamination method, a hot melt lamination method, an extrusion lamination method, or the like, which is bonded through a predetermined adhesive, is used. For example, in the case of the dry lamination method, it is common to use a one-component or two-component polyurethane adhesive, but this is not a limitation, and depending on the type of resin constituting the layer to be laminated, etc. The type of the adhesive may be selected as appropriate.

なお、ラミネートするフィルム間の貼合せ接着力を向上するために、ラミネーションに先だって（あるいはラミネーションと同時に）、ラミネートする層のいずれか一方、あるいは両方の貼合接着する面に対して、コロナ放電処理、オゾン処理、アンカーコート剤塗布等による表面処理を施すようにしてもよい。   In order to improve the adhesive strength between the films to be laminated, prior to lamination (or at the same time as the lamination), one or both of the layers to be laminated are subjected to corona discharge treatment. Surface treatment by ozone treatment, anchor coating agent application, or the like may be performed.

なお、環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる層は、多層の外側フィルムにおいて、中間層以外の層としても問題はなく、これについてもチューブ状フィルムと同様である。   In addition, the layer which consists of mixed resin of cyclic polyolefin resin and polyolefin resin does not have a problem also as layers other than an intermediate | middle layer in a multilayer outer film, This is the same as that of a tubular film.

（３）引裂開始部５１について：
次に、本実施形態に係る多重袋に形成される引裂開始部５１について説明する。本発明の第２実施形態に係る多重袋１は、図１及び図２に示すように、多重フィルム２の両端を内側フィルム４同士が対向するように重ね合わせた合掌部５に対して、引裂開始部５１が形成されている。引裂開始部５１は、横シール部７に対して略平行に開封するために形成され、例えば、横シール部７に対して略平行となるように形成すれば、使用者が横シール部７に対して略平行に開封しやすくなる。 (3) About the tear start part 51:
Next, the tear start part 51 formed in the multiple bag according to the present embodiment will be described. As shown in FIGS. 1 and 2, the multiple bag 1 according to the second embodiment of the present invention is torn against the palm portion 5 in which both ends of the multiple film 2 are overlapped so that the inner films 4 face each other. A start portion 51 is formed. The tear start portion 51 is formed to open substantially parallel to the lateral seal portion 7. For example, if the tear start portion 51 is formed so as to be substantially parallel to the lateral seal portion 7, the user can contact the lateral seal portion 7. On the other hand, it becomes easy to open it substantially parallel.

合掌部５に形成される引裂開始部５１は、初期の引き裂き強度を弱め、易開封性を向上させる。引裂開始部５１は、スリット（切れ目）、Ｖノッチ、Ｉノッチ、ミシン目、微多孔の集合体、等の任意の形状とすることができる。   The tear start part 51 formed in the palm part 5 weakens the initial tear strength and improves easy-openability. The tear start portion 51 can have an arbitrary shape such as a slit (cut), a V notch, an I notch, a perforation, or a microporous aggregate.

引裂開始部５１は、図１及び図２に示すように、合掌部の外縁５２から少なくとも背シール部６まで達するように形成されることが好ましい。引裂開始部５１が背シール部６まで達するようにすれば、開封時の引き裂きの繰り出しをスムースに行うことができ、多重フィルム２が集まった背シール部６を容易に引き裂くことができる、易開封性に優れた多重袋１となる。また、引裂開始部５１の長さとしては、特に制限はないが、概ね５〜２０ｍｍであればよい。   As shown in FIGS. 1 and 2, the tear start portion 51 is preferably formed so as to reach at least the back seal portion 6 from the outer edge 52 of the palm portion. If the tear start portion 51 reaches the back seal portion 6, the tear can be smoothly drawn out at the time of opening, and the back seal portion 6 in which the multiple films 2 are gathered can be easily torn. It becomes the multiple bag 1 excellent in property. Moreover, there is no restriction | limiting in particular as the length of the tear start part 51, However, What is necessary is just about 5-20 mm in general.

また、引裂開始部５１は、細幅線状の背シール部６を複数形成された場合にあっては、図７のようにしてもよい。図７は、多重袋１の他の態様を示した正面図である。図７にあっては、背シール部６が合掌部５に対して細幅線状に２本形成されている態様を示している。このように、細幅線状の背シール部６を複数形成した場合にあっては、引裂開始部５１は複数の細幅線状の背シール部６のうち少なくとも合掌部の外縁５２側に形成された背シール部６１に達するように形成されている。なお、本発明にあって、細幅線状の背シール部６，６１は、ヒートシール（溶着）により、概ね２〜１０ｍｍ程度の幅からなる略直線状に形成された背シール部６を指す。また、複数の背シール部６，６１の数は、概ね２〜５とすればよい。   Further, the tear starting portion 51 may be configured as shown in FIG. 7 when a plurality of narrow line-shaped back seal portions 6 are formed. FIG. 7 is a front view showing another aspect of the multiple bag 1. FIG. 7 shows an aspect in which two back seal portions 6 are formed in a narrow line shape with respect to the palm portion 5. As described above, when a plurality of narrow line-shaped back seal portions 6 are formed, the tear start portion 51 is formed on the outer edge 52 side of at least the palm portion of the plurality of narrow line-shaped back seal portions 6. It is formed so as to reach the back seal portion 61 made. In addition, in this invention, the narrow line-shaped back seal parts 6 and 61 point out the back seal part 6 formed in the substantially linear form which has a width | variety about 2-10 mm by heat sealing (welding). . Moreover, what is necessary is just to make the number of the some back seal parts 6 and 61 into 2-5 in general.

（Ｄ）多重袋１の製造方法（第１実施形態（第１発明）、第２実施形態（第２発明）共通
）：
多重フィルム２を用いた、図１に示した構成の本発明に係る多重袋１は、例えば、縦ピロー型製袋機等を使用して製造することができる。一例を説明すると、多重フィルム２を巻回したロールから多重フィルム２を供給し、供給された多重フィルム２を、案内ロール群を経由させた後、フォーマー等により筒状に成形し、背シールバーで背シール部６を形成してから充填物を充填した後、横シールバーで横シール部７が形成すると同時に切断することにより、図１等に示した多重袋１を簡便に得ることができる。 (D) Manufacturing method of multiple bag 1 (common to first embodiment (first invention) and second embodiment (second invention)):
The multiple bag 1 according to the present invention having the configuration shown in FIG. 1 using the multiple film 2 can be manufactured by using, for example, a vertical pillow type bag making machine. For example, the multiple film 2 is supplied from a roll around which the multiple film 2 is wound, and the supplied multiple film 2 is passed through a guide roll group, and then formed into a cylindrical shape by a former or the like, and a back seal bar. After the back seal portion 6 is formed, the filling is filled, and then the horizontal seal portion 7 is formed at the same time as the horizontal seal bar is cut, so that the multiple bag 1 shown in FIG. .

（Ｅ）多重袋を構成する多重フィルムの厚さ（第１実施形態（第１発明）、第２実施形態
（第２発明）共通）：
本発明に係る多重袋１において、多重フィルム２における外側フィルム３、内側フィルム４の厚さは、３０〜１５０μｍとすることが好ましい。また、図８及び図９に示すような３層構成にする場合にあっては、内層３１，４１や外層３３，４３は、概ね１０〜７０μｍとすることが好ましく、中間層３２，４２は、概ね７〜３０μｍとすることが好ましい。 (E) Thickness of the multiple film constituting the multiple bag (common to the first embodiment (first invention) and the second embodiment (second invention)):
In the multiple bag 1 according to the present invention, the thickness of the outer film 3 and the inner film 4 in the multiple film 2 is preferably 30 to 150 μm. 8 and 9, the inner layers 31, 41 and the outer layers 33, 43 are preferably about 10 to 70 μm, and the intermediate layers 32, 42 are It is preferably about 7 to 30 μm.

（Ｆ）本発明の効果：
以上説明した本発明の第１実施形態に係る多重袋１は、外側フィルム３と内側フィルム４からなる多重フィルム２で構成される多重袋１の合掌部５に形成される引裂開始部５１が合掌部の外縁５２から少なくとも背シール部６まで達するように形成されているので、開封時の引き裂きの繰り出しをスムースに行うことができ、４枚のフィルムが集まった背シール部６を含め、多重フィルム２を容易に引き裂くことができる、易開封性に優れた多重袋１となる。 (F) Effects of the present invention:
In the multiple bag 1 according to the first embodiment of the present invention described above, the tear start portion 51 formed on the joint portion 5 of the multiple bag 1 composed of the multiple film 2 composed of the outer film 3 and the inner film 4 is a palm. Since it is formed so as to reach at least the back seal portion 6 from the outer edge 52 of the portion, it is possible to smoothly perform the tearing out at the time of opening, including the back seal portion 6 in which four films are gathered, and the multiple film It becomes the multiple bag 1 excellent in easy-openability which can tear 2 easily.

また、以上説明した本発明の第２実施形態に係る多重袋１は、外側フィルム３と内側フィルム４からなる多重フィルム２で構成される多重袋１の少なくとも外側フィルム３が環状オレフィン系樹脂とポリオレフィン系樹脂との混合樹脂からなる中間層３２，４２を有するので、かかる中間層３２，４２が易引裂樹脂層となって合掌部５に形成された引裂開始部５１からの引き裂きを容易とし、４枚のフィルムが集まった背シール部６を含め、多重フィルム２を容易に引き裂くことができる、易開封性に優れた多重袋１となる。   In addition, the multiple bag 1 according to the second embodiment of the present invention described above includes at least the outer film 3 of the multiple bag 1 composed of the multiple film 2 composed of the outer film 3 and the inner film 4. Since the intermediate layers 32 and 42 made of a mixed resin with a series resin are included, the intermediate layers 32 and 42 become easy tear resin layers to facilitate tearing from the tear start portion 51 formed in the palm portion 5. The multiple bag 1 including the back seal portion 6 on which the sheets of film are gathered can be easily torn and the multiple bag 1 is excellent in easy-openability.

前記した多重袋１は、例えば、業務用や工業用等に使用される液体、半流動体、粉体、固形、ペースト体等の材料、食品等の運搬、保管、販売等に用いることができ、特に、ジュース、ミネラルウォーター、清涼飲料水、コーヒー、紅茶、緑茶、調味料、植物性油、マヨネーズ、ソース、ケチャップ、ジュース等の液体食品等の運搬等に用いられる袋や、これらを運搬等するためのバックインボックス用の多重袋１として有用である。なお、前記した製法では内容物を充填した状態で製袋化された例を示したが、未だ充填物が充填されてない状態や、シール部等が形成されていない状態で使用されても問題はない。   The above-described multiple bag 1 can be used, for example, for transporting, storing, selling, etc., materials such as liquids, semi-fluids, powders, solids, pastes, etc., foods used for business use and industrial use. Especially, bags used for transporting liquid foods such as juice, mineral water, soft drinks, coffee, tea, green tea, seasonings, vegetable oil, mayonnaise, sauces, ketchup, juice, etc. This is useful as a multiple bag 1 for back-in-box. In the above-described manufacturing method, an example in which a bag is formed with the contents filled therein is shown, but there is a problem even if it is used in a state where the filling is not yet filled or a seal portion or the like is not formed. There is no.

また、バックインボックスに用いられる場合、内容物を充填した多重袋１を、収容された段ボール箱から、所定の容器（バケツ等）に多重袋１のまま移し、かかる所定の容器に入れた状態で開封して内容物を取り出して利用されることもある。多重袋１の開封に際しては、合掌部５が形成された面だけでなくその反対面を含んだ全周を引き裂いて、多重袋１から引き裂かれた不要部を取り外した場合にあっては、不要部がゴミとなり、処理が面倒となる。よって、全周を引き裂いて取り除くことはせず、合掌部５が形成された面のみを引き裂いて開封し、引き裂かれた部分を多重袋１から取り外さずに内容物を取り出すようにすることが好ましい。   In addition, when used in a back-in box, the multiple bag 1 filled with the contents is transferred from the accommodated cardboard box to the predetermined container (bucket, etc.) as it is, and put in the predetermined container. In some cases, the contents are taken out and opened. When opening the multiple bag 1, it is not necessary if the entire circumference including not only the surface on which the palm portion 5 is formed but also the opposite surface is torn and the unnecessary portion torn from the multiple bag 1 is removed. Part becomes garbage and processing becomes troublesome. Therefore, it is preferable not to tear and remove the entire circumference, but to tear and open only the surface on which the palm portion 5 is formed, and to take out the contents without removing the torn portion from the multiple bag 1. .

（Ｇ）実施形態の変形：
なお、以上説明した態様は、本発明の一態様を示したものであって、本発明は、前記した実施形態に限定されるものではなく、本発明の構成を備え、目的及び効果を達成できる範囲内での変形や改良が、本発明の内容に含まれるものであることはいうまでもない。また、本発明を実施する際における具体的な構造及び形状等は、本発明の目的及び効果を達成できる範囲内において、他の構造や形状等としても問題はない。本発明は前記した各実施形態に限定されるものではなく、本発明の目的を達成できる範囲での変形や改良は、本発明に含まれるものである。 (G) Variation of embodiment:
The aspect described above shows one aspect of the present invention, and the present invention is not limited to the above-described embodiment, and has the configuration of the present invention and can achieve the objects and effects. It goes without saying that modifications and improvements within the scope are included in the content of the present invention. Further, the specific structure, shape, and the like in carrying out the present invention are not problematic as other structures, shapes, and the like as long as the objects and effects of the present invention can be achieved. The present invention is not limited to the above-described embodiments, and modifications and improvements within the scope that can achieve the object of the present invention are included in the present invention.

例えば、前記した実施形態では、多重フィルム２の構成として、チューブ状フィルム２１及びブロッキング接着フィルム２２を例に挙げて説明したが、多重フィルムとしてはこれらには限定されず、外側フィルム３と内側フィルム４からなる任意の構成の多重フィルムを使用することができる。   For example, in the above-described embodiment, the tubular film 21 and the blocking adhesive film 22 are described as examples of the configuration of the multiple film 2, but the multiple film is not limited to these, and the outer film 3 and the inner film. A multi-film of any configuration consisting of 4 can be used.

なお、図８には、チューブ状フィルムを使用した場合において、外側フィルム３及び内側フィルム４を３層とした構成を示しているが、かかる構成には制限されず、外側フィルム３や内側フィルム４は４層以上の層構成としてもよく、例えば、中間層３２，４２と外層３３，４３、中間層３２，４２と内層３１，４１の間に他の層を形成するようにしてもよい。かかる他の層を構成する樹脂としては、チューブ状フィルム（（Ｂ）（１）、（Ｃ）（１））のおける前記した内層３１，４１や中間層３２，４２を構成する樹脂等を使用することができる。   FIG. 8 shows a configuration in which the outer film 3 and the inner film 4 are three layers in the case of using a tubular film, but the outer film 3 and the inner film 4 are not limited to this configuration. 4 may have a layer structure of four or more layers. For example, another layer may be formed between the intermediate layers 32 and 42 and the outer layers 33 and 43, or between the intermediate layers 32 and 42 and the inner layers 31 and 41. As the resin constituting the other layers, the resins constituting the inner layers 31 and 41 and the intermediate layers 32 and 42 in the tubular film ((B) (1), (C) (1)) are used. can do.

また、図９には、ブロッキング接着フィルム２２を使用した場合において、外側フィルム３を３層とした構成を示しているが、かかる構成には制限されず、外側フィルム３は４層以上の層構成としてもよく、例えば、中間層３２と外層３３、中間層３２と内層３１の間に他の層を形成するようにしてもよい。かかる他の層を構成する樹脂としては、ブロッキング接着フィルム（（Ｂ）（２）、（Ｃ）（２））における前記した外層３３や中間層３２を構成する樹脂等を使用することができる。   FIG. 9 shows a configuration in which the outer film 3 has three layers when the blocking adhesive film 22 is used. However, the outer film 3 is not limited to such a configuration, and the outer film 3 has a layer configuration of four or more layers. For example, another layer may be formed between the intermediate layer 32 and the outer layer 33, or between the intermediate layer 32 and the inner layer 31. As the resin constituting the other layer, the resin constituting the outer layer 33 and the intermediate layer 32 in the blocking adhesive film ((B) (2), (C) (2)) can be used.

チューブ状フィルム２１における外側フィルム３及び内側フィルム４は単層、２層としてもよい。単層とする場合は、図８に示した３層構造のチューブ状フィルム２１（（Ｂ）（１）、（Ｃ）（１））における前記した外層３３，４３を構成する樹脂を使用すればよい。また、２層とする場合は、外側に現れる層について、前記した外層３３，４３を構成する樹脂等を使用すればよく、内側に現れる層（隙間Ｃと対面する層）については、前記した内層３１，４１や中間層３２，４２を構成する樹脂等を使用することができる。   The outer film 3 and the inner film 4 in the tubular film 21 may be a single layer or two layers. In the case of a single layer, if the resin constituting the outer layers 33 and 43 in the tubular film 21 ((B) (1), (C) (1)) having the three-layer structure shown in FIG. 8 is used. Good. In the case of two layers, the resin that constitutes the outer layers 33 and 43 may be used for the layer that appears on the outside, and the inner layer described above for the layer that appears on the inner side (the layer facing the gap C). For example, a resin constituting the intermediate layers 32 and 42 can be used.

ブロッキング接着フィルム２２における外側フィルム３は単層、２層としてもよい。単層とする場合は、図９に示した３層構造のブロッキング接着フィルム２２（（Ｂ）（２）、（Ｃ）（２））における前記した内層３１を構成する樹脂等を使用すればよい。また、２層とする場合は、外側に現れる層について、前記した外層３３や中間層３２を構成する樹脂等を使用することができ、ブロッキング接着する層について、前記した内層３１を構成する樹脂等を使用することができる。   The outer film 3 in the blocking adhesive film 22 may be a single layer or two layers. In the case of a single layer, a resin or the like constituting the inner layer 31 in the blocking adhesive film 22 ((B) (2), (C) (2)) having a three-layer structure shown in FIG. 9 may be used. . Moreover, when it is set as two layers, the resin etc. which comprise the above-mentioned outer layer 33 and the intermediate | middle layer 32 can be used about the layer which appears outside, The resin which comprises the above-mentioned inner layer 31 about the layer which carries out blocking adhesion | attachment, etc. Can be used.

なお、本発明において、例えば、環状ポリオレフィン樹脂とポリオレフィン系樹脂の混合樹脂からなる中間層等の「中間層」とは、フィルムにおける外層及び内層（３層の場合、前記図８や図９を参照。）以外の層を指し、３層構成の場合の文字通りの中間層のほか、４層以上の構成における最外層及び最内層以外の層についても「中間層」に含まれるものである。   In the present invention, for example, an “intermediate layer” such as an intermediate layer made of a mixed resin of a cyclic polyolefin resin and a polyolefin-based resin refers to an outer layer and an inner layer in a film (in the case of three layers, refer to FIGS. 8 and 9). In addition to the literal intermediate layer in the case of the three-layer configuration, the layers other than the outermost layer and the innermost layer in the configuration of four or more layers are also included in the “intermediate layer”.

本発明にあって、「横シール部７に対して略平行に開封するための引裂開始部５１」とは、横方向（横シール部７の長手方向）に開封するために合掌部５に形成される引裂開始部５１のことを指し、かかる引裂開始部５１を合掌部５に形成した上で、例えば、横シール部７等に縦方向（背シール部６の長手方向）等に開封するための図示しない引裂開始部を別途形成してもよい。   In the present invention, “a tear start portion 51 for opening substantially parallel to the lateral seal portion 7” is formed in the palm portion 5 for opening in the lateral direction (longitudinal direction of the lateral seal portion 7). For example, the tear start portion 51 is formed in the palm portion 5 and then opened in the longitudinal direction (longitudinal direction of the back seal portion 6) or the like in the lateral seal portion 7 or the like. A tear start portion (not shown) may be formed separately.

なお、多重フィルム２を構成する前記した樹脂（樹脂材料）には、本発明の効果を損なわない範囲において、例えば、可塑剤、帯電防止剤、酸化防止剤、滑剤、防曇剤、紫外線吸収剤、熱安定剤、増核剤、離型剤、着色剤及び中和剤等、樹脂材料の分野で一般に使用される各種添加剤を添加するようにしてもよい。
その他、本発明の実施の際の具体的な構造及び形状等は、本発明の目的を達成できる範囲で他の構造等としてもよい。 The above-described resin (resin material) constituting the multiple film 2 is, for example, a plasticizer, an antistatic agent, an antioxidant, a lubricant, an antifogging agent, and an ultraviolet absorber, as long as the effects of the present invention are not impaired. Various additives generally used in the field of resin materials, such as a heat stabilizer, a nucleating agent, a releasing agent, a coloring agent, and a neutralizing agent, may be added.
In addition, the specific structure, shape, and the like in the implementation of the present invention may be other structures as long as the object of the present invention can be achieved.

本発明は、材料や食品等の包装及び運搬等に有利に使用することができ、産業上の利用可能性は高いものである。   INDUSTRIAL APPLICABILITY The present invention can be advantageously used for packaging and transporting materials and foods, and has high industrial applicability.

１ …… 多重袋
２ …… 多重フィルム
２１ …… チューブ状フィルム
２２ …… ブロッキング接着フィルム
３ …… 外側フィルム
４ …… 内側フィルム
３１，４１ …… 内層
３２，４２ …… 中間層
３３，４３ …… 外層
５…… 合掌部
５１ …… 引裂開始部
５２ …… 合掌部の外縁
６ …… 背シール部
６１ …… 合掌部の外縁側に形成された背シール部
７ …… 横シール部
Ｂ …… ブロッキング接着されている面
Ｃ …… 隙間 DESCRIPTION OF SYMBOLS 1 ... Multiple bag 2 ... Multiple film 21 ... Tubular film 22 ... Blocking adhesive film 3 ... Outer film 4 ... Inner film 31, 41 ... Inner layer 32, 42 ... Intermediate layer 33, 43 ... Outer layer 5 …… Joint part 51 …… Tear start part 52 …… Outer edge of joint part 6 …… Back seal part 61 …… Back seal part formed on outer edge side of joint part 7 …… Side seal part B …… Blocking Bonded surface C ...... Gap

Claims (4)

フィルムの両端を前記フィルム同士が対向するように重ね合わせて合掌部が形成され、
前記合掌部に所定の幅で、重ね合わされる前記フィルム同士を溶着して一体化した背シール部が形成されるとともに、
前記背シール部と直交する側の両端縁付近を所定の幅で溶着した横シール部が形成されることで内容物が充填密封された袋が形成され、
前記合掌部には前記横シール部に対して略平行に引裂くように開封するための、前記横シール部に対して略平行に形成される引裂開始部を有し、
前記引裂開始部は前記合掌部の外縁から少なくとも前記背シール部まで達するように形成されることを特徴とする袋。 A palm portion is formed by overlapping both ends of the film so that the films face each other,
A back seal portion is formed by welding the films to be overlapped with each other at a predetermined width on the palm portion, and integrated.
A bag in which the contents are filled and sealed is formed by forming a lateral seal part in which the vicinity of both end edges on the side orthogonal to the back seal part is welded with a predetermined width,
The joint portion has a tear start portion formed to be substantially parallel to the lateral seal portion for opening so as to tear substantially parallel to the lateral seal portion,
The bag according to claim 1, wherein the tear start portion is formed to reach at least the back seal portion from an outer edge of the palm portion. 前記背シール部は前記合掌部に対して細幅線状に複数形成され、
前記引裂開始部は前記複数の背シール部のうち少なくとも前記合掌部の外縁側に形成された前記背シール部に達するように形成されていることを特徴とする請求項１に記載の袋。 The back seal portion is formed in a plurality of narrow lines with respect to the palm portion,
2. The bag according to claim 1, wherein the tear start portion is formed so as to reach at least the back seal portion formed on the outer edge side of the joint portion among the plurality of back seal portions. フィルムの両端を前記フィルム同士が対向するように重ね合わせて合掌部が形成され、
前記合掌部に所定の幅で、重ね合わされる前記フィルム同士を溶着して一体化した背シール部が形成されるとともに、
前記背シール部と直交する側の両端縁付近を所定の幅で溶着した横シール部が形成されることで内容物が充填密封された袋が形成され、
前記合掌部には前記横シール部に対して略平行に引裂くように開封するための、前記横シール部に対して略平行に形成される引裂開始部を有し、
少なくとも前記フィルムは環状ポリオレフィン樹脂とポリオレフィン系樹脂との混合樹脂からなる中間層を有する多層構成であることを特徴とする袋。 A palm portion is formed by overlapping both ends of the film so that the films face each other,
A back seal portion is formed by welding the films to be overlapped with each other at a predetermined width on the palm portion, and integrated.
A bag in which the contents are filled and sealed is formed by forming a lateral seal part in which the vicinity of both end edges on the side orthogonal to the back seal part is welded with a predetermined width,
The joint portion has a tear start portion formed to be substantially parallel to the lateral seal portion for opening so as to tear substantially parallel to the lateral seal portion,
At least the film has a multilayer structure having an intermediate layer made of a mixed resin of a cyclic polyolefin resin and a polyolefin resin. 前記混合樹脂は、前記環状ポリオレフィン樹脂を前記混合樹脂全体に対して３〜９９質量％含有することを特徴とする請求項３に記載の袋。   The said mixed resin contains 3-99 mass% of said cyclic polyolefin resin with respect to the said mixed resin whole, The bag of Claim 3 characterized by the above-mentioned.
JP2019107607A 2015-02-27 2019-06-10 bag Active JP6971443B2 (en)