JP2016003285A - 粘着剤組成物、及び表示装置 - Google Patents
粘着剤組成物、及び表示装置 Download PDFInfo
- Publication number
- JP2016003285A JP2016003285A JP2014124538A JP2014124538A JP2016003285A JP 2016003285 A JP2016003285 A JP 2016003285A JP 2014124538 A JP2014124538 A JP 2014124538A JP 2014124538 A JP2014124538 A JP 2014124538A JP 2016003285 A JP2016003285 A JP 2016003285A
- Authority
- JP
- Japan
- Prior art keywords
- meth
- mass
- sensitive adhesive
- pressure
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】水酸基を有する単量体に由来する構成単位を含む(メタ)アクリル系共重合体と、芳香族ジイソシアネート化合物に由来する部分構造及びイソシアヌレート環構造を有する多価イソシアネート化合物と、式(1)で表されるN−置換イミダゾール化合物と、イオン性化合物と、を含み前記イオン性化合物のカチオンは、金属カチオン又は炭化水素基の合計の炭素数が7以上の有機カチオンである、粘着剤組成物。
(R1はアルキル基、アリール基、又はアラルキル基;R2〜R4は各々独立にH、アルキル基、アリール基又はアラルキル基;R3及びR4は互いに連結して環を形成してもよい)
【選択図】なし
Description
また、液晶表示装置には入力装置としてタッチパネルが搭載されることがある。近年では、液晶表示装置の内部にタッチパネルを有するものも増えてきている。タッチパネルと液晶表示装置を構成する部材(偏光板など)との貼着にも、アクリル系粘着剤が用いられることが多い。タッチパネルを構成する透明電極フィルムは、粘着剤に含まれる酸性成分により腐食されるため、偏光板とタッチパネルとを貼着する場合には、酸性成分を含まない粘着剤が求められる。
<1> 水酸基を有する単量体に由来する構成単位を含む(メタ)アクリル系共重合体と、芳香族ジイソシアネート化合物に由来する部分構造及びイソシアヌレート環構造を有する多価イソシアネート化合物と、下記一般式(1)で表されるN−置換イミダゾール化合物と、イオン性化合物と、を含み、前記イオン性化合物のカチオンは、金属カチオン又は炭化水素基の合計の炭素数が7以上の有機カチオンである、粘着剤組成物。
R3及びR4は互いに連結して環を形成してもよい。
<3> 前記N−置換イミダゾール化合物の含有量が、前記(メタ)アクリル系共重合体100質量部に対して0.01質量部〜0.6質量部である<1>又は<2>に記載の粘着剤組成物。
<4> 前記多価イソシアネート化合物の含有量が、前記(メタ)アクリル系共重合体100質量部に対して0.01質量部〜0.5質量部である<1>〜<3>のいずれか1つに記載の粘着剤組成物。
<5> 前記(メタ)アクリル系共重合体は、水酸基を有する単量体に由来する構成単位を0.3質量%〜12質量%有する<1>〜<4>のいずれか1つに記載の粘着剤組成物。
また(メタ)アクリレートとは、アクリレート及びメタクリレートの少なくとも一方を意味し、(メタ)アクリルとはアクリル及びメタクリルの少なくとも一方を意味する。
本発明における粘着剤組成物は、水酸基を有する単量体に由来する構成単位を含む(メタ)アクリル系共重合体と、芳香族ジイソシアネート化合物に由来する部分構造及びイソシアヌレート環構造を有する多価イソシアネート化合物と、一般式(1)で表されるN−置換イミダゾール化合物と、金属塩又はカチオンが有する炭化水素基の合計の炭素数が7以上であるイオン性化合物と、を含む。
本発明における粘着剤組成物は、必要に応じて更に、シランカップリング剤、その他の添加剤等の他の成分を含んでもよい。
本発明の効果が得られる理由は明確ではないが、本発明者らは、以下のように推定している。
本発明における粘着剤組成物は、芳香族ジイソシアネート化合物に由来する部分構造及びイソシアネレート環構造を有する多価イソシアネート化合物と、一般式(1)で表されるN−置換イミダゾール化合物とを含むことで、前記多価イソシアネート化合物と水酸基を有する単量体に由来する構成単位を含む(メタ)アクリル系共重合体との架橋反応が促進されるため、粘着剤組成物の養生時間を短縮することができると考えられる。
また、前記多価イソシアネート化合物と前記N−置換イミダゾール化合物とを含む組成物に、帯電防止剤としてカチオンが金属カチオン又は炭化水素基の合計の炭素数が7以上の有機カチオンであるイオン性化合物を用いることで、前記多価イソシアネート化合物とイオン性化合物が反応しにくくなるため、透明性を維持しつつ、帯電防止効果を付与することができると考えられる。
また、(メタ)アクリル系共重合体が、水酸基を有する単量体に由来する構成単位を有しており、これがイソシアネレート環構造を有する多価イソシアネート化合物で架橋されることで、粘着剤層としたときの弾性と粘性のバランスに優れると考えられる。
本発明における粘着剤組成物は、水酸基を有する単量体に由来する構成単位の少なくとも1種を含む(メタ)アクリル系共重合体(以下、単に「共重合体」ともいう)を含む。
(メタ)アクリル系共重合体における水酸基を有する単量体に由来する構成単位以外の成分は、水酸基を有する単量体と共重合可能なその他の単量体に由来する構成単位の中から選択することができる。
本発明における(メタ)アクリル系共重合体は、共重合体の総質量に対して(メタ)アクリル系単量体に由来する構成単位を50質量%以上含むことが好ましい。
ここでいう(メタ)アクリル系単量体とは、後述する水酸基を有する(メタ)アクリル系単量体、アルキル(メタ)アクリレート、環状基を有する(メタ)アクリレートなどを総称したものを意味する。
本発明における(メタ)アクリル系共重合体は、水酸基を有する単量体に由来する構成単位の少なくとも1種を含む。
(メタ)アクリル系共重合体は、水酸基を有する単量体に由来する構成単位を含むことで、後述する特定の構造を有する多価イソシアネート化合物と架橋反応することができる。このため、粘着剤層としたときの凝集力が向上して耐久性に優れる。さらには該粘着剤組成物を、表示装置の偏光板に適用した場合に光漏れを抑制することができる。
水酸基を有する単量体は、1種を単独で用いても2種以上を組み合わせて用いてもよい。
(メタ)アクリル系共重合体における水酸基を有する単量体に由来する構成単位の含有量が0.3質量%以上であると架橋反応が進行しやすく、養生時間をより短縮することができる。また、水酸基を有する単量体に由来する構成単位の含有量が12質量%以下であると、ポットライフがより良好になる。
本発明における(メタ)アクリル系共重合体は、その他の単量体に由来する構成単位の少なくとも1種を含むことが好ましい。
本発明におけるその他の単量体は、本発明の趣旨を越えない限り、前記水酸基を有する単量体と共重合可能な単量体の中から選択して用いることができる。
その他の単量体は、1種を単独で用いても2種以上を組み合わせて用いてもよい。
本発明における(メタ)アクリル系共重合体は、その他の単量体に由来する構成単位として、アルキル(メタ)アクリレートに由来する構成単位を含むことが好ましい。
アルキル(メタ)アクリレートのアルキル基の炭素数は、粘着剤組成物の凝集力及び接着力を調整しやすい観点から、1〜20が好ましく、1〜18がより好ましく、1〜12が更に好ましい。アルキル(メタ)アクリレートのアルキル基は、直鎖状であっても分岐鎖状であってもよい。
本発明における(メタ)アクリル系共重合体は、その他の単量体に由来する構成単位として、環状基を有する単量体に由来する構成単位を含むことが好ましい。
環状基を有する単量体は、分子内に少なくとも1つの環状基を有し、水酸基を有する単量体と共重合可能な重合性化合物であれば特に制限はない。環状基を有する単量体における環状基として、芳香族炭化水素基、芳香族複素環基、脂肪族炭化水素基等が挙げられ、中でも芳香族炭化水素基が好ましく、炭素数6〜炭素数10の芳香族炭化水素基であることがより好ましい。
環状基を有する単量体における環状基の含有数は、1〜2であることが好ましく、1であることがより好ましい。
ここで実質的に含まないとは、不可避的に混入する酸性基を有する単量体に由来する構成単位の存在を許容することを意味する。
(メタ)アクリル系共重合体における酸性基を有する単量体に由来する構成単位の含有量を0.5質量%以下とすることで、本発明の粘着剤組成物に由来する粘着剤層がタッチパネル等の透明電極と接触する場合に、電極の腐食を抑制することができる。このため、本発明の粘着剤組成物は、タッチパネルが搭載された表示装置用の偏光板に好適に使用することができる。
第一の態様として、(メタ)アクリル系共重合体が、水酸基を有する(メタ)アクリル単量体に由来する構成単位と、アルキル(メタ)アクリレートに由来する構成単位と、を含む態様が挙げられる。
第二の態様として、(メタ)アクリル系共重合体が、水酸基を有する(メタ)アクリル系単量体に由来する構成単位と、アルキル(メタ)アクリレートに由来する構成単位と、環状基を有する単量体に由来する構成単位と、を含む態様が挙げられる。
(メタ)アクリル系共重合体は、水酸基を有する単量体、及びその他の単量体を含む単量体組成物を重合することで製造することができる。単量体組成物の重合方法は、特に制限されるものではなく、通常用いられる重合方法から適宜選択することができる。重合方法としては、溶液重合、乳化重合、懸濁重合等を挙げることができる。中でも製造が比較的簡単である溶液重合が好ましい。
なお、(メタ)アクリル系共重合体の重量平均分子量(Mw)及び数平均分子量(Mn)は、反応温度、反応時間、溶剤量、触媒の種類や量を調整することにより、所望の分子量に調整することができる。
また(メタ)アクリル系共重合体の分散度(Mw/Mn)は特に制限されず、例えば2〜10とすることができ、4〜9であることが好ましく、5〜8であることがより好ましい。分散度が前記範囲であることで、粘着剤層としたときの耐久性に優れる。
(1)(メタ)アクリル系共重合体溶液を剥離シート(離型シート)上に塗工し、100℃で2分間乾燥させ、フィルム状の(メタ)アクリル系共重合体を得る。
(2)前記(1)で得られたフィルム状の(メタ)アクリル系共重合体をテトラヒドロフランにて固形分0.2質量部になるように溶解させる。
(3)下記条件にて、ゲルパーミエーションクロマトグラフィー(GPC)を用いて、標準ポリスチレン換算値として、(メタ)アクリル系共重合体の重量平均分子量(Mw)及び数平均分子量(Mn)を測定する。
・GPC :HLC−8220 GPC(東ソー株式会社製)
・カラム :TSK−GEL GMHXL 4本使用(東ソー株式会社製)
・移動相溶媒:テトラヒドロフラン
・流速 :0.8ml/min
・カラム温度:40℃
本発明における粘着剤組成物は、芳香族ジイソシアネート化合物に由来する部分構造及びイソシアヌレート環構造を有する多価イソシアネート化合物(以下、単に「多価イソシアネート化合物」ともいう)の少なくとも1種を含む。
多価イソシアネート化合物は、(メタ)アクリル系共重合体に対して架橋剤として作用する。すなわち、本発明の粘着組成物は、(メタ)アクリル系共重合体が水酸基を有する単量体に由来する構成単位と、特定の構造を有する多価イソシアネート化合物と、含むことで、粘着剤層としたときの優れた耐久性と、養生時間の短縮とが両立できる。
多価イソシアネート化合物は1種を単独で用いても2種以上を組み合わせて用いてもよい。
多価イソシアネート化合物の含有量が0.01質量部以上であると、架橋反応が充分に進行し、凝集力が十分に高くなるため、粘着剤層としたときの接着性及び耐久性に優れる。また多価イソシアネート化合物の含有量が0.5質量部以下であると、多価イソシアネート化合物とイオン性化合物とが反応しにくく、粘着剤組成物の白濁をより抑制することができ、粘着剤組成物の透明性に優れる。
粘着剤組成物がその他の架橋剤を含む場合、その含有量は本発明の効果を損なわない範囲であれば特に制限されない。その他の架橋剤の含有量は、(メタ)アクリル系共重合体100質量部に対して、5質量部以下であることが好ましく、1質量部以下であることがより好ましい。
本発明における粘着剤組成物は、下記一般式(1)で表されるN−置換イミダゾール化合物の少なくとも1種を含む。下記一般式(1)で表されるN−置換イミダゾール化合物は、粘着剤組成物において、硬化促進剤として機能することができる。粘着剤組成物が下記一般式(1)で表されるN−置換イミダゾール化合物を含むことで、酸性成分を実質的に含まなくても、粘着剤層としたときの優れた耐久性と十分なポットライフを維持しつつ、養生時間をより短縮することができる。
一般式(1)で表されるN−置換イミダゾール化合物の含有量が0.01質量部以上であれば、養生時間短縮の効果が十分である。また、一般式(1)で表されるN−置換イミダゾール化合物の含有量が0.6質量部以下であると、ポットライフが十分に得られる。
本発明における粘着剤組成物は、カチオンが金属カチオン又は炭化水素基の合計の炭素数が7以上の有機カチオンであるイオン性化合物(以下特定イオン性化合物ともいう)の少なくとも1種を含む。
粘着剤組成物が、特定イオン性化合物を含有することで、粘着剤組成物の透明性を維持しつつ、帯電防止性を付与することができる。
以下、カチオンが金属カチオンの特定イオン性化合物を特定金属塩ともいう。また、カチオンが炭化水素基の合計の炭素数が7以上の有機カチオンの特定イオン性化合物を特定有機塩ともいう。
特定イオン性化合物の含有量が0.1質量部以上であると、帯電防止性向上の効果により優れる。
特定金属塩のカチオンとしては、例えば、アルカリ金属、アルカリ土類金属等の金属カチオンが挙げられる。
カチオンとして、金属カチオンを含む場合、例えば、Li+、Na+、K+であることが好ましく、Li+であることがより好ましい。
また、特定金属塩のアニオンとしては、例えば、Cl−、Br−、I−、BF4 −、PF6 −、SCN−、ClO4 −、CF3COO−、SbF6 −、NbF6 −、TaF6 −、F(HF)n −、C4F9SO3 −、C3F7COO−、CF3SO3 −、(CF3SO2)2N−、(CF3SO2)3C−、(C2F5SO2)2N−、(CF3SO2)(CF3CO)N−、AlCl4 −、Al2Cl7 −、ClO4 −、NO3 −、CH3COO−、CH3SO3 −、AsF6 −、(CN)2N−、(C2F5SO2)2N−、(C3F7SO2)2N−、(C4F9SO2)2N−、(CF3SO2)(C2F5SO2)N−、(CF3SO2)(C4F9SO2)N−、(C2F5SO2)(C4FOSO2)N−等が挙げられる。
これらの中でもClO4 −、(CF3SO2)2N−(以下、TFSIともいう)が好ましい。
また、特定金属塩は1種を単独で用いても2種以上を組み合わせて用いてもよい。
特定有機塩は、炭化水素基の合計の炭素数が7以上のカチオンと、アニオンとからなる。
カチオンが有する炭化水素基合計の炭素数が7以上であることで、既述の多価イソシアネートと併用しても粘着剤組成物の白濁が抑えられ、透明性を維持することができる。
カチオンが有する炭化水素基は、透明性の観点から、炭素数が11以上であることが好ましく、炭素数が11以上25以下であることがより好ましい。
これらの中でも、粘着剤層としたときの透明性の観点から、ドデシルトリメチルアンモニウム(炭素数15)、オクチルトリメチルアンモニウム(炭素数11)、アミルトリエチルアンモニウム(炭素数11)、トリブチルメチルアンモニウム(炭素数13)、メチルトリ−N−オクチルアンモニウム(炭素数25)が好ましい。
これらの中でもPF6 −、(CF3SO2)2N−(以下、TFSIともいう)、(FSO2)2N−(以下、FSIともいう)が好ましい。
また、これらは1種を単独で用いても2種以上を組み合わせて用いてもよい。
粘着剤組成物において、特定有機塩の含有量は、前記(メタ)アクリル系共重合体100質量部に対して、0.1質量部以上であることが好ましく、0.2質量部以上がより好ましく、0.2質量部〜8質量部がより好ましい。
特定有機塩の含有量が0.1質量部以上であると、帯電防止性向上の効果により優れる。
本発明の粘着剤組成物は、さらにシランカップリング剤の少なくとも1種を含むことが好ましい。
粘着剤組成物がシランカップリング剤を含むことで、粘着剤組成物を偏光板の粘着剤層として用いた表示装置(例えば液晶表示装置)が高温高湿環境下に曝されても、粘着剤層と偏光板又は液晶セルとの間に、剥がれが発生し難くなる。更に粘着剤組成物が平滑なガラスに、より優れた接着性を示すようになる。
チオール基を有するオリゴマー型のシランカップリング剤は、チオール基を有する部分構造とチオール基を有さない部分構造からなるシランカップリング剤であることが好ましく、例えば、信越化学工業株式会社製の商品名「X−41−1810」、「X−41−1805」、「X−41−1818」を挙げることができる。
粘着剤組成物は、上記成分の他、更に必要に応じて、溶剤、紫外線吸収剤等の耐候性安定剤、タッキファイアー、可塑剤、軟化剤、染料、顔料、無機充填剤などを含有しでもよい。粘着剤組成物がその他の成分を含有する場合、その含有率は本発明の効果を損なわない範囲で適宜選択することができる。
本発明の表示装置は、情報を入力するタッチパネルと、偏光板上に既述の本発明の粘着剤組成物により形成された粘着剤層を有する粘着剤付偏光板と、を少なくとも有する。
本発明におけるタッチパネルは特に限定されるものではないが、タッチパネルの構成として、例えば、ガラス板及び該ガラス板上に蒸着されたITO層を有するシート状の光学材と、保護材となるカバーフィルムと、光学材及びカバーフィルムの間を接着する粘着剤層とを重層した構成が挙げられる。
本発明の粘着剤付偏光板は、少なくとも、偏光板と、既述の本発明の粘着剤組成物により偏光板上に形成された粘着剤層と、を含む。
本発明の粘着剤付偏光板は、上記の粘着剤層を含むため、透明性と帯電防止性とを両立することができる。
本発明における偏光板は、少なくとも偏光子を含んで構成されることが好ましく、偏光子単体を用いてもよく、偏光子と保護用シートとを積層したものを用いてもよい。
偏光板として偏光子と保護シートとを積層したものを用いる場合は、保護用シートとして例えばトリアセチルセルロース(TAC)やポリシクロオレフィン(COP)、アクリルフィルム等を用いることができる。
偏光子と保護用シートとを積層したものは例えば2層構造(例えばTAC/偏光子)や3層構造(例えばTAC/偏光子/TAC)に構成され、偏光板として用いることができる。
また、偏光板の粘着剤層が設けられていない側の表面(露出面)には、その表面を保護する表面保護シートを更に設けてもよい。表面保護シートには、PETフィルムの片面に粘着加工されたプロテクトフィルム等が好適に用いられる。
本発明の表示装置の構成例として、アウトセル型のタッチパネル付液晶表示装置、及びオンセル型のタッチパネル付液晶表示装置等を挙げることができる。
アウトセル型のタッチパネル付液晶表示装置は、液晶表示パネルの両面に本発明の粘着剤付偏光板を、それぞれについて粘着剤層が液晶表示パネルの表面(例えばガラス基板の表面)に接触するように配置し、粘着剤層を介して液晶表示パネルの両面に偏光板を接着し、さらにいずれか一方の偏光板の液晶表示パネル側ではない面にタッチパネルを外付けした構造(タッチパネル/粘着剤層/偏光板/粘着剤層/液晶表示パネル/粘着剤層/偏光板の構造)を備えることが好ましい。
オンセル型のタッチパネル付液晶表示装置は、偏光板と液晶表示パネルの間にタッチパネルを組み込んだ構造(偏光板/粘着剤層/タッチパネル/粘着剤層/液晶表示パネル/粘着剤層/偏光板の構造)を備えることが好ましい。本発明の表示装置としては、オンセル型のタッチパネル付表示装置が好ましい。
温度計、撹枠機、窒素導入管、及び還流冷却管を備えた反応器内に、n−ブチルアクリレート(BA)を98部と、2−ヒドロキシエチルアクリレート(2HEA)を2部と、酢酸エチル(EAc)を70部と、を入れ、混合した後、反応容器内を窒素置換した。その後、撹枠下に窒素雰囲気中で、反応容器内の混合物を70℃に昇温した後に、アゾビスジメチルバレロニトリル(ABVN)を0.02部と、酢酸エチル(EAc)を200部
と、を逐次添加し6時間反応させた。反応終了後、反応混合物を酢酸エチルで希釈し、(メタ)アクリル系共重合体1の溶液(固形分16質量%)を得た。
得られた(メタ)アクリル系共重合体1の重量平均分子量(Mw)及び数平均分子量(Mn)を、ゲルパーミエーションクロマトグラフィ(GPC)を用いて既述条件で測定したところ、重量平均分子量(Mw)は152万、分散度(Mw/Mn)は6.8であった。
製造例1において、(メタ)アクリル系共重合体1の合成に用いた単量体の種類及び比率を下記表1に示すように変更したこと以外は、製造例1と同様にして、(メタ)アクリル系共重合体2〜(メタ)アクリル共重合体9の溶液(固形分16質量%)をそれぞれ得た。
また、得られた各(メタ)アクリル系共重合体について、製造例1と同様にして、Mw及びMnの測定を行なった。結果は、下記表1に示す。
表1中、「BA」はn−ブチルアクリレート、「PHEA」はフェノキシエチルアクリレート、「MA」はメチルアクリレート、「t−BA」はt−ブチルアクリレート、「2HEA」は2−ヒドロキシエチルアクリレートを示す。
−粘着剤組成物の調製−
(メタ)アクリル系共重合体として、前記製造例1で得た(メタ)アクリル系共重合体1の溶液を固形分として100部と、多価イソシアネート化合物(架橋剤)としてコロネート2037(日本ポリウレタン工業株式会社製)を固形分として0.125部と、イミダゾール化合物(硬化促進剤)としてキュアゾール1B2PZ(四国化成株式会社製、1−ベンジル−2−フェニルイミダゾール)を固形分として0.05部と、シランカップリング剤としてX−41−1810(信越化学工業株式会社製、チオール基を有するオリゴマー型)を固形分として0.1部と、イオン性化合物としてドデシルトリメチルアンモニウムFSI(炭素数が15の炭化水素基を有するカチオン含有)を固形分として0.1部と、を充分に攪拌混合して粘着剤組成物を得た。
上記で得られた粘着剤組成物が養生に要する時間(養生時間)を以下のようにしてゲル分率を測定することで評価した。
粘着剤組成物をシリコーン系離型剤で表面処理した剥離フィルム(藤森工業株式会社製、100E−0010N023)上に、乾燥後の厚みが20μmとなるようにフィルム状の粘着剤層を作製した。次に、作製した粘着剤層を23℃、50%RH環境下に移した後、168時間経過後まで保管した。粘着剤層のゲル分率を、保管開始から24時間毎に以下のようにしてそれぞれ測定した。所定の保管時間が経過した後のゲル分率と、168時間(7日間)経過後のゲル分率とを比較して、両者のゲル分率の差が3%以下となるのに要した保管時間を養生終了時間とし、下記評価基準に従って評価した。
1.精密天秤にて質量を正確に測定した250メッシュの金網(100mm×100mm)にフィルム状粘着剤層を約0.25g貼付し、ゲル分が漏れないように包む。その後、精密天秤にて質量を正確に測定して試料を作製する。
2.得られた試料を酢酸エチル80mlに3日間浸漬する。
3.試料を取り出して少量の酢酸エチルにて洗浄し、120℃で24時間乾燥させる。その後、精密天秤にて質量を正確に測定する。
4.下式によりゲル分率を計算する。
ゲル分率(質量%)=(Z−X)/(Y−X)×100
但し、Xは金網の質量(g)、Yは粘着剤層を貼付した金網の浸漬前の質量(g)、Zは浸漬後、乾燥させた粘着剤層を貼付した金網の質量(g)である。
A:養生終了時間が24時間未満である。
B:養生終了時間が24時間以上48時間未満である。
C:養生終了時間が48時間以上である。
上記で得られた粘着剤組成物をシリコーン系離型剤で表面処理した剥離フィルム(藤森工業株式会社製、100E−0010N023)上に塗布した後、100℃、1分間の乾燥条件で乾燥し、23℃、50%RHの環境下で1日間養生した。養生終了後の粘着剤層の厚みは20μmであった。次に、粘着剤層の剥離フィルムと反対側の表面に離型処理が施されていない厚さ100μmのPETフィルム(商品名:A4100、東洋紡績株式会社製)を重ね、加圧ニップロールを通して圧着し、試験用粘着シートを作製した。
上記で得られた試験用粘着シートの剥離フィルムを剥離して、粘着剤層の表面抵抗値をR12704 RESISTIVITY CHAMBER(株式会社アドバンテスト製)を用いて、23℃、50%RH、印加電圧100Vの条件下で測定し、下記評価基準に従って帯電防止性を評価した。表面抵抗値が小さいほど静電気の発生抑制効果が高く、帯電防止性に優れる。評価基準のA及びBが実用上問題ないレベルである。
A:表面抵抗値が1×1012Ω/□未満である。
B:表面抵抗値が1×1012Ω/□以上1×1013Ω/□未満である。
C:表面抵抗値が1×1013Ω/□以上である。
上記で得られた試験用粘着シートを80mm×60mmにカットしてサンプル片とし、得られたサンプル片の剥離フィルムを剥離し、露出した粘着剤層の表面を、厚さ1.8mmのガラス板(商品名:光学ソーダガラス、松浪硝子株式会社製)に重ね、卓上ラミネート機を用いて圧着し、透明性評価用試験サンプルとした。得られた透明性評価用試験サンプルのヘイズを、分光測色計CM−3500d(コニカミノルタ株式会社製)を用いて測定し、下記評価基準に従って透明性を評価した。評価基準のA及びBが実用上問題ないレベルである。
A:ヘイズが0.5未満である。
B:ヘイズが0.5以上1.0未満である。
C:ヘイズが1.0以上である。
上記で得られた粘着剤組成物のポットライフを、以下のようにして粘度を測定して粘度上昇率を算出することで評価した。
粘着剤組成物を粘度1500mPa・sとなるように酢酸エチルを用いて調整した後、BH型回転粘度計にて25℃、1分、10rpmでの粘度(a)を測定した。さらに25℃、50%RHの条件下で密閉容器にて24時間放置した後、BH型回転粘度計にて25℃、1分、10rpmでの粘度(b)を測定した。
得られた粘度(a)と粘度(b)を用いて、下式により粘度上昇率(%)を算出した。
粘度上昇率(%)=24時開放置後の粘度(b)/配合直後の粘度(a)×100
A:粘度上昇率(%)が110%未満である。
B:粘度上昇率(%)が110%以上120%未満である。
C:粘度上昇率(%)が120%以上である。
実施例1において、粘着剤組成物の組成を下記表2、下記表3に示すように変更したこと以外は、実施例1と同様にして粘着剤組成物を作製し、実施例1と同様にして評価を行った。評価結果を表2、表3に示す。
(架橋剤)
コロネート2037:日本ポリウレタン工業株式会社製、トリレンジイソシアネートのイソシアヌレート体
コロネートL:日本ポリウレタン工業株式会社製、トリレンジイソシアネートのトリメチロールプロパンアダクト体
(硬化促進剤)
1B2PZ:四国化成工業株式会社製、1−ベンジル−2−フェニルイミダゾール
(シランカップリング剤)
X−41−1810:信越化学工業株式会社製、チオール基を有するオリゴマー型
(イオン性化合物)
表2及び表3中、FSIはフルオロスルホニルイミド((FSO2)2N−)、TFSIはトリフルオロメタンスルホニルイミド((CF3SO2)2N−)を示す。
表2及び表3中、例えば、「炭素数 C15」で表される記載は、カチオンが有する炭化水素基の合計の炭素数が15であることを示す。
Claims (6)
- 水酸基を有する単量体に由来する構成単位を含む(メタ)アクリル系共重合体と、
芳香族ジイソシアネート化合物に由来する部分構造及びイソシアヌレート環構造を有する多価イソシアネート化合物と、
下記一般式(1)で表されるN−置換イミダゾール化合物と、
イオン性化合物と、を含み、
前記イオン性化合物のカチオンは、金属カチオン又は炭化水素基の合計の炭素数が7以上の有機カチオンである、
粘着剤組成物。
式中、R1はアルキル基、アリール基、又はアラルキル基を示す。式中、R2、R3及びR4は、それぞれ独立に、水素原子、アルキル基、アリール基又はアラルキル基を示す。
R3及びR4は互いに連結して環を形成してもよい。 - 前記イオン性化合物の含有量が、前記(メタ)アクリル系共重合体100質量部に対して0.1質量部以上である請求項1に記載の粘着剤組成物。
- 前記N−置換イミダゾール化合物の含有量が、前記(メタ)アクリル系共重合体100質量部に対して0.01質量部〜0.6質量部である請求項1又は請求項2に記載の粘着剤組成物。
- 前記多価イソシアネート化合物の含有量が、前記(メタ)アクリル系共重合体100質量部に対して0.01質量部〜0.5質量部である請求項1〜請求項3のいずれか1項に記載の粘着剤組成物。
- 前記(メタ)アクリル系共重合体は、水酸基を有する単量体に由来する構成単位を0.3質量%〜12質量%有する請求項1〜請求項4のいずれか1項に記載の粘着剤組成物。
- タッチパネルと、
請求項1〜請求項5のいずれか1項に記載の粘着剤組成物により形成された粘着剤層を含む粘着剤付偏光板と、
を有する表示装置。