JP2012001817A - Electroless palladium plating bath and electroless palladium plating method - Google Patents
Electroless palladium plating bath and electroless palladium plating method Download PDFInfo
- Publication number
- JP2012001817A JP2012001817A JP2011173492A JP2011173492A JP2012001817A JP 2012001817 A JP2012001817 A JP 2012001817A JP 2011173492 A JP2011173492 A JP 2011173492A JP 2011173492 A JP2011173492 A JP 2011173492A JP 2012001817 A JP2012001817 A JP 2012001817A
- Authority
- JP
- Japan
- Prior art keywords
- acid
- unsaturated carboxylic
- electroless palladium
- palladium plating
- carboxylic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、保存安定性が高く、連続使用時の浴安定性が良好な工業的使用に耐え得る無電解パラジウムめっき浴及びこれを用いた無電解パラジウムめっき方法に関する。 The present invention relates to an electroless palladium plating bath that has high storage stability and can withstand industrial use with good bath stability during continuous use, and an electroless palladium plating method using the same.
従来、プリント配線板や電子部品の実装工程で、高信頼性が要求される用途の表面処理には無電解ニッケル／置換金めっきが多用されている。 Conventionally, electroless nickel / displacement gold plating has been frequently used for surface treatment in applications where high reliability is required in the mounting process of printed wiring boards and electronic components.
置換金めっきは下地となるニッケルとめっき浴中の酸化還元電位の差を利用して金を析出させるため、金がニッケルを侵食し、酸化（溶出）による腐食点が発生する。この酸化による腐食点は、その後のはんだリフロー時において、はんだ層のＳｎとＮｉを接続させる際の阻害因子となり、強度などの接合特性を低下させるという問題がある。 In displacement gold plating, gold is deposited by utilizing the difference between the underlying nickel and the oxidation-reduction potential in the plating bath, so that gold corrodes nickel and corrosion points due to oxidation (elution) occur. This corrosion point due to oxidation becomes a hindrance when connecting the Sn and Ni of the solder layer during the subsequent solder reflow, and there is a problem that joint characteristics such as strength are lowered.
また、ワイヤボンディングされる部位に無電解ニッケル／置換金めっき皮膜を用いる場合、めっき処理後に加熱処理を行うのであるが、その加熱処理により、Ａｕ皮膜表面にＮｉが拡散し、ワイヤボンディングの成功率が低下する。従って、Ａｕ皮膜上へのＮｉの拡散を防ぐために、無電解ニッケル／置換金めっき皮膜の上に、更に無電解Ａｕめっきを施し、Ａｕの膜厚を厚くすることで、ワイヤボンディングの成功率の低下を抑えているが、コスト的な問題がある。 In addition, when an electroless nickel / displacement gold plating film is used for the part to be wire bonded, the heat treatment is performed after the plating process, but Ni diffuses on the Au film surface by the heat treatment, and the success rate of the wire bonding Decreases. Therefore, in order to prevent the diffusion of Ni on the Au film, electroless Au plating is further applied on the electroless nickel / displacement gold plating film to increase the thickness of the Au film, thereby increasing the wire bonding success rate. Although the decrease is suppressed, there is a cost problem.
一方、近年の鉛フリー化の推進によって、接合に錫−鉛合金を用いない新たな錫を主成分とする合金（例えばＳｎ−ＡｇやＳｎ−Ａｇ−Ｃｕ）を使用する動きがあるが、従来の錫−鉛共晶はんだと比べ、はんだ接合時に熱負荷がかかるため、接合特性が低下するという問題がある。 On the other hand, with the recent promotion of lead-free, there is a movement to use a new tin-based alloy (for example, Sn-Ag or Sn-Ag-Cu) that does not use a tin-lead alloy for bonding. Compared with the tin-lead eutectic solder, a thermal load is applied during solder joining, which causes a problem that joint characteristics are deteriorated.
そこで無電解ニッケルめっき層と置換型金めっき層の間に無電解パラジウムめっきによりパラジウム皮膜を挟むことで、上記問題を回避する方法が近年行われるようになった。これに用いる無電解パラジウムめっき浴の還元剤には、次亜リン酸化合物、亜リン酸化合物、ギ酸化合物、水素化ホウ素化合物等が用いられるが、特に、次亜リン酸や次亜リン酸ナトリウム等の次亜リン酸塩を含有する無電解パラジウムめっき浴から得られるパラジウム皮膜が、その他の還元剤を使用する無電解パラジウムめっき浴から得られるパラジウム皮膜よりも優れたはんだ接合特性やワイヤボンディング特性を有する。 Therefore, in recent years, a method for avoiding the above problem has been performed by sandwiching a palladium film by electroless palladium plating between the electroless nickel plating layer and the displacement type gold plating layer. Hypophosphorous acid compounds, phosphorous acid compounds, formic acid compounds, borohydride compounds, etc. are used as the reducing agent for the electroless palladium plating bath used for this purpose. In particular, hypophosphorous acid and sodium hypophosphite are used. Palladium films obtained from electroless palladium plating baths containing hypophosphites such as the above are superior to solder films and wire bonding characteristics over palladium films obtained from electroless palladium plating baths using other reducing agents. Have
還元剤として次亜リン酸化合物を含有する無電解パラジウムめっき浴は、古くから数多く提案されている（特公昭４６−２６７６４号公報（特許文献１）参照）が、これらのめっき浴は浴安定性が悪く、短時間で分解してしまうという問題がある。そのため、浴安定性を改善することを目的として添加物を加えることが提案されている（特開昭６２−１２４２８０号公報（特許文献２）、特公昭５３−３７０４５号公報（特許文献３）、特開平５−３９５８０号公報（特許文献４）、特開平８−２６９７２７号公報（特許文献５））が、電子工業等の分野における工業的規模での使用に耐えるほどの保存安定性や連続使用時の浴安定性の改善には至っていない。 Many electroless palladium plating baths containing a hypophosphite compound as a reducing agent have been proposed for a long time (see Japanese Patent Publication No. 46-26764 (Patent Document 1)), but these plating baths have bath stability. However, there is a problem that it decomposes in a short time. Therefore, it has been proposed to add an additive for the purpose of improving bath stability (Japanese Patent Laid-Open No. 62-124280 (Patent Document 2), Japanese Patent Publication No. 53-37045 (Patent Document 3)), JP-A-5-39580 (Patent Document 4) and JP-A-8-269727 (Patent Document 5) have storage stability and continuous use enough to withstand use on an industrial scale in fields such as the electronics industry. The bath stability has not been improved.
本発明は、上記事情に鑑みなされたものであり、工業的使用に耐え得る高い保存安定性を有し、連続使用時においても浴安定性が良好である無電解パラジウムめっき浴及びこれを用いた無電解パラジウムめっき方法を提供することを目的とする。 The present invention has been made in view of the above circumstances, and has an electroless palladium plating bath having high storage stability that can withstand industrial use and good bath stability even during continuous use, and the same. An object is to provide an electroless palladium plating method.
本発明者は、上記課題を解決するため鋭意検討を重ねた結果、次亜リン酸、次亜リン酸塩等の次亜リン酸化合物を還元剤とした無電解パラジウムめっき浴において、安定剤として不飽和カルボン酸、不飽和カルボン酸無水物、不飽和カルボン酸塩及び不飽和カルボン酸誘導体から選ばれる不飽和カルボン酸化合物を添加することにより、無電解パラジウムめっき浴の安定性が顕著に向上すると共に、この無電解パラジウムめっき浴が長期間使用しても、優れたはんだ接合特性とワイヤボンディング特性を有するパラジウム皮膜を形成できることを見出し、本発明をなすに至った。 As a result of intensive studies in order to solve the above problems, the present inventor as a stabilizer in an electroless palladium plating bath using a hypophosphite compound such as hypophosphorous acid and hypophosphite as a reducing agent. By adding an unsaturated carboxylic acid compound selected from unsaturated carboxylic acids, unsaturated carboxylic acid anhydrides, unsaturated carboxylic acid salts and unsaturated carboxylic acid derivatives, the stability of the electroless palladium plating bath is significantly improved. In addition, the present inventors have found that a palladium film having excellent solder bonding characteristics and wire bonding characteristics can be formed even when this electroless palladium plating bath is used for a long period of time.
従って、本発明は、パラジウム化合物と、錯化剤としてアンモニア及びアミン化合物から選ばれる少なくとも１種と、還元剤として次亜リン酸及び次亜リン酸塩から選ばれる少なくとも１種と、不飽和カルボン酸、不飽和カルボン酸無水物、不飽和カルボン酸塩及び不飽和カルボン酸誘導体から選ばれる不飽和カルボン酸化合物を少なくとも１種とを含有することを特徴とする無電解パラジウムめっき浴、及びこの無電解パラジウムめっき浴中に被めっき物を浸漬して該被めっき物上に無電解パラジウムめっき皮膜を形成することを特徴とする無電解パラジウムめっき方法を提供する。 Accordingly, the present invention provides a palladium compound, at least one selected from ammonia and an amine compound as a complexing agent, at least one selected from hypophosphorous acid and hypophosphite as a reducing agent, An electroless palladium plating bath characterized by containing at least one unsaturated carboxylic acid compound selected from acids, unsaturated carboxylic acid anhydrides, unsaturated carboxylic acid salts and unsaturated carboxylic acid derivatives; Provided is an electroless palladium plating method characterized by immersing an object to be plated in an electrolytic palladium plating bath to form an electroless palladium plating film on the object to be plated.
上記不飽和カルボン酸、不飽和カルボン酸無水物、不飽和カルボン酸塩及び不飽和カルボン酸誘導体としては、アクリル酸、プロピオール酸、クロトン酸、イソクロトン酸、メタクリル酸、マレイン酸、フマル酸、シトラコン酸、トランス−２−ブテン−１，４−ジカルボン酸、イタコン酸、テトロル酸、アコニット酸、ムコン酸、ソルビン酸、チグリン酸、アンゲリカ酸、セネシオ酸、グルタコン酸、メサコン酸、オレイン酸、リノール酸及び桂皮酸並びにそれらの無水物、塩及び誘導体が好ましい。 Examples of the unsaturated carboxylic acid, unsaturated carboxylic acid anhydride, unsaturated carboxylic acid salt and unsaturated carboxylic acid derivative include acrylic acid, propiolic acid, crotonic acid, isocrotonic acid, methacrylic acid, maleic acid, fumaric acid, citraconic acid , Trans-2-butene-1,4-dicarboxylic acid, itaconic acid, tetrolic acid, aconitic acid, muconic acid, sorbic acid, tiglic acid, angelic acid, senecioic acid, glutaconic acid, mesaconic acid, oleic acid, linoleic acid and Cinnamic acid and their anhydrides, salts and derivatives are preferred.
本発明の無電解パラジウムめっき浴は、浴安定性が高く、浴の分解が起こりにくく、従来の無電解パラジウムめっき浴に比べて浴寿命が長い。しかも、長時間使用してもめっき皮膜特性への影響もなく、優れたはんだ接合特性及びワイヤボンディング特性を得ることができる。 The electroless palladium plating bath of the present invention has high bath stability, is unlikely to decompose, and has a longer bath life than conventional electroless palladium plating baths. In addition, excellent solder joint characteristics and wire bonding characteristics can be obtained without affecting the plating film characteristics even when used for a long time.
以下、本発明につき、更に詳しく説明する。
本発明の無電解パラジウムめっき浴は、パラジウム化合物と、錯化剤としてアンモニア及びアミン化合物から選ばれる少なくとも１種と、還元剤として次亜リン酸及び次亜リン酸塩から選ばれる次亜リン酸化合物を少なくとも１種と、不飽和カルボン酸、不飽和カルボン酸無水物、不飽和カルボン酸塩及び不飽和カルボン酸誘導体から選ばれる不飽和カルボン酸化合物を少なくとも１種とを含有するものである。
Hereinafter, the present invention will be described in more detail.
The electroless palladium plating bath of the present invention comprises a palladium compound, at least one selected from ammonia and an amine compound as a complexing agent, and hypophosphorous acid selected from hypophosphorous acid and hypophosphite as a reducing agent. It contains at least one compound and at least one unsaturated carboxylic acid compound selected from unsaturated carboxylic acids, unsaturated carboxylic acid anhydrides, unsaturated carboxylic acid salts and unsaturated carboxylic acid derivatives.
ここで、パラジウム化合物としては、水溶性のものであればいずれのものでもよく、例えば塩化パラジウム、硫酸パラジウム、酢酸パラジウム、硝酸パラジウム、テトラアンミンパラジウム塩酸塩などを用いることができる。その含有量はパラジウム濃度として、０．００１〜０．５ｍｏｌ／Ｌ、特に０．００５〜０．１ｍｏｌ／Ｌとすることが望ましい。少なすぎるとめっき速度が低下し、多すぎると皮膜物性が低下するおそれがある。 Here, any palladium compound may be used as long as it is water-soluble. For example, palladium chloride, palladium sulfate, palladium acetate, palladium nitrate, tetraamminepalladium hydrochloride and the like can be used. The content is preferably 0.001 to 0.5 mol / L, particularly 0.005 to 0.1 mol / L, as the palladium concentration. If the amount is too small, the plating rate may decrease, and if it is too large, the film properties may decrease.
また、還元剤としては、次亜リン酸及び次亜リン酸塩から選ばれる少なくとも１種を含有する。その含有量は０．００１〜５ｍｏｌ／Ｌ、特に０．２〜２ｍｏｌ／Ｌとすることが好ましい。少なすぎると析出速度が低下し、多すぎると浴が不安定になるおそれがある。次亜リン酸塩としては、次亜リン酸ナトリウム、次亜リン酸アンモニウムなどが上げられる。 Moreover, as a reducing agent, at least 1 sort (s) chosen from hypophosphorous acid and hypophosphite is contained. The content is preferably 0.001 to 5 mol / L, particularly preferably 0.2 to 2 mol / L. If the amount is too small, the deposition rate decreases, and if the amount is too large, the bath may become unstable. Examples of hypophosphites include sodium hypophosphite and ammonium hypophosphite.
更に、錯化剤としてアンモニア及びアミン化合物から選ばれる少なくとも１種を含有する。その含有量は０．００１〜１０ｍｏｌ／Ｌ、特に０．１〜２ｍｏｌ／Ｌとすることが好ましい。少なすぎると浴の安定性が低下し、多すぎるとめっき速度が低下する。アミン化合物としては、メチルアミン、ジメチルアミン、トリメチルアミン、ベンジルアミン、メチレンジアミン、エチレンジアミン、テトラメチレンジアミン、ジエチレントリアミン、ＥＤＴＡ、ＥＤＴＡナトリウム、ＥＤＴＡカリウム、グリシンなどが挙げられ、これらを１種単独で又は２種以上を併用して使用することができる。 Furthermore, it contains at least one selected from ammonia and an amine compound as a complexing agent. The content is preferably 0.001 to 10 mol / L, particularly 0.1 to 2 mol / L. If the amount is too small, the stability of the bath decreases, and if it is too large, the plating rate decreases. Examples of the amine compound include methylamine, dimethylamine, trimethylamine, benzylamine, methylenediamine, ethylenediamine, tetramethylenediamine, diethylenetriamine, EDTA, EDTA sodium, EDTA potassium, glycine, and the like. The above can be used in combination.
本発明の無電解パラジウムめっき浴は、上記成分と共に、不飽和カルボン酸、不飽和カルボン酸無水物、不飽和カルボン酸塩及び不飽和カルボン酸誘導体から選ばれる不飽和カルボン酸化合物を少なくとも１種含有する。不飽和カルボン酸として具体的には、アクリル酸、プロピオール酸、クロトン酸、イソクロトン酸、メタクリル酸、マレイン酸、フマル酸、シトラコン酸、トランス−２−ブテン−１，４−ジカルボン酸、イタコン酸、テトロル酸、アコニット酸、ムコン酸、ソルビン酸、チグリン酸、アンゲリカ酸、セネシオ酸、グルタコン酸、メサコン酸、オレイン酸、リノール酸、桂皮酸などが挙げられ、また、不飽和カルボン酸無水物及び不飽和カルボン酸塩としては、これら不飽和カルボン酸の酸無水物及びナトリウム塩、アンモニウム塩等の塩が挙げられる。更に、不飽和カルボン酸誘導体としては、メタクリル酸エチル、メタクリル酸フェニル、アクリル酸イソブチル、プロピオール酸メチル、マレイン酸ヒドラジド等が挙げられ、これら不飽和カルボン酸、不飽和カルボン酸無水物、不飽和カルボン酸塩又は不飽和カルボン酸誘導体は１種単独で又は２種以上を併用して使用することができる。 The electroless palladium plating bath of the present invention contains at least one unsaturated carboxylic acid compound selected from unsaturated carboxylic acid, unsaturated carboxylic acid anhydride, unsaturated carboxylic acid salt, and unsaturated carboxylic acid derivative together with the above components. To do. Specific examples of the unsaturated carboxylic acid include acrylic acid, propiolic acid, crotonic acid, isocrotonic acid, methacrylic acid, maleic acid, fumaric acid, citraconic acid, trans-2-butene-1,4-dicarboxylic acid, itaconic acid, Examples include tetrolic acid, aconitic acid, muconic acid, sorbic acid, tiglic acid, angelic acid, senecioic acid, glutaconic acid, mesaconic acid, oleic acid, linoleic acid, cinnamic acid, and unsaturated carboxylic acid anhydrides and unsaturated carboxylic acids. Examples of the saturated carboxylate include acid anhydrides of these unsaturated carboxylic acids and salts such as sodium salts and ammonium salts. Furthermore, examples of the unsaturated carboxylic acid derivative include ethyl methacrylate, phenyl methacrylate, isobutyl acrylate, methyl propiolate, maleic hydrazide, and the like. These unsaturated carboxylic acid, unsaturated carboxylic acid anhydride, unsaturated carboxylic acid derivative, and the like. The acid salts or unsaturated carboxylic acid derivatives can be used alone or in combination of two or more.
特に、不飽和カルボン酸、不飽和カルボン酸無水物、不飽和カルボン酸塩及び不飽和カルボン酸誘導体としては、アクリル酸、メタクリル酸、マレイン酸、フマル酸、イタコン酸、シトラコン酸、メサコン酸並びにそれらの無水物、塩及び誘導体が好ましい。これら不飽和カルボン酸化合物を用いることで、浴安定性に優れ、なおかつはんだ付け性及びワイヤボンディング性等に優れたパラジウム皮膜を得ることができる。 In particular, unsaturated carboxylic acids, unsaturated carboxylic acid anhydrides, unsaturated carboxylic acid salts and unsaturated carboxylic acid derivatives include acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, citraconic acid, mesaconic acid and the like. The anhydrides, salts and derivatives of are preferred. By using these unsaturated carboxylic acid compounds, it is possible to obtain a palladium film that is excellent in bath stability and excellent in solderability and wire bonding properties.
不飽和カルボン酸化合物の含有量は０．００１〜１０ｍｏｌ／Ｌ、特に０．０１〜０．５ｍｏｌ／Ｌとすることが好ましい。この量が少なすぎるとめっき浴の安定性に対する効果が十分に達成されず、また多すぎるとめっき速度が低下する傾向にある。 The content of the unsaturated carboxylic acid compound is preferably 0.001 to 10 mol / L, particularly 0.01 to 0.5 mol / L. When this amount is too small, the effect on the stability of the plating bath is not sufficiently achieved, and when it is too large, the plating rate tends to decrease.
本発明のめっき浴はｐＨ４〜１０、特に６〜８であることが好ましく、ｐＨが低すぎるとめっき浴の安定性が低下し、ｐＨが高すぎるとめっき速度が上昇してはんだ接合特性及びワイヤボンディング特性が低下する傾向にある。 The plating bath of the present invention preferably has a pH of 4 to 10, particularly 6 to 8. If the pH is too low, the stability of the plating bath is lowered, and if the pH is too high, the plating rate is increased to increase the solder joint characteristics and the wire. Bonding characteristics tend to deteriorate.
上述した無電解パラジウムめっき浴は電子部品のボンディング用めっきなどとして好適に使用されるが、これを用いてめっきを行う場合は、このめっき浴中に被めっき物を浸漬すればよい。被めっき物の材質としては、鉄、コバルト、ニッケル、銅、錫、銀、金、白金、パラジウムなどやこれらの合金といった無電解パラジウムめっき皮膜の還元析出に触媒性のある金属を挙げることができる。また、触媒性のない金属であれば、いわゆるガルバニックイニシエーションを行う（被めっき物に対し還元析出が生じるまで電気を与える）か、又は上記触媒活性のある金属のめっき皮膜を形成してからめっきを行えばよく、またガラス、セラミックス、プラスチック等、或いは上記触媒活性のない金属などに対しては常法に従ってパラジウム核などの金属触媒核を付着させた後にめっきを行うことができる。 The electroless palladium plating bath described above is suitably used as a plating for bonding electronic components, but when plating is performed using this, an object to be plated may be immersed in the plating bath. Examples of the material of the object to be plated include metals having catalytic properties for reduction deposition of electroless palladium plating films such as iron, cobalt, nickel, copper, tin, silver, gold, platinum, palladium, and alloys thereof. . If the metal has no catalytic properties, so-called galvanic initiation is performed (electricity is applied to the object to be plated until reduction deposition occurs), or plating is performed after forming a plating film of the above catalytically active metal. In addition, it is possible to perform plating after attaching a metal catalyst nucleus such as a palladium nucleus according to a conventional method for glass, ceramics, plastic, or the like, or a metal having no catalytic activity.
本発明の無電解パラジウムめっき浴は、無電解ニッケルめっき等により形成されたニッケル皮膜上に、パラジウムめっき皮膜を形成することができ、このパラジウムめっき皮膜上に置換金めっきにより金めっき皮膜を形成すれば、プリント配線板や電子部品における表面処理に従来用いられている無電解ニッケル皮膜／置換金めっき皮膜のはんだ付け性及びワイヤボンディング性の低下の問題を、高価な金の使用量を増加させることなく回避することができることから、このような用途に特に有用である。この場合、パラジウムめっき皮膜の厚さは、０．００１〜０．５μｍが好適である。 The electroless palladium plating bath of the present invention can form a palladium plating film on a nickel film formed by electroless nickel plating or the like, and a gold plating film can be formed on the palladium plating film by displacement gold plating. For example, to increase the amount of expensive gold used for the problem of deterioration in solderability and wire bondability of electroless nickel film / displacement gold plating film conventionally used for surface treatment of printed wiring boards and electronic parts. This is particularly useful for such applications. In this case, the thickness of the palladium plating film is preferably 0.001 to 0.5 μm.
なお、めっき温度は３０〜８０℃、特に４０〜７０℃とすることが望ましい。また、必要に応じてめっき浴を攪拌することができる。 The plating temperature is preferably 30 to 80 ° C, particularly 40 to 70 ° C. Moreover, a plating bath can be stirred as needed.
以下、実施例及び比較例を挙げて本発明を具体的に説明するが、本発明は下記実施例に限定されるものではない。 EXAMPLES Hereinafter, although an Example and a comparative example are given and this invention is demonstrated concretely, this invention is not limited to the following Example.
［実施例１〜８、比較例１〜５］
表２及び３に示される組成の無電解パラジウムめっき浴を調製し、めっき浴のめっき性能、めっき皮膜の特性及びめっき浴の安定性を以下の方法で評価した。更に、実施例１，２，５及び６においては、以下に記載の方法で５０℃連続めっき試験を行った後のめっき浴を用いてめっき皮膜特性を評価した。結果を表２及び３に示す。
[Examples 1-8, Comparative Examples 1-5]
Electroless palladium plating baths having the compositions shown in Tables 2 and 3 were prepared, and the plating performance of the plating bath, the characteristics of the plating film, and the stability of the plating bath were evaluated by the following methods. Furthermore, in Examples 1, 2, 5, and 6, the plating film characteristics were evaluated using a plating bath after performing a 50 ° C. continuous plating test by the method described below. The results are shown in Tables 2 and 3.
めっき皮膜外観
銅板（大きさ１０ｃｍ×２０ｃｍ 厚さ０．１ｍｍ）に対して、表１に示される処理（１）〜（５）〔前処理〕、及び処理（６）〜（８）〔めっき処理〕を施し、得られためっき皮膜の外観を目視にて評価し、外観ムラがない場合を「良」、外観ムラがある場合を「不良」とした。
Treatment (1) to (5) [pretreatment] and treatment (6) to (8) [plating treatment] shown in Table 1 for the plated copper appearance copper plate (size 10 cm × 20 cm, thickness 0.1 mm) The appearance of the plating film thus obtained was visually evaluated, and “good” was given when there was no unevenness in appearance, and “bad” when there was appearance unevenness.
析出速度
銅板（大きさ１０ｃｍ×２０ｃｍ 厚さ０．１ｍｍ）に対して、表１に示される処理（１）〜（６）を施し、表２及び３に示される無電解パラジウムめっき浴（１Ｌ）に６０分間浸漬し、形成されたパラジウム皮膜の厚さから析出速度を算出した。
The deposition rate copper plate (size 10 cm × 20 cm, thickness 0.1 mm) was subjected to the treatments (1) to (6) shown in Table 1, and the electroless palladium plating bath (1 L) shown in Tables 2 and 3 For 60 minutes, and the deposition rate was calculated from the thickness of the formed palladium film.
５０℃連続めっき試験
銅板（大きさ１０ｃｍ×２０ｃｍ 厚さ０．１ｍｍ）に対して、表１に示される処理（１）〜（５）を施し、更に表１の（６）の無電解Ｎｉ−Ｐめっき浴を用いて膜厚５μｍのＮｉ−Ｐ皮膜を形成した後、表２及び３に示される無電解パラジウムめっき浴に浸漬し、パラジウム皮膜を連続形成した。なお、２時間経過毎にめっき浴中のパラジウムの減量分を補充した。
The 50 ° C. continuous plating test copper plate (size 10 cm × 20 cm, thickness 0.1 mm) was subjected to the treatments (1) to (5) shown in Table 1, and the electroless Ni— in Table 1 (6). After forming a 5 μm-thick Ni—P film using a P plating bath, it was immersed in an electroless palladium plating bath shown in Tables 2 and 3 to continuously form a palladium film. Note that the reduced amount of palladium in the plating bath was replenished every 2 hours.
８０℃加熱試験
めっき浴５００ｍｌをポリエチレン製容器中に密閉したものを８０℃恒温槽中で保存した。
80 ° C. Heat Test A 500 ml plating bath sealed in a polyethylene container was stored in an 80 ° C. constant temperature bath.
室温放置試験
めっき浴５００ｍｌをポリエチレン製容器中に密閉したものを室温で保存した。
Room temperature standing test 500 ml of plating bath sealed in a polyethylene container was stored at room temperature.
はんだ接合性
Ｄａｇｅ社製ボンドテスタＳＥＲＩＥＳ４０００により１条件につき２０点評価し、合金層部分で断裂又は切断せずに、はんだ部分が切断した場合を「良」、合金層部分で一部でも断裂又は切断した場合を「不良」とした。なお、測定条件は以下のとおりである。
Solder Joinability 20 points per condition was evaluated by a bond tester SERIES 4000 manufactured by Dage, and when the solder part was cut without being cut or cut at the alloy layer part, “good”, even at the alloy layer part was partly cut or cut. The case was determined as “bad”. The measurement conditions are as follows.
〔測定条件〕
測定方式：ボールプルテスト
基板：上村工業（株）製ＢＧＡ基板（パット径 φ０．５ｍｍ）
半田ボール：千住金属製 φ０．６ｍｍ Ｓｎ−３．０Ａｇ−０．５Ｃｕ
リフロー：マルチリフロー（タムラ製作所製）
リフロー条件：Ｔｏｐ ２６０℃
リフロー回数：１回及び５回
フラックス：千住金属製 ５２９Ｄ−１（ＲＭＡタイプ）
テストスピード：１７０μｍ／秒
半田マウント後エージング：２〜３時間
〔Measurement condition〕
Measuring method: Ball pull test Substrate: BGA substrate manufactured by Uemura Kogyo Co., Ltd. (pad diameter φ0.5 mm)
Solder ball: Senju Metal φ0.6mm Sn-3.0Ag-0.5Cu
Reflow: Multi-reflow (made by Tamura Seisakusho)
Reflow conditions: Top 260 ° C
Reflow frequency: 1 time and 5 times Flux: 529D-1 (RMA type) made by Senju Metal
Test speed: 170 μm / sec Aging after solder mounting: 2-3 hours
ワイヤボンディング性
Ｋ＆Ｓ社製４５２４Ａワイヤプルテスタによりワイヤボンディングを行い、Ｄａｇｅ社製ボンドテスタＳＥＲＩＥＳ４０００により１条件につき１０点評価し、第１又は第２ボンド部分で断裂又は切断せずに、ワイヤ自体が切断した場合を「良」、第１又は第２ボンド部分で一部でも断裂又は切断した場合を「不良」とした。なお、測定条件は以下のとおりである。
Wire bonding property Wire bonding was performed with a K & S 4524A wire pull tester, 10 points were evaluated per condition with a Dage bond tester SERIES 4000, and the wire itself was cut without being broken or cut at the first or second bond part. The case was “good”, and the case where even a part of the first or second bond portion was torn or cut was “bad”. The measurement conditions are as follows.
〔測定条件〕
キャピラリー：４０４７２−００１０−３２０１
ワイヤ：１Ｍｉｌ−Ｇｏｌｄ
ステージ温度：１８０℃
超音波（ｍＷ）：２５（第１），１１５(第２)
ボンディング時間：（ミリ秒）：３６（第１），１３６（第２）
引っ張り力（ｇｆ）：４４（第１），７０（第２）
ステップ（第１から第２への長さ）：０．８１２ｍｍ
測定方式：ワイヤープルテスト
基板：上村工業（株）ＢＧＡ基板
テストスピード：１７０μｍ／秒
〔Measurement condition〕
Capillary: 40472-0010-3201
Wire: 1 Mil-Gold
Stage temperature: 180 ° C
Ultrasound (mW): 25 (first), 115 (second)
Bonding time: (milliseconds): 36 (first), 136 (second)
Tensile force (gf): 44 (first), 70 (second)
Step (length from the first to the second): 0.812mm
Measurement method: Wire pull test Substrate: UGAMURA BGA substrate Test speed: 170 μm / sec
Claims (3)