JP2010208067A - 塗装鋼板および外装部材 - Google Patents
塗装鋼板および外装部材 Download PDFInfo
- Publication number
- JP2010208067A JP2010208067A JP2009054499A JP2009054499A JP2010208067A JP 2010208067 A JP2010208067 A JP 2010208067A JP 2009054499 A JP2009054499 A JP 2009054499A JP 2009054499 A JP2009054499 A JP 2009054499A JP 2010208067 A JP2010208067 A JP 2010208067A
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- mass
- film
- coated steel
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】質量%で、Al:5〜95%を含有し、残部元素としてZn:95%以下、Mg:10%以下:Si:12%以下の1種以上を含有し、Al、Zn、Mg、Si以外の元素の合計含有量が3%以下(0%を含む)である溶融めっき浴を用いてAl含有めっき層2を形成しためっき鋼板の、当該めっき層の上に、化成処理皮膜3、下塗り塗膜4、上塗り塗膜5を有する塗装鋼板において、前記下塗り塗膜中に顔料としてリン酸マンガン、亜リン酸マンガンの1種以上が合計10〜35質量%含有されていることを特徴とする塗装鋼板。下塗り塗膜の平均厚さ(乾燥後、鋼板片面あたり)は2〜25μmの範囲とすることが望ましい。
【選択図】図1
Description
〔めっき鋼板〕
塗装原板となるめっき鋼板としては、溶融Zn−Al系めっき鋼板または溶融Al系めっき鋼板が採用される。これらは亜鉛めっき鋼板よりもめっき表面の耐食性に優れる。特に溶融Zn−Al系めっき鋼板は亜鉛による犠牲防食作用を併せ持つ。めっき基材の鋼板は用途に応じて従来一般的なものが使用できる。
溶融めっき鋼板を塗装原板として使用する場合には、多くの場合、下地処理として化成処理が施される。以前はクロメート処理が多用されていたが、最近では環境に配慮してクロムフリー処理が主流となっている。ただし、クロムフリー処理によりクロメート処理と同等以上の耐食性を安定して確保することは必ずしも容易ではなく、その意味でも後述の防錆顔料の配合が重要となる。クロムフリー処理としては、例えばエッチング作用のあるチタン化合物、フッ化物を有機樹脂に溶解した水溶液を用いて有機−無機複合皮膜を形成する処理等、種々のものが知られている。本発明では、これら公知の手法で形成した化成処理層を有するものが利用できる。特にチタン化合物、フッ化物を含有する無機−有機複合皮膜型のクロムフリー化成処理層を有するものが好適である。
本発明では、下塗り塗膜(プライマー)中に顔料としてリン酸マンガン、亜リン酸マンガンの1種以上を配合させる。具体的には例えばリン酸第一マンガン;Mn(H2PO4)2、リン酸第二マンガン;MnH3(PO4)2、亜リン酸マンガン;MnHPO3の1種以上を合計10〜35質量%配合させることができる。この含有量は乾燥塗膜中の質量%であり、塗料調合時には揮発成分の含有量を考慮して顔料の添加量を設定する。上記顔料の合計含有量が10質量%未満では金属露出部へ保護皮膜を迅速に形成させる作用が小さく、結果的に従来の防錆顔料を添加した場合に対するメリットが十分に発揮されないことがある。下塗り塗膜の厚さが2〜5μm程度と比較的薄い場合は上記顔料の合計含有量を20質量%以上とすることがより効果的である。一方、35質量%を超えて多量に含有させても効果は飽和し不経済となり、また、塗布性や塗膜密着性を損なう要因となる。リン酸マンガン、亜リン酸マンガンの合計含有量は30質量%以下とすることがより好ましく、25質量%以下とすることが一層好ましい。配合させる顔料粉末は例えばレーザー回折式粒度分布測定装置を用いた体積平均粒子径D50において2〜10μm程度とすればよい。なお、他の顔料を複合して配合させても良いが、その場合は全ての顔料の合計量を35質量%以下とすることがより好ましい。
上塗り塗膜は、従来から塗装鋼板に使用されている種々のものが適用対象となる。上塗り塗膜の乾燥後の平均厚さは10〜40μm程度である。塗装方法も従来一般的な手法が採用できる。
以下の3種類の公知の方法で化成処理層を形成させた。
(化成処理A);ヘキサフルオロチタン酸:55g/L、ヘキサフルオロジルコニウム酸:10g/L、アミノメチル置換ポリビニルフェノール:72g/Lを含有する塗布型クロムフリー化成処理液をめっき層表面に常温で塗布し、水洗することなく100℃で乾燥させた。上面、裏面とも下記の付着量とした。
Ti換算付着量:10mg/m2、Zr換算付着量:2.5mg/m2、F換算付着量:20mg/m2、ポリビニルフェノール換算付着量:40mg/m2
リン酸第一マンガン(平均粒子径D50;約6μm)、リン酸第二マンガン(平均粒子径D50;約6μm)、亜リン酸マンガン(平均粒子径D50;約6μm)の各粉末を顔料として用意した。その他の顔料として表1に示す各種公知の顔料を用意した。エポキシ樹脂をベースとし、表1に示す顔料を配合した下塗り塗料を調合し、バーコーター法により化成処理層の上に塗布し、215℃で乾燥・焼付けを行って下塗り塗膜を形成させた。上面、裏面とも乾燥塗膜の平均厚さが5μmとなるようにした。表1中の組成は乾燥後の下塗り塗膜中における値である。
ポリエステル樹脂をベースとする上塗り塗料を調合し、バーコーター法により下塗り塗膜の上に塗布し、215℃で乾燥・焼付けを行って上塗り塗膜を形成させた。乾燥後の上塗り塗膜の平均厚さは、上面が11μm、裏面が5μmとなるようにした。
上面の上塗り塗膜が曲げの外側となるように常温で2t密着曲げ加工を行い、曲げ加工部(曲げの外側表面)についてJIS Z1522に規定されるセロハン粘着テープを貼付した後、剥がす方法で塗膜剥離試験を行い、曲げ加工部の外側表面の面積に占める塗膜剥離が生じた面積の割合を測定し、以下の基準で塗膜密着性を評価した。○評価以上を合格と判定した。
◎:塗膜剥離が認められない
○:塗膜剥離面積率:5%未満
△: 〃 :5%以上20%未満
×: 〃 :20%以上
各塗装鋼板からせん断加工により切り出した板材を用いて、上記と同様の2t密着曲げ加工を施した試験片を用意した。この試験片には曲げ加工部と切断端面があり、それらの箇所でめっき金属および鋼素地が露出している。酸性雨を模擬した試験液として、0.1%食塩水を硫酸でpH=4に調整した液を調製した。各試験片について、「上記試験液による塩水噴霧(35℃×1h)→乾燥(50℃×4h)→湿潤(相対湿度98%、50℃×3h)」を1サイクルとする促進試験を300サイクル実施した。
白錆評価は、曲げ加工部の外側表面に占める白錆発生部分の面積率を測定することにより行った。
塗膜下腐食評価は、光学顕微鏡を用いて断面から曲げ加工部の下塗り塗膜下に生じている腐食箇所の面積を測定し、測定面積に占める腐食箇所(めっき金属の溶解が生じた部分)の面積率を求めることにより行った。
また、切断端面の上面塗膜部についてエッジクリープ長さ(図1のxに相当する長さ)を測定した。切断端面の全域を調べて、最もエッジクリープ長さの長い部分の値を当該試験片のエッジクリープ長さの成績値として採用し、評価した。
各評価基準は以下のとおりとし、それぞれ○評価以上を合格と判定した。
◎:白錆発生面積率:10%未満
○: 〃 :10%以上20%未満
△: 〃 :20%以上50%未満
×: 〃 :50%以上
(塗膜下腐食評価)
◎:腐食面積率:3%未満
○: 〃 :3%以上5%未満
△: 〃 :5%以上10%未満
×: 〃 :10%以上
(エッジクリープ評価)
◎:エッジクリープ長さ:1.0mm未満
○: 〃 :1.0mm以上2.0mm未満
△: 〃 :2.0mm以上3.0mm未満
×: 〃 :3.0mm以上
促進試験の場合と同様の2t密着曲げ加工を施した試験片を用いて、1年間の大気暴露試験を行った。暴露地は千葉県市川市の海岸から5mの地点である。暴露角度は南向き35°であり、傾斜の下部に曲げ加工部が位置するように試験片を設置した。
1年間の大気暴露後に、曲げ加工部について上記促進試験の場合と同様の方法で白錆評価および塗膜下腐食評価を行い、○評価以上を合格と判定した。
また、切断端面の上面塗膜部について上記促進試験の場合と同様の方法でエッジクリープ長さを求め、下記の基準で評価して、○評価以上を合格と判定した。
◎:エッジクリープ長さ:0.5mm未満
○: 〃 :0.5mm以上1.0mm未満
△: 〃 :1.0mm以上1.5mm未満
×: 〃 :1.5mm以上
これらの結果を表2に示す。
2 めっき層
3 化成処理層
4 下塗り塗膜
5 上塗り塗膜
6 切断端面
10 腐食箇所
11 保護皮膜
20 エッジクリープ
Claims (3)
- 質量%で、Al:5〜95%を含有し、残部元素としてZn:95%以下、Mg:10%以下:Si:12%以下の1種以上を含有し、Al、Zn、Mg、Si以外の元素の合計含有量が3%以下(0%を含む)である溶融めっき浴を用いてAl含有めっき層を形成しためっき鋼板の、当該めっき層の上に、化成処理皮膜、下塗り塗膜、上塗り塗膜を有する塗装鋼板において、前記下塗り塗膜中に顔料としてリン酸マンガン、亜リン酸マンガンの1種以上が合計10〜35質量%含有されていることを特徴とする塗装鋼板。
- 下塗り塗膜の平均厚さが2〜25μmである請求項1に記載の塗装鋼板。
- 請求項1に記載の塗装鋼板を素材として成形され、切断端面の金属露出部および曲げ加工部の金属露出部の少なくとも一方を持つ建築物の外装部材。