JP2010013666A - ポリウレタン−ビニル重合体複合樹脂水性分散液 - Google Patents
ポリウレタン−ビニル重合体複合樹脂水性分散液 Download PDFInfo
- Publication number
- JP2010013666A JP2010013666A JP2009242066A JP2009242066A JP2010013666A JP 2010013666 A JP2010013666 A JP 2010013666A JP 2009242066 A JP2009242066 A JP 2009242066A JP 2009242066 A JP2009242066 A JP 2009242066A JP 2010013666 A JP2010013666 A JP 2010013666A
- Authority
- JP
- Japan
- Prior art keywords
- component
- polyurethane
- vinyl polymer
- diol
- composite resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ポリウレタン(A)とビニル重合体(B)とを水性媒体中で分散してなるポリウレタン−ビニル重合体複合樹脂水性分散液において、上記(A)成分を構成するジオール成分は、所定の構造式を有し、数平均分子量が500〜5000であるポリカーボネートジオールを含有し、このポリカーボネートジオールの連結基Rとしてヘキサメチレン単位を有するものが、ジオール成分全体の40モル%以上有し、上記(B)成分のガラス転移温度(Tg)は20℃以上、80℃以下であり、かつ、(A)成分100重量部あたりの(B)成分の含有量が20重量部以上、400重量部以下であるポリウレタン−ビニル重合体複合樹脂水性分散液を用いる。
【選択図】なし
Description
さらに、水性分散液なので、環境面への負荷も小さくできる。
なお、上記のビニル基を有する単量体は、単独で用いてもよく、2種以上を混合して用いてもよい。
まず、ラジカル重合性単量体の存在下に、上記ポリカーボネートジオール、及びカルボキシル基含有ポリオールを含むジオール成分と、ポリイソシアネートとを反応させて、カルボキシル基を含有するポリウレタンを製造する(a)工程を行う。
また、上記ポリオールとしてポリカーボネートジオールを含むポリオールを用い、さらに、カルボキシル基を有するポリオールを併用するのが好ましい。
[ガラス転移温度]
ビニル重合体中の各構成単量体a,b,…の構成重量分率をWa,Wb,…とし、各構成単量体a,b,…の単独重合体のガラス転移温度Tga,Tgb,…としたとき、下記の式で、共重合体であるビニル重合体のTgの値を求める。
1/Tg=Wa/Tga+Wb/Tgb+…
基材として、市販のアルミホイル(住軽アルミ箔(株)製、厚み25μm)の鏡面部分に、バーコーターNo.10を用いて、6g/m2の塗布量(乾燥後)となるように、得られた組成物を塗工した。そして、80℃で20秒間乾燥した後、室温で3日間、乾燥した。
得られた積層体の塗工面に市販のセロハンテープを貼り、剥がしたときの状態を下記の基準で評価した。
○:塗膜の剥離なし
△:塗膜の一部分が剥離した
×:塗膜の全面が剥離した
上記の密着性試験で得られた積層体の塗工面を上にした状態で、未塗工の基材(鏡面でない側)と重ね合わせた。その上に、0.5g/m2となるように荷重をかけ、50℃で24時間放置した。その後、積層体同士を剥がしたときの状態で評価した。
○:抵抗なく剥離できた
△:剥離する際、少し抵抗があった
×:剥離する際、抵抗があった
[ポリカーボネートジオール]
・(株)クラレ製:クラレポリオールC−2090…1,6−へキサンジオール/3−メチル−1,5−ペンタンジオール=10/90(モル比)、OHV:56mgKOH/g、以下、「C2090」と称する。なお、「OHV」は、JISK 1557で測定された水酸基価(単位:mgKOH/g)を意味する。
・ジメチロールプロピオン酸…マリンクロッド ケミカル(Mallinckrodt Chemical Inc)社製、以下、「DPMA」と称する。
・4,4’−ジシクロヘキシルメタンジイソシアネート…住友バイエルウレタン(株)製:デスモジュールW、以下、「H12MDI」と称する。
・ジブチルチンジラウレート…和光純薬工業(株)製:試薬、以下、「DBTBL」と称する。
[重合安定剤]
・ハイドロキノン…和光純薬工業(株)製:試薬、以下、「HQ」と称する。
・メタクリル酸メチル…三菱レイヨン(株)製、以下、「MMA」と称する。
・アクリル酸ブチル…三菱化学(株)製、以下、「BA」と称する。
・レドックス系開始剤…7重量%t−ブチルハイドロパーオキサイド水溶液(以下、「H70」と称する。)と、1重量%アスコルビン酸水溶液(以下、「AsA」と称する。)とを用いた。
・トリエチルアミン…和光純薬工業(株)製、以下、「TEA」と称する。
温度計、撹拌装置及び還流冷却管を備えた4つ口フラスコに、表1に示す仕込みの各成分を加え、内温50℃とした。次いで、表1に示す添加物の各成分を添加して90℃に加温し、5時間反応させてウレタンポリマーを得た。
次いで、表1に示す量の水を、50℃で15分間かけて滴下し、乳白色の透明性のある分散液を得た。
Claims (3)
- ポリウレタン(A)とビニル重合体(B)とを水性媒体中で分散してなるポリウレタン−ビニル重合体複合樹脂水性分散液の製造方法において、
上記(A)成分及び(B)成分は、下記の特徴を有し、
下記の(a)〜(d)の工程を順に行うことにより、(A)成分100重量部あたりの(B)成分の含有量が20重量部以上、400重量部以下であるポリウレタン−ビニル重合体複合樹脂水性分散液を製造する、ポリウレタン−ビニル重合体複合樹脂水性分散液の製造方法。
・(A)成分:この(A)成分を構成するジオール成分は、その構造式が下記式(1)で示され、数平均分子量が500〜5000であるポリカーボネートジオールを含有し、
このポリカーボネートジオールの使用量は、ジオール成分全体の40重量%以上90重量%以下であり、
かつ、このポリカーボネートジオールのうち、下記式(1)中の連結基Rとしてヘキサメチレン単位を有するものの含有量が、ジオール成分全体の40モル%以上であり、
一方、(A)成分を構成するジオール成分として、カルボキシル基を有するポリオールを含む。
・(B)成分:ガラス転移温度(Tg)が20℃以上、80℃以下である。
・(a)工程:活性水素を有さないラジカル重合性単量体の存在下に、上記ポリカーボネートジオールを含むジオール成分と、ポリイソシアネートとを反応させて、カルボキシル基を含有するポリウレタンを製造する工程
・(b)工程:カルボキシル基を塩基性化合物により中和する工程
・(c)工程:水を加えて上記ポリウレタンとラジカル重合性単量体とを水中に分散させて水性分散液を得る工程
・(d)工程:上記ラジカル重合性単量体を重合させて、ビニル重合体を得る工程 - アンダーコート剤の一部として用いられる、請求項1に記載のポリウレタン−ビニル重合体複合樹脂水性分散液の製造方法。
- 上記アンダーコート剤は、アルミニウム基材用として用いられる請求項2に記載のポリウレタン−ビニル重合体複合樹脂水性分散液の製造方法。