JP2009167075A - 光学ガラス組成物、プリフォーム及び光学素子 - Google Patents
光学ガラス組成物、プリフォーム及び光学素子 Download PDFInfo
- Publication number
- JP2009167075A JP2009167075A JP2008114130A JP2008114130A JP2009167075A JP 2009167075 A JP2009167075 A JP 2009167075A JP 2008114130 A JP2008114130 A JP 2008114130A JP 2008114130 A JP2008114130 A JP 2008114130A JP 2009167075 A JP2009167075 A JP 2009167075A
- Authority
- JP
- Japan
- Prior art keywords
- optical
- less
- refractive index
- preform
- glass composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】重量%表示で、SiO2を1.0%以上12.0%以下、B2O3を8.0%以上18.0%以下、ZnOを0%以上6.0%以下、ZrO2を1.0%以上10.0%以下、La2O3を25.0%以上47.0%以下、R2O(ただし、RはLi、Na及びKの少なくとも1つ)を0%以上5.0%以下、Nb2O5を0%以上15.0%以下、TiO2を0%以上7.0%以下、Ta2O5を0%以上15.0%以下、Nb2O5+TiO2+Ta2O5を1.0%以上、Gd2O3を0%以上25.5%以下、WO3を0.5%以上15.0%以下、及びGd2O3+WO3を0.5%以上26.0%以下含み、ndが1.88以上1.92以下で、νdが33以上37以下である光学ガラス組成物、プリフォーム及び光学素子。
【選択図】なし
Description
(1)重量%表示で、
SiO2を1.0%以上12.0%以下、
B2O3を8.0%以上18.0%以下、
ZnOを0%以上6.0%以下、
ZrO2を1.0%以上10.0%以下、
La2O3を25.0%以上47.0%以下、
R2O(ただし、RはLi、Na及びKの少なくとも1つ)を0%以上5.0%以下、
Nb2O5を0%以上15.0%以下、
TiO2を0%以上7.0%以下、
Ta2O5を0%以上15.0%以下、
Nb2O5+TiO2+Ta2O5を1.0%以上、
Gd2O3を0%以上25.5%以下、
WO3を0.5%以上15.0%以下、及び
Gd2O3+WO3を0.5%以上26.0%以下含み、
d線に対する屈折率(nd)が1.88以上1.92以下で、d線に対するアッベ数(νd)が33以上37以下である、光学ガラス組成物、
(2)上記(1)項に記載の光学ガラス組成物からなり、かつ加熱により軟化させて少なくともプレス成形に供するための、プリフォーム、並びに
(3)上記(1)項に記載の光学ガラス組成物からなる、光学素子
に関する。
まず、本発明の実施の形態1に係る光学ガラス組成物について詳細に説明する。該光学ガラス組成物は、以下の組成を有する。
次に、本発明の実施の形態2に係るプリフォーム及びその製造方法について詳細に説明する。該プリフォームは、加熱により軟化させて少なくともプレス成形に供するためのもので、最終目的とするプレス成形品の大きさや形状に応じて、該プリフォームの重量や形状は適宜決定される。本実施の形態2に係るプリフォームは、上記実施の形態1に係る光学ガラス組成物からなるものであり、実施の形態1における光学ガラス組成物の諸特性を損なわずに得ることができる。
次に、本発明の実施の形態3に係る光学素子について説明する。実施の形態3に係る光学素子は、上記実施の形態1に係る光学ガラス組成物の組成が決定する光学恒数を有している。すなわち、d線に対する屈折率(nd)が1.88〜1.92であり、d線に対するアッベ数(νd)が33〜37である。また、該光学素子は、可視領域において着色による光吸収量の少ない特性を併せ持つ。実施の形態1に係る光学ガラス組成物を用いた光学素子は、デジタルカメラ、ビデオカメラ、モバイル機器等の光学系に好適な光学素子である。
(1)各表における組成欄の各成分割合は、バッチ原料から計算した重量%で表す。
(2)nd及びνdは、室温における屈折率及びアッベ数である。
Claims (3)
- 重量%表示で、
SiO2を1.0%以上12.0%以下、
B2O3を8.0%以上18.0%以下、
ZnOを0%以上6.0%以下、
ZrO2を1.0%以上10.0%以下、
La2O3を25.0%以上47.0%以下、
R2O(ただし、RはLi、Na及びKの少なくとも1つ)を0%以上5.0%以下、
Nb2O5を0%以上15.0%以下、
TiO2を0%以上7.0%以下、
Ta2O5を0%以上15.0%以下、
Nb2O5+TiO2+Ta2O5を1.0%以上、
Gd2O3を0%以上25.5%以下、
WO3を0.5%以上15.0%以下、及び
Gd2O3+WO3を0.5%以上26.0%以下含み、
d線に対する屈折率(nd)が1.88以上1.92以下で、d線に対するアッベ数(νd)が33以上37以下である、光学ガラス組成物。 - 請求項1に記載の光学ガラス組成物からなり、かつ加熱により軟化させて少なくともプレス成形に供するための、プリフォーム。
- 請求項1に記載の光学ガラス組成物からなる、光学素子。