JP2008246909A - 感熱転写インクシート、インクカートリッジ、感熱転写インクシートの染料層用塗布組成物および感熱転写記録方法 - Google Patents
感熱転写インクシート、インクカートリッジ、感熱転写インクシートの染料層用塗布組成物および感熱転写記録方法 Download PDFInfo
- Publication number
- JP2008246909A JP2008246909A JP2007092239A JP2007092239A JP2008246909A JP 2008246909 A JP2008246909 A JP 2008246909A JP 2007092239 A JP2007092239 A JP 2007092239A JP 2007092239 A JP2007092239 A JP 2007092239A JP 2008246909 A JP2008246909 A JP 2008246909A
- Authority
- JP
- Japan
- Prior art keywords
- heat
- ink sheet
- sensitive transfer
- dye
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)支持体上に熱移行性染料が樹脂バインダー中に含有されてなる染料層を設けた感熱転写インクシートにおいて、前記染料層に少なくとも1種の下記一般式[1]で表される化合物で修飾されたポリビニルアセタールを含有することを特徴とする感熱転写インクシート。
(2)前記一般式[1]において、R1およびR2のいずれか一方が、炭素数4〜50の分岐の炭化水素基であるか、またはR1とR2が互いに結合して環状の炭化水素を形成する基であることを特徴とする(1)に記載の感熱転写インクシート。
(3)前記一般式[1]2において、R1およびR2のいずれか一方が、炭素数8〜40の分岐の炭化水素基であるか、またはR1とR2が互いに結合して環状の炭化水素を形成する基であることを特徴とする(1)に記載の感熱転写インクシート。
(4)前記(1)〜(3)のいずれか1項に記載の感熱転写インクシートが充填されていることを特徴とするインクカートリッジ。
(5)支持体上にポリマーラテックスを含有するインク受容層を有する受像シート上に(1)〜(3)のいずれか1項に記載の感熱転写インクシートを用いて画像を形成することを特徴とする感熱転写記録方法。
(6)熱移行性染料と少なくとも1種の下記一般式[1]で表される化合物で修飾されたポリビニルアセタールを含有することを特徴とする感熱転写インクシートの染料層用塗布組成物。
本発明のポリビニルアセタールは一般式[1]で表されるアルデヒドおよび/またはケトンで修飾されてなる。本発明のポリビニルアセタールは、一般式[1]で表されるケトンで修飾されてなるいわゆるケタールも包含するものである。
ここで、R1およびR2のいずれか一方が、炭素数4〜50の分岐の炭化水素基であるか、またはR1とR2が互いに結合して環状の炭化水素を形成する基であることが好ましく、炭素数8〜40の分岐の炭化水素基であるか、またはR1とR2が互いに結合して環状の炭化水素を形成する基であることがより好ましく、炭素数12〜30の分岐の炭化水素基であるか、またはR1とR2が互いに結合して環状の炭化水素を形成する基であることがさらに好ましい。
R1とR2が互いに結合して形成される環状の炭化水素は、5員〜7員環の炭化水素(該環としては、例えば、シクロペンタン環、シクロヘキサン環、シクロペンタン環)が好ましく、該環は他の環で縮合環を形成してもよい。該縮合環は、炭化水素環が好ましく、複数の環の縮合環も好ましい。ここで、形成される環は、飽和環であっても不飽和環(ただし芳香環は原理的に形成できるものでなく、芳香環であることはない)のいずれかであり、飽和環が好ましい。
一般式[1]で示される化合物は必要に応じて2種類以上組み合わせて使用してもよい。
アセタール化に用いられる酸触媒としては、塩酸、硫酸、リン酸等の無機酸、酢酸、p−トルエンスルホン酸等が挙げられる。また、触媒の使用量は、反応に用いられるアルデヒドおよび/またはケトン1モルに対して0.005〜0.2モルが好ましい。
アセタール化の反応温度は、20℃〜100℃程度であり、40℃〜90℃が好ましい。
イエロー画像を形成することができる熱移行性イエロー染料を含有するイエローインクシートとしては、例えば、特開平1−225592号公報などに記載されたものを好ましく用いることができる。
次に、本発明のインクシートと組み合わせて用いられる受容シートについて説明する。
感熱転写受像シートは、支持体上に染料受容層(受容層)が形成されている。受容層と支持体との間には下地層が形成されていることが好ましく、例えば白地調整層、帯電調節層、接着層、プライマー層が形成される。また、下地層と支持体との間には断熱層が形成されていることが好ましい。支持体と受容層との間にある各層を単に「中間層」といい、上述の下地層や断熱層が含まれる。感熱転写受像シートは、少なくとも1層の受容層および少なくとも1層の中間層を含有する。支持体の裏面側にはカール調整層、筆記層、帯電調整層が形成されていることが好ましい。
受容層は、インクシートから移行してくる染料を受容し、形成された画像を維持する役割を果たす。
そのため受容層には染着しやすい樹脂(染着性受容ポリマー)が用いられる。
例えば、ポリエチレン、ポリプロピレン等のポリオレフィン樹脂、ポリ塩化ビニル、ポリ塩化ビニリデン等のハロゲン化樹脂、ポリ酢酸ビニル、ポリアクリル酸エステル等のビニル系樹脂、およびその共重合体、ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル系樹脂、ポリスチレン系樹脂、ポリアミド系樹脂、ポリカーボネート、フェノール樹脂、ポリウレタン、エポキシ樹脂、ポリサルフォン、ブチラール樹脂、メラミン樹脂、ポリビニルアルコール、エチレンやプロピレン等のオレフィンと他のビニル系モノマーとの共重合体、塩化ビニル酢酸ビニル共重合体、スチレンアクリル共重合体、アイオノマー、セルロース樹脂、天然ゴム、合成ゴム等の単体または混合物を用いることができるがこれらに限定されない。受容層に用いられる受容ポリマーはラテックス化されていることが好ましい。
ポリマーラテックスについて説明する。感熱転写受像シートにおいて、受容層に用いうるポリマーラテックスは水不溶な疎水性ポリマーが微細な粒子として水溶性の分散媒中に分散したものである。分散状態としてはポリマーが分散媒中に乳化されているもの、乳化重合されたもの、ミセル分散されたもの、あるいはポリマー分子中に部分的に親水的な構造を持ち分子鎖自身が分子状分散したものなどいずれでもよい。なおポリマーラテックスについては、奥田平,稲垣寛編集,「合成樹脂エマルジョン」,高分子刊行会発行(1978年)、杉村孝明,片岡靖男,鈴木聡一,笠原啓司編集,「合成ラテックスの応用」,高分子刊行会発行(1993年)、室井宗一著,「合成ラテックスの化学」,高分子刊行会発行(1970年)、三代澤良明監修,「水性コーティング材料の開発と応用」,シーエムシー出版(2004年)および特開昭64−538号公報などに記載されている。分散粒子の平均粒子サイズは1〜50000nm、より好ましくは5〜1000nm程度の範囲が好ましい。分散粒子の粒径分布に関しては特に制限は無く、広い粒径分布を持つものでも単分散の粒径分布を持つものでもよい。
(a)共役ジエン類:1,3−ペンタジエン、イソプレン、1−フェニル−1,3−ブタジエン、1−α−ナフチル−1,3−ブタジエン、1−β−ナフチル−1,3−ブタジエン、シクロペンタジエン等。
(b) オレフィン類:エチレン、プロピレン、塩化ビニル、塩化ビニリデン、6−ヒドロキシ−1−ヘキセン、4−ペンテン酸、8−ノネン酸メチル、ビニルスルホン酸、トリメチルビニルシラン、トリメトキシビニルシラン、1,4−ジビニルシクロヘキサン、1,2,5−トリビニルシクロヘキサン等。
(e) 不飽和ニトリル類:アクリロニトリル、メタクリロニトリル等。
(f) スチレンおよびその誘導体:スチレン、ビニルトルエン、p−tert−ブチルスチレン、ビニル安息香酸、ビニル安息香酸メチル、α−メチルスチレン、p−クロロメチルスチレン、ビニルナフタレン、p−ヒドロキシメチルスチレン、p−スチレンスルホン酸ナトリウム塩、p−スチレンスルフィン酸カリウム塩、p−アミノメチルスチレン、1,4−ジビニルベンゼン等。
(g) ビニルエーテル類:メチルビニルエーテル、ブチルビニルエーテル、メトキシエチルビニルエーテル等。
(h) ビニルエステル類:酢酸ビニル、プロピオン酸ビニル、安息香酸ビニル、サリチル酸ビニルクロロ酢酸ビニル等。
(i) α,β−不飽和カルボン酸およびその塩類:アクリル酸、メタクリル酸、イタコン酸、マレイン酸、アクリル酸ナトリウム、メタクリル酸アンモニウム、イタコン酸カリウム等。
(j) その他の重合性単量体:N−ビニルイミダゾール、4−ビニルピリジン、N−ビニルピロリドン、2−ビニルオキサゾリン、2−イソプロペニルオキサゾリン、ジビニルスルホン等。
(重合体の合成)
<AP−1の合成>
攪拌機、還流冷却器を備えた反応器に、ポリビニルアルコール(PVA110、クラレ(株)製)20g、塩化メチレン400g、塩酸 2.0g、およびA−7 96gを加え40℃で40時間加熱して反応を完結させた。次に、反応液をメタノール中に再沈殿させて反応生成物を得た。質量平均分子量は1.6×106であった。
(2−1)試料101(本発明)の作製
厚さ6.0μmのポリエステルフィルム(ルミラー、商品名、(株)東レ製)を基材フィルムとして用いた。そのフィルム背面側に耐熱スリップ層(厚み1μm)を形成し、かつ表面側に下記組成のイエロー、マゼンタ、シアン組成物を、それぞれ単色に塗布(乾膜時の塗布量1g/m2)した。
イエローインキ
染料(マクロレックスイエロー6G、商品名、バイエル社製) 5.5質量部
重合体AP−1 4.4質量部
メチルエチルケトン/トルエン(質量比1/1) 90質量部
マゼンタインキ
マゼンタ染料(ディスパーズレッド60) 5.5質量部
重合体AP−1 4.4質量部
メチルエチルケトン/トルエン(質量比1/1) 90質量部
シアンインキ
シアン染料(ディスパーズレッド63) 5.5質量部
重合体AP−1 4.4質量部
メチルエチルケトン/トルエン(質量比1/1) 90質量部
次に、上記例示化合物AP−1をAP−7に変えた以外は試料101の作製と同様にして、本発明の試料102を作製した。
(2−3)試料103(本発明)の作製
次に、上記例示化合物AP−1をAP−11に変えた以外は試料101の作製と同様にして、本発明の試料103を作製した。
(2−4)試料104(本発明)の作製
次に上記例示化合物AP−1をAP−18に変えた以外は試料101の作製と同様にして、本発明の試料104を作製した。
(2−5)試料105(本発明)の作製
次に、上記例示化合物AP−1をAP−22に変えた以外は試料101の作製と同様にして、本発明の試料105を作製した。
厚さ6.0μmのポリエステルフィルム(ルミラー、商品名、(株)東レ製)を基材フィルムとして用いた。そのフィルム背面側に耐熱スリップ層(厚み1μm)を形成し、かつ表面側に下記組成のイエロー、マゼンタ、シアン組成物を、それぞれ単色に塗布(乾膜時の塗布量1g/m2)した。
イエローインキ
染料(マクロレックスイエロー6G、商品名、バイエル社製) 5.5質量部
ポリビニルブチラール 4.5質量部
(エスレックBX−1、商品名、積水化学工業(株)製)
メチルエチルケトン/トルエン(質量比1/1) 90質量部
マゼンタインキ
マゼンタ染料(ディスパーズレッド60) 5.5質量部
ポリビニルブチラール 4.5質量部
(エスレックBX−1、商品名、積水化学工業(株)製)
メチルエチルケトン/トルエン(質量比1/1) 90質量部
シアンインキ
シアン染料(ディスパーズレッド63) 5.5質量部
ポリビニルブチラール 4.5質量部
(エスレックBX−1、商品名、積水化学工業(株)製)
メチルエチルケトン/トルエン(質量比1/1) 90質量部
特開平4−45993号公報に記載の実施例1のインクシートを作製した。
(2−8)試料108(比較例)の作製
特開2002―307844号公報に記載の実施例1のインクシートを作製した。
<受像シート1>
ポリエチレンで両面ラミネートした紙支持体表面に、コロナ放電処理を施した後ドデシルベンゼンスルホン酸ナトリウムを含むゼラチン下塗層を設けた。さらに下記組成の中間層Aをバーコーターにより塗布し乾燥した後、引き続いて下記組成の受容層Aをバーコーターにより塗布し乾燥させた。バーコーター塗布は40℃で行い、乾燥は各層50℃で16時間行った。それぞれの乾燥時の塗布量が中間層A:1.0g/m2、受容層A:2.5g/m2となるように塗布を行った。
中間層A
ポリエステル樹脂(バイロン200、商品名、東洋紡積(株)製) 10質量部
蛍光増白剤(Uvitex OB、商品名、チバガイギー社製) 1質量部
酸化チタン 30質量部
メチルエチルケトン/トルエン(質量比1/1) 90質量部
受容層A
ポリエステル樹脂 100質量部
(特開平2-265789号公報の実施例1に記載の樹脂)
アミノ変性シリコーン 5質量部
(信越化学工業(株)社製、商品名、X−22−3050C)
エポキシ変性シリコーン
(信越化学工業(株)社製、商品名、X−22−300E) 5質量部
メチルエチルケトン/トルエン(質量比1/1) 400質量部
上記の各インクシートを使用し、上記受像シート1に、日本電産コパル社製昇華型プリンターASK2000(商品名)に装填可能なように加工し、高速プリントモードで最高濃度を得られる設定で黒色ベタの画像を出力した。
上記の条件で得られた黒画像のVisual濃度をPhotographic Densitometer(X-Rite incorporated社製)で測定した。表1に試料106の転写濃度を100としたときの相対値を示す。
(インク融着性評価)
インク融着性は、画像のDmaxが得られる印画部分で溶着状態を以下の基準で判断した。
評価ランク
5:受像シートがインクシートからスムーズに剥がれ、受像シートにインクの融着(張り付き)が全く認められない。
4:融着が発生した濃度領域の印画面積に対して、融着した面積が1%以下であった。
3:融着が発生した濃度領域の印画面積に対して、融着した面積が1%を超え、10%以下であった。
2:融着が発生した濃度領域の印画面積に対して、融着した面積が10%を超え、20%以下であった。
1:融着が発生した濃度領域の印画面積に対して、融着した面積が20%を超えた。
得られた結果を、表1に示す。
感熱転写用インクシートと受像シートをそれぞれ染料層と受像層が接触するように重ねあわせ、感熱転写用インクシートの表面温度が70℃になるように熱ロールラミネーターに通した後、染着層に移行した染料の濃度をPhotographic Densitometer(X-Rite incorporated社製)で測定し、試験前後の濃度の変化率(ΔD)を算出した。
本発明例の試料101から105はいずれも相対転写濃度に優れ、インクの融着がないことがわかった。このように本発明の樹脂バインダーを使用することにより高感度で面状欠陥のない感熱転写インクシートを得ることができた。
受像シート1を下記受像シート2に代えたこと以外は実施例1と同様にして試料を作製した。
<受像シート2>
ポリエチレンで両面ラミネートした紙支持体表面に、コロナ放電処理を施した後ドデシルベンゼンスルホン酸ナトリウムを含むゼラチン下塗層を設けた。この上に、米国特許第2,761,791号明細書に記載の第9図に例示された方法により、前記組成の中間層B、受容層Bを支持体側からこの順に積層させた状態で重層塗布を行った。塗布後すぐに50℃16時間乾燥させた。それぞれの乾燥時の塗布量は中間層B:15g/m2、中間層A:1.0g/m2、受容層A:2.5g/m2となるように塗布を行った。
中間層B
中空ポリマーラテックス 563質量部
(MH5055、商品名、日本ゼオン(株)製)
ゼラチン 120質量部
ここで、中空ポリマーラテックスは外径0.5μmの中空構造ポリマーの水分散体である。
受容層B
重合体P−9 48質量部
ベンゾトリアゾール系紫外線吸収剤ポリマーラテックス 15質量部
(ULS1700、商品名、一方社油脂工業(株)製)
モンタン酸ワックス(J537、商品名、中京油脂(株)製) 10質量部
この結果を下記表2にまとめた。
Claims (6)
- 前記一般式[1]において、R1およびR2のいずれか一方が、炭素数4〜50の分岐の炭化水素基であるか、またはR1とR2が互いに結合して環状の炭化水素を形成する基であることを特徴とする請求項1に記載の感熱転写インクシート。
- 前記一般式[1]において、R1およびR2のいずれか一方が、炭素数8〜40の分岐の炭化水素基であるか、またはR1とR2が互いに結合して環状の炭化水素を形成する基であることを特徴とする請求項1に記載の感熱転写インクシート。
- 請求項1〜3のいずれか1項に記載の感熱転写インクシートが充填されていることを特徴とするインクカートリッジ。
- 支持体上にポリマーラテックスを含有するインク受容層を有する受像シート上に請求項1〜3のいずれか1項に記載の感熱転写インクシートを用いて画像を形成することを特徴とする感熱転写記録方法。