JP2007520599A - 表面処理された炭酸カルシウム粒子 - Google Patents
表面処理された炭酸カルシウム粒子 Download PDFInfo
- Publication number
- JP2007520599A JP2007520599A JP2006550169A JP2006550169A JP2007520599A JP 2007520599 A JP2007520599 A JP 2007520599A JP 2006550169 A JP2006550169 A JP 2006550169A JP 2006550169 A JP2006550169 A JP 2006550169A JP 2007520599 A JP2007520599 A JP 2007520599A
- Authority
- JP
- Japan
- Prior art keywords
- calcium carbonate
- coating agent
- acid
- coating
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
合成によって製造された炭酸カルシウムが、機能的な充填剤又は添加剤としてのその使用のための必要条件を実質的により良く満たす。
通常、合成炭酸カルシウムは、水酸化カルシウムと二酸化炭素を反応させることによって調製される。
沈降炭酸カルシウムの加工特性は、脂肪酸、ワックス、無機塩などでコーティングすることによって影響され得ることが知られている。
従って、コーティングによって例えば、封止剤の保存寿命が改善され得るか、又は材料への充填剤の導入に必要とされる有機マトリックスを有する炭酸カルシウムの湿潤性、又は降伏値又は分散性が影響され得る。
欧州特許第1279433号明細書は、それ自体が公知のコーティング剤で複合的にコーティングすることにより、粒状材料、例えば過炭酸ナトリウムの特性を改善するための方法を開示している。ここで、粒子上のコーティング剤は、コーティングマトリックスを形成し、コーティング剤による粒子の完全な被覆が行われる。
本発明の粒子は、炭酸カルシウムのコア及び該コアの表面の少なくとも一部を被覆しているコーティングを含み、該コーティングは少なくとも2つの異なる連続した工程で行われ、各工程は異なるコーティング剤を用いる。
合成炭酸カルシウムは、任意の方法で得ることができる。これらの方法中では、石灰乳から出発する二酸化炭素による炭酸カルシウムの沈殿(炭酸塩化方法)又は石灰水から出発してアルカリ金属炭酸塩を加えることによる沈殿(苛性化(caustification)方法)又は塩化カルシウムを含有する溶液から出発してアルカリ金属炭酸塩の添加による沈殿が考慮され得る。
本発明の情況内のさらに好ましい方法では、炭酸カルシウムが二酸化炭素含有ガスによる石灰乳の炭酸塩化によって沈殿される。この好ましい方法では、石灰乳が一般的には生石灰を水で消化することによって得られ、及び二酸化炭素含有ガスが有利には濃厚なガス、特に石灰窯ガスである。
この方法で沈殿した炭酸カルシウムは、任意の公知な技術、例えば濾過、噴霧及び遠心分離によって調製媒体から任意に単離することができる。濾過及び遠心分離による技術が好ましい。
本発明では、本発明の炭酸カルシウムの比表面積が、通常は2m2/g以上、好ましくは10m2/g以上及びさらに好ましくは50m2/g以上である。70m2/g以上の比表面積が特に推奨される。炭酸カルシウムの粒子の比表面積は、一般的には300m2/g以下、有利には150m2/g以下である。100m2/g以下の比表面積の値が、特に好ましい。比表面積は、標準的なBET方法(ISO 9277 標準)によって測定される。
本発明の炭酸カルシウムの粒子は、特許出願WO 03004414に記載及び請求されている方法を用いて得られる種々のナノスケールの構造-ナノファゴット、ナノロザリオ及びナノアコーディオン-を示し得る。ナノファゴット、ナノロザリオ及びナノアコーディオンの定義は、文献WO 03004414の5頁33行目〜7頁9行目に与えられており、及び参照としてここに組み込まれる。
本発明の第一のコーティング剤は、アルキルスルフェート、スルホン酸、カルボン酸、それらの塩及びそれらのエステル、脂肪アルコール、多価アルコール又はそれらの混合物から選択することができる。
本発明の第一の実施態様では、第一のコーティング剤が、カルボン酸、それらの塩及びそれらのエステルから選択される。
カルボン酸は、脂肪族又は芳香族でよい。脂肪族カルボン酸が好ましい。
第三の変形では、第一のコーティング剤が脂肪族カルボン酸の塩であり、これはカルボン酸のカルシウム塩でもよい。しかし、第一のコーティング剤はまた、例えば脂肪族カルボン酸のナトリウム、カリウム又はアンモニウムの塩の形状で存在してもよい。
第四の変形では、第一のコーティング剤が、脂肪族カルボン酸のエステルであり、以下の化学式R1COOR2を有する。R1及びR2は同じでも異なっていてもよく、及び任意の脂肪族又は芳香族、直鎖又は分枝又は環式、置換又は非置換、飽和又は不飽和の炭化水素基を意味する。炭化水素基は、通常は6以上、好ましくは8以上、さらに好ましくは10以上及び最も好ましくは14以上の炭素原子の数を有する。炭化水素基は、一般的には32以下、有利には28以下、さらに有利には24以下及び最も有利には22以下の炭素原子の数を有する。
コーティングされた炭酸カルシウム粒子上の第一のコーティング剤の量は、一般的には0.1質量%以上、好ましくは0.5質量%以上及びさらに特に1質量%以上である。この含有量は、通常20質量%以下及びさらに特に15質量%以下である。5質量%以下の含有量が特に好適である。
多価アルコールは、上記のように定義される。グリセロール及び1,2-エタンジオールが好ましく、及びグリセロールが最も好ましい。
カルボン酸のエステルは、脂肪族又は芳香族カルボン酸のエステルにすることができる。芳香族カルボン酸のエステルが好ましく、及びフタル酸のエステルが最も好ましい。フタル酸は、オルト-、メタ-及びパラ-異性体又はそれらの混合物の任意の1つでよい。フタル酸のエステルは、モノ-及びジ-アルキルフタレート及びそれらの混合物から選択される。ジアルキルフタレートが好ましい。“アルキル”により炭化水素鎖を意味することを意図し、これは、直鎖又は分枝又は環式、飽和又は不飽和、置換又は非置換であり、通常1以上、好ましくは4以上、さらに好ましくは6以上及び最も好ましくは8以上の炭素原子の数を含む。炭素原子のその数は、一般的には24以下、有利には20以下、さらに有利には18以下及び最も有利には14以下である。ジ-n-オクチル-イソフタレートが特に最も好ましいエステルである。
何らかの理論で確定されている訳ではないが、第一のコーティング後に残っているCaCO3表面上の何もない領域は、第二のコーティング剤で被覆されると信じられている。
本発明に関連して、第一及び第二のコーティング剤は、同じ材料であると同様に異なる材料からなってもよい。第一及び第二のコーティング剤は異なるのが好ましい。
炭酸カルシウム粒子の表面処理のための本発明の方法では、コーティング剤が炭酸カルシウム粒子に適用され、まず炭酸カルシウム粒子を第一のコーティング剤と接触させ、及び続いて第二のコーティング剤を適用すると考えられる。
炭酸カルシウム粒子は、例えばミリングプロセス中及び/又は沈殿後に、それ自体公知の手法により液体又は固体形態の第一のコーティング剤と接触され、該コーティング剤は、炭酸カルシウム粒子の表面上に保持される。
第二の実施態様では、第一のコーティング剤による炭酸カルシウム粒子の処理を、水系又は有機系に溶解したコーティング剤で行う。
第三の実施態様では、第一のコーティング剤による炭酸カルシウム粒子の処理を、固体、液体又は気体形態の純粋なコーティング剤で行う。
コーティングされた炭酸カルシウム粒子は、上記のように液体、溶解、固体又は気体形態の第二のコーティング剤と本質的に公知の手法で再び接触され、第二のコーティング剤は、炭酸カルシウムの表面上に保持される。
溶解形態で第二のコーティング剤を用いるのが好ましい。
本発明の表面処理された炭酸カルシウム粒子は、優れた分散性を有することが見出された。それらは、凝集体を形成する低い傾向を示す。存在する表面処理された炭酸カルシウム粒子の全ての凝集体は、材料への導入に際してより良く分散する。
脂肪酸でコーティングされたCaCO3の降伏値は、例えば30Pa〜350Paの範囲で制御可能である。多価アルコール又は置換されている多価アルコールによる追加のコーティングの結果として、降伏値の増加が達成され得る。降伏値は、一般的には100Pa以上、好ましくは200Pa以上、さらに好ましくは600Pa以上である。1000Pa以上の値が最も好ましい。
使用者のための利点は、第一に降伏値の定常的な増加にある。第二のコーティングの結果として、使用者が一定の処方で作業するのを可能にする非常に一定な質を製造することができる。調合された材料の流動学的な挙動のその後の調整は、不必要である。さらに、分散プロセスは促進されて、一方では使用者の処理能力を増加させるが、他方で材料のより良い表面の平滑も達成される。さらに、非常に高い降伏値を有する表面処理された炭酸カルシウム粒子の使用により、封止剤における炭酸カルシウムの割合が減少され得、これは材料の密度に関してプラスの効果を有する。特に自動車産業部門では、低密度を有する封止剤、底部封止材料及び接着剤が好ましい。
炭酸カルシウム粒子を含有する可塑剤混合物の流動学的性質は、以下の手順に従って得られた。以下の調合物は、35gの可塑剤(例えば、ジ-オクチルフタレート、ジ-イソノニルフタレート、アジペート、セバケート)、25gのポリビニルクロライドポリマー(例えば、Vestolit、Vinolit)、4gの溶媒(例えば、炭化水素の誘導体)、16.2gの天然炭酸カルシウム、0.5gのヒュームドシリカ、2.3gの乾燥剤(例えば、CaO)、1gの促進剤(例えば、ポリアミン、ポリアミド)及び16gのコーティングされた炭酸カルシウム粒子を、溶解用ディスク攪拌器(直径80mm)を備えたINOX-ビーカー(直径120mm、高さ85mm)で混合することによって調製した。該混合物は、1分間で250rpm及び10分間で800rpmでディスクを回転させることによって均質化した。生じた混合物の底部を流動学的測定に用いた。
・熱平衡に到達するまでプローブを5分間25℃に保つ、
・2分にわたって0〜100s-1に速め、120のデータポイントを測定する、
・100s-1で1分保ち、20のデータポイントを測定する、
・2分にわたって100〜0s-1に遅らせ、120のデータポイントを測定する。
150g/Lの濃度の水酸化カルシウムを有する石灰乳を、反応器において18℃まで加熱した。この出発温度に到達した後、CO2含有ガスを反応器に通し、CO2供給を一定に保った。
CO2/空気混合物 : 30:70
ガス供給 : 1m3/時間(10Lの石灰乳に基づく)
沈殿時間 : 100分
1035gの水を75℃まで加熱し、及び122gのステアリン酸を加えた。この混合物を、15分間加熱した。60mLの25質量%アンモニウム溶液を攪拌しながら加え、及び該混合物を30分間均質化した。淡い色の均質なエマルジョンは、10質量%のステアリン酸を含んでいた。
例2で調製したコーティング剤を、例1で調製した20Lの炭酸カルシウム懸濁液に入れ、及び該混合物を75℃で1時間攪拌した。
コーティングされた炭酸カルシウムを分離し、乾燥し及び粉砕した。この手法でコーティングした炭酸カルシウムは、3質量%のステアレートのコーティングを含んでいた。
グリセロールを1:3の比で水に溶解させ、及び沈降炭酸カルシウム粒子(コーティングされていないもの及びコーティングされたもの)上に噴霧した。
サンプルを50℃で乾燥し、及び続いてピン止めされたディスクミルにおいて18000rpmで粉砕した。
沈降炭酸カルシウム(例1)を、例3と同じようにして、炭酸カルシウム100g当たり2gのステアリン酸でコーティングした。異なる量のグリセロールを第二のコーティングとして適用し、及び流動性を決定した。
沈降炭酸カルシウム(例1)を、例3と同じようにして、炭酸カルシウム100g当たり3gのステアリン酸でコーティングした。異なる量のグリセロールを第二のコーティングとして適用し、及び流動性を決定した。
Claims (9)
- 炭酸カルシウムのコア及び該コアの表面の少なくとも一部を被覆しているコーティングを含む粒子であって、該コーティングは少なくとも2種の異なる連続した工程で行われ、各工程は異なるコーティング剤を用いる、粒子。
- 第一の工程で用いられるアルキルスルフェート、スルホン酸、カルボン酸、それらの塩及びそれらのエステル、脂肪アルコール、多価アルコール又はそれらの混合物から選択される第一のコーティング剤、及び第二の工程で用いられる多価アルコール、カルボン酸のエステル、又はそれらの混合物から選択される第二のコーティング剤を含む、請求項1記載の粒子。
- カルボン酸が脂肪酸であり、及び多価アルコールがジオール又はトリオールである、請求項2記載の粒子。
- カルボン酸がステアリン酸であり、及び多価アルコールが1,2-エタンジオール又はグリセロールである、請求項2記載の粒子。
- 第一のコーティング剤として用いられるカルボン酸が脂肪酸であり、及び第二のコーティング剤として用いられるカルボン酸のエステルがフタル酸エステルである、請求項2記載の粒子。
- 請求項1〜5のいずれか1項に記載の粒子の調製方法であって、該粒子をまず第一のコーティング剤と接触させ、及び続いて第二のコーティング剤を該粒子に適用する、方法。
- 第二のコーティング剤が、液体、溶解、固体又は気体形態で適用される、請求項6記載の方法。
- 充填剤としての、請求項1〜5のいずれか1項に記載の粒子の使用。
- ゴム、インク、プラスチゾル、シーラント、紙、塗料、コーティング、医薬品、食品及び化粧品における、請求項8記載の使用。