JP2007168794A - Sealed container - Google Patents

Sealed container Download PDF

Info

Publication number
JP2007168794A
JP2007168794A JP2005342170A JP2005342170A JP2007168794A JP 2007168794 A JP2007168794 A JP 2007168794A JP 2005342170 A JP2005342170 A JP 2005342170A JP 2005342170 A JP2005342170 A JP 2005342170A JP 2007168794 A JP2007168794 A JP 2007168794A
Authority
JP
Japan
Prior art keywords
sealed
main body
terephthalate resin
container
copolymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2005342170A
Other languages
Japanese (ja)
Other versions
JP4843298B2 (en
Inventor
Tomohito Hayama
山 知 人 葉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sun A Kaken Co Ltd
Original Assignee
Sun A Kaken Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sun A Kaken Co Ltd filed Critical Sun A Kaken Co Ltd
Priority to JP2005342170A priority Critical patent/JP4843298B2/en
Publication of JP2007168794A publication Critical patent/JP2007168794A/en
Application granted granted Critical
Publication of JP4843298B2 publication Critical patent/JP4843298B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide a sealed container whose lid is not made of a polycarbonate that may have a harmful influence on human health, and which is sealed while retaining transparency and heat resistance. <P>SOLUTION: The sealed container 10 has a dome lid 2 which is heat-sealed to be easily unsealed. The dome lid 2 is made of a mixture of a polybutylene terephthalate resin copolymer and a polyethylene terephthalate resin homopolymer or polyethylene terephthalate resin copolymer. The polybutylene terephthalate resin copolymer is a copolymer composed of a terephthalic acid component, a tetramethylene glycol component, a polyvalent carboxylic acid component, and a polyvalent alcohol component. The polyethylene terephthalate resin homopolymer is composed of terephthalic acid and an ethylene glycol component. The polyethylene terephthalate resin copolymer is composed of a copolymer composed of: terephthalic acid component and an ethylene glycol component, or 1,4-cyclohexanedimethanol component, a polyvalent carboxylic acid component; and a polyvalent alcohol component. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、密封容器に係り、特に、合成樹脂製のドーム蓋を本体容器にヒートシール密封した密封容器で、本体容器内の被包装物（被包装物は、例えば、食品用密封容器であり、例えば、食品である。）がよく見える透明性に優れた密封容器に関する。     The present invention relates to a sealed container, in particular, a sealed container in which a synthetic resin dome lid is heat-sealed and sealed to a main body container, and the packaged object in the main body container (the packaged object is, for example, a sealed container for foods) , For example, food).

従来、ポリカーボネートを使用している蓋を有した密封容器がある（特許文献１参照）。
特許第３１３０７９３号公報 Conventionally, there is a sealed container having a lid using polycarbonate (see Patent Document 1).
Japanese Patent No. 3130793

しかしながら、従来の密封容器にあっては、ポリカーボネートの原料であるビスフェノールAに内分泌かく乱作用の疑いがあり、該ビスフェノールAが食品に溶出し、人の健康に影響を与える恐れがあるという問題点があった。
本発明は、上述した問題点を除去するようにした密封容器を提供することを目的としている。 However, in conventional sealed containers, there is a suspicion of endocrine disrupting action in bisphenol A, which is a raw material of polycarbonate, and there is a problem that the bisphenol A may be eluted into food and affect human health. there were.
An object of the present invention is to provide a sealed container in which the above-described problems are eliminated.

本発明の密封容器は、フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、この密封容器内には、被包装物が内在し、前記ドーム蓋は、ポリブチレンテレフタレート系樹脂の共重合体であり、前記ポリブチレンテレフタレート系樹脂の共重合体は、テレフタル酸成分とテトラメチレングリコール成分と多価カルボン酸成分と多価アルコール成分との共重合体である。     The sealed container of the present invention has a concave main body container having a flange portion, a dome lid that covers the opening of the main body container and forms a convex portion above, and is heat-sealed at the flange portion, and The heat-sealed dome lid and the flange portion of the main body container are easy-open sealed containers, in which the package is contained, and the dome cover is a polybutylene terephthalate system A copolymer of a resin, and the copolymer of the polybutylene terephthalate resin is a copolymer of a terephthalic acid component, a tetramethylene glycol component, a polyvalent carboxylic acid component, and a polyhydric alcohol component.

また、請求項２記載の密封容器は、フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体とポリブチレンテレフタレート系樹脂の単独重合体の混合物であり、前記ポリブチレンテレフタレート系樹脂の単独重合体は、テレフタル酸とテトラメチレングリコールの重合体である。     The sealed container according to claim 2 has a concave main body container having a flange portion and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side. The sealed and heat-sealed dome lid and the flange portion of the main body container are easy-opening sealed containers, and in the sealed container, an object to be packaged is contained, A polybutylene terephthalate resin copolymer according to claim 1 and a polybutylene terephthalate resin homopolymer, wherein the polybutylene terephthalate resin homopolymer is a polymer of terephthalic acid and tetramethylene glycol. It is.

また、請求項３記載の密封容器は、フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体とポリエチレンテレフタレート系樹脂の単独重合体の混合物であり、前記ポリエチレンテレフタレート系樹脂の単独重合体は、テレフタル酸とエチレングリコールの重合体である。     Further, the sealed container according to claim 3 has a concave main body container having a flange portion and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side. The sealed and heat-sealed dome lid and the flange portion of the main body container are easy-opening sealed containers, and in the sealed container, an object to be packaged is contained, 2. The polybutylene terephthalate resin copolymer according to claim 1 and a polyethylene terephthalate resin homopolymer, wherein the polyethylene terephthalate resin homopolymer is a polymer of terephthalic acid and ethylene glycol.

また、請求項４記載の密封容器は、フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体とポリエチレンテレフタレート系樹脂の共重合体の混合物であり、前記ポリエチレンテレフタレート系樹脂の共重合体は、テレフタル酸成分とエチレングリコール成分又は１．４シクロヘキサンジメタノール成分と多価カルボン酸成分と多価アルコール成分との共重合体である。     Further, the sealed container according to claim 4 has a concave main body container having a flange portion, a dome lid that covers the opening of the main body container and forms a convex portion on the upper side. The sealed and heat-sealed dome lid and the flange portion of the main body container are easy-opening sealed containers, and in the sealed container, an object to be packaged is contained, It is a mixture of a copolymer of polybutylene terephthalate resin and a copolymer of polyethylene terephthalate resin according to claim 1, wherein the copolymer of polyethylene terephthalate resin is a terephthalic acid component and an ethylene glycol component or 1.4. It is a copolymer of a cyclohexanedimethanol component, a polyvalent carboxylic acid component, and a polyhydric alcohol component.

また、請求項５記載の密封容器は、フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体と請求項３記載のポリエチレンテレフタレート系樹脂の単独重合体と請求項４記載のポリエチレンテレフタレート系樹脂の共重合体の混合物である。     Further, the sealed container according to claim 5 has a concave main body container having a flange portion, a dome lid that covers the opening of the main body container and forms a convex portion on the upper side. The sealed and heat-sealed dome lid and the flange portion of the main body container are easy-opening sealed containers, and in the sealed container, an object to be packaged is contained, A mixture of a copolymer of polybutylene terephthalate resin according to claim 1, a homopolymer of polyethylene terephthalate resin according to claim 3, and a copolymer of polyethylene terephthalate resin according to claim 4.

また、請求項６記載の密封容器は、フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体と請求項２記載のポリブチレンテレフタレート系樹脂の単独重合体と請求項３記載のポリエチレンテレフタレート系樹脂の単独重合体の混合物である。     The sealed container according to claim 6 has a concave main body container having a flange portion and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side. The sealed and heat-sealed dome lid and the flange portion of the main body container are easy-opening sealed containers, and in the sealed container, an object to be packaged is contained, A copolymer of the polybutylene terephthalate resin according to claim 1, a homopolymer of polybutylene terephthalate resin according to claim 2, and a homopolymer of polyethylene terephthalate resin according to claim 3.

また、請求項７記載の密封容器は、フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体と請求項２記載のポリブチレンテレフタレート系樹脂の単独重合体と請求項４記載のポリエチレンテレフタレート系樹脂の共重合体の混合物である。     Further, the sealed container according to claim 7 has a concave main body container having a flange portion, a dome lid that covers the opening of the main body container and forms a convex portion on the upper side. The sealed and heat-sealed dome lid and the flange portion of the main body container are easy-opening sealed containers, and in the sealed container, an object to be packaged is contained, A copolymer of the polybutylene terephthalate resin copolymer according to claim 1, the polybutylene terephthalate resin homopolymer according to claim 2, and the polyethylene terephthalate resin copolymer according to claim 4.

また、請求項８記載の密封容器は、フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体と請求項２記載のポリブチレンテレフタレート系樹脂の単独重合体と請求項３記載のポリエチレンテレフタレート系樹脂の単独重合体と請求項４記載のポリエチレンテレフタレート系樹脂の共重合体の混合物である。     Further, the sealed container according to claim 8 has a concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side. The sealed and heat-sealed dome lid and the flange portion of the main body container are easy-opening sealed containers, and in the sealed container, an object to be packaged is contained, A copolymer of the polybutylene terephthalate resin according to claim 1, a homopolymer of the polybutylene terephthalate resin according to claim 2, a homopolymer of the polyethylene terephthalate resin according to claim 3, and the polyethylene according to claim 4. It is a mixture of copolymers of terephthalate resin.

また、請求項９記載の密封容器は、請求項１乃至８記載の密封容器において、本体容器がポリプロピレン樹脂を主成分とする外層基材層とし、最内面層に共重合ポリエステル系樹脂層が積層された多層シートから成形されたものである。     The sealed container according to claim 9 is the sealed container according to claims 1 to 8, wherein the main body container is an outer layer base material layer mainly composed of polypropylene resin, and a copolymer polyester resin layer is laminated on the innermost surface layer. The multilayer sheet is formed.

本発明の密封容器によれば、従来のように蓋に健康に影響を与える恐れがあるポリカーボネートを使用せず、しかも、透明性と耐熱性（例えば、２００℃に耐える耐熱性）を有して密封されているため、被包装物を良好に包装することができる。     According to the sealed container of the present invention, there is no use of polycarbonate which may affect the health of the lid as in the prior art, and it has transparency and heat resistance (for example, heat resistance that can withstand 200 ° C.). Since it is sealed, it is possible to package an article to be packaged satisfactorily.

本発明の密封容器の一実施例を図面を参照して説明する。
図１乃至図３において、１０は密封容器で、密封容器１０は、フランジ部１１を有する凹状の本体容器１と、この本体容器１の開口部を覆い、上方に凸型部を形成するドーム蓋２を有している。フランジ部１１において、ヒートシールされ、かつヒートシールされたドーム蓋２と本体容器１のフランジ部１１は易開封性である密封容器１０となっている。なお、密封容器１０内には、被包装物（図示せず）が内在し、上方に凸型部を形成するドーム蓋２は、ボリューム感でディスプレー効果が大きく、しかも、密封容器１０は、従来の嵌合方式と異なり、外部からの細菌の侵入が防止でき、チルド流通に適している。更に、より望ましくは、密封容器１０内をガス置換（ガスは、例えば、窒素であり、置換の量は、例えば、９８％である。）し、ヒートシール密封すれば、チルドにより食品の賞味期限を長くすることができる。 An embodiment of the sealed container of the present invention will be described with reference to the drawings.
1 to 3, reference numeral 10 denotes a sealed container. The sealed container 10 covers a concave main body container 1 having a flange portion 11, and a dome lid that covers an opening of the main body container 1 and forms a convex portion upward. 2 has. In the flange portion 11, the heat-sealed and heat-sealed dome lid 2 and the flange portion 11 of the main body container 1 form a sealed container 10 that is easily openable. The sealed container 10 contains an object to be packaged (not shown), and the dome lid 2 that forms a convex portion on the upper side has a large volume and a large display effect. Unlike the fitting method, bacteria can be prevented from entering from the outside, making it suitable for chilled distribution. More preferably, if the inside of the sealed container 10 is replaced with gas (the gas is, for example, nitrogen, and the amount of replacement is, for example, 98%), and heat sealed, the shelf life of the food is reduced by chilling. Can be lengthened.

ドーム蓋２の樹脂組成物は、ポリブチレンテレフタレート系樹脂（ＰＢＴ系樹脂）の共重合体である。このポリブチレンテレフタレート系樹脂の共重合体は、テレフタル酸成分とテトラメチレングリコール成分と多価カルボン酸成分と多価アルコール成分との共重合体である。
多価カルボン酸を例示すれば、テレフタル酸、イソフタル酸、２．６ーナフタレンジカルボン酸、その他の芳香族ジカルボン酸、アジピン酸、その他の脂肪族ジカルボン酸、３価以上の多価カルボン酸であり、
また、多価アルコールを例示すれば、エチレングリコール、１．４ーブタンジオール、ネオペンチルグリコール、その他のジオール、ジエチレングリコール、ポリテトラメチレングリコール、その他のポリアルキレングリコール、１．４ーシクロヘキサンジメタノール、単位モノマー中の炭素数が２つ以上であるポリエーテルグリコールである。
ポリブチレンテレフタレート系樹脂の共重合体は、例えば、ポリプラスチック株式会社製 商品名 ジュラネックス６００ＪＰである。 The resin composition of the dome lid 2 is a copolymer of polybutylene terephthalate resin (PBT resin). The copolymer of the polybutylene terephthalate resin is a copolymer of a terephthalic acid component, a tetramethylene glycol component, a polyvalent carboxylic acid component, and a polyhydric alcohol component.
Examples of polyvalent carboxylic acids are terephthalic acid, isophthalic acid, 2.6-naphthalenedicarboxylic acid, other aromatic dicarboxylic acids, adipic acid, other aliphatic dicarboxylic acids, and trivalent or higher polyvalent carboxylic acids. ,
Examples of polyhydric alcohols include ethylene glycol, 1.4-butanediol, neopentyl glycol, other diols, diethylene glycol, polytetramethylene glycol, other polyalkylene glycols, 1.4-cyclohexanedimethanol, and unit monomers. Is a polyether glycol having 2 or more carbon atoms.
A copolymer of polybutylene terephthalate resin is, for example, a product name DURANEX 600JP manufactured by Polyplastics Co., Ltd.

なお、ドーム蓋２の組成物であるポリブチレンテレフタレート系樹脂の共重合体は、結晶性ポリエステル樹脂であり、初期のシートの透明性を維持しつつ、成形加工技術で結晶化させることにより耐熱性を向上させることができる。ドーム蓋２の成形加工方法は、真空成形、圧空成形、真空圧空成形である。その結果、熱成形時の加工性が飛躍的に有利で、かつ成型品の稜辺・稜角がシャープに仕上がり、表面状態が均一できれいなドーム蓋２を得ることができる。また、ポリブチレンテレフタレート（ＰＢＴ）系樹脂のようなポリエステル系樹脂層のみのシートから成形されたドーム蓋２は、例えば、熱可塑性のオレフィン系樹脂層を含む多層シートから成形されたドーム蓋よりも、透明性が良好で光沢も出る（ヘイズ１０％以下）。     The copolymer of polybutylene terephthalate resin, which is the composition of the dome lid 2, is a crystalline polyester resin, and is heat resistant by being crystallized by a molding technique while maintaining the transparency of the initial sheet. Can be improved. The forming method of the dome lid 2 is vacuum forming, pressure forming, or vacuum / pressure forming. As a result, it is possible to obtain a dome lid 2 that is remarkably advantageous in workability at the time of thermoforming, has a sharp ridge side and ridge angle, and has a uniform and clean surface state. Further, the dome lid 2 formed from a sheet having only a polyester resin layer such as a polybutylene terephthalate (PBT) resin is, for example, more than a dome lid formed from a multilayer sheet including a thermoplastic olefin resin layer. Excellent transparency and gloss (haze 10% or less).

また、ドーム蓋２のポリブチレンテレフタレート系樹脂の共重合体は、透明性、耐熱性が良好な結晶性ポリマーで、かつ成形加工性が良好である。ポリブチレンテレフタレート系樹脂のシートまたは成形品の特性値は、結晶化度２０％〜６０％、ガラス転位点２０℃〜６５℃、融点２００℃〜２５０℃、固有粘度０．９〜１．２ｄｌ／ｇ、ヘイズ１０％以下、耐寒実用温度−２０℃〜−３０℃、耐熱水性１１５℃〜１２５℃、０．２５ｍｍ厚さにおける酸素のガスバリア性能が酸素ガス透過度１０ｃｍ3／ｍ2．２４ｈｒ．ａｔｍ以下、０．２５ｍｍ厚さにおける窒素のガスバリア性能が窒素ガス透過度２ｃｍ3／ｍ2．２４ｈｒ．ａｔｍ以下、０．２５ｍｍ厚さにおける水蒸気のガスバリア性能が水蒸気透過度３ｇ／ｍ2．２４ｈｒ．ａｔｍ以下である。 The copolymer of polybutylene terephthalate resin of the dome lid 2 is a crystalline polymer having good transparency and heat resistance, and has good moldability. The characteristic values of the sheet or molded product of polybutylene terephthalate resin are as follows: crystallinity 20% to 60%, glass transition point 20 ° C. to 65 ° C., melting point 200 ° C. to 250 ° C., intrinsic viscosity 0.9 to 1.2 dl / g, haze of 10% or less, cold resistant practical temperature of -20 ° C to -30 ° C, hot water resistance of 115 ° C to 125 ° C, and a gas barrier performance of oxygen of 0.25 mm thickness has an oxygen gas permeability of 10 cm 3 / m 2 . 24 hr. The gas barrier performance of nitrogen at a thickness of 0.25 mm or less is less than atm and the nitrogen gas permeability is 2 cm 3 / m 2 . 24 hr. The gas barrier performance of water vapor at a thickness of 0.25 mm or less and atm or less is a water vapor permeability of 3 g / m 2 . 24 hr. is atm or less.

ドーム蓋２の樹脂組成物は、上述した例の他に、上述したポリブチレンテレフタレート系樹脂の共重合体とポリブチレンテレフタレート系樹脂の単独重合体の混合物であり、ポリブチレンテレフタレート系樹脂の単独重合体は、テレフタル酸とテトラメチレングリコールの重合体である。
２種の混合物は、
１種のポリブチレンテレフタレート系樹脂の共重合体 １０〜９０重量部
１種のポリブチレンテレフタレート系樹脂の単独重合体 ９０〜１０重量部
で全体として、１００重量部よりなるものである。
ポリブチレンテレフタレート系樹脂の単独重合体としては、例えば、ポリプラスチック株式会社製 商品名 ジュラネックス６００ＦＰである。 The resin composition of the dome lid 2 is a mixture of the above-mentioned copolymer of polybutylene terephthalate resin and a homopolymer of polybutylene terephthalate resin described above. The coalescence is a polymer of terephthalic acid and tetramethylene glycol.
The two mixtures are
One type of polybutylene terephthalate resin copolymer 10 to 90 parts by weight One type of polybutylene terephthalate resin homopolymer 90 to 10 parts by weight As a whole, 100 parts by weight.
As a homopolymer of polybutylene terephthalate resin, for example, trade name “DURANEX 600FP” manufactured by Polyplastics Co., Ltd. is used.

ドーム蓋２の樹脂組成物は、上述した例の他に、上述したポリブチレンテレフタレート系樹脂の共重合体とポリエチレンテレフタレート系樹脂（ＰＥＴ系樹脂）の単独重合体の混合物であり、ポリエチレンテレフタレート系樹脂の単独重合体は、テレフタル酸とエチレングリコールの重合体である
２種の混合物は、
１種のポリブチレンテレフタレート系樹脂の共重合体 １０〜９０重量部
１種のポリエチレンテレフタレート系樹脂の単独重合体 ９０〜１０重量部
で全体として、１００重量部よりなるものである。
ポリエチレンテレフタレート系樹脂の単独重合体としては、例えば、三菱レイヨン株式会社製 商品名 ダイヤナイトＭＡ５２１Ｈである。 The resin composition of the dome lid 2 is a mixture of a copolymer of the above-mentioned polybutylene terephthalate resin and a homopolymer of a polyethylene terephthalate resin (PET resin) in addition to the above-described example, and a polyethylene terephthalate resin. The homopolymer of is a polymer of terephthalic acid and ethylene glycol.
One type of polybutylene terephthalate resin copolymer 10 to 90 parts by weight One type of polyethylene terephthalate resin homopolymer 90 to 10 parts by weight As a whole, 100 parts by weight.
As a homopolymer of a polyethylene terephthalate resin, for example, Mitsubishi Rayon Co., Ltd. trade name Dianite MA521H is available.

ドーム蓋２の樹脂組成物は、上述した例の他に、上述したポリブチレンテレフタレート系樹脂の共重合体とポリエチレンテレフタレート系樹脂の共重合体の混合物であり、ポリエチレンテレフタレート系樹脂の共重合体は、テレフタル酸成分とエチレングリコール成分又は１．４シクロヘキサンジメタノール成分と多価カルボン酸成分と多価アルコール成分との共重合体である。
２種の混合物は、
１種のポリブチレンテレフタレート系樹脂の共重合体 １０〜９０重量部
１種のポリエチレンテレフタレート系樹脂の共重合体 ９０〜１０重量部
で全体として、１００重量部よりなるものである。
ポリエチレンテレフタレート系樹脂の共重合体としては、例えば、鐘紡株式会社製 商品名 ＦＦＳ３０Ｍである。 The resin composition of the dome lid 2 is a mixture of the above-described copolymer of polybutylene terephthalate resin and the copolymer of polyethylene terephthalate resin, in addition to the example described above, and the copolymer of polyethylene terephthalate resin is A copolymer of a terephthalic acid component and an ethylene glycol component or a 1.4 cyclohexanedimethanol component, a polyvalent carboxylic acid component, and a polyhydric alcohol component.
The two mixtures are
One type of polybutylene terephthalate-based resin copolymer 10 to 90 parts by weight One type of polyethylene terephthalate-based resin copolymer 90 to 10 parts by weight As a whole, 100 parts by weight.
An example of a copolymer of polyethylene terephthalate resin is trade name FFS30M manufactured by Kanebo Co., Ltd.

また、本体容器１用複合シートの最内面層１１ｂのヒートシーラブル・イージーピーラブル樹脂層は、ドーム蓋２とヒートシール性が良好で、かつ易開封機能に優れた特性を必要とする。
そのため、本体容器１がポリプロピレン樹脂を主成分とする外層基材層１１ａとし、最内面層１１ｂに共重合ポリエステル系樹脂層が積層された多層シートから成形されている。
詳述すれば、本体容器１は、ポリプロピレン系樹脂を主成分とする外層基材層１１ａか、又はポリプロピレン主成分／エチレンー酢酸ビニル共重合体ケン化物／ポリプロピレン主成分あるいはポリプロピレン主成分／ＭＸＤ６主成分／ポリプロピレン主成分などを外層基材層１１ａとして、最内面層１１ｂに共重合ポリエステル系樹脂を主成分とする最内面層１１ｂとなっている。外層基材層１１ａと最内面層１１ｂを積層する方法は、周知の共押出し法、押出しラミネート法、接着剤を用いたドライラミネート法、サーマルラミネート法である。 最内面層１１ｂは、結晶融点をもつ共重合ポリエステル系樹脂を主成分とする組成物であり、ガラス転移点−８０℃〜−４０℃、融点１２３℃〜１５０℃である。成形蓋体であるドーム蓋２は、特に、耐熱性向上のために結晶化させているため、表面が不活性のポリブチレンテレフレート系組成樹脂である。このドーム蓋２にヒートシールを容易にし、確実なヒートシール強度と易開封性機能を有し、耐熱水性、耐寒性、耐油性を備えた上記シーランドが構成される。 Further, the heat-sealable and easy-to-peelable resin layer of the innermost surface layer 11b of the composite sheet for the main body container 1 has good heat sealability with the dome lid 2 and requires excellent characteristics for easy opening.
Therefore, the main body container 1 is formed from a multilayer sheet in which the outer layer base material layer 11a mainly composed of polypropylene resin is used and the copolymer polyester resin layer is laminated on the innermost surface layer 11b.
More specifically, the main body container 1 is the outer layer base material layer 11a mainly composed of a polypropylene resin, or a polypropylene main component / ethylene-vinyl acetate copolymer saponified product / polypropylene main component or polypropylene main component / MXD6 main component. The outermost base material layer 11a is used as an outer layer base material layer 11a, and the innermost surface layer 11b is composed of a copolymer polyester resin as a main component. A method of laminating the outer layer base material layer 11a and the innermost surface layer 11b is a known co-extrusion method, extrusion lamination method, dry lamination method using an adhesive, or thermal lamination method. The innermost layer 11b is a composition mainly composed of a copolyester resin having a crystalline melting point, and has a glass transition point of −80 ° C. to −40 ° C. and a melting point of 123 ° C. to 150 ° C. The dome lid 2 which is a molded lid body is a polybutylene terephthalate composition resin whose surface is inactive because it is crystallized particularly for improving heat resistance. The dome lid 2 can be easily heat-sealed, has a reliable heat-sealing strength and an easy-opening function, and has the above-mentioned sealand with hot water resistance, cold resistance, and oil resistance.

次に、被包装物（例えば、食品）を入れて密封する状態について説明する。従来の調理法、新しい過熱蒸気調理法等で調理した惣菜類をドーム形状成形蓋であるドーム蓋２と本体容器１を用いて、本体容器１に惣菜（被包装物）を盛りつけた後、ドーム蓋２を被せながら、容器施蓋内の空気を窒素ガスで９７％置換し、ヒートシール密封することにより、チルド惣菜類のロングライフ化が可能になり、トータル的な流通コストが削減でき、しかも電子レンジで温めると、作りたてのふっくらした食感が楽しめる効果が実現できる。     Next, a state in which an object to be packaged (for example, food) is put and sealed will be described. After preparing prepared dishes (packaged items) in the main body container 1 using the dome lid 2 and the main body container 1 which are dome-shaped molding lids, the dome is prepared using the conventional cooking method, the new superheated steam cooking method, etc. Replacing 97% of the air inside the container lid with nitrogen gas while covering the lid 2 and heat-sealing it makes it possible to extend the life of chilled vegetables and reduce the total distribution cost. When heated in a microwave oven, you can enjoy the effect of enjoying a fresh, fresh texture.

１、 複数の調理器で、異なる食材を別々にスチームコンベクションオーブン方式に より、常圧で調理と殺菌を同時に行った野菜類の煮物をクリーンな冷風冷却器で 急速に２０℃の品温まで下げ、本実施例で得られた本体容器１に１５０ｇ充填し 、ドーム形状成形蓋であるドーム蓋２を被せながら、図示しない移動式挿入ノズ ルから窒素ガスをフラッシュし、包装内の空気を窒素ガスで９７％置換し、ヒー トシールを行って密封した。
２、 従来の調理方式で調理された畜肉と根菜類の煮物を１２０ｇ、本実施例の本体 容器１に品温４５℃でホット充填し、ドーム蓋２を被せながら包装内の空気を窒 素ガスで９５．５％置換し、ヒートシール密封した。この後シャワー式含気レト ルト殺菌装置（図示せず）を用いて加圧状態で９８℃、１０分間加熱した。 1. Using a steam convection oven method with different ingredients separately in multiple cookers, cooked and sterilized vegetables at normal pressure at the same time with a cool cool air cooler to quickly lower the product temperature to 20 ° C The main body container 1 obtained in this example is filled with 150 g, and the dome lid 2 which is a dome-shaped molding lid is covered, and nitrogen gas is flushed from a movable insertion nozzle (not shown), and the air in the package is nitrogen gas. It was replaced with 97% and sealed with a heat seal.
2. 120g of cooked meat and root vegetables cooked by the conventional cooking method, hot-fill the main body container 1 of this embodiment at an article temperature of 45 ° C, and cover the dome lid 2 with nitrogen gas. 95.5% and heat sealed. Thereafter, it was heated at 98 ° C. for 10 minutes in a pressurized state using a shower type aerated retort sterilizer (not shown).

上述の１、２のヒートシール条件は、シール機：２連機、エアーシリンダφ１２５ｍｍ、受圧面積１２３ｃｍ2、シリンダ力（負荷率９０％）、バネ常数（容器１個当たり）５０ｋｇｆ／１０ｍｍ×４本＝２００ｋｇｆ
上述の１の実施例 使用圧力（ゲージ圧） ３ｋｇ／ｃｍ2
力／容器 １個当たり １６６ｋｇｆ／個
温度 第１シール１７０℃、第２シール１７０℃、時間２秒 ２度打ち
上述の２の実施例 使用圧力（ゲージ圧） ４ｋｇ／ｃｍ2
力／容器 １個当たり ２００ｋｇｆ／個
温度 第１シール１７５℃、第２シール１７５℃、時間２秒 ２度打ち

ヒートシールにより良好な密封性を保ち、ピンホールチェッカーで、試験したらシール抜けが無かった。
上述２の加熱殺菌したドーム蓋２と本体容器１の耐収縮性は良好で、縦０．６７％、横０．５４％（一辺が０．６７％、他の辺が０．５４％）であった。
また、冷蔵で１０日間保存後、手で開封しピールオープン性と味覚調査を行ったが、手で滑らかに開封することが出来た。また、風味・テクスチュアー共に良好な状態が保たれていることが判明した。
特に、ドーム蓋２の樹脂は、透明性を維持して成形加工技術により結晶化させることにより、耐熱性、防湿性、酸素ガスバリア性が向上し、１７０℃〜２００℃のヒートシール熱盤に溶融ブロッキング、溶融破断を防止してヒートシール密封することができる。 The above-mentioned heat sealing conditions 1 and 2 are: sealing machine: double-unit, air cylinder φ125 mm, pressure receiving area 123 cm 2 , cylinder force (load factor 90%), spring constant (per container) 50 kgf / 10 mm × 4 pieces = 200kgf
Example 1 described above Working pressure (gauge pressure) 3 kg / cm 2
166kgf / piece per force / container
Temperature 1st seal 170 ° C., 2nd seal 170 ° C., time 2 seconds 2 strokes 2 embodiment described above Working pressure (gauge pressure) 4 kg / cm 2
200kgf / piece per force / container
Temperature 1st seal 175 ° C, 2nd seal 175 ° C, time 2 seconds

Good sealability was maintained by heat sealing, and there was no seal omission when tested with a pinhole checker.
Shrink resistance of the heat-sterilized dome lid 2 and the main body container 1 of 2 above is good, 0.67% length, 0.54% width (0.67% on one side, 0.54% on the other side) there were.
In addition, after being stored in the refrigerator for 10 days, it was opened by hand, and peel-opening and taste were examined, but it could be opened smoothly by hand. It was also found that both the flavor and texture were kept in good condition.
In particular, the resin of the dome lid 2 is improved in heat resistance, moisture resistance, and oxygen gas barrier properties by maintaining transparency and crystallizing by a molding technique, and is melted in a heat seal hot plate at 170 ° C. to 200 ° C. Heat sealing can be performed by preventing blocking and melt fracture.

図１は、本発明の一実施例の密封容器の概略的斜視図である。FIG. 1 is a schematic perspective view of a sealed container according to an embodiment of the present invention. 図２は、図１の密封容器の概略的正面図である。FIG. 2 is a schematic front view of the sealed container of FIG. 図３は、図１の密封容器の本体容器の一部を拡大して示す概略的断面図である。3 is an enlarged schematic cross-sectional view showing a part of the main body container of the sealed container of FIG.

符号の説明Explanation of symbols

１ 本体容器
２ ドーム蓋
１０ 密封容器 1 Main body container 2 Dome lid 10 Sealed container

Claims (9)

フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、
この密封容器内には、被包装物が内在し、前記ドーム蓋は、ポリブチレンテレフタレート系樹脂の共重合体であり、
前記ポリブチレンテレフタレート系樹脂の共重合体は、テレフタル酸成分とテトラメチレングリコール成分と多価カルボン酸成分と多価アルコール成分との共重合体である
ことを特徴とする密封容器。 A concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side, and is heat-sealed and heat-sealed at the flange portion And the flange portion of the main body container is an easily openable sealed container,
In this sealed container, there is an object to be packaged, and the dome lid is a copolymer of polybutylene terephthalate resin,
The copolymer of the polybutylene terephthalate-based resin is a copolymer of a terephthalic acid component, a tetramethylene glycol component, a polyvalent carboxylic acid component, and a polyhydric alcohol component. フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、
この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体とポリブチレンテレフタレート系樹脂の単独重合体の混合物であり、
前記ポリブチレンテレフタレート系樹脂の単独重合体は、テレフタル酸とテトラメチレングリコールの重合体である
ことを特徴とする密封容器。 A concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side, and is heat-sealed and heat-sealed at the flange portion And the flange portion of the main body container is an easily openable sealed container,
In the sealed container, there is an object to be packaged, and the dome lid is a mixture of the copolymer of polybutylene terephthalate resin and the homopolymer of polybutylene terephthalate resin according to claim 1,
The above-mentioned polybutylene terephthalate resin homopolymer is a polymer of terephthalic acid and tetramethylene glycol. フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、
この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体とポリエチレンテレフタレート系樹脂の単独重合体の混合物であり、
前記ポリエチレンテレフタレート系樹脂の単独重合体は、テレフタル酸とエチレングリコールの重合体である
ことを特徴とする密封容器。 A concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side, and is heat-sealed and heat-sealed at the flange portion And the flange portion of the main body container is an easily openable sealed container,
In the sealed container, there is an item to be packaged, and the dome lid is a mixture of the copolymer of polybutylene terephthalate resin according to claim 1 and a homopolymer of polyethylene terephthalate resin,
The sealed container characterized in that the homopolymer of the polyethylene terephthalate resin is a polymer of terephthalic acid and ethylene glycol. フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、
この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体とポリエチレンテレフタレート系樹脂の共重合体の混合物であり、
前記ポリエチレンテレフタレート系樹脂の共重合体は、テレフタル酸成分とエチレングリコール成分又は１．４シクロヘキサンジメタノール成分と多価カルボン酸成分と多価アルコール成分との共重合体である
ことを特徴とする密封容器。 A concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side, and is heat-sealed and heat-sealed at the flange portion And the flange portion of the main body container is an easily openable sealed container,
In the sealed container, there is an object to be packaged, and the dome lid is a mixture of the copolymer of polybutylene terephthalate resin and the copolymer of polyethylene terephthalate resin according to claim 1,
The polyethylene terephthalate resin copolymer is a copolymer of a terephthalic acid component and an ethylene glycol component or a 1.4 cyclohexanedimethanol component, a polyvalent carboxylic acid component, and a polyhydric alcohol component. container. フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、
この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体と請求項３記載のポリエチレンテレフタレート系樹脂の単独重合体と請求項４記載のポリエチレンテレフタレート系樹脂の共重合体の混合物である
ことを特徴とする密封容器。 A concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side, and is heat-sealed and heat-sealed at the flange portion And the flange portion of the main body container is an easily openable sealed container,
In the sealed container, an object to be packaged is present, and the dome lid is formed of a copolymer of polybutylene terephthalate resin according to claim 1 and a homopolymer of polyethylene terephthalate resin according to claim 3. 5. A sealed container, which is a mixture of a copolymer of polyethylene terephthalate resin according to 4. フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、
この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体と請求項２記載のポリブチレンテレフタレート系樹脂の単独重合体と請求項３記載のポリエチレンテレフタレート系樹脂の単独重合体の混合物である
ことを特徴とする密封容器。 A concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side, and is heat-sealed and heat-sealed at the flange portion And the flange portion of the main body container is an easily openable sealed container,
In the sealed container, an object to be packaged is present, and the dome lid is formed of a copolymer of the polybutylene terephthalate resin according to claim 1 and a homopolymer of the polybutylene terephthalate resin according to claim 2. Item 6. A sealed container, which is a mixture of a homopolymer of the polyethylene terephthalate resin according to Item 3. フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、
この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体と請求項２記載のポリブチレンテレフタレート系樹脂の単独重合体と請求項４記載のポリエチレンテレフタレート系樹脂の共重合体の混合物である
ことを特徴とする密封容器。 A concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side, and is heat-sealed and heat-sealed at the flange portion And the flange portion of the main body container is an easily openable sealed container,
In the sealed container, an object to be packaged is present, and the dome lid is formed of a copolymer of the polybutylene terephthalate resin according to claim 1 and a homopolymer of the polybutylene terephthalate resin according to claim 2. Item 7. A sealed container, which is a mixture of a copolymer of polyethylene terephthalate resin according to Item 4. フランジ部を有する凹状の本体容器と、この本体容器の開口部を覆い、上方に凸型部を形成するドーム蓋を有し、前記フランジ部において、ヒートシールされ、かつヒートシールされた前記ドーム蓋と前記本体容器の前記フランジ部は易開封性である密封容器であって、
この密封容器内には、被包装物が内在し、前記ドーム蓋は、請求項１記載のポリブチレンテレフタレート系樹脂の共重合体と請求項２記載のポリブチレンテレフタレート系樹脂の単独重合体と請求項３記載のポリエチレンテレフタレート系樹脂の単独重合体と請求項４記載のポリエチレンテレフタレート系樹脂の共重合体の混合物である
ことを特徴とする密封容器。 A concave main body container having a flange portion, and a dome lid that covers the opening of the main body container and forms a convex portion on the upper side, and is heat-sealed and heat-sealed at the flange portion And the flange portion of the main body container is an easily openable sealed container,
In the sealed container, an object to be packaged is present, and the dome lid is formed of a copolymer of the polybutylene terephthalate resin according to claim 1 and a homopolymer of the polybutylene terephthalate resin according to claim 2. A sealed container comprising a homopolymer of the polyethylene terephthalate resin according to Item 3 and a copolymer of the polyethylene terephthalate resin according to Claim 4. 本体容器がポリプロピレン樹脂を主成分とする外層基材層とし、最内面層に共重合ポリエステル系樹脂層が積層された多層シートから成形されたことを特徴とする請求項１乃至８記載の密封容器。     9. The sealed container according to claim 1, wherein the main body container is formed from a multilayer sheet in which an outer layer base material layer mainly composed of polypropylene resin is used and a copolymer polyester resin layer is laminated on the innermost surface layer. .
JP2005342170A 2005-11-22 2005-11-28 Sealed container Active JP4843298B2 (en)