JPH0542642A - Lid material - Google Patents
Lid materialInfo
- Publication number
- JPH0542642A JPH0542642A JP20170491A JP20170491A JPH0542642A JP H0542642 A JPH0542642 A JP H0542642A JP 20170491 A JP20170491 A JP 20170491A JP 20170491 A JP20170491 A JP 20170491A JP H0542642 A JPH0542642 A JP H0542642A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- acid
- container
- resin layer
- mol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、蓋材に係り、特にポリ
エチレンテレフタレートを形成してなる容器を密封し、
かつ開封容易な蓋材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lid material, and more particularly, to sealing a container formed of polyethylene terephthalate,
The present invention also relates to a lid material that can be easily opened.
【０００２】[0002]
【従来の技術】従来より、ポリエチレンテレフタレート
等の熱可塑性樹脂を深絞り成形した容器に食品等の内容
物を充填し、可撓性を有する蓋材で密封した包装体が広
く使用されている。このような包装体では、内容物を容
器から取り出す際に、手により蓋材を容易に剥離できる
こと、すなわち易開封性が要求される。このため、蓋材
としては、可撓性を有する基材の片面に易開封性樹脂層
を形成したものが使用され、この易開封性樹脂層を容器
開口部のフランジ部等に熱融着することにより容器の密
封が行われていた。そして、易開封の形態としては、易
開封性樹脂が破壊することで開封する凝集破壊タイプ
と、界面部で剥離する界面剥離タイプが主なものであ
る。凝集破壊タイプとしては、従来よりポリプロピレ
ン、ポリエチレンをベースとするもの（特開昭５７−７
７４６５号等）等が使用されていた。しかし、これらの
場合、蓋材の剥離初期に必要とされる力が大きく開封し
難いこと、剥離面が荒れて外観、舌ざわりが悪いこと、
および熱融着に必要な熱量が大きく蓋材による密封速度
が上がらないこと等の問題点があった。ポリエステル容
器に対する蓋材として、このような問題を解決するため
に、易開封性樹脂としてポリエチレンテレフタレート系
樹脂とポリブチレンテレフタレート系樹脂との混合物を
使用することが提案された（特公昭６３−５７２３６
号）。2. Description of the Related Art Conventionally, a package has been widely used in which a container formed by deep-drawing a thermoplastic resin such as polyethylene terephthalate is filled with contents such as food and sealed with a flexible lid material. In such a package, it is required that the lid material can be easily peeled off by hand when the contents are taken out from the container, that is, easy opening. Therefore, as the lid member, a flexible base material having an easily openable resin layer formed on one surface thereof is used, and the easily openable resin layer is heat-sealed to the flange of the container opening or the like. Thus, the container was sealed. The easy-open form mainly includes a cohesive failure type in which the easy-open resin is broken to open and a interface peeling type in which the interface peels. The cohesive failure type has hitherto been based on polypropylene and polyethylene (JP-A-57-7).
7465, etc.) were used. However, in these cases, the force required at the initial peeling of the lid material is large and it is difficult to open, the peeled surface is rough, and the appearance and texture are not good,
In addition, there is a problem that the amount of heat required for heat fusion is large and the sealing speed by the lid material cannot be increased. In order to solve such a problem as a lid material for a polyester container, it has been proposed to use a mixture of a polyethylene terephthalate resin and a polybutylene terephthalate resin as an easily openable resin (Japanese Patent Publication No. 63-57236).
issue).
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、上述の
ポリエチレンテレフタレート系樹脂とポリブチレンテレ
フタレート系樹脂との混合物からなる易開封性樹脂は、
成膜性が悪く、基材に形成される易開封性樹脂層の厚み
にムラが生じ、このため蓋材の剥離に要する力が不均一
になるという問題があった。また、上記の易開封性樹脂
は、従来の他の易開封性樹脂に比べれば熱融着温度は低
いものの未だ不充分であり、容器への熱融着において容
器に変形が生じたり、蓋材による密封速度が遅いという
問題があった。However, an easily-openable resin made of a mixture of the above-mentioned polyethylene terephthalate resin and polybutylene terephthalate resin is
There is a problem in that the film-forming property is poor, and the thickness of the easily-openable resin layer formed on the base material becomes uneven, so that the force required for peeling the lid material becomes uneven. In addition, the above-mentioned easy-open resin is still insufficient in heat fusion temperature as compared with other conventional easy-open resins, but is still insufficient, and deformation of the container occurs in heat fusion to the container, or a lid material. However, there was a problem that the sealing speed was slow.
【０００４】本発明は、上述したような事情に鑑み創案
されたものであり、容器への熱融着温度が低く、かつ密
封速度の速い蓋材を提供することを目的とする。The present invention was devised in view of the above-mentioned circumstances, and an object thereof is to provide a lid member having a low heat fusion temperature to a container and a high sealing speed.
【０００５】[0005]
【課題を解決するための手段】このような目的を達成す
るために、本発明は基材の片面に易開封性樹脂層を有
し、ポリエチレンテレフタレートを構成材料として形成
してなる容器の表面に前記易開封性樹脂層を熱融着する
ことにより前記容器を密封する蓋材において、前記易開
封性樹脂層が、テレフタル酸を主体とした酸成分として
のジカルボン酸と、アルコール成分としてのエチレング
リコール４０〜８０ｗｔ％、１，４−シクロヘキサンジ
メタノール６０〜２０ｗｔ％の混合物との共重合体であ
るポリエチレンテレフタレート系樹脂８０〜５０ｗｔ
％、５０〜９０モル％がテレフタル酸である酸成分とし
てのジカルボン酸と、アルコール成分としての１，４−
ブタンジオールとの重合体であるポリブチレンテレフタ
レート系樹脂２０〜５０ｗｔ％の樹脂混合物により形成
されるような構成とした。In order to achieve such an object, the present invention has an easily-openable resin layer on one surface of a base material, and a polyethylene terephthalate is used as a constituent material on the surface of a container. In the lid material for sealing the container by heat-sealing the easily-openable resin layer, the easily-openable resin layer comprises dicarboxylic acid as an acid component mainly composed of terephthalic acid and ethylene glycol as an alcohol component. Polyethylene terephthalate resin 80 to 50 wt which is a copolymer with a mixture of 40 to 80 wt% and 1,4-cyclohexanedimethanol 60 to 20 wt%
%, 50 to 90 mol% is terephthalic acid, and dicarboxylic acid as an acid component and 1,4-as an alcohol component.
It was configured to be formed by a resin mixture of 20 to 50 wt% of polybutylene terephthalate resin which is a polymer with butanediol.
【０００６】[0006]
【作用】蓋材は、基材と、この基材の片面に形成された
易開封性樹脂層とを有し、易開封性樹脂層はポリエチレ
ンテレフタレート系樹脂８０〜５０ｗｔ％、ポリブチレ
ンテレフタレート系樹脂２０〜５０ｗｔ％の樹脂混合物
により形成され、上記ポリエチレンテレフタレート系樹
脂はテレフタル酸を主体とした酸成分としてのジカルボ
ン酸と、アルコール成分としてのエチレングリコール４
０〜８０ｗｔ％、１，４−シクロヘキサンジメタノール
６０〜２０ｗｔ％の混合物との共重合体であり、また、
上記のポリブチレンテレフタレート系樹脂は５０〜９０
モル％がテレフタル酸である酸成分としてのジカルボン
酸と、アルコール成分としての１，４−ブタンジオール
との重合体である。これにより、易開封性樹脂層の厚さ
は均一となり、ポリエチレンテレフタレートを構成材料
として形成してなる容器の表面に上記易開封性樹脂層を
介して蓋材を熱融着する場合に、熱融着温度が従来の易
開封性樹脂に比較して低く、容器の密封速度を高くする
ことができ、さらに蓋材の剥離による容器の開封が容易
となる。The lid member has a base material and an easy-opening resin layer formed on one surface of the base material. The easy-opening resin layer is made of polyethylene terephthalate resin 80 to 50 wt% and polybutylene terephthalate resin. The polyethylene terephthalate resin is formed of a resin mixture of 20 to 50 wt%, and the polyethylene terephthalate resin is a dicarboxylic acid mainly containing terephthalic acid and an ethylene glycol 4 as an alcohol component.
A copolymer with a mixture of 0 to 80 wt% and 1,4-cyclohexanedimethanol 60 to 20 wt%, and
The above polybutylene terephthalate resin is 50 to 90.
It is a polymer of a dicarboxylic acid as an acid component having a mole% of terephthalic acid and 1,4-butanediol as an alcohol component. Thereby, the thickness of the easy-open resin layer becomes uniform, and when the lid member is heat-sealed to the surface of the container formed by using polyethylene terephthalate as a constituent material through the easy-open resin layer, heat fusion is performed. The attachment temperature is lower than that of the conventional easily openable resin, the sealing speed of the container can be increased, and the container can be easily opened by peeling the lid material.
【０００７】[0007]
【実施例】以下、本発明の実施例について図面を参照し
て説明する。図１は、本発明の蓋材の一実施例を用いた
包装体を示す断面図である。図１において、包装体１は
蓋材２と、この蓋材２により開口部７を密封された容器
５とを有する。蓋材２は、基材３と、この基材３の一方
に面に形成された易開封性樹脂層４とからなる。また、
容器５は深絞り成形により成形され、本体６と、本体６
の上端部周縁に形成されたフランジ部８とからなる。そ
して、易開封性樹脂層４を介して容器５の開口部７を覆
うようにフランジ部８に蓋材２を熱融着することにより
容器５が密封される。Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a cross-sectional view showing a package using an embodiment of the lid material of the present invention. In FIG. 1, a package 1 has a lid member 2 and a container 5 whose opening 7 is sealed by the lid member 2. The lid member 2 includes a base material 3 and an easily-openable resin layer 4 formed on one surface of the base material 3. Also,
The container 5 is formed by deep drawing, and the main body 6 and the main body 6 are formed.
And a flange portion 8 formed on the periphery of the upper end portion of the. Then, the lid member 2 is heat-sealed to the flange portion 8 so as to cover the opening portion 7 of the container 5 via the easy-open resin layer 4, so that the container 5 is sealed.
【０００８】蓋材２の基材３としては、アルミニウム箔
等の金属箔、ポリエチレンテレフタレート、ポリプロピ
レン、ナイロン等の延伸フィルム、各種の紙、あるいは
これらの積層体等のいずれであってもよい。また、この
ような基材３の易開封性樹脂層４形成面側には、予めア
ンカーコート剤層を設けたり、コロナ放電処理を施して
もよい。The base material 3 of the lid member 2 may be a metal foil such as an aluminum foil, a stretched film of polyethylene terephthalate, polypropylene, nylon or the like, various types of paper, or a laminate of these. In addition, an anchor coat agent layer may be provided in advance or a corona discharge treatment may be performed on the surface of the base material 3 on which the easily-sealable resin layer 4 is formed.
【０００９】本発明の蓋材の易開封性樹脂層４は、ポリ
エチレンテレフタレート系樹脂とポリブチレンテレフタ
レート系樹脂を主体とする混合物からなる。易開封性樹
脂層４を構成するポリエチレンテレフタレート系樹脂
は、テレフタル酸を主体とした酸成分としてのジカルボ
ン酸と、アルコール成分としてのエチレングリコールと
１，４−シクロヘキサンジメタノールの混合物との共重
合体である。ジカルボン酸の主体であるテレフタル酸
は、酸成分の８０〜１００モル％、好ましくは９０〜１
００モル％を占める。また、テレフタル酸以外の酸成分
としては、イソフタル酸、セバシン酸、アジピン酸、ア
ゼライン酸等の芳香族ジカルボン酸および脂肪族ジカル
ボン酸を０〜２０モル％用いることができる。アルコー
ル成分としてのエチレングリコールと１，４−シクロヘ
キサンジメタノールの混合比は、混合物に対してエチレ
ングリコールが４０〜８０モル％、１，４−シクロヘキ
サンジメタノールが６０〜２０モル％であることが好ま
しい。エチレングリコールが４０モル％未満であり、
１，４−シクロヘキサンジメタノールが６０モル％を越
えるとヒートシール強度が小さくなり、またエチレング
リコールが８０モル％を越え、１，４−シクロヘキサン
ジメタノールが２０ｗｔ％未満であると結晶化速度が速
くなり、低結晶性による比較的低温での熱融着性能が損
われることとなり好ましくない。また、上記混合物以外
のアルコール成分としては、ジエチレングリコール、ブ
タンジオール、１，６−ヘキサンジオール等を０〜２０
モル％の範囲で用いることができる。このようなポリエ
チレンテレフタレート系樹脂は比較的低温での熱融着性
が良好であり、易開封性樹脂層４に使用することにより
蓋材２による容器５の密封時の熱融着温度を低下するこ
とができる。The easily openable resin layer 4 of the lid material of the present invention is composed of a mixture mainly composed of polyethylene terephthalate resin and polybutylene terephthalate resin. The polyethylene terephthalate-based resin forming the easy-open resin layer 4 is a copolymer of dicarboxylic acid as an acid component mainly containing terephthalic acid, and a mixture of ethylene glycol and 1,4-cyclohexanedimethanol as an alcohol component. Is. Terephthalic acid, which is the main component of dicarboxylic acid, is 80 to 100 mol% of the acid component, preferably 90 to 1
It occupies 00 mol%. Further, as the acid component other than terephthalic acid, 0 to 20 mol% of aromatic dicarboxylic acid and aliphatic dicarboxylic acid such as isophthalic acid, sebacic acid, adipic acid and azelaic acid can be used. The mixing ratio of ethylene glycol as an alcohol component and 1,4-cyclohexanedimethanol is preferably 40 to 80 mol% of ethylene glycol and 60 to 20 mol% of 1,4-cyclohexanedimethanol to the mixture. .. Ethylene glycol is less than 40 mol%,
When 1,4-cyclohexanedimethanol exceeds 60 mol%, the heat seal strength becomes small, and when ethylene glycol exceeds 80 mol% and 1,4-cyclohexanedimethanol is less than 20 wt%, the crystallization rate is high. This is not preferable because the low crystallinity impairs the heat fusion performance at a relatively low temperature. In addition, as the alcohol component other than the above mixture, diethylene glycol, butanediol, 1,6-hexanediol or the like is added in an amount of 0 to 20.
It can be used in the range of mol%. Such a polyethylene terephthalate resin has a good heat fusion property at a relatively low temperature, and when it is used for the easily-openable resin layer 4, the heat fusion temperature at the time of sealing the container 5 with the lid material 2 is lowered. be able to.
【００１０】易開封性樹脂層４を構成するポリブチレン
テレフタレート系樹脂は、５０〜９０モル％がテレフタ
ル酸である酸成分としてのジカルボン酸と、アルコール
成分としての１，４−ブタンジオールとの重合体であ
る。テレフタル酸以外の酸成分としては、イソフタル
酸、セバシン酸、アジピン酸、アゼライン酸等の芳香族
ジカルボン酸および脂肪族ジカルボン酸を１０〜５０モ
ル％、好ましくは１５〜４０モル％用いることができ
る。この中で、イソフタル酸が熱融着性、剥離性等の点
から好ましい。また、１，４−ブタンジオール以外のア
ルコール成分として、エチレングリコール、ジエチレン
グリコール、１，４−シクロヘキサンジメタノール、
１，６−ヘキサンジオール、ネオペンチルグリコール等
を０〜２０モル％の範囲で用いて共重合体としてもよ
い。The polybutylene terephthalate-based resin constituting the easily-openable resin layer 4 is composed of dicarboxylic acid as an acid component having 50 to 90 mol% of terephthalic acid and 1,4-butanediol as an alcohol component. It is united. As acid components other than terephthalic acid, aromatic dicarboxylic acids such as isophthalic acid, sebacic acid, adipic acid, and azelaic acid and aliphatic dicarboxylic acids can be used in an amount of 10 to 50 mol%, preferably 15 to 40 mol%. Of these, isophthalic acid is preferable from the viewpoints of heat-sealing property and peeling property. Further, as alcohol components other than 1,4-butanediol, ethylene glycol, diethylene glycol, 1,4-cyclohexanedimethanol,
A copolymer may be prepared by using 1,6-hexanediol, neopentyl glycol or the like in the range of 0 to 20 mol%.
【００１１】このようなポリブチレンテレフタレート系
樹脂を、上述のポリエチレンテレフタレート系樹脂と共
に使用することにより、比較的低温での熱融着性のみな
らず、良好な開封性も兼ね備えた易開封性樹脂層４とす
ることができる。このためには、ポリエチレンテレフタ
レート系樹脂とポリブチレンテレフタレート系樹脂との
混合比は、樹脂混合物に対してポリエチレンテレフタレ
ート系樹脂が８０〜５０ｗｔ％、ポリブチレンテレフタ
レート系樹脂が２０〜５０ｗｔ％であることが好まし
い。ポリエチレンテレフタレート系樹脂が５０ｗｔ％未
満であり、ポリブチレンテレフタレート系樹脂が５０ｗ
ｔ％を越えると比較的低温での熱融着性が劣り、またポ
リエチレンテレフタレート系樹脂が８０ｗｔ％を越え、
ポリブチレンテレフタレート系樹脂が２０ｗｔ％未満で
あると比較的低温での熱融着性が良すぎて所望の易開封
性が得られないことになる。By using such a polybutylene terephthalate-based resin together with the above-mentioned polyethylene terephthalate-based resin, not only the heat-sealing property at a relatively low temperature but also the easy-opening resin layer having a good unsealing property is obtained. It can be 4. For this purpose, the mixing ratio of the polyethylene terephthalate resin and the polybutylene terephthalate resin is 80 to 50 wt% of the polyethylene terephthalate resin and 20 to 50 wt% of the polybutylene terephthalate resin with respect to the resin mixture. preferable. Polyethylene terephthalate resin is less than 50 wt% and polybutylene terephthalate resin is 50 w
If it exceeds t%, the heat-sealing property at a relatively low temperature becomes poor, and the polyethylene terephthalate resin exceeds 80 wt%.
When the content of the polybutylene terephthalate resin is less than 20% by weight, the heat fusion property at a relatively low temperature is so good that the desired easy-open property cannot be obtained.
【００１２】なお、本発明では易開封性樹脂層４に酸化
防止剤、熱安定剤、紫外線吸収剤、可塑剤、粘度調節
剤、滑剤、顔料等を必要に応じて添加してもよい。ま
た、酸化チタン、マイカ等の無機微粒子を上記の樹脂混
合物に対して０〜２０ｗｔ％、好ましくは０．０１〜１
０ｗｔ％程度添加してもよい。In the present invention, an antioxidant, a heat stabilizer, an ultraviolet absorber, a plasticizer, a viscosity modifier, a lubricant, a pigment and the like may be added to the easily openable resin layer 4 if necessary. Further, inorganic fine particles such as titanium oxide and mica are 0 to 20 wt% with respect to the above resin mixture, preferably 0.01 to 1
You may add about 0 wt%.
【００１３】易開封性樹脂層４を基材３上に形成するに
は、上述の樹脂混合物を溶融して基材３上に押出しラミ
ネートする方法、予め上述の樹脂混合物を用いて成形し
たフィルムを基材３に接着剤を介してラミネートする方
法等によることができる。このような易開封性樹脂層４
の厚みは、使用目的等により適宜決定することができ、
通常２０〜１５０μｍ程度である。In order to form the easily-openable resin layer 4 on the substrate 3, a method of melting the above-mentioned resin mixture and extruding and laminating on the substrate 3, or a film formed by using the above-mentioned resin mixture in advance is used. For example, a method of laminating the base material 3 with an adhesive may be used. Such an easily openable resin layer 4
The thickness of can be appropriately determined depending on the purpose of use,
Usually, it is about 20 to 150 μm.
【００１４】容器５はポリエチレンテレフタレートを構
成材料として形成したものである。この容器５に用いら
れるポリエチレンテレフタレートは、酸成分の８０モル
％以上がテレフタル酸であり、アルコール成分の８０モ
ル％以上がエチレングリコールであるポリエステルであ
り、他にポリエチレン、アイオノマー、上記のポリエチ
レンテレフタレート以外のポリエステル等が適宜添加さ
れたものである。また、容器５の深絞り成形は、射出成
形、圧空成形、真空成形等の公知の成形方法により行う
ことができる。The container 5 is formed of polyethylene terephthalate as a constituent material. The polyethylene terephthalate used in this container 5 is a polyester in which 80 mol% or more of the acid component is terephthalic acid and 80 mol% or more of the alcohol component is ethylene glycol. Other than polyethylene, ionomer, and polyethylene terephthalate described above. The polyester and the like are appropriately added. The deep drawing of the container 5 can be carried out by a known molding method such as injection molding, pressure molding, vacuum molding or the like.
【００１５】上述のような蓋材２を熱融着して容器５を
密封するには、ヒートシール法、高周波誘導加熱法等の
公知の方法を用いることができる。次に、実験例を示し
て本発明をより具体的に説明する。 実験例 基材として厚み５０μｍのアルミニウム箔を用い、この
アルミニウム箔にアンカーコート剤（イソシアネート系
化合物）を塗布し、このアンカーコート剤上に下記の樹
脂混合物を用い押出しラミネート法により３０μｍの厚
みの易開封性樹脂層を形成し、その後、所定の形状に打
ち抜いて蓋材（試料ー１）とした。 （樹脂混合物の組成） ・ポリエチレンテレフタレート（ＰＥＴ）系樹脂 …６０ｗｔ％ 酸成分：テレフタル酸…１００モル％ アルコール成分： エチレングリコール…５０ｗｔ％ １，４−シクロヘキサンジメタノール…５０ｗｔ％ ・ポリブチレンテレフタレート（ＰＢＴ）系樹脂 …４０ｗｔ％ 酸成分：テレフタル酸…８０モル％ イソフタル酸…２０モル％ アルコール成分： １，４−ブタンジオール…９０モル％ エチレングリコール…１０モル％ また、上記の樹脂混合物の組成のうち、ＰＥＴ系樹脂と
ＰＢＴ系樹脂の混合比を下記のようした他は試料−１と
同様にして試料−２、比較試料−１，２を作成した。 ・試料−２ ：ＰＥＴ系樹脂…７５ｗｔ％ ＰＢＴ系樹脂…２５ｗｔ％ ・比較試料−１ ：ＰＥＴ系樹脂…３０ｗｔ％ ＰＢＴ系樹脂…７０ｗｔ％ ・比較試料−２ ：ＰＥＴ系樹脂…９０ｗｔ％ ＰＢＴ系樹脂…１０ｗｔ％ また、試料−１の樹脂混合物の組成のうち、ＰＥＴ系樹
脂のアルコール成分のエチレングリコール（ＥＧ）と
１，４−シクロヘキサンジメタノール（ＣＨＤＭ）の混
合比を下記のようした他は試料−１と同様にして試料−
３、比較試料−３，４を作成した。 ・試料−３ ：ＥＧ …７５モル％ ＣＨＤＭ…２５モル％ ・比較試料−３ ：ＥＧ …３５モル％ ＣＨＤＭ…６５モル％ ・比較試料−４ ：ＥＧ …９０モル％ ＣＨＤＭ…１０モル％ また、酸成分としてテレフタル酸が９０モル％、イソフ
タル酸が１０モル％であり、アルコール成分としてエチ
レングリコールが９０モル％、１，４−シクロヘキサン
ジメタノールが１０モル％であるポリエチレンテレフタ
レートシートを準備した。そして、このフィルムに上記
の各蓋材試料を下記の条件により熱融着し、密封性、開
封性、高速熱融着適性を下記の方法により評価した。 （熱融着条件） シール温度：１６０℃〜２２０℃ シール圧：２kg／cm2 シール時間：１秒 （密封性評価方法）引張り試験機により、剥離角度１８
０°、引張り速度３００mm／min にてヒートシール強度
（kg／１５mm）を測定した。To seal the container 5 by heat-sealing the lid member 2 as described above, a known method such as a heat sealing method or a high frequency induction heating method can be used. Next, the present invention will be described more specifically by showing experimental examples. Experimental Example An aluminum foil having a thickness of 50 μm was used as a substrate, an anchor coating agent (isocyanate compound) was applied to the aluminum foil, and the following resin mixture was applied onto the anchor coating agent by an extrusion laminating method to obtain a thickness of 30 μm. An openable resin layer was formed and then punched into a predetermined shape to obtain a lid material (Sample-1). (Composition of resin mixture) -Polyethylene terephthalate (PET) -based resin: 60 wt% Acid component: terephthalic acid: 100 mol% Alcohol component: Ethylene glycol: 50 wt% 1,4-Cyclohexanedimethanol: 50 wt% -Polybutylene terephthalate (PBT) ) Resin: 40 wt% Acid component: terephthalic acid: 80 mol% Isophthalic acid: 20 mol% Alcohol component: 1,4-butanediol: 90 mol% Ethylene glycol: 10 mol% Further, of the composition of the above resin mixture , Sample 2 and Comparative Samples 1 and 2 were prepared in the same manner as Sample 1 except that the mixing ratio of PET resin and PBT resin was as follows. -Sample-2: PET-based resin ... 75 wt% PBT-based resin ... 25 wt% -Comparative sample-1: PET-based resin ... 30 wt% PBT-based resin ... 70 wt% -Comparative sample-2: PET-based resin ... 90 wt% PBT-based resin 10 wt% Samples other than the composition of the resin mixture of Sample-1 except that the mixing ratio of ethylene glycol (EG) and 1,4-cyclohexanedimethanol (CHDM), which are alcohol components of PET-based resin, were as follows: Sample as in -1
3, Comparative Samples-3 and 4 were prepared. -Sample-3: EG ... 75 mol% CHDM ... 25 mol% -Comparative sample-3: EG ... 35 mol% CHDM ... 65 mol% -Comparative sample-4: EG ... 90 mol% CHDM ... 10 mol% A polyethylene terephthalate sheet having 90 mol% of terephthalic acid as a component, 10 mol% of isophthalic acid, 90 mol% of ethylene glycol and 10 mol% of 1,4-cyclohexanedimethanol as an alcohol component was prepared. Then, the above-mentioned respective lid material samples were heat-sealed to this film under the following conditions, and the sealing property, the unsealing property, and the high-speed heat-sealing suitability were evaluated by the following methods. (Heat fusion condition) Sealing temperature: 160 ° C to 220 ° C Sealing pressure: 2 kg / cm 2 Sealing time: 1 second (Sealing property evaluation method) Peeling angle 18 by a tensile tester
The heat seal strength (kg / 15 mm) was measured at 0 ° and a pulling speed of 300 mm / min.
【００１６】評価基準 １．０kg／１５mm以上…密封性良好 １．０kg／１５mm未満…密封性不良 （開封性評価方法）接着強度が１．０kg／１５mm〜２．
２kg／１５mmの範囲内にあるとき、開封性良好とした。 （高速熱融着適性評価方法）接着強度が１．０kg／１５
mm以上である温度範囲内で最低温度がポリエチレンテレ
フタレート系樹脂の融解ピーク温度より１５℃以上低い
場合は“○”、それそれ以外の場合を“×”とした。Evaluation Criteria 1.0 kg / 15 mm or more ... Good sealing property Less than 1.0 kg / 15 mm ... Poor sealing property (opening property evaluation method) Adhesive strength 1.0 kg / 15 mm-2.
When it was within the range of 2 kg / 15 mm, the unsealing property was good. (High-speed heat fusion suitability evaluation method) Adhesive strength 1.0 kg / 15
When the lowest temperature was lower than the melting peak temperature of the polyethylene terephthalate-based resin by 15 ° C. or more within the temperature range of mm or more, “◯” was given, and in other cases, “X” was given.
【００１７】[0017]
【表１】 上記の評価結果を表１に示した。表１から明らかなよう
に、試料−１〜３は良好な特性を示した。しかし、比較
試料−１，４は密封性、高速熱融着適性が劣り、比較試
料−２，３は開封性が劣っていた。[Table 1] The evaluation results are shown in Table 1. As is clear from Table 1, Samples -1 to 3 exhibited good characteristics. However, Comparative Samples-1 and 4 were inferior in sealing property and suitability for high-speed heat fusion, and Comparative Samples-2 and 3 were inferior in unsealing property.
【００１８】[0018]
【発明の効果】以上詳述したように、本発明によれば易
開封性樹脂層の厚さが均一であり、容器への熱融着温度
が低く密封速度を高くすることができるとともに、剥離
による容器の開封が容易な蓋材が可能となる。As described in detail above, according to the present invention, the easily-openable resin layer has a uniform thickness, the heat-sealing temperature to the container is low, the sealing speed can be increased, and the peeling can be achieved. It is possible to provide a lid material that is easy to open the container.
【図１】本発明の蓋材の一実施例を用いた包装体を示す
断面図である。FIG. 1 is a cross-sectional view showing a package using an embodiment of a lid material of the present invention.
１…包装体 ２…蓋材 ３…基材 ４…易開封性樹脂層 ５…容器 ６…本体 ７…開口部 ８…フランジ部 DESCRIPTION OF SYMBOLS 1 ... Packaging body 2 ... Lid material 3 ... Base material 4 ... Easy-opening resin layer 5 ... Container 6 ... Main body 7 ... Opening part 8 ... Flange part
Claims (1)
リエチレンテレフタレートを構成材料として形成してな
る容器の表面に前記易開封性樹脂層を熱融着することに
より前記容器を密封する蓋材において、前記易開封性樹
脂層が、テレフタル酸を主体とした酸成分としてのジカ
ルボン酸と、アルコール成分としてのエチレングリコー
ル４０〜８０ｗｔ％、１，４−シクロヘキサンジメタノ
ール６０〜２０ｗｔ％の混合物との共重合体であるポリ
エチレンテレフタレート系樹脂８０〜５０ｗｔ％、５０
〜９０モル％がテレフタル酸である酸成分としてのジカ
ルボン酸と、アルコール成分としての１，４−ブタンジ
オールとの重合体であるポリブチレンテレフタレート系
樹脂２０〜５０ｗｔ％の樹脂混合物により形成されてい
ることを特徴とする蓋材。1. A container having an easily-openable resin layer on one surface of a base material and sealing the container by heat-sealing the easily-openable resin layer on the surface of the container formed of polyethylene terephthalate as a constituent material. In the lid material, the easily-openable resin layer comprises dicarboxylic acid as an acid component mainly composed of terephthalic acid, ethylene glycol 40 to 80 wt% as an alcohol component, and 60 to 20 wt% of 1,4-cyclohexanedimethanol. Polyethylene terephthalate resin that is a copolymer with a mixture 80 to 50 wt%, 50
It is formed by a resin mixture of 20 to 50 wt% of polybutylene terephthalate resin which is a polymer of dicarboxylic acid as an acid component having 90 to 90 mol% of terephthalic acid and 1,4-butanediol as an alcohol component. A lid material characterized by that.