JP2005179729A - Method of producing sintered compact, and sintered compact - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a method of producing a sintered compact having excellent thermal conductivity, and to provide the sintered compact having excellent thermal conductivity. <P>SOLUTION: The method of producing a sintered compact comprises: a compacting stage where a composition comprising a fibrous carbon based substance 2 and a metal-containing thermally conductive substance 3 is compacted into a prescribed shape to obtain a molded body; and a firing stage where the molded body is fired, and each fibrous carbon-based substance 2 is mutually joined via the thermally conductive substance 3 to obtain a fired body. Thus, a sintered compact 1 in which each fibrous carbon-based substance 2 is mutually joined via the thermally conductive substance 3 is obtained. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

本発明は、焼結体の製造方法および焼結体に関するものである。   The present invention relates to a method for producing a sintered body and a sintered body.

半導体チップに接合して用いられるヒートシンクのような冷却用部材には、優れた熱伝導性（高い熱伝導率）が求められる。
従来、このような冷却用部材には、主として、合金等の金属材料で構成されたものが用いられてきた。
しかしながら、金属材料は、一般に、比重（密度）が大きく、用途（例えば、モバイル型（またはノート型）のパーソナルコンピュータ等）によっては、製品の軽量化にとって極めて不利であった。 A cooling member such as a heat sink used by being bonded to a semiconductor chip is required to have excellent thermal conductivity (high thermal conductivity).
Conventionally, such a cooling member has been mainly composed of a metal material such as an alloy.
However, the metal material generally has a large specific gravity (density), which is extremely disadvantageous for reducing the weight of the product depending on the application (for example, a mobile (or notebook) personal computer).

また、マグネシウム合金のような比較的比重の小さい金属材料も開発されているが、さらなる軽量化、熱伝導性の向上が求められている。
一方、近年、熱伝導性に優れ、かつ、低比重のグラファイト（黒鉛）を用いた成形体を製造する方法が提案されている（例えば、特許文献１参照）。
しかしながら、このような方法では、得られる成形体はフィルム形状を有するものとなり、比較的肉厚の大きい成形体や、複雑な形状を有する成形体を製造するのは困難であった。
また、このような方法で得られる成形体（フィルム）では、厚み方向に対して垂直な方向（主面方向）にのみ熱伝導が優れており、厚み方向では熱伝導が良くないという課題を有していた。 In addition, metal materials having a relatively low specific gravity such as magnesium alloys have been developed, but further weight reduction and improved thermal conductivity are required.
On the other hand, in recent years, there has been proposed a method for producing a molded body using graphite (graphite) having excellent thermal conductivity and low specific gravity (see, for example, Patent Document 1).
However, in such a method, the obtained molded product has a film shape, and it has been difficult to produce a molded product having a relatively large thickness or a molded product having a complicated shape.
In addition, the molded body (film) obtained by such a method has a problem that heat conduction is excellent only in a direction (main surface direction) perpendicular to the thickness direction, and heat conduction is not good in the thickness direction. Was.

特開平５−１３２３６０号公報JP-A-5-132360

本発明の目的は、熱伝導性に優れた焼結体を製造する方法、および、熱伝導性に優れた焼結体を提供することにある。   An object of the present invention is to provide a method for producing a sintered body excellent in thermal conductivity and a sintered body excellent in thermal conductivity.

このような目的は、下記の本発明により達成される。
本発明の焼結体の製造方法は、繊維状炭素系物質と、金属を含む熱伝導性物質とを含む組成物を所定の形状に成形して、成形体を得る成形工程と、
前記成形体を焼成して、前記熱伝導性物質を介して前記繊維状炭素系物質同士を互いに接合することにより、焼成体を得る焼成工程とを有することを特徴とする。
これにより、熱伝導性に優れた成形体を製造することができる。 Such an object is achieved by the present invention described below.
The method for producing a sintered body of the present invention includes a molding step of molding a composition containing a fibrous carbon-based material and a thermally conductive material containing a metal into a predetermined shape to obtain a molded body,
And firing the molded body and joining the fibrous carbon-based materials to each other through the thermally conductive material to obtain a fired body.
Thereby, the molded object excellent in thermal conductivity can be manufactured.

本発明の焼結体の製造方法では、前記組成物は、バインダーも含むものであることが好ましい。
これにより、成形工程でバインダーにより繊維状炭素系物質同士が固定されるので、成形工程から焼成工程への移行時に成形体の型崩れを確実に防止できる。また、焼成工程でも、繊維状炭素系物質同士が熱伝導性物質を介して接合されるだけでなく、バインダーによって繊維状炭素系物質同士が固定されるので、焼結体の機械的強度が向上する。 In the manufacturing method of the sintered compact of this invention, it is preferable that the said composition also contains a binder.
Thereby, since fibrous carbonaceous materials are fixed with a binder at a formation process, it can prevent reliably a shape-loss of a molded object at the time of transfer to a baking process from a formation process. Also, in the firing process, the fibrous carbon-based materials are not only joined to each other via a thermally conductive material, but the fibrous carbon-based materials are fixed to each other by a binder, so the mechanical strength of the sintered body is improved. To do.

本発明の焼結体の製造方法では、前記バインダーは、熱硬化性樹脂を主成分とするものであることが好ましい。
これにより、繊維状炭素系物質同士を熱硬化性樹脂により、より確実に固定することができる。
本発明の焼結体の製造方法では、前記成形工程での成形は、前記バインダーが溶融もしくは硬化する温度以上の温度で、前記組成物を加熱しつつ行われることが好ましい。
これにより、熱硬化性樹脂が成形工程での加熱により溶融もしくは硬化するので、より確実に繊維状炭素系物質同士を熱硬化性樹脂により固定しておくことができる。 In the method for producing a sintered body of the present invention, it is preferable that the binder is mainly composed of a thermosetting resin.
Thereby, fibrous carbonaceous materials can be more reliably fixed with a thermosetting resin.
In the method for producing a sintered body according to the present invention, the molding in the molding step is preferably performed while heating the composition at a temperature equal to or higher than a temperature at which the binder is melted or cured.
Thereby, since a thermosetting resin melts or hardens | cures by the heating in a formation process, fibrous carbonaceous materials can be more reliably fixed with a thermosetting resin.

本発明の焼結体の製造方法では、前記熱硬化性樹脂は、フェノール樹脂およびエポキシ樹脂のうち少なくとも一方を主成分とするものであることが好ましい。
これらのものは、加熱により比較的低温で溶融と同時に硬化するので好ましい。
本発明の焼結体の製造方法では、前記成形工程にて前記バインダーは粒子状をなしていることが好ましい。
これにより、組成物は、適度な流動性を有するものとなるため、成形工程における組成物の成形性をより向上させることができる。 In the method for producing a sintered body of the present invention, it is preferable that the thermosetting resin has at least one of a phenol resin and an epoxy resin as a main component.
These are preferable because they are cured simultaneously with melting at a relatively low temperature by heating.
In the method for producing a sintered body of the present invention, it is preferable that the binder is in the form of particles in the molding step.
Thereby, since a composition has moderate fluidity | liquidity, the moldability of the composition in a formation process can be improved more.

本発明の焼結体の製造方法では、前記成形工程にて前記熱伝導性物質および前記バインダーの双方が粒子状をなしており、前記熱伝導性物質の平均粒径は前記バインダーの平均粒径よりも小さいことが好ましい。
これにより、繊維状炭素系物質同士をさらに接近させた状態で固定することができる。
本発明の焼結体の製造方法では、前記成形工程にて前記熱伝導性物質は粒子状をなしていることが好ましい。
これにより、組成物は、適度な流動性を有するものとなるため、成形工程における組成物の成形性をより向上させることができる。 In the method for producing a sintered body according to the present invention, both the thermally conductive material and the binder are in the form of particles in the molding step, and the average particle size of the thermally conductive material is the average particle size of the binder. Is preferably smaller.
Thereby, it is possible to fix the fibrous carbon-based materials in a state where they are brought closer to each other.
In the method for producing a sintered body according to the present invention, it is preferable that the thermally conductive substance is in a particulate form in the molding step.
Thereby, since a composition has moderate fluidity | liquidity, the moldability of the composition in a formation process can be improved more.

本発明の焼結体の製造方法では、前記繊維状炭素系物質は、カーボンナノチューブおよび気相成長炭素繊維のうちいずれか一方を主成分とするものであることが好ましい。
これにより、得られる焼結体は、その熱伝導性が特に優れたものになるとともに、機械的強度（形状の安定性）も向上する。
本発明の焼結体の製造方法では、前記焼成工程での焼成温度は前記熱伝導性物質の融点以上であることが好ましい。
これにより、成形体中の熱伝導性物質が焼成工程で溶融するので、その後に硬化した熱伝導物質により焼結体中で繊維状炭素系物質同士が確実に接合され、得られる焼結体は、特に優れた熱伝導性を有するとともに、優れた形状の安定性を有するものとすることができる。 In the method for producing a sintered body according to the present invention, it is preferable that the fibrous carbon-based material contains one of carbon nanotubes and vapor grown carbon fibers as a main component.
As a result, the obtained sintered body has a particularly excellent thermal conductivity, and also improves the mechanical strength (shape stability).
In the method for producing a sintered body according to the present invention, it is preferable that the firing temperature in the firing step is equal to or higher than the melting point of the thermally conductive material.
Thereby, since the heat conductive material in the molded body is melted in the firing step, the fibrous carbon-based materials are reliably bonded to each other in the sintered body by the cured heat conductive material, and the obtained sintered body is In addition to having excellent thermal conductivity, it can have excellent shape stability.

本発明の焼結体の製造方法では、前記焼成工程での焼成温度は前記熱伝導性物質の沸点以上であることが好ましい。
これにより、成形体中の熱伝導性物質が焼成工程で気化して前記成形体中で分散するので、その後に均一に分布した状態で硬化した熱伝導物質により焼結体中で繊維状炭素系物質同士が確実に接合され、得られる焼結体は、特に優れた熱伝導性を有するとともに、優れた形状の安定性を有するものとすることができる。 In the method for producing a sintered body according to the present invention, the firing temperature in the firing step is preferably equal to or higher than the boiling point of the thermally conductive substance.
As a result, the thermally conductive material in the molded body is vaporized in the firing step and dispersed in the molded body, so that the fibrous carbon system in the sintered body by the thermally conductive material cured in a uniformly distributed state thereafter. The sintered body obtained by bonding the substances reliably can have excellent thermal conductivity and excellent shape stability.

本発明の焼結体の製造方法では、前記熱伝導性物質は、Ｃｕ、Ａｇ、Ａｌ、またはこれらを含む合金、これらの金属を含む酸化物よりなる群から選択される少なくとも１種を主成分とするものであることが好ましい。
これらのものは、熱伝導性が優れているので、繊維状炭素系物質同士間の熱伝導性を高め、得られる焼結体熱は、特に優れた熱伝導性を有するものとなる。 In the method for producing a sintered body according to the present invention, the thermal conductive material is mainly composed of at least one selected from the group consisting of Cu, Ag, Al, alloys containing these, and oxides containing these metals. It is preferable that
Since these have excellent thermal conductivity, the thermal conductivity between the fibrous carbonaceous materials is increased, and the obtained sintered body heat has particularly excellent thermal conductivity.

本発明の焼結体の製造方法では、前記焼成工程は、不活性ガス雰囲気中または減圧下で行われることが好ましい。
これにより、熱伝導性物質が金属単体である場合に、焼成工程中における熱伝導物質の酸化が防止され、得られる焼結体の熱伝導率の均一化が図られる。また、焼成工程中における繊維状炭素系物質の酸化も防止されるので、得られる焼結体は、特に優れた熱伝導性および機械的強度を有する。 In the method for producing a sintered body according to the present invention, the firing step is preferably performed in an inert gas atmosphere or under reduced pressure.
Thereby, when a heat conductive substance is a metal simple substance, the oxidation of a heat conductive substance in a baking process is prevented, and the uniform thermal conductivity of the sintered compact obtained is achieved. Moreover, since oxidation of the fibrous carbonaceous material during the firing process is also prevented, the obtained sintered body has particularly excellent thermal conductivity and mechanical strength.

本発明の焼結体の製造方法では、前記焼結工程の後に、前記焼結体に樹脂系材料を含浸させる含浸工程を有することが好ましい。
これにより、焼結体の機械的強度が特に優れたものになる。
本発明の焼結体は、本発明の焼結体の製造方法により製造されたことを特徴とする。
これにより、熱伝導性に優れた焼結体が得られる。
本発明の焼結体は、金属を含む熱伝導性物質を介して繊維状炭素系物質同士が接合されてなることを特徴とする。
これにより、熱伝導性に優れた焼結体が得られる。 In the method for manufacturing a sintered body according to the present invention, it is preferable that the method includes an impregnation step of impregnating the sintered body with a resin material after the sintering step.
Thereby, the mechanical strength of the sintered body becomes particularly excellent.
The sintered body of the present invention is manufactured by the method for manufacturing a sintered body of the present invention.
Thereby, the sintered compact excellent in heat conductivity is obtained.
The sintered body of the present invention is characterized in that fibrous carbon-based materials are bonded to each other through a heat conductive material containing a metal.
Thereby, the sintered compact excellent in heat conductivity is obtained.

以下、本発明の焼結体の製造方法および焼結体の好適な実施形態について、添付図面を参照しつつ詳細に説明する。
まず、本発明の焼結体について説明する。
図１は、本発明の焼結体の好適な実施形態について、そのミクロ構造を模式的に示す断面図である。 Hereinafter, preferred embodiments of a method for producing a sintered body and a sintered body according to the present invention will be described in detail with reference to the accompanying drawings.
First, the sintered body of the present invention will be described.
FIG. 1 is a cross-sectional view schematically showing the microstructure of a preferred embodiment of the sintered body of the present invention.

図１に示す焼結体１は、金属を含む熱伝導性物質３を介して繊維状炭素系物質２同士が接合（連結）されてなる基材１０中に、非晶質の炭素４を含み、さらに、基材１０と炭素４とで画成される空間（空隙）に、充填物１１が充填されて構成されている。
なお、本明細書中において、「金属を含む熱伝導性物質」とは、金属単体や合金を主成分として構成されたもののみならず、金属の酸化物、窒化物、酸窒化物、炭化物などの化合物を主成分として構成されたものをも含む概念である。 A sintered body 1 shown in FIG. 1 includes amorphous carbon 4 in a base material 10 in which fibrous carbon-based materials 2 are joined (connected) via a thermally conductive material 3 containing metal. Further, the space (gap) defined by the base material 10 and the carbon 4 is filled with the filler 11.
In the present specification, the “thermally conductive substance containing a metal” is not limited to those composed of a single metal or an alloy as a main component, but also metal oxides, nitrides, oxynitrides, carbides, etc. It is also a concept including those composed of the above compound as a main component.

繊維状炭素系物質２としては、単層カーボンナノチューブ、多層カーボンナノチューブ等のカーボンナノチューブ、気相成長炭素繊維、カーボンナノファイバー、ＣＮナノチューブ、ＣＮナノファイバー、ＢＣＮナノチューブ、ＢＣＮナノファイバー等が挙げられるが、これらの中でも特に、カーボンナノチューブ、気相成長炭素繊維、カーボンナノファイバーを含むものであるのが好ましく、カーボンナノチューブおよび／または気相成長炭素繊維を含むものであるのがより好ましく、カーボンナノチューブおよび気相成長炭素繊維のうちの少なくとも一方を主成分とするものがさらに好ましい。   Examples of the fibrous carbon-based material 2 include carbon nanotubes such as single-walled carbon nanotubes and multi-walled carbon nanotubes, vapor-grown carbon fibers, carbon nanofibers, CN nanotubes, CN nanofibers, BCN nanotubes, and BCN nanofibers. Among these, carbon nanotubes, vapor-grown carbon fibers, and carbon nanofibers are preferred, carbon nanotubes and / or vapor-grown carbon fibers are more preferred, and carbon nanotubes and vapor-grown carbon are preferred. More preferably, the main component is at least one of the fibers.

繊維状炭素系物質２がこのような材料で構成されたものであると、焼結体１は、その熱伝導性が特に優れたものになるとともに、機械的強度（形状の安定性）も向上する。
また、繊維状炭素系物質２は、１本鎖構造（分岐鎖を有さない直鎖状構造）を有するものであってもよいし、分岐鎖構造を有するものであってもよい。
熱伝導性物質３としては、金属単体が望ましいが、合金、金属の酸化物、窒化物、酸窒化物、炭化物などの化合物を主成分として構成されたものであってもかまわず、特に限定されない。これらの中でも、熱伝導性物質３としては、Ｃｕ、Ａｇ、Ａｌ、またはこれらを含む合金、これらを含む酸化物のうちの少なくとも１種を主成分とするものが好ましい。このように熱伝導性物質３が構成されていると、繊維状炭素系物質同士を接合する熱伝導性物質３が優れた熱伝導性を有するので、得られる焼結体は、特に優れた熱伝導性を有するものとなる。 When the fibrous carbonaceous material 2 is composed of such a material, the sintered body 1 has particularly excellent thermal conductivity and improved mechanical strength (shape stability). To do.
Moreover, the fibrous carbonaceous material 2 may have a single chain structure (a straight chain structure not having a branched chain) or a branched chain structure.
The heat conductive material 3 is preferably a single metal, but may be composed of a compound such as an alloy, metal oxide, nitride, oxynitride, carbide, etc. as a main component, and is not particularly limited. . Among these, as the heat conductive material 3, a material containing at least one of Cu, Ag, Al, an alloy containing these, and an oxide containing these as a main component is preferable. When the heat conductive material 3 is configured in this manner, the heat conductive material 3 that joins the fibrous carbon-based materials has excellent heat conductivity. It has conductivity.

焼結体１は、熱伝導性物質３を介して繊維状炭素系物質２同士が接合された構成（特に、３次元的なネットワークを形成した構成）の基材１０を有することにより、熱伝導性（伝熱性）に優れたものとなる。このため、焼結体１が、比較的肉厚の大きい（厚肉の）部材（例えば、肉厚が１０ｍｍ以上の部材）であっても、十分な伝熱性（放熱性、抜熱性）を発揮することができる。   The sintered body 1 has a base material 10 having a configuration (particularly, a configuration in which a three-dimensional network is formed) in which the fibrous carbon-based materials 2 are bonded to each other via the heat conductive material 3, so that heat conduction is achieved. Excellent in heat transfer properties. For this reason, even if the sintered body 1 is a relatively thick (thick) member (for example, a member having a thickness of 10 mm or more), sufficient heat conductivity (heat dissipation and heat extraction) is exhibited. can do.

したがって、本発明の焼結体１は、例えば、冷却用部材、ノートパソコンやビデオプロジェクター等の筐体で放熱を必要とする箇所を構成する部材等、優れた熱伝導性が要求されるような部材に、好適に適用することができる。
なお、本明細書中において、「接合」とは、物理的な結合や、化学的な結合（共有結合等）を含む概念である。 Therefore, the sintered body 1 of the present invention is required to have excellent thermal conductivity, for example, a member for constituting a portion that requires heat dissipation in a casing such as a cooling member or a notebook computer or a video projector. It can apply suitably to a member.
Note that in this specification, “bonding” is a concept including physical bonding or chemical bonding (covalent bonding or the like).

また、本発明の焼結体１では、繊維状炭素系物質２と熱伝導性物質３とを含む材料で構成されており、これにより、十分な熱伝導性を発揮することができる。
これにより、焼結体１（後述するような成形体）の加工性が特に優れたものとなり、製造工程中における加工、製造後における加工（例えば、バリ取り等）を比較的容易に行うことができる。その結果、本発明によれば、複雑な形状の焼結体１や、微小な焼結体１であっても、容易かつ確実に製造することが可能である。 Moreover, in the sintered compact 1 of this invention, it is comprised with the material containing the fibrous carbonaceous material 2 and the heat conductive substance 3, Thereby, sufficient heat conductivity can be exhibited.
Thereby, the workability of the sintered body 1 (molded body as will be described later) becomes particularly excellent, and processing during the manufacturing process and processing after the manufacturing (for example, deburring, etc.) can be performed relatively easily. it can. As a result, according to the present invention, even a sintered body 1 having a complicated shape or a minute sintered body 1 can be easily and reliably manufactured.

しかも、本発明においては、焼結体１が繊維状炭素系物質２を含むものであるため、焼結体１においては、製造時等における優れた加工性と、機械的強度、弾性等成形体としての優れた特性とを両立することができる。
また、本発明の焼結体１は、少なくとも、繊維状炭素系物質２と熱伝導性物質３とを含む材料で構成されたものであればよいが、本実施形態の焼結体１は、構成成分として、炭素４を含み、さらには充填物１１を含んでいる。これにより、例えば、焼結体１の機械的強度が特に優れたものとなる。 Moreover, in the present invention, since the sintered body 1 contains the fibrous carbon-based material 2, the sintered body 1 has excellent workability at the time of production and the like as a molded body such as mechanical strength and elasticity. It is possible to achieve both excellent characteristics.
In addition, the sintered body 1 of the present invention may be any material that includes at least the fibrous carbon-based material 2 and the heat conductive material 3, but the sintered body 1 of the present embodiment is It contains carbon 4 as a constituent component, and further contains a filler 11. Thereby, for example, the mechanical strength of the sintered body 1 becomes particularly excellent.

炭素４は、基材１０を形成した後に、その間隙に充填されたものであってもよいが、後述するように、焼結体１の製造の際に、バインダーが変化（非晶質化）して得られるものであるのが好ましい。これにより、焼結体１の製造工程の簡略化を図ることができる。なお、炭素４は非晶質でなくともよく、炭素４としては、グラファイト、ガラス状繊維、ソフトカーボン、ハードカーボンなどの各種炭素物質を用いることができる。   The carbon 4 may be filled in the gap after forming the base material 10, but as described later, the binder is changed (amorphized) during the production of the sintered body 1. Is preferably obtained. Thereby, the manufacturing process of the sintered compact 1 can be simplified. The carbon 4 may not be amorphous, and various carbon materials such as graphite, glassy fiber, soft carbon, and hard carbon can be used as the carbon 4.

また、基材１０の間隙に、炭素４が存在することにより、焼結体１の機械的強度を優れたものとすることができる。
充填物１１は、主として樹脂で構成されるものが好ましい。この樹脂としては、特に限定されないが、例えば、ポリイミド、フェノール樹脂、メラミン樹脂、ユリア樹脂、不飽和ポリエステル樹脂、エポキシ樹脂、ポリウレタン樹脂等が挙げられ、これらから選択される少なくとも１種または２種以上を組み合わせて用いることができる。 Further, the presence of the carbon 4 in the gap between the base materials 10 can make the sintered body 1 excellent in mechanical strength.
The filler 11 is preferably composed mainly of a resin. Examples of the resin include, but are not limited to, polyimide, phenol resin, melamine resin, urea resin, unsaturated polyester resin, epoxy resin, polyurethane resin, and the like. At least one or more selected from these resins can be used. Can be used in combination.

これにより、焼結体１の機械的強度を特に優れたものとするとともに、樹脂の種類等に応じて、焼結体１としてのガスバリア性、液体不透過性、耐熱性、加工性、耐薬品性（例えば、耐酸性等）、耐水性さらに難燃性等の他の特性のさらなる向上を図ることができる。
例えば、樹脂としてポリイミドを主成分とするものを用いた場合には、焼結体１の耐熱性を特に優れたものとすることができ、樹脂としてフェノール樹脂を主成分とするものを用いた場合には、焼結体１の耐酸性、耐水性さらに難燃性を特に優れたものとすることができる。 As a result, the mechanical strength of the sintered body 1 is made particularly excellent, and the gas barrier property, liquid impermeability, heat resistance, workability, chemical resistance as the sintered body 1 depending on the type of resin and the like. It is possible to further improve other properties such as property (for example, acid resistance), water resistance, and flame retardancy.
For example, when a resin mainly containing polyimide is used, the heat resistance of the sintered body 1 can be made particularly excellent, and when a resin mainly containing a phenol resin is used. In particular, it is possible to make the sintered body 1 particularly excellent in acid resistance, water resistance and flame retardancy.

焼結体１中における繊維状炭素系物質２の含有率（含有量）は、特に限定されないが、５０〜９８ｗｔ％であるのが好ましく、８０〜９０ｗｔ％であるのがより好ましく、８５〜９０ｗｔ％であるのがさらに好ましい。
焼結体１中における繊維状炭素系物質２の含有率が前記下限値未満であると、焼結体１の用途等によっては、十分な熱伝導性を発揮させるのが困難になる可能性がある。一方、焼結体１中における繊維状炭素系物質２の含有率が前記上限値を超えると、繊維状炭素系物質２以外の成分（熱伝導性物質３、炭素４、充填物１１等）の含有率が相対的に低下するため、例えば、繊維状炭素系物質２と熱伝導性物質３との接合箇所（接合点）の数が低下し、焼結体１の用途等によっては、焼結体１としての熱伝導性、機械的強度を十分に発揮させるのが困難になる可能性がある。 The content (content) of the fibrous carbonaceous material 2 in the sintered body 1 is not particularly limited, but is preferably 50 to 98 wt%, more preferably 80 to 90 wt%, and 85 to 90 wt%. % Is more preferable.
If the content of the fibrous carbonaceous material 2 in the sintered body 1 is less than the lower limit, depending on the use of the sintered body 1, it may be difficult to exert sufficient thermal conductivity. is there. On the other hand, when the content of the fibrous carbonaceous material 2 in the sintered body 1 exceeds the upper limit, components other than the fibrous carbonaceous material 2 (thermally conductive material 3, carbon 4, filler 11 and the like) Since the content rate is relatively lowered, for example, the number of joints (joint points) between the fibrous carbon-based material 2 and the heat conductive material 3 is reduced. There is a possibility that it is difficult to sufficiently exhibit the thermal conductivity and mechanical strength of the body 1.

このような焼結体１は、室温付近（例えば、２０℃）での熱伝導率が、８０Ｗ・ｍ^−１・Ｋ^−１以上であるのが好ましく、１５０Ｗ・ｍ^−１・Ｋ^−１以上であるのがより好ましい。このような条件を満足することにより、冷却用部材等のように、特に優れた熱伝導性が要求される部材に、焼結体１をより好適に適用することができる。
特に、本発明では、金属材料単独でなくても優れた熱伝導性を発揮することができるので、金属材料のみで構成されていた従来の部材に代わり、本発明の焼結体１を適用することにより、部材の軽量化、成形性の向上等、優れた効果が得られる。 Such a sintered body 1 preferably has a thermal conductivity in the vicinity of room temperature (for example, 20 ° C.) of 80 W · m ⁻¹ · K ⁻¹ or more, and 150 W · m ⁻¹ · K ⁻¹ or more. It is more preferable that By satisfying such conditions, the sintered body 1 can be more suitably applied to a member that requires particularly excellent thermal conductivity, such as a cooling member.
In particular, in the present invention, excellent thermal conductivity can be exhibited without using a metal material alone, and therefore, the sintered body 1 of the present invention is applied in place of the conventional member composed only of the metal material. Thus, excellent effects such as weight reduction of the member and improvement of moldability can be obtained.

なお、焼結体１中には、前述したような、繊維状炭素系物質２、熱伝導性物質３、炭素４、充填物１１以外の成分が含まれていてもよい。例えば、焼結体１中には、ハードカーボン、ソフトカーボン、グラッシーカーボン、フラーレン、ダイヤモンド、ダイヤモンド様炭素（ＤＬＣ）、可塑剤、酸化防止剤、着色剤、光沢剤、各種フィラー等が含まれていてもよい。   The sintered body 1 may contain components other than the fibrous carbon-based material 2, the heat conductive material 3, the carbon 4, and the filler 11 as described above. For example, the sintered body 1 contains hard carbon, soft carbon, glassy carbon, fullerene, diamond, diamond-like carbon (DLC), plasticizer, antioxidant, colorant, brightener, various fillers, and the like. May be.

次に、焼結体１の製造方法の一例を説明する。
本実施形態の焼結体１の製造方法は、繊維状炭素系物質２と、主として熱硬化性樹脂で構成されるバインダーと、金属を含む熱伝導性物質とを混合して、成形体形成用の組成物（成形体形成用組成物）を得る組成物調製工程［１］と、この組成物を加熱しつつ成形して、成形体を得る成形工程［２］と、得られた成形体を焼成して、焼結体を得る焼成工程［３］と、得られた焼結体に樹脂系材料を含浸させる含浸工程［４］とを有する。以下、各工程を詳細に説明する。 Next, an example of a method for manufacturing the sintered body 1 will be described.
The method of manufacturing the sintered body 1 of the present embodiment is for forming a molded body by mixing a fibrous carbon-based material 2, a binder mainly composed of a thermosetting resin, and a heat conductive material containing a metal. A composition preparation step [1] for obtaining a composition (molded body forming composition), a molding step [2] for molding the composition while heating the composition, and a molded body obtained There are a firing step [3] for obtaining a sintered body by firing, and an impregnation step [4] for impregnating the obtained sintered body with a resin material. Hereinafter, each process will be described in detail.

［１］組成物調製工程
まず、繊維状炭素系物質２と、バインダーと、金属を含む熱伝導性物質とを混合して、成形体形成用の組成物を得る。
熱伝導性物質は、後述する工程［３］の加熱により、溶融して、繊維状炭素系物質２同士を接合する機能を有するものである。 [1] Composition Preparation Step First, the fibrous carbon-based material 2, a binder, and a thermally conductive material containing a metal are mixed to obtain a composition for forming a molded body.
The thermally conductive material is melted by heating in step [3] to be described later and has a function of joining the fibrous carbonaceous materials 2 together.

熱伝導性物質は、Ｃｕ、Ａｇ、Ａｌ、またはこれらを含む合金、これらの金属を含む酸化物よりなる群から選択される少なくとも１種の成分を主成分とするものであることが好ましい。このような熱伝導性物質は優れた熱伝導性を有するので、繊維状炭素系物質同士を接合する熱伝導性物質３が優れた熱伝導性を有し、その結果、得られる焼結体は、特に優れた熱伝導性を有するものとなる。   It is preferable that the heat conductive material is mainly composed of at least one component selected from the group consisting of Cu, Ag, Al, alloys containing these, and oxides containing these metals. Since such a heat conductive material has excellent heat conductivity, the heat conductive material 3 for joining the fibrous carbon-based materials has excellent heat conductivity. As a result, the obtained sintered body is In particular, it has excellent thermal conductivity.

バインダーは、次工程［２］の加熱により、繊維状炭素系物質２同士の間で溶融した後硬化（または半硬化）して、これらを接近させた状態で固定（保持）する機能を有するものである。したがって、次工程［２］への移行時に成形体の型崩れを確実に防止できる。また、後述の工程［３］でも、繊維状炭素系物質同士が熱伝導性物質を介して接合されるだけでなく、バインダーによって繊維状炭素系物質同士が固定されるので、焼結体の機械的強度が向上する。なお、バインダーを用いなくとも熱伝導性物質３のみで次工程［２］の成形により繊維状炭素系物質２同士を接近させた状態で固定（保持）することができる場合などには、本発明の製造方法では、バインダーは必ずしも必要ではない。   The binder has a function of melting (or semi-curing) after melting between the fibrous carbonaceous materials 2 by heating in the next step [2], and fixing (holding) them in a state where they are brought close to each other. It is. Therefore, it is possible to reliably prevent the molded body from being deformed during the transition to the next step [2]. Also, in the step [3] described later, the fibrous carbonaceous materials are not only joined to each other via the heat conductive material, but the fibrous carbonaceous materials are fixed to each other by the binder. The mechanical strength is improved. In the case where the fibrous carbonaceous material 2 can be fixed (held) in the state of being brought close to each other by molding in the next step [2] without using a binder, the present invention can be used. In this production method, a binder is not always necessary.

また、バインダーとしては、次工程［２］または後述する工程［３］の加熱により、炭素４に変化（変換）するもの、例えば、ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体、エチレン−酢酸ビニル共重合体（ＥＶＡ）等のポリオレフィン、環状ポリオレフィン、変性ポリオレフィン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリスチレン、ポリアミド、ポリイミド、ポリアミドイミド、ポリカーボネート、ポリ−（４−メチルペンテン−１）、アイオノマー、アクリル系樹脂、ポリメチルメタクリレート、アクリロニトリル−ブタジエン−スチレン共重合体（ＡＢＳ樹脂）、アクリロニトリル−スチレン共重合体（ＡＳ樹脂）、ブタジエン−スチレン共重合体、ポリオキシメチレン、ポリビニルアルコール（ＰＶＡ）、エチレン−ビニルアルコール共重合体（ＥＶＯＨ）、ポリエチレンテレフタレート（ＰＥＴ）、ポリブチレンテレフタレート（ＰＢＴ）、ポリシクロヘキサンテレフタレート（ＰＣＴ）等のポリエステル、ポリエーテル、ポリエーテルケトン（ＰＥＫ）、ポリエーテルエーテルケトン（ＰＥＥＫ）、ポリエーテルイミド、ポリアセタール（ＰＯＭ）、ポリフェニレンオキシド、変性ポリフェニレンオキシド、ポリサルフォン、ポリエーテルサルフォン、ポリフェニレンサルファイド、ポリアリレート、芳香族ポリエステル（液晶ポリマー）、ポリテトラフルオロエチレン、ポリフッ化ビニリデン、その他フッ素系樹脂、スチレン系、ポリオレフィン系、ポリ塩化ビニル系、ポリウレタン系、ポリエステル系、ポリアミド系、ポリブタジエン系、トランスポリイソプレン系、フッ素ゴム系、塩素化ポリエチレン系等の各種熱可塑性エラストマーのような各種熱可塑性樹脂、エポキシ樹脂、フェノール樹脂、ユリア樹脂、メラミン樹脂、不飽和ポリエステル、シリコーン樹脂、ポリウレタンのような熱硬化性樹脂等、またはこれらを主とする共重合体、ブレンド体、ポリマーアロイ等が挙げられ、これらのうちの１種または２種以上を組み合わせて用いることができる。これらの中でも、バインダーとしては各種熱硬化性樹脂が好ましい。各種熱硬化性樹脂をバインダーとして用いると、熱硬化性樹脂が成形工程や焼成工程での加熱により溶融もしくは炭化するので、より確実に繊維状炭素系物質同士を熱硬化性樹脂により固定しておくことができる。   The binder may be one that changes (converts) to carbon 4 by heating in the next step [2] or step [3] described below, such as polyethylene, polypropylene, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer. Polyolefin such as polymer (EVA), cyclic polyolefin, modified polyolefin, polyvinyl chloride, polyvinylidene chloride, polystyrene, polyamide, polyimide, polyamideimide, polycarbonate, poly- (4-methylpentene-1), ionomer, acrylic resin , Polymethyl methacrylate, acrylonitrile-butadiene-styrene copolymer (ABS resin), acrylonitrile-styrene copolymer (AS resin), butadiene-styrene copolymer, polyoxymethylene, polyvinyl alcohol (PVA), Polyester such as len-vinyl alcohol copolymer (EVOH), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polycyclohexane terephthalate (PCT), polyether, polyether ketone (PEK), polyether ether ketone (PEEK) ), Polyetherimide, polyacetal (POM), polyphenylene oxide, modified polyphenylene oxide, polysulfone, polyethersulfone, polyphenylene sulfide, polyarylate, aromatic polyester (liquid crystal polymer), polytetrafluoroethylene, polyvinylidene fluoride, other fluorine Resin, styrene, polyolefin, polyvinyl chloride, polyurethane, polyester, polyamide, polybutadiene, Various thermoplastic resins such as Lance polyisoprene, fluororubber, chlorinated polyethylene, and other thermoplastic elastomers, epoxy resins, phenol resins, urea resins, melamine resins, unsaturated polyesters, silicone resins, polyurethanes, etc. Thermosetting resins and the like, or copolymers, blends, polymer alloys and the like mainly containing these resins can be used, and one or more of these can be used in combination. Among these, various thermosetting resins are preferable as the binder. When various thermosetting resins are used as the binder, the thermosetting resin melts or carbonizes by heating in the molding process or firing process, so that the fibrous carbonaceous materials are more reliably fixed with the thermosetting resin. be able to.

また、バインダーとしては、前述の熱硬化性樹脂の中でも、特に、エポキシ樹脂およびフェノール樹脂の少なくとも一方を主成分とするものが好ましい。これらのものは、後述する加熱により比較的低温で溶融するとともに、比較的容易に非晶質状態となることから好ましい。
これらのバインダーおよび熱伝導性物質は、いずれか一方が粒子状をなしているのが好ましく、双方が粒子状をなしているのがより好ましい。後述するように、組成物（成形体形成用組成物）中には、実質的に液体が含まれないものが好ましいが、バインダーおよび／または熱伝導性物質を粒子状とすることにより、組成物は、適度な流動性を有するものとなる。これにより、次工程［２］における組成物の成形性をより向上させることができる。 As the binder, among the above-mentioned thermosetting resins, those having at least one of an epoxy resin and a phenol resin as a main component are particularly preferable. These are preferable because they are melted at a relatively low temperature by heating, which will be described later, and relatively easily become amorphous.
Either one of these binders and the thermally conductive material is preferably in the form of particles, and more preferably both are in the form of particles. As will be described later, the composition (molded body forming composition) is preferably substantially free of liquid, but the composition can be obtained by making the binder and / or the heat conductive substance into particles. Has moderate fluidity. Thereby, the moldability of the composition in the next step [2] can be further improved.

また、バインダーおよび／または熱伝導性物質を粒子状とすることにより、組成物中において各成分がより均一に混ざり合った状態となる。その結果、得られる焼結体１を、特性の安定性（例えば、各部位での、熱伝導率の均一性や、外的応力に対する安定性の均一性等）に優れたものとすることができる。
また、各成分がより均一に混ざり合った状態の組成物を用いることにより、後述する工程［３］における加熱による成形体の各部位における収縮率のバラツキをより小さいものとすることができ、得られる焼結体１の寸法を、設計値からの誤差がより小さいものとすることができる。 Further, by forming the binder and / or the heat conductive material in the form of particles, the components are more uniformly mixed in the composition. As a result, the obtained sintered body 1 should be excellent in stability of characteristics (for example, uniformity of thermal conductivity, uniformity of stability against external stress, etc. at each part). it can.
Further, by using a composition in which each component is mixed more uniformly, variation in shrinkage rate at each part of the molded body due to heating in the step [3] to be described later can be reduced. The size of the sintered body 1 to be obtained can be set to have a smaller error from the design value.

バインダーおよび熱伝導性物質の双方を粒子状とする場合、粒子状の熱伝導性物質（以下、「熱伝導性物質粒子」と言う。）の平均粒径は、粒子状のバインダー（以下、「バインダー粒子」と言う。）の平均粒径より小さいのが好ましい。これにより、次工程［２］において、組成物に加わる圧力がバインダーに十分に伝達されるので、繊維状炭素系物質２同士をより接近させた状態で固定するという効果が発揮される。また、この状態では、熱伝導性物質粒子は、繊維状炭素系物質２同士に確実に接触した状態で存在することになる。その結果、後述する工程［３］において、繊維状炭素系物質２同士を熱伝導性物質３により確実に接合することができる。   When both the binder and the thermally conductive material are in the form of particles, the average particle size of the particulate thermally conductive material (hereinafter referred to as “thermally conductive material particles”) It is preferably smaller than the average particle size of “binder particles”. Thereby, in the next step [2], since the pressure applied to the composition is sufficiently transmitted to the binder, the effect of fixing the fibrous carbonaceous materials 2 in a state where they are brought closer to each other is exhibited. Further, in this state, the heat conductive material particles are present in a state in which the fibrous carbonaceous material 2 is in reliable contact with each other. As a result, in the step [3] described later, the fibrous carbon-based materials 2 can be reliably bonded to each other by the heat conductive material 3.

熱伝導性物質粒子の平均粒径をＡ［μｍ］とし、バインダー粒子の平均粒径をＢ［μｍ］としたとき、Ａ／Ｂ≦０．１なる関係を満足するのが好ましく、Ａ／Ｂ≦０．０５なる関係を満足するのがより好ましい。これにより、前記効果がより顕著に発揮される。
具体的には、熱伝導性物質粒子の平均粒径Ａは、１〜３０μｍであるのが好ましく、１〜１０μｍであるのがより好ましい。 When the average particle diameter of the thermally conductive material particles is A [μm] and the average particle diameter of the binder particles is B [μm], it is preferable that the relationship of A / B ≦ 0.1 is satisfied. It is more preferable to satisfy the relationship of ≦ 0.05. Thereby, the said effect is exhibited more notably.
Specifically, the average particle diameter A of the heat conductive material particles is preferably 1 to 30 μm, and more preferably 1 to 10 μm.

また、バインダー粒子の平均粒径Ｂは、１０〜２００μｍであるのが好ましく、１０〜５０μｍであるのがより好ましい。
また、組成物中における繊維状炭素系物質２の含有率（含有量）は、特に限定されないが、５０〜９０ｗｔ％であるのが好ましく、８０〜９０ｗｔ％であるのがより好ましく、８５〜９０ｗｔ％であるのがさらに好ましい。これにより、得られる焼結体１は、特に優れた熱伝導性を有するとともに、優れた形状の安定性を有するものとすることができる。 Moreover, it is preferable that the average particle diameter B of binder particle | grains is 10-200 micrometers, and it is more preferable that it is 10-50 micrometers.
Moreover, the content rate (content) of the fibrous carbonaceous material 2 in the composition is not particularly limited, but is preferably 50 to 90 wt%, more preferably 80 to 90 wt%, and 85 to 90 wt%. % Is more preferable. Thereby, the obtained sintered body 1 can have particularly excellent thermal conductivity and excellent shape stability.

これに対し、組成物中における繊維状炭素系物質２の含有率が前記下限値未満であると、得られる焼結体１は、その用途等によっては、十分な熱伝導性を発揮するのが困難となる可能性がある。また、組成物中における繊維状炭素系物質２の含有率が前記上限値を超えると、次工程［２］における組成物の成形性が低下するとともに、得られる焼結体１の機械的強度が低下する傾向を示す。   On the other hand, when the content of the fibrous carbonaceous material 2 in the composition is less than the lower limit, the obtained sintered body 1 exhibits sufficient thermal conductivity depending on its use and the like. It can be difficult. Moreover, when the content rate of the fibrous carbonaceous material 2 in a composition exceeds the said upper limit, while the moldability of the composition in the following process [2] will fall, the mechanical strength of the obtained sintered compact 1 will be sufficient. Shows a downward trend.

また、組成物は、実質的に液体（溶媒や分散媒）を含まないものであるのが好ましい。これにより、次工程［２］の加熱により、前記液体が気化して成形体の形状が崩れてしまうことを防止することができる。
なお、必要に応じて、上記のような混合の後（または、上記のような混合に代えて）、混練処理（混練工程）を施してもよい。これにより、各成分がより均一に混ざり合った組成物（成形体形成用組成物）を得ることができる。 Moreover, it is preferable that a composition does not contain a liquid (a solvent or a dispersion medium) substantially. Thereby, it can prevent that the said liquid evaporates and the shape of a molded object collapse | crumbles by the heating of next process [2].
In addition, you may give a kneading | mixing process (kneading process) after the above mixing (or replacing with the above mixing) as needed. Thereby, the composition (composition for forming a molded body) in which the components are mixed more uniformly can be obtained.

［２］成形工程
次に、得られた組成物を加熱しつつ成形して、成形体を得る。
成形体の形状は、特に限定されないが、目的とする焼結体１に対応する形状（ただし、後述する焼成工程等での収縮分を見込んだ形状）に、成形することができる。
このように、目的とする焼結体１に対応する形状の成形体を作製することにより、後の工程における、研削、研磨等の機械加工等を省略または簡素化することができ、このような機械加工等に伴う削りかすの発生を好適に防止することができる。 [2] Molding step Next, the obtained composition is molded while being heated to obtain a molded body.
Although the shape of the molded body is not particularly limited, it can be molded into a shape corresponding to the target sintered body 1 (however, a shape that allows for shrinkage in a firing step or the like described later).
Thus, by producing a molded body having a shape corresponding to the intended sintered body 1, machining such as grinding and polishing in the subsequent steps can be omitted or simplified. The generation of shavings accompanying machining or the like can be suitably prevented.

組成物の成形方法としては、特に限定されず、目的とする焼結体１の形状等に応じて、圧縮成形（プレス成形）、押出成形、射出成形、カレンダー成形等を適宜選択して用いることができる。
また、成形時には、繊維状炭素系物質２同士ができるだけ接近するように前記組成物に圧力をかけるのが好ましい。かかる観点からは、組成物の成形方法としては、圧縮成形（プレス成形）が好適である。これにより、繊維状炭素系物質２同士を接近させることにより、熱伝導性物質の溶融の条件（例えば、次工程［３］における焼成温度等）を緩和することができる。 The molding method of the composition is not particularly limited, and compression molding (press molding), extrusion molding, injection molding, calendar molding, or the like is appropriately selected and used depending on the shape of the target sintered body 1 and the like. Can do.
In molding, it is preferable to apply pressure to the composition so that the fibrous carbonaceous materials 2 are as close as possible. From this point of view, compression molding (press molding) is suitable as a method for molding the composition. Thereby, the conditions (for example, the calcination temperature etc. in the following process [3]) of a heat conductive substance can be relieve | moderated by making the fibrous carbonaceous materials 2 approach.

本工程［２］における加熱の温度（加熱温度）は、バインダーが溶融する温度以上、かつ、熱伝導性物質が溶融する温度より低い温度とされる。かかる加熱温度は、バインダーおよび熱伝導性物質の種類等によっても若干異なるが、１３０〜３００℃であるのが好ましく、１５０〜２５０℃であるのがより好ましい。これにより、繊維状炭素系物質２同士をバインダーにより、より確実に固定することができる。
加圧の時間は、特に限定されないが、１〜１２０分であるのが好ましく、１０〜９０分であるのがより好ましい。 The heating temperature (heating temperature) in this step [2] is not less than the temperature at which the binder melts and is lower than the temperature at which the thermally conductive material melts. The heating temperature is slightly different depending on the kind of the binder and the thermally conductive material, but is preferably 130 to 300 ° C, more preferably 150 to 250 ° C. Thereby, fibrous carbonaceous materials 2 can be more reliably fixed with a binder.
The pressurization time is not particularly limited, but is preferably 1 to 120 minutes, and more preferably 10 to 90 minutes.

また、加圧の圧力は、特に限定されないが、高いほど繊維状炭素物質２間の距離を小さくでき、場合によっては繊維状炭素物質２同士を直接重なり合わせることができるので熱伝導率を上昇させることができる。例えば、前記加圧の圧力としては、５０Ｍｐａ以上が好ましい。
以上のような条件で、成形体を形成することにより、より高密度な成形体が得られ、得られる焼結体１の機械的強度もより向上する。 In addition, the pressure of the pressurization is not particularly limited, but as the pressure increases, the distance between the fibrous carbon materials 2 can be reduced, and in some cases, the fibrous carbon materials 2 can be directly overlapped to increase the thermal conductivity. be able to. For example, the pressurizing pressure is preferably 50 Mpa or more.
By forming the molded body under the above conditions, a higher-density molded body is obtained, and the mechanical strength of the obtained sintered body 1 is further improved.

［３］焼成工程
次に、得られた成形体を焼成して、焼結体１を得る。
このとき、成形体中の熱伝導性物質が溶融した後に硬化することにより、熱伝導性物質３を介して繊維状炭素系物質２同士が接合される。その結果、３次元的なネットワークが形成された基材１０を有する焼結体１が得られる。 [3] Firing step Next, the obtained molded body is fired to obtain a sintered body 1.
At this time, the fibrous carbonaceous materials 2 are joined to each other through the thermally conductive material 3 by curing after the thermally conductive material in the molded body is melted. As a result, the sintered body 1 having the base material 10 on which a three-dimensional network is formed is obtained.

このような焼結体１は、熱伝導性物質３を介した繊維状炭素系物質２同士の接合強度が高く、結果として、特に熱伝導性に優れたものとなる。また、このような焼結体１では、比較的肉厚の大きいもの（例えば、肉厚が１０ｍｍ以上の部材）であっても、十分な伝熱性（放熱性）を発揮することができる。
さらに、成形体中の熱伝導性物質が溶融もしくは気化する温度まで加熱するならば、成形体中に熱伝導性物質が分布し、より均一な熱伝導性成形体を得ることが可能となる。 Such a sintered body 1 has high bonding strength between the fibrous carbon-based materials 2 via the heat conductive material 3, and as a result, is particularly excellent in heat conductivity. Moreover, in such a sintered body 1, even if it is a comparatively large thing (for example, member with thickness 10mm or more), sufficient heat transfer property (heat dissipation) can be exhibited.
Furthermore, if heating is performed to a temperature at which the thermally conductive material in the molded body melts or vaporizes, the thermally conductive material is distributed in the molded body, and a more uniform thermally conductive molded body can be obtained.

本工程［３］における焼成の温度（焼成温度）は、熱伝導性物質が溶融する温度以上とされ、熱伝導性物質の種類等によっても若干異なるが、１７００〜３５００℃であるのが好ましく、２５００〜３０００℃であるのがより好ましい。このような温度で焼成を行うことにより、より緻密で、熱伝導性物質３を介した繊維状炭素系物質２同士の接合強度が大きい焼結体１を得ることができる。かかる焼結体１は、特に優れた熱伝導性を有し、かつ、形状の安定性等に優れたものとなる。   The calcination temperature (calcination temperature) in this step [3] is not less than the temperature at which the thermally conductive material melts, and varies slightly depending on the type of thermally conductive material, but is preferably 1700 to 3500 ° C., It is more preferable that it is 2500-3000 degreeC. By firing at such a temperature, it is possible to obtain a sintered body 1 that is denser and has a higher bonding strength between the fibrous carbonaceous materials 2 via the thermally conductive material 3. The sintered body 1 has particularly excellent thermal conductivity and excellent shape stability and the like.

焼成の時間（焼成時間）は、特に限定されないが、焼成温度を前記範囲とする場合には、０．５〜１０時間であるのが好ましく、１〜７．５時間であるのがより好ましい。
また、成形体の焼成は、Ａｒ、Ｈｅ、Ｎｅ、Ｎ_２等の不活性ガス雰囲気中、または、減圧下（例えば、１×１０^−２Ｔｏｒｒ以下）で行われるのが好ましい。これにより、熱伝導性物質が金属単体である場合に、本工程［３］における熱伝導性物質の酸化を防止することができ、焼結体１の熱伝導率が均一となる。また、繊維状炭素系物質の酸化も防止されるので、得られる焼結体１は、特に優れた熱伝導性および機械的強度を有するものとなる。
なお、本工程［３］は、２回以上に分けて行ってもよい。すなわち、本発明の焼結体の製造方法は、例えば、成形体に対して、比較的温和な条件での仮焼成を施した後に、本焼成を施すものであってもよい。 The firing time (firing time) is not particularly limited, but when the firing temperature is within the above range, it is preferably 0.5 to 10 hours, and more preferably 1 to 7.5 hours.
Moreover, it is preferable that the compact is fired in an inert gas atmosphere such as Ar, He, Ne, N ₂ or under reduced pressure (for example, 1 × 10 ⁻² Torr or less). Thereby, when a heat conductive substance is a metal simple substance, the oxidation of the heat conductive substance in this process [3] can be prevented, and the heat conductivity of the sintered compact 1 becomes uniform. Moreover, since oxidation of the fibrous carbonaceous material is also prevented, the obtained sintered body 1 has particularly excellent thermal conductivity and mechanical strength.
In addition, you may perform this process [3] divided into 2 times or more. That is, the method for producing a sintered body according to the present invention may be, for example, a method in which a main body is subjected to preliminary firing after being subjected to temporary firing under relatively mild conditions.

［４］含浸工程
次に、得られた焼結体１に樹脂系材料を含浸させる。
焼結体１へ樹脂系材料を含浸させる方法（含浸方法）は、いかなるものであってもよいが、例えば、樹脂系材料中に焼結体１を浸漬する方法（ディッピング法）、樹脂系材料をドクターブレード法、刷毛塗り、スプレー塗装、ロールコート法等により焼結体１に塗布する方法（塗布法）を用いることができる。 [4] Impregnation step Next, the obtained sintered body 1 is impregnated with a resin material.
Any method for impregnating the sintered body 1 with the resin material (impregnation method) may be used. For example, a method of dipping the sintered body 1 in the resin material (dipping method), a resin material The method (application | coating method) which apply | coats to the sintered compact 1 by doctor blade method, brush coating, spray coating, roll coating method etc. can be used.

また、含浸方法としては、例えば、真空含浸（減圧含浸）法、過圧含浸法等を用いるようにしてもよい。
この樹脂系材料としては、前述した充填物１１の主材料である樹脂またはその前駆体（例えば、前記樹脂に対応するモノマー、ダイマー、トリマー、オリゴマー、プレポリマー等）等を含むものが好適に用いられる。 Further, as the impregnation method, for example, a vacuum impregnation (reduced pressure impregnation) method, an overpressure impregnation method, or the like may be used.
As this resin-based material, a resin or a precursor thereof (for example, a monomer, a dimer, a trimer, an oligomer, a prepolymer, etc. corresponding to the resin) that is the main material of the filler 11 described above is preferably used. It is done.

具体的には、樹脂系材料としては、樹脂の溶融物、樹脂またはその前駆体を含む液体（溶液または分散液）等が挙げられる。これらのものは、適度な流動性を有することから、焼結体１中に効率よく含浸させることができる。
樹脂系材料として、樹脂の溶融物を用いる場合には、溶融物を固化（硬化）させることにより、充填物１１とすることができる。 Specifically, examples of the resin material include a resin melt, a liquid (solution or dispersion) containing a resin or a precursor thereof. Since these have appropriate fluidity, they can be efficiently impregnated into the sintered body 1.
When a resin melt is used as the resin material, the filler 11 can be obtained by solidifying (curing) the melt.

また、樹脂系材料として、樹脂またはその前駆体を含む液体を用いる場合には、例えば、脱溶媒処理、脱分散媒処理、熱処理、光照射等のうちの１種または２種以上の処理を施すことにより、樹脂系材料を樹脂に変換して、充填物１１とすることができる。
さらに、樹脂系材料として、樹脂またはその前駆体を含む液体を用いる場合には、樹脂系材料中には、溶解補助剤、分散剤、分散助剤、繊維状炭素系物質、グラファイト、ハードカーボン、ソフトカーボン、グラッシーカーボン、アモルファスカーボン（非晶質の炭素）、フラーレン、ダイヤモンド、ダイヤモンド様炭素（ＤＬＣ）、可塑剤、酸化防止剤、着色剤、光沢剤、各種フィラー等が含まれていてもよい。例えば、溶解補助剤、分散剤、分散助剤等が含まれることにより、樹脂系材料の流動性を向上させ、本工程［４］を効率よく行うことができる。
以上のような工程を経て、図１に示すような焼結体１が得られる。 Moreover, when using the liquid containing resin or its precursor as a resin-type material, 1 type (s) or 2 or more types of processing among a solvent removal process, a dedispersion medium process, heat processing, light irradiation etc. are performed, for example. Thus, the resin material can be converted into a resin to form the filler 11.
Furthermore, when a resin or a liquid containing a precursor thereof is used as the resin material, the resin material includes a dissolution aid, a dispersant, a dispersion aid, a fibrous carbonaceous material, graphite, hard carbon, Soft carbon, glassy carbon, amorphous carbon (amorphous carbon), fullerene, diamond, diamond-like carbon (DLC), plasticizer, antioxidant, colorant, brightener, various fillers, etc. may be included. . For example, by including a solubilizing agent, a dispersing agent, a dispersing aid, etc., the fluidity of the resin material can be improved, and this step [4] can be performed efficiently.
Through the above steps, a sintered body 1 as shown in FIG. 1 is obtained.

また、本発明の焼結体の製造方法では、必要に応じて、前記工程［１］の組成物調製工程の前処理（前工程）や、前記各工程間での中間処理（中間工程）、前記工程［４］の含浸工程後の後処理（後工程）があってもよい。
また、本実施形態では、前記工程［２］において、目的とする焼結体１の形状に対応する形状の成形体を作製するものとして説明したが、例えば、角柱形状、円柱形状、円筒形状等、比較的単純な形状の成形体を作製しておき、前記工程［３］の前後等において、最終的な焼結体１に対応する形状に加工してもよい。 Moreover, in the manufacturing method of the sintered compact of the present invention, if necessary, pre-treatment (pre-process) of the composition preparation step of the step [1], intermediate treatment (intermediate step) between the respective steps, There may be a post-treatment (post-step) after the impregnation step of the step [4].
In the present embodiment, the process [2] has been described as producing a molded body having a shape corresponding to the desired shape of the sintered body 1. For example, a prismatic shape, a columnar shape, a cylindrical shape, or the like is used. Alternatively, a molded body having a relatively simple shape may be prepared and processed into a shape corresponding to the final sintered body 1 before and after the step [3].

前述したように、本発明においては、製造工程において得られる成形体、最終的に得られる焼結体１についても、優れた加工性を有することから、かかる方法を適用することも可能である。
次に、本発明の焼結体１を冷却用部材としてのヒートシンクに適用した一例を説明する。 As described above, in the present invention, the molded body obtained in the manufacturing process and the finally obtained sintered body 1 also have excellent workability, and thus this method can be applied.
Next, an example in which the sintered body 1 of the present invention is applied to a heat sink as a cooling member will be described.

ヒートシンクは、例えば、ＣＰＵ用の半導体チップ等に接合して用いられるが、半導体チップはその作動により発熱するため、ヒートシンクには、その熱を効率よく放熱する性能が求められる。
一方、本発明の成形体は、前述したように、熱伝導性に優れているため、本発明を適用したヒートシンク（冷却用部材）は、特に優れた性能（ヒートシンクとして求められる性能）を有するものとなる。 The heat sink is used by being bonded to, for example, a semiconductor chip for CPU. However, since the semiconductor chip generates heat due to its operation, the heat sink is required to have a performance of efficiently radiating the heat.
On the other hand, as described above, the molded body of the present invention is excellent in thermal conductivity. Therefore, the heat sink (cooling member) to which the present invention is applied has particularly excellent performance (performance required as a heat sink). It becomes.

図２は、本発明を適用したヒートシンクを示す平面図、図３は、図２中のII−II線断面図、図４は、図３の部分拡大断面図である。
これらの図に示すように、ヒートシンク（焼結体）１’は、基板５と、基板５の放熱面側（図３中上側）に基板５と一体的に形成された複数の突起（凸部）６と、各突起６を囲むように基板５と一体的に形成されたモールド枠（壁部）７とで構成されている。各突起６は、円柱状または円錐台状をなしている。また、基板５の四隅には、円形のモールド孔（孔）８が形成されている。 2 is a plan view showing a heat sink to which the present invention is applied, FIG. 3 is a sectional view taken along the line II-II in FIG. 2, and FIG. 4 is a partially enlarged sectional view of FIG.
As shown in these drawings, the heat sink (sintered body) 1 ′ includes a substrate 5 and a plurality of protrusions (convex portions) formed integrally with the substrate 5 on the heat dissipation surface side (upper side in FIG. 3) of the substrate 5. ) 6 and a mold frame (wall portion) 7 formed integrally with the substrate 5 so as to surround each protrusion 6. Each protrusion 6 has a columnar shape or a truncated cone shape. In addition, circular mold holes (holes) 8 are formed at the four corners of the substrate 5.

基板５の前記放熱面と反対側（図３中、下側）には、発熱体である半導体チップ（図示せず）と接合される接合面５１が形成されている。
また、ヒートシンク１’の少なくとも一部には、例えば、表面処理が施されていてもよい。本実施形態のヒートシンク（焼結体）１’では、接合面５１にメッキ層（被覆層）９が形成されている。このメッキ層９は、半導体チップとの接着機能またはそれを補助する機能を得るための層である。このように、本発明の焼結体は、繊維状炭素系物質、熱導電性物質を含まない部位を有していてもよい。 On the side opposite to the heat dissipation surface of the substrate 5 (lower side in FIG. 3), a bonding surface 51 is formed to be bonded to a semiconductor chip (not shown) as a heating element.
Further, for example, surface treatment may be performed on at least a part of the heat sink 1 ′. In the heat sink (sintered body) 1 ′ of the present embodiment, a plating layer (coating layer) 9 is formed on the bonding surface 51. The plated layer 9 is a layer for obtaining a bonding function with the semiconductor chip or a function for assisting the bonding. Thus, the sintered body of the present invention may have a portion that does not contain a fibrous carbonaceous material and a thermally conductive material.

メッキ層９としては、例えば、Ａｇメッキ、またはＡｇ−Ｐｄ合金メッキ等のＡｇ系合金メッキ、ＡｕメッキまたはＡｕ系合金メッキ、ＰｔメッキまたはＰｔ系合金メッキ、ＮｉメッキまたはＮｉ系合金メッキ、ＣｒメッキまたはＣｒ系合金メッキ等が挙げられる。このなかでも、特に、Ａｇ、Ａｕ、Ｐｔまたはこれらを主とする合金メッキのような、貴金属メッキが好ましい。   As the plating layer 9, for example, Ag plating, Ag-based alloy plating such as Ag-Pd alloy plating, Au plating or Au-based alloy plating, Pt plating or Pt-based alloy plating, Ni plating or Ni-based alloy plating, Cr plating Or Cr alloy plating etc. are mentioned. Among these, noble metal plating such as Ag, Au, Pt or alloy plating mainly containing these is particularly preferable.

メッキ層９の厚さは、特に限定されないが、好ましくは０．５〜２０μｍ程度、より好ましくは１〜１０μｍ程度とされる。
なお、メッキ層９の形成は、例えば、ヒートシンク１’の全表面に対しなされても良い。また、メッキ層等の被覆層の形成目的は、前述したものに限らず、例えば、保護層の形成、防食等であってもよい。 The thickness of the plating layer 9 is not particularly limited, but is preferably about 0.5 to 20 μm, more preferably about 1 to 10 μm.
The plated layer 9 may be formed on the entire surface of the heat sink 1 ′, for example. In addition, the purpose of forming the coating layer such as a plating layer is not limited to that described above, and may be, for example, formation of a protective layer, corrosion prevention, or the like.

また、表面処理としては、前記メッキの他に、例えば、樹脂被覆層の形成、黒色塗装等の塗装が挙げられる。
なお、ヒートシンク１’のメッキ層９を除く部位は、図１を参照しつつ説明した前記実施形態の焼結体１と同様の材料、すなわち、繊維状炭素系物質と熱導電性物質と炭素とを含む材料で構成されている。 In addition to the plating, examples of the surface treatment include formation of a resin coating layer and coating such as black coating.
The portion of the heat sink 1 ′ excluding the plating layer 9 is made of the same material as that of the sintered body 1 of the embodiment described with reference to FIG. 1, that is, a fibrous carbon-based material, a heat conductive material, and carbon. It is comprised with the material containing.

なお、ヒートシンクの形状、構造等は、図示のものに限定されず、例えば、ヒートシンク１’の全体形状や、放熱用の突起（凸部）６の形状、配置等は、いかなるものでもよい。
以上、本発明の焼結体の製造方法および焼結体について、好適な実施形態に基づいて説明したが、本発明はこれに限定されるものではない。
例えば、前述した実施形態では、本発明の焼結体をヒートシンクに適用した構成について説明したが、本発明の焼結体は、プロジェクターの液晶パネル保持部材、ライトガイド等の部材に適用してもよく、冷却用部材以外の部材に適用してもよい。 The shape, structure, and the like of the heat sink are not limited to those shown in the drawing, and for example, the overall shape of the heat sink 1 ′ and the shape, arrangement, etc. of the heat dissipation protrusions (convex portions) 6 may be any.
As mentioned above, although the manufacturing method and sintered compact of the sintered compact of this invention were demonstrated based on suitable embodiment, this invention is not limited to this.
For example, in the embodiment described above, the configuration in which the sintered body of the present invention is applied to a heat sink has been described. However, the sintered body of the present invention may be applied to members such as a liquid crystal panel holding member and a light guide of a projector. It may be applied to members other than the cooling member.

［冷却用部材（ヒートシンク）の製造］
以下のようにして、各実施例および各比較例において、図２、図３に示すような冷却用部材（ヒートシンク）を、それぞれ、２０個ずつ製造した。
（実施例１）
まず、繊維状炭素系物質としてカーボンナノチューブ（昭和電工株式会社製、ＶＧＣＦ）：１ｋｇ、バインダーとしてフェノール樹脂の粒子：７０ｇと、熱伝導性物質粒子としてＣｕ粒子：５０ｇを用意した。
なお、Ｃｕ粒子の平均粒径Ａは、２μｍ、フェノール樹脂粒子の平均粒子Ｂは、４０μｍであり、Ａ／Ｂ＝０．０５であった。 [Manufacture of cooling members (heat sinks)]
In each example and each comparative example, 20 cooling members (heat sinks) as shown in FIGS. 2 and 3 were produced as follows.
(Example 1)
First, carbon nanotubes (VGCF, manufactured by Showa Denko KK): 1 kg as a fibrous carbon-based material, phenol resin particles: 70 g as a binder, and Cu particles: 50 g as heat conductive material particles were prepared.
The average particle diameter A of Cu particles was 2 μm, the average particle B of phenol resin particles was 40 μm, and A / B = 0.05.

次に、これらを混合し、さらに、混練装置を用いて混練することにより、成形体形成用組成物を得た。なお、成形体形成用組成物中には、液体は含まれていなかった。
次に、圧縮成形（熱プレス）により、成形体形成用組成物を、図２、図３に示すヒートシンクに対応する形状に成形し、成形体を得た。
なお、圧縮成形は、圧力５０ＭＰａ、１５０℃×１５分で行った。 Next, these were mixed and further kneaded using a kneader to obtain a composition for forming a molded body. In addition, the liquid was not contained in the composition for molded object formation.
Next, the composition for forming a molded body was molded into a shape corresponding to the heat sink shown in FIGS. 2 and 3 by compression molding (hot pressing) to obtain a molded body.
The compression molding was performed at a pressure of 50 MPa and 150 ° C. for 15 minutes.

また、成形体の形状寸法は、以後の焼成等での収縮分を見込んで決定し、ヒートシンク（メッキ層が形成されていない焼結体）が、全体寸法＝縦２５ｍｍ×横２５ｍｍ、突起寸法＝外径φ１．２５ｍｍ、長さ１ｍｍ、基板厚さ７ｍｍとなるようにした。
次に、得られた成形体を室温（常温）となるまで放置した後、不活性雰囲気（Ａｒガス雰囲気）中、Ｃｕの融点（１０８４℃）より高い温度である１２００℃×２時間で焼成することにより焼結体を得た。 Further, the shape dimensions of the molded body are determined in consideration of the shrinkage due to the subsequent firing or the like, and the heat sink (sintered body on which no plating layer is formed) has an overall dimension = vertical 25 mm × horizontal 25 mm, projection dimension = The outer diameter was 1.25 mm, the length was 1 mm, and the substrate thickness was 7 mm.
Next, the obtained molded body is allowed to stand until it reaches room temperature (room temperature), and then fired in an inert atmosphere (Ar gas atmosphere) at 1200 ° C. × 2 hours, which is a temperature higher than the melting point of Cu (1084 ° C.). As a result, a sintered body was obtained.

次に、ディッピング法を用いて、得られた焼結体に樹脂系材料を含浸させた。
なお、樹脂系材料としては、液状のフェノール樹脂（住友ベークライト株式会社製、スミライトレジンＰＲ−５１４６４）を用いた。
次に、フェノール樹脂を含浸させた焼結体から、表面に付着しているフェノール樹脂を除去し、さらに、１５０℃×６０分間で加熱することにより、液状のフェノール樹脂を硬化させ、ヒートシンクを得た。 Next, the obtained sintered body was impregnated with a resin material using a dipping method.
In addition, as a resin-type material, the liquid phenol resin (Sumitomo Bakelite Co., Ltd. make, Sumilite resin PR-51464) was used.
Next, the phenol resin adhering to the surface is removed from the sintered body impregnated with the phenol resin, and the liquid phenol resin is cured by heating at 150 ° C. for 60 minutes to obtain a heat sink. It was.

このようにして得られたヒートシンクにおいては、熱伝導性物質がカーボンナノチューブに融着して、この熱伝導性物質を介してカーボンナノチューブ同士が接合され、３次元的なネットワークが形成さていること、また、カーボンナノチューブ同士の間隙には、非晶質の炭素が存在することが、走査型電子顕微鏡（ＳＥＭ）の観察から確認された。
また、ヒートシンク（焼結体）中におけるカーボンナノチューブの含有率は、９０ｗｔ％以上であった。
また、本実施例においては、製造工程中における削りかす等の発生を生じることなく、ヒートシンクを好適に製造することができた。 In the heat sink thus obtained, the thermally conductive material is fused to the carbon nanotubes, and the carbon nanotubes are bonded to each other through the thermally conductive material, thereby forming a three-dimensional network. Further, it was confirmed from observation with a scanning electron microscope (SEM) that amorphous carbon exists in the gap between the carbon nanotubes.
Moreover, the content rate of the carbon nanotube in a heat sink (sintered body) was 90 wt% or more.
Moreover, in the present Example, the heat sink was able to be suitably manufactured without generating shavings or the like during the manufacturing process.

（実施例２）
焼成温度をＣｕの沸点（２５７１℃）以上である２６００℃とした以外は、前記実施例１と同様にして、ヒートシンクを製造した。
また、ヒートシンク（焼結体）中におけるカーボンナノチューブの含有率は、９０ｗｔ％以上であった。 (Example 2)
A heat sink was manufactured in the same manner as in Example 1 except that the firing temperature was 2600 ° C., which is higher than the boiling point of Cu (2571 ° C.).
Moreover, the content rate of the carbon nanotube in a heat sink (sintered body) was 90 wt% or more.

（実施例３）
金属粒子としてＡｇを用い、焼成温度をＡｇの融点（９６１℃）以上である１０００℃とした以外は、前記実施例１と同様にして、ヒートシンクを製造した。
また、ヒートシンク（焼結体）中におけるカーボンナノチューブの含有率は、９０ｗｔ％以上であった。 (Example 3)
A heat sink was manufactured in the same manner as in Example 1 except that Ag was used as the metal particles, and the firing temperature was 1000 ° C. which is not lower than the melting point of Ag (961 ° C.).
Moreover, the content rate of the carbon nanotube in a heat sink (sintered body) was 90 wt% or more.

（実施例４）
焼成温度をＡｇの沸点（２１５５℃）以上である２２００℃とした以外は、前記実施例３と同様にして、ヒートシンクを製造した。
また、ヒートシンク（焼結体）中におけるカーボンナノチューブの含有率は、９０ｗｔ％以上であった。 Example 4
A heat sink was manufactured in the same manner as in Example 3 except that the firing temperature was 2200 ° C. which is higher than the boiling point of Ag (2155 ° C.).
Moreover, the content rate of the carbon nanotube in a heat sink (sintered body) was 90 wt% or more.

（実施例５）
金属粒子としてＡｌを用い、焼成温度をＡｌの融点（６６０℃）以上である８００℃とした以外は、前記実施例１と同様にして、ヒートシンクを製造した。
また、ヒートシンク（焼結体）中におけるカーボンナノチューブの含有率は、９０ｗｔ％以上であった。 (Example 5)
A heat sink was manufactured in the same manner as in Example 1 except that Al was used as the metal particles and the firing temperature was 800 ° C., which is higher than the melting point of Al (660 ° C.).
Moreover, the content rate of the carbon nanotube in a heat sink (sintered body) was 90 wt% or more.

（実施例６）
焼成温度をＡｌの沸点（２４６７℃）以上である２５００℃とした以外は、前記実施例５と同様にして、ヒートシンクを製造した。
また、ヒートシンク（焼結体）中におけるカーボンナノチューブの含有率は、９０ｗｔ％以上であった。 (Example 6)
A heat sink was manufactured in the same manner as in Example 5 except that the firing temperature was 2500 ° C. which is higher than the boiling point of Al (2467 ° C.).
Moreover, the content rate of the carbon nanotube in a heat sink (sintered body) was 90 wt% or more.

（実施例７）
成形工程において、略角柱状の成形体を成形し、焼成工程の後に、研削、研磨加工を施すことにより、図２、図３に示すような形状（全体寸法＝縦２５ｍｍ×横２５ｍｍ、突起寸法＝外径φ１．２５ｍｍ、長さ１ｍｍ、基板厚さ７ｍｍ）とした以外は、前記実施例１と同様にして、ヒートシンクを製造した。
このようにして得られたヒートシンクにおいては、熱伝導性物質がカーボンナノチューブに溶着して、この熱伝導性物質を介してカーボンナノチューブ同士が接合され、３次元的なネットワークが形成さていること、また、カーボンナノチューブ同士の間隙には、非晶質の炭素が存在することが、走査型電子顕微鏡（ＳＥＭ）の観察から確認された。
また、ヒートシンク（焼結体）中におけるカーボンナノチューブの含有率は、８５ｗｔ％であった。 (Example 7)
In the molding step, a substantially prismatic shaped body is formed, and after the firing step, grinding and polishing are performed to obtain a shape as shown in FIGS. 2 and 3 (overall dimensions = vertical 25 mm × width 25 mm, projection dimensions) = Outer diameter φ1.25 mm, length 1 mm, substrate thickness 7 mm) A heat sink was manufactured in the same manner as in Example 1 described above.
In the heat sink thus obtained, the thermally conductive substance is welded to the carbon nanotubes, and the carbon nanotubes are joined to each other through the thermally conductive substance to form a three-dimensional network. It was confirmed from observation with a scanning electron microscope (SEM) that amorphous carbon was present in the gap between the carbon nanotubes.
Moreover, the content rate of the carbon nanotube in a heat sink (sintered body) was 85 wt%.

（比較例１）
熱伝導性物質を含まずに、カーボンナノチューブとフェノール樹脂とのみを混合そして混練して、成形体形成用組成物質を得た以外は、前記実施例１と同様にして、ヒートシンクを製造した。
また、ヒートシンク（焼結体）中におけるカーボンナノチューブの含有率は、９０ｗｔ％以上であった。 (Comparative Example 1)
A heat sink was manufactured in the same manner as in Example 1 except that a carbon nanotube and a phenol resin alone were not mixed and kneaded to obtain a molded body forming composition material without containing a heat conductive material.
Moreover, the content rate of the carbon nanotube in a heat sink (sintered body) was 90 wt% or more.

（比較例２）
Ｍｇ合金（ＡＺ９１Ｄ）を用いて、鋳造により、図２、図３に示すようなヒートシンクを製造した。
なお、得られたヒートシンクは、全体寸法＝縦２５ｍｍ×横２５ｍｍ、突起寸法＝外径φ１．２５ｍｍ、長さ１ｍｍ、基板厚さ７ｍｍであった。 (Comparative Example 2)
A heat sink as shown in FIGS. 2 and 3 was manufactured by casting using an Mg alloy (AZ91D).
The obtained heat sink had overall dimensions = vertical 25 mm × horizontal 25 mm, projection dimensions = outer diameter φ1.25 mm, length 1 mm, and substrate thickness 7 mm.

［ヒートシンク（焼結体）の評価］
前記各実施例および各比較例で製造されたヒートシンクについて、２０℃における熱伝導率を測定した。
ここで熱伝導率の測定は、レーザーフラッシュ法を用いて行った。
これらの結果を表１に示す。 [Evaluation of heat sink (sintered body)]
About the heat sink manufactured by each said Example and each comparative example, the heat conductivity in 20 degreeC was measured.
Here, the thermal conductivity was measured using a laser flash method.
These results are shown in Table 1.

表１から明らかなように、各実施例のヒートシンクは、いずれも、優れた熱伝導性を有していた。
これに対して、各比較例のヒートシンクは、いずれも、熱伝導性に劣るものであった。 As is clear from Table 1, each of the heat sinks of each example had excellent thermal conductivity.
On the other hand, all of the heat sinks of the comparative examples were inferior in thermal conductivity.

本発明の成形体の好適な実施形態について、そのミクロ構造を模式的に示す断面図である。It is sectional drawing which shows typically the microstructure about suitable embodiment of the molded object of this invention. 本発明を適用したヒートシンクを示す平面図である。It is a top view which shows the heat sink to which this invention is applied. 図２中のII−II線断面図である。It is the II-II sectional view taken on the line in FIG. 図３の部分拡大断面図である。FIG. 4 is a partially enlarged sectional view of FIG. 3.

符号の説明Explanation of symbols

１……焼結体 １０……基材 １’……ヒートシンク ２……繊維状炭素系物質 ３……熱伝導性物質 ４……炭素 １１……充填物 ５……基板 ５１……接合面 ６……突起 ７……モールド枠 ８……モールド孔 ９……メッキ層
DESCRIPTION OF SYMBOLS 1 ... Sintered body 10 ... Base material 1 '... Heat sink 2 ... Fibrous carbon type material 3 ... Thermally conductive material 4 ... Carbon 11 ... Filler 5 ... Substrate 51 ... Bonding surface 6 ... Protrusions 7 ... Mold frame 8 ... Mold hole 9 ... Plating layer

Claims (16)

繊維状炭素系物質と、金属を含む熱伝導性物質とを含む組成物を所定の形状に成形して、成形体を得る成形工程と、
前記成形体を焼成して、前記熱伝導性物質を介して前記繊維状炭素系物質同士を互いに接合することにより、焼成体を得る焼成工程とを有することを特徴とする焼結体の製造方法。 Molding a composition containing a fibrous carbon-based material and a thermally conductive material containing a metal into a predetermined shape to obtain a molded body; and
A method for producing a sintered body comprising: firing the molded body and joining the fibrous carbonaceous materials to each other via the thermally conductive material to obtain a fired body. . 前記組成物は、バインダーも含むものである請求項１に記載の焼結体の製造方法。   The method for producing a sintered body according to claim 1, wherein the composition also includes a binder. 前記バインダーは、熱硬化性樹脂を主成分とするものである請求項２に記載の焼結体の製造方法。   The method for producing a sintered body according to claim 2, wherein the binder contains a thermosetting resin as a main component. 前記成形工程での成形は、前記バインダーが溶融もしくは硬化する温度以上の温度で、前記組成物を加熱しつつ行われる請求項３に記載の焼結体の製造方法。   The method for producing a sintered body according to claim 3, wherein the forming in the forming step is performed while heating the composition at a temperature equal to or higher than a temperature at which the binder is melted or cured. 前記熱硬化性樹脂は、フェノール樹脂およびエポキシ樹脂のうち少なくとも一方を主成分とするものである請求項３または４に記載の焼結体の製造方法。   The method for producing a sintered body according to claim 3 or 4, wherein the thermosetting resin contains at least one of a phenol resin and an epoxy resin as a main component. 前記成形工程にて前記バインダーは粒子状をなしている請求項２ないし５のいずれかに記載の焼結体の製造方法。   The method for producing a sintered body according to any one of claims 2 to 5, wherein the binder is in the form of particles in the molding step. 前記成形工程にて前記熱伝導性物質および前記バインダーの双方が粒子状をなしており、前記熱伝導性物質の平均粒径は前記バインダーの平均粒径よりも小さい請求項２ないし５のいずれかに記載の焼結体の製造方法。   6. The heat conductive material and the binder are both in the form of particles in the molding step, and the average particle size of the heat conductive material is smaller than the average particle size of the binder. The manufacturing method of the sintered compact described in 2. 前記成形工程にて前記熱伝導性物質は粒子状をなしている請求項１ないし７のいずれかに記載の焼結体の製造方法。   The method for manufacturing a sintered body according to any one of claims 1 to 7, wherein the thermally conductive substance is in the form of particles in the molding step. 前記繊維状炭素系物質は、カーボンナノチューブおよび気相成長炭素繊維のうちいずれか一方を主成分とするものである請求項１ないし８のいずれかに記載の焼結体の製造方法。   The method for producing a sintered body according to any one of claims 1 to 8, wherein the fibrous carbon-based material contains one of carbon nanotubes and vapor-grown carbon fibers as a main component. 前記焼成工程での焼成温度は前記熱伝導性物質の融点以上である請求項１ないし９のいずれかに記載の焼結体の製造方法。   The method for producing a sintered body according to any one of claims 1 to 9, wherein a firing temperature in the firing step is equal to or higher than a melting point of the thermally conductive material. 前記焼成工程での焼成温度は前記熱伝導性物質の沸点以上である請求項１ないし９のいすれかに記載の焼結体の製造方法。   The method for producing a sintered body according to any one of claims 1 to 9, wherein a firing temperature in the firing step is equal to or higher than a boiling point of the thermally conductive substance. 前記熱伝導性物質は、Ｃｕ、Ａｇ、Ａｌ、またはこれらを含む合金、これらの金属を含む酸化物よりなる群から選択される少なくとも１種を主成分とするものである請求項１ないし１１のいずれかに記載の焼結体の製造方法。   12. The heat conductive material according to claim 1, wherein the heat conductive material is mainly composed of at least one selected from the group consisting of Cu, Ag, Al, alloys containing these, and oxides containing these metals. The manufacturing method of the sintered compact in any one. 前記焼成工程は、不活性ガス雰囲気中または減圧下で行われる請求項１ないし１２のいずれかに記載の焼結体の製造方法。   The method for producing a sintered body according to any one of claims 1 to 12, wherein the firing step is performed in an inert gas atmosphere or under reduced pressure. 前記焼結工程の後に、前記焼結体に樹脂系材料を含浸させる含浸工程を有する請求項１ないし１３のいずれかに記載の焼結体の製造方法。   The method for producing a sintered body according to any one of claims 1 to 13, further comprising an impregnation step of impregnating the sintered body with a resin material after the sintering step. 請求項１ないし１４のいずれかに記載の焼結体の製造方法により製造されたことを特徴とする焼結体。   A sintered body manufactured by the method for manufacturing a sintered body according to any one of claims 1 to 14. 金属を含む熱伝導性物質を介して繊維状炭素系物質同士が接合されてなることを特徴とする焼結体。   A sintered body characterized in that fibrous carbonaceous materials are bonded to each other through a heat conductive material containing a metal.