JP2005146206A

JP2005146206A - Adhesive method and adhesive structure

Info

Publication number: JP2005146206A
Application number: JP2003389244A
Authority: JP
Inventors: Hiroyuki Harada; 裕之原田
Original assignee: Hori Glass Co Ltd
Current assignee: Hori Glass Co Ltd
Priority date: 2003-11-19
Filing date: 2003-11-19
Publication date: 2005-06-09

Abstract

<P>PROBLEM TO BE SOLVED: To provide an adhesion technique which allows an adhesive layer to have a controllable thickness, can protect bodies to be adhered from contacting each other, and provides simple and low-priced adhesion work. <P>SOLUTION: The method is a method for adhering a body 2 to be adhered such as an inner mirror supporting bracket to an automobile glass 1 via an adhesive layer 3, and comprises coating an adhesive agent on the adhering surface of the body 2 to be adhered followed by putting a gauze containing a silane coupling agent to press. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

本発明は、接着剤を介して被着体相互を接着するに際し、プライマーを使用する接着方法および接着構造に関するものである。 The present invention relates to a bonding method and a bonding structure using a primer when bonding adherends to each other via an adhesive.

例えば自動車用ガラスに対し、インナーミラー取付用ブラケット、モール、プロテクター、位置決め用基準ピン、ヒンジ等の各部材を取り付ける場合、通常、エポキシ系、ウレタン系、シリコーン系、変性シリコーン系等の自動車ガラス用接着剤が使用されている（例えば特許文献１参照）。 For example, when mounting each member such as inner mirror mounting bracket, molding, protector, positioning reference pin, hinge, etc. to automotive glass, it is usually used for automotive glass such as epoxy, urethane, silicone and modified silicone. An adhesive is used (for example, see Patent Document 1).

この場合、上記接着剤と被着体であるガラス、金属及びエンジニアリングプラスティックとの界面の接着力を強化するためにプライマーと呼ばれる樹脂やシランカップリング剤を塗布させる手法が古くから用いられている。 In this case, a technique of applying a resin called a primer or a silane coupling agent has been used for a long time in order to enhance the adhesive force at the interface between the adhesive and the glass, metal, and engineering plastic as the adherend.

しかしながら、このようなプライマーを塗布することは、非常に手間がかかり、作業性やコストアップなどの問題点があった。 However, applying such a primer is very time-consuming and has problems such as workability and cost increase.

一方、この問題点を解決するべく、シランカップリング剤を含有する接着剤が開発・製造されているが、シランカップリング剤を含有することにより、接着剤が不安定になり、結果的に製品寿命が極端に短くなるなどという新たな問題が発生することが判明した。
特開平１１−９２７３５号公報 On the other hand, in order to solve this problem, an adhesive containing a silane coupling agent has been developed and manufactured. However, the inclusion of the silane coupling agent makes the adhesive unstable, resulting in a product. It has been found that a new problem such as extremely short lifespan occurs.
JP-A-11-92735

そこで本発明は、簡単な作業で安価にプライマーを用いることができ、しかも接着剤が不安定になるといった問題をもたらさない接着技術を提供することにある。 Therefore, the present invention provides an adhesion technique that can use a primer with a simple operation at low cost and does not cause a problem that the adhesive becomes unstable.

上記課題を解決した本発明の接着方法は、接着剤を介して被着体相互を接着する方法において、
プライマー液を保持しかつ保持したプライマー液を放出する機能を有するプライマー液供給材を、被着体の接着面間に挟んだ状態で前記接着を行うことを特徴とするものである。 The bonding method of the present invention that has solved the above problems is a method of bonding adherends to each other via an adhesive.
The adhesion is performed in a state where a primer liquid supply material having a function of holding the primer liquid and releasing the held primer liquid is sandwiched between the adhesion surfaces of the adherend.

本発明に従って、プライマー液供給材を接着面間に挟むと、この供給材からプライマー液が接着面に供給され、シランカップリング剤を塗布したのと同じ効果が発揮される。この場合、プライマー液供給材を配置するだけで済むため、塗布作業と比べて容易にしかも安価にプライマーによる効果を得ることができる。また、予め接着剤中にシランカップリング剤を含有させるような場合と異なり、接着剤が不安定になる等の問題が実質的に発生しないという利点ももたらされる。 In accordance with the present invention, when the primer solution supply material is sandwiched between the adhesive surfaces, the primer solution is supplied from the supply material to the adhesion surface, and the same effect as when the silane coupling agent is applied is exhibited. In this case, since only the primer solution supply material needs to be arranged, the effect of the primer can be obtained easily and at a lower cost than the application work. In addition, unlike the case where a silane coupling agent is previously contained in the adhesive, there is an advantage that problems such as unstable adhesive do not substantially occur.

本発明のプライマー液供給材としては、作業性・低コスト・接着力の確保の観点からガーゼを用いるのが好ましい。特に、一方の被着体がガラスであり、他方の被着体が硬質部材であると、従来の接着方法では、硬質部材とガラスとの直接接触によりガラスに傷を付けてしまうおそれがあるが、本発明においてプライマー供給材としてガーゼを用いると、これが柔軟なスペーサーとなり、傷防止としても機能するため好適である。 As the primer solution supply material of the present invention, it is preferable to use gauze from the viewpoint of ensuring workability, low cost, and adhesive strength. In particular, if one adherend is glass and the other adherend is a hard member, the conventional bonding method may damage the glass due to direct contact between the hard member and the glass. In the present invention, it is preferable to use gauze as a primer supply material because it becomes a flexible spacer and functions as a scratch prevention.

また、本発明を自動車用ガラスに対する各種部材の取付けに適用する場合、プライマー液としては、下記一般式で表されるシランカップリング剤を用いるのが好ましい。
Ｙ〜（ＣＨ₂）_nＳｉＸ₃ ・・・（１）
ここに、式中のＸはアルコキシ基やアセトキシ基、イソプロポキシ基、アミノ基、ハロゲン等の加水分解性の置換基で、無機と反応し、Ｙは有機質と反応しやすいビニル基、エポキシ基、アミノ基、メタクリル基、メルカプト基などである。 Moreover, when applying this invention to attachment of the various members with respect to the glass for motor vehicles, it is preferable to use the silane coupling agent represented by the following general formula as a primer liquid.
Y to (CH ₂ ) _n SiX ₃ (1)
Here, X in the formula is a hydrolyzable substituent such as an alkoxy group, an acetoxy group, an isopropoxy group, an amino group, or a halogen, and reacts with inorganic, Y is a vinyl group, epoxy group, An amino group, a methacryl group, a mercapto group, and the like.

さらに、この場合における具体的な接着手順としては、前記取付部材に接着剤を塗布し、その接着剤の表面に前記プライマー液供給材を載せた後、この取付部材を他方の被着体に圧着するという手順が推奨される。 Furthermore, as a specific bonding procedure in this case, an adhesive is applied to the mounting member, the primer liquid supply material is placed on the surface of the adhesive, and then the mounting member is crimped to the other adherend. The recommended procedure is to

他方、本発明においては、上記プライマー液供給材を用いた接着構造も提案される。 On the other hand, in the present invention, an adhesion structure using the primer solution supply material is also proposed.

以上のとおり、本発明によれば、簡単な作業で安価にプライマーを用いることができ、しかも接着剤が不安定になるといった問題をもたらさない等の利点がもたらされる。 As described above, according to the present invention, it is possible to use a primer with a simple operation at low cost, and further, there are advantages such as not causing a problem that the adhesive becomes unstable.

以下、本発明の実施形態について詳説する。
図１および図２は、本発明に係る接着構造の適用例を示している。符号１は自動車用ガラスを示し、符号２はインナーミラー取付用ブラケット等の金属製被着体を示しており、両被着体１，２は接着剤層３により接着されている。そして、本発明に従って接着面間にプライマー液供給材４が挟まれており、このプライマー液供給材４に保持されたプライマー液が接着面に供給された状態で接着がなされている。また、プライマー液供給材４の介在によって接着剤層３の厚みの下限がプライマー液供給材４の厚さに規制され、かつ両被着体１，２は非接触とされている。 Hereinafter, embodiments of the present invention will be described in detail.
1 and 2 show application examples of the adhesive structure according to the present invention. Reference numeral 1 denotes an automotive glass, reference numeral 2 denotes a metal adherend such as an inner mirror mounting bracket, and the adherends 1 and 2 are bonded together by an adhesive layer 3. And according to this invention, the primer liquid supply material 4 is pinched | interposed between the adhesion surfaces, and adhesion | attachment is made in the state by which the primer liquid hold | maintained at this primer liquid supply material 4 was supplied to the adhesion surface. Further, the lower limit of the thickness of the adhesive layer 3 is regulated by the thickness of the primer liquid supply material 4 by the interposition of the primer liquid supply material 4, and both the adherends 1 and 2 are not in contact with each other.

本発明のプライマー液供給材４としては、プライマー液を保持し且つ保持したプライマー液を接着面に供給しうるものであれば材質・形状等は特に限定されないが、例えば、織布（ガーゼ含む）、不織布、スポンジ（ゴム・合成樹脂製のものを含む）等を、接着面の形状等に応じて、粒子状、糸状、ひも状、シート状に形成してなるものを用いることができる。 The primer solution supply material 4 of the present invention is not particularly limited as long as it can hold the primer solution and supply the held primer solution to the adhesive surface. For example, woven cloth (including gauze) , Non-woven fabrics, sponges (including those made of rubber / synthetic resin), etc. can be used which are formed in the form of particles, threads, strings, or sheets according to the shape of the adhesive surface.

汎用性の観点からは、プライマー液供給材はシート状とするのが好ましく、この場合、接着面相互を繋ぐ接着剤の連続性を担保し、接着面積を極端に減少させないために、所望する接着力の確保に十分な通液性を有する有孔シートとすることができ、この場合、シートの厚さ、透過孔の孔径や数、材質を問わず使用することができる。具体的には、一般的な繊維を織り上げたガーゼや、合成繊維糸を編成した網状体の他、紙、合成樹脂、ゴムなどからなるシートに多数の穴を開口したものを用いることができる。かかる有孔シートは接着面間に介在させたとしても、接着剤が孔を通って両接着面を直接的に繋ぐことができる。なお、粒子状等の場合には、それらの間において両接着面が接着剤層により直接的に接着される。 From the viewpoint of versatility, the primer solution supply material is preferably in the form of a sheet. In this case, in order to secure the continuity of the adhesive connecting the bonding surfaces and not extremely reduce the bonding area, the desired bonding is performed. A perforated sheet having sufficient liquid permeability for securing force can be obtained. In this case, the sheet can be used regardless of the thickness of the sheet, the diameter and number of the permeation holes, and the material. Specifically, it is possible to use a sheet made of paper, synthetic resin, rubber, or the like in which a large number of holes are opened, in addition to a gauze woven from general fibers or a net-like body knitted with synthetic fiber yarns. Even if such a perforated sheet is interposed between the adhesive surfaces, the adhesive can directly connect the two adhesive surfaces through the holes. In the case of particles or the like, both adhesive surfaces are directly bonded by an adhesive layer between them.

プライマー液供給材４の厚さや外径は接着剤層３の厚みの下限を定めるものであり、任意に選択できるが、０．１ｍｍ以上とするのが好ましい。プライマー液供給材４の面積や長さは接着面の形状、面積により適宜定めることができるが、被着体の面積より大きくなると、被着体の脇からはみ出して外観見栄えが悪くなり、小さすぎるとプライマー液の吸収率の低下により接着力が悪化したり、接着面全体にプライマー液を供給できない。よって、プライマー液供給材４の面積若しくは長さは、被着体１，２の接着面に対し、５０〜９０％とするのが好ましい。 The thickness and outer diameter of the primer liquid supply material 4 determine the lower limit of the thickness of the adhesive layer 3 and can be arbitrarily selected, but are preferably 0.1 mm or more. The area and length of the primer liquid supply material 4 can be determined as appropriate depending on the shape and area of the bonding surface. However, when the area is larger than the area of the adherend, the appearance of the primer sticks out from the side of the adherend and the appearance looks worse and is too small. As a result, the adhesive strength deteriorates due to a decrease in the absorption rate of the primer solution, or the primer solution cannot be supplied to the entire bonding surface. Therefore, the area or length of the primer liquid supply material 4 is preferably 50 to 90% with respect to the adhesion surfaces of the adherends 1 and 2.

以上より、プライマー液の保持・供給機能、接着力を阻害しない程度の目の粗さ、コスト及び作業性の良さの点を考慮すると、本発明のプライマー液供給材４の具体例としては、医療用で使われているガーゼが最適である。 From the above, in consideration of the maintenance and supply function of the primer solution, the degree of eye roughness that does not hinder the adhesive force, cost, and good workability, as a specific example of the primer solution supply material 4 of the present invention, The gauze used for the best is the best.

接着の手順としては、図１に示すように、一方の被着体２に接着剤３を塗布し、その上にプライマー液を染み込ませた供給材４を載せ、しかる後に図２に示すように、他方の被着体１と圧着させる方法が作業性の点では好ましい。また図示しないが、各被着体１，２の接着面に供給材４をそれぞれ個別に配置し、これらの供給材４側を接着剤を介して接着することもできる。いずれにせよ、プライマー液供給材４が接着面間に配置され、プライマー液が少なくとも一方の被着体と接着剤との間に供給される限り、接着手順は適宜定めることができる。 As shown in FIG. 1, as shown in FIG. 1, an adhesive 3 is applied to one adherend 2, and a supply material 4 soaked with a primer solution is placed thereon, and then, as shown in FIG. The method of pressure bonding with the other adherend 1 is preferable in terms of workability. Although not shown, it is also possible to individually arrange the supply materials 4 on the bonding surfaces of the adherends 1 and 2 and bond these supply material 4 sides via an adhesive. In any case, as long as the primer liquid supply material 4 is disposed between the bonding surfaces and the primer liquid is supplied between at least one adherend and the adhesive, the bonding procedure can be appropriately determined.

本発明の接着剤３としては、被着体１，２の種類・用途に応じて適宜選択すれば良く、特に限定されるものではない。接着剤３は、１液であっても２液以上であっても良い。自動車用ガラス１に対して各種部材の取り付けを行う場合を想定すると、接着剤３の具体例としては、シリコーン系接着剤、変性シリコーン系接着剤、ポリサルファイド系接着剤、ポリウレタン系接着剤、エポキシ系接着剤、弾性エポキシ系接着剤、第二世代アクリル（ＳＧＡ）、シアノアクリレート等を挙げることができる。 The adhesive 3 of the present invention may be appropriately selected according to the type and application of the adherends 1 and 2, and is not particularly limited. The adhesive 3 may be one liquid or two liquids or more. Assuming the case where various members are attached to the glass 1 for automobiles, specific examples of the adhesive 3 include a silicone-based adhesive, a modified silicone-based adhesive, a polysulfide-based adhesive, a polyurethane-based adhesive, and an epoxy-based adhesive. Adhesives, elastic epoxy adhesives, second generation acrylic (SGA), cyanoacrylates and the like can be mentioned.

接着剤３の塗布方式は特に限定されず、使用する接着剤３に最適の方式で行なうことが出来る。接着剤３の塗布量は、被着体１，２の質量や形状等に応じて適宜定めることができる。自動車用ガラス１に各種部材２の取り付けを行う場合を想定すると、接着剤塗布量は０．０２〜０．１ｇ／ｃｍ²とするのが好ましい。 The application method of the adhesive 3 is not particularly limited, and can be performed by a method optimal for the adhesive 3 to be used. The application amount of the adhesive 3 can be appropriately determined according to the mass and shape of the adherends 1 and 2. Assuming the case where various members 2 are attached to the glass 1 for automobiles, the amount of adhesive applied is preferably 0.02 to 0.1 g / cm ² .

本発明のプライマー液としては、被着体１，２の種類や接着剤の種類、接着物の用途等に応じて適宜定めることができる。自動車用ガラス１に対して各種部材の取り付けを行う場合を想定すると、プライマー液としては、ポリイソシアネート組成物や下記一般式で示されるシランカップリング剤（相互になじみの悪いガラス、シリカ、金属、粘土等の無機材料と高分子等の有機材料とを化学結合できる官能基を有する有機ケイ素化合物をいう）などを用いることができる。
Ｙ〜（ＣＨ₂）_nＳｉＸ₃ ・・・（１）
（式中のＸはアルコキシ基やアセトキシ基、イソプロポキシ基、アミノ基、ハロゲン等の加水分解性の置換基で、無機と反応し、Ｙは有機質と反応しやすいビニル基、エポキシ基、アミノ基、メタクリル基、メルカプト基などである。） The primer solution of the present invention can be appropriately determined according to the types of adherends 1 and 2, the type of adhesive, the use of the adhesive, and the like. Assuming that various members are attached to the automotive glass 1, the primer liquid may be a polyisocyanate composition or a silane coupling agent represented by the following general formula (glass, silica, metal, An organic silicon compound having a functional group capable of chemically bonding an inorganic material such as clay and an organic material such as a polymer) can be used.
Y to (CH ₂ ) _n SiX ₃ (1)
(X in the formula is a hydrolyzable substituent such as an alkoxy group, acetoxy group, isopropoxy group, amino group, halogen, etc., and reacts with inorganic, Y is a vinyl group, epoxy group, amino group that easily reacts with organic matter. Methacrylic group, mercapto group, etc.)

シランカップリング剤は各種のものが市販されており、具体例としては、ビニルトリクロルシラン、ビニルトリス（βメトキシエトキシ）シラン、ビニルトリエトキシシラン、ビニルトリメトキシシランなどのビニルシラン、γ―メタクリロキシプロピルトリメトキシシランなどのアクリルシラン、β―（３，４エポキシシクロヘキシル）エチルトリメトキシシラン、γ―グリシドキシプロピルトリメトキシシラン、γ―グリシドキシプロピルメチルジエトキシシランなどのエポキシシラン、N−β―（アミノメチル）γ―アミノプロピルトリメトキシシラン、Ｎ−β―（アミノエチル）γ―アミノプロピルメチルジメトキシシラン、γ―アミノプロピルトリエトキシシラン、Ｎ−フェニル―γ―アミノプルピルトリエトキシシランなどのアミノシラン、γ―メルカプトプロピルトリメトキシシラン、γ―クロロプロピルトリメトキシシラン等が挙げられるが、これらに限定されるものではない。 Various silane coupling agents are commercially available. Specific examples include vinyl silanes such as vinyltrichlorosilane, vinyltris (βmethoxyethoxy) silane, vinyltriethoxysilane, vinyltrimethoxysilane, and γ-methacryloxypropyltri Acrylic silanes such as methoxysilane, epoxy silanes such as β- (3,4 epoxy cyclohexyl) ethyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldiethoxysilane, N-β- (Aminomethyl) γ-aminopropyltrimethoxysilane, N-β- (aminoethyl) γ-aminopropylmethyldimethoxysilane, γ-aminopropyltriethoxysilane, N-phenyl-γ-aminopropyltriethoxysilane, etc. Aminosila , .Gamma.-mercaptopropyltrimethoxysilane, .gamma.-chloro-but trimethoxysilane and the like, but is not limited thereto.

プライマー液供給材４にプライマー液を保持させる方法としては、供給材４に霧吹きなどでプライマー液を噴霧する方法、供給材４をプライマー液に浸漬し、スクイズ（圧搾）する方法等を用いることができるが、これに限定されるものではない。プライマー液供給材４におけるプライマー液の保持量は、少なすぎると効果が期待できず、多すぎるとかえって硬化を阻害するため、実験等を通じて適宜設定するのが望ましい。具体的に、ガーゼにシランカップリング剤を保持させる場合には繊維重量に対し５〜３０重量部のシランカップリング剤を保持させるのが好ましい。 As a method for holding the primer solution on the primer solution supply material 4, a method of spraying the primer solution on the supply material 4 by spraying, a method of immersing the supply material 4 in the primer solution and squeezing (squeezing), or the like is used. Yes, but not limited to this. If the amount of the primer solution retained in the primer solution supply material 4 is too small, the effect cannot be expected. If the amount is too large, curing is rather inhibited. Specifically, when the gauze holds the silane coupling agent, it is preferable to hold 5 to 30 parts by weight of the silane coupling agent relative to the fiber weight.

本発明の被着体１，２は、接着に先立って、埃や油分を除去する為に脱脂をしても良い。脱脂は通常、有機溶剤で行うことができ、メタノール、エタノール、イソプロピルアルコール等の低級アルコールや、アセトンやメチルエチルケトン等のケトン類を用いることができるが、これらに限定されるものではない。 Prior to bonding, the adherends 1 and 2 of the present invention may be degreased to remove dust and oil. Degreasing can usually be performed with an organic solvent, and lower alcohols such as methanol, ethanol and isopropyl alcohol, and ketones such as acetone and methyl ethyl ketone can be used, but are not limited thereto.

本発明の被着体は、図示形態のように一方の被着体１が自動車用ガラスであり、他方の被着体２がインナーミラー取付用ブラケット等の取付部材である場合に好適である。取付部材の材質としては、鋼鉄、ステンレス、アルミニウムなどの金属やＰＢＴ、ＰＥＴ、ＰＯＭ、ポリアミド樹脂などのエンジニアリングプラスティック等、特に限定なく適用できる。また、取付部材としては、インナーミラー取り付け樹脂製ブラケット、キャッチハンドル締結用ブラケット、モール、プロテクター、位置決め基準ピン等があるが、特に限定なく適用できる。また、自動車用ガラス１としては、自動車用の強化ガラス、黒色セラミックプリントガラス、中間層にポリビニルブチラールを使用した合せガラス等があるが、特に限定なく適用できる。 The adherend of the present invention is suitable when one adherend 1 is an automotive glass and the other adherend 2 is an attachment member such as an inner mirror attachment bracket as shown in the figure. The material of the mounting member can be applied without particular limitation, such as metals such as steel, stainless steel, and aluminum, and engineering plastics such as PBT, PET, POM, and polyamide resin. Further, examples of the mounting member include an inner mirror mounting resin bracket, a catch handle fastening bracket, a molding, a protector, a positioning reference pin, and the like. Examples of the glass 1 for automobiles include tempered glass for automobiles, black ceramic printed glass, and laminated glass using polyvinyl butyral as an intermediate layer.

（ピン型被着体の作製）
図３に示すように、接着面が約１７０ｍｍ²の供試被着体Ａを６−ナイロン（三菱エンジニアリングプラスチックス(株)製、ガラス繊維３０％入り、グレード名１０１３Ｇ（Ｈ）３０−１））を用い、公知の射出成型法で作製した。 (Production of pin type adherend)
As shown in FIG. 3, the test adherend A having an adhesive surface of about 170 mm ² is made of 6-nylon (Mitsubishi Engineering Plastics Co., Ltd., 30% glass fiber, grade name 1013G (H) 30-1). ) And a known injection molding method.

（接着剤の準備）
構造用アクリル接着剤（商品名：MA３２０、ＩＴＷインダストリー社製）を、先端にスタチックミキサーノズル（商品名ＭＣ０８−２４、ＭＩＸＰＡＣ社製）を装着した2液混合塗布カートリッジ（第1液：活性剤第２液＝１０：１、ＭＩＸＰＡＣ社製）に充填した。 (Preparation of adhesive)
Two-component mixed coating cartridge (first liquid: active) with a structural acrylic adhesive (trade name: MA320, manufactured by ITW Industry) and a static mixer nozzle (trade name: MC08-24, manufactured by MIX PAC) at the tip Agent second liquid = 10: 1, manufactured by MIX PAC).

（実施例１）
２５℃、６０％相対湿度の雰囲気下で、供試被着体Ａの接着面ｆに上記接着剤を０．１ｇ吐出し、この接着剤の上に、予め１５０mm²の円形に切断した厚さ約０．２ｍｍの医療用ガーゼ（日本薬局方）に、ガーゼ重量に対して２０重量％のγ―グリシドキシプロピルトリメトキシシラン（信越化学工業(株)製）を全体に均一になるように含ませたものを載せた後、このガーゼ側面を自動車用黒セラミック付き合わせガラスに接着し、常温で２４時間経時させた後、引張強度を測定し、剥離状態を観察した。また作業者により作業性について評価した。 (Example 1)
In an atmosphere of 25 ° C. and 60% relative humidity, 0.1 g of the adhesive was discharged onto the adhesive surface f of the test adherend A, and the thickness was previously cut into a circle of 150 mm ² on the adhesive. About 20mm of γ-glycidoxypropyltrimethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd.) with a weight of about 0.2mm for medical gauze (Japanese Pharmacopoeia) After putting the inclusion, this gauze side surface was adhered to a laminated glass with black ceramic for automobiles, and after 24 hours at room temperature, the tensile strength was measured and the peeled state was observed. The workability was evaluated by the workers.

（比較例１）
ガーゼにシランカップリング剤を含有させずに用いたこと以外は、実施例１と同様にして試験を行った。 (Comparative Example 1)
The test was performed in the same manner as in Example 1 except that the gauze was used without containing a silane coupling agent.

（比較例２）
ガーゼに代えて、平均粒経０．２ｍｍのガラスビーズを上下に重ならないように接着面に多数載せた以外は、比較例１と同様にして試験を行った。 (Comparative Example 2)
A test was conducted in the same manner as in Comparative Example 1 except that a large number of glass beads having an average particle size of 0.2 mm were placed on the adhesive surface so as not to overlap each other in place of gauze.

（比較例３）
供試被着体の接着面に、接着剤の塗布に先立って、γ―グリシドキシプロピルトリメトキシシラン（信越化学工業(株)製）を刷毛で塗布した以外は、比較例２と同様にして試験を行った。 (Comparative Example 3)
Similar to Comparative Example 2, except that γ-glycidoxypropyltrimethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd.) was applied to the adhesive surface of the test adherend with a brush prior to application of the adhesive. The test was conducted.

（試験結果）
試験結果を表１に示した。表１からも明らかなように、被着体の接着面に、接着剤塗布後、シランカップリング剤を含んだ繊維状シートを載せ、圧着させることで、シランカップリング剤を塗布した場合と同じレベルの引張強度が発揮され、かつ作業性も良好であった。 (Test results)
The test results are shown in Table 1. As is clear from Table 1, after applying the adhesive on the adherend surface of the adherend, a fibrous sheet containing the silane coupling agent is placed and pressure bonded, which is the same as when the silane coupling agent is applied. The tensile strength of the level was exhibited, and the workability was also good.

本発明は、自動車用ガラスに対し、インナーミラー取付用ブラケット、モール、プロテクター、位置決め用基準ピン、ヒンジ等の各部材を取り付ける場合のみならず、他の一般的または特殊な接着用途にも適用できるものである。 The present invention can be applied not only to the case of attaching each member such as an inner mirror mounting bracket, a molding, a protector, a positioning reference pin, and a hinge to an automotive glass, but also to other general or special bonding applications. Is.

本発明に係る接着方法を示した説明図である。It is explanatory drawing which showed the adhesion | attachment method based on this invention. 本発明に係る接着構造を示した断面図である。It is sectional drawing which showed the adhesion structure which concerns on this invention. 実験１における供試被着体Ａの正面及び底面を示した図である。FIG. 3 is a diagram showing a front surface and a bottom surface of a test adherend A in Experiment 1.

符号の説明Explanation of symbols

１…自動車用ガラス、２…インナーミラー取付用ブラケット、３…接着剤（及び接着剤層）、４…プライマー液供給材。 DESCRIPTION OF SYMBOLS 1 ... Automotive glass, 2 ... Bracket for inner mirror attachment, 3 ... Adhesive (and adhesive layer), 4 ... Primer liquid supply material.

Claims

接着剤を介して被着体相互を接着する方法において、
プライマー液を保持しかつ保持したプライマー液を放出する機能を有するプライマー液供給材を、被着体の接着面間に挟んだ状態で前記接着を行うことを特徴とする接着方法。 In a method of bonding adherends to each other via an adhesive,
A bonding method characterized in that the bonding is performed in a state where a primer liquid supply material having a function of holding the primer liquid and releasing the held primer liquid is sandwiched between the bonding surfaces of the adherend.

前記プライマー液供給材としてガーゼを用いた請求項１記載の接着方法。 The bonding method according to claim 1, wherein gauze is used as the primer solution supply material.

一方の前記被着体が自動車用ガラスであり、他方の前記被着体が自動車用ガラスに取付けられる取付部材であり、前記プライマーが下記一般式で表されるシランカップリング剤である、請求項１または２記載の接着方法。
Ｙ〜（ＣＨ₂）_nＳｉＸ₃ ・・・（１）
ここに、式中のＸはアルコキシ基やアセトキシ基、イソプロポキシ基、アミノ基、ハロゲン等の加水分解性の置換基で、無機と反応し、Ｙは有機質と反応しやすいビニル基、エポキシ基、アミノ基、メタクリル基、メルカプト基などである。 The one adherend is an automotive glass, the other adherend is an attachment member attached to the automotive glass, and the primer is a silane coupling agent represented by the following general formula. 3. The bonding method according to 1 or 2.
Y to (CH ₂ ) _n SiX ₃ (1)
Here, X in the formula is a hydrolyzable substituent such as an alkoxy group, an acetoxy group, an isopropoxy group, an amino group, or a halogen, and reacts with inorganic, Y is a vinyl group, epoxy group, An amino group, a methacryl group, a mercapto group, and the like.

前記取付部材に接着剤を塗布し、その接着剤の表面に前記プライマー液供給材を載せた後、この取付部材を他方の被着体に圧着する、請求項３記載の接着方法。 The bonding method according to claim 3, wherein an adhesive is applied to the mounting member, and the primer liquid supply material is placed on the surface of the adhesive, and then the mounting member is pressure-bonded to the other adherend.

接着剤を介して被着体相互を接着してなる接着構造において、
プライマー液を保持しかつ保持したプライマー液を放出する機能を有するプライマー液供給材を、被着体の接着面間に挟んだ状態で前記接着を行って形成されたことを特徴とする接着構造。 In an adhesive structure formed by adhering adherends to each other via an adhesive,
An adhesive structure formed by performing the adhesion in a state where a primer liquid supply material having a function of holding and releasing the retained primer liquid is sandwiched between adhesion surfaces of adherends.