JP2004107408A - Anti-fogging composition for agricultural film - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an antifogging composition which can impart an antifogging property to base films over a long period, has large adhesive strength to the base films, and large folding resistance, and hardly causes the dropping of inorganic substances contained in coating films, and to provide an agricultural antifogging film coated with the antifogging composition. <P>SOLUTION: This antifogging composition for agricultural films, comprising an olefinic resin emulsion solution to be coated on the surfaces of the agricultural films, is characterized by adding an inorganic additive, a silicon-based surfactant and a silane-based coupling agent. The antifogging composition for the agricultural films is characterized in that the inorganic additive is synthetic hectorite, and is added in an amount of 100 to 2,000 pts. wt. per 100 pts. wt. of the olefin resin component of the olefinic resin emulsion. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は、合成樹脂からなる基材フィルムに塗布してフィルム表面に防曇性塗膜を形成することにより防曇性を付与する防曇組成物、さらに当該防曇組成物をフィルムの少なくとも片面に塗布して得た防曇性農業用フィルムに関する。
【０００２】
【従来の技術】
【特許文献１】特開平８−５３５５８号公報
【特許文献２】特開平９−１００４６７号公報
【０００３】
近年、農作物の短期育成または季節外の育成を目的として、農業用合成樹脂フィルムなどの農業用フィルムの被膜下で野菜等を栽培する、いわゆるハウス栽培や、トンネル栽培が広く行われるようになってきている。これらに使用される合成樹脂フィルムとしては、光線透過性、保湿性、防曇性に優れた軟質塩化ビニルフィルムが使用されていたが、近年では、塩化ビニル樹脂／アクリル樹脂、あるいは、ポリエチレン／エチレン−酢酸ビニル共重合体／ポリエチレンまたはエチレン−酢酸ビニル共重合体のような二層、あるいは三層に積層した多層フィルムも使用されるようになってきている。
【０００４】
しかしながら、合成樹脂フィルムはもともと樹脂が所有する疎水性のため、成型加工中あるいは成形品が静電気を帯びやすく、また被覆した地表面や農作物から蒸発した水蒸気の一部がフィルム表面で凝縮して水滴が生じ、透明性が損なわれる傾向が強い。このような現象は、日光の透過率をさげ、その結果作物の生育を悪くし、またフィルム表面に生じた水滴が落下することにより、作物の若芽を痛め、種々の病害の原因となる等の問題点があった。
【０００５】
この問題を解決するため、フィルム原料に防曇剤を練り込んだり、あるいはフィルム表面に防曇剤を塗布するなどしたりしてフィルム表面の曇りの発生を防止することが行われている。しかしながら、フィルム樹脂原料に防曇剤を練り込んだ場合には、練り込んだ防曇剤がフィルム表面に噴出し、水滴により流出するため、長期に渡ってフィルムに防曇性を付与することはできない。
【０００６】
また、フィルムの表面に防曇剤を塗布する場合、従来は、コロイダルシリカ、コロイダルアルミナ等の無機物を、アクリル系やウレタン系の水性塗料に添加し、フィルム表面に親水性の塗膜を形成させるものであった。しかしながら、アク
リル系の塗料を用いた場合「
【特許文献１】、
【特許文献２】」には、フィルム表面に形成した塗膜が硬いものとなり、その結果折り曲げに弱く、またフィルムを折り曲げた際に塗膜中に含有された無機物が脱落し易いという欠点があり、長期展張に問題があった。
【０００７】
【発明が解決しようとする課題】
したがって本発明は、上記現状に鑑み、フィルム表面に防曇性の塗膜を設けるにあたって、基材フィルムに長期にわたって防曇性を付与し、また、基材フィルとの接着強度も強く、折り曲げに強く、塗膜に含有される無機物が脱落しにくい農業用防曇性フィルムを形成し得る防曇組成物、ならびに当該防曇組成物を塗布した農業用防曇性フィルムを提供することを課題とする
【０００８】
【課題を解決するための手段】
かかる課題を解決するための本発明は、オレフィン系樹脂エマルジョン溶液からなり、無機添加物、シリコン系界面活性剤およびシラン系カップリング剤が添加されていることを特徴とする、農業用フィルムの表面に塗布される農業用フィルム用防曇組成物である。
【０００９】
すなわち本発明は、防曇性の配合組成として、無機物／シリコン系界面活性剤／シラン系カップリング剤の特定の組合せからなる防曇性材料等を使用し、これらの防曇性材料を基材フィルムに塗布し、防曇性塗膜を形成するにあたって、親水性の塗料としてオレフィン系樹脂エマルジョンを使用した点に特徴を有するものである。
【００１０】
かくする基本的構成を有する本発明の防曇組成物を基材フィルムの表面に塗布して得た農業用防曇性フィルムは、基材フィルムに対する塗膜の塗工性が良好なものであり、基材フィルムと防曇性塗膜との密着性が強く、防滴性ならびに防滴持続性がよく、折り曲げに対する塗膜強度が改善されたものである。
【００１１】
【発明の実施の形態】
本発明は、上記したように基材フィルムの表面の少なくとも一方の面に塗布して防曇性塗膜を形成する防曇性組成物として、オレフィン系樹脂エマルジョンを主成分とする点に特徴がある。すなわちオレフィン系樹脂エマルジョンを使用することにより、親水性の無機添加物を均一に組成物中に分散させ、フィルム表面に強固に付着させることが可能となる。また、オレフィン系樹脂エマルジョンによってフィルム表面に形成される樹脂層は、アクリル系樹脂等と比較して柔軟性を有する一方、ウレタン系樹脂と比較して耐光性にも優れているため、無機添加物の欠落を長期間防止できる。このため、オレフィン系樹脂エマルジョンとしては、特に柔軟性を有するエチレン系樹脂エマルジョンが好ましい。
【００１２】
本発明が提供する防曇性組成物を構成するオレフィン系樹脂エマルジョンの樹脂成分としては、０．１％〜４．０％程度が好ましい。樹脂成分が０．１％未満であると所望の塗膜を形成することができず、無機添加物の欠落が発生してしまう可能性がある。また、樹脂成分が４．０％を超えてしまうと、樹脂層自体が厚くなる傾向となり、形成される樹脂層中に無機添加物が埋没してしまう可能性が高くなり、無機添加物の添加量に伴った防曇性能を発揮できなくなる。
【００１３】
この樹脂成分の調整は、無機添加物等を添加する段階で調整しておいても良いし、樹脂成分が１０〜４０％のエマルジョンに無機添加物を添加した後、水やアルコール等の親水性有機溶媒を使用して希釈して調製しても良い。
【００１４】
本発明が提供する防曇組成物において使用される無機添加物としては、防曇性を付与し得る親水性を有する無機添加物であれば、特に制限されない。また、無機添加物の粒径としては１０〜１００ｎｍ程度のものが好ましい。粒径が１０ｎｍ未満であると、形成される樹脂層に埋没する可能性が高くなり、十分な性能を発揮できなくなる可能性がある。また、粒径が１００ｎｍを超えると、欠落して防曇性の劣化が起こり、さらに無機物を保持するための樹脂層を厚くすると、樹脂層の柔軟性、透明性を損ねるおそれがある。
【００１５】
そのため、本発明においては、無機添加物として合成層状ケイ酸塩である合成ヘクトライトを使用することが好ましい。この合成ヘクトライトは、エマルジョン等への分散性が良く、形成される樹脂層に均一に分散された状態となる。
【００１６】
本発明において、無機添加物、特に合成ヘクトライトの配合量は、オレフィン系樹脂エマルジョンのオレフィン系樹脂１００重量部に対して、１００〜２０００重量部が好ましい。１００重量部未満では、防曇性が十分ではなく、２０００重量部を超えて配合しても防曇性自体は殆ど変化なく、形成される樹脂層の透明性を低下してしまい、農業用フィルム自体の透明性の低下となってしまい好ましくない。
【００１７】
本発明が提供する防曇組成物に添加されるシリコン系界面活性剤は、防曇組成物に添加される無機添加物の分散性を向上させ、基材フィルムに塗布する際のぬれ性を向上させ、基材フィルムへの防曇性樹脂層の密着力を高め、さらに、防曇性樹脂層の防曇性も向上させることができるものである。シリコン系界面活性剤のオレフィン系樹脂エマルジョンへの配合量は、オレフィン系樹脂成分１００重量部に対して、１〜１００重量部程度が好ましい。１重量部未満であると、上記のような効果が得られず、また、１００重量部を超えてしまうと、防曇性樹脂層の強度を低下させてしまい、防曇性能の持続性を低下させることとなる。
【００１８】
また、本発明が提供する防曇組成物に添加されるシラン系カップリング剤は、オレフィン系樹脂と無機添加物との密着性を高める効果を有し、防曇性を長期的に持続することを可能とするものである。シラン系カップリング剤のオレフィン樹脂系エマルジョンへの配合量は、オレフィン系樹脂成分１００重量部に対して、１〜５０重量部程度が好ましい。１重量部未満であると、オレフィン系樹脂と無機添加物との密着性を高めることができず、所望の防曇性能の持続性を得ることができず、また、５０重量部を超えてしまうと防曇性自体を低下させてしまう可能性がある。
【００１９】
本発明の防曇組成物においては、光安定剤を添加してもよい。光安定剤としては、ヒンダードアミン系化合物が好ましく、本発明の防曇組成物が、オレフィン系樹脂エマルジョンであるため、分散性を考慮するとエマルジョンタイプの光安定剤が好ましい。その場合の配合量は、オレフィン系樹脂成分１００重量部に対して、１〜１００重量部が好ましい。
【００２０】
本発明が提供する防曇組成物においては、その他、必要に応じて顔料、分散剤、消泡剤等の慣用の添加剤を配合してもよい。
【００２１】
本発明が提供する防曇組成物を塗布する農業用フィルムとしての基材フィルムは、エチレン−酢酸ビニル共重合体（ＥＶＡ）、ポリエチレン（ＰＥ）、ポリエチレンテレフタレート（ＰＥＴ）、ポリプロピレン（ＰＰ）等の熱可塑性樹脂の単層フィルム、あるいはこれらの熱可塑性フィルムを積層した多層フィルムのいずれであってもよい。そのなかでも、特に農業用フィルムとして広く使用されているポリエチレンとＥＶＡからなる積層（２層／３層）フィルムに対して、好適に適用し、かかるフィルムに防曇性を付与することができる。なお、基材フィルムに防曇組成物を塗布する場合には、フィルム表面をコロナ放電処理あるいはプラズマ処理をしておくのが好ましい。
【００２２】
基材フィルムには、保湿剤として、シリカ、長石、水酸化マグネシウム、水酸化アルミニウム、ハイドロタルサイト類、ゼオライト類、タルク、耐候剤として、ベンゾフェノン系、ベンゾトリアゾール系紫外線吸収剤、また、滑剤としてメチレンビスアマイド等のアマイド系化合物、ソルビタン脂肪酸系エステル、グリセリン脂肪酸エステルなどの防滴剤、フッ素系界面活性剤等を練り込んだものであってもよい。
【００２３】
本発明防曇組成物の水溶液を基材フィルムに塗布する場合には、グラビアコート、ロールコート、スプレーコート、バーコート、ナイフコート等の方法で行うことができる。組成物の塗布量としては、ウエットで、５〜２０ｇ／ｍ^２／ウエット状態の塗布量で基材フィルムの塗布され、乾燥することにより、本発明の防曇性農業用フィルムを得ることができる。
【００２４】
【実施例】
以下に本発明を実施例および比較例により、さらに詳細に説明するが、本発明はかかる実施例に限定されるものではない。
【００２５】
実施例１〜８／比較例１〜８：
下記表１（実施例１〜８）および表２（比較例１〜８）の配合処方に基づく防曇組成物の水溶液を基材フィルムに塗布し、防曇性農業用フィルムを得た。
なお、使用した基材フィルムは以下のものである。
【００２６】
基材フィルム（Ａ）：
外層／中間層／内層＝１／３／１の層厚比を有する、０．１ｍｍ厚の３層積層フィルムである。
（１）外層樹脂成分：
ポリエチレン（ＫＦ２８２：日本ポリケム社製）１００重量部／メチレンビスステアリン酸アマイド（ミネックス＃７：白石カルシウム社製）０．１重量部／９４４ＬＤ（チバスペシャルティケミカルズ社製）０．５重量部／バイオソーブ＃１３０（共同薬品社製）０．１重量部
（２）中間層樹脂成分：
ＥＶＡ（ウルトラセン６３０：東ソー社製）１００重量部／フジレインＬＳ（富士化学社製）１０重量部／９４４ＬＤ（チバスペシャルティケミカルズ社製）０．５重量部／バイオソーブ＃１３０（共同薬品社製）０．１重量部
（３）内層樹脂成分：
ＥＶＡ（ウルトラセン５１３：東ソー社製）１００重量部／メチレンビスステアリン酸アマイド（ミネックス＃７：白石カルシウム社製）０．１重量部／９４４ＬＤ（チバスペシャルティケミカルズ社製）０．５重量部／バイオソーブ＃１３０（共同薬品社製）０．１重量部
上記の外層／中間層／内層成分の混合物を使用し、インフレーション法にて基材フィルム（Ａ）を調製した。
【００２７】
基材フィルム（Ｂ）：
０．１ｍｍ厚を有する、下記成分からなる単層フィルムである。
ポリエチレン（０１３８Ｎ：出光化学社製）６０重量部／ＥＶＡ（ウルトラセン６３０：東ソー社製）２０重量部／ポリエチレン（１０１４Ｔ：出光化学社製）２０重量部／メチレンビスステアリン酸アマイド（ミネックス＃７：白石カルシウム社製）０．３重量部／９４４ＬＤ（チバスペシャルティケミカルズ社製）０．５重量部／バイオソーブ＃１３０（共同薬品社製）０．１重量部／ステアリン酸０．２重量部／フジレインＬＳ（富士化学社製）５重量部
上記の混合物を用い、カレンダー法により基材フィルム（Ｂ）を調製した。
【００２８】
基材フィルム（Ｃ）：
０．１ｍｍ厚を有する、下記成分からなる単層フィルムである。
ポリエチレンテレフタレート（ＰＥＴ）１００重量部／バイオソーブ＃１３０（共同薬品社製）０．１重量部／メチレンビスステアリン酸アマイド（ミネックス＃７：白石カルシウム社製）０．１重量部
上記の混合物を用い、Ｔダイ法により基材フィルム（Ｃ）を調製した。
【００２９】
なお、各基材フィルムへの防曇組成物の塗布に際しては、フィルム表面の塗布面をコロナ処理した後、グラビアコート法にて塗工し、塗工後９０℃にて３０秒間乾燥させた。
また、塗工液は、ホモミキサーにて５，０００回転／分の回転数で１０分間攪拌し、塗工液とした。
【００３０】
得られた各実施例、比較例の農業用防曇性フィルムについて、塗工液分散性、レベリング性、塗膜の密着性、フィルムの折り曲げ性、防滴性、防滴持続性を一定の基準で評価し、その結果をあわせて表中に示した。
【００３１】
【表１】

【００３２】
＊１：ラポナイトＳ（日本シリカ工業社製）合成ヘクトライト
＊２：ＳＴ−２０（日産化学社製）コロイダルシリカ（固形分２０％）
＊３：ＳＢ−１２５０Ｅ（ユニチカ社製）ポリエチレン系エマルジョン（固形分２５．２％）
＊４：ネオクリルＡ６２３（楠本化成社製）アクリル系エマルジョン（固形分３５％）
【００３３】
【表２】

【００３４】
＊１：ラポナイトＳ（日本シリカ工業社製）合成ヘクトライト
＊２：ＳＴ−２０（日産化学社製）コロイダルシリカ（固形分２０％）
＊３：ＳＢ−１２５０Ｅ（ユニチカ社製）ポリエチレン系エマルジョン（固形分２５．２％）
＊４：ネオクリルＡ６２３（楠本化成社製）アクリル系エマルジョン（固形分３５％）
【００３５】
１）塗工液分散性の評価：
ホモミキサーにて５，０００回転／分の回転数で１０分間攪拌後、１時間以上静置したときの塗工液の状態を目視で判定した。その評価基準は以下のとおりである。
◎：均一に分散している。
○：若干分離しているが、塗工に問題はない。
□：若干沈殿物が見られる。
△：沈殿物が見られる。
×：完全に分散しないで、添加剤が見られる。
【００３６】
２）レベリング性の評価：
グラビアロールにて塗布後、塗工液のはじきを目視にて判定した。その評価基準は以下のとおりである。
◎：はじきがない。
×：はじいている部分が見られる。
【００３７】
３）塗膜の密着性の評価
防曇組成物水溶液を塗工し、乾燥したフィルムにセロテープ（登録商標）を貼り、指で１０回強く押さえた後セロテープ（登録商標）を剥離し、そのときの塗膜の剥離状態を目視にて判定した。その評価基準は以下のとおりである。
◎：全く剥がれない。
○：若干剥がれるが、問題はない。
□：１／３程度剥がれている。
△：１／２程度剥がれている。
×：全面が剥がれている。
【００３８】
４）フィルムの折り曲げ性の評価
防曇組成物水溶液を塗工したフィルムを４つ折にして、ガラス板で上下を５０℃×５時間×１ｋｇの条件で挟んだ後、取り出し、折り目部分の塗膜の状態を目視にて判定した。その評価基準は以下のとおりである。
◎：全く問題がない。
○：若干亀裂が見られるが、問題はない。
□：亀裂が多く見られる。
△：亀裂から塗膜が一部脱落している。
×：塗膜が完全に脱落している。
【００３９】
５）防滴性の評価
防曇組成物水溶液を塗工したフィルムを、間口１．５ｍ×５ｍのトンネルハウスに展帳し、展帳１日後に、フィルム上の水滴の流れを目視にて判定した。その評価基準は以下のとおりである。
◎：全面が液状に流れている。
○：若干の水滴の付着が見られるが、問題はない。
□：水滴の付着が見られる。
△：水滴の付着が多く見られる。
×：全面に水滴が付着している。
【００４０】
６）防滴持続性の評価
上記５）の防滴性で検討したトンネルハウスを２年間放置後、フィルム上の流滴性を目視にて判定した。その評価基準は以下のとおりである。
◎：全面が液状に流れている。
○：若干の水滴の付着が見られるが、問題はない。
□：水滴の付着が見られる。
△：水滴の付着が多く見られる。
×：全面に水滴が付着している。
【００４１】
表中に示した結果から判明するように、本発明の防曇組成物を塗布した農業用防曇性フィルム（実施例１〜８）は、塗工液分散性、レベリング性、塗膜の密着性、フィルムの折り曲げ性、防滴性、防滴持続性において、極めて優れたものであることが理解される。
【００４２】
【発明の効果】
以上記載のように、本発明のオレフィン系樹脂／無機物／シリコン系界面活性剤／シラン系カップリング剤を主成分とするオレフィン樹脂系エマルジョンからなる防曇組成物を塗工することにより、従来の防曇剤を塗布した防曇性農業用フィルムより、フィルムの折り曲げ性に優れ、防滴性の持続に優れた、極めて良好な農業用防曇性フィルムを得ることができ、その農業上の利用価値は多大なものである。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention provides an antifogging composition that imparts antifogging properties by forming an antifogging coating film on a film surface by applying to a base film made of a synthetic resin, and the antifogging composition further includes at least one surface of a film The present invention relates to an antifogging agricultural film obtained by applying the composition to an agricultural film.
[0002]
[Prior art]
[Patent Document 1] JP-A-8-53558 [Patent Document 2] JP-A 9-100467 [0003]
In recent years, so-called house cultivation and tunnel cultivation, in which vegetables and the like are cultivated under a film of an agricultural film such as a synthetic synthetic resin film for the purpose of short-term cultivation of crops or cultivation outside the season, have been widely performed. ing. As a synthetic resin film used for these, a soft vinyl chloride film excellent in light transmittance, moisture retention and anti-fog properties has been used. In recent years, a vinyl chloride resin / acrylic resin or polyethylene / ethylene resin has been used. Multilayer films, such as vinyl acetate copolymer / polyethylene or ethylene-vinyl acetate copolymer, which are laminated in two or three layers, are also being used.
[0004]
However, since the synthetic resin film is inherently hydrophobic in the resin, the molded product is easily charged with static electricity during the molding process or the molded product, and some of the water vapor evaporated from the coated ground surface and agricultural crops condenses on the film surface and water droplets And transparency tends to be impaired. Such a phenomenon lowers the transmittance of sunlight, and consequently deteriorates the growth of the crop.Moreover, water drops formed on the film surface fall, thereby damaging the young shoots of the crop and causing various diseases. There was a problem.
[0005]
In order to solve this problem, it has been practiced to knead an antifogging agent into the film material or to apply an antifogging agent to the film surface to prevent the film surface from fogging. However, when the antifogging agent is kneaded into the film resin raw material, the kneaded antifogging agent spouts out onto the film surface and flows out by water droplets, so that it is not possible to impart antifogging property to the film for a long time. Can not.
[0006]
In addition, when the antifogging agent is applied to the surface of the film, conventionally, an inorganic substance such as colloidal silica or colloidal alumina is added to an acrylic or urethane-based water-based paint to form a hydrophilic coating film on the film surface. Was something. However, when using acrylic paint,
[Patent Document 1],
[Patent Document 2] has the drawback that the coating film formed on the film surface becomes hard, and as a result, is weak in bending, and that the inorganic substances contained in the coating film easily fall off when the film is bent. There was a problem with the long-term expansion.
[0007]
[Problems to be solved by the invention]
Therefore, in view of the above situation, the present invention provides an anti-fogging property to a base film over a long period of time when providing an anti-fogging coating film on a film surface, and also has a strong adhesive strength with a base material fill, and can be bent. It is an object of the present invention to provide an antifogging composition which can form an agricultural antifogging film which is strong and in which inorganic substances contained in the coating film are hard to fall off, and an agricultural antifogging film coated with the antifogging composition. [0008]
[Means for Solving the Problems]
The present invention for solving such a problem has a surface of an agricultural film, comprising an olefin-based resin emulsion solution, wherein an inorganic additive, a silicon-based surfactant and a silane-based coupling agent are added. It is an antifogging composition for agricultural films which is applied to a film.
[0009]
That is, the present invention uses an antifogging material composed of a specific combination of an inorganic substance, a silicon-based surfactant, and a silane-based coupling agent or the like as the antifogging compounding composition. It is characterized in that an olefin-based resin emulsion is used as a hydrophilic coating material when forming an antifogging coating film by applying the film to a film.
[0010]
The agricultural antifogging film obtained by applying the antifogging composition of the present invention having the basic structure to the surface of the base film has good coatability of the coating film on the base film. The adhesiveness between the substrate film and the anti-fog coating film is strong, the drip-proof property and the drip-proof durability are good, and the coating strength against bending is improved.
[0011]
BEST MODE FOR CARRYING OUT THE INVENTION
The present invention is characterized in that an olefin-based resin emulsion is used as a main component, as an antifogging composition for forming an antifogging coating film by applying to at least one of the surfaces of the substrate film as described above. is there. That is, by using the olefin-based resin emulsion, it becomes possible to uniformly disperse the hydrophilic inorganic additive in the composition and to firmly adhere it to the film surface. In addition, the resin layer formed on the film surface by the olefin-based resin emulsion has flexibility as compared with acrylic resins and the like, but also has excellent light resistance as compared with urethane-based resins. Can be prevented for a long time. Therefore, an ethylene resin emulsion having flexibility is particularly preferable as the olefin resin emulsion.
[0012]
The resin component of the olefin resin emulsion constituting the antifogging composition provided by the present invention is preferably about 0.1% to 4.0%. If the resin component is less than 0.1%, a desired coating film cannot be formed, and there is a possibility that the inorganic additive may be missing. On the other hand, if the resin component exceeds 4.0%, the resin layer itself tends to become thicker, and the possibility that the inorganic additive is buried in the formed resin layer becomes higher, and the addition of the inorganic additive is increased. The anti-fog performance with the amount cannot be exhibited.
[0013]
The adjustment of the resin component may be adjusted at the stage of adding the inorganic additive or the like, or after adding the inorganic additive to the emulsion having the resin component of 10 to 40%, the hydrophilicity such as water or alcohol may be adjusted. It may be prepared by diluting with an organic solvent.
[0014]
The inorganic additive used in the antifogging composition provided by the present invention is not particularly limited as long as it is a hydrophilic inorganic additive capable of imparting antifogging properties. Further, the particle size of the inorganic additive is preferably about 10 to 100 nm. If the particle size is less than 10 nm, there is a high possibility that the particle will be buried in the formed resin layer, and sufficient performance may not be exhibited. On the other hand, if the particle size exceeds 100 nm, the particles may be lost and the anti-fogging property may be deteriorated. If the resin layer for holding the inorganic substance is thickened, the flexibility and transparency of the resin layer may be impaired.
[0015]
Therefore, in the present invention, it is preferable to use synthetic hectorite which is a synthetic layered silicate as an inorganic additive. This synthetic hectorite has good dispersibility in an emulsion or the like, and is in a state of being uniformly dispersed in the formed resin layer.
[0016]
In the present invention, the compounding amount of the inorganic additive, particularly the synthetic hectorite, is preferably from 100 to 2,000 parts by weight based on 100 parts by weight of the olefin resin in the olefin resin emulsion. If the amount is less than 100 parts by weight, the anti-fogging property is not sufficient, and if it exceeds 2000 parts by weight, the anti-fogging property itself hardly changes, the transparency of the formed resin layer is reduced, and the agricultural film is used. It is not preferable because the transparency of the film itself is reduced.
[0017]
The silicon-based surfactant added to the antifogging composition provided by the present invention improves the dispersibility of the inorganic additive added to the antifogging composition, and improves the wettability when applied to the base film. Thus, the adhesion of the anti-fogging resin layer to the base film can be increased, and the anti-fogging property of the anti-fogging resin layer can be further improved. The blending amount of the silicone surfactant in the olefin resin emulsion is preferably about 1 to 100 parts by weight based on 100 parts by weight of the olefin resin component. If the amount is less than 1 part by weight, the above effects cannot be obtained. If the amount exceeds 100 parts by weight, the strength of the antifogging resin layer is reduced, and the durability of the antifogging performance is reduced. Will be done.
[0018]
Further, the silane coupling agent added to the antifogging composition provided by the present invention has an effect of increasing the adhesion between the olefin resin and the inorganic additive, and maintains the antifogging property for a long time. Is made possible. The blending amount of the silane coupling agent in the olefin resin emulsion is preferably about 1 to 50 parts by weight based on 100 parts by weight of the olefin resin component. If the amount is less than 1 part by weight, the adhesion between the olefin-based resin and the inorganic additive cannot be increased, the desired durability of the anti-fog performance cannot be obtained, and the amount exceeds 50 parts by weight. In this case, the antifogging property itself may be reduced.
[0019]
In the antifogging composition of the present invention, a light stabilizer may be added. As the light stabilizer, a hindered amine compound is preferable. Since the antifogging composition of the present invention is an olefin resin emulsion, an emulsion type light stabilizer is preferable in consideration of dispersibility. In this case, the amount is preferably 1 to 100 parts by weight based on 100 parts by weight of the olefin resin component.
[0020]
In the antifogging composition provided by the present invention, other conventional additives such as a pigment, a dispersant, and an antifoaming agent may be blended as necessary.
[0021]
The base film as an agricultural film to which the antifogging composition provided by the present invention is applied includes ethylene-vinyl acetate copolymer (EVA), polyethylene (PE), polyethylene terephthalate (PET), polypropylene (PP) and the like. It may be either a single-layer film of a thermoplastic resin or a multilayer film in which these thermoplastic films are laminated. Among them, particularly, it is suitably applied to a laminated (two-layer / three-layer) film composed of polyethylene and EVA, which is widely used as an agricultural film, and can impart antifogging property to such a film. When the antifogging composition is applied to the substrate film, it is preferable that the film surface is subjected to a corona discharge treatment or a plasma treatment.
[0022]
In the base film, as a humectant, silica, feldspar, magnesium hydroxide, aluminum hydroxide, hydrotalcites, zeolites, talc, as a weathering agent, benzophenone-based, benzotriazole-based ultraviolet absorber, and as a lubricant Amide compounds such as methylene bisamide, sorbitan fatty acid esters, glycerin fatty acid esters and other drip-proofing agents, fluorine surfactants and the like may be kneaded.
[0023]
When the aqueous solution of the antifogging composition of the present invention is applied to a substrate film, it can be performed by a method such as gravure coating, roll coating, spray coating, bar coating, knife coating, and the like. With respect to the application amount of the composition, the base film is applied in a wet amount of 5 to 20 g / m ² / wet, and then dried, whereby the antifogging agricultural film of the present invention can be obtained. .
[0024]
【Example】
Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples, but the present invention is not limited to these Examples.
[0025]
Examples 1-8 / Comparative Examples 1-8:
An aqueous solution of the anti-fogging composition based on the formulation shown in Table 1 (Examples 1 to 8) and Table 2 (Comparative Examples 1 to 8) was applied to a substrate film to obtain an anti-fogging agricultural film.
In addition, the base film used was as follows.
[0026]
Base film (A):
It is a 0.1 mm thick three-layer laminated film having a layer thickness ratio of outer layer / intermediate layer / inner layer = 1/3/1.
(1) Outer layer resin component:
100 parts by weight of polyethylene (KF282: manufactured by Nippon Polychem) /0.1 part by weight of methylene bisstearic acid amide (Minex # 7: manufactured by Shiraishi Calcium Co.) / 0.5 part by weight of 944LD (manufactured by Ciba Specialty Chemicals) / Biosorb # 130 (manufactured by Kyodo Yakuhin) 0.1 part by weight (2) Intermediate layer resin component:
EVA (Ultracene 630: manufactured by Tosoh Corporation) 100 parts by weight / Fujirain LS (manufactured by Fuji Chemical Co., Ltd.) 10 parts by weight / 944LD (Ciba Specialty Chemicals) 0.5 part by weight / Biosorb # 130 (manufactured by Kyodo Yakuhin) 0 .1 part by weight (3) Inner layer resin component:
100 parts by weight of EVA (Ultracene 513: manufactured by Tosoh Corporation) /0.1 part by weight of methylene bisstearic acid amide (Minex # 7: manufactured by Shiraishi Calcium Co.) / 0.5 part by weight of 944LD (manufactured by Ciba Specialty Chemicals) / Biosorb # 130 (manufactured by Kyodo Yakuhin Co., Ltd.) 0.1 part by weight Using the above mixture of the outer layer / intermediate layer / inner layer components, a base film (A) was prepared by an inflation method.
[0027]
Base film (B):
A single-layer film having a thickness of 0.1 mm and comprising the following components:
60 parts by weight of polyethylene (0138N: manufactured by Idemitsu Chemical Co., Ltd.) / 20 parts by weight of EVA (Ultracene 630: manufactured by Tosoh Corporation) / 20 parts by weight of polyethylene (1014T: manufactured by Idemitsu Chemical Co., Ltd.) / Methylene bisstearic acid amide (Minex # 7: 0.3 parts by weight / 944LD (manufactured by Ciba Specialty Chemicals) 0.5 parts by weight / 0.1 parts by weight of Biosorb # 130 (manufactured by Kyodo Yakuhin) / 0.2 parts by weight of stearic acid / Fujilein LS A base film (B) was prepared by a calender method using 5 parts by weight (manufactured by Fuji Chemical Co., Ltd.) of the above mixture.
[0028]
Base film (C):
A single-layer film having a thickness of 0.1 mm and comprising the following components:
100 parts by weight of polyethylene terephthalate (PET) /0.1 parts by weight of Biosorb # 130 (manufactured by Kyodo Yakuhin) /0.1 parts by weight of amide methylene bisstearate (Minex # 7: manufactured by Shiraishi Calcium Co.) A substrate film (C) was prepared by a T-die method.
[0029]
In applying the antifogging composition to each base film, the coating surface of the film surface was subjected to a corona treatment, then applied by a gravure coating method, and dried at 90 ° C. for 30 seconds after the application.
Further, the coating liquid was stirred for 10 minutes at a rotation speed of 5,000 revolutions / minute using a homomixer to obtain a coating liquid.
[0030]
For each of the obtained examples, the antifogging film for agricultural use of the comparative example, the coating liquid dispersibility, leveling property, adhesion of the coating film, bendability of the film, drip-proof property, drip-proof durability are fixed standards. And the results are shown in the table.
[0031]
[Table 1]

[0032]
* 1: Laponite S (manufactured by Nippon Silica Co., Ltd.) synthetic hectorite * 2: ST-20 (manufactured by Nissan Chemical Industries, Ltd.) colloidal silica (solid content: 20%)
* 3: SB-1250E (manufactured by Unitika) polyethylene emulsion (solid content: 25.2%)
* 4: Neoacryl A623 (Kusumoto Kasei Co., Ltd.) acrylic emulsion (solid content 35%)
[0033]
[Table 2]

[0034]
* 1: Laponite S (manufactured by Nippon Silica Co., Ltd.) synthetic hectorite * 2: ST-20 (manufactured by Nissan Chemical Industries, Ltd.) colloidal silica (solid content: 20%)
* 3: SB-1250E (manufactured by Unitika) polyethylene emulsion (solid content: 25.2%)
* 4: Neoacryl A623 (Kusumoto Kasei Co., Ltd.) acrylic emulsion (solid content 35%)
[0035]
1) Evaluation of coating liquid dispersibility:
After stirring with a homomixer at a rotation speed of 5,000 rpm for 10 minutes, the state of the coating liquid when allowed to stand for 1 hour or more was visually determined. The evaluation criteria are as follows.
：: Uniformly dispersed.
：: Slightly separated, but no problem in coating.
□: Some precipitate is observed.
Δ: A precipitate is observed.
×: Additives are seen without complete dispersion.
[0036]
2) Leveling property evaluation:
After coating with a gravure roll, the repellency of the coating liquid was visually determined. The evaluation criteria are as follows.
A: No repelling.
X: The repelled part is seen.
[0037]
3) Evaluation of adhesion of coating film An aqueous solution of the anti-fog composition was applied, a cellophane tape (registered trademark) was applied to the dried film, and the cellophane tape (registered trademark) was peeled off after strongly pressing with a finger 10 times. Of the coating film was visually determined. The evaluation criteria are as follows.
A: No peeling at all.
：: slight peeling, but no problem.
□: About 1/3 peeled off.
Δ: About １ ／ peeled.
×: The entire surface is peeled off.
[0038]
4) Evaluation of bending property of film The film coated with the aqueous solution of the anti-fog composition was folded into four pieces, sandwiched between glass plates at 50 ° C. × 5 hours × 1 kg, then taken out, and the coating film at the fold portion was taken out. Was visually determined. The evaluation criteria are as follows.
A: There is no problem at all.
：: Some cracks are observed, but there is no problem.
□: Many cracks are seen.
Δ: Part of the coating film was dropped from the crack.
X: The coating film has completely fallen off.
[0039]
5) Evaluation of drip-proof property The film coated with the aqueous solution of the anti-fog composition was exhibited in a tunnel house having a width of 1.5 m × 5 m, and one day after the exhibition, the flow of water droplets on the film was visually determined. did. The evaluation criteria are as follows.
：: The entire surface is flowing in a liquid state.
：: Some water droplets adhered, but no problem.
□: Adhesion of water droplets is observed.
Δ: Many adhesion of water droplets is observed.
×: Water droplets adhered to the entire surface.
[0040]
6) Evaluation of drip-proof durability After leaving the tunnel house examined for the drip-proof property of the above 5) for 2 years, the drip-proof property on the film was visually determined. The evaluation criteria are as follows.
：: The entire surface is flowing in a liquid state.
：: Some water droplets adhered, but no problem.
□: Adhesion of water droplets is observed.
Δ: Many adhesion of water droplets is observed.
×: Water droplets adhered to the entire surface.
[0041]
As can be seen from the results shown in the table, the agricultural anti-fog film coated with the anti-fog composition of the present invention (Examples 1 to 8) has a coating liquid dispersibility, a leveling property, and adhesion of a coating film. It is understood that the film is extremely excellent in properties, film folding property, drip-proof property and drip-proof durability.
[0042]
【The invention's effect】
As described above, a conventional antifogging composition comprising an olefin resin emulsion containing an olefin resin / inorganic substance / silicone surfactant / silane coupling agent as a main component of the present invention is applied. From the anti-fog agricultural film coated with the anti-fog agent, it is possible to obtain an extremely good agricultural anti-fog film excellent in film bending property and excellent drip-proof property, and its agricultural use. The value is enormous.

Claims (4)

農業用フィルムの表面に塗布されるオレフィン系樹脂エマルジョン溶液からなる農業用フィルム用防曇組成物であって、無機添加物、シリコン系界面活性剤およびシラン系カップリング剤が添加されていることを特徴とする農業用フィルム用防曇組成物。An agricultural film antifogging composition comprising an olefin resin emulsion solution applied to the surface of an agricultural film, wherein an inorganic additive, a silicon surfactant, and a silane coupling agent are added. Characteristic antifogging composition for agricultural films. 無機添加物が合成ヘクトライトであり、オレフィン系樹脂エマルジョンのオレフィン樹脂成分１００重量部に対して、１００〜２，０００重量部添加されていることを特徴とする請求項１に記載の農業用フィルム用防曇組成物。The agricultural film according to claim 1, wherein the inorganic additive is synthetic hectorite, and is added in an amount of 100 to 2,000 parts by weight based on 100 parts by weight of the olefin resin component of the olefin resin emulsion. Antifogging composition. オレフィン系樹脂エマルジョン溶液が、エチレン系樹脂エマルジョン溶液であることを特徴とする請求項１または２に記載の農業用フィルム用防曇組成物。The antifogging composition for agricultural films according to claim 1 or 2, wherein the olefin resin emulsion solution is an ethylene resin emulsion solution. オレフィン系樹脂エマルジョン溶液のオレフィン樹脂成分が０．１％〜４％であることを特徴とする請求項１、２または３に記載の農業用フィルム用防曇組成物。The antifogging composition for agricultural films according to claim 1, 2 or 3, wherein the olefin resin component of the olefin resin emulsion solution is 0.1% to 4%.