JP2004017590A

JP2004017590A - Decorative material for flooring material

Info

Publication number: JP2004017590A
Application number: JP2002178989A
Authority: JP
Inventors: Yasuo Nakai; 中井　康夫
Original assignee: Dai Nippon Printing Co Ltd
Current assignee: Dai Nippon Printing Co Ltd
Priority date: 2002-06-19
Filing date: 2002-06-19
Publication date: 2004-01-22
Anticipated expiration: 2022-06-19
Also published as: JP4060647B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a decorative material for a flooring material which is a decorative material for the flooring material using plywood and eliminates the selective coating work for a groove part and prevents the damage of the design effect caused by color blur, turbidity or the like of the groove part. <P>SOLUTION: In the decorative material for the flooring material which is manufactured by laminating a laminate with a thickness of 450-800 μm comprising a sheet made of a synthetic resin and a decorative sheet on plywood so that the sheet made of the synthetic resin is positioned on the side of the plywood and has the groove part formed thereto by cutting processing so that the deepest part thereof is positioned in the sheet made of the synthetic resin from the decorative sheet side, a color concealing layer is provided between the plywood and the sheet made of the synthetic resin. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は、住宅等の床面に用いられる床材用化粧材に関し、さらに詳しくは、耐キャスター性、耐衝撃性、耐水性に優れた床材用化粧材に関するものである。
【０００２】
【従来の技術】
従来から床材としては、木質系基材に木目柄等の美麗な印刷を施した化粧シートを貼着したものが用いられている。たとえば、合板に木目柄等の美麗な印刷を施した化粧シートを貼着したもの、あるいは、合板と中密度繊維板（ＭＤＦ）を積層した積層体の前記中密度繊維板面に木目柄等の美麗な印刷を施した化粧シートを貼着したものなどを代表的なものとして例示することができる。
【０００３】
しかし、前者は耐キャスター性や耐衝撃性に劣るといった問題、また、床材には通常意匠性を向上する目的で切削加工等により溝部や面取部が設けられるが、これらの部分に毛羽立ちやササクレ等を生じ、靴下やストッキングの繊維がこれに引掛り伝線するといった問題、また、色ブレやダク等の問題があり、後者は上記した前者の問題はないものの中密度繊維板（ＭＤＦ）が耐水性に劣るために水の浸入により中密度繊維板が膨らみ、意匠性を損なうといった問題がある。さらにまた、前者、後者共に溝部や面取部を設けた部位に透明ないし着色した塗料を塗布することにより、耐水性を持たせたり、あるいは、化粧シートを貼着した部位との色合いの差を解消しているが、このような塗布作業は溝部や面取部のみを選択的に塗布しなけらばならず、結構手間が掛かるといった問題があった。
【０００４】
【発明が解決しようとする課題】
そこで本発明は、木質系基材として合板を用い、耐水性はもとより耐キャスター性や耐衝撃性に優れ、毛羽立ちやササクレ等のない溝部や面取部を有し、色ブレやダク等で意匠性を損なうことがない床材用化粧材を提供することにある。特に溝部の選択的塗布作業をなくし、溝部の色ブレやダク等で意匠性を損なうことがない床材用化粧材を提供することにある。
【０００５】
【課題を解決するための手段】
本発明者は、上記課題を達成するために、請求項１記載の本発明は、合板上に、合成樹脂製シートと装飾シートとからなる厚さが４５０〜８００μｍの積層体を前記合成樹脂製シートが前記合板側に位置するように積層すると共に前記装飾シート側から前記合成樹脂製基材シート内にその最深部が位置する溝部が切削加工により形成された床材用化粧材において、前記合板と前記合成樹脂製基材シートの間に着色隠蔽層が設けられていることを特徴とするものである。
【０００６】
また、請求項２記載の本発明は、請求項１記載の床材用化粧材において、前記着色隠蔽層が前記合成樹脂製シートの前記合板側の面に設けられた印刷層であることを特徴とするものである。
【０００７】
また、請求項３記載の本発明は、請求項１記載の床材用化粧材において、前記着色隠蔽層が前記合成樹脂製シートの前記合板側の面に設けられた着色樹脂層であることを特徴とするものである。
【０００８】
上記請求項１〜３のいずれかに記載の構成とすることにより、耐水性、耐キャスター性、耐衝撃性に優れ、切削加工により形成された溝部や面取部も毛羽立ちやササクレ等がなく、また、合板を用いた場合に発生する色ブレやダク等で意匠性を損なうことがない床材用化粧材とすることができる。特に溝部の選択的塗布作業をなくし、溝部の色ブレやダク等で意匠性を損なうことがない床材用化粧材とすることができる。
【０００９】
また、請求項４記載の本発明は、請求項１〜３のいずれかに記載の床材用化粧材において、前記装飾シートの表面に表面保護層が形成されていることを特徴とするものである。このように構成することにより、耐擦傷性、耐摩耗性、耐汚染性等の表面物性に優れた床材用化粧材とすることができる。
【００１０】
【発明の実施の形態】
上記の本発明について、図面等を用いて以下に詳述する。
図１は本発明にかかる床材用化粧材の基本的構成を示す断面図、図２は本発明にかかる床材用化粧材を構成する装飾シートの第１実施形態を示す断面図、図３は本発明にかかる床材用化粧材を構成する装飾シートの第２実施形態を示す断面図、図４は本発明にかかる床材用化粧材を構成する装飾シートの第３実施形態を示す断面図、図５は本発明にかかる床材用化粧材を構成する装飾シートの第４実施形態を示す断面図であり、図中の１は床材用化粧材、２は合板、３は合成樹脂製シート、４，４’，４”，４’’’，４””は装飾シート、５は着色隠蔽層、６は溝部、４０，４０’はオレフィン系熱可塑性樹脂シート、４０”はオレフィン系熱可塑性樹脂層、４１は凹凸模様、４２はワイピングインキ、４３，４５はプライマー層、４４は表面保護層、４６は絵柄層、４７はベタ印刷層、４８は接着剤層をそれぞれ示す。
【００１１】
図１は本発明にかかる床材用化粧材の基本的構成を示す断面図あって、床材用化粧材１は合板２上に、着色隠蔽層５と合成樹脂製シート３と装飾シート４を順に設け、前記装飾シート４側から前記合成樹脂製シート３内にその最深部が位置する溝部６を切削加工により設けたものである。なお、前記合成樹脂製シート３と前記装飾シート４の積層した厚さが４５０〜８００μｍになるように設計されている。この理由としては、切削加工により設ける溝部６が少なくとも４００μｍ深さであることと、通常前記合成樹脂製シート３と前記装飾シート４の積層したものを前記合板２に貼着するために、生産性を考慮すると前記合成樹脂製シート３と前記装飾シート４の積層したものをロール状で取扱えることが肝要であり、これらから必然的に前記合成樹脂製シート３と前記装飾シート４の積層した厚さが４５０〜８００μｍになるように設計されている。このように構成することにより、耐水性、耐キャスター性、耐衝撃性に優れ、切削加工により形成された溝部や面取部も毛羽立ちやササクレ等がなく、また、合板を用いた場合に発生する色ブレやダク等で意匠性を損なうことがない床材用化粧材を得ることができる。特に溝部の選択的塗布作業をなくし、溝部の色ブレやダク等で意匠性を損なうことがない床材用化粧材とすることができる。
【００１２】
まず、床材用化粧材１を構成する合成樹脂製シート３について説明する。合成樹脂製シート３を形成する樹脂としては、昨今の環境問題を考慮してハロゲン元素を分子構造中に含まない樹脂が適当であり、たとえば、ポリプロピレン、エチレン−ビニルアルコール共重合体、ポリメチレン、ポリメチルペンテン、ポリエチレンテレフタレート、耐熱性の高いポリアルキレンテレフタレート〔たとえばエチレングリコールの一部を１，４−シクロヘキサンジメタノールやジエチレングリコール等で置換したポリエチレンテレフタレートである、いわゆる商品名ＰＥＴ−Ｇ（イーストマンケミカルカンパニー製）〕、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリエチレンナフタレート−イソフタレート共重合体、ポリカーボネート、ポリアリレート、ポリイミド、ポリスチレン、ポリアミド、ＡＢＳ等の樹脂などを挙げることができ、これらの樹脂は、単独であってもよいし、混合物であってもよいし、さらにこれらの樹脂で構成される前記合成樹脂製シート３は単層であっても複層であってもよいものである。また、前記合成樹脂製シート３の厚さとしては、後述する前記装飾シート４の厚さとも関連するが、上記したように切削加工により設ける溝部６が少なくとも４００μｍ深さであることやロールロール状で取扱えることを勘案すると概ね３００〜６００μｍが適当である。また、前記合成樹脂製シート３は必要な面に、必要に応じてコロナ放電処理、オゾン処理、プラズマ処理等の易接着処理を施すことができる。
【００１３】
次に、床材用化粧材１を構成する着色隠蔽層５について説明する。前記着色隠蔽層５は、前記合成樹脂製シート３の一方の面にグラビア印刷、オフセット印刷、シルクスクリーン印刷等の周知の印刷法でインキを用いてベタ柄を印刷することにより形成することができるし、また、前記合成樹脂製シート３の一方の面に、たとえば、有機顔料および／ないし無機顔料を混合した熱可塑性樹脂をＴダイ押出機で加熱溶融押出しすることにより形成することができる。顔料の熱可塑性樹脂への混合方法としては、予めバンバリーミキサー等で両者をメルトブレンドし、マスターバッチ化したものを所定の混合比にする方法、あるいは、熱可塑性樹脂との直接混合方法のいずれであってもよい。そして、前記インキとしては、ビヒクルとして、塩素化ポリエチレン、塩素化ポリプロピレン等の塩素化ポリオレフィン、ポリエステル、イソシアネートとポリオールからなるポリウレタン、ポリアクリル、ポリ酢酸ビニル、ポリ塩化ビニル、塩化ビニル−酢酸ビニル共重合体、セルロース系樹脂、ポリアミド系樹脂等を１種ないし２種以上混合して用い、これに顔料、溶剤、各種補助剤等を加えてインキ化したものを用いることができるが、環境問題や被印刷面との接着性等を考慮すると、ポリエステル、イソシアネートとポリオールからなるポリウレタン、ポリアクリル、ポリアミド系樹脂等の１種ないし２種以上混合したものが適当である。また、有機顔料および／ないし無機顔料を混合した熱可塑性樹脂としては特に限定はされないが、例示するならば、ポリエチレンやポリプロピレン等のオレフィン系熱可塑性樹脂がコストや加工適性を考慮すると適当である。また、積層方法としては前記合成樹脂製シート３の一方の面にＴダイ押出機で加熱溶融押出しして形成するのみならず、たとえば、予め有機顔料および／ないし無機顔料を混合した熱可塑性樹脂を用いて着色隠蔽シートを作製しておき、これと前記合成樹脂製シート３とを周知のドライラミネーション法で積層してもよいものである。
【００１４】
また、前記着色隠蔽層５の別の形成方法としては、前記合成樹脂製シート３を、たとえば、マルチマニホールドタイプの多層押出機で少なくとも２層からなるシートを製造し、その一方の外層を有機顔料および／ないし無機顔料で着色した層として形成してもよいものである。
【００１５】
次に、床材用化粧材１を構成する装飾シート４について説明する。装飾シート４を構成する基材シートとしては、薄紙，上質紙，クラフト紙，和紙，チタン紙，樹脂含浸紙，紙間強化紙等の紙、木質繊維，ガラス繊維，石綿，ポリエステル繊維，ビニロン繊維，レーヨン繊維等の繊維からなる織布や不織布、あるいは、ポリオレフィン，ポリエステル，ポリアクリル，ポリアミド，ポリウレタン，ポリスチレン等の合成樹脂製シートなどの１種ないし２種以上の積層体を用いることができ、その厚さとしては概ね２０〜３００μｍが適当である。また、前記基材は必要に応じて必要な層に顔料等を添加して着色してもよいし、必要な面にコロナ放電処理、プラズマ処理、オゾン処理等の易接着処理を施してもよいものである。
【００１６】
図２は本発明にかかる床材用化粧材を構成する装飾シートの第１実施形態を示す断面図であって、装飾シート４’は透明なオレフィン系熱可塑性樹脂シート４０の一方の面にエンボス加工を施して凹凸模様４１を設け、その上からワイピング処理を施して前記凹凸模様４１の凹部内にワイピングインキ４２を充填した後に、表出面全面にプライマー層４３を設け、該プライマー層４３上に表面保護層４４を形成すると共に前記オレフィン系熱可塑性樹脂シート４０の他方の面にプライマー層４５を介して絵柄層４６、ベタ印刷層４７を形成したものである。
【００１７】
図３は本発明にかかる床材用化粧材を構成する装飾シートの第２実施形態を示す断面図であって、装飾シート４”は着色したオレフィン系熱可塑性樹脂シート４０’の一方の面にプライマー層４５を設け、該プライマー層４５上にベタ印刷層４７、絵柄層４６を順に印刷形成し、さらに前記絵柄層４６上に２液硬化型ウレタン樹脂等の周知のドライラミネーション用接着剤で形成した接着剤層４８を介して透明なオレフィン系熱可塑性樹脂シート４０ないし透明なオレフィン系熱可塑性樹脂層４０”を周知のドライラミネーション法ないしＴダイ押出し法で積層し、前記オレフィン系熱可塑性樹脂シート４０ないし前記オレフィン系熱可塑性樹脂層４０”の表出面全面にプライマー層４３を設け、該プライマー層４３上に表面保護層４４を形成したものである。
【００１８】
図４は本発明にかかる床材用化粧材を構成する装飾シートの第３実施形態を示す断面図であって、装飾シート４’’’は着色したオレフィン系熱可塑性樹脂シート４０’の一方の面にプライマー層４５を設け、該プライマー層４５上にベタ印刷層４７、絵柄層４６を順に印刷形成し、さらに前記絵柄層４６上に２液硬化型ウレタン樹脂等の周知のドライラミネーション用接着剤で形成した接着剤層４８を介して透明なオレフィン系熱可塑性樹脂シート４０ないし透明なオレフィン系熱可塑性樹脂層４０”を周知のドライラミネーション法ないしＴダイ押出し法で積層し、前記オレフィン系熱可塑性樹脂シート４０ないし前記オレフィン系熱可塑性樹脂層４０”の表面にエンボス加工を施して凹凸模様４１を設け、その上からワイピング処理を施して前記凹凸模様４１の凹部内にワイピングインキ４２を充填した後に、表出面全面にプライマー層４３を設け、該プライマー層４３上に表面保護層４４を形成したものである。なお、今まで基材シートを用いた装飾シート４について説明してきたが、装飾シート４はこれに限ることはなく、たとえば、突板であってもよいものである。
【００１９】
そして、前記プライマー層４３は前記オレフィン系熱可塑製性樹脂シート４０ないし前記オレフィン系熱可塑性樹脂層４０”と前記表面保護層４４との接着強度を向上させる目的で設けるものであり、前記プライマー層４３を設ける方が接着強度面から望ましい。また、図２〜４に示した前記プライマー層４５はオレフィン系熱可塑性樹脂シート４０ないし４０’と絵柄層４６、ベタ印刷層４７等の印刷層との接着性を向上させる目的で設けるものであり、前記プライマー層４３と同様の樹脂を用いて同様に形成するのが前記プライマー層４３と同様の意味で好ましい。
【００２０】
前記プライマー層４３、４５は、上記したようにオレフィン系熱可塑性樹脂シート４０、４０’、４０”の表面の接着性を高めるためのものであり、これに用いる樹脂としてはエステル樹脂、ウレタン樹脂、アクリル樹脂、ポリカーボネート樹脂、塩化ビニル−酢酸ビニル共重合体、ポリビニルブチラール樹脂、ニトロセルロース樹脂等を挙げることができ、これらの樹脂は単独ないし混合して塗料組成物、または、インキ組成物とし、ロールコート法やグラビア印刷法等の適宜の塗布手段を用いて形成することができる。
【００２１】
また、凹凸模様４１は加熱プレスやヘアライン加工などにより形成することができる。前記凹凸模様４１としては、たとえば、導管溝、石板表面凹凸、布表面テクスチュア、梨地、砂目、ヘアライン、万線条溝等である。
【００２２】
また、前記絵柄層４６および前記ベタ印刷層４７は、一般的にはグラビア印刷、オフセット印刷、シルクスクリーン印刷等の周知の印刷法でインキを用いて形成することができる。前記絵柄層４６としては、たとえば、木目模様、石目模様、布目模様、皮紋模様、幾何学模様、文字、記号、線画、各種抽象模様柄であり、前記ベタ印刷層４７としては、隠蔽性を有する着色インキでベタ印刷したものである。また、図２〜４においては、前記絵柄層４６および前記ベタ印刷層４７の両方を設けた構成を示したが、いずれか一方の構成であっても構わない。
【００２３】
また、前記絵柄層４６および前記ベタ印刷層４７に用いるインキ、あるいは、ワイピングインキ４２としては、着色隠蔽層５のところで説明した同じインキを用いて形成すればよいものであり説明は省略する。
【００２４】
なお、図２〜４に示した化粧層４’、４”、４’’’は、本発明にかかる床材用化粧材を構成する装飾シート４の実施例を例示したものであって、本発明の趣旨を逸脱しない範囲であれば、これに限るものではなく、たとえば、薄紙の一方の面にベタ印刷層、絵柄層を順に印刷形成し、この絵柄層を形成した面全面に表面保護層を設けた構成からなる化粧層であってもよいものである。
【００２５】
次に、装飾シート４の表面に設ける表面保護層４４について説明する。この表面保護層４４は床材用化粧材１（図１参照）に要求される耐擦傷性、耐磨耗性、耐水性、耐汚染性等の表面物性を付与するために設けられるものであり、この表面保護層４４を形成する樹脂としては、熱硬化型樹脂ないし電離放射線硬化型樹脂等の硬化型樹脂を用いて形成するのが適当である。
【００２６】
熱硬化型樹脂としては、不飽和ポリエステル樹脂、ポリウレタン樹脂（２液硬化型ポリウレタンも含む）、エポキシ樹脂、アミノアルキッド樹脂、フェノール樹脂、尿素樹脂、ジアリルフタレート樹脂、メラミン樹脂、グアナミン樹脂、メラミン−尿素共縮合樹脂、珪素樹脂、ポリシロキサン樹脂等を挙げることができる。上記樹脂には必要に応じて、架橋剤、重合開始剤等の硬化剤、または、重合促進剤を添加して用いる。たとえば、硬化剤としては、イソシアネートまたは有機スルホン酸塩等が不飽和ポリエステル樹脂やポリウレタン樹脂等に添加され、有機アミン等がエポキシ樹脂に添加され、メチルエチルケトンパーオキサイド等の過酸化物やアゾイソブチルニトリル等のラジカル開始剤が不飽和ポリエステル樹脂には添加される。上記熱硬化型樹脂で表面保護層を形成する方法としては、たとえば、上記した熱硬化型樹脂を溶液化し、ロールコート法、グラビアコート法等の周知の塗布法で塗布し、乾燥すると共に硬化させることにより形成することができる。塗布量としては、固形分で概ね５〜３０μｍが適当であり、好ましくは１５〜２５μｍである。
【００２７】
電離放射線硬化型樹脂としては、電離放射線を照射することにより架橋重合反応を起こして３次元の高分子構造に変化する樹脂である。電離放射線は、電磁波または荷電粒子線のうち分子を重合、架橋し得るエネルギー量子を有するものを意味し、可視光線、紫外線（近紫外線、真空紫外線等）、Ｘ線、電子線、イオン線等がある。通常は紫外線や電子線が用いられる。紫外線源としては、超高圧水銀灯、高圧水銀灯、低圧水銀灯、カーボンアーク灯、ブラックライト蛍光灯、メタルハライドランプ灯の光源が使用できる。紫外線の波長としては、１９０〜３８０ｎｍの波長域を使用することができる。また、電子線源としては、コッククロフトワルト型、バンデグラフト型、共振変圧器型、絶縁コア変圧器型、あるいは、直線型、ダイナミトロン型、高周波型等の各種電子線加速器を用いることができる。用いる電子線としては、１００〜１０００ｋｅＶ、好ましくは１００〜３００ｋｅＶのものが使用される。電子線の照射量は、通常２〜１５Ｍｒａｄ程度である。
【００２８】
そして、電離放射線硬化型樹脂は、分子中に、（メタ）アクリロイル基、（メタ）アクリロイルオキシ基等のラジカル重合性不飽和基、又はエポキシ基等のカチオン重合性官能基を有する単量体、プレポリマー又はポリマー（以下、これらを総称して化合物と呼称する）からなる。これら単量体、プレポリマー、及びポリマーは、単体で用いるか、或いは複数種混合して用いる。尚、本明細書で（メタ）アクリレートとは、アクリレート又はメタアクリレートの意味で用いる。
【００２９】
ラジカル重合性不飽和基を有するプレポリマーとしては、ポリエステル（メタ）アクリレート、ウレタン（メタ）アクリレート、エポキシ（メタ）アクリレート、メラミン（メタ）アクリレート、トリアジン（メタ）アクリレート、ポリビニルピロリドン等が挙げられる。このプレポリマーは、通常、分子量が１００００程度以下のものが用いられる。分子量が１００００を超えると硬化した樹脂層の耐擦傷性、耐摩耗性、耐薬品性、耐熱性等の表面物性が不足する。上記のアクリレートとメタアクリレートは共用し得るが、電離放射線での架橋硬化速度という点ではアクリレートの方が速い為、高速度、短時間で能率よく硬化させるという目的ではアクリレートの方が有利である。
【００３０】
カチオン重合性官能基を有するプレポリマーとしては、ビスフェノール型エポキシ樹脂、ノボラック型エポキシ樹脂、脂環型エポキシ樹脂等のエポキシ系樹脂、脂肪族系ビニルエーテル、芳香族系ビニルエーテル、ウレタン系ビニルエーテル、エステル系ビニルエーテル等のビニルエーテル系樹脂、環状エーテル化合物、スピロ化合物等のプレポリマーが挙げられる。
【００３１】
ラジカル重合性不飽和基を有する単量体の例としては、（メタ）アクリレート化合物の単官能単量体として、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ブチル（メタ）アクリレート、メトキシエチル（メタ）アクリレート、メトキシブチル（メタ）アクリレート、ブトキシエチル（メタ）アクリレート、２エチルヘキシル（メタ）アクリレート、Ｎ，Ｎ−ジメチルアミノメチル（メタ）アクリレート、Ｎ，Ｎ−ジメチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ−ジエチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ−ジエチルアミノプロピル（メタ）アクリレート、Ｎ，Ｎ−ジベンジルアミノエチル（メタ）アクリレート、ラウリル（メタ）アクリレート、イソボニル（メタ）アクリレート、エチルカルビトール（メタ）アクリレート、フェノキシエチル（メタ）アクリレート、フェノキシポリエチレングリコール（メタ）アクリレート、テトラヒドロフルフリル（メタ）アクリレート、メトキシプロピレングリコール（メタ）アクリレート、２−（メタ）アクリロイルオキシエチル−２−ヒドロキシプロピルフタレート、２−（メタ）アクリロイルオキシプロピルハイドロゲンテレフタレート等が挙げられる。
【００３２】
また、ラジカル重合性不飽和基を有する多官能単量体として、エチレングリコールジ（メタ）アクリレート、ジエチレングリコールジ（メタ）アクリレート、トリエチレングリコールジ（メタ）アクリレート、プロピレングリコールジ（メタ）アクリレート、ジプロピレングリコール（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、１，６ヘキサンジオールジ（メタ）アクリレート、１，９−ノナンジオールジ（メタ）アクリレート、テトラエチレングリコールジ（メタ）アクリレート、トリプロピレングリコールジ（メタ）アクリレート、ビスフェノール−Ａ−ジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、トリメチロールプロパンエチレンオキサイドトリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、グリセリンポリエチレンオキサイドトリ（メタ）アクリレート、トリス（メタ）アクリロイルオキシエチルフォスフェ−ト等が挙げられる。カチオン重合性官能基を有する単量体は、上記カチオン重合性官能基を有するプレポリマーの単量体を用いることができる。
【００３３】
上記の電離放射線硬化型樹脂は電子線を照射すれば十分に硬化するが、紫外線を照射して硬化させる場合には、増感剤として光重合開始剤を添加する。ラジカル重合性不飽和基を有する樹脂系の場合の光重合開始剤は、アセトフェノン類、ベンゾフェノン類、チオキサントン類、ベンゾイン、ベンゾインメチルエーテル、ミヒラーベンゾイルベンゾエート、ミヒラーケトン、ジフェニルサルファイド、ジベンジルジサルファイド、ジエチルオキサイト、トリフェニルビイミダゾール、イソプロピル−Ｎ，Ｎ−ジメチルアミノベンゾエート等を単独又は混合して用いることができる。又、カチオン重合性官能基を有する樹脂系の場合は、芳香族ジアゾニウム塩、芳香族スルホニウム塩、メタロセン化合物、ベンゾインスルホン酸エステル、フリールオキシスルホキソニウムジアリルヨードシル塩等を単独又は混合物として用いることができる。尚、これら光重合開始剤の添加量は一般に、電離放射線硬化型樹脂１００重量部に対して、０．１〜１０重量部程度である。また、この電離放射線硬化型樹脂で保護層を形成する方法としては、たとえば、この電離放射線硬化型樹脂を溶液化し、グラビアコート法、ロールコート法等の周知の塗布法で塗布することにより形成することができる。この場合の塗布量としては、固形分として概ね５〜３０μｍが適当であり、より好ましくは１５〜２５μｍである。
【００３４】
また、電離放射線硬化型樹脂から形成された表面保護層４４に、より一層耐擦傷性、耐磨耗性を付与する場合には、粉末状の酸化アルミニウム、炭化珪素、二酸化珪素、チタン酸カルシウム、チタン酸バリウム、マグネシウムパイロボレート、酸化亜鉛、窒化珪素、酸化ジルコニウム、酸化クロム、酸化鉄、窒化硼素、ダイアモンド、金剛砂、ガラス繊維等の研磨材を加えることにより達成することができる。この研磨材の電離放射線硬化型樹脂１００重量部に対する割合は１〜８０重量部が適当である。
【００３５】
なお、今までは表面保護層４４を装飾シート４の表面に設けることで説明してきたが、表面保護層４４は装飾シート４の表面に設けるのみならず、たとえば、図２に示した実施例において、プライマー層４３と表面保護層４４を設けない図５に示すような構成の装飾シート４””とし、図示はしないが、この装飾シート４””と合成樹脂製シート３と着色隠蔽層５と合板２とからなる積層体を作製すると共に前記装飾シート４””側から前記合成樹脂製シート３内にその最深部が位置する溝部６（図１参照）を切削加工により形成し、その後に前記積層体の表面にプライマー層４３と表面保護層４４を設けるようにしてもよいものである。このように前記積層体の表面に前記プライマー層４３と前記表面保護層４４を設ける構成とすることにより、特に前記溝部６（図１参照）の端面が前記プライマー層４３と前記表面保護層４４とで被覆されることになり、前記溝部６に外力が加わっても前記装飾シート４””の前記合成樹脂製シート３からの剥離を一層防止することができる。
【００３６】
【実施例】
次に、本発明について、以下に実施例を挙げてさらに詳しく説明する。
実施例１
〔装飾シートの作製〕
両面コロナ放電処理を施した６０μｍ厚さのオレフィン系樹脂シートの一方の面にアクリル−ウレタン系樹脂（アクリルポリオール１００重量部にヘキサメチレンジイソシアネート５重量部を添加した樹脂）溶液をグラビア塗布法で固形分が２ｇ／ｍ^２となるように塗布して印刷用プライマー層を形成し、該印刷用プライマー層上にアクリル−ウレタン系樹脂（アクリルポリオール１００重量部にヘキサメチレンジイソシアネート５重量部を添加した樹脂）からなる印刷インキを用いてグラビア印刷法でベタ柄印刷層と絵柄印刷層とを順次印刷して木目模様の印刷層を形成すると共に前記印刷層上に固形分で１０ｇ／ｍ^２となるようにウレタン系接着剤を塗布して接着剤層を形成し、該接着剤層上にプロピレン系樹脂を８０μｍ厚さになるようにＴダイ押出機で加熱溶融押出しして透明樹脂層を形成した。その後、前記透明樹脂層面にコロナ放電処理を施すと共に該コロナ放電処理にアクリル−ウレタン系樹脂（アクリルポリオール１００重量部にヘキサメチレンジイソシアネート５重量部を添加した樹脂）溶液をグラビア塗布法で固形分が１ｇ／ｍ^２となるように塗布して表面保護層用プライマー層を形成し、そして該表面保護層用プライマー層上にウレタンアクリレート系電離放射線硬化型樹脂をロールコート法で固形分が１５ｇ／ｍ^２となるように塗布・乾燥して未硬化の電離放射線硬化型樹脂層を形成し、該未硬化の電離放射線硬化型樹脂層に酸素濃度２００ｐｐｍ以下の環境下で電子線（加速電圧１２５ｋｅＶ、５Ｍｒａｄ）を照射して硬化させて電離放射線硬化型樹脂からなる表面保護層を形成すると共に、該表面保護層側から版深５０μｍの木目導管柄エンボス版でエンボス加工を行って、木目導管柄の凹凸模様を形成した装飾シートを作製した。
【００３７】
〔着色隠蔽層の形成〕
合成樹脂製シートとして厚さが３００μｍの透明な２軸延伸ポリエチレンテレフタレートフィルムを用い、該フィルムの一方の面にコロナ放電処理を施した後に、一方の面全面にグラビア印刷法にて黄色のウレタン系インキでベタ柄を印刷して着色隠蔽層を形成した。
【００３８】
〔装飾シートと着色隠蔽層を設けた合成樹脂製シートの貼合〕
上記で作製した装飾シートの裏面（凹凸模様を設けた面の反対面）にグラビア塗布法にて固形分が５ｇ／ｍ^２となるようにウレタン系接着剤を塗布して接着剤層を形成し、該接着剤層上に上記で作製した着色隠蔽層を設けた２軸延伸ポリエチレンテレフタレートフィルムからなる合成樹脂製シートを着色隠蔽層が外側に位置するように貼合して第１中間積層体を作製した。
【００３９】
〔床材用化粧材の作製〕
１２ｍｍ厚さの合板の一方の面に接着剤（中央理化工業製：リカボンドＢＡ−１０Ａ／ＢＡ−１０Ｂ＝１００／５）をウエット状態で１０ｇ／尺^２塗布し、上記で作製した第１中間積層体を前記着色隠蔽層面が前記接着剤面に位置するように貼合すると共に、冷圧プレス機（プレス圧：２ｋｇ／ｃｍ^２、プレス時間：１時間）にてプレスして第１中間化粧材を作製した。得られた第１中間化粧材を所定寸法に裁断すると共にテノーナーを用いてその最深部が前記合成樹脂製シート内に位置するように切削加工して溝部を形成した本発明の床材用化粧材を作製した。
【００４０】
実施例２
〔装飾シートと合成樹脂製シートの貼合〕
合成樹脂製シートとして厚さが３５０μｍの透明な２軸延伸ポリエチレンテレフタレートフィルムの一方の面にコロナ放電処理を施した後に、前記コロナ放電処理面にグラビア塗布法にて固形分が５ｇ／ｍ^２となるようにウレタン系接着剤を塗布して接着剤層を形成し、実施例１で作製した装飾シートをその裏面（凹凸模様を設けた面の反対面）が前記接着剤層に位置するように貼合して第２中間積層体を作製した。
【００４１】
〔着色隠蔽層の形成及び床材用化粧材の作製〕
１２ｍｍ厚さの合板の一方の面に下記する配合からなる接着剤をウエット状態で１０ｇ／尺^２塗布し、上記で作製した第２中間積層体を前記合成樹脂製シートが前記接着剤面に位置するように貼合すると共に、冷圧プレス機（プレス圧：２ｋｇ／ｃｍ^２、プレス時間：１時間）にてプレスして第２中間化粧材を作製した。得られた第２中間化粧材を所定寸法に裁断すると共にテノーナーを用いてその最深部が前記合成樹脂製シート内に位置するように切削加工して溝部を形成した本発明の床材用化粧材を作製した。本実施例の場合は、接着剤により形成される層が着色隠蔽層となる。

【００４２】
実施例３
〔着色隠蔽層の形成〕
合成樹脂製シートとして厚さが４００μｍの透明なポリプロピレンフィルムを用い、該フィルムの一方の面にコロナ放電処理を施した後に、前記コロナ放電処理面に固形分が１０ｇ／ｍ^２となるようにウレタン系接着剤を塗布して接着剤層を形成し、該接着剤層上に黄色に着色したプロピレン系樹脂をＴダイ押出機で加熱溶融押出しして２０μｍ厚さの着色隠蔽層を形成した。
【００４３】
〔装飾シートと着色隠蔽層を設けた合成樹脂製シートの貼合〕
実施例１で作製した装飾シートの裏面（（凹凸模様を設けた面の反対面）にグラビア塗布法にて固形分が５ｇ／ｍ^２となるようにウレタン系接着剤を塗布して接着剤層を形成し、該接着剤層上に上記で作製した着色隠蔽層を設けたポリプロピレンフィルムからなる合成樹脂製シートを着色隠蔽層が外側に位置するように貼合して第３中間積層体を作製した。
【００４４】
〔床材用化粧材の作製〕
１２ｍｍ厚さの合板の一方の面に接着剤（中央理化工業製：リカボンドＢＡ−１０Ａ／ＢＡ−１０Ｂ＝１００／５）をウエット状態で１０ｇ／尺^２塗布し、上記で作製した第３中間積層体を前記着色隠蔽層面が前記接着剤面に位置するように貼合すると共に、冷圧プレス機（プレス圧：２ｋｇ／ｃｍ^２、プレス時間：１時間）にてプレスして第３中間化粧材を作製した。得られた第３中間化粧材を所定寸法に裁断すると共にテノーナーを用いてその最深部が前記合成樹脂製シート内に位置するように切削加工して溝部を形成した本発明の床材用化粧材を作製した。
【００４５】
本発明の床材用化粧材は、実施例１〜３のいずれのものも、溝部を上部から見た場合に、溝部全体が着色隠蔽層の色に着色された状態を呈し、意匠性に優れた溝部とすることができた。
【００４６】
【発明の効果】
本発明の床材用化粧材は、今まで縷々説明したように、木質系基材として合板を用い、溝部の選択的塗布作業をなくすことができると共に、溝部の色ブレやダク等で意匠性を損なうことがないという優れた効果を奏するものである。また、耐水性はもとより耐キャスター性や耐衝撃性に優れ、毛羽立ちやササクレ等のない溝部や面取部とすることができる等の優れた効果を奏するものである。
【図面の簡単な説明】
【図１】本発明にかかる床材用化粧材の基本的構成を示す断面図である。
【図２】本発明にかかる床材用化粧材を構成する装飾シートの第１実施形態を示す断面図である。
【図３】本発明にかかる床材用化粧材を構成する装飾シートの第２実施形態を示す断面図である。
【図４】本発明にかかる床材用化粧材を構成する装飾シートの第３実施形態を示す断面図である。
【図５】本発明にかかる床材用化粧材を構成する装飾シートの第４実施形態を示す断面図である。
【符号の説明】
１　　　　　　　　　　　　　　　　　床材用化粧材
２　　　　　　　　　　　　　　　　　合板
３　　　　　　　　　　　　　　　　　合成樹脂製シート
４，４’，４”，４’’’，４””　　装飾シート
５　　　　　　　　　　　　　　　　　着色隠蔽層
６　　　　　　　　　　　　　　　　　溝部
４０，４０’　　　　　　　　　　　　オレフィン系熱可塑性樹脂シート
４０”　　　　　　　　　　　　　　　オレフィン系熱可塑性樹脂層
４１　　　　　　　　　　　　　　　　凹凸模様
４２　　　　　　　　　　　　　　　　ワイピングインキ
４３，４５　　　　　　　　　　　　　プライマー層
４４　　　　　　　　　　　　　　　　表面保護層
４６　　　　　　　　　　　　　　　　絵柄層
４７　　　　　　　　　　　　　　　　ベタ印刷層
４８　　　　　　　　　　　　　　　　接着剤層[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a decorative material for flooring used for floors of houses and the like, and more particularly to a decorative material for flooring excellent in caster resistance, impact resistance and water resistance.
[0002]
[Prior art]
Conventionally, as a flooring material, a wooden base material to which a decorative sheet having beautifully printed woodgrain pattern or the like is stuck is used. For example, a plywood laminated with a decorative sheet on which a beautiful pattern such as a grain pattern is applied, or a laminate obtained by laminating a plywood and a medium density fiberboard (MDF) has a woodgrain pattern or the like on the surface of the medium density fiberboard. A sheet to which a decorative sheet with beautiful printing is attached can be exemplified as a typical example.
[0003]
However, the former has problems such as poor caster resistance and impact resistance, and floors are usually provided with grooves or chamfers by cutting or the like for the purpose of improving design. A medium-density fiberboard (MDF), which has a problem of causing sores and the like, socks and stocking fibers are hooked on it, and there are problems such as color blurring and ducks, and the latter does not have the former problem described above. However, there is a problem that the medium-density fiberboard swells due to infiltration of water due to poor water resistance, thereby impairing the design. Furthermore, by applying a transparent or colored paint to the parts provided with grooves and chamfers in both the former and the latter, water resistance is imparted, or the difference in color between the parts to which the decorative sheet is attached is reduced. However, such a coating operation has to selectively apply only the groove and the chamfered portion, and has a problem that it takes much time and effort.
[0004]
[Problems to be solved by the invention]
Therefore, the present invention uses a plywood as a wooden base material, has excellent caster resistance and impact resistance as well as water resistance, has grooves and chamfers without fluffing or sacrifices, etc. An object of the present invention is to provide a decorative material for flooring materials that does not impair the properties. In particular, it is an object of the present invention to provide a decorative material for flooring, which eliminates the task of selectively applying grooves, and does not impair the design properties due to color blur or duck of the grooves.
[0005]
[Means for Solving the Problems]
In order to achieve the above object, the present inventor of the present invention described in claim 1 discloses a method in which a laminate having a thickness of 450 to 800 μm comprising a synthetic resin sheet and a decorative sheet is formed on a plywood by the synthetic resin. A flooring decorative material in which a sheet is laminated so that the sheet is located on the plywood side and a groove portion whose deepest portion is located in the synthetic resin base sheet from the decorative sheet side is formed by cutting. And a colored concealing layer provided between the synthetic resin base sheet and the synthetic resin base sheet.
[0006]
According to a second aspect of the present invention, in the decorative material for flooring according to the first aspect, the colored concealing layer is a printing layer provided on the surface of the synthetic resin sheet on the plywood side. It is assumed that.
[0007]
According to a third aspect of the present invention, in the decorative material for flooring according to the first aspect, the colored concealing layer is a colored resin layer provided on a surface of the synthetic resin sheet on the plywood side. It is a feature.
[0008]
By adopting the configuration according to any one of claims 1 to 3, water resistance, caster resistance, and excellent impact resistance, the grooves and chamfers formed by the cutting process are free of fuzz, rust, and the like, Further, it is possible to provide a decorative material for flooring, which does not impair the design property due to color blur, duck or the like generated when using plywood. In particular, it is possible to provide a decorative material for flooring in which the selective application of the groove is eliminated, and the design is not impaired due to color blur or duck of the groove.
[0009]
The present invention according to claim 4 is the decorative material for flooring according to any one of claims 1 to 3, wherein a surface protective layer is formed on a surface of the decorative sheet. is there. With this configuration, a decorative material for flooring having excellent surface properties such as scratch resistance, abrasion resistance, and stain resistance can be obtained.
[0010]
BEST MODE FOR CARRYING OUT THE INVENTION
The present invention will be described in detail below with reference to the drawings and the like.
FIG. 1 is a cross-sectional view showing a basic configuration of a decorative material for flooring according to the present invention. FIG. 2 is a cross-sectional view showing a first embodiment of a decorative sheet constituting the decorative material for flooring according to the present invention. FIG. 4 is a sectional view showing a second embodiment of the decorative sheet constituting the decorative material for flooring according to the present invention, and FIG. 4 is a sectional view showing a third embodiment of the decorative sheet constituting the decorative material for flooring according to the present invention. Drawing 5 and Drawing 5 are sectional views showing a 4th embodiment of a decorative sheet which constitutes a decorative material for flooring concerning the present invention. In the figure, 1 is decorative material for flooring, 2 is plywood, 3 is synthetic resin. 4, 4 ', 4 ", 4'", 4 "" are decorative sheets, 5 is a color concealing layer, 6 is a groove, 40 and 40 'are olefin-based thermoplastic resin sheets, and 40 "is olefin-based. A thermoplastic resin layer, 41 is an uneven pattern, 42 is a wiping ink, 43 and 45 are primer layers, and 44 is a surface protection. Layer 46 is pattern layer, 47 is solid printing layer, 48 denotes an adhesive layer, respectively.
[0011]
FIG. 1 is a cross-sectional view showing a basic structure of a decorative material for flooring according to the present invention. The decorative material for flooring 1 is a plywood 2 on which a colored concealing layer 5, a synthetic resin sheet 3, and a decorative sheet 4 are provided. The grooves 6 are provided in order from the decorative sheet 4 side in the synthetic resin sheet 3 at the deepest position by cutting. The synthetic resin sheet 3 and the decorative sheet 4 are designed so that the laminated thickness is 450 to 800 μm. The reason for this is that the groove 6 provided by the cutting process has a depth of at least 400 μm and the productivity is usually high because the synthetic resin sheet 3 and the decorative sheet 4 are laminated on the plywood 2. In consideration of the above, it is important that the laminate of the synthetic resin sheet 3 and the decorative sheet 4 can be handled in the form of a roll. From these, it is inevitable that the laminated thickness of the synthetic resin sheet 3 and the decorative sheet 4 is increased. Is designed to be 450 to 800 μm. With such a configuration, water resistance, caster resistance, and impact resistance are excellent, and the grooves and chamfers formed by the cutting process are free of fuzz, rust, etc., and also occur when plywood is used. It is possible to obtain a decorative material for flooring which does not impair the design properties due to color blur or ducks. In particular, it is possible to provide a decorative material for flooring in which the selective application of the groove is eliminated, and the design is not impaired due to color blur or duck of the groove.
[0012]
First, the synthetic resin sheet 3 constituting the decorative material 1 for flooring will be described. As the resin forming the synthetic resin sheet 3, a resin containing no halogen element in its molecular structure is suitable in consideration of recent environmental problems. For example, polypropylene, ethylene-vinyl alcohol copolymer, polymethylene, and polymethylene Methylpentene, polyethylene terephthalate, polyalkylene terephthalate having high heat resistance [for example, polyethylene terephthalate in which ethylene glycol is partially substituted with 1,4-cyclohexanedimethanol or diethylene glycol, so-called trade name PET-G (Eastman Chemical Company) Polybutylene terephthalate, polyethylene naphthalate, polyethylene naphthalate-isophthalate copolymer, polycarbonate, polyarylate, polyimide, polystyrene, polyamide, ABS These resins may be used alone or as a mixture, and the synthetic resin sheet 3 composed of these resins may be a single layer. May also be a multilayer. The thickness of the synthetic resin sheet 3 is also related to the thickness of the decorative sheet 4 described later. However, as described above, the groove 6 provided by cutting has a depth of at least 400 μm, Considering that it can be handled by the above, it is generally appropriate that the thickness is 300 to 600 μm. Further, the synthetic resin sheet 3 may be subjected to an easy adhesion treatment such as a corona discharge treatment, an ozone treatment, or a plasma treatment on a required surface as needed.
[0013]
Next, the colored concealing layer 5 constituting the floor covering decorative material 1 will be described. The colored concealing layer 5 can be formed by printing a solid pattern on one surface of the synthetic resin sheet 3 using ink by a known printing method such as gravure printing, offset printing, or silk screen printing. Further, it can be formed on one surface of the synthetic resin sheet 3 by, for example, heat-melting and extruding a thermoplastic resin mixed with an organic pigment and / or an inorganic pigment using a T-die extruder. As a method for mixing the pigment with the thermoplastic resin, either a method in which the two are melt-blended in advance using a Banbury mixer or the like and a master batch is formed to a predetermined mixing ratio, or a method in which the pigment is directly mixed with the thermoplastic resin. There may be. As the ink, chlorinated polyethylene, chlorinated polyolefin such as chlorinated polypropylene, polyester, polyurethane composed of isocyanate and polyol, polyacryl, polyvinyl acetate, polyvinyl chloride, vinyl chloride-vinyl acetate copolymer are used as vehicles. One or more kinds of coalesce, cellulose-based resin, polyamide-based resin, etc. may be used as a mixture, and pigments, solvents, various auxiliaries and the like may be added thereto to form an ink. In consideration of the adhesiveness to the printing surface and the like, a mixture of at least one of polyester, polyurethane composed of isocyanate and polyol, polyacryl, polyamide resin and the like is suitable. The thermoplastic resin mixed with an organic pigment and / or an inorganic pigment is not particularly limited. For example, an olefin-based thermoplastic resin such as polyethylene or polypropylene is suitable in consideration of cost and processability. In addition, the laminating method is not only formed by heat-melting and extruding one surface of the synthetic resin sheet 3 with a T-die extruder, but also, for example, using a thermoplastic resin in which an organic pigment and / or an inorganic pigment are previously mixed. Alternatively, a colored concealing sheet may be prepared beforehand, and this and the synthetic resin sheet 3 may be laminated by a known dry lamination method.
[0014]
As another method of forming the colored concealing layer 5, as the synthetic resin sheet 3, for example, a multi-manifold type multilayer extruder is used to produce a sheet comprising at least two layers, and one of the outer layers is formed of an organic pigment. And / or a layer colored with an inorganic pigment.
[0015]
Next, the decorative sheet 4 constituting the floor covering decorative material 1 will be described. Examples of the base sheet constituting the decorative sheet 4 include thin paper, woodfree paper, kraft paper, Japanese paper, titanium paper, resin-impregnated paper, paper between sheets, wood fiber, glass fiber, asbestos, polyester fiber, and vinylon fiber. , A woven or nonwoven fabric made of fibers such as rayon fibers, or one or more kinds of laminates such as sheets made of synthetic resin such as polyolefin, polyester, polyacryl, polyamide, polyurethane, and polystyrene. An appropriate thickness is approximately 20 to 300 μm. Further, the base material may be colored by adding a pigment or the like to a necessary layer as needed, or may be subjected to a corona discharge treatment, a plasma treatment, or an easy adhesion treatment such as an ozone treatment on a necessary surface. Things.
[0016]
FIG. 2 is a cross-sectional view showing a first embodiment of a decorative sheet constituting a decorative material for flooring according to the present invention, in which a decorative sheet 4 ′ is embossed on one surface of a transparent olefin-based thermoplastic resin sheet 40. After processing is performed to provide an uneven pattern 41, a wiping process is performed from above to fill the recesses of the uneven pattern 41 with the wiping ink 42, and then a primer layer 43 is provided on the entire exposed surface, and A surface protection layer 44 is formed, and a picture layer 46 and a solid printing layer 47 are formed on the other surface of the olefin-based thermoplastic resin sheet 40 via a primer layer 45.
[0017]
FIG. 3 is a cross-sectional view showing a second embodiment of the decorative sheet constituting the decorative material for flooring according to the present invention. The decorative sheet 4 ″ is provided on one surface of a colored olefin-based thermoplastic resin sheet 40 ′. A primer layer 45 is provided, a solid printing layer 47 and a pattern layer 46 are sequentially formed on the primer layer 45 by printing, and further formed on the pattern layer 46 with a known dry lamination adhesive such as a two-component curable urethane resin. The transparent olefin-based thermoplastic resin sheet 40 or the transparent olefin-based thermoplastic resin layer 40 ″ is laminated by a well-known dry lamination method or a T-die extrusion method via the adhesive layer 48, and the olefin-based thermoplastic resin sheet is formed. A primer layer 43 is provided on the entire surface of the exposed surface of the olefin-based thermoplastic resin layer 40 ″, and a surface protective layer 44 is formed on the primer layer 43. It was done.
[0018]
FIG. 4 is a sectional view showing a third embodiment of the decorative sheet constituting the decorative material for flooring according to the present invention, wherein the decorative sheet 4 ″ ″ is one of the colored olefin-based thermoplastic resin sheets 40 ′. A primer layer 45 is provided on the surface, a solid printing layer 47 and a picture layer 46 are sequentially printed on the primer layer 45, and a well-known dry lamination adhesive such as a two-component curable urethane resin is further formed on the picture layer 46. A transparent olefin-based thermoplastic resin sheet 40 or a transparent olefin-based thermoplastic resin layer 40 ″ is laminated by a well-known dry lamination method or a T-die extrusion method via an adhesive layer 48 formed by The surface of the resin sheet 40 or the olefin-based thermoplastic resin layer 40 ″ is embossed to provide an uneven pattern 41, and a wiping process is performed thereon. After the wiping ink 42 is filled in the concave portions of the uneven pattern 41, a primer layer 43 is provided on the entire exposed surface, and a surface protective layer 44 is formed on the primer layer 43. Although the decorative sheet 4 using the base sheet has been described, the decorative sheet 4 is not limited to this, and may be, for example, a veneer.
[0019]
The primer layer 43 is provided for the purpose of improving the adhesive strength between the olefin-based thermoplastic resin sheet 40 or the olefin-based thermoplastic resin layer 40 ″ and the surface protective layer 44. It is desirable from the viewpoint of adhesive strength to provide 43. Further, the primer layer 45 shown in Fig. 2 to 4 is composed of the olefin-based thermoplastic resin sheets 40 to 40 'and the printing layers such as the pattern layer 46 and the solid printing layer 47. It is provided for the purpose of improving the adhesiveness, and is preferably formed in the same manner using the same resin as the primer layer 43 in the same meaning as the primer layer 43.
[0020]
The primer layers 43 and 45 are for improving the adhesiveness of the surface of the olefin-based

thermoplastic resin sheet

40, 40 ′, 40 ″ as described above, and as the resin used for this, an ester resin, a urethane resin, An acrylic resin, a polycarbonate resin, a vinyl chloride-vinyl acetate copolymer, a polyvinyl butyral resin, a nitrocellulose resin, and the like can be given, and these resins can be used alone or as a mixture to form a coating composition, or an ink composition, and a roll. It can be formed using an appropriate application means such as a coating method or a gravure printing method.
[0021]
Further, the concavo-convex pattern 41 can be formed by heating press, hairline processing, or the like. Examples of the uneven pattern 41 include a conduit groove, surface unevenness of a stone plate, texture of a cloth surface, satin finish, grain, a hairline, and a linear groove.
[0022]
In addition, the pattern layer 46 and the solid printing layer 47 can be generally formed using ink by a known printing method such as gravure printing, offset printing, or silk screen printing. The pattern layer 46 is, for example, a wood pattern, a stone pattern, a cloth pattern, a leather pattern, a geometric pattern, a character, a symbol, a line drawing, or various abstract patterns. Solid printed with a colored ink having the following formula: 2 to 4 show a configuration in which both the picture layer 46 and the solid printing layer 47 are provided, but either one of them may be used.
[0023]
Further, the ink used for the picture layer 46 and the solid printing layer 47 or the wiping ink 42 may be formed using the same ink as described for the color concealing layer 5, and the description is omitted.
[0024]
The decorative layers 4 ′, 4 ″, 4 ′ ″ shown in FIGS. 2 to 4 are examples of the decorative sheet 4 constituting the decorative material for flooring according to the present invention. The present invention is not limited to this as long as it does not depart from the gist of the invention.For example, a solid printing layer and a pattern layer are sequentially formed on one side of thin paper by printing, and a surface protection layer is formed on the entire surface on which the pattern layer is formed. It may be a decorative layer having a configuration provided with.
[0025]
Next, the surface protection layer 44 provided on the surface of the decorative sheet 4 will be described. The surface protective layer 44 is provided for imparting surface properties such as abrasion resistance, abrasion resistance, water resistance, and stain resistance required for the floor covering decorative material 1 (see FIG. 1). As the resin for forming the surface protective layer 44, it is appropriate to use a curable resin such as a thermosetting resin or an ionizing radiation curable resin.
[0026]
Examples of the thermosetting resin include unsaturated polyester resin, polyurethane resin (including two-component curing polyurethane), epoxy resin, amino alkyd resin, phenol resin, urea resin, diallyl phthalate resin, melamine resin, guanamine resin, and melamine-urea. Co-condensation resins, silicon resins, polysiloxane resins and the like can be mentioned. If necessary, a curing agent such as a crosslinking agent or a polymerization initiator, or a polymerization accelerator may be added to the resin. For example, as a curing agent, an isocyanate or an organic sulfonate is added to an unsaturated polyester resin or a polyurethane resin, an organic amine is added to an epoxy resin, a peroxide such as methyl ethyl ketone peroxide, or azoisobutyl nitrile. Is added to the unsaturated polyester resin. As a method of forming a surface protective layer with the above-mentioned thermosetting resin, for example, the above-mentioned thermosetting resin is converted into a solution, applied by a known coating method such as a roll coating method, a gravure coating method, and dried and cured. Can be formed. The coating amount is suitably about 5 to 30 μm in solid content, and preferably 15 to 25 μm.
[0027]
The ionizing radiation-curable resin is a resin that undergoes a cross-linking polymerization reaction upon irradiation with ionizing radiation to change into a three-dimensional polymer structure. Ionizing radiation refers to electromagnetic waves or charged particle beams having energy quanta that can polymerize and crosslink molecules, and include visible light, ultraviolet light (near ultraviolet light, vacuum ultraviolet light, etc.), X-rays, electron beams, ion beams, and the like. is there. Usually, ultraviolet rays or electron beams are used. Ultraviolet light sources, high pressure mercury lamps, low pressure mercury lamps, carbon arc lamps, black light fluorescent lamps, and metal halide lamp lamps can be used as the ultraviolet light source. As the wavelength of the ultraviolet light, a wavelength range of 190 to 380 nm can be used. As the electron beam source, various electron beam accelerators such as Cockcroft-Wald type, Van degraft type, resonance transformer type, insulating core transformer type, linear type, dynamitron type and high frequency type can be used. As an electron beam to be used, an electron beam of 100 to 1000 keV, preferably 100 to 300 keV is used. The irradiation amount of the electron beam is usually about 2 to 15 Mrad.
[0028]
The ionizing radiation-curable resin is a monomer having a radically polymerizable unsaturated group such as a (meth) acryloyl group or a (meth) acryloyloxy group, or a cationically polymerizable functional group such as an epoxy group in a molecule, It is composed of a prepolymer or a polymer (hereinafter, these are collectively referred to as compounds). These monomers, prepolymers, and polymers may be used alone or as a mixture of two or more. In this specification, (meth) acrylate is used to mean acrylate or methacrylate.
[0029]
Examples of the prepolymer having a radical polymerizable unsaturated group include polyester (meth) acrylate, urethane (meth) acrylate, epoxy (meth) acrylate, melamine (meth) acrylate, triazine (meth) acrylate, and polyvinylpyrrolidone. This prepolymer usually has a molecular weight of about 10,000 or less. When the molecular weight exceeds 10,000, the cured resin layer has insufficient surface properties such as scratch resistance, abrasion resistance, chemical resistance, and heat resistance. Although the above acrylate and methacrylate can be used in common, acrylate is faster in terms of the rate of crosslinking and curing by ionizing radiation. Therefore, acrylate is more advantageous for the purpose of efficiently curing at a high speed and in a short time.
[0030]
Examples of the prepolymer having a cationically polymerizable functional group include epoxy resins such as bisphenol-type epoxy resins, novolak-type epoxy resins, and alicyclic-type epoxy resins, aliphatic vinyl ethers, aromatic vinyl ethers, urethane vinyl ethers, and ester vinyl ethers. And prepolymers such as cyclic ether compounds and spiro compounds.
[0031]
Examples of the monomer having a radical polymerizable unsaturated group include, as monofunctional monomers of a (meth) acrylate compound, methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, methoxyethyl ( (Meth) acrylate, methoxybutyl (meth) acrylate, butoxyethyl (meth) acrylate, 2ethylhexyl (meth) acrylate, N, N-dimethylaminomethyl (meth) acrylate, N, N-dimethylaminoethyl (meth) acrylate, N , N-diethylaminoethyl (meth) acrylate, N, N-diethylaminopropyl (meth) acrylate, N, N-dibenzylaminoethyl (meth) acrylate, lauryl (meth) acrylate, isobonyl (meth) acrylate, ethyl carbitol ( Me A) acrylate, phenoxyethyl (meth) acrylate, phenoxypolyethylene glycol (meth) acrylate, tetrahydrofurfuryl (meth) acrylate, methoxypropylene glycol (meth) acrylate, 2- (meth) acryloyloxyethyl-2-hydroxypropyl phthalate, -(Meth) acryloyloxypropyl hydrogen terephthalate and the like.
[0032]
Examples of the polyfunctional monomer having a radical polymerizable unsaturated group include ethylene glycol di (meth) acrylate, diethylene glycol di (meth) acrylate, triethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, and diethylene glycol di (meth) acrylate. Propylene glycol (meth) acrylate, neopentyl glycol di (meth) acrylate, 1,6 hexanediol di (meth) acrylate, 1,9-nonanediol di (meth) acrylate, tetraethylene glycol di (meth) acrylate, tripropylene Glycol di (meth) acrylate, bisphenol-A-di (meth) acrylate, trimethylolpropane tri (meth) acrylate, trimethylolpropane ethylene oxide tri (meth) acrylate Pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, glycerin polyethylene oxide tri (meth) acrylate, tris (meth) acryloyloxyethyl Phosphate and the like. As the monomer having a cationically polymerizable functional group, a prepolymer monomer having the above cationically polymerizable functional group can be used.
[0033]
The above ionizing radiation-curable resin cures sufficiently when irradiated with an electron beam, but when it is cured by irradiating ultraviolet rays, a photopolymerization initiator is added as a sensitizer. The photopolymerization initiator in the case of a resin having a radical polymerizable unsaturated group is acetophenones, benzophenones, thioxanthones, benzoin, benzoin methyl ether, Michler benzoyl benzoate, Michler ketone, diphenyl sulfide, dibenzyl disulfide, diethyl Oxite, triphenylbiimidazole, isopropyl-N, N-dimethylaminobenzoate and the like can be used alone or in combination. In the case of a resin having a cationically polymerizable functional group, an aromatic diazonium salt, an aromatic sulfonium salt, a metallocene compound, a benzoinsulfonic acid ester, a freeloxysulfoxonium diallyliodosyl salt, or the like is used alone or as a mixture. be able to. In addition, the addition amount of these photopolymerization initiators is generally about 0.1 to 10 parts by weight based on 100 parts by weight of the ionizing radiation-curable resin. As a method of forming a protective layer with the ionizing radiation-curable resin, for example, the protective layer is formed by applying a solution to the ionizing radiation-curable resin and applying the solution by a known coating method such as a gravure coating method or a roll coating method. be able to. In this case, the coating amount is suitably about 5 to 30 μm as a solid content, and more preferably 15 to 25 μm.
[0034]
When the surface protective layer 44 formed of the ionizing radiation-curable resin is to be further provided with scratch resistance and abrasion resistance, powdery aluminum oxide, silicon carbide, silicon dioxide, calcium titanate, It can be achieved by adding an abrasive such as barium titanate, magnesium pyroborate, zinc oxide, silicon nitride, zirconium oxide, chromium oxide, iron oxide, boron nitride, diamond, gold sand and glass fiber. An appropriate ratio of the abrasive to 100 parts by weight of the ionizing radiation-curable resin is 1 to 80 parts by weight.
[0035]
Although the description has been given by providing the surface protective layer 44 on the surface of the decorative sheet 4 so far, the surface protective layer 44 is not only provided on the surface of the decorative sheet 4 but also in the embodiment shown in FIG. A decorative sheet 4 ″ ″ having a configuration as shown in FIG. 5 without the primer layer 43 and the surface protective layer 44 is provided, and although not shown, the decorative sheet 4 ″ ″, the synthetic resin sheet 3 and the colored concealment layer 5 are not shown. A laminated body made of the plywood 2 is produced, and a groove 6 (see FIG. 1), the deepest portion of which is located in the synthetic resin sheet 3 from the decorative sheet 4 ″ ″ side, is formed by cutting, and thereafter, The primer layer 43 and the surface protection layer 44 may be provided on the surface of the laminate. By providing the primer layer 43 and the surface protection layer 44 on the surface of the laminate in this way, particularly, the end face of the groove 6 (see FIG. 1) is formed by the primer layer 43 and the surface protection layer 44. Thus, even if an external force is applied to the groove 6, the decorative sheet 4 "" can be further prevented from peeling from the synthetic resin sheet 3.
[0036]
【Example】
Next, the present invention will be described in more detail with reference to the following examples.
Example 1
(Preparation of decorative sheet)
An acryl-urethane resin (a resin obtained by adding 5 parts by weight of hexamethylene diisocyanate to 100 parts by weight of an acrylic polyol) is solidified by gravure coating on one surface of an olefin resin sheet having a thickness of 60 μm that has been subjected to a corona discharge treatment on both sides. 2 g / m per minute ² Is applied so as to form a printing primer layer, and a printing ink composed of an acrylic-urethane resin (a resin obtained by adding 5 parts by weight of hexamethylene diisocyanate to 100 parts by weight of an acrylic polyol) is formed on the printing primer layer. The solid pattern printing layer and the pattern printing layer are sequentially printed by a gravure printing method to form a wood-grained printing layer and a solid content of 10 g / m on the printing layer. ² A urethane-based adhesive is applied so as to form an adhesive layer, and a propylene-based resin is heated and melt-extruded with a T-die extruder to a thickness of 80 μm on the adhesive layer to form a transparent resin layer. Formed. Thereafter, the surface of the transparent resin layer is subjected to a corona discharge treatment, and a solution of an acryl-urethane resin (a resin obtained by adding 5 parts by weight of hexamethylene diisocyanate to 100 parts by weight of an acrylic polyol) is subjected to a gravure coating method. 1g / m ² To form a primer layer for a surface protective layer, and a urethane acrylate-based ionizing radiation-curable resin having a solid content of 15 g / m2 on the surface protective layer by a roll coating method. ² An uncured ionizing radiation-curable resin layer is formed by applying and drying such that the electron beam (acceleration voltage 125 keV, 5 Mrad) is applied to the uncured ionizing radiation-curable resin layer in an environment having an oxygen concentration of 200 ppm or less. To form a surface protective layer made of an ionizing radiation curable resin, and embossing with a 50 μm deep wood grain pipe pattern embossing plate from the surface protective layer side to obtain an uneven pattern of the wood grain pipe pattern. Was formed.
[0037]
(Formation of colored concealing layer)
A transparent biaxially stretched polyethylene terephthalate film having a thickness of 300 μm is used as a synthetic resin sheet, and one surface of the film is subjected to a corona discharge treatment. A solid pattern was printed with the ink to form a colored concealing layer.
[0038]
[Lamination of synthetic resin sheet provided with decorative sheet and colored concealing layer]
The solid content is 5 g / m by the gravure coating method on the back surface (the surface opposite to the surface provided with the uneven pattern) of the decorative sheet prepared above. ² A urethane-based adhesive is applied so as to form an adhesive layer, and a synthetic resin sheet made of a biaxially stretched polyethylene terephthalate film provided with the colored concealing layer prepared above on the adhesive layer is colored and concealed. The first intermediate laminate was prepared by laminating the layers so that the layers were located on the outside.
[0039]
[Production of decorative materials for flooring]
An adhesive (manufactured by Chuo Rika Kogyo Co., Ltd .: Ricabond BA-10A / BA-10B = 100/5) is wet on one surface of a 12 mm thick plywood in a wet state at a rate of 10 g / size. ² It is applied and the first intermediate laminate produced above is bonded so that the surface of the colored concealing layer is positioned on the surface of the adhesive, and a cold press machine (press pressure: 2 kg / cm). ² , Press time: 1 hour) to produce a first intermediate decorative material. The obtained first intermediate decorative material is cut into a predetermined size, and is cut using a tenoner so that the deepest portion is located in the synthetic resin sheet to form a groove portion. Was prepared.
[0040]
Example 2
[Lamination of decorative sheet and synthetic resin sheet]
After subjecting one surface of a transparent biaxially stretched polyethylene terephthalate film having a thickness of 350 μm as a synthetic resin sheet to a corona discharge treatment, the corona discharge treated surface has a solid content of 5 g / m 2 by a gravure coating method. ² A urethane-based adhesive is applied to form an adhesive layer so that the back surface (the surface opposite to the surface provided with the uneven pattern) of the decorative sheet prepared in Example 1 is positioned on the adhesive layer. To produce a second intermediate laminate.
[0041]
(Formation of colored concealing layer and preparation of decorative material for flooring)
An adhesive having the following composition is applied to one surface of a 12 mm thick plywood in a wet state at 10 g / size. ² After applying, the second intermediate laminate produced above is bonded so that the synthetic resin sheet is positioned on the adhesive surface, and a cold press machine (press pressure: 2 kg / cm). ² , Press time: 1 hour) to produce a second intermediate decorative material. The obtained second intermediate decorative material is cut into a predetermined size and is cut using a tenoner so that the deepest portion is located in the synthetic resin sheet to form a groove portion. Was prepared. In the case of this embodiment, the layer formed by the adhesive becomes the colored concealing layer.

[0042]
Example 3
(Formation of colored concealing layer)
A transparent polypropylene film having a thickness of 400 μm was used as a synthetic resin sheet, and after one surface of the film was subjected to corona discharge treatment, the solid content of the corona discharge treated surface was 10 g / m 2. ² A urethane-based adhesive is applied to form an adhesive layer, and a yellow-colored propylene-based resin is heated and melt-extruded on the adhesive layer by a T-die extruder to form a colored concealing layer having a thickness of 20 μm. Was formed.
[0043]
[Lamination of synthetic resin sheet provided with decorative sheet and colored concealing layer]
The solid content was 5 g / m2 by the gravure coating method on the back surface (the surface opposite to the surface provided with the uneven pattern) of the decorative sheet prepared in Example 1. ² A urethane-based adhesive is applied so as to form an adhesive layer, and a synthetic resin sheet made of a polypropylene film provided with the colored concealing layer prepared above on the adhesive layer is coated with the colored concealing layer on the outside. A third intermediate laminate was prepared by laminating so as to be positioned.
[0044]
[Production of decorative materials for flooring]
An adhesive (manufactured by Chuo Rika Kogyo Co., Ltd .: Ricabond BA-10A / BA-10B = 100/5) is wet on one surface of a 12 mm thick plywood in a wet state at a rate of 10 g / size. ² It is applied and the third intermediate laminate prepared above is bonded so that the surface of the colored concealing layer is positioned on the surface of the adhesive, and a cold press machine (press pressure: 2 kg / cm). ² , Press time: 1 hour) to produce a third intermediate decorative material. The flooring decorative material of the present invention, wherein the obtained third intermediate decorative material is cut into a predetermined size and is cut using a tenoner so that the deepest portion is located in the synthetic resin sheet to form a groove. Was prepared.
[0045]
The flooring decorative material of the present invention, in any of Examples 1 to 3, when the groove is viewed from above, exhibits a state in which the entire groove is colored with the color of the colored concealing layer, and is excellent in design. Groove was formed.
[0046]
【The invention's effect】
As described in detail above, the decorative material for flooring of the present invention uses plywood as a wooden base material, and can eliminate the selective application work of the groove portion, and can improve the design of the groove portion due to color blur and duck. This has an excellent effect of not impairing the image quality. Further, it is excellent in caster resistance and impact resistance as well as in water resistance, and has excellent effects such as being able to form grooves and chamfers without fluffing or crepe.
[Brief description of the drawings]
FIG. 1 is a sectional view showing a basic configuration of a decorative material for flooring according to the present invention.
FIG. 2 is a sectional view showing a first embodiment of a decorative sheet constituting the decorative material for flooring according to the present invention.
FIG. 3 is a sectional view showing a second embodiment of the decorative sheet constituting the decorative material for flooring according to the present invention.
FIG. 4 is a cross-sectional view showing a third embodiment of the decorative sheet constituting the decorative material for flooring according to the present invention.
FIG. 5 is a cross-sectional view showing a fourth embodiment of the decorative sheet constituting the decorative material for flooring according to the present invention.
[Explanation of symbols]
1 Cosmetic materials for flooring
2 plywood
3 Synthetic resin sheet
4,4 ', 4 ", 4'", 4 "" decorative sheet
5 Color hiding layer
6 groove
40,40 'olefin-based thermoplastic resin sheet
40 "olefinic thermoplastic resin layer
41 Uneven pattern
42 Wiping ink
43,45 Primer layer
44 Surface protective layer
46 Picture layer
47 Solid printing layer
48 adhesive layer

Claims

合板上に、合成樹脂製シートと装飾シートとからなる厚さが４５０〜８００μｍの積層体を前記合成樹脂製シートが前記合板側に位置するように積層すると共に前記装飾シート側から前記合成樹脂製シート内にその最深部が位置する溝部が切削加工により形成された床材用化粧材において、前記合板と前記合成樹脂製シートの間に着色隠蔽層が設けられていることを特徴とする床材用化粧材。On a plywood, a laminate of a synthetic resin sheet and a decorative sheet having a thickness of 450 to 800 μm is laminated so that the synthetic resin sheet is positioned on the plywood side, and the synthetic resin sheet is formed from the decorative sheet side. A floor covering decorative material in which a groove at the deepest portion thereof is formed by cutting in a sheet, wherein a colored concealing layer is provided between the plywood and the synthetic resin sheet. Cosmetics.

前記着色隠蔽層が前記合成樹脂製シートの前記合板側の面に設けられた印刷層であることを特徴とする請求項１記載の床材用化粧材。The floor covering decorative material according to claim 1, wherein the colored concealing layer is a printed layer provided on the surface of the synthetic resin sheet on the plywood side.

前記着色隠蔽層が前記合成樹脂製シートの前記合板側の面に設けられた着色樹脂層であることを特徴とする請求項１記載の床材用化粧材。The decorative material for flooring according to claim 1, wherein the colored concealing layer is a colored resin layer provided on a surface of the synthetic resin sheet on the plywood side.

前記装飾シートの表面に表面保護層が形成されていることを特徴とする請求項１〜３のいずれかに記載の床材用化粧材。The decorative material for flooring according to any one of claims 1 to 3, wherein a surface protective layer is formed on a surface of the decorative sheet.