JP2003193176A - 耐熱球状黒鉛鋳鉄 - Google Patents
耐熱球状黒鉛鋳鉄Info
- Publication number
- JP2003193176A JP2003193176A JP2002337083A JP2002337083A JP2003193176A JP 2003193176 A JP2003193176 A JP 2003193176A JP 2002337083 A JP2002337083 A JP 2002337083A JP 2002337083 A JP2002337083 A JP 2002337083A JP 2003193176 A JP2003193176 A JP 2003193176A
- Authority
- JP
- Japan
- Prior art keywords
- cast iron
- weight
- heat
- resistant spheroidal
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
改善し、優れた高温強度と耐酸化性を有する新たな耐熱
球状黒鉛鋳鉄を提供する。 【解決手段】 C:2.5〜3.0重量%、Si:2.
0〜3.0重量%、Mn:0.8〜1.2重量%、M
o:0.15〜0.4重量%、Cr:1.7〜3.0重
量%、Ni:17.0〜20.0重量%を必須成分と
し、かつP:0.1重量%以下、S:0.02重量%以
下、Mg:0.06重量%以下含んでもよく、残部をF
eとする構成元素からなって、球状化率が75〜100
%、黒鉛サイズが10〜70μm、セメンタイト析出量
が全組織中5%以下であるオーステナイト系組織を有し
ている。
Description
鉄、詳しくは、鉄を基材とし、これにC、Si、Mn、
Mo、Cr、およびNiを含み、耐熱性および高温にお
ける耐酸化性に優れる耐熱球状黒鉛鋳鉄に関する。
ゾートマニホールド)は、各気筒のポート出口から集合
して一本の排気管につなぐ役目をしており、ヘッドから
出る排気ガスを最も先に受ける個所に置かれているの
で、エンジンの出力と密接な関係を有している。
CD50M、FCD45F、FCD−HおよびFCD−
50HSなど高温耐酸化鋳鉄(表1参照)であり、高温
における物性向上と耐酸化性のために通常の球状黒鉛鋳
鉄材よりSi成分、Mo成分などが多く使用されてい
る。
温度が約630〜760℃の範囲に使用されたとき、引
張り強度は約75MPaとなり、許容される使用領域の
限界である。しかし、近年自動車の出力は増大傾向にあ
り、それに伴い排気温度は730〜900℃、あるいは
それ以上と高くなり、自動車用排気系条件は益々過酷な
状態になって、これまでの高温耐酸化鋳鉄では対応が難
しくなっている。
ビンハウジングなどの排気系部品で、従来に比べて高い
温度で使用できる耐熱鋳鉄としては、例えば、鋳造性に
優れたフェライト系耐熱鋳鋼およびそれからなる排気系
部品を提案があり、Wおよび/またはMo:1.0〜
5.0%、Nb:0.40〜6.0%、更にNi、Nを
組み合わせて含有させることで、通常のα相のほかにγ
相からα+炭化物に変態した相を得た〔特許文献1参
照〕。これによりそれまでの高合金鋼に比べて耐熱疲労
性および耐酸化性が向上し、室温における延性を損なう
ことなく、耐熱鋳鉄と同等の鋳造性、加工性を有する耐
熱鋳鋼が得られ、耐熱熱疲労性をも向上するものであ
る。また、さらに、C:0.05〜1.00%、Si:
2%以下、Mn:2%以下、Cr:16.0〜25.0
%、Nb:4.0〜20.0%、Wおよび/またはM
o:1.0〜5.0%、Ni:0.1〜2.0%、N:
0.01〜0.15%、残部:Feおよび不可避不純物
からなり、Nbの含有量を増加することによりフェライ
ト基地および結晶粒界を強化し、通常のα相のほかにラ
ーベス相(Fe2 M)を適量析出させることにより、
高温強度とくにクリープ破断強度が向上できる提案があ
る〔特許文献2参照〕。
頁、および表2)
は、Nbのような高価な元素を用いていることから鋳鉄
は高価となり、実用上から安価なものが望まれている。
従って、本発明の目的は、安価な元素構成で高温におけ
る機械的物性を改善し、優れた高温強度と耐酸化性を有
する新たな耐熱球状黒鉛鋳鉄を提供することである。
意検討の結果、鋳鉄にC、Si、Mn、Mo、Cr、お
よびNiを必須成分として特定量含み、かつ任意成分と
してP、S、Mgのそれぞれを特定量以下に抑えて加え
られ、残部をFeとする構成により耐熱性および高温に
おける耐酸化性に優れる鋳鉄が製造できることを見い出
し、本発明を完成するに至った。
鋳鉄であり、C:2.5〜3.0重量%、Si:2.0
〜3.0重量%、Mn:0.8〜1.2重量%、Mo:
0.15〜0.4重量%、Cr:1.7〜3.0重量
%、Ni:17.0〜20.0重量%を必須成分とし、
かつP:0.1重量%以下、S:0.02重量%以下、
Mg:0.06重量%以下含んでもよく、残部をFeと
する構成元素からなっている。
黒鉛鋳鉄であり、球状化率が75〜100%、黒鉛サイ
ズが10〜70μm、セメンタイト析出量が全組織中5
%以下であるオーステナイト系組織を有している。
ーステナイト系組織を示し、構成金属成分としてC、S
i、Mn、Mo、Cr、Niを必須成分として含み、か
つ任意成分としてP、S、Mgとして含み、残部がFe
からなっている。
フェライト系組織であり、FCD−HはSiが3.2〜
3.8重量%であり、一般の鋳鉄に較べSi含量が非常
に高く、これによりフェライトを安定化させ、Moが添
加されておらず、使用領域での内部的相変態(Phas
e Transformation)により材料的、寸
法的変化が起きることを抑制している。この材料では、
Siの含有割合が多い程高温用材料に適している。FC
D−50HSでは、FCD−HよりSi含有量を狭い範
囲に制御して、Moを0.4〜0.6重量%を添加して
いる。Siの下限値を高くすることで高温領域における
酸化特性の向上を目的とし、さらにMoの添加で高温に
おける強度の上昇および耐酸化性の向上を行っている。
よび高温での強度の保持を考慮して判断され、本発明の
実施例によれば、FCD−Hの場合730℃以下、FC
D50−HSの場合750℃以下であり、耐酸化性はF
CD−HはCD50−HSに比べて3倍以上低いことが
分った。
とは異なり、成分元素の構成は、C:2.5〜3.0重
量%、Si:2.0〜3.0重量%、Mn:0.8〜
1.2重量%、Mo:0.15〜0.4重量%、Cr:
1.7〜3.0重量%、Ni:17.0〜20.0重量
%と、その他、P:0.1重量%以下、S:0.02重
量%以下、Mg0.06重量%以下含んでもよく、残部
がFeである元素構成でなっている。
り、黒鉛晶出及び炭化物形成に必要な成分で成形加工性
や靭性など機械性質と関連した成分である。
り、酸化抑制に作用し、強度を強める役割を果し、強度
と柔軟性のバランスをよくする。
あり、組織内部に微細に分散して強度を上げる効果があ
る。しかし、この範囲を超えて過度に添加されると柔軟
性および耐食性が低下する。
あり、高温における強度を上げ、耐孔食性を向上する成
分である。しかし、0.4重量%を超えると靭性、柔軟
性の低下をもたらす。また、高温強度、クリープ特性に
非常に重要な影響を及ぼす。
り、耐酸化性をよくする成分で、特に高温下での排気系
に用いたときその材料表面に緻密なCr2O3組織を形
成して高温での耐酸化性を向上させる。しかし、3.0
重量%を超えると、材料の強度を低下させる。
であり、Crと同様に材料の耐酸化性をよくし、かつ材
料の高温での強度を保持させる効果がある。
度向上効果をもつ成分であるが、0.1重量%を超える
と靭性を劣化させ脆くなる。
硫化物を生成して耐孔食性を劣化させる元素でもあるの
で、0.02重量%を超えるとこの好ましくない影響は
著しくなる。
り、0.06重量%を超えると酸化物形成が多くなり鋳
造品質に影響する。
75〜100%、黒鉛サイズが10〜70μm、セメン
タイト析出量が最大で5%であるオーステナイト系組織
を有することを確認した。この材料の使用可能な最大温
度は850℃であって、従来FCD−H(730℃以
下)、FCD50−HS(750℃)に比べて非常に優
れている。
系に用いられる材質に代えて適用可能であり、高温用鋳
鉄合金素材として優れた耐熱特性と耐酸化性を示す。ま
た、高出力エンジンの排気マニホールドに好適に使用で
きる。
細に説明する。但し、下記実施例は本発明を例示するた
めのものであり、本発明の内容がこれらに限定されるも
のではない。
耐熱球状黒鉛鋳鉄〔C:2.7重量%、Si:2.5重
量%、Mn:1.0重量%、Mo:0.3重量%、C
r:2.3重量%、Ni:18.5重量%、P:0.0
5重量%、S:0.02重量%、Mg:0.05重量%
で残部がFeよりなる組成〕および従来の耐熱鋳鉄の物
性を比較した。それぞれの鋳鉄の試験片について、70
0±14℃まで加熱した後、その温度で到達したときか
ら1時間保持した後300℃まで濾内で冷却した後空冷
し、引張り強度、降伏強度、延伸率、硬さを通常の方法
で測定した。結果を下記表2に示す。また、走査電子顕
微鏡(SEM)を用いて球状化率,黒鉛サイズ、基地組
織、セメンタイト析出量をそれぞれ測定した。結果を表
3に示す。
て、各温度における引張り強度の測定結果を表4および
図1に示した。
耐熱黒鉛鋳鉄は約730〜750℃付近で引張り強度7
5MPaであり、自動車排気系の条件が約730〜90
0℃になると満足すべき値ではない。これに対し、本発
明(実施例)の耐熱球状黒鉛鋳鉄は、低温においては比
較に示した鋳鉄より引張り強度が低いが、高温では逆転
し、比較に示した鋳鉄より高い値を示している。
び比較例1〜5の高温領域における耐酸化性を測定する
ために試験片を直径5mm×長さ10mmの円柱形状に
し、試験炉で760℃で加熱し、50時間ごとに200
時間まで段階別に大気中で酸化させながら、時間による
試験片の酸化増加量を計算した。結果を下記表5および
図2に示す。
D50M)では、他の比較例2〜5および実施例に比べ
て耐酸化性の劣化が実験初期から加速化されている。酸
化量は、実施例に比べて最大4.5倍、平均約3倍であ
り、これは低いSi成分とMo成分が添加されていない
ために高温耐酸化性および強度の低下を示す要因である
と推定される。実施例は、耐熱特性および耐酸化性にす
べて優れている。
優れ、特に高温における耐酸化性、、機械的物性に優れ
ているので、苛酷な条件で作動される自動車排気系の排
気マニホールドなどの用途に好適に使用できる。
引張り強度の変化を示すグラフである。
示すグラフである。
Claims (2)
- 【請求項1】 C:2.5〜3.0重量%、Si:2.
0〜3.0重量%、Mn:0.8〜1.2重量%、M
o:0.15〜0.4重量%、Cr:1.7〜3.0重
量%、Ni:17.0〜20.0重量%を必須成分と
し、かつP:0.1重量%以下、S:0.02重量%以
下、Mg:0.06重量%以下含んでもよく、残部をF
eとする構成元素からなることを特徴とする耐熱球状黒
鉛鋳鉄。 - 【請求項2】 前記耐熱球状黒鉛鋳鉄は、球状化率が7
5〜100%、黒鉛サイズが10〜70μm、セメンタ
イト析出量が全組織中5%以下であるオーステナイト系
組織を有することを特徴とする請求項1記載の耐熱球状
黒鉛鋳鉄。