JP2002256223A - Coating for stairs of plastic escalator and method for coating film - Google Patents
Coating for stairs of plastic escalator and method for coating filmInfo
- Publication number
- JP2002256223A JP2002256223A JP2001053024A JP2001053024A JP2002256223A JP 2002256223 A JP2002256223 A JP 2002256223A JP 2001053024 A JP2001053024 A JP 2001053024A JP 2001053024 A JP2001053024 A JP 2001053024A JP 2002256223 A JP2002256223 A JP 2002256223A
- Authority
- JP
- Japan
- Prior art keywords
- coating
- escalator
- meth
- weight
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、新規なプラスチッ
ク製エスカレーター階段用塗料に関する。TECHNICAL FIELD The present invention relates to a novel plastic escalator staircase paint.
【０００２】[0002]
【従来の技術】エスカレーターの階段は、周知のように
ライザー部と踏み板とで構成された階段がお互いに連結
されており、そしてこれらの複数の階段が順次移動する
ように構成されている。2. Description of the Related Art As is well known, the stairs of an escalator are formed by connecting a stair including a riser portion and a tread plate to each other, and the plurality of stairs are sequentially moved.
【０００３】従来から、エスカレーターの階段は無塗装
もしくは塗装のアルミニウムダイキャスト又は軽合金成
型品等の金属製階段が使用されている。しかしながら、
このような金属製階段は、製造コストが高く、そして重
量製品であるためにエスカレーターに負担がかかり耐久
性が劣るといった問題点があることから、このような金
属製階段に代えて耐久性、加工性等に優れたＦＲＰ（ガ
ラス繊維強化プラスチック）等による代替の動きがでて
きている。Conventionally, metal stairs such as unpainted or painted aluminum die-cast or light alloy molded products have been used for the stairs of the escalator. However,
Such metal stairs have high manufacturing costs and have a problem that the escalator is burdensome and inferior in durability because it is a heavy product. There is a trend toward alternatives such as FRP (glass fiber reinforced plastic) having excellent properties and the like.
【０００４】また、このようなＦＲＰを階段に成型加工
したものは、意匠性が劣るとともに歩行者がスリップし
易いといった問題点がある。このために、ＦＲＰ製階段
に通常のイソシアネート硬化型アクリル系樹脂塗料など
のプラスチック塗料を塗装することが考えられるが、こ
のものではＦＲＰ製階段に対する付着性、耐衝撃性が十
分でないこと、耐スリップ性及び耐磨耗性等の性能が劣
り、ＦＲＰ製階段用塗料としては十分でないことがわか
った。[0004] In addition, such an FRP molded into a staircase has problems that the design is inferior and that pedestrians easily slip. To this end, it is conceivable to apply a plastic paint such as a normal isocyanate-curable acrylic resin paint to the FRP step, but this method has insufficient adhesion and impact resistance to the FRP step, and has slip resistance. It was found that the performance such as wearability and abrasion resistance was inferior, and that it was not sufficient as an FRP step coating.
【０００５】[0005]
【課題を解決するための手段】 本発明者は、上記目的
を達成するために鋭意検討を重ねた結果、特に水酸基含
有基体樹脂、ポリイソシアネート化合物硬化剤及び弗素
樹脂粒子を必須樹脂成分とすることを特徴とするプラス
チック製エスカレーター階段用塗料が、プラスチック製
エスカレーター階段用に適した塗料であることを見出
し、本発明を完成するに至った。Means for Solving the Problems The present inventors have conducted intensive studies to achieve the above object, and as a result, in particular, a resin containing a hydroxyl group-containing base resin, a polyisocyanate compound curing agent, and a fluorine resin particle as essential resin components. The present inventors have found that a plastic escalator staircase paint characterized by the following is a paint suitable for a plastic escalator staircase, and have completed the present invention.
【０００６】即ち、本発明は、水酸基含有基体樹脂、ポ
リイソシアネート化合物硬化剤及び弗素樹脂粒子を必須
樹脂成分とすることを特徴とするプラスチック製エスカ
レーター階段用塗料を提供する。That is, the present invention provides a plastic escalator staircase paint comprising a hydroxyl group-containing base resin, a polyisocyanate compound curing agent and fluorine resin particles as essential resin components.
【０００７】また、本発明は、上記した塗料を、ガラス
繊維強化プラスチック製のエスカレーター用踏み板部及
び/又はライザー部にスプレー塗装し、磨耗減量が３０
ｍｇ以下の範囲、磨耗係数０．４〜０．９の範囲の硬化
塗膜を形成することによりプラスチック製エスカレータ
ー階段用塗膜形成方法を提供する。Further, the present invention spray-coats the above-mentioned paint on a glass fiber reinforced plastic escalator tread plate and / or a riser to reduce the abrasion loss by 30%.
The present invention provides a method for forming a plastic escalator step coating film by forming a cured coating film in the range of not more than mg and a wear coefficient of 0.4 to 0.9.
【０００８】更に、本発明は、上記の塗膜形成方法によ
り製造されるプラスチック製エスカレーター塗装階段を
提供する。Further, the present invention provides a plastic escalator painting staircase produced by the above-mentioned coating film forming method.
【０００９】[0009]
【発明の実施の形態】本発明の塗料は、水酸基含有基体
樹脂、軟質アクリル樹脂、ポリイソシアネート化合物硬
化剤を必須樹脂成分とする。また、該塗料に弗素樹脂粒
子を配合することができる。BEST MODE FOR CARRYING OUT THE INVENTION The paint of the present invention contains a hydroxyl group-containing base resin, a soft acrylic resin and a polyisocyanate compound curing agent as essential resin components. Further, fluorine resin particles can be blended in the paint.
【００１０】これらの各成分について以下に詳細に説明
する。Each of these components will be described in detail below.
【００１１】水酸基含有基体樹脂：水酸基含有基体樹脂
は、ガラス転移温度１０〜８５℃、好ましくは4０〜８
０℃、重量平均分子量１,０００〜８０,０００、好まし
くは２,０００〜５０,０００、水酸基価１０〜３００Ｋ
ＯＨｍｇ/ｇ、好ましくは２０〜２５０ＫＯＨｍｇ/ｇの
範囲内に含まれる樹脂が使用でき、特にビニル系樹脂が
好適である。かかるビニル系樹脂は、例えば、水酸基含
有ビニル系不飽和単量体とその他のビニル系不飽和単量
体とをラジカル共重合反応を行うことによって調製する
ことができる。 Hydroxyl-containing base resin: The hydroxyl-containing base resin has a glass transition temperature of 10 to 85 ° C., preferably 40 to 8 ° C.
0 ° C., weight average molecular weight 1,000 to 80,000, preferably 2,000 to 50,000, hydroxyl value 10 to 300K
Resins contained in the range of OH mg / g, preferably 20 to 250 KOH mg / g can be used, and vinyl resins are particularly preferred. Such a vinyl resin can be prepared, for example, by performing a radical copolymerization reaction between a hydroxyl group-containing vinyl unsaturated monomer and another vinyl unsaturated monomer.
【００１２】水酸基含有ビニル系不飽和単量体は、1分
子中に水酸基及びラジカル重合性不飽和二重結合をそれ
ぞれ1個以上有する化合物であり、例えば、ヒドロキシ
エチル（メタ）アクリレート、ヒドロキシプロピル（メ
タ）アクリレート、ヒドロキシブチル（メタ）アクリレ
ートなどの炭素数が２〜１０のアルキレングリコールと
（メタ）アクリル酸との等モル付加物があげられる。The hydroxyl group-containing vinyl unsaturated monomer is a compound having one or more hydroxyl groups and one or more radically polymerizable unsaturated double bonds in one molecule. For example, hydroxyethyl (meth) acrylate, hydroxypropyl ( Equimolar addition products of alkylene glycols having 2 to 10 carbon atoms, such as (meth) acrylate and hydroxybutyl (meth) acrylate, and (meth) acrylic acid are exemplified.
【００１３】その他のビニル系不飽和単量体は、1分子
中にラジカル重合性不飽和二重結合を１個以上有する化
合物で、上記の水酸基含有ビニル系不飽和単量体は含ま
れない。具体的には、（メタ）アクリル酸メチル、（メ
タ）アクリル酸エチル、（メタ）アクリル酸プロピル、
（メタ）アクリル酸ブチル、（メタ）アクリル酸ヘキシ
ル、（メタ）アクリル酸２−エチルヘキシル、（メタ）
アクリル酸ラウリル、（メタ）アクリル酸ステアリルな
どの炭素数が１〜２０のモノアルコールと（メタ）アク
リル酸とのモノエステル化物；アクリル酸、メタクリル
酸、クロトン酸、イタコン酸、マレイン酸、フマル酸、
２−カルボキシエチル（メタ）アクリレート、２−カル
ボキシプロピル（メタ）アクリレート、５−カルボキシ
ペンチル（メタ）アクリレートなどのカルボキシル基含
有不飽和化合物；グリシジル（メタ）アクリレート，ア
リルグリシジルエーテルなどのグリシジル基カルボキシ
ル基含有不飽和化合物；パーフルオロブチルエチル（メ
タ）アクリレート、パーフルオロイソノニルエチル（メ
タ）アクリレ−ト、パーフルオロオクチルエチル（メ
タ）アクリレートなどのパーフルオロアルキル（メタ）
アクリレート；スチレン、α−メチルスチレン、ビニル
トルエン、α−クロルスチレンなどのビニル芳香族化合
物；Ｎ，Ｎ−ジメチルアミノエチル（メタ）アクリレー
ト、Ｎ，Ｎ−ジエチルアミノエチル（メタ）アクリレー
ト、Ｎ−ｔ−ブチルアミノエチル（メタ）アクリレート
などの含窒素アルキル（メタ）アクリレート；アクリル
アミド、メタクリルアミド、Ｎ−メチル（メタ）アクリ
ルアミド、Ｎ−エチル（メタ）アクリルアミド、Ｎ−メ
チロール（メタ）アクリルアミド、Ｎ−メトキシメチル
（メタ）アクリルアミド、Ｎ−ブトキシメチル（メタ）
アクリルアミド、Ｎ，Ｎ−ジメチル（メタ）アクリルア
ミド、Ｎ，Ｎ−ジメチルアミノプロピル（メタ）アクリ
ルアミド、Ｎ，Ｎ−ジメチルアミノエチル（メタ）アク
リルアミド等の重合性アミド類；２−ビニルピリジン、
１−ビニル−２−ピロリドン、４−ビニルピリジンなど
の芳香族含窒素モノマー、アクリロニトリル、メタクリ
ロニトリル等の重合性ニトリルなどがあげられる。これ
らは単独で、又は2種以上複数で使用することができ
る。The other vinyl unsaturated monomers are compounds having one or more radically polymerizable unsaturated double bonds in one molecule, and do not include the above-mentioned hydroxyl group-containing vinyl unsaturated monomers. Specifically, methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate,
Butyl (meth) acrylate, hexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, (meth)
Monoesters of monoalcohols having 1 to 20 carbon atoms, such as lauryl acrylate and stearyl (meth) acrylate, and (meth) acrylic acid; acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, fumaric acid ,
Carboxyl group-containing unsaturated compounds such as 2-carboxyethyl (meth) acrylate, 2-carboxypropyl (meth) acrylate and 5-carboxypentyl (meth) acrylate; glycidyl group carboxyl groups such as glycidyl (meth) acrylate and allyl glycidyl ether Included unsaturated compounds: perfluoroalkyl (meth) such as perfluorobutylethyl (meth) acrylate, perfluoroisononylethyl (meth) acrylate, and perfluorooctylethyl (meth) acrylate
Acrylate; vinyl aromatic compounds such as styrene, α-methylstyrene, vinyltoluene, α-chlorostyrene; N, N-dimethylaminoethyl (meth) acrylate, N, N-diethylaminoethyl (meth) acrylate, Nt- Nitrogen-containing alkyl (meth) acrylates such as butylaminoethyl (meth) acrylate; acrylamide, methacrylamide, N-methyl (meth) acrylamide, N-ethyl (meth) acrylamide, N-methylol (meth) acrylamide, N-methoxymethyl (Meth) acrylamide, N-butoxymethyl (meth)
Polymerizable amides such as acrylamide, N, N-dimethyl (meth) acrylamide, N, N-dimethylaminopropyl (meth) acrylamide, N, N-dimethylaminoethyl (meth) acrylamide; 2-vinylpyridine;
Examples thereof include aromatic nitrogen-containing monomers such as 1-vinyl-2-pyrrolidone and 4-vinylpyridine, and polymerizable nitriles such as acrylonitrile and methacrylonitrile. These can be used alone or in combination of two or more.
【００１４】水酸基含有基体樹脂としてのビニル系樹脂
は、上記の水酸基含有ビニル系不飽和単量体とその他の
ビニル系不飽和単量体とを溶液重合などの既知の方法に
より共重合せしめることによって調製することができ
る。ガラス転移温度は不飽和単量体成分及びその比率な
どによって容易に調整できる。The vinyl-based resin as the hydroxyl-containing base resin is obtained by copolymerizing the above-mentioned hydroxyl-containing vinyl-unsaturated monomer with another vinyl-unsaturated monomer by a known method such as solution polymerization. Can be prepared. The glass transition temperature can be easily adjusted by the unsaturated monomer components and the ratio thereof.
【００１５】該水酸基含有基体樹脂は、例えば、２種以
上の混合樹脂であっても構わない。即ち、ガラス転移温
度、重量平均分子量、モノマー組成、水酸基含有量等の
構成要因の少なくとも１つが異なる２種以上の水酸基含
有基体樹脂の混合物が包含される。このような混合物は
プラスチック製エスカレーター階段に要求される、塗膜
外観や塗膜性能に応じて適宜混合することができる。The hydroxyl group-containing base resin may be, for example, a mixed resin of two or more kinds. That is, a mixture of two or more types of hydroxyl-containing base resins differing in at least one of constituent factors such as glass transition temperature, weight average molecular weight, monomer composition, and hydroxyl content is included. Such a mixture can be appropriately mixed according to the appearance and performance of a coating film required for a plastic escalator staircase.
【００１６】ポリイソシアネート化合物硬化剤：ポリイ
ソシアネート化合物は、水酸基含有基体樹脂を硬化させ
るための硬化剤成分であり、脂肪族系（変性）ポリイソ
シアネート化合物、脂環式（変性）ポリイソシアネート
化合物を使用することができるが、特に脂肪族系（変
性）ポリイソシアネート化合物を使用することが好まし
い。 Polyisocyanate compound curing agent: A polyisocyanate compound is a curing agent component for curing a hydroxyl-containing base resin, and uses an aliphatic (modified) polyisocyanate compound or an alicyclic (modified) polyisocyanate compound. In particular, it is preferable to use an aliphatic (modified) polyisocyanate compound.
【００１７】脂肪族系（変性）ポリイソシアネート化合
物は、脂肪族炭化水素の炭素原子に２個以上のフリーの
イソシアネート基が直接結合してなる、例えば、ヘキサ
メチレンジイソシアネート、トリメチレンジイソシアネ
ート、１，４−テトラメチレンジイソシアネート、ペン
タメチレンジイソシアネート、１，２−プロピレンジイ
ソシアネート、１，２−ブチレンジイソシアネート、ト
リメチルヘキサメチレンジイソシアネート、ダイマー酸
ジイソシアネート、リジンジイソシアネート、２，３−
ブチレンジイソシアネート、１，３−ブチレンジイソシ
アネート等の脂肪族系ポリイソシアネート化合物、及び
該脂肪族系ポリイソシアネート化合物の過剰量と多価ア
ルコール、ポリエステルポリオールもしくは水等との付
加物、あるいは上記した各脂肪族系ポリイソシアネート
化合物同志の重合体、更にはイソシアネート・ビゥレッ
ト体等が挙げられるが、これらの中でもポリエステルポ
リオールで変性した脂肪族系ポリイソシアネート化合物
が、塗膜の硬化性に優れること、及び機械的性質に優れ
た塗膜が形成できるのでこのものを使用することが好ま
しい。Aliphatic (modified) polyisocyanate compounds are obtained by directly bonding two or more free isocyanate groups to carbon atoms of an aliphatic hydrocarbon. For example, hexamethylene diisocyanate, trimethylene diisocyanate, 1,4 -Tetramethylene diisocyanate, pentamethylene diisocyanate, 1,2-propylene diisocyanate, 1,2-butylene diisocyanate, trimethylhexamethylene diisocyanate, dimer acid diisocyanate, lysine diisocyanate, 2,3-
Aliphatic polyisocyanate compounds such as butylene diisocyanate and 1,3-butylene diisocyanate, and adducts of an excess amount of the aliphatic polyisocyanate compound with a polyhydric alcohol, polyester polyol or water, or each of the above aliphatics Polymers based on polyisocyanate compounds, and isocyanate / biuret compounds, among which aliphatic polyisocyanate compounds modified with polyester polyols have excellent curability of coating films and mechanical properties It is preferable to use this film since a coating film having excellent heat resistance can be formed.
【００１８】弗素樹脂粒子：該弗素粒子は、ポリテトラ
フルオロエチレン（ＰＴＦＥ）系粒子であり、平均粒子
径０．１〜２０μｍ、好ましくは１〜１０μｍのもので
ある。ＰＴＦＥの共重合体を用いる場合、コモノマーと
しては、フッ化ビニル、フッ化ビニリデン、塩化トリフ
ルオロエチレン、ヘキサフルオロプロピレン、パーフル
オロ（アルコキシエチレン）（アルコキシ基の炭素数は
１〜５）、パーフルオロ（アルキル）エチレン（アルキ
ル基の炭素数は１〜８）、エチレン、プロピレンなどが
使用できる。特に好ましいＴＦＥ樹脂としては、ＰＴＦ
Ｅ、テトラフルオロエチレン／ヘキサフルオロプロピレ
ン共重合体、テトラフルオロエチレン／パーフルオロ
（アルコキシエチレン）共重合体、及びテトラフルオロ
エチレン／ヘキサフルオロプロピレン／パーフルオロ
（アルコキシエチレン）共重合体などがある。平均粒子
径０．１μｍ未満になると耐スリップ性が低下し、一
方、平均粒子径２０μｍを超えると塗膜外観が低下する
ので好ましくない。Fluororesin particles: The fluorine particles are polytetrafluoroethylene (PTFE) particles having an average particle diameter of 0.1 to 20 μm, preferably 1 to 10 μm. When a PTFE copolymer is used, examples of the comonomer include vinyl fluoride, vinylidene fluoride, trifluoroethylene chloride, hexafluoropropylene, perfluoro (alkoxyethylene) (alkoxy group has 1 to 5 carbon atoms), perfluoro (Alkyl) ethylene (the alkyl group has 1 to 8 carbon atoms), ethylene, propylene and the like can be used. Particularly preferred TFE resins include PTF
E, a tetrafluoroethylene / hexafluoropropylene copolymer, a tetrafluoroethylene / perfluoro (alkoxyethylene) copolymer, and a tetrafluoroethylene / hexafluoropropylene / perfluoro (alkoxyethylene) copolymer. If the average particle diameter is less than 0.1 μm, the slip resistance is reduced, while if the average particle diameter is more than 20 μm, the appearance of the coating film is undesirably reduced.
【００１９】本発明の塗料において、水酸基含有基体樹
脂、ポリイソシアネート化合物、弗素樹脂粒子のそれぞ
れの配合割合は次の通りである。水酸基含有基体樹脂と
ポリイソシアネート化合物との配合割合（固形分換算）
は、水酸基含有基体樹脂の水酸基１個当たり、ポリイソ
シアネート化合物のＮＣＯ基が平均約０．５〜１．８
個、好ましくは平均約０．７〜１．５個の範囲に入るよ
うに配合することが好ましい。ＮＣＯ基が平均約０．５
個未満になると硬化性が劣り、一方１．８個を超えると
貯蔵安定性、塗膜物性が低下する。In the coating composition of the present invention, the respective proportions of the hydroxyl group-containing base resin, the polyisocyanate compound and the fluororesin particles are as follows. Mixing ratio of hydroxyl group-containing base resin and polyisocyanate compound (solid content conversion)
Means that the average number of NCO groups of the polyisocyanate compound is about 0.5 to 1.8 per hydroxyl group of the hydroxyl group-containing base resin.
It is preferable that the compound is blended so as to fall within the range of about 0.7 to 1.5 on average. NCO groups average about 0.5
When the number is less than 1.8, the curability is inferior. On the other hand, when the number exceeds 1.8, the storage stability and the physical properties of the coating film deteriorate.
【００２０】また、弗素樹脂粒子の配合割合は、水酸基
含有基体樹脂、ポリイソシアネート化合物及び弗素樹脂
粒子の総合計重量換算で１〜４０重量％、好ましくは５
〜２０重量％の範囲である。該弗素樹脂粒子が１重量％
未満になると耐磨耗性及び耐スリップ性が低下し、一
方、４０重量％を超えて配合すると塗膜の付着性、塗膜
強度等が低下するので好ましくない。The mixing ratio of the fluororesin particles is 1 to 40% by weight, preferably 5% by weight in terms of the total weight of the hydroxyl-containing base resin, the polyisocyanate compound and the fluororesin particles.
-20% by weight. 1% by weight of the fluororesin particles
When the amount is less than the above, the abrasion resistance and the slip resistance are reduced. On the other hand, when the amount exceeds 40% by weight, the adhesion of the coating film, the strength of the coating film and the like are undesirably reduced.
【００２１】本発明の塗料は、上記した水酸基含有基体
樹脂、ポリイソシアネート化合物を有機溶剤に溶解し、
必要に応じて弗素樹脂粒子を分散させることにより製造
できる。有機溶剤としては、ＮＣＯ基と実質的に反応を
起こさない、揮発性の有機溶剤であれば、特に制限なし
に従来から公知のものを使用することができる。具体的
には、例えば、炭化水素系、エ−テル系、ケトン系、エ
ステル系、炭化水素系などの種類から揮発性のものを選
択して使用することができる。The paint of the present invention is obtained by dissolving the above-mentioned hydroxyl-containing base resin and polyisocyanate compound in an organic solvent,
It can be produced by dispersing fluororesin particles as required. As the organic solvent, a conventionally known organic solvent can be used without particular limitation as long as it is a volatile organic solvent that does not substantially react with the NCO group. Specifically, for example, volatile compounds can be selected from the group consisting of hydrocarbons, ethers, ketones, esters, and hydrocarbons.
【００２２】本発明の塗料は、必要に応じて着色剤、充
填剤、流動性調整剤、ハジキ防止剤、垂れ止め剤、硬化
触媒、その他の添加剤等が配合できる。The paint of the present invention may contain, if necessary, a colorant, a filler, a fluidity-controlling agent, an anti-cissing agent, an anti-dripping agent, a curing catalyst, and other additives.
【００２３】本発明の塗料は、プラスチック、金属及び
これらのものが組合わさった基材に塗装することができ
る。塗装は、従来から公知の塗装手段、例えばスプレー
塗装、刷毛塗装、ローラ塗装等の方法で行うことができ
る。これらの中でもスプレー塗装が好ましい。The paint of the present invention can be applied to plastics, metals and substrates in which these are combined. The coating can be performed by a conventionally known coating method, for example, a method such as spray coating, brush coating, and roller coating. Of these, spray coating is preferred.
【００２４】上記スプレー塗装は、従来から公知のスプ
レー塗装機を使用して、手動もしくは自動で塗装するこ
とができる。塗装粘度は、通常１０〜３０秒、特に１５
〜２０の範囲が好ましい。塗装膜厚は、踏み板の凸面部
の乾燥膜厚で２０〜５０μｍ、３０〜４０μｍの範囲が
好ましい。また、塗装する前のエスカレーター用基材
は、必要に応じて表面処理やプライマーを塗装を施して
おくこともできる。The above spray coating can be performed manually or automatically using a conventionally known spray coating machine. The coating viscosity is usually 10 to 30 seconds, especially 15
The range of ~ 20 is preferable. The coating thickness is preferably in the range of 20 to 50 μm and 30 to 40 μm in terms of the dry thickness of the convex portion of the tread. In addition, the escalator base material before coating may be subjected to a surface treatment or a primer if necessary.
【００２５】本発明塗料は、磨耗減量が３０ｍｇ以下、
好ましくは１０〜２０ｍｇの範囲、摩擦係数０．４〜
０．９、好ましくは０．５〜０．７の範囲の硬化塗膜に
なるように塗膜を形成することが好ましい。The paint of the present invention has an abrasion loss of 30 mg or less,
Preferably in the range of 10-20 mg, friction coefficient 0.4-
It is preferable to form the coating film so as to obtain a cured coating film in the range of 0.9, preferably 0.5 to 0.7.
【００２６】該磨耗減量は、平板の試験板に塗料を乾燥
膜厚が３０〜４０μｍになるように塗装し、次いで８０
℃で２０分間乾燥し、室温に１日放置したものを試験板
とし、このものをテーバー式摩耗試験機により 摩耗輪
ＣＳ１７を用い、荷重１０００ｇ、１０００回転させ
て、塗膜が磨耗して減量したときの重量（ｍｇ）を示
す。The abrasion loss is measured by applying a paint to a flat test plate so that the dry film thickness is 30 to 40 μm,
A test plate was dried at 20 ° C. for 20 minutes and left at room temperature for 1 day. The test plate was worn by a Taber abrasion tester using a wear wheel CS17 at a load of 1,000 g and rotated 1,000 times, and the coating film was worn and reduced in weight. The weight (mg) at the time is shown.
【００２７】この試験方法はＪＩＳ Ｋ ５４００塗料一
般試験方法の８．９耐摩耗性項目による。This test method is based on the 8.9 abrasion resistance item of JIS K 5400 paint general test method.
【００２８】また、本発明において、摩擦係数は、平板
の試験板に塗料を乾燥膜厚が４０μｍになるように塗装
し、次いで８０℃で２０分間乾燥した後、常温で１日間
放置したものを試験板とし、この塗膜と硬質ゴムとの磨
耗係数を示す。摩擦係数は 硬質ゴムを試験板の上に置
き、その引っ張り荷重量を 積載荷重量で除した値とし
た。Further, in the present invention, the coefficient of friction is determined by coating a flat test plate with a coating so that the dry film thickness becomes 40 μm, drying the coating at 80 ° C. for 20 minutes, and then allowing it to stand at room temperature for 1 day. As a test plate, the abrasion coefficient between the coating film and the hard rubber is shown. The coefficient of friction was a value obtained by placing hard rubber on a test plate and dividing the tensile load by the load.
【００２９】[0029]
【実施例】 次ぎに、実施例を挙げて、更に詳細に説明
する。 実施例１ レタンＰＧ８０ベース（関西ペイント株式会社製、商品
名、水酸基含有アクリル系樹脂、水酸基価約８０ＫＯＨ
ｍｇ/ｇ、重量平均分子量約３万、ガラス転移温度約６
０℃）１００重量部（固形分）、デュラネートＥ５００
４−９０Ｔ（旭化成工業株式会社製、商品名、ポリエス
テルポリオール変性ヘキサメチレンジイソシアネート化
合物、ＮＣＯ基含有率８．４％、加熱残分９０％）３０
重量部（ＯＨ/ＮＣＯ＝１/１）、ダイニオンＴＦ−９２
０５（Ｄｙｎｅｏｎ Ｇｍｂｈ社製、商品名、ポリテト
ラフルオロエチレン、平均粒子径５μｍ粉末）１５重量
部、トルエン溶剤 ４０重量部を配合して実施例１の塗
料を製造した。Next, the present invention will be described in more detail with reference to examples. Example 1 Rethane PG80 base (manufactured by Kansai Paint Co., Ltd., trade name, hydroxyl group-containing acrylic resin, hydroxyl value about 80 KOH
mg / g, weight average molecular weight about 30,000, glass transition temperature about 6
0 ° C) 100 parts by weight (solid content), Duranate E500
4-90T (manufactured by Asahi Chemical Industry Co., Ltd., trade name, polyester polyol-modified hexamethylene diisocyanate compound, NCO group content 8.4%, heating residue 90%) 30
Parts by weight (OH / NCO = 1/1), Dyneon TF-92
05 (manufactured by Dyneon Gmbh, trade name, polytetrafluoroethylene, powder having an average particle size of 5 μm) (15 parts by weight) and toluene solvent (40 parts by weight) were blended to prepare the coating material of Example 1.
【００３０】実施例２ 実施例２において、ＯＨ/ＮＣＯ＝１/１の比を１/０．
８とした以外は実施例1と同様にして製造した。Example 2 In Example 2, the ratio of OH / NCO = 1/1 was changed to 1/0.
Except having set it as 8, it manufactured like Example 1.
【００３１】実施例３ 実施例1において、ＯＨ/ＮＣＯ＝１/１の比を１/１．２
とした以外は実施例1と同様にして製造した。Example 3 In Example 1, the ratio of OH / NCO = 1/1 was changed to 1 / 1.2.
It was manufactured in the same manner as in Example 1, except that
【００３２】実施例4 実施例1において、ＴＦ−９２０５を２０重量部とした
以外は実施例１と同様にして製造した。Example 4 Production was carried out in the same manner as in Example 1 except that TF-9205 was changed to 20 parts by weight.
【００３３】比較例１ レタンＰＧ８０ベース（上記と同様のもの）１００重量
部（固形分）、デュラネートＥ５００４−９０Ｔ（上記
と同様のもの）３０重量部（ＯＨ/ＮＣＯ＝１/１）、ト
ルエン溶剤 ４０重量部を配合して比較例１の塗料を製
造した。Comparative Example 1 100 parts by weight (solid content) of a urethane PG80 base (same as above), 30 parts by weight of duranate E5004-90T (same as above) (OH / NCO = 1/1), toluene solvent The paint of Comparative Example 1 was produced by mixing 40 parts by weight.
【００３４】試験板作成方法 ＦＲＰの平板に実施例及び比較例の塗料（希釈粘度１８
秒）を乾燥膜厚が３０μｍになるようにスプレー塗装
し、８０℃で２０分乾燥した後、２０℃で１６時間放置
して乾燥させた。Test Plate Preparation Method The paints of Examples and Comparative Examples (diluted viscosity 18
Second) was spray-coated so that the dry film thickness became 30 μm, dried at 80 ° C. for 20 minutes, and then left at 20 ° C. for 16 hours to dry.
【００３５】得られた塗装試験板について下記の試験を
行った。The following tests were performed on the obtained coated test plates.
【００３６】塗膜外観：目視による ハジキ、凹み、タ
レ、アワ、ワレ等を観察する。Appearance of coating film: Repelling, dents, sagging, millet, cracking, etc. are visually observed.
【００３７】付着性：ＪＩＳ Ｋ−５４００ ８．５．
２（１９９０）碁盤目−テ−プ法に準じて、１ｍｍ×１
ｍｍのマス目を１００個作成し、その表面にテ−プを密
着させ剥離した際のマス目の剥れ程度を試験した。剥れ
の全くないものを○とした。Adhesion: JIS K-5400 8.5.
2 (1990) 1 mm × 1 in accordance with the grid-tape method
100 squares of mm were prepared, and the degree of peeling of the squares when a tape was adhered to the surface and peeled was tested. A sample without any peeling was marked with “○”.
【００３８】耐衝撃性：試験板を温度２０±１℃、湿度
７５±２％の恒温恒湿に２４時間置いたのち、デュポン
式衝撃試験器に規定の大きさの受台と撃心１/２インチ
を取り付け、試験板の塗面を上向きにして、その間に挟
み次に規定のおもり500ｇと規定の高さから撃心の上に
落し、塗膜の衝撃によるワレ、ハガレがないときを合格
とする。Impact resistance: The test plate was placed in a thermo-hygrostat at a temperature of 20 ± 1 ° C. and a humidity of 75 ± 2% for 24 hours. Attach 2 inches, place the test plate with the coated surface facing upwards, sandwich it between them, then drop it onto the shooting point from the specified weight of 500 g and the specified height, and pass if there is no crack or peeling due to the impact of the coating film And
【００３９】耐水性：２０℃上水に１０日間浸漬後、上
記付着性試験を行った。Water resistance: The above adhesion test was performed after immersion in water at 20 ° C. for 10 days.
【００４０】耐湿性：塗板を５０℃、１００％ＲＨの耐
湿性試験箱の中に１０日間置いた後とり出し、上記付着
性試験を行った。Moisture resistance: The coated plate was placed in a humidity resistance test box at 50 ° C. and 100% RH for 10 days, taken out, and subjected to the above adhesion test.
【００４１】冷熱サイクル試験：試験塗板を「７０℃で
１時間放置→２０℃の水道水中に１時間浸漬→−２０℃
で１時間放置」を１サイクルとするテストを５０サイク
ル連続して試験後の上記付着性を調べた。Cooling / heating cycle test: The test coated plate was left at 70 ° C. for 1 hour → immersed in 20 ° C. tap water for 1 hour → −20 ° C.
The test was repeated for 50 cycles in which the test was left for 1 hour for 1 cycle, and the adhesion was examined after the test.
【００４２】耐洗浄剤性：弱アルカリ性の洗浄剤を塗膜
表面に載せ、５０℃で４時間スポット試験を行った。塗
膜の外観を目視で評価した。Detergent resistance: A weak alkaline detergent was placed on the surface of the coating film, and a spot test was conducted at 50 ° C. for 4 hours. The appearance of the coating film was visually evaluated.
【００４３】耐候性：サンシャインウエザーオメーター
を用いて、５００時間試験後の塗膜の光沢保持率を調べ
た。実施例及び比較例の結果を表１に示す。Weather resistance: The gloss retention of the coating film after the test for 500 hours was examined using a sunshine weatherometer. Table 1 shows the results of Examples and Comparative Examples.
【００４４】表１ Table 1
【００４５】[0045]
【発明の効果】 本発明塗料によって形成された塗膜
は、特に、耐磨耗性、耐スリップ性に優れた性能を持つ
ものである。また、本発明は、上記した構成を有するこ
とから、従来に比べ軽量化が可能となること、歩行者が
スリップしたりする恐れがないこと、靴などにより磨耗
し難いのでメンテナスの回数が少なくて済むといった効
果がある。EFFECT OF THE INVENTION The coating film formed by the coating material of the present invention has particularly excellent performance in abrasion resistance and slip resistance. In addition, since the present invention has the above-described configuration, it is possible to reduce the weight as compared with the related art, there is no risk of pedestrians slipping, and it is difficult to wear by shoes etc. This has the effect of ending.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０９Ｄ 175/04 Ｃ０９Ｄ 175/04 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C09D 175/04 C09D 175/04
Claims (3)
化合物硬化剤及び弗素樹脂粒子を必須樹脂成分とするこ
とを特徴とするプラスチック製エスカレーター階段用塗
料。1. A plastic escalator staircase paint comprising a hydroxyl group-containing base resin, a polyisocyanate compound curing agent and fluorine resin particles as essential resin components.
００ＫＯＨｍｇ/ｇ、重量平均分子量１,０００〜８０,
０００のアクリル系樹脂であることを特徴とする請求項
１に記載のエスカレーター階段用塗料。2. The method of claim 1, wherein the hydroxyl-containing base resin has a hydroxyl value of 10 to 3
00KOHmg / g, weight average molecular weight 1,000-80,
The escalator staircase paint according to claim 1, which is an acrylic resin of 000.
レンジイソシアネートとポリエステルポリオールとの変
性ウレタンプレポリマーであることを特徴とする請求項
１又は２に記載のエスカレーター階段用塗料。3. The escalator step coating according to claim 1, wherein the polyisocyanate compound is a modified urethane prepolymer of hexamethylene diisocyanate and a polyester polyol.