JP2001262737A - Fireproof panel - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a fireproof panel receivable of a fireproof structure test as prescribed in JIS-A-1304, and provided with a sufficiently high bending rigidity and strength as the whole panel. SOLUTION: In this panel provided with an FRP skin layer comprising phenol resin as matrix resin at least on one surface of a core member comprising inorganic material, the rate of the inorganic material in the whole panel is within 50-82 wt.%.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、耐火性能を有す
る、建築物の床材、壁材、天井材、屋根材、間仕切り材
等に好適な耐火パネルに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fire-resistant panel having fire resistance and suitable for flooring, wall, ceiling, roof, partition, etc. of a building.

【０００２】[0002]

【従来の技術】建築物等の耐火パネルとしては、一般に
無機系コア材を主体としそれに石綿を含有させて強度を
確保したものが用いられてきたが、特定化学物質等障害
予防規則の改正（平成７年１月）により石綿の含有量に
ついての規制が厳しくなったことから、石綿を含有しな
いか含有してもごく少量に抑えた無機系コア材の使用が
要求されている。2. Description of the Related Art In general, fireproof panels for buildings and the like have been used in which inorganic core material is mainly used and asbestos is contained to secure strength. (January 1995), the regulations on the content of asbestos have become strict, and the use of an inorganic core material containing no or little asbestos has been required.

【０００３】このような無機系コア材を使用する場合、
そのままでは耐火パネルとしての十分な強度や剛性を確
保することが困難な場合が多いので、無機系コアボード
の少なくとも片面に織布や不織布に樹脂を含浸させた表
面材層、つまりＦＲＰスキン層を設け、パネル全体とし
ての強度、剛性をもたせるようにした構造が提案されて
いる（特開平１０−２０５０５７号公報）。When using such an inorganic core material,
In many cases, it is difficult to secure sufficient strength and rigidity as a fireproof panel as it is, so at least one surface of the inorganic core board is made of a woven fabric or nonwoven fabric impregnated with resin, that is, an FRP skin layer. There has been proposed a structure in which the panel is provided to have strength and rigidity as a whole panel (Japanese Patent Application Laid-Open No. 10-205057).

【０００４】[0004]

【発明が解決しようとする課題】しかしながら、特開平
１０−２０５０５７号公報に開示された耐火パネル構造
では、ＦＲＰスキン層をコア材の片面に設ける場合、ま
た、コア材の両面に設ける場合においても、ある一定量
以上のＦＲＰ層がないと、パネル全体に、風荷重等に耐
えることができるだけの強度、剛性をもたせることが困
難である。一方、パネル全体としてある一定量以上の無
機質の材料がないと、十分な耐火性能が得られず、火災
等に対しクラックが裏面にまで達し、裏面側の温度を規
定したＪＩＳ−Ａ−１３０４の耐火構造試験に合格しな
いことになる。However, in the fireproof panel structure disclosed in Japanese Patent Application Laid-Open No. H10-205057, even when the FRP skin layer is provided on one side of the core material or when the FRP skin layer is provided on both sides of the core material. Without a certain amount or more of the FRP layer, it is difficult to give the entire panel sufficient strength and rigidity to withstand wind loads and the like. On the other hand, if there is no inorganic material of a certain amount or more in the entire panel, sufficient fire resistance cannot be obtained, cracks reach the rear surface against fire, etc., and the temperature of the rear surface side of JIS-A-1304 is defined. It will not pass the fire resistant structure test.

【０００５】そこで本発明の課題は、上記のような従来
技術の問題点に着目し、とくにＪＩＳ−Ａ−１３０４に
規定されている耐火構造試験に合格し得るとともに、パ
ネル全体として十分に高い曲げ剛性、強度を備えた耐火
パネルを提供することにある。Accordingly, an object of the present invention is to pay attention to the above-mentioned problems of the prior art, and in particular to be able to pass a fireproof structure test specified in JIS-A-1304 and to obtain a sufficiently high bending strength for the entire panel. An object of the present invention is to provide a fireproof panel having rigidity and strength.

【０００６】[0006]

【課題を解決するための手段】上記課題を解決するため
に、本発明の耐火パネルは、無機材料からなるコア材の
少なくとも片面にフェノール樹脂をマトリックス樹脂と
するＦＲＰスキン層を設けたパネルであって、パネル全
体の無機系材料が５０〜８２重量％の範囲にあることを
特徴とするものからなる。Means for Solving the Problems In order to solve the above problems, a fireproof panel of the present invention is a panel in which an FRP skin layer using a phenolic resin as a matrix resin is provided on at least one surface of a core material made of an inorganic material. The inorganic material of the entire panel is in the range of 50 to 82% by weight.

【０００７】すなわち本発明は、耐火性能向上のために
無機系材料のパネル全体に対する重量構成を最適な範囲
内に設定するとともに、併せてパネル全体の剛性や強度
を十分に高く保つことができるようにしたものである。That is, the present invention sets the weight composition of the inorganic material with respect to the entire panel within the optimum range in order to improve the fire resistance performance, and also keeps the rigidity and strength of the entire panel sufficiently high. It was made.

【０００８】パネル全体における無機系材料には、コア
材を構成する無機材料に加え、ＦＲＰスキン層に含まれ
る無機系材料を含む。The inorganic material in the entire panel includes the inorganic material contained in the FRP skin layer in addition to the inorganic material constituting the core material.

【０００９】上記コア材の重量としては、３ｋｇ／ｍ²
以下であることが好ましい。これよりも重くなると、パ
ネル全体の重量が大きくなり、取り扱いにくくなる。The weight of the core material is 3 kg / m ²
The following is preferred. If it is heavier than this, the weight of the entire panel will increase, making it difficult to handle.

【００１０】また、上記耐火パネルは、コア材の厚み方
向に延びるリブを有することが好ましく、このリブはＦ
ＲＰスキン層と一体に成形されていることが好ましい。
したがって、コア材の両面にＦＲＰスキン層が配置され
る場合には、リブは両ＦＲＰスキン層を接続する構成と
することが好ましい。リブの存在により、耐火パネル全
体としての強度、剛性がより高められる。このリブの配
設ピッチは、コア材の厚みの０．５〜１０倍、好ましく
は１〜５倍の範囲にあることが望ましい。Preferably, the refractory panel has a rib extending in a thickness direction of the core material.
It is preferable to be formed integrally with the RP skin layer.
Therefore, when the FRP skin layers are arranged on both surfaces of the core material, it is preferable that the ribs connect both the FRP skin layers. The presence of the ribs further enhances the strength and rigidity of the entire refractory panel. It is desirable that the arrangement pitch of the ribs is in the range of 0.5 to 10 times, preferably 1 to 5 times the thickness of the core material.

【００１１】このような本発明に係る耐火パネルにおい
ては、無機材料からなるコア材と、耐火性能に優れたフ
ェノール樹脂をマトリックス樹脂とするＦＲＰスキン層
とからなるサンドイッチパネル構造とされ、かつ、パネ
ル全体の無機系材料の重量構成が５０〜８２重量％の範
囲とされるので、最適な無機系材料比により十分に高い
耐火性能が確保されつつ、サンドイッチ構造により十分
に高い強度、剛性が確保される。無機系材料の構成比が
５０重量％未満では、十分に高い耐火性能が得られない
おそれが生じ、ＪＩＳ−Ａ−１３０４に規定の耐火試験
に合格しない場合が生じるおそれがある。逆に８２重量
％を超えると、無機系材料の含有率が高くなりすぎ、耐
火性能としては十分であるものの、パネル全体として十
分に高い強度、剛性を確保することが困難になる。本発
明で規定した範囲とすることにより、ＪＩＳ−Ａ−１３
０４に規定の耐火構造試験時にも熱炎が裏面に達するこ
とはなく、確実に試験に合格できるようになり、同時に
パネル全体としての必要な強度、剛性を確保できるよう
になる。The refractory panel according to the present invention has a sandwich panel structure including a core material made of an inorganic material and an FRP skin layer using a phenol resin having excellent fire resistance performance as a matrix resin. Since the weight composition of the entire inorganic material is in the range of 50 to 82% by weight, a sufficiently high fire resistance performance is secured by the optimal inorganic material ratio, and a sufficiently high strength and rigidity are secured by the sandwich structure. You. If the composition ratio of the inorganic material is less than 50% by weight, a sufficiently high fire resistance may not be obtained, and the fire resistance test specified in JIS-A-1304 may not be passed. On the other hand, when the content exceeds 82% by weight, the content of the inorganic material becomes too high, and although the fire resistance is sufficient, it is difficult to secure sufficiently high strength and rigidity as the whole panel. According to the range specified in the present invention, JIS-A-13
Even during the fireproof structure test specified in 04, the hot flame does not reach the back surface, so that the test can be surely passed, and at the same time, the necessary strength and rigidity of the entire panel can be secured.

【００１２】また、無機系コア材の厚み方向に延びるリ
ブを適切なピッチで設けることにより、パネル全体とし
ての曲げ剛性、強度をさらに高めることが可能になり、
耐火特性のみならず機械特性にも優れた耐火パネルを実
現できる。Also, by providing ribs extending in the thickness direction of the inorganic core material at an appropriate pitch, it is possible to further increase the bending rigidity and strength of the entire panel,
A fire-resistant panel excellent not only in fire-resistant characteristics but also in mechanical characteristics can be realized.

【００１３】[0013]

【発明の実施の形態】以下に、本発明の望ましい実施の
形態を、図面を参照して説明する。図１は、本発明の一
実施態様に係る耐火パネル１を示している。耐火パネル
１は、無機材料からなるコア材２と、その片面に設けら
れた、フェノール樹脂をマトリックス樹脂とするＦＲＰ
スキン層３とからなる。DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the present invention will be described below with reference to the drawings. FIG. 1 shows a fireproof panel 1 according to one embodiment of the present invention. The refractory panel 1 is composed of a core material 2 made of an inorganic material and an FRP provided on one side thereof and using a phenol resin as a matrix resin.
And a skin layer 3.

【００１４】コア材２として用いる無機材料としては、
たとえば珪酸カルシウム、気泡コンクリート、モルタ
ル、軽量骨材コンクリート、石綿スレート、パーライト
板、パルプセメント板、木毛セメント板、木片セメント
板、ロックウール板、泡ガラス、石膏ボード等を使用で
きる。The inorganic materials used as the core material 2 include:
For example, calcium silicate, cellular concrete, mortar, lightweight aggregate concrete, asbestos slate, perlite plate, pulp cement plate, wood wool cement plate, wood chip cement plate, rock wool plate, foam glass, gypsum board and the like can be used.

【００１５】ＦＲＰスキン層３においては、マトリック
ス樹脂として、耐火性能に優れたフェノール樹脂を用
い、強化繊維として、ガラス繊維、炭素繊維、アラミド
繊維や、無機ウィスカー、ロックファイバー、ロックウ
ール等の無機繊維、金属繊維、およびこれらの混合物が
使用できる。マトリックス樹脂中には、不燃性の有機成
分を極力減らすため、タルク、クレー、カオリン、焼石
膏、水酸化アルミニウム等の無機粉末を加え、さらに耐
火性能を向上させることができる。In the FRP skin layer 3, a phenol resin having excellent fire resistance is used as a matrix resin, and glass fibers, carbon fibers, aramid fibers, and inorganic fibers such as inorganic whiskers, rock fibers, and rock wool are used as reinforcing fibers. , Metal fibers, and mixtures thereof. In order to reduce nonflammable organic components as much as possible, inorganic powders such as talc, clay, kaolin, calcined gypsum and aluminum hydroxide can be added to the matrix resin to further improve the fire resistance.

【００１６】そして本発明においては、コア材２を構成
する無機材料と、ＦＲＰスキン層３に含まれる無機系材
料（上記のような強化繊維およびＦＲＰスキン層３に添
加される無機物）のパネル全体に対する総重量が、５０
〜８２重量％の範囲内とされる。In the present invention, the whole panel of the inorganic material constituting the core material 2 and the inorganic material contained in the FRP skin layer 3 (the above-mentioned reinforcing fiber and the inorganic substance added to the FRP skin layer 3) is used. The total weight is 50
８２82% by weight.

【００１７】このように構成された耐火パネル１におい
ては、パネル全体に対する無機系材料が５０重量％以上
であるので、優れた耐火性能を発揮することができ、Ｊ
ＩＳ−Ａ−１３０４に規定の耐火試験に容易に合格でき
るようになる。In the fireproof panel 1 thus configured, since the inorganic material is 50% by weight or more based on the entire panel, excellent fireproof performance can be exhibited.
It is possible to easily pass the fire resistance test specified in IS-A-1304.

【００１８】また、パネル全体に対する無機系材料が８
２重量％以下であるので、過剰な無機系材料の配合によ
りパネルの強度や剛性が大きく低下することが防止さ
れ、パネル全体として必要な強度や剛性を確保できるよ
うになる。Further, the inorganic material is 8
Since the content is 2% by weight or less, the strength and rigidity of the panel are prevented from being significantly reduced by the excessive blending of the inorganic material, and the necessary strength and rigidity of the entire panel can be secured.

【００１９】本発明においては、パネルの断面構成とし
て、種々の形態を採り得る。たとえば図２に示すよう
に、無機材料からなるコア材１２の両面にＦＲＰスキン
層１３を配したサンドイッチ構造の耐火パネル１１とす
ることができる。In the present invention, various forms can be adopted as the cross-sectional configuration of the panel. For example, as shown in FIG. 2, a fireproof panel 11 having a sandwich structure in which FRP skin layers 13 are arranged on both surfaces of a core material 12 made of an inorganic material can be obtained.

【００２０】また、パネル全体の強度、剛性をより高め
るために、コア材の厚み方向に延びるリブを配設するこ
とができる。リブは、前述したように、ＦＲＰスキン層
と一体に成形することが好ましく、配設ピッチはコア材
の厚みの０．５〜１０倍の範囲にあることが好ましい。In order to further increase the strength and rigidity of the entire panel, ribs extending in the thickness direction of the core material can be provided. As described above, the rib is preferably formed integrally with the FRP skin layer, and the arrangement pitch is preferably in the range of 0.5 to 10 times the thickness of the core material.

【００２１】たとえば図３に示す耐火パネル２１では、
コア材２２の片面に設けられたＦＲＰスキン層２３に対
してリブ２４が一体に成形されている。リブ２４は、Ｆ
ＲＰスキン層２３と同種のＦＲＰからなることが、強
度、剛性向上の点から好ましい。また、図４に示す耐火
パネル３１では、コア材３２の両面に設けられたＦＲＰ
スキン層３３の間にリブ３４が設けられ、リブ３４で両
ＦＲＰスキン層３３が一体に接合されている。For example, in the fireproof panel 21 shown in FIG.
A rib 24 is formed integrally with an FRP skin layer 23 provided on one surface of the core material 22. The rib 24 is
It is preferable to be made of the same type of FRP as the RP skin layer 23 from the viewpoint of improving strength and rigidity. In the fireproof panel 31 shown in FIG.
A rib 34 is provided between the skin layers 33, and the two FRP skin layers 33 are integrally joined by the rib 34.

【００２２】[0022]

【実施例】以下、本発明を、実施例に基づいて説明す
る。 実施例１ 図３に示した、コア材の両面にＦＲＰスキン層を配した
サンドイッチ構造の耐火パネルで、リブのない一様な断
面形状の耐火パネルを作成した。コア材には、厚さ５０
ｍｍの軽量珪酸カルシウム板（重量：５５００ｇ／
ｍ² ）を用い、ＦＲＰスキン層には、フェノール樹脂を
マトリックス樹脂とし（樹脂重量：５０００ｇ／
ｍ² ）、ガラスロービングクロス（１層当たり重量：５
８０ｇ／ｍ² ）を５プライ積層し、それを上下のスキン
層に配置した（このクロスの総重量：５８００ｇ／
ｍ² ）。また、このＦＲＰスキン層には無機充填材とし
てタルクを１２００ｇ／ｍ² 添加した。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below based on embodiments. Example 1 As shown in FIG. 3, a fire-resistant panel having a uniform cross-sectional shape without ribs was prepared as a sandwich-type fire-resistant panel in which FRP skin layers were arranged on both surfaces of a core material. The core material has a thickness of 50
mm lightweight calcium silicate plate (weight: 5500 g /
m ² ), and a phenol resin is used as a matrix resin in the FRP skin layer (resin weight: 5000 g /
m ² ), glass roving cloth (weight per layer: 5)
80 g / m ² ) were laminated in five plies, which were arranged on the upper and lower skin layers (total weight of this cloth: 5800 g / m)
m ² ). Also, 1200 g / m ² of talc was added to the FRP skin layer as an inorganic filler.

【００２３】その結果、パネル全体に対する無機系材料
の重量構成は７１重量％であった。このパネル構成（ト
ータル厚み：５６ｍｍ）にて、幅６００ｍｍ、長さ２４
００ｍｍに成形した耐火パネルを、スパン２１００ｍｍ
で４点曲げ（圧子間隔：７００ｍｍ）試験した結果、曲
げ強度は５２ＭＰａと十分に高い値が得られた。また、
ＪＩＳ−Ａ−１３０４に規定の３０分耐火試験を行った
結果、パネル裏面温度を１３０℃（２６０℃以下が合
格）と十分に低く抑えることができた。As a result, the weight composition of the inorganic material relative to the entire panel was 71% by weight. With this panel configuration (total thickness: 56 mm), width 600 mm, length 24
A refractory panel molded to 00 mm has a span of 2100 mm
As a result of a four-point bending test (indenter interval: 700 mm), a sufficiently high bending strength of 52 MPa was obtained. Also,
As a result of conducting a 30-minute fire resistance test specified in JIS-A-1304, the rear surface temperature of the panel was able to be sufficiently suppressed to 130 ° C. (260 ° C. or less passed).

【００２４】実施例２ 実施例１に比べ、コア材に厚さ３０ｍｍの軽量珪酸カル
シウム板（重量：３３００ｇ／ｍ² ）を用い、フェノー
ル樹脂重量を８０００ｇ／ｍ² とし、タルクを添加しな
かった。その他は実施例１と同様にして試験したとこ
ろ、パネル全体に対する無機系材料の重量構成は５３重
量％であり、曲げ強度は５５ＭＰａ、３０分耐火試験裏
面温度は１６０℃と良好な結果が得られた。Example 2 Compared with Example 1, a lightweight calcium silicate plate (weight: 3300 g / m ² ) having a thickness of 30 mm was used for the core material, the phenol resin weight was 8000 g / m ^2, and no talc was added. . Other than the above, the test was conducted in the same manner as in Example 1. The weight composition of the inorganic material with respect to the entire panel was 53% by weight, the bending strength was 55 MPa, and the 30-minute fireproof test back surface temperature was 160 ° C. Was.

【００２５】実施例３ 実施例１に比べ、ガラスロービングクロスを上下ＦＲＰ
スキン層において２プライ積層し（クロス総重量：２３
２０ｇ／ｍ² ）、フェノール樹脂重量を２１００ｇ／ｍ
² とし、タルク充填量をを２４０ｇ／ｍ² に変更した以
外、実施例１と同様にして試験した。パネル全体に対す
る無機系材料の重量構成は７９重量％であり、曲げ強度
は２３ＭＰａ、３０分耐火試験裏面温度は１３０℃と良
好な結果が得られた。Example 3 Compared to Example 1, the glass roving cloth was moved up and down by FRP.
Two plies are laminated on the skin layer (total cloth weight: 23
20 g / m ² ), and the phenol resin weight is 2100 g / m ^2
The test was performed in the same manner as in Example 1 except that the talc filling amount was changed to 240 g / m ² . The weight composition of the inorganic material with respect to the entire panel was 79% by weight, the bending strength was 23 MPa, and the 30 minute fire resistance test back surface temperature was 130 ° C., which was a good result.

【００２６】比較例１ コア材を厚さ１５ｍｍの軽量珪酸カルシウム板（重量：
１６５０ｇ／ｍ² ）とし、フェノール樹脂重量を９００
０ｇ／ｍ² とし、タルクを添加しなかったこと以外、実
施例１と同様にして試験した。パネル全体に対する無機
系材料の重量構成は４５重量％であり、曲げ強度は４７
ＭＰａ、３０分耐火試験裏面温度は３００℃となり、と
くに耐火性能に劣っていた。Comparative Example 1 A lightweight calcium silicate plate having a thickness of 15 mm (weight:
1650 g / m ² ) and the phenol resin weight is 900
The test was carried out in the same manner as in Example 1 except that 0 g / m ^{2 was used} and talc was not added. The weight composition of the inorganic material with respect to the entire panel was 45% by weight, and the bending strength was 47%.
MPa, 30 minutes fire resistance test The back surface temperature was 300 ° C., and the fire resistance was particularly poor.

【００２７】比較例２ 実施例１に比べ、ガラスロービングクロスを上下ＦＲＰ
スキン層において１プライづつとし（クロス総重量：１
１６０ｇ／ｍ² ）、フェノール樹脂重量を１２００ｇ／
ｍ² とし、タルクを２４０ｇ／ｍ² 添加して試験した。
パネル全体に対する無機系材料の重量構成は８５重量％
となり、曲げ強度は８．７ＭＰａ、３０分耐火試験裏面
温度は１７０℃となり、とくに曲げ強度に劣っていた。Comparative Example 2 Compared to Example 1, the glass roving cloth was
One ply in the skin layer (total cloth weight: 1
160 g / m ² ) and the phenol resin weight is 1200 g / m ²
m ^2, and talc was added at 240 g / m ² for testing.
85% by weight of inorganic material based on the entire panel
The bending strength was 8.7 MPa, the back temperature of the 30 minute fire resistance test was 170 ° C., and the bending strength was particularly poor.

【００２８】[0028]

【発明の効果】以上説明したように、本発明の耐火パネ
ルによれば、コア材、フェノール樹脂を用いたＦＲＰス
キン層からなるパネル全体に対する無機系材料の重量構
成を５０〜８２重量％の範囲とすることにより、優れた
耐火性能と、パネルに必要な強度、剛性との両方を、同
時に達成できる。As described above, according to the refractory panel of the present invention, the weight composition of the inorganic material is in the range of 50 to 82% by weight based on the whole panel comprising the core material and the FRP skin layer using phenol resin. By doing so, both excellent fire resistance and the strength and rigidity required for the panel can be achieved simultaneously.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の一実施態様に係る耐火パネルの部分断
面図である。FIG. 1 is a partial cross-sectional view of a fireproof panel according to one embodiment of the present invention.

【図２】本発明の別の実施態様に係る耐火パネルの部分
断面図である。FIG. 2 is a partial cross-sectional view of a fireproof panel according to another embodiment of the present invention.

【図３】本発明のさらに別の実施態様に係る耐火パネル
の部分断面図である。FIG. 3 is a partial cross-sectional view of a fireproof panel according to yet another embodiment of the present invention.

【図４】本発明のさらに別の実施態様に係る耐火パネル
の部分断面図である。FIG. 4 is a partial cross-sectional view of a fireproof panel according to still another embodiment of the present invention.

【符号の説明】[Explanation of symbols]

１、１１、２１、３１ 耐火パネル ２、１２、２２、３２ コア材 ３、１３、２３、３３ ＦＲＰスキン層 ２４、３４ リブ 1, 11, 21, 31 fireproof panel 2, 12, 22, 32 core material 3, 13, 23, 33 FRP skin layer 24, 34 rib

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.⁷ 識別記号 ＦＩ テーマコート゛(参考） Ｅ０４Ｃ 2/26 Ｅ０４Ｃ 2/26 Ｒ Ｆターム(参考） 2E001 DE01 FA03 FA07 FA11 FA14 GA42 HA01 HA02 HA03 HA07 HA21 HA32 HD11 JA06 JA22 JA25 JA29 JB07 2E162 CA01 CA02 CA05 CA06 CA14 CA21 CA35 CD04 FA00 FA14 FA16 FA20 FB07 FD07 4F100 AA00A AA03A AC10B AC10C AC10H AG00B AG00C AK33B AK33C BA02 BA03 BA06 BA10A BA10B BA10C DB00B DB00C DG12B DG12C DH02B DH02C GB07 GB08 JJ07 JK01 JK04 YY00 YY00A YY00B YY00C ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. ⁷ Identification symbol FI Theme coat ゛ (Reference) E04C 2/26 E04C 2/26 R F-term (Reference) 2E001 DE01 FA03 FA07 FA11 FA14 GA42 HA01 HA02 HA03 HA07 HA21 HA32 HD11 JA06 JA22 JA25 JA29 JB07 2E162 CA01 CA02 CA05 CA06 CA14 CA21 CA35 CD04 FA00 FA14 FA16 FA20 FB07 FD07 4F100 AA00A AA03A AC10B AC10C AC10H AG00B AG00C AK33B AK33C BA02 BA03 BA06 BA10A02 JBDBB00B12B02B00 YY00B YY00C

Claims (5)

【特許請求の範囲】[Claims] 【請求項１】 無機材料からなるコア材の少なくとも片
面にフェノール樹脂をマトリックス樹脂とするＦＲＰス
キン層を設けたパネルであって、パネル全体の無機系材
料が５０〜８２重量％の範囲にあることを特徴とする耐
火パネル。1. A panel in which an FRP skin layer using a phenol resin as a matrix resin is provided on at least one surface of a core material made of an inorganic material, wherein the inorganic material of the entire panel is in a range of 50 to 82% by weight. Characterized by fireproof panel. 【請求項２】 コア材の重量が３ｋｇ／ｍ² 以下であ
る、請求項１の耐火パネル。2. The fireproof panel according to claim 1, wherein the weight of the core material is 3 kg / m ² or less. 【請求項３】 コア材の厚み方向に延びるリブを有す
る、請求項１または２の耐火パネル。3. The fireproof panel according to claim 1, further comprising a rib extending in a thickness direction of the core material. 【請求項４】 リブがＦＲＰスキン層と一体に成形され
ている、請求項３の耐火パネル。4. The fireproof panel of claim 3, wherein the ribs are formed integrally with the FRP skin layer. 【請求項５】 リブの配設ピッチがコア材の厚みの０．
５〜１０倍の範囲にある、請求項３または４の耐火パネ
ル。5. The arrangement pitch of the ribs is set at 0.
5. The refractory panel of claim 3 or 4, wherein the panel is in the range of 5 to 10 times.