JP2001206790A - Coloring glaze - Google Patents
Coloring glazeInfo
- Publication number
- JP2001206790A JP2001206790A JP2000013580A JP2000013580A JP2001206790A JP 2001206790 A JP2001206790 A JP 2001206790A JP 2000013580 A JP2000013580 A JP 2000013580A JP 2000013580 A JP2000013580 A JP 2000013580A JP 2001206790 A JP2001206790 A JP 2001206790A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- glaze
- feldspar
- base
- kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、成形した直後の
素地に施す色化粧釉（色釉）に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a color glaze applied to a base immediately after molding.
【０００２】[0002]
【従来の技術】周知のように通常の作陶においては、色
化粧釉は成形した素地を乾燥して素焼きをした後に施し
ている。2. Description of the Related Art As is well known, in normal pottery making, a color decorative glaze is applied after drying a formed base and firing it.
【０００３】これは、主に長石（陶石）、ろう石、カオ
リンを等量前後の重量比率で配合したベース釉（基礎
釉）に、着色顔料と水を加えた慣用の色化粧釉は、素地
との膨張ないしは収縮係数の差が大きいため、色化粧釉
がひび割れや剥離を起こすからである。[0003] This is a conventional color decorative glaze made by adding a coloring pigment and water to a base glaze (basic glaze) in which feldspar (porcelain stone), pyroxene, and kaolin are blended in approximately equal weight ratios. This is because the difference in the coefficient of expansion or contraction from the base material is large, so that the colored decorative glaze cracks or peels off.
【０００４】従って従来の作陶には時間がかかるととも
に、近年行われている短時間の作陶体験も、成形と色化
粧釉掛けの連続した体験ができない状況にある。[0004] Therefore, conventional pottery making takes a long time, and even in the recent short-term pottery making experience, it is not possible to continuously experience molding and color makeup glaze.
【０００５】[0005]
【発明が解決しようとする課題】この発明は、従来の上
記のような作陶状況に鑑み、成形直後の素地に施すこと
が可能な色化粧釉、特にベース釉を提供することを課題
としている。SUMMARY OF THE INVENTION It is an object of the present invention to provide a color decorative glaze, particularly a base glaze, which can be applied to a base immediately after molding in view of the above-mentioned conventional ceramic making conditions. .
【０００６】[0006]
【課題を解決するための手段】この発明に係る色化粧釉
は、長石６０重量％前後、カオリン２０重量％前後、蛙
目粘土２０重量％前後からなるベース釉に、着色顔料と
水を配合することからなる。The color decorative glaze according to the present invention comprises a base glaze comprising about 60% by weight of feldspar, about 20% by weight of kaolin, and about 20% by weight of Frogme clay, which is mixed with a coloring pigment and water. Consisting of
【０００７】一般には、ベース釉は、長石５５〜６５重
量％、カオリン１５〜２５重量％及び蛙目粘土１５〜２
５重量％で形成することができる。In general, the base glaze comprises 55 to 65% by weight of feldspar, 15 to 25% by weight of kaolin and 15 to 2% of Frogme clay.
It can be formed at 5% by weight.
【０００８】着色顔料としては、一般には、Ａｌ、Ｓ
ｉ、Ｃｒ、Ｍｎ、Ｆｅ、Ｃｏ、Ｎｉ、Ｃｕ、Ｚｎ、Ｓ
ｅ、Ｚｒ、Ｃｄ、Ｔｉ、Ｖ、Ｍｇ、Ｃａ、Ｐｂ、Ｓｎ、
Ｓｂ、Ｐｒ等の金属の酸化物や炭酸塩などを一種以上含
む無機顔料を用いることができ、ベース釉に対しては、
慣用的な配合比（例えばベース釉１００に対して８〜１
０の重量比）で配合することができる。[0008] Generally, Al, S
i, Cr, Mn, Fe, Co, Ni, Cu, Zn, S
e, Zr, Cd, Ti, V, Mg, Ca, Pb, Sn,
Inorganic pigments containing one or more oxides or carbonates of metals such as Sb and Pr can be used.
Conventional compounding ratio (for example, 8 to 1 for 100 base glazes)
(Weight ratio of 0).
【０００９】水も慣用的な量、例えばベース釉と着色顔
料の合計重量前後の量（例えばベース釉と着色顔料１０
０に対して、８０〜１２０の重量比）用いることができ
る。Water is also used in a conventional amount, for example, an amount around the total weight of the base glaze and the color pigment (for example, the base glaze and the color pigment 10).
0 to 80) (weight ratio of 80 to 120).
【００１０】[0010]
【実施例】実施例１ 水分を約２５重量％含む慣用の陶土により、約３０分／
個の時間で、複数個の茶碗類と皿類の素地を成形した
後、直ちに長石５５重量％、カオリン２４重量％、蛙目
粘土２１重量％からなるベース釉に、濃ブルー色顔料
（Ｃｏ、Ａｌ、Ｚｎの酸化物を含む海碧類）を、１０：
０．８の重量比（約７．４重量％）で配合するとともに
ベース釉と顔料の重量とほぼ同量の水を加えて形成した
濃ブルー色化粧釉を、約２０分／個の時間施した。これ
を４日間自然乾燥した後、透明釉（長石５８重量％、石
灰１７重量％、蛙目粘土９重量％、珪石１０重量％、亜
鉛華３重量％、炭酸バリウム３重量％）をスプレーで施
し、これを焼成窯に入れて、１２６０℃の温度で１８時
間焼成し、この後２４時間かけて冷却した。これにより
得られた茶碗類、皿類の製品には、ひび割れや剥がれの
欠陥は全く認められなかった。EXAMPLE 1 A conventional porcelain clay containing about 25% by weight of water was used for about 30 minutes /
After a plurality of bowls and dishes are formed in a time, the base glaze consisting of 55% by weight of feldspar, 24% by weight of kaolin and 21% by weight of Frogme clay is immediately coated with a deep blue pigment (Co, Sea marine species containing oxides of Al and Zn)
0.8% by weight (approximately 7.4% by weight) and a dark blue makeup glaze formed by adding approximately the same amount of water as the weight of the base glaze and the pigment were applied for approximately 20 minutes / piece. did. After air drying for 4 days, a transparent glaze (58% by weight of feldspar, 17% by weight of lime, 9% by weight of Frogme clay, 10% by weight of silica stone, 3% by weight of zinc white, 3% by weight of barium carbonate) is applied by spraying. This was placed in a firing kiln, fired at a temperature of 1260 ° C. for 18 hours, and then cooled over 24 hours. No cracking or peeling defects were observed in the bowls and dishes obtained by this.
【００１１】実施例２ ベース釉として、長石６２重量％、カオリン２３重量
％、蛙目粘土１５重量％からなるもの、着色顔料とし
て、イエロー色顔料（Ｚｒ、Ｓｉ、Ｐｒの酸化物を含む
プラセオジム黄類）を１０：１の重量比（約９重量％）
で、及び透明釉として、長石５７重量％、石灰１５重量
％、蛙目粘土１３重量％、珪石８重量％、亜鉛華５重量
％、炭酸バリウム２重量％を含むものを用いた以外は実
施例１とほぼ同一の条件の下で、複数個の茶碗類、皿類
を作製したところ、いずれにもひび割れ、剥がれは認め
られなかった。Example 2 A base glaze consisting of 62% by weight of feldspar, 23% by weight of kaolin and 15% by weight of Frogme clay, and a yellow pigment (praseodymium yellow containing oxides of Zr, Si and Pr) as a coloring pigment Class) in a 10: 1 weight ratio (about 9% by weight)
Example 2 except that a glaze containing 57% by weight of feldspar, 15% by weight of lime, 13% by weight of Frogme clay, 8% by weight of silica, 5% by weight of zinc white, and 2% by weight of barium carbonate was used as the transparent glaze. When a plurality of bowls and dishes were prepared under substantially the same conditions as in 1, no cracking or peeling was observed in any of them.
【００１２】実施例３ ベース釉として、長石６０重量％、カオリン１８重量
％、蛙目粘土２２重量％からなるもの、着色顔料とし
て、ピンク色顔料（Ａｌ、Ｍｎの酸化物を含む陶試紅
類）を１０：１の重量比（約９重量％）で、及び透明釉
として、長石６１重量％、石灰１４重量％、蛙目粘土１
０重量％、珪石８重量％、亜鉛華４重量％、炭酸バリウ
ム３重量％を含むものを用いた以外は実施例１とほぼ同
一の条件下で、複数個の茶碗類、皿類を作製したとこ
ろ、いずれにも欠陥は認められなかった。Example 3 A base glaze composed of 60% by weight of feldspar, 18% by weight of kaolin, and 22% by weight of Frogme clay, and a pink pigment as a coloring pigment (ceramic lipsticks containing oxides of Al and Mn) At a weight ratio of 10: 1 (about 9% by weight) and as a transparent glaze, 61% by weight of feldspar, 14% by weight of lime,
A plurality of bowls and dishes were prepared under substantially the same conditions as in Example 1 except that a material containing 0% by weight, 8% by weight of silica stone, 4% by weight of zinc white, and 3% by weight of barium carbonate was used. However, no defects were found in any of them.
【００１３】実施例４ ベース釉として、長石６３重量％、カオリン１６重量
％、蛙目粘土２１重量％からなるもの、着色顔料とし
て、ピーコックグリーン色顔料（Ｚｎ、Ｃｏ、Ａｌ、Ｃ
ｒの酸化物を含む）、及び透明釉として、長石５５重量
％、石灰１４重量％、蛙目粘土８重量％、珪石１３重量
％、亜鉛華７重量％、炭酸バリウム３重量％を含むもの
を用いた以外は実施例１とほぼ同一の条件で、複数個の
茶碗類、皿類を作製したところ、欠陥は認められなかっ
た。Example 4 A base glaze composed of 63% by weight of feldspar, 16% by weight of kaolin and 21% by weight of Frogme clay, and a peacock green color pigment (Zn, Co, Al, C) as a coloring pigment
and a transparent glaze containing 55% by weight of feldspar, 14% by weight of lime, 8% by weight of Frogme clay, 13% by weight of quartzite, 7% by weight of zinc white and 3% by weight of barium carbonate. A plurality of bowls and dishes were prepared under substantially the same conditions as in Example 1 except that they were used, and no defects were observed.
【００１４】実施例５ ベース釉として、長石５８重量％、カオリン１８重量
％、蛙目粘土２４重量％からなるもの、着色顔料とし
て、ブラック色顔料（Ｃｏ、Ｃｒ、Ｆｅの酸化物等を含
む）、及び透明釉として、長石５５重量％、石灰１９重
量％、蛙目粘土１０重量％、珪石１０重量％、亜鉛華４
重量％、炭酸バリウム２重量％を含むものを用いた以外
は実施例１とほぼ同一の条件で、複数個の茶碗類、皿類
を作製したところ、欠陥は認められなかった。Example 5 A base glaze comprising 58% by weight of feldspar, 18% by weight of kaolin and 24% by weight of Frogme clay, and a black pigment (including oxides of Co, Cr and Fe) as a coloring pigment And as transparent glaze, 55% by weight of feldspar, 19% by weight of lime, 10% by weight of Frogme clay, 10% by weight of silica, 4% of zinc white
A plurality of bowls and dishes were prepared under substantially the same conditions as in Example 1 except that the composition contained 2% by weight and 2% by weight of barium carbonate. No defect was found.
【００１５】実施例６ ベース釉として、長石６２重量％、カオリン１８重量
％、蛙目粘土２０重量％からなるもの、着色顔料とし
て、グリーン色顔料（Ｃｒ、Ａｌの酸化物を含むクロム
緑類）、及び透明釉として、長石６３重量％、石灰１５
重量％、蛙目粘土９重量％、珪石８重量％、亜鉛華４重
量％、炭酸バリウム１重量％を含むものを用いた以外は
実施例１とほぼ同一の条件で、複数個の茶碗類、皿類を
作製したところ、欠陥は認められなかった。Example 6 A base glaze composed of 62% by weight of feldspar, 18% by weight of kaolin and 20% by weight of Frogme clay, and a green pigment (chromium green containing oxides of Cr and Al) as a coloring pigment , As transparent glaze, feldspar 63% by weight, lime 15
A plurality of teacups were prepared under substantially the same conditions as in Example 1 except that a composition containing 1% by weight, 9% by weight of Frogme clay, 8% by weight of silica stone, 4% by weight of zinc white and 1% by weight of barium carbonate was used. When the dishes were prepared, no defects were observed.
【００１６】実施例７ ベース釉として、長石５７重量％、カオリン２３重量
％、蛙目粘土２０重量％からなるもの、着色顔料とし
て、ブルー色顔料（Ｚｒ、Ｓｉ、Ｖの酸化物を含むバナ
ジウム青類）、及び透明釉として、長石５８重量％、石
灰１５重量％、蛙目粘土９重量％、珪石１１重量％、亜
鉛華５重量％、炭酸バリウム２重量％を含むものを用い
た以外は実施例１とほぼ同一の条件で、複数個の茶碗
類、皿類を作製したところ、欠陥は認められなかった。Example 7 A base glaze comprising 57% by weight of feldspar, 23% by weight of kaolin and 20% by weight of Frogme clay, and a blue pigment (vanadium blue containing oxides of Zr, Si, V) as a coloring pigment Class) and transparent glaze, except that those containing 58% by weight of feldspar, 15% by weight of lime, 9% by weight of Frogme clay, 11% by weight of silica stone, 5% by weight of zinc white and 2% by weight of barium carbonate were used. When a plurality of bowls and dishes were prepared under substantially the same conditions as in Example 1, no defects were found.
【００１７】実施例８ ベース釉として、長石５９重量％、カオリン２０重量
％、蛙目粘土２１重量％からなるもの、着色顔料とし
て、レッド色顔料（Ｚｒ、Ｓｉの酸化物、Ｃｄの硫化
物、Ｓｅを含むセレンカドミウム赤類やＦｅの酸化物の
べンガラ類）、及び透明釉として、長石５９重量％、石
灰１４重量％、蛙目粘土１０重量％、珪石９重量％、亜
鉛華５重量％、炭酸バリウム３重量％を含むものを用い
た以外は実施例１とほぼ同一の条件で、複数個の茶碗
類、皿類を作製したところ、欠陥は認められなかった。Example 8 A base glaze consisting of 59% by weight of feldspar, 20% by weight of kaolin and 21% by weight of Frogme clay, and a red pigment (Zr, oxide of Si, sulfide of Cd, Selenium cadmium reds containing Se and red oxides of Fe oxide) and as transparent glaze, feldspar 59% by weight, lime 14% by weight, Frogme clay 10% by weight, silica stone 9% by weight, zinc white 5% by weight When a plurality of bowls and dishes were prepared under substantially the same conditions as in Example 1 except that a barium carbonate containing 3% by weight was used, no defect was observed.
【００１８】[0018]
【発明の効果】以上説明したところから明らかなよう
に、この発明の色化粧釉によれば、成形した直後の素地
に施しても、ひび割れや剥がれの欠陥が生じないので、
作陶時間を大幅に短縮することができる。As is apparent from the above description, according to the color decorative glaze of the present invention, even if it is applied to the base immediately after molding, cracks and peeling defects do not occur.
Pottery making time can be greatly reduced.
【００１９】従って短時間の作陶体験においても、成形
と色化粧釉掛けの両者を連続した形で体験することがで
きる。Therefore, even in a short period of pottery making experience, it is possible to experience both molding and color makeup glaze in a continuous form.
Claims (2)
％前後、蛙目粘土２０重量％前後からなるベース釉に、
着色顔料と水を配合してなる色化粧釉。1. A base glaze composed of about 60% by weight of feldspar, about 20% by weight of kaolin, and about 20% by weight of Frogme clay.
A color makeup glaze composed of a color pigment and water.
オリン１５〜２５重量％及び蛙目粘土１５〜２５重量％
からなる、請求項１記載の色化粧釉。2. A base glaze comprising 55 to 65% by weight of feldspar, 15 to 25% by weight of kaolin and 15 to 25% by weight of Frogme clay.
The color decorative glaze according to claim 1, comprising: