KR20190047539A - Glace Composition for Ceramic Ware Comprising Ashes from Peanut shell and Preparation Method thereof - Google Patents
Glace Composition for Ceramic Ware Comprising Ashes from Peanut shell and Preparation Method thereof Download PDFInfo
- Publication number
- KR20190047539A KR20190047539A KR1020170141535A KR20170141535A KR20190047539A KR 20190047539 A KR20190047539 A KR 20190047539A KR 1020170141535 A KR1020170141535 A KR 1020170141535A KR 20170141535 A KR20170141535 A KR 20170141535A KR 20190047539 A KR20190047539 A KR 20190047539A
- Authority
- KR
- South Korea
- Prior art keywords
- peanut shell
- shell material
- glaze
- composition
- rti
- Prior art date
Abstract
Description
본 개시는 땅콩껍질재를 포함하는 도자기용 유약 조성물 및 이의 제조방법에 관한 것이다.This disclosure relates to a glaze composition for a pottery comprising a peanut shell material and a method of making the same.
이 부분에 기술된 내용은 단순히 본 개시에 대한 배경정보를 제공할 뿐 종래기술을 구성하는 것은 아니다.The description in this section merely provides background information on this disclosure and does not constitute prior art.
일반적으로 유약이란, 도자기의 표면에 점착되는 얇은 유리층으로서 도자기의 흡수성을 저하시키고 심미감을 표출시키며 도자기에 튼튼한 역할을 부여하는 역할을 한다. Generally, a glaze is a thin glass layer adhered to the surface of ceramics, which reduces the water absorption of ceramics, expresses aesthetics, and plays a role in imparting a strong role to ceramics.
즉, 유약은 도자기나 옹기류 등의 표면에 칠해지고 열처리 융착되어 그 표면에 광택 또는 무광택의 표면층을 형성시키기 위하여 사용되는 제제로서 투수성을 없애고 미적 효과를 증가시키며 도자기의 강도를 향상시킬 수 있다.That is, the glaze is used to form a surface layer of gloss or matte on the surface of a ceramic or a pottery, and is heat-treated and fused to eliminate surface permeability, increase the aesthetic effect, and improve the strength of the ceramic .
도자기에 표면에 칠해져서 소성에 의해 광택을 띄게 하는 유약은 통상 장석, 규석, 고령토, 석회석, 활석, 형석, 골분을 주성분으로 구성된다. The glaze, which is painted on the surface of the ceramics and made glossy by firing, is mainly composed of feldspar, silica, kaolin, limestone, talc, fluorite, and bone meal.
이와 같이 종래의 도자기용 유약은 흙이나 돌가루만을 사용하여 유약을 만들기 때문에 나무재를 사용하였던 과거 고려, 조선 시대의 청자나 백자와 같은 고급스러운 자연미를 살리지 못하는 한계가 있었다.Thus, conventional glazes for ceramics use gypsum only by using soil or stone powder, so there was a limit in using gypsum in the past, such as celadon and white porcelain in the past.
종래기술인 등록특허 제 10-1079706호의 솔잎, 콩깍지재, 장석, 대합조개 껍질 등을 사용한 유약 조성물, 등록특허 제 10-0387920호의 산화철, 코발트 등을 사용한 유약 조성물 등은 발색력이 좋지 못해 역시 고급스러운 자연미를 살리지 못하는 단점이 있었다.Glaze composition using pine needle, bean pod material, feldspar, clam shell, etc. of the prior art Patent No. 10-1079706, glaze composition using iron oxide, cobalt of the registered patent No. 10-0387920, etc., It can not be saved.
이에 본 발명자는 따뜻하고 부드러운 느낌을 주는 고급스러운 자연미를 살릴 수 있는 도자기용 유약을 개발하고자 예의 연구를 거듭하였고, 그 결과 땅콩껍질의 재를 첨가하여 도자기용 유약을 제조하여 도자기에 적용하는 경우 부드럽고, 따뜻한 느낌을 발현할 수 있으며 매트(matt)한 특징에 의해 세련된 느낌을 발현할 수 있다는 것을 알게 되어 본 발명을 완성하기에 이르렀다.Accordingly, the inventor of the present invention has made intensive studies to develop a glaze for ceramics which can provide a warm, soft feeling and a luxurious natural beauty. As a result, when a glaze for ceramics is added by adding peanut shell ashes, A warm feeling can be expressed, and a sophisticated feeling can be expressed by a matt feature. Thus, the present invention has been completed.
본 발명의 일 목적은 따뜻하고 부드러운 느낌과 세련된 느낌을 발현시켜 고급스러운 자연미를 살릴 수 있는 환경 친화적인 도자기용 유약 및 이의 제조방법을 제공하는 것이다.It is an object of the present invention to provide an environmentally friendly glaze for ceramics and a method for producing the glaze which can create a warm and soft feeling and a sophisticated feel,
본 발명의 일 목적을 달성하기 위해, 본 발명은 땅콩껍질을 태운 재의 분말인 땅콩껍질재 및 통상의 유약 원료를 포함하는 땅콩껍질재를 포함한 도자기용 유약 조성물을 제공한다.In order to accomplish one object of the present invention, the present invention provides a glaze composition for a pottery comprising a peanut shell material comprising a peanut shell material, which is a powder of the material bearing the peanut shell, and a peanut shell material comprising a common glaze material.
땅콩껍질재는 땅콩껍질을 태우고 남은 재를 말한다. 이러한 땅콩껍질재를 도자기용 유약의 원료로 사용하는 경우, 환경 친화적이고 고급스러운 자연미를 나타내는 도자기를 제공할 수 있다.The peanut shell is the ash left after burning the peanut shell. When such a peanut shell material is used as a raw material of a glaze for ceramics, it is possible to provide a ceramics exhibiting environment-friendly and luxurious natural beauty.
땅콩껍질재는 산화 알루미늄(Al2O3)이 많이 함유되어 이를 이용하여 도자기용 유약을 제조하는 경우 유약의 물성을 높일 수 있고, 유약의 점성을 높여 물처럼 흐르는 것을 방지할 수 있으며 광이 덜 나는 매트(matt)한 느낌을 낼 수 있다. 땅콩껍질재를 도자기용 유약에 첨가하는 경우 청자 유약, 이라보 유약, 천목 유약, 분청 투명 유약, 매트 유약 등에 적용할 수 있다. 특히 땅콩껍질재에 함유되는 산화철 때문에 청자 유약, 이라보 유약 및 천목 유약에 적용하는 것이 바람직하다. 다만, 반드시 이에 한정되는 것은 아니고 공지의 어떠한 유약에도 적용될 수 있다. 또한, 땅콩껍질재는 다량의 실리카(SiO2) 성분을 포함하므로, 땅콩껍질재를 첨가하여 유약을 제조하는 경우 별도로 규석을 첨가하지 않을 수 있다(시험예 참조).The peanut shell material contains a large amount of aluminum oxide (Al 2 O 3 ). When the glaze for ceramics is manufactured by using it, it is possible to increase the physical properties of the glaze, increase the viscosity of the glaze and prevent it from flowing like water, I can feel a matt feeling. When the peanut shell material is added to the glaze for ceramics, it can be applied to the celadon glaze, the iris glaze, the glaze glaze, the clear glaze, and the mat glaze. Especially, it is preferable to apply to the celadon glaze, the iris glaze and the glaze glaze due to the iron oxide contained in the peanut shell material. However, the present invention is not limited thereto and can be applied to any known glaze. In addition, since the peanut shell material contains a large amount of silica (SiO2) component, when peanut shell material is added to produce glaze, silica may not be added separately (see Test Example).
통상의 도자기용 유약 원료에는 이 기술분야에서 널리 사용되는 도자기 유약 원료 성분이 모두 포함될 수 있으며, 구체적으로 장석과 도석, 백운석, 석회석, 규석 및 이들의 혼합물로 이루어진 군으로부터 선택된 것을 포함할 수 있으나, 반드시 이에 제한되는 것은 아니다.Conventional ceramics glaze raw materials may include ceramics glaze raw materials widely used in this technical field and may specifically include feldspar and selected from the group consisting of stones, dolomite, limestone, silica and mixtures thereof, But it is not necessarily limited thereto.
통상의 유약 원료의 성분 중 장석이나 도석의 알카리 성분은 유약 원료 중 규석 성분과 반응하며 유리질을 만드는 융제 역할을 하며, 석회석과 석회석의 일종인 백운석은 유약을 더 잘 녹게 한다. 이들의 혼합 비율은 본 발명의 속하는 기술분야의 통상의 지식을 가진 자에게 자명한 것이다.The feldspar or the alkaline component of the stones of the glaze raw material reacts with the glaze component of the glaze raw material and serves as a flux for making the vitreous material. Dolomite, which is a kind of limestone and limestone, melts the glaze more easily. These mixing ratios are apparent to those skilled in the art to which the present invention belongs.
본 발명의 일 실시예에 따른 도자기용 유약 조성물은 땅콩껍질재 10∼60 중량% 및 통상의 유약 원료 40∼90중량%를 혼합하여 제조될 수 있다. 다만, 땅콩껍질재의 함량이 10~60중량%의 범위를 벗어나는 경우, 따뜻하고 부드러운 느낌을 주는 고급스러운 자연미의 발현이 미미할 수 있다.The glaze composition for ceramics according to an embodiment of the present invention may be prepared by mixing 10 to 60% by weight of a peanut shell material and 40 to 90% by weight of a common glaze material. However, when the content of the peanut shell material is out of the range of 10 to 60% by weight, the appearance of luxurious natural beauty giving a warm and soft feeling may be insignificant.
또한, 본 발명의 일 실시예에 따른 도자기용 유약 조성물은 고령토, 점토, 탄산바륨, 도석, 활석, 백운석, 골회, 황토, 벤토 나이트, 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석, 산화아연 등을 제조하고자 하는 유약의 종류에 따라 더 포함할 수 있으며, 이는 땅콩껍질재를 포함한 도자기용 유약 조성물 100 중량부에 대하여 10∼50 중량부가 포함되는 것이 바람직하다.The glaze composition for ceramics according to one embodiment of the present invention may further comprise at least one selected from the group consisting of kaolin, clay, barium carbonate, talc, talc, dolomite, Tin and zinc oxide may be further added depending on the kind of the glaze to be produced, and it is preferable that 10 to 50 parts by weight of the glaze composition is contained in 100 parts by weight of the glaze composition including the peanut shell material.
본 발명의 일 실시예에 따른 도자기용 유약 조성물은 도자기에 적용되는 경우 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석 등의 발색 원료를 첨가하여 비취색, 올리브 그린색, 브라운 색 등을 나타낼 수 있다. The glaze composition for ceramics according to an embodiment of the present invention may be applied to ceramics by adding a coloring material such as copper oxide, cobalt oxide, manganese oxide, nickel oxide, titanium oxide and tin oxide to a jade color, olive green color, Lt; / RTI >
또한, 본 발명은 땅콩껍질재를 포함하는 도자기용 유약 조성물의 제조방법을 제공할 수 있다. 도자기용 유약 조성물의 제조방법은 땅콩껍질재를 준비하는 단계 및 땅콩껍질재와 통상의 유약 원료를 혼합하는 단계를 포함할 수 있다.In addition, the present invention can provide a method for manufacturing a glaze composition for a pottery comprising a peanut shell material. The method of making a glaze composition for a ceramics may comprise the steps of preparing a peanut shell and mixing the peanut shell with a conventional glaze raw material.
땅콩껍질재를 준비하는 단계는, 이 기술분야에서 이용되는 일반적인 방법으로 얻어질 수 있다. 예를 들면, 땅콩껍질이 타고 남은 재를 물에 넣어 분쇄 과정을 거친 다음 체를 이용하여 재 이외의 이물질을 걸러 준다. 체로 걸러 낸 땅콩껍질의 재가 침전되어 가라앉으면 침전된 재로부터 잿물을 분리해 내고(여러번 반복), 남아 있는 재를 건조시켜 분말 상태로 만들어서 사용할 수 있다.The step of preparing the peanut shell may be obtained by a general method used in this technical field. For example, the peanut shells are buried in the water, ground and ground, and then sieved to remove foreign matter other than ash. When the ash of the peanut husk that has been sieved is sedimented and settled, it is possible to separate the lye from the settled ashes (repeat several times) and dry the remaining ash to powder.
이와 같이 제조된 땅콩껍질재를 통상의 유약 원료와 혼합하여 본 발명의 일 실시예에 따른 도자기용 유약 조성물을 제조할 수 있다.The thus prepared peanut shell material can be mixed with a common glaze raw material to produce a glaze composition for a ceramics according to an embodiment of the present invention.
본 발명의 추가적인 해결수단은 아래에서 이어지는 설명에서 일부 설명될 것이고, 그 설명으로부터 부분적으로 용이하게 확인할 수 있게 되거나, 또는 본 발명의 실시에 의해 지득될 수 있다.Additional solutions of the invention will be set forth in part in the description which follows, and in part will be readily apparent from the description, or may be learned by practice of the invention.
전술한 일반적인 설명 및 다음의 상세한 설명 모두는 단지 예시적이고 설명을 위한 것이며 청구범위에 기재된 본 발명을 제한하지 않는다.It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention, as claimed.
본 발명에 따른 땅콩껍질재를 포함하는 도자기용 유약 조성물은 고급스러운 자연미를 살릴 수 있으며, 유약이 부드럽고 따뜻하며 고급스러운 느낌을 발현할 수 있다. 청자 유약, 이라보 유약, 천목 유약 등의 색유약 및 매트 유약 등의 제조에 사용될 수 있다.The glaze composition for a pottery including the peanut shell material according to the present invention can enjoy a luxurious natural beauty and a glaze can express a soft, warm and luxurious feeling. Celadon glaze, iribo glaze, glaze glaze, and the like.
도 1은 본 발명의 실시예1에 따라 산화분위기로 제조된 도자기 시험편이다.
도 2는 본 발명의 실시예2에 따라 환원분위기로 제조된 도자기 시험편이다.1 is a porcelain test piece produced in an oxidizing atmosphere according to Example 1 of the present invention.
2 is a porcelain test piece produced in a reducing atmosphere according to Example 2 of the present invention.
이하, 첨부된 도면을 참조하여 본 개시의 구체적인 실시형태에 대하여 상세하게 서술하도록 한다. Hereinafter, specific embodiments of the present disclosure will be described in detail with reference to the accompanying drawings.
다만, 본 개시의 구체적 일 실시 형태를 설명함에 있어, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 개시의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략한다. In the following description, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present disclosure unnecessarily obscure.
시험예: 땅콩껍질재 성분 분석Test Example: Peanut shell ingredient analysis
아래의 표 1은 XRF로 분석한 땅콩껍질재의 성분분석표이다. 표 1을 참조하면, 땅콩껍질재를 XRF를 사용하여 성분 분석한 결과를 파악할 수 있다. 땅콩껍질재는 산화알루미늄(Al2O3)을 포함할 수 있다. 산화알루미늄(Al2O3)은 도자기용 유약의 물성을 높일 수 있고, 유약의 점성을 높여 물처럼 흐르는 것을 방지할 수 있으며 광이 덜 나는 매트(matt)한 느낌을 낼 수 있게 한다. 땅콩껍질재는 산화알루미늄(Al2O3)이 약 21.54중량% 함유되어 있다. 땅콩껍질 재는 기존의 초목재에 소량만 함유되어 있는 산화알루미늄(Al2O3)이 다량으로 함유되어 있어 유약의 흐름성을 막아주며 유약 자체의 물성을 향상시켜 줄 수 있다.Table 1 below shows the compositional analysis of peanut shells analyzed by XRF. Referring to Table 1, the peanut shell material can be analyzed using XRF. It may comprise a peanut shell material aluminum oxide (Al 2 O 3). Aluminum oxide (Al 2 O 3 ) can increase the physical properties of the glaze for ceramics, increase the viscosity of the glaze, prevent it from flowing like water, and make it feel less matt. The peanut shell material contains about 21.54% by weight of aluminum oxide (Al 2 O 3 ). Peanut shells contain a large amount of aluminum oxide (Al 2 O 3 ), which is only contained in small quantities in existing super wood, which prevents the flow of glaze and can improve the physical properties of the glaze itself.
또한, 땅콩껍질재는 산화철(Fe2O3)을 포함할 수 있다. 산화철(Fe2O3)은 유약의 색상에 영향을 미친다. 산화분위기로 소성을 하는 경우, 산화철의 함유량이 적으면 흰색, 미색, 아이보리 색 등의 밝은 색을 띠며, 함유량이 많으면 검정색, 붉은색 등의 어두운 색을 띤다. 환원분위기로 소성을 하는 경우, 산화철의 함유량이 적으면 푸른색 등의 밝은 색을 띠며, 함유량이 많으면 검정색, 붉은색 등의 어두운 색을 띤다. 땅콩껍질재는 산화철(Fe2O3)이 약 16.09중량% 함유되어 있다. 땅콩껍질 재는 기존의 초목재에 통상 3~5중량% 가량 함유되는 산화철(Fe2O3)이 다량 함유되어 있어 산화철을 사용한 각종유약, 즉, 청자 유약, 이라보 유약, 천목 유약 등의 제조에 사용될 수 있다.In addition, the peanut shell material may comprise iron oxide (Fe 2 O 3 ). Iron oxide (Fe 2 O 3 ) affects the color of the glaze. When firing in an oxidizing atmosphere, when the content of iron oxide is small, it is light in color such as white, off-white, and ivory. When the content is large, it is dark in color such as black and red. When firing in a reducing atmosphere, when the content of iron oxide is small, it has a bright color such as blue. When the content is large, it has a dark color such as black and red. The peanut shell material contains about 16.09% by weight of iron oxide (Fe 2 O 3 ). The peanut shell material contains a large amount of iron oxide (Fe 2 O 3 ), which is usually contained in an amount of 3 to 5% by weight in the conventional super wood, and is used for the production of various kinds of glazes using iron oxide such as celadon glaze, Can be used.
또한, 땅콩껍질재는 실리카(SiO2)를 포함할 수 있다. 땅콩껍질재는 실리카(SiO2)가 약 38.52중량% 함유되어 있다. 땅콩껍질재는 실리카(SiO2)가 다량 함유되어 유약 제조시 규석이나 규사를 사용하지 않고서도 부드럽고 따뜻한 느낌을 발현하는 유약을 만들 수 있다.It may also include a silica material peanut shells (SiO 2). The silica material is peanut shells (SiO 2) is contained about 38.52% by weight. The peanut shell material contains a large amount of silica (SiO 2 ) and can produce a glaze that produces a soft and warm feeling without using silica or silica in the production of glaze.
실시예 1Example 1
장석, 석회석 및 땅콩껍질재를 아래 표 2에 나타난 성분들의 조성비에 따라 혼합하여 21가지 종류의 유약을 제조하였다. 이후 21 가지의 유약을 21개의 초벌구이한 백자시험편들에 시유하여 가마에 넣어 산화분위기로 1240℃에서 약 1 시간 동안 소성하였다. 도 1은 제조된 21개의 시험편의 사진이다.21 kinds of glaze were prepared by mixing the feldspar, limestone and peanut shell materials according to the composition ratios shown in Table 2 below. Then, 21 kinds of glaze were added to 21 pieces of unglazed white porcelain specimens and fired in an oxidizing atmosphere at 1240 ° C for about 1 hour in a kiln. Figure 1 is a photograph of the 21 specimens produced.
실시예 2Example 2
장석, 석회석 및 땅콩껍질재를 위의 표 2에 나타난 성분들의 조성비에 따라 혼합하여 21가지 종류의 유약을 제조하였다. 이후 21 가지의 유약을 21개의 초벌구이한 백자시험편들에 시유하여 가스가마에 넣어 환원분위기로 1240℃에서 약 1 시간 동안 소성하였다. 도 2는 제조된 21개의 시험편의 사진이다.Feldspar, limestone and peanut shells were mixed according to the composition ratio of the ingredients shown in Table 2 above to produce 21 types of glaze. Then, 21 kinds of glaze were added to 21 unglazed white porcelain test specimens and fired in a reducing furnace at 1240 ° C for about 1 hour in a gas kiln. Figure 2 is a photograph of the 21 specimens produced.
도 1 내지 도 2를 참조하면, 본 발명에 따른 도자기용 유약 조성물을 사용하여 백자 시험편에 시유하여 소성하는 경우, 별도의 발색 원료를 첨가하지 않고도 따뜻하고 부드러운 푸른색, 아이보리색, 검정색 등의 색상을 발현시킬 수 있다.1 and 2, when baking and baking a white flake test piece using the glaze composition for a ceramic according to the present invention, the color such as warm, soft blue, ivory, or black can be obtained without adding a separate coloring material Lt; / RTI >
본 실시예는 본 개시의 기술적 사상을 예시적으로 설명한 것에 불과하고, 본 개시가 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 개시의 본질적인 특성에서 벗어나지 않는 범위에서 본 실시예의 다양한 수정 및 변형이 가능할 것이다. 본 실시예는 본 개시의 기술적 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 따라서 본 실시예에 의하여 본 개시의 권리범위가 한정되는 것은 아니다. 본 개시의 보호범위는 청구범위에 의하여 해석되어야 하며, 그와 동등하거나 균등하다고 인정되는 모든 기술적 사상은 본 개시의 권리범위에 포함되는 것으로 해석되어야 한다.It will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present disclosure, It will be possible. The present embodiments are intended to illustrate and not to limit the technical spirit of the present disclosure, and thus the scope of the present disclosure is not limited by the present embodiment. The scope of protection of the present disclosure should be construed according to the scope of the claims, and all technical ideas which are deemed to be equivalent or equivalent should be construed as being included in the scope of the present disclosure.
Claims (6)
장석 및 석회석을 포함하는 통상의 유약원료
를 포함하는 땅콩껍질재를 포함하는 도자기용 유약 조성물.Peanut shell material, powder of ash; And
Conventional glaze raw materials including feldspar and limestone
≪ / RTI > wherein the peanut shell material comprises a peanut shell material.
상기 땅콩껍질재는 10~60중량%, 상기 통상의 유약원료는 40~90중량%인 것
을 특징으로 하는 땅콩껍질재를 포함하는 도자기용 유약 조성물.The method according to claim 1,
The peanut shell material is 10 to 60 wt%, and the conventional glaze material is 40 to 90 wt%
≪ / RTI > wherein the composition comprises a peanut shell material.
상기 통상의 유약원료는,
상기 장석은 30~80중량%, 상기 석회석은 10~60중량%인 것
을 특징으로 하는 땅콩껍질재를 포함하는 도자기용 유약 조성물.3. The method of claim 2,
The above-
The feldspar is 30 to 80% by weight, and the limestone is 10 to 60% by weight
≪ / RTI > wherein the composition comprises a peanut shell material.
고령토, 점토, 탄산바륨, 도석, 활석, 백운석, 골회, 황토, 벤토 나이트, 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석, 산화아연으로 이루어진 군으로부터 선택되는 하나 이상의 혼합물을 더 포함하는 것
을 특징으로 하는 땅콩껍질재를 포함하는 도자기용 유약 조성물.The method according to claim 1,
There may be further added at least one compound selected from the group consisting of kaolin, clay, barium carbonate, stoneware, talc, dolomite, alum, loess, bentonite, copper oxide, cobalt oxide, manganese oxide, nickel oxide, titanium oxide, tin oxide, Include
≪ / RTI > wherein the composition comprises a peanut shell material.
상기 혼합물은, 땅콩껍질재를 포함하는 유약 조성물 전체 100중량부에 있어서 10~50중량부인 것
을 특징으로 하는 땅콩껍질재를 포함하는 도자기용 유약 조성물.5. The method of claim 4,
The mixture is 10 to 50 parts by weight per 100 parts by weight of the entire glaze composition including the peanut shell material
≪ / RTI > wherein the composition comprises a peanut shell material.
장석 및 석회석을 포함하는 통상의 유약 원료와 상기 땅콩껍질재를 혼합하는 단계
를 포함하는 땅콩껍질재를 포함하는 도자기용 유약 조성물의 제조방법.Preparing a peanut shell material; And
Mixing the peanut shell material with a conventional glaze raw material including feldspar and limestone
≪ / RTI > wherein the peanut shell material comprises a peanut shell material.