JP2001000600A - Golf club and production of golf club head - Google Patents
Golf club and production of golf club headInfo
- Publication number
- JP2001000600A JP2001000600A JP11176033A JP17603399A JP2001000600A JP 2001000600 A JP2001000600 A JP 2001000600A JP 11176033 A JP11176033 A JP 11176033A JP 17603399 A JP17603399 A JP 17603399A JP 2001000600 A JP2001000600 A JP 2001000600A
- Authority
- JP
- Japan
- Prior art keywords
- golf club
- plating
- stainless steel
- plating layer
- club head
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ゴルフクラブ及び
ゴルフクラブヘッドの製造方法に関し、特にメッキ処理
されたゴルフクラブ及びゴルフクラブヘッドの製造方法
に関する。The present invention relates to a golf club and a method for manufacturing a golf club head, and more particularly, to a plated golf club and a method for manufacturing a golf club head.
【０００２】[0002]
【発明が解決しようとする課題】ゴルフクラブは一般的
にウッド形、アイアン形及びパターの３種類を有する。
これらゴルフクラブはシャフトの下端にゴルフクラブヘ
ッドが設けられている。前記アイアン形ゴルフクラブの
ヘッドは背面がほぼ平らなマッスルバック形状から背面
の中央部を切り欠くように凹部を形成したキャビティバ
ック形状へと変化した。さらに、よりスイートエリヤの
ワイド化、低重心化をするためにアンダーカットという
ソール上面をフェース側に深くえぐるように形成するキ
ャビティのタイプが登場している。Golf clubs generally have three types, a wood type, an iron type and a putter.
In these golf clubs, a golf club head is provided at a lower end of a shaft. The head of the iron-type golf club changed from a muscle back shape having a substantially flat back surface to a cavity back shape in which a recess was formed so as to cut out the center of the back surface. Furthermore, in order to make the sweet area wider and lower the center of gravity, an undercut type of cavity, which is formed so that the upper surface of the sole is deeply cut in the face side, has appeared.
【０００３】一方、素材についてはアイアン形ヘッドに
おいては軟鉄が多く用いられ、それに耐食性をもたせる
ためにメッキを行っていた。しかしながら、上述のよう
に深くえぐられたアンダーカットの部分はメッキの形成
が悪く、耐食性に必要なメッキ厚を確保することが難し
いという問題がある。その上、アンダーカットの部分に
はごみや水分が溜まりやすく腐食しやすくなっている。On the other hand, as a raw material, soft iron is often used in an iron type head, and plating is performed to impart corrosion resistance thereto. However, there is a problem that the undercut portion deeply formed as described above has poor plating formation, and it is difficult to secure a plating thickness necessary for corrosion resistance. In addition, dirt and moisture easily accumulate and corrode easily in the undercut portion.
【０００４】このような問題を解決するため、耐食性に
優れたステンレス鋼が用いられる。しかし、スレンレス
は素材のままでは軟らかいことが多く、例えばオーステ
ナイト系のＳＵＳ３０４はＪＩＳ規格ではロックウェル
硬度（Ｂスケール）ＨＲＢ９０以下となっており（固溶
化状態）、傷つきやすくなるという問題がある。また、
それ以上素材が硬くなってしまうと加工性が悪くなると
いう問題がある。In order to solve such a problem, stainless steel having excellent corrosion resistance is used. However, stainless steel is often soft as it is, and for example, austenitic SUS304 has a Rockwell hardness (B scale) of HRB90 or less according to JIS (solid solution state) and has a problem of being easily damaged. Also,
If the material becomes harder than that, there is a problem that workability deteriorates.
【０００５】そこで、本発明はこれらの課題に鑑みてな
されたものであり、美観に優れ、傷がつきにくいととも
に耐蝕性に優れたヘッドを備えたゴルフクラブ及びゴル
フクラブヘッドの製造方法を提供することを目的とす
る。Accordingly, the present invention has been made in view of these problems, and provides a golf club having a head having excellent aesthetics, being resistant to scratches and having excellent corrosion resistance, and a method of manufacturing a golf club head. The purpose is to:
【０００６】[0006]
【課題を解決するための手段】本発明の請求項１記載の
ゴルフクラブは、ステンレス鋼製の部材を有するゴルフ
クラブヘッドの少なくとも前記ステンレス鋼製の部材に
ビッカース硬度５００以上のメッキを施したものであ
る。このような構成を採用することにより、該メッキ層
の硬度がビッカース硬度で５００以上であるので、ゴル
フクラブヘッドの表面が傷つきにくくなっている。A golf club according to a first aspect of the present invention is a golf club head having a stainless steel member, wherein at least the stainless steel member is plated with a Vickers hardness of 500 or more. It is. By adopting such a configuration, the hardness of the plating layer is Vickers hardness of 500 or more, so that the surface of the golf club head is hardly damaged.
【０００７】また、請求項２記載のゴルフクラブは、前
記ステンレス鋼がオーステナイト系からなるものであ
る。このため、比較的軟らかい素材を加工すればよいの
で加工性を向上することができる。[0007] In the golf club according to the second aspect, the stainless steel is made of an austenitic steel. Therefore, it is sufficient to process a relatively soft material, so that workability can be improved.
【０００８】請求項３記載のゴルフクラブは、前記請求
項１又は２において、前記ステンレス鋼の硬度がロック
ウェル硬度（Ｂスケール）で９０以下のものである。こ
のため、素材が比較的軟らかく例えば上述のキャビティ
やアンダーカット等の加工性を向上することができる。According to a third aspect of the present invention, in the golf club according to the first or second aspect, the stainless steel has a Rockwell hardness (B scale) of 90 or less. For this reason, the material is relatively soft, and workability such as the above-described cavity and undercut can be improved.
【０００９】請求項４記載のゴルフクラブは、前記請求
項１乃至３のいずれか１項において、前記メッキを２層
以上に形成したものである。このため、ゴルフクラブヘ
ッドの表面が美観を損ないにくく、しかも傷がつきにく
くなっている。A golf club according to a fourth aspect is the golf club according to any one of the first to third aspects, wherein the plating is formed in two or more layers. For this reason, the surface of the golf club head is less likely to impair the aesthetic appearance and is less likely to be damaged.
【００１０】さらに、請求項５記載のゴルフクラブは、
請求項１乃至４のいずれか１項において、前記メッキが
下側よりストライクニッケルメッキ及び光沢ニッケルメ
ッキ層、硬質メッキ層からなるものである。このためス
テンレス鋼製の部材にストライクニッケルメッキによる
活性点を形成し、さらに光沢ニッケルメッキで光沢を付
与して美観の向上を図るとともに、硬質メッキによりメ
ッキ層自体の硬度をビッカース硬度で５００以上として
耐傷付き性を向上させることができる。[0010] Further, the golf club according to claim 5 is
The plating according to any one of claims 1 to 4, wherein the plating comprises a strike nickel plating, a bright nickel plating layer, and a hard plating layer from below. For this reason, an active point is formed on a stainless steel member by strike nickel plating, and furthermore, gloss is imparted by bright nickel plating to improve aesthetic appearance, and the hardness of the plating layer itself is set to Vickers hardness of 500 or more by hard plating. The scratch resistance can be improved.
【００１１】また、請求項６記載の本発明のゴルフクラ
ブヘッドの製造方法は、ステンレス鋼製の部材を有し、
少なくとも前記ステンレス鋼製の部材にメッキを有する
ゴルフクラブヘッドの製造方法であり、前記ステンレス
鋼の部材にストライクニッケルメッキを施し、次に光沢
ニッケルメッキを施し、さらにその上に硬質メッキ層を
形成するものである。ステンレス鋼の表面には、薄く強
靭な酸化被膜を有するので、通常のメッキ処理では密着
性の良好なメッキが得られないため、ストライクニッケ
ルメッキを施し、ステンレス部材に高い密着性をもって
メッキを形成し、さらに光沢ニッケルメッキで光沢を付
与して美観の向上を図るとともに、硬質メッキによりメ
ッキ層自体の硬度をビッカース硬度で５００以上として
耐傷付き性を向上させる。According to a sixth aspect of the present invention, there is provided a method for manufacturing a golf club head, comprising a member made of stainless steel,
A method for manufacturing a golf club head having plating on at least the stainless steel member, wherein the stainless steel member is subjected to strike nickel plating, then to bright nickel plating, and further a hard plating layer is formed thereon. Things. Since the stainless steel surface has a thin and tough oxide film, it cannot be plated with good adhesion by ordinary plating, so strike nickel plating is applied to form stainless steel with high adhesion. Further, gloss is imparted by bright nickel plating to improve the aesthetic appearance, and the hardness of the plating layer itself is increased to 500 or more in Vickers hardness by hard plating to improve scratch resistance.
【００１２】[0012]
【発明の実施形態】以下、本発明のゴルフクラブヘッド
の第１実施例について詳細に説明する。図１及び図２
は、アイアン形のゴルフクラブヘッド１を示しており、
同図において２は前面のフェース、３は後面のバック、
４は下面のソール、５は上面のトップであり、６は一側
のトウ、７は他側のヒール、８はこのヒール７側に設け
られるホーゼルである。このホーゼル８は図示しないシ
ャフトの下端が接続される。また、フェース２にはスコ
アライン９が形成されている。なお、３Ａは後面側に凹
状に形成されるキャビティであり、ソール４の上面はフ
ェース２側を深くえぐるようにアンダーカットに形成さ
れている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a first embodiment of the golf club head according to the present invention will be described in detail. 1 and 2
Shows an iron-shaped golf club head 1;
In the figure, 2 is a front face, 3 is a back face,
4 is a sole on the lower surface, 5 is a top on the upper surface, 6 is a toe on one side, 7 is a heel on the other side, and 8 is a hosel provided on the heel 7 side. The hosel 8 is connected to a lower end of a shaft (not shown). A score line 9 is formed on the face 2. 3A is a cavity formed in a concave shape on the rear surface side, and the upper surface of the sole 4 is formed undercut so as to go deeper into the face 2 side.
【００１３】このゴルフクラブヘッド１は、図３に示す
ようにステンレス鋼等の素地11上にメッキ層12を有し、
このメッキ層12は、さらにストライクニッケルメッキ1
3、光沢ニッケルメッキ層14及び硬質メッキ層15からな
る。このメッキ層12は、ビッカース硬度（Ｈｖ）で５０
０以上である。メッキ層12の硬度がビッカース硬度（Ｈ
ｖ）で５００未満では、耐傷付き性が充分でない。この
ようなメッキ層12の厚さは、強度、耐摩耗性、耐傷付き
性、経済性などの点から１１〜３０μｍとするのが好ま
しい。そしてストライクニッケルメッキ13は素地11上に
メッキの活性点を形成し、メッキ層12の密着性を良くし
たり、被覆力を向上させることができる。各層14，15は
具体的には、光沢ニッケルメッキ層14、１０〜２５μｍ
及び硬質メッキ層15、１〜５μｍとするのが好ましい。
また、素地11としては、ステンレス鋼、特に加工性等か
らオーステナイト系ステンレス鋼であるＳＵＳ３０４が
用いられている。また、このステンレス鋼製の素地11の
硬度はロックウェル硬度（Ｂスケール：ＨＲＢ）で９０
以下であるのが好ましい。このようなロックウェル硬度
の素地11とビッカース硬度５００以上のメッキ層12とを
組み合わせることにより素材の加工性に優れ、かつ耐傷
つき性を向上することができる。As shown in FIG. 3, the golf club head 1 has a plating layer 12 on a substrate 11 of stainless steel or the like.
This plating layer 12 is made of strike nickel plating 1
3. It comprises a bright nickel plating layer 14 and a hard plating layer 15. This plating layer 12 has a Vickers hardness (Hv) of 50
0 or more. The hardness of the plating layer 12 is Vickers hardness (H
If v) is less than 500, the scratch resistance is not sufficient. The thickness of the plating layer 12 is preferably 11 to 30 μm from the viewpoint of strength, abrasion resistance, scratch resistance, economy and the like. The strike nickel plating 13 forms an active point of plating on the substrate 11 to improve the adhesion of the plating layer 12 and improve the covering power. Specifically, each of the layers 14 and 15 has a bright nickel plating layer 14 and a thickness of 10 to 25 μm.
And the thickness of the hard plating layer 15 is preferably 1 to 5 μm.
As the substrate 11, stainless steel, particularly SUS304, which is an austenitic stainless steel due to its workability and the like, is used. The hardness of the stainless steel substrate 11 is 90 in Rockwell hardness (B scale: HRB).
It is preferred that: By combining such a base material 11 having a Rockwell hardness and a plating layer 12 having a Vickers hardness of 500 or more, the workability of the material is excellent and the scratch resistance can be improved.
【００１４】上述したような本実施例のゴルフクラブヘ
ッド１は、例えば、以下のような方法により製造するこ
とができる。すなわち、オーステナイト系ステンレス鋼
であるＳＵＳ３０４の丸棒を熱間鍛造により成形した
後、切削、冷間プレス加工、研磨などにより、所定の形
状のアイアン形ゴルフクラブヘッド１の形状としてこれ
を素地11とし、この素地11にメッキ層12を形成する。そ
して、例えば従来Ｓ２０Ｃ等の低炭素鋼のメッキ工程
は、脱脂―超音波洗浄―電解脱脂―酸電解―錆び取り洗
浄―陽極電解―酸活性―半光沢ニッケルメッキー光沢ニ
ッケルメッキというものであったが、ステンレス鋼の表
面には、薄く強靭な酸化被膜を有するので、通常のメッ
キ処理では密着性の良好なメッキ層12が得られないた
め、該ステンレス製の素地11の表面の酸化被膜を除去し
た後速やかにメッキを施す必要がある。そこで、ストラ
イクニッケルメッキを施す。このストライクニッケルメ
ッキは、脱脂、超音波洗浄により素地11の表面を洗浄し
た後、陰極電解で素地11の表面を電気的に還元し、さら
に中濃度の塩酸で化学的にさらに還元し、ウッド浴（塩
素系）によりニッケルメッキを施すことにより行ない、
これによりストライクニッケルメッキ13を形成する。こ
れはステンレス鋼の場合は不動態皮膜があるのでメッキ
の形成が悪いものであるが、このストライクニッケルメ
ッキ13により、ステンレス鋼の表面に活性点を形成する
ものである。続いて通常のニッケルメッキを施すことに
より光沢ニッケルメッキ層14を形成し、この際ストライ
クニッケルメッキ13により光沢ニッケルメッキ層14の密
着性を向上することができる。さらにビッカース硬度５
００以上の硬質メッキ層15を形成することによりメッキ
層12を全体としてビッカース硬度５００以上とする。こ
のような硬質メッキ層15は、硬質クロムメッキ、ニッケ
ルボロン及びニッケルスズなどのニッケル合金メッキな
どを常法により形成すればよい。このようにして本実施
例のアイアン形ゴルフクラブヘッド１を製造することが
できる。The golf club head 1 of the present embodiment as described above can be manufactured, for example, by the following method. That is, a round bar of SUS304, which is an austenitic stainless steel, is formed by hot forging, and then cut, cold-pressed, polished, or the like to form an iron-type golf club head 1 having a predetermined shape, which is used as a base material 11. Then, a plating layer 12 is formed on the substrate 11. And, for example, the plating process of low carbon steel such as S20C in the past was, for example, degreasing, ultrasonic cleaning, electrolytic degreasing, acid electrolysis, rust removal cleaning, anodic electrolysis, acid activity, semi-bright nickel plating, and bright nickel plating. Since the surface of the stainless steel has a thin and tough oxide film, the plating film 12 having good adhesion cannot be obtained by ordinary plating, and thus the oxide film on the surface of the stainless steel substrate 11 was removed. It is necessary to apply plating immediately afterwards. Therefore, strike nickel plating is performed. In this strike nickel plating, after cleaning the surface of the substrate 11 by degreasing and ultrasonic cleaning, the surface of the substrate 11 is electrically reduced by cathodic electrolysis, and further reduced chemically by a middle concentration of hydrochloric acid. (Chlorine) by nickel plating,
Thus, strike nickel plating 13 is formed. In the case of stainless steel, the formation of plating is poor due to the presence of a passivation film, but active spots are formed on the surface of stainless steel by the strike nickel plating 13. Subsequently, normal nickel plating is performed to form the bright nickel plating layer 14, and at this time, the strike nickel plating 13 can improve the adhesion of the bright nickel plating layer 14. Vickers hardness 5
By forming the hard plating layer 15 of 00 or more, the plating layer 12 as a whole has a Vickers hardness of 500 or more. Such a hard plating layer 15 may be formed by hard chromium plating, nickel alloy plating such as nickel boron and nickel tin, or the like by an ordinary method. Thus, the iron-type golf club head 1 of the present embodiment can be manufactured.
【００１５】以上詳述したとおり本実施例のアイアン形
ゴルフクラブヘッド１は、オーステナイト系ステンレス
鋼からなる素地11にビッカース硬度５００以上のメッキ
層12を形成したものであり、該メッキ層12がビッカース
硬度で５００以上であるので、ステンレス鋼製の素地11
に傷がつきにくくなっている。特に、前記ステンレス鋼
がオーステナイト系であるので、その硬度は比較的軟ら
かいので加工性に優れる。その上、素地11のオーステナ
イト系ステンレス鋼の硬度がロックウェル硬度（Ｂスケ
ール）で９０以下であり比較的軟らかいので、加工性に
優れキャビティ３Ａやアンダーカットなどを容易に形成
することができる。また、メッキ層12を２層に形成する
ことにより傷がつきにくくなっている。特に本実施例に
おいては、メッキ層12が２層構造を有し、下側よりスト
ライクニッケルメッキ13及び光沢ニッケルメッキ層14、
硬質メッキ層15からなるので、ステンレス鋼製の素地11
の表面の酸化被膜を除去した後、迅速にメッキ処理され
るので、ストライクニッケルメッキ13が形成され、さら
に光沢ニッケルメッキ層14で光沢を付与して美観の向上
を図るとともに、硬質メッキ層15によりメッキ層12自体
の硬度をビッカース硬度で５００以上として耐傷付き性
を向上させることができる。特にオーステナイト系ステ
ンレス鋼においては、優れた耐食性を備えているので前
記酸化被膜を確実に除去する上述のメッキ層12の形成は
有効である。As described in detail above, the iron-type golf club head 1 of this embodiment is formed by forming a plating layer 12 having a Vickers hardness of 500 or more on a base material 11 made of austenitic stainless steel. Since the hardness is 500 or more, the stainless steel substrate 11
Is less likely to be scratched. In particular, since the stainless steel is austenitic, its workability is excellent because its hardness is relatively soft. In addition, the hardness of the austenitic stainless steel of the base 11 is 90 or less in Rockwell hardness (B scale) and relatively soft, so that the workability is excellent and the cavity 3A and the undercut can be easily formed. Further, by forming the plating layer 12 in two layers, the plating layer 12 is hardly damaged. In particular, in the present embodiment, the plating layer 12 has a two-layer structure, and the strike nickel plating 13 and the bright nickel plating layer 14,
Since the hard plating layer 15 is used, the stainless steel base 11
After removing the oxide film on the surface of the surface, it is quickly plated, so that strike nickel plating 13 is formed, and furthermore, the bright nickel plating layer 14 gives gloss and improves the aesthetic appearance, and the hard plating layer 15 By setting the hardness of the plating layer 12 itself to 500 or more in Vickers hardness, the scratch resistance can be improved. Particularly, austenitic stainless steel has excellent corrosion resistance, and therefore, the formation of the above-described plated layer 12 for reliably removing the oxide film is effective.
【００１６】また、このような素地11にメッキを有する
ゴルフクラブヘッド１を製造する本実施例の方法は、素
地11にストライクニッケルメッキ13を形成し、次に通常
のニッケルメッキを施して光沢ニッケルメッキ層14を形
成し、さらに硬質メッキ層15を形成するものであるた
め、ストライクニッケルメッキによりメッキ密着性の良
好な下地を形成し、さらに光沢ニッケルメッキで光沢を
付与して美観の向上を図るとともに、硬質メッキにより
メッキ層自体の硬度をビッカース硬度で５００以上とし
て耐傷付き性を向上させることができる。特にオーステ
ナイト系ステンレス鋼においては、優れた耐食性を備え
ているので前記酸化被膜を確実に除去する上述のメッキ
層12形成の方法は有効である。Further, the method of this embodiment for manufacturing the golf club head 1 having a plating on the substrate 11 is such that a strike nickel plating 13 is formed on the substrate 11, and then a normal nickel plating is applied to obtain a bright nickel plating. Since the plating layer 14 is formed and the hard plating layer 15 is further formed, a base with good plating adhesion is formed by strike nickel plating, and gloss is imparted by bright nickel plating to improve aesthetic appearance. At the same time, the hardness of the plating layer itself can be increased to 500 or more in Vickers hardness by hard plating to improve the scratch resistance. In particular, since austenitic stainless steel has excellent corrosion resistance, the above-described method of forming the plating layer 12 for reliably removing the oxide film is effective.
【００１７】次に本発明の第２実施例について図４及び
図５に基いて説明する。第２実施例のアイアン形ゴルフ
クラブヘッド１は、フェース２に略矩形の開口部１Ｂが
形成されると共に、シャフト（図示せず）の下端が接続
されるたステンレス製の部材であるヘッド本体１Ａと、
この開口部１Ｂに嵌着などにより接合されたチタン合金
製の板状のフェース部材２Ａとからなるものであり、基
本的には前述した第１実施例と同様の構成を有するの
で、同一の構成には同一の符号を付しその詳細な説明を
省略する。Next, a second embodiment of the present invention will be described with reference to FIGS. The iron-type golf club head 1 of the second embodiment has a head body 1A which is a stainless steel member having a substantially rectangular opening 1B formed in a face 2 and a lower end of a shaft (not shown) connected thereto. When,
It is composed of a titanium alloy plate-like face member 2A joined to the opening 1B by fitting or the like. The face member 2A has basically the same configuration as that of the first embodiment described above. Are denoted by the same reference numerals, and a detailed description thereof will be omitted.
【００１８】このような実施例においては、チタン合金
製の板状のフェース部材２Ａは、腐蝕しにくく、また硬
くて耐傷付き性にも優れているので、メッキ層12はゴル
フクラブヘッド１の全体に形成する必要なく、ステンレ
ス製の部材であるヘッド本体１Ａにのみ形成すればよ
い。このようにステンレス製のヘッド本体１Ａにのみメ
ッキ層12を形成することにより前述した第１実施例と同
様の効果を得ることができる。特に、開口部１Ｂの周縁
部ではメッキ層12も剥離したりしやすいが、このメッキ
層12を下側よりストライクニッケルメッキ13及び光沢ニ
ッケルメッキ層14、硬質メッキ層15の２層構造とするこ
とにより、メッキ層12がヘッド本体１Ａの素地11に良好
な密着性をもって強固に密着するので、メッキ層12自身
も剥離したりしにくくなっている。In this embodiment, since the plate-like face member 2A made of a titanium alloy is hardly corroded and hard and has excellent scratch resistance, the plating layer 12 is formed on the entire golf club head 1. Need only be formed on the head body 1A, which is a member made of stainless steel. By forming the plating layer 12 only on the head body 1A made of stainless steel as described above, the same effects as those of the first embodiment can be obtained. In particular, the plating layer 12 is easily peeled off at the periphery of the opening 1B. However, the plating layer 12 should have a two-layer structure of a strike nickel plating 13, a bright nickel plating layer 14, and a hard plating layer 15 from below. As a result, the plating layer 12 firmly adheres to the substrate 11 of the head main body 1A with good adhesion, so that the plating layer 12 itself is not easily peeled off.
【００１９】以上本発明について前記実施例に基き説明
してきたが、本発明は前記実施例に限られるものではな
く、種々の変形実施が可能である。例えば、ゴルフクラ
ブヘッド１の形状としては、前述した第１実施例及び第
２実施例に示すタイプのものに限らず、ステンレス製の
部材を用いていれば、アイアン型ゴルフクラブヘッドに
限らず、パターやメタルウッド等と称する金属殻によっ
て形成した中空形状のものにも適用可能である。Although the present invention has been described based on the above embodiment, the present invention is not limited to the above embodiment, and various modifications can be made. For example, the shape of the golf club head 1 is not limited to the types shown in the first and second embodiments described above, and is not limited to the iron type golf club head if a stainless steel member is used. It is also applicable to a hollow shape formed by a metal shell called a putter or a metal wood.
【００２０】[0020]
【発明の効果】本発明の請求項１記載のゴルフクラブ
は、ステンレス鋼製の部材を有するゴルフクラブヘッド
の少なくとも前記ステンレス鋼製の部材にビッカース硬
度５００以上のメッキを施したものであるので、加工性
に優れると共に傷がつきにくくなっている。The golf club according to the first aspect of the present invention is a golf club head having a stainless steel member, wherein at least the stainless steel member is plated with a Vickers hardness of 500 or more. It has excellent workability and is hardly damaged.
【００２１】また、請求項２記載のゴルフクラブヘッド
は、前記ステンレス鋼がオーステナイト系からなるもの
であるので、比較的軟らかい材質であるので例えばキャ
ビティやアンダーカットなどの加工を容易に行うことが
できる。Further, in the golf club head according to the second aspect, since the stainless steel is made of austenitic material, it is a relatively soft material, so that processing such as cavities and undercuts can be easily performed. .
【００２２】請求項３記載のゴルフクラブヘッドは、前
記請求項１又は２において、前記ステンレス鋼の硬度が
ロックウェル硬度（Ｂスケール）で９０以下のものであ
るので、ステンレス鋼製の部材を所定の硬度以下とする
ことにより、加工性に優れ例えばキャビティやアンダー
カットなどの加工を容易に行うことができる。According to a third aspect of the present invention, in the golf club head according to the first or second aspect, the stainless steel has a Rockwell hardness (B scale) of 90 or less. By setting the hardness to not more than, the workability is excellent and, for example, processing such as cavity and undercut can be easily performed.
【００２３】請求項４記載のゴルフクラブヘッドは、前
記請求項１乃至３のいずれか１項において、前記メッキ
を２層以上に形成したものであるので、ゴルフクラブヘ
ッドの表面において美観を損ないにくく、しかも傷がつ
きにくくなっている。According to a fourth aspect of the present invention, there is provided a golf club head according to any one of the first to third aspects, wherein the plating is formed in two or more layers. Moreover, it is hard to be damaged.
【００２４】さらに、請求項５記載のゴルフクラブヘッ
ドは、請求項１乃至４のいずれか１項において、前記メ
ッキが下側よりストライクニッケルメッキ及び光沢ニッ
ケルメッキ層、硬質メッキ層からなるものであるので、
ステンレス鋼製の部材にストライクニッケルメッキが形
成され、さらに光沢ニッケルメッキで光沢を付与して美
観の向上を図るとともに、硬質メッキによりメッキ層自
体の硬度をビッカース硬度で５００以上として耐傷付き
性を向上させることができる。Further, in the golf club head according to the fifth aspect, in any one of the first to fourth aspects, the plating comprises a strike nickel plating, a bright nickel plating layer, and a hard plating layer from below. So
A strike nickel plating is formed on the stainless steel member, and the gloss is enhanced by bright nickel plating to improve the aesthetic appearance. The hardness of the plating layer itself is increased to Vickers hardness of 500 or more by hard plating to improve the scratch resistance. Can be done.
【００２５】また、請求項６記載の本発明のゴルフクラ
ブヘッドの製造方法は、ステンレス鋼製の部材を有し、
少なくとも前記ステンレス鋼製の部材にメッキを有する
ゴルフクラブヘッドの製造方法であり、前記ステンレス
鋼の部材にストライクニッケルメッキを施し、次に光沢
ニッケルメッキを施し、さらにその上に硬質メッキ層を
形成するものであるので、ストライクニッケルメッキに
よりステンレス部材に高い密着性をもってメッキを形成
し、さらに光沢ニッケルメッキで光沢を付与して美観の
向上を図るとともに、その上に硬質メッキによりメッキ
層自体の硬度をビッカース硬度で５００以上として耐傷
付き性を向上させる。According to a sixth aspect of the present invention, there is provided a method for manufacturing a golf club head, comprising a member made of stainless steel.
A method for manufacturing a golf club head having plating on at least the stainless steel member, wherein the stainless steel member is subjected to strike nickel plating, then to bright nickel plating, and further a hard plating layer is formed thereon. Because of this, strike nickel plating is used to form plating with high adhesion to stainless steel members, and glossy nickel plating is used to improve the aesthetic appearance by adding luster and hard plating to increase the hardness of the plating layer itself. A Vickers hardness of 500 or more improves scratch resistance.
【図１】本発明の第１実施例のゴルフクラブヘッドを示
す断面図である。FIG. 1 is a sectional view showing a golf club head according to a first embodiment of the present invention.
【図２】同上正面図である。FIG. 2 is a front view of the same.
【図３】前記ゴルフクラブヘッドの層構成を示す断面図
である。FIG. 3 is a sectional view showing a layer structure of the golf club head.
【図４】本発明の第２実施例のゴルフクラブヘッドを示
す断面図である。FIG. 4 is a sectional view showing a golf club head according to a second embodiment of the present invention.
【図５】同上正面図である。FIG. 5 is a front view of the same.
１ ゴルフクラブヘッド 11 素地（ステンレス部材） 12 メッキ層 13 ストライクニッケルメッキ 14 光沢ニッケルメッキ層 15 硬質メッキ層 1 Golf club head 11 Base material (stainless steel member) 12 Plating layer 13 Strike nickel plating 14 Bright nickel plating layer 15 Hard plating layer
Claims (6)
ラブヘッドの少なくとも前記ステンレス鋼製の部材にビ
ッカース硬度５００以上のメッキを施したものであるこ
とを特徴とするゴルフクラブ。1. A golf club comprising a golf club head having a stainless steel member, wherein at least the stainless steel member is plated with a Vickers hardness of 500 or more.
らなるものであることを特徴とする請求項１記載のゴル
フクラブ。2. The golf club according to claim 1, wherein said stainless steel is made of austenitic.
硬度（Ｂスケール）で９０以下のものであることを特徴
とする請求項１又は２記載のゴルフクラブ。3. The golf club according to claim 1, wherein said stainless steel has a Rockwell hardness (B scale) of 90 or less.
あることを特徴とする請求項１乃至３のいずれか１項記
載のゴルフクラブ。4. The golf club according to claim 1, wherein the plating is formed in two or more layers.
ルメッキ及び光沢ニッケルメッキ層、硬質メッキ層から
なるものであることを特徴とする請求項４記載のゴルフ
クラブ。5. The golf club according to claim 4, wherein the plating comprises a strike nickel plating, a bright nickel plating layer, and a hard plating layer from the lower side.
も前記ステンレス鋼製の部材にメッキを有するゴルフク
ラブヘッドの製造方法において、前記ステンレス鋼製の
部材にストライクニッケルメッキを施し、次に光沢ニッ
ケルメッキを施し、さらにその上に硬質メッキ層を形成
することを特徴とするゴルフクラブヘッドの製造方法。6. A method for manufacturing a golf club head having a stainless steel member and plating at least on the stainless steel member, wherein the stainless steel member is subjected to strike nickel plating, A method for manufacturing a golf club head, comprising plating and further forming a hard plating layer thereon.