JP2000141875A - Ink jet recording sheet - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a superior ink jet recording sheet of superior light fastness of a recorded image, particularly light fastness of a magenta image and free from the yellowing of surface, the deterioration of the picture quality and the like. SOLUTION: A recorded image is formed on an ink jet recording sheet by using an aqueous ink, and in the recording sheet, at least one kind of benzotrizol compound represented by the formula 3-[3-(benzotriazol-2-yl)-4- hydroxyphenyl]decaglyceryl propionate or the like [In the formula, R1 represents a hydrogen atom or a 1-5C alkyl, and R2 represents a hydrogen atom or a chlorine atom. (m) represents 0 or 1-4 integer and (n) represents 1-12 integer.] is contained in the recording sheet.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、水性インクを用い
たプリンター、コピー等に用いられるインクジェット記
録用シートに関し、特に記録画像の耐光性に優れたイン
クジェット記録用シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording sheet for use in printers, copiers and the like using an aqueous ink, and more particularly to an ink jet recording sheet having excellent light fastness of a recorded image.

【０００２】[0002]

【従来の技術】インクジェット記録方式は多色化が容易
であり、低騒音で、記録速度が比較的高速であるうえ、
大面積の記録も可能である等の利点を有しており、現在
では各種のプリンター、ファクシミリ、コンピューター
端末機等種々の分野に広く使用され、急速に普及してい
る。水性インクを用いるインクジェット方式では、プリ
ント速度、解像度、階調性等のプリンターの性能向上に
伴って、被記録シートに対しても、インクの高速吸収
性、高濃度化、高画質化、画像の耐水性、さらには画像
の耐光性も要求されるようになっている。2. Description of the Related Art Ink-jet recording is easy to achieve multi-color recording, has low noise, has a relatively high recording speed,
It has advantages such as being able to record on a large area, and is currently widely used in various fields such as various printers, facsimile machines and computer terminals, and is rapidly spreading. In the ink jet method using water-based ink, with the improvement of printer performance such as printing speed, resolution, gradation, etc., high-speed absorption of ink, high density, high image quality, Water resistance and also light resistance of images are required.

【０００３】このような要求に答えるため、支持体上に
顔料および接着剤を主体とするインク受理層を設けたシ
ートに関する提案が多数なされてきた。例えば、非晶質
シリカおよび高分子バインダーからなる塗布層（特開昭
５５−５１５８３号公報、同５７−１５７７８６号公
報、同６２−１５８０８４号公報）、ゼオライト等のイ
ンク吸着顔料を有する塗布層（特開昭５６−１４４１７
２号公報）、微粉ケイ酸および水溶性樹脂からなる塗布
層（特開昭５６−１４８５８３号公報）、多孔質のカチ
オン性アルミナ水和物を有する塗布層（特開昭６０−２
３２９９０号公報）等を支持体上に設ける方法が提案さ
れている。[0003] In order to respond to such demands, there have been many proposals regarding sheets provided with an ink receiving layer mainly composed of a pigment and an adhesive on a support. For example, a coating layer composed of amorphous silica and a polymer binder (JP-A-55-51583, JP-A-57-157786 and JP-A-62-158084), and a coating layer having an ink-adsorbing pigment such as zeolite ( JP-A-56-14417
No. 2), a coating layer composed of finely divided silicic acid and a water-soluble resin (Japanese Patent Application Laid-Open No. 56-148583), and a coating layer having a porous cationic alumina hydrate (Japanese Patent Application Laid-Open No. Sho 60-2).
No. 32990) is provided on a support.

【０００４】なかでも、非晶質シリカはインクの吸収速
度が早く、インク吸収容量が大きく、しかも高画質に印
字ができ、そのうえ染料の発色を損なわないため、最も
インクジェット記録に適合した顔料であると考えられて
いる。しかしながら、非晶質シリカを主成分とするイン
ク受理層は染料の発色を鮮明にする反面、染料の光によ
る分解を助長し、記録画像が経時的に変色または褪色し
やすいという欠点がある。[0004] Among them, amorphous silica is a pigment most suitable for ink jet recording because it has a high ink absorption speed, a large ink absorption capacity, can print with high image quality, and does not impair the coloring of the dye. It is believed that. However, while the ink-receiving layer containing amorphous silica as a main component makes the coloring of the dye clear, it has the disadvantage that it promotes the decomposition of the dye by light and the recorded image is easily discolored or faded with time.

【０００５】さらに、印字の耐水性改良の観点から、ポ
リカチオン高分子電解質（特開昭５６−８４９９２号公
報、同６０−４９９９０号公報、同６１−１２５８７８
号公報）、塩基性ラテックス（特開昭５７−３６６９２
号公報）等をインク受理層に含有させる方法が提案され
ている。しかし、かかる耐水性向上剤の使用により印字
の耐水性は改善されるものの、染料の光分解を促進さ
せ、耐光性が低下するという問題が生じる。Further, from the viewpoint of improving the water resistance of printing, polycationic polymer electrolytes (JP-A-56-89992, JP-A-60-49990, and JP-A-61-125878).
Japanese Patent Application Laid-Open No. 57-36692), basic latex
Has been proposed in the ink receiving layer. However, although the use of such a water resistance improver improves the water resistance of the print, it causes a problem that photodecomposition of the dye is accelerated and light resistance is reduced.

【０００６】一方、画像の耐光性を向上させるための一
般的な方法はインクの耐光性を向上させることである
が、インクジェット記録に使用されるインクはノズルに
目詰まりを生じないこと、鮮やかな色調を有すること、
熱に安定であること等が必須条件であるため、必ずしも
耐光性に優れた染料や顔料を選択することができず、現
状では特にマゼンタインクの耐光性が著しく不足してい
る。On the other hand, a general method for improving the light fastness of an image is to improve the light fastness of the ink. However, the ink used for ink jet recording does not cause clogging of the nozzles and has a vivid color. Having a color tone,
Since heat stability is an essential condition, it is not always possible to select a dye or pigment having excellent light fastness, and at present, the light fastness of magenta ink is particularly insufficient.

【０００７】インクジェット記録用シートの面から画像
の耐光性を改善する方法としては、リンタングステン
酸、リンモリブデン酸、塩化第二クロム等の金属酸化
物、金属塩化物またはタンニン酸のうちの少なくとも一
つを添加する方法（特開昭５７−８７９８７号公報）、
ヒンダードフェノール類等の酸化防止剤を添加する方法
（特開昭５７−７４１９２号公報）、ベンゾフェノン
系、ベンゾトリアゾール系やフェニルサリチル酸系等の
紫外線吸収剤を添加する方法（特開昭５７−７４１９３
号、同５７−８７９８８号、同６３−２２２８８５号公
報）およびヒンダードピペリジン系の光安定剤等を添加
する方法（特開昭６１−１４６５９１号公報）等が提案
されている。しかし、上記方法ではいずれも充分に満足
のいく耐光性が得られていないのが現状である。As a method for improving the light fastness of an image from the surface of an ink jet recording sheet, at least one of a metal oxide such as phosphotungstic acid, phosphomolybdic acid, chromic dichloride, a metal chloride or tannic acid is used. (JP-A-57-87987),
A method of adding an antioxidant such as a hindered phenol (JP-A-57-74192), and a method of adding an ultraviolet absorber such as a benzophenone-based, benzotriazole-based or phenylsalicylic acid-based (JP-A-57-74193).
And JP-A-57-87988 and JP-A-63-222885) and a method of adding a hindered piperidine-based light stabilizer and the like (Japanese Patent Application Laid-Open No. 61-146591). However, at the present time, none of the above methods has provided sufficiently satisfactory light resistance.

【０００８】[0008]

【発明が解決しようとする課題】本発明の課題は、記録
濃度、記録画質および記録画像の耐水性に優れ、しかも
画像の耐光性にも優れたインクジェット記録用シートを
提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide an ink jet recording sheet which is excellent in recording density, recording quality and water resistance of a recorded image, and is also excellent in light resistance of an image.

【０００９】[0009]

【課題を解決するための手段】本発明は、水性インクを
用いて記録画像を形成するインクジェット記録用シート
において、該記録用シート中に、一般式（１）で表され
るベンゾトリアゾール化合物の少なくとも１種を含有せ
しめることを特徴とするインクジェット記録用シートに
係る。According to the present invention, there is provided an ink jet recording sheet for forming a recorded image using an aqueous ink, wherein at least one of a benzotriazole compound represented by the general formula (1) is contained in the recording sheet. The present invention relates to a sheet for ink jet recording characterized in that it contains one kind.

【００１０】[0010]

【化２】 Embedded image

【００１１】〔式中、Ｒ₁ は水素原子または炭素数１〜
５のアルキル基を示し、Ｒ₂ は水素原子または塩素原子
を示す。ｍは０または１〜４の整数を、ｎは１〜１２の
整数を示す。〕[Wherein, R ₁ is a hydrogen atom or a group having 1 to 1 carbon atoms.
5 represents an alkyl group, and R ₂ represents a hydrogen atom or a chlorine atom. m represents 0 or an integer of 1 to 4, and n represents an integer of 1 to 12. ]

【００１２】[0012]

【発明の実施の形態】インクジェット記録用シート中に
上記一般式（１）で表されるベンゾトリアゾール化合物
を含有させることにより、他の品質を損なうことなく、
記録画像の耐光性、特にマゼンタ画像の耐光性が大幅に
改善される。BEST MODE FOR CARRYING OUT THE INVENTION By including a benzotriazole compound represented by the above general formula (1) in an ink jet recording sheet, other quality is not impaired.
The light fastness of the recorded image, especially the light fastness of the magenta image is greatly improved.

【００１３】記録画像の耐光性が大幅に改善される理由
については定かではないが、一般式（１）で表される化
合物は、親水性が高く水性インクと速やかに混和し、紫
外線吸収剤としてとりわけ効率よく機能し、染料の分解
を抑制するためではないかと考えられる。The reason why the light fastness of a recorded image is greatly improved is not clear, but the compound represented by the general formula (1) has a high hydrophilicity, is readily mixed with an aqueous ink, and serves as an ultraviolet absorber. In particular, it is thought to function efficiently and suppress the decomposition of the dye.

【００１４】前記一般式（１）で表されるベンゾトリア
ゾール化合物の具体例としては、例えば、下記が挙げら
れる。３−（ベンゾトリアゾール−２−イル）−４−ヒ
ドロキシ安息香酸モノグリセリルエステル、３−（ベン
ゾトリアゾール−２−イル）−４−ヒドロキシ安息香酸
ジグリセリルエステル、３−（ベンゾトリアゾール−２
−イル）−４−ヒドロキシ安息香酸テトラグリセリルエ
ステル、３−（ベンゾトリアゾール−２−イル）−４−
ヒドロキシ安息香酸ヘキサグリセリルエステル、３−
（ベンゾトリアゾール−２−イル）−４−ヒドロキシ安
息香酸デカグリセリルエステル、３−（ベンゾトリアゾ
ール−２−イル）−４−ヒドロキシフェニル酢酸モノグ
リセリルエステル、３−（ベンゾトリアゾール−２−イ
ル）−４−ヒドロキシフェニル酢酸ジグリセリルエステ
ル、３−（ベンゾトリアゾール−２−イル）−４−ヒド
ロキシフェニル酢酸テトラグリセリルエステル、３−
（ベンゾトリアゾール−２−イル）−４−ヒドロキシフ
ェニル酢酸ヘキサグリセリルエステル、３−（ベンゾト
リアゾール−２−イル）−４−ヒドロキシフェニル酢酸
デカグリセリルエステル、３−〔３−（ベンゾトリアゾ
ール−２−イル）−４−ヒドロキシフェニル〕プロピオ
ン酸モノグリセリルエステル、３−〔３−（ベンゾトリ
アゾール−２−イル）−４−ヒドロキシフェニル〕プロ
ピオン酸ジグリセリルエステル、３−〔３−（ベンゾト
リアゾール−２−イル）−４−ヒドロキシフェニル〕プ
ロピオン酸テトラグリセリルエステル、３−〔３−（ベ
ンゾトリアゾール−２−イル）−４−ヒドロキシフェニ
ル〕プロピオン酸ヘキサグリセリルエステル、Specific examples of the benzotriazole compound represented by the general formula (1) include the following. 3- (benzotriazol-2-yl) -4-hydroxybenzoic acid monoglyceryl ester, 3- (benzotriazol-2-yl) -4-hydroxybenzoic acid diglyceryl ester, 3- (benzotriazole-2)
-Yl) -4-hydroxybenzoic acid tetraglyceryl ester, 3- (benzotriazol-2-yl) -4-
Hexaglyceryl hydroxybenzoate, 3-
(Benzotriazol-2-yl) -4-hydroxybenzoic acid decaglyceryl ester, 3- (benzotriazol-2-yl) -4-hydroxyphenylacetic acid monoglyceryl ester, 3- (benzotriazol-2-yl) -4 -Hydroxyphenylacetic acid diglyceryl ester, 3- (benzotriazol-2-yl) -4-hydroxyphenylacetic acid tetraglyceryl ester, 3-
(Benzotriazol-2-yl) -4-hydroxyphenylacetic acid hexaglyceryl ester, 3- (benzotriazol-2-yl) -4-hydroxyphenylacetic acid decaglyceryl ester, 3- [3- (benzotriazol-2-yl) ) -4-Hydroxyphenyl] propionic acid monoglyceryl ester, 3- [3- (benzotriazol-2-yl) -4-hydroxyphenyl] propionic acid diglyceryl ester, 3- [3- (benzotriazol-2-yl) ) -4-Hydroxyphenyl] propionic acid tetraglyceryl ester, 3- [3- (benzotriazol-2-yl) -4-hydroxyphenyl] propionic acid hexaglyceryl ester,

【００１５】３−〔３−（ベンゾトリアゾール−２−イ
ル）−４−ヒドロキシフェニル〕プロピオン酸オクタグ
リセリルエステル、３−〔３−（ベンゾトリアゾール−
２−イル）−４−ヒドロキシフェニル〕プロピオン酸デ
カグリセリルエステル、４−〔３−（ベンゾトリアゾー
ル−２−イル）−４−ヒドロキシフェニル〕ブタン酸テ
トラグリセリルエステル、４−〔３−（ベンゾトリアゾ
ール−２−イル）−４−ヒドロキシフェニル〕ブタン酸
ヘキサグリセリルエステル、４−〔３−（ベンゾトリア
ゾール−２−イル）−４−ヒドロキシフェニル〕ブタン
酸デカグリセリルエステル、５−〔３−（ベンゾトリア
ゾール−２−イル）−４−ヒドロキシフェニル〕ペンタ
ン酸ヘキサグリセリルエステル、４−〔３−（ベンゾト
リアゾール−２−イル）−４−ヒドロキシフェニル〕ブ
タン酸デカグリセリルエステル、６−〔３−（ベンゾト
リアゾール−２−イル）−４−ヒドロキシフェニル〕ヘ
キサン酸ヘキサグリセリルエステル、６−〔３−（ベン
ゾトリアゾール−２−イル）−４−ヒドロキシフェニ
ル〕ヘキサン酸デカグリセリルエステル、３−〔３−
（ベンゾトリアゾール−２−イル）−４−ヒドロキシ−
５−メチルフェニル〕プロピオン酸ヘキサグリセリルエ
ステル、３−〔３−（ベンゾトリアゾール−２−イル）
−４−ヒドロキシ−５−メチルフェニル〕プロピオン酸
デカグリセリルエステル、３−（ベンゾトリアゾール−
２−イル）−４−ヒドロキシ−５−tert−ブチル安息香
酸ヘキサグリセリルエステル、３−（ベンゾトリアゾー
ル−２−イル）−４−ヒドロキシ−５−tert−ブチル安
息香酸デカグリセリルエステル、Octaglyceryl 3- [3- (benzotriazol-2-yl) -4-hydroxyphenyl] propionate, 3- [3- (benzotriazole-
2-yl) -4-hydroxyphenyl] propionic acid decaglyceryl ester, 4- [3- (benzotriazol-2-yl) -4-hydroxyphenyl] butanoic acid tetraglyceryl ester, 4- [3- (benzotriazole- 2-yl) -4-hydroxyphenyl] butanoic acid hexaglyceryl ester, 4- [3- (benzotriazol-2-yl) -4-hydroxyphenyl] butanoic acid decaglyceryl ester, 5- [3- (benzotriazole- 2- (yl) -4-hydroxyphenyl] pentanoic acid hexaglyceryl ester, 4- [3- (benzotriazol-2-yl) -4-hydroxyphenyl] butanoic acid decaglyceryl ester, 6- [3- (benzotriazole- 2-yl) -4-hydroxyphenyl] hexanoic acid hexag Seriruesuteru, 6- [3- (benzotriazol-2-yl) -4-hydroxyphenyl] hexanoic acid decaglyceryl esters, 3- [3-
(Benzotriazol-2-yl) -4-hydroxy-
5-methylphenyl] propionic acid hexaglyceryl ester, 3- [3- (benzotriazol-2-yl)
-4-hydroxy-5-methylphenyl] propionic acid decaglyceryl ester, 3- (benzotriazole-
2-yl) -4-hydroxy-5-tert-butylbenzoic acid hexaglyceryl ester, 3- (benzotriazol-2-yl) -4-hydroxy-5-tert-butylbenzoic acid decaglyceryl ester,

【００１６】３−（ベンゾトリアゾール−２−イル）−
４−ヒドロキシ−５−tert−ブチルフェニル酢酸ヘキサ
グリセリルエステル、３−（ベンゾトリアゾール−２−
イル）−４−ヒドロキシ−５−tert−ブチルフェニル酢
酸デカグリセリルエステル、３−〔３−（ベンゾトリア
ゾール−２−イル）−４−ヒドロキシ−５−tert−ブチ
ルフェニル〕プロピオン酸ヘキサグリセリルエステル、
３−〔３−（ベンゾトリアゾール−２−イル）−４−ヒ
ドロキシ−５−tert−ブチルフェニル〕プロピオン酸デ
カグリセリルエステル、４−〔３−（ベンゾトリアゾー
ル−２−イル）−４−ヒドロキシ−５−tert−ブチルフ
ェニル〕ブタン酸ヘキサグリセリルエステル、４−〔３
−（ベンゾトリアゾール−２−イル）−４−ヒドロキシ
−５−tert−ブチルフェニル〕ブタン酸デカグリセリル
エステル、５−〔３−（ベンゾトリアゾール−２−イ
ル）−４−ヒドロキシ−５−tert−ブチルフェニル〕ペ
ンタン酸ヘキサグリセリルエステル、５−〔３−（ベン
ゾトリアゾール−２−イル）−４−ヒドロキシ−５−te
rt−ブチルフェニル〕ペンタン酸デカグリセリルエステ
ル、６−〔３−（ベンゾトリアゾール−２−イル）−４
−ヒドロキシ−５−tert−ブチルフェニル〕ヘキサン酸
ヘキサグリセリルエステル、６−〔３−（ベンゾトリア
ゾール−２−イル）−４−ヒドロキシ−５−tert−ブチ
ルフェニル〕ヘキサン酸デカグリセリルエステル、３−
〔３−（ベンゾトリアゾール−２−イル）−４−ヒドロ
キシ−５−tert−アミルフェニル〕プロピオン酸ヘキサ
グリセリルエステル、３−〔３−（ベンゾトリアゾール
−２−イル）−４−ヒドロキシ−５−tert−アミルフェ
ニル〕プロピオン酸デカグリセリルエステル、3- (benzotriazol-2-yl)-
4-hydroxy-5-tert-butylphenylacetic acid hexaglyceryl ester, 3- (benzotriazole-2-
Yl) -4-hydroxy-5-tert-butylphenylacetic acid decaglyceryl ester, 3- [3- (benzotriazol-2-yl) -4-hydroxy-5-tert-butylphenyl] propionic acid hexaglyceryl ester,
3- [3- (Benzotriazol-2-yl) -4-hydroxy-5-tert-butylphenyl] propionic acid decaglyceryl ester, 4- [3- (benzotriazol-2-yl) -4-hydroxy-5 -Tert-butylphenyl] butanoic acid hexaglyceryl ester, 4- [3
-(Benzotriazol-2-yl) -4-hydroxy-5-tert-butylphenyl] butanoic acid decaglyceryl ester, 5- [3- (benzotriazol-2-yl) -4-hydroxy-5-tert-butyl Hexaglyceryl phenyl] pentanoate, 5- [3- (benzotriazol-2-yl) -4-hydroxy-5-te
rt-butylphenyl] pentanoic acid decaglyceryl ester, 6- [3- (benzotriazol-2-yl) -4
-Hydroxy-5-tert-butylphenyl] hexanoic acid hexaglyceryl ester, 6- [3- (benzotriazol-2-yl) -4-hydroxy-5-tert-butylphenyl] hexanoic acid decaglyceryl ester, 3-
[3- (benzotriazol-2-yl) -4-hydroxy-5-tert-amylphenyl] propionic acid hexaglyceryl ester, 3- [3- (benzotriazol-2-yl) -4-hydroxy-5-tert -Amylphenyl] propionic acid decaglyceryl ester,

【００１７】３−（５−クロロベンゾトリアゾール−２
−イル）−４−ヒドロキシ安息香酸ヘキサグリセリルエ
ステル、３−（５−クロロベンゾトリアゾール−２−イ
ル）−４−ヒドロキシ安息香酸デカグリセリルエステ
ル、３−（５−クロロベンゾトリアゾール−２−イル）
−４−ヒドロキシフェニル酢酸ヘキサグリセリルエステ
ル、３−（５−クロロベンゾトリアゾール−２−イル）
−４−ヒドロキシフェニル酢酸デカグリセリルエステ
ル、３−〔３−（５−クロロベンゾトリアゾール−２−
イル）−４−ヒドロキシフェニル〕プロピオン酸ヘキサ
グリセリルエステル、３−〔３−（５−クロロベンゾト
リアゾール−２−イル）−４−ヒドロキシフェニル〕プ
ロピオン酸デカグリセリルエステル、４−〔３−（５−
クロロベンゾトリアゾール−２−イル）−４−ヒドロキ
シフェニル〕ブタン酸ヘキサグリセリルエステル、４−
〔３−（５−クロロベンゾトリアゾール−２−イル）−
４−ヒドロキシフェニル〕ブタン酸デカグリセリルエス
テル、５−〔３−（５−クロロベンゾトリアゾール−２
−イル）−４−ヒドロキシフェニル〕ペンタン酸ヘキサ
グリセリルエステル、５−〔３−（５−クロロベンゾト
リアゾール−２−イル）−４−ヒドロキシフェニル〕ペ
ンタン酸デカグリセリルエステル、６−〔３−（５−ク
ロロベンゾトリアゾール−２−イル）−４−ヒドロキシ
フェニル〕ヘキサン酸ヘキサグリセリルエステル、６−
〔３−（５−クロロベンゾトリアゾール−２−イル）−
４−ヒドロキシフェニル〕ヘキサン酸デカグリセリルエ
ステル、３−〔３−（５−クロロベンゾトリアゾール−
２−イル）−４−ヒドロキシ−５−tert−ブチルフェニ
ル〕プロピオン酸ヘキサグリセリルエステル、３−〔３
−（５−クロロベンゾトリアゾール−２−イル）−４−
ヒドロキシ−５−tert−ブチルフェニル〕プロピオン酸
デカグリセリルエステル等。勿論、これらに限定される
ものではない。3- (5-chlorobenzotriazole-2)
-Yl) -4-hydroxybenzoic acid hexaglyceryl ester, 3- (5-chlorobenzotriazol-2-yl) -4-hydroxybenzoic acid decaglyceryl ester, 3- (5-chlorobenzotriazol-2-yl)
-4-Hydroxyphenylacetic acid hexaglyceryl ester, 3- (5-chlorobenzotriazol-2-yl)
4-hydroxyphenylacetic acid decaglyceryl ester, 3- [3- (5-chlorobenzotriazole-2-
Yl) -4-hydroxyphenyl] propionic acid hexaglyceryl ester, 3- [3- (5-chlorobenzotriazol-2-yl) -4-hydroxyphenyl] propionic acid decaglyceryl ester, 4- [3- (5-
Chlorobenzotriazol-2-yl) -4-hydroxyphenyl] butanoic acid hexaglyceryl ester, 4-
[3- (5-chlorobenzotriazol-2-yl)-
4-hydroxyphenyl] butanoic acid decaglyceryl ester, 5- [3- (5-chlorobenzotriazole-2)
-Yl) -4-hydroxyphenyl] pentanoic acid hexaglyceryl ester, 5- [3- (5-chlorobenzotriazol-2-yl) -4-hydroxyphenyl] pentanoic acid decaglyceryl ester, 6- [3- (5 -Chlorobenzotriazol-2-yl) -4-hydroxyphenyl] hexanoic acid hexaglyceryl ester, 6-
[3- (5-chlorobenzotriazol-2-yl)-
4-hydroxyphenyl] hexanoic acid decaglyceryl ester, 3- [3- (5-chlorobenzotriazole-
2-yl) -4-hydroxy-5-tert-butylphenyl] propionic acid hexaglyceryl ester, 3- [3
-(5-chlorobenzotriazol-2-yl) -4-
[Hydroxy-5-tert-butylphenyl] propionic acid decaglyceryl ester and the like. Of course, it is not limited to these.

【００１８】前記一般式（１）で表される化合物のイン
クジェット記録用シート中の含有量としては、０．１〜
３ｇ／ｍ² 程度、好ましくは０．２〜１ｇ／ｍ² 程度で
ある。因みに、０．１ｇ／ｍ² より少ないと耐光性改善
効果が不十分となり、また３ｇ／ｍ² より多いと画質の
低下を招く恐れがあるため好ましくない。The content of the compound represented by the general formula (1) in the ink jet recording sheet is 0.1 to 0.1.
3 g / m ² approximately, preferably 0.2~1g / m ² approximately. Incidentally, if the amount is less than 0.1 g / m ² , the effect of improving light resistance becomes insufficient, and if it is more than 3 g / m ² , the image quality may be deteriorated.

【００１９】なお、インクジェット記録用シート中に
は、本発明の効果を阻害しない範囲で、フェノール系、
チオエーテル系、リン系の酸化防止剤、ヒンダードアミ
ン系光安定剤、ベンゾトリアゾール系、ベンゾフェノン
系の紫外線吸収剤、一重項酸素クエンチャー等を添加す
ることも可能である。In the ink jet recording sheet, a phenol-based sheet or a phenol-based sheet may be used as long as the effects of the present invention are not impaired.
It is also possible to add a thioether-based or phosphorus-based antioxidant, a hindered amine-based light stabilizer, a benzotriazole-based or benzophenone-based ultraviolet absorber, a singlet oxygen quencher, or the like.

【００２０】前記一般式（１）で表される特定の化合物
を含むインクジェット記録用シートの作成方法として
は、例えば抄紙工程中でサイズプレス等によって特定の
化合物を溶解または分散した塗液を原紙に塗布または含
浸する方法、インク吸収性顔料、接着剤、カチオン性ポ
リマーおよび特定の化合物を混合して得たインク受理層
用塗液を、上質紙（酸性紙，中性紙）、合成紙、フィル
ム、不織布等の支持体に塗工機を用いて塗布乾燥してイ
ンク受理層を形成する方法、顔料および接着剤からなる
インク受理層上に特定の化合物を溶解または分散した塗
液を塗布する方法等が挙げられる。As a method for preparing an ink jet recording sheet containing the specific compound represented by the general formula (1), for example, a coating solution in which a specific compound is dissolved or dispersed by a size press or the like in a paper making process is applied to base paper. A method of coating or impregnating, a coating liquid for an ink receiving layer obtained by mixing an ink-absorbing pigment, an adhesive, a cationic polymer and a specific compound, into a high-quality paper (acid paper, neutral paper), synthetic paper, film A method of forming an ink receiving layer by applying and drying a support such as a nonwoven fabric using a coating machine, and a method of applying a coating solution in which a specific compound is dissolved or dispersed on an ink receiving layer composed of a pigment and an adhesive. And the like.

【００２１】なかでも、インク受理層中に前記特定の化
合物を含有させる方法は、他の品質を損なうことなく、
画像の耐光性の改善により効果を発揮するため好まし
い。Above all, the method of incorporating the specific compound into the ink receiving layer can be performed without impairing other qualities.
It is preferable because the effect is exhibited by improving the light fastness of the image.

【００２２】インク受理層中に含有せしめる顔料として
は、例えばゼオライト、軽質炭酸カルシウム、重質炭酸
カルシウム、炭酸マグネシウム、カオリン、タルク、硫
酸カルシウム、硫酸バリウム、酸化チタン、酸化亜鉛、
硫化亜鉛、炭酸亜鉛、サチンホワイト、ケイ酸アルミニ
ウム、ケイソウ土、ケイ酸カルシウム、ケイ酸マグネシ
ウム、合成非晶質シリカ、水酸化アルミニウム、アルミ
ナ、アルミナ水和物、リトポン、尿素−ホルマリン樹脂
フィラー等が挙げられる。これらは単独または二種以上
を混合して用いられる。これらのなかでも、合成非晶質
シリカ、アルミナおよびアルミナ水和物はインク受理性
に優れているため、好ましく用いられる。Examples of the pigment to be contained in the ink receiving layer include zeolite, light calcium carbonate, heavy calcium carbonate, magnesium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium oxide, zinc oxide,
Zinc sulfide, zinc carbonate, satin white, aluminum silicate, diatomaceous earth, calcium silicate, magnesium silicate, synthetic amorphous silica, aluminum hydroxide, alumina, alumina hydrate, lithopone, urea-formalin resin filler, etc. No. These may be used alone or in combination of two or more. Among these, synthetic amorphous silica, alumina and alumina hydrate are preferably used because of their excellent ink receptivity.

【００２３】インク受理層中の顔料の使用量としては、
インク受理層の固形分に対して２０〜９０重量％程度、
好ましくは３０〜８０重量％程度である。なお、９０重
量％を越えるとインク受理層の塗膜強度が低下し、また
２０重量％未満になるとインクの吸収性が低下し、記録
後のインク乾燥性が不充分となり画質が低下する恐れが
ある。The amount of the pigment used in the ink receiving layer is as follows:
About 20 to 90% by weight based on the solid content of the ink receiving layer,
Preferably, it is about 30 to 80% by weight. If the content exceeds 90% by weight, the coating strength of the ink receiving layer decreases, and if the content is less than 20% by weight, the ink absorbency decreases, the ink drying property after recording becomes insufficient, and the image quality may deteriorate. is there.

【００２４】本発明において、記録画像の耐水性を向上
させる目的でカチオン性ポリマーを用いることができ
る。かかるカチオン性ポリマーは、水に溶解あるいは乳
化したときに解離してカチオン性を呈するポリマーであ
れば使用できるが、なかでも主鎖または側鎖に４級アン
モニウム基を有するポリマーが好ましい。このようなカ
チオン性ポリマーとしては、例えばジメチルジアリルア
ンモニウム塩重合物、エピクロロヒドリン・ジメチルア
ミン重合物、ポリアミドポリアミンエピクロロヒドリン
重合物、エチレンイミン酸塩重合物、ポリエチレンイミ
ン４級アンモニウム塩重合物、アクリルアミド・ジアリ
ルジメチルアンモニウムクロライド共重合物、（ジ）ア
ルキルアミノアルキル（メタ）アクリレート酸塩重合
物、（メタ）アクリロイルオキシアルキルトリアルキル
アンモニウム塩重合物、（メタ）アクリルアミドアルキ
ルトリアルキルアンモニウム塩重合物、（メタ）アクリ
ル（ジ）アルキルアミノアルキルアミド酸塩重合物、ポ
リアルキレンポリアミンジシアンジアミドアンモニウム
塩縮合物等が挙げられる。これらは単独または二種以上
を混合して用いられる。カチオン性ポリマーの含有量
は、通常０．１〜４ｇ／ｍ ² 、好ましくは０．２〜２ｇ
／ｍ² の範囲で調節される。In the present invention, the water resistance of a recorded image is improved.
Cationic polymers can be used for
You. Such cationic polymers can be dissolved in water or milk.
Is a polymer that dissociates when it becomes
Quaternary anions in the main chain or side chain.
Polymers having a monium group are preferred. Such a mosquito
As the thionic polymer, for example, dimethyl diallyl
Ammonium salt polymer, epichlorohydrin / dimethyla
Min polymer, polyamide polyamine epichlorohydrin
Polymer, ethylene iminate polymer, polyethylene imine
Quaternary ammonium salt polymer, acrylamide / diali
Dimethylammonium chloride copolymer, (di) a
Polymerization of alkylaminoalkyl (meth) acrylate
Substance, (meth) acryloyloxyalkyltrialkyl
Ammonium salt polymer, (meth) acrylamide alkyl
Rutrialkylammonium salt polymer, (meth) acrylic
(Di) alkylaminoalkylamidate polymer,
Polyalkylene polyamine dicyandiamide ammonium
Salt condensates and the like. These can be used alone or in combination
Are used as a mixture. Cationic polymer content
Is usually 0.1 to 4 g / m ^Two, Preferably 0.2 to 2 g
/ M^TwoIs adjusted in the range.

【００２５】インク受理層には、接着剤として、例えば
酸化澱粉、エーテル化澱粉等の澱粉誘導体、カルボキシ
メチルセルロース、ヒドロキシエチルセルロース等のセ
ルロース誘導体、カゼイン、ゼラチン、大豆タンパク、
完全（部分）ケン化ポリビニルアルコール、ケイ素変性
ポリビニルアルコール、アセトアセチル基変性ポリビニ
ルアルコール、スチレン−無水マレイン酸共重合体の
塩、スチレン−ブタジエン系ラテックス、アクリル系ラ
テックス、ポリエステルポリウレタン系ラテックス、酢
酸ビニル系ラテックス等の水性接着剤、或いはポリメチ
ルメタクリレート、ポリウレタン樹脂、不飽和ポリエス
テル樹脂、塩化ビニル−酢酸ビニルコポリマー、ポリビ
ニルブチラール、アルキッド樹脂等の有機溶剤可溶性樹
脂が、単独あるいは複数を混合して用いられる。これら
の接着剤は、一般に顔料１００重量部に対して５〜１２
０重量部程度、好ましくは８〜５０重量部程度の範囲で
使用される。In the ink receiving layer, adhesives such as starch derivatives such as oxidized starch and etherified starch, cellulose derivatives such as carboxymethylcellulose and hydroxyethylcellulose, casein, gelatin, soy protein,
Complete (partial) saponified polyvinyl alcohol, silicon-modified polyvinyl alcohol, acetoacetyl group-modified polyvinyl alcohol, styrene-maleic anhydride copolymer salt, styrene-butadiene latex, acrylic latex, polyester polyurethane latex, vinyl acetate An aqueous adhesive such as latex or an organic solvent-soluble resin such as polymethyl methacrylate, a polyurethane resin, an unsaturated polyester resin, a vinyl chloride-vinyl acetate copolymer, polyvinyl butyral, and an alkyd resin is used alone or in combination of two or more. These adhesives are generally used in an amount of 5 to 12 parts per 100 parts by weight of the pigment.
It is used in an amount of about 0 parts by weight, preferably about 8 to 50 parts by weight.

【００２６】更に、インク受理層中には、顔料分散剤、
増粘剤、架橋剤、流動性変性剤、消泡剤、抑泡剤、離型
剤、発泡剤、浸透剤、着色染料、着色顔料、蛍光増白
剤、防腐剤、防バイ剤、耐水化剤等を適宜添加すること
もできる。Furthermore, a pigment dispersant,
Thickeners, crosslinkers, fluidity modifiers, defoamers, defoamers, release agents, foaming agents, penetrants, coloring dyes, coloring pigments, fluorescent brighteners, preservatives, anti-foaming agents, waterproofing Agents and the like can be appropriately added.

【００２７】インク受理層は、インク受理層用塗液をバ
ーコーター、ブレードコーター、エアナイフコーター、
グラビアコーター、ダイコーター等の塗工方式で支持体
上の少なくとも片面に乾燥後の塗布量が２〜２０ｇ／ｍ
² 程度となるように塗布乾燥して形成される。因みに、
塗布量が２ｇ／ｍ² より少ないと記録画質が低下し、ま
た２０ｇ／ｍ² より多いと塗膜強度と生産性が低下する
恐れがある。インク受理層形成後、例えばスーパーカレ
ンダー、グロスカレンダーなどで加圧下のロールニップ
間を通して表面の平滑性を与えることも勿論可能であ
る。The ink receiving layer is prepared by applying a coating solution for the ink receiving layer to a bar coater, a blade coater, an air knife coater,
The coating amount after drying on at least one surface of the support by a coating method such as a gravure coater or a die coater is 2 to 20 g / m2.
It is formed by coating and drying so as to be about ² . By the way,
If the coating amount is less than 2 g / m ² , the recorded image quality will decrease, and if it exceeds 20 g / m ² , the coating film strength and productivity may decrease. After the ink receiving layer is formed, it is, of course, possible to impart a smooth surface through a roll nip under pressure using, for example, a super calender or a gloss calender.

【００２８】記録画像を形成するための水性インクと
は、着色剤および液媒体、その他の添加剤からなる記録
液体である。着色剤としては直接染料、酸性染料、反応
性染料等の各種水溶性染料が挙げられる。また、水性イ
ンクの液媒体としては、水単独、あるいは水および水溶
性有機溶剤の併用がある。水溶性有機溶剤としては、例
えばエチルアルコール、イソプロピルアルコール等の一
価アルコール、エチレングリコール、ジエチレングリコ
ール、ポリエチレングリコール、グリセリン等の多価ア
ルコール、トリエチレングリコールモノメチルエーテ
ル、トリエチレングリコールモノエチルエーテル等の多
価アルコールの低級アルキルエーテル等が挙げられる。
さらに添加剤としては、例えばｐＨ調整剤、金属封鎖
剤、防バイ剤、粘度調整剤、表面張力調整剤、界面活性
剤、および防錆剤等が挙げられる。The aqueous ink for forming a recorded image is a recording liquid comprising a colorant, a liquid medium, and other additives. Examples of the coloring agent include various water-soluble dyes such as direct dyes, acid dyes, and reactive dyes. As the liquid medium of the aqueous ink, there is water alone or a combination of water and a water-soluble organic solvent. Examples of the water-soluble organic solvent include monohydric alcohols such as ethyl alcohol and isopropyl alcohol, polyhydric alcohols such as ethylene glycol, diethylene glycol, polyethylene glycol and glycerin, and polyhydric alcohols such as triethylene glycol monomethyl ether and triethylene glycol monoethyl ether. And lower alkyl ethers of alcohols.
Further, examples of the additives include a pH adjuster, a metal sequestering agent, an anti-binder, a viscosity adjuster, a surface tension adjuster, a surfactant, and a rust inhibitor.

【００２９】[0029]

【実施例】以下に実施例を挙げて本発明をより具体的に
説明するが、勿論これらに限定されるものではない。な
お、例中の「部」および「％」は、特に断わらない限り
それぞれ重量部および重量％を示す。The present invention will be described in more detail with reference to the following Examples, but it should be understood that the present invention is by no means restricted to such specific Examples. In the examples, "parts" and "%" indicate parts by weight and% by weight, respectively, unless otherwise specified.

【００３０】実施例１ ３−〔３−（ベンゾトリアゾール−２−イル）−４−ヒ
ドロキシフェニル〕プロピオン酸デカグリセリルエステ
ル６部、合成非晶質シリカ（商品名：ファインシールＸ
４５，徳山曹達製）１００部、ケイ素変性ポリビニルア
ルコール（商品名：Ｒ１１３０，クラレ製）３０部、カ
チオン性ポリマー（商品名：ＰＡＳ−Ｊ−８１，日東紡
製）１０部、少量の消泡剤、分散剤および水からなる固
形分濃度１５％のインク受理層用塗液を、６５ｇ／ｍ²
の上質紙上に固形分で１２ｇ／ｍ ² となるようにワイヤ
ーバーにて塗布乾燥してインク受理層を設けた後、スー
パーキャレンダー処理してインクジェット記録用シート
を作成した。Example 1 3- [3- (benzotriazol-2-yl) -4-h
(Droxyphenyl) decaglyceryl ester propionate
6 parts, synthetic amorphous silica (trade name: Fine Seal X)
45, manufactured by Tokuyama Soda) 100 parts, silicon-modified polyvinyl alcohol
30 parts of Rukoru (trade name: R1130, made by Kuraray)
Thion polymer (trade name: PAS-J-81, Nitto Boss)
10 parts, a solid consisting of a small amount of defoamer, dispersant and water
A coating solution for ink receiving layer having a concentration of 15%^Two
12g / m solids on high quality paper ^TwoTo be a wire
After coating and drying with a bar to provide an ink receiving layer,
Percalender treatment sheet for inkjet recording
It was created.

【００３１】実施例２ 実施例１において、３−〔３−（ベンゾトリアゾール−
２−イル）−４−ヒドロキシフェニル〕プロピオン酸デ
カグリセリルエステルの代わりに、３−〔３−（ベンゾ
トリアゾール−２−イル）−４−ヒドロキシフェニル〕
プロピオン酸ヘキサグリセリルエステルを用いた以外
は、実施例１と同様にしてインクジェット記録用シート
を作成した。Example 2 In Example 1, 3- [3- (benzotriazole-
2- [yl] -4-hydroxyphenyl] propionic acid decaglyceryl ester is replaced by 3- [3- (benzotriazol-2-yl) -4-hydroxyphenyl]
An ink jet recording sheet was prepared in the same manner as in Example 1, except that hexaglyceryl propionate was used.

【００３２】実施例３ 実施例１において、３−〔３−（ベンゾトリアゾール−
２−イル）−４−ヒドロキシフェニル〕プロピオン酸デ
カグリセリルエステルの代わりに、３−（ベンゾトリア
ゾール−２−イル）−４−ヒドロキシフェニル酢酸デカ
グリセリルエステルを用いた以外は、実施例１と同様に
してインクジェット記録用シートを作成した。Example 3 In Example 1, 3- [3- (benzotriazole-
2- (yl) -4-hydroxyphenyl] propionic acid decaglyceryl ester in the same manner as in Example 1 except that 3- (benzotriazol-2-yl) -4-hydroxyphenylacetic acid decaglyceryl ester was used. To prepare an ink jet recording sheet.

【００３３】実施例４ 実施例１において、３−〔３−（ベンゾトリアゾール−
２−イル）−４−ヒドロキシフェニル〕プロピオン酸デ
カグリセリルエステルの代わりに、３−〔３−（ベンゾ
トリアゾール−２−イル）−４−ヒドロキシ−５−tert
−ブチルフェニル〕プロピオン酸デカグリセリルエステ
ルを用いた以外は、実施例１と同様にしてインクジェッ
ト記録用シートを作成した。Example 4 In Example 1, 3- [3- (benzotriazole-
3- [3- (benzotriazol-2-yl) -4-hydroxy-5-tert instead of 2-yl) -4-hydroxyphenyl] propionic acid decaglyceryl ester
[Butylphenyl] propionic acid decaglyceryl ester was used to prepare an inkjet recording sheet in the same manner as in Example 1.

【００３４】比較例１ 実施例１において、３−〔３−（ベンゾトリアゾール−
２−イル）−４−ヒドロキシフェニル〕プロピオン酸デ
カグリセリルエステルを使用しない以外は、実施例１と
同様にしてインクジェット記録用シートを作成した。Comparative Example 1 In Example 1, 3- [3- (benzotriazole-
A sheet for inkjet recording was prepared in the same manner as in Example 1, except that decaglyceryl ester of 2-yl) -4-hydroxyphenyl] propionate was not used.

【００３５】比較例２ 実施例１において、３−〔３−（ベンゾトリアゾール−
２−イル）−４−ヒドロキシフェニル〕プロピオン酸デ
カグリセリルエステルの代わりに、下記の添加剤分散液
５５部を添加した以外は、実施例１と同様にしてインク
ジェット記録用シートを作成した。 〔添加剤分散液の調製〕２−（２′−ヒドロキシ−５′
−メチルフェニル）ベンゾトリアゾール１５部、ポリビ
ニルアルコールの５％水溶液１０部、水３０部からなる
混合物をサンドミルで平均粒子径が１．０μｍとなるま
で粉砕して分散液を得た。Comparative Example 2 In Example 1, 3- [3- (benzotriazole-
A sheet for ink jet recording was prepared in the same manner as in Example 1 except that 55 parts of the following additive dispersion was added instead of decaglyceryl ester of 2-yl) -4-hydroxyphenyl] propionate. [Preparation of additive dispersion] 2- (2'-hydroxy-5 '
A mixture of 15 parts of (-methylphenyl) benzotriazole, 10 parts of a 5% aqueous solution of polyvinyl alcohol, and 30 parts of water was pulverized by a sand mill until the average particle diameter became 1.0 μm to obtain a dispersion.

【００３６】比較例３ 実施例１において、３−〔３−（ベンゾトリアゾール−
２−イル）−４−ヒドロキシフェニル〕プロピオン酸デ
カグリセリルエステルの代わりに、メチル−３−〔３−
tert−ブチル−５−（２Ｈ−ベンゾトリアゾール−２−
イル）−４−ヒドロキシフェニル〕プロピオネートとポ
リエチレングリコール（分子量約３０００）との縮合物
を用いた以外は、実施例１と同様にしてインクジェット
記録用シートを作成した。Comparative Example 3 In Example 1, 3- [3- (benzotriazole-
2-yl) -4-hydroxyphenyl] propionic acid decaglyceryl ester is replaced by methyl-3- [3-
tert-butyl-5- (2H-benzotriazole-2-
Il) -4-hydroxyphenyl] propionate and an inkjet recording sheet were prepared in the same manner as in Example 1 except that a condensate of polyethylene glycol (molecular weight: about 3000) was used.

【００３７】上記の実施例および比較例で得たインクジ
ェット記録用シートについて、下記の評価を行った。 〔画像部の耐光性〕インクジェット記録用シートにイン
クジェットプリンター（機種名：ＰＭ−７００Ｃ、セイ
コーエプソン製）を用いて、マゼンタのインクでベタ印
字した。得られた画像部について、光源：キセノン，６
３゜Ｃ，４０％ＲＨの条件に設定したウェザーメーター
（機種名：SUNSHINE XENON LONG LIFE WEATHER MET
ER，スガ試験機製）で７２時間光照射し、照射前後の濃
度をマクベス濃度計（型式：ＲＤ−９１４、マゼンタフ
ィルター使用、マクベス社製）で測定し、下記の式より
画像褪色率を算出し、表に示した。The following evaluations were performed on the ink jet recording sheets obtained in the above Examples and Comparative Examples. [Light resistance of image section] Solid printing was performed on the ink jet recording sheet with magenta ink using an ink jet printer (model name: PM-700C, manufactured by Seiko Epson Corporation). Regarding the obtained image portion, a light source: xenon, 6
Weather meter set to 3 ゜ C, 40% RH (Model name: SUNSHINE XENON LONG LIFE WEATHER MET
ER, manufactured by Suga Test Instruments Co., Ltd.) for 72 hours, and the density before and after the irradiation was measured by a Macbeth densitometer (model: RD-914, using a magenta filter, manufactured by Macbeth), and the image fading rate was calculated by the following equation. , Are shown in the table.

【００３８】画像褪色率（％）＝〔１−（照射後の濃
度）／（照射前の濃度）〕×１００Image fading rate (%) = [1− (density after irradiation) / (density before irradiation)] × 100

【００３９】〔地肌部の耐光性〕ウェザーメーターによ
る光照射前後の地肌部のＩＳＯ白色度を、分光白色度測
定計（機種名：ＳＣ−１０ＷＮ、スガ試験機製）で測定
し、表に示した。[Light resistance of the background portion] The ISO whiteness of the background portion before and after light irradiation by a weather meter was measured with a spectral whiteness meter (model name: SC-10WN, manufactured by Suga Test Instruments) and shown in the table. .

【００４０】〔画質〕印字後の画像について目視により
観察し、その画質を評価し、表に示した。 ○：優れている △：やや劣っているが、実用上問題ない ×：劣っている[Image quality] The image after printing was visually observed, and the image quality was evaluated. ：: excellent △: slightly inferior, but no problem in practical use ×: inferior

【００４１】[0041]

【表１】 [Table 1]

【００４２】[0042]

【発明の効果】表から明らかなように、本発明のインク
ジェット記録用シートは、光に長時間暴露された場合で
もマゼンタ画像の褪色が少なく、しかも地肌部の黄変
や、画質の劣化もない優れた記録用シートであった。As is clear from the table, the ink jet recording sheet of the present invention has little discoloration of the magenta image even when exposed to light for a long time, and has no yellowing of the background and no deterioration of the image quality. It was an excellent recording sheet.

─────────────────────────────────────────────────────
────────────────────────────────────────────────── ───

【手続補正書】[Procedure amendment]

【提出日】平成１１年３月２６日（１９９９．３．２
６）[Submission date] March 26, 1999 (1999.3.2
6)

【手続補正１】[Procedure amendment 1]

【補正対象書類名】明細書[Document name to be amended] Statement

【補正対象項目名】００３７[Correction target item name] 0037

【補正方法】変更[Correction method] Change

【補正内容】[Correction contents]

【００３７】上記の実施例および比較例で得たインクジ
ェット記録用シートについて、下記の評価を行った。 〔画像部の耐光性〕インクジェット記録用シートにイン
クジェットプリンター（機種名：ＰＭ−７００Ｃ、セイ
コーエプソン製）を用いて、マゼンタのインクでベタ印
字した。得られた画像部について、光源：キセノン，６
３゜Ｃ，４０％ＲＨの条件に設定したウェザーメーター
（機種名：SUNSHINE XENON LONG LIFE WEATHER MET
ER，スガ試験機製）で７２時間光照射し、照射前後の濃
度をマクベス濃度計（型式：ＲＤ−９１４、グリーンフ
ィルター使用、マクベス社製）で測定し、下記の式より
画像褪色率を算出し、表に示した。The following evaluations were performed on the ink jet recording sheets obtained in the above Examples and Comparative Examples. [Light resistance of image section] Solid printing was performed on the ink jet recording sheet with magenta ink using an ink jet printer (model name: PM-700C, manufactured by Seiko Epson Corporation). Regarding the obtained image portion, a light source: xenon, 6
Weather meter set to 3 ゜ C, 40% RH (Model name: SUNSHINE XENON LONG LIFE WEATHER MET
ER, manufactured by Suga Test Instruments Co., Ltd. for 72 hours, and the density before and after the irradiation is measured using a Macbeth densitometer (model: RD-914, Greenfield).
( Using a filter , manufactured by Macbeth Co., Ltd.), and the image fading rate was calculated from the following formula, and is shown in the table.

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】水性インクを用いて記録画像を形成するイ
ンクジェット記録用シートにおいて、該記録用シート中
に、一般式（１）で表されるベンゾトリアゾール化合物
の少なくとも１種を含有せしめたことを特徴とするイン
クジェット記録用シート。 【化１】 〔式中、Ｒ₁ は水素原子または炭素数１〜５のアルキル
基を示し、Ｒ₂ は水素原子または塩素原子を示す。ｍは
０または１〜４の整数を、ｎは１〜１２の整数を示
す。〕1. An ink jet recording sheet for forming a recorded image using an aqueous ink, wherein the recording sheet contains at least one benzotriazole compound represented by the general formula (1). Characteristic inkjet recording sheet. Embedded image [Wherein, R ₁ represents a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, and R ₂ represents a hydrogen atom or a chlorine atom. m represents 0 or an integer of 1 to 4, and n represents an integer of 1 to 12. ]